ZYGLO ZL-2C

ZYGLO ZL-27A

ZYGLO ZL-37

General Description Zyglo ZL-2C, ZL-27A, ZL-37 are general purpose post high sensitivity applications. They all exhibit outstanding penetrating and indication stability characteristics which provides for maximum reliability in locating surface-open flaws and discontinuities They are safe to use on most engineering and aerospace alloys including aluminium, steel, nickel and titanium. These post emulsifiable (post removable) penetrants are formulated to be immiscible with water. This property guards againsover-removal from defects by over washing, and allows the penetrant to separate readily from water, making effluent clean up easier. ZL-2C, ZL-27A and ZL-37 are used in conjunction with a hydrophilic remover or lipophilic emulsifier to render them washawith water. The penetrants fluoresce a bright green-yellow when exposed to ultraviolet radiation (UVshould therefore be used with a suitable UV source such as the Applications ZL-2C, ZL-27A and ZL-37 are typically used on castings, turbine components, welds, forgings, and rough and machined surfaces to find cracks, seams, laps, laminations and porosity. Composition ZL-2C, ZL-27A and ZL-37 contain a blend of

Product Data Sheet

Product Data Sheet Zyglo ZL

27A

37 are general purpose post emulsifiable fluorescent penetrants used for a wide range of medium to

They all exhibit outstanding penetrating and indication stability characteristics which provides for maximum reliability in and discontinuities They are safe to use on most engineering and aerospace alloys including

These post emulsifiable (post removable) penetrants are formulated to be immiscible with water. This property guards againsremoval from defects by over washing, and allows the penetrant to separate readily from water, making effluent clean up

37 are used in conjunction with a hydrophilic remover or lipophilic emulsifier to render them washa

yellow when exposed to ultraviolet radiation (UV-A) peak wavelength of 365 nm, and should therefore be used with a suitable UV source such as the Magnaflux ZB-100F or Magnaflux ZB

37 are typically used on castings, turbine components, welds, forgings, and rough and machined surfaces to find cracks, seams, laps, laminations and porosity.

37 contain a blend of petroleum distillates, oils, alkyl aryl phosphate and fluorescent dyes.

POST EMULSIFIABLE

FLUORESCENT PENETRANTS

Product Data Sheet

Zyglo ZL-2C, ZL-27A, ZL-37 page 1

emulsifiable fluorescent penetrants used for a wide range of medium to

They all exhibit outstanding penetrating and indication stability characteristics which provides for maximum reliability in and discontinuities They are safe to use on most engineering and aerospace alloys including

These post emulsifiable (post removable) penetrants are formulated to be immiscible with water. This property guards against removal from defects by over washing, and allows the penetrant to separate readily from water, making effluent clean up

37 are used in conjunction with a hydrophilic remover or lipophilic emulsifier to render them washable

A) peak wavelength of 365 nm, and Magnaflux ZB-100-LED.

37 are typically used on castings, turbine components, welds, forgings, and rough and machined

petroleum distillates, oils, alkyl aryl phosphate and fluorescent dyes.

POST EMULSIFIABLE

FLUORESCENT PENETRANTS

Typical Properties (not a specification)

Property Colour Odour Flash point Density Viscosity @ 38 °C Corrosion Meets AMS 2644Sulfur content Chloride content Fluoride content Sodium content AMS 2644 class Type 1 Method B/DAMS 2644 sensitivity Level 2

Like all Magnaflux materials, Zyglo ZL-2C, ZLconsistency and uniformity to assure optimum process control and inspection reliability. Benefits � Wide range of medium to high sensitivity � Immiscible with water – guarding against over General Method of Use 1. Pre-clean the test part 2. Apply penetrant to the cleaned test part and allow contact time3. When using hydrophilic emulsifiers pre-4. Dip the test part in the emulsifier for a predetermined time5. Remove the excess penetrant by spraying the test part with clean water6. Dry, develop and then inspect using a UV light source

Pre-cleaning

Test parts must be clean and dry, and free from oilapplied. To clean the surface we recommend the use of the Magnaflux cleaner Spotcheck SKC Method of Application Penetrants can be applied by immersion dip, brush, flow on, conventional or electrostatic spray. Whichever method of application is used, the test area must be completely covered with penetrant. Penetration Time and Temperature The generally accepted minimum penetration time is 2 to 5 minutes, 10 minutes being adequate for most situations, although specific process specifications may require longer. Detailed processing parameters will normally be specified in the controllprocess specification (where applicable). Zyglo water washable penetrants should be used at temperatures between 10°C and 55°C.

Product Data Sheet

Product Data Sheet

ot a specification)

ZL-2C ZL-27A ZLYellow/green Yellow/green Yellow/green

Bland Bland Bland> 93 °C > 93 °C (bulk product) > 93

0.89 g/cm3 0.93 g/cm3 0.956.0 cS 9.2 cS 13.5

Meets AMS 2644 Meets AMS 2644 Meets AMS 2644< 300 ppm < 300 ppm < 300 ppm< 300 ppm < 300 ppm < 300 ppm< 50 ppm < 50 ppm < 50 ppm

< 100 ppm < 100 ppm < 100 ppmType 1 Method B/D Type 1 Method B/D Type 1 Method B/DLevel 2 – medium Level 3 – high Level 4 –

2C, ZL-27A and ZL-37 are closely controlled to provide unique batch to batch consistency and uniformity to assure optimum process control and inspection reliability.

Wide range of medium to high sensitivity applications guarding against over-removal as a result of over washing

Apply penetrant to the cleaned test part and allow contact time -rinse the test part using a water spray

Dip the test part in the emulsifier for a predetermined time Remove the excess penetrant by spraying the test part with clean water Dry, develop and then inspect using a UV light source

free from oil, grease or other foreign contaminating substances before penetrant is To clean the surface we recommend the use of the Magnaflux cleaner Spotcheck SKC-S.

can be applied by immersion dip, brush, flow on, conventional or electrostatic spray. Whichever method of application is used, the test area must be completely covered with penetrant.

Penetration Time and Temperature

ration time is 2 to 5 minutes, 10 minutes being adequate for most situations, although specific process specifications may require longer. Detailed processing parameters will normally be specified in the controll

Zyglo water washable penetrants should be used at temperatures between 10°C and 55°C.

Product Data Sheet

Product Data Sheet Zyglo ZL-2C, ZL-27A, ZL-37 page 2

ZL-37 Yellow/green

Bland > 93 °C

0.95 g/cm3 13.5 cS

Meets AMS 2644 00 ppm 00 ppm

< 50 ppm < 100 ppm

Type 1 Method B/D – ultra high

are closely controlled to provide unique batch to batch

grease or other foreign contaminating substances before penetrant is S.

can be applied by immersion dip, brush, flow on, conventional or electrostatic spray. Whichever method of

ration time is 2 to 5 minutes, 10 minutes being adequate for most situations, although specific process specifications may require longer. Detailed processing parameters will normally be specified in the controlling

Penetrant Removal ZL-2C, ZL-27A and ZL-37 require the use of a lipophilic or hydrophilic emulsifier to render them water washable. The penetrant covered part under test is immersed in the emulsifier (hydrophilic emulsifiers can be applied by spray) for a predetermined length of time then washed with a water spray. When using hydrophilic emulsifier it is preferable to prethe penetrant covered test part with plain water before the emulsifier is applied. This prepenetrant lowering the amount of penetrant entering and contaminating the emulsifier tank. The preeasily treated to separate the penetrant and water. The water can be re Component Drying Once the surface penetrant has been removed, the component should be dried prior to developer application.achieved by placing the component in a controlled recirculating warm air dryer at a temperature of between 50°C and 70°C, until just dry. Zyglo developers should then be used to maximise the sensitivity of the penetrants. Developing A developer is used to maximise the sensitivity and to provide a white contrasting background against which the indications can be readily seen. Three types of developer can be used: � Dry powder developers are free flowing lightweight powders wh

dusting, electrostatic spray or by puffer.� Solvent based developers are quick drying materials which are applied by spraying. The component under test must be

dry before developer application. � Aqueous or water based developers

the component must be dried before inspection. Note: To maximise penetrant sensitivity, parts should not remain in aqueous developers for any lengthminimum of 10 minutes development time before inspecting the component in a dindications, if present, will appear bright green Recommended Pre-cleaner/Emulsifiers

Product typePre-cleanerEmulsifier

Developer

Post Cleaning Post cleaning of the tested component can be carried out if required, by an appropriate technique. Developer residues can be removed either by wiping with a cloth or by a watdegreasing or solvent soak. Penetrant Rinse Water Disposal Dye penetrant process rinse waters should not be discharged to local authority waterways or sewers without some form of effluent treatment. Magnaflux can advise on suitable equipment for this purpose, for further information please contact Magnaflux.

Product Data Sheet

Product Data Sheet Zyglo ZL

37 require the use of a lipophilic or hydrophilic emulsifier to render them water washable. The t under test is immersed in the emulsifier (hydrophilic emulsifiers can be applied by spray) for a

predetermined length of time then washed with a water spray. When using hydrophilic emulsifier it is preferable to prewith plain water before the emulsifier is applied. This pre-rinse removes the bulk of the surface

penetrant lowering the amount of penetrant entering and contaminating the emulsifier tank. The preant and water. The water can be re-used in further pre-rinsing operations.

Once the surface penetrant has been removed, the component should be dried prior to developer application.achieved by placing the component in a controlled recirculating warm air dryer at a temperature of between 50°C and 70°C,

Zyglo developers should then be used to maximise the sensitivity of the penetrants.

developer is used to maximise the sensitivity and to provide a white contrasting background against which the Three types of developer can be used:

are free flowing lightweight powders which are applied to the dry component by powder storm, dusting, electrostatic spray or by puffer.

are quick drying materials which are applied by spraying. The component under test must be

r water based developers are applied prior to component drying, by dipping or spraying. After application the component must be dried before inspection.

: To maximise penetrant sensitivity, parts should not remain in aqueous developers for any lengthminimum of 10 minutes development time before inspecting the component in a darkened area under UVindications, if present, will appear bright green-yellow against the white developer background.

Emulsifiers/Developers for ZL-2C, ZL-27A and ZL

Product type Product name Type cleaner Spotcheck SKC-S Solvent based

Emulsifier Zyglo ZR-10C Zyglo ZE-4B

Hydrophilic Lipophilic

Developer Zyglo ZP-4B Zyglo ZP-5B

Zyglo ZP-14A Zyglo ZP-9F

Spotcheck SKD-S2

Dry Aqueous Aqueous

Solvent based Solvent based

Post cleaning of the tested component can be carried out if required, by an appropriate technique. Developer residues can be removed either by wiping with a cloth or by a water and detergent wash. Penetrant residues can be removed by vapour

Dye penetrant process rinse waters should not be discharged to local authority waterways or sewers without some form of

Magnaflux can advise on suitable equipment for this purpose, for further information please contact Magnaflux.

Product Data Sheet

Zyglo ZL-2C, ZL-27A, ZL-37 page 3

37 require the use of a lipophilic or hydrophilic emulsifier to render them water washable. The t under test is immersed in the emulsifier (hydrophilic emulsifiers can be applied by spray) for a

predetermined length of time then washed with a water spray. When using hydrophilic emulsifier it is preferable to pre-rinse rinse removes the bulk of the surface

penetrant lowering the amount of penetrant entering and contaminating the emulsifier tank. The pre-rinse effluent can be rinsing operations.

Once the surface penetrant has been removed, the component should be dried prior to developer application. This is generally achieved by placing the component in a controlled recirculating warm air dryer at a temperature of between 50°C and 70°C,

developer is used to maximise the sensitivity and to provide a white contrasting background against which the fluorescent

ich are applied to the dry component by powder storm,

are quick drying materials which are applied by spraying. The component under test must be

to component drying, by dipping or spraying. After application

: To maximise penetrant sensitivity, parts should not remain in aqueous developers for any length of time. Allow a arkened area under UV(A) (365 nm), where

27A and ZL-37

Post cleaning of the tested component can be carried out if required, by an appropriate technique. Developer residues can be er and detergent wash. Penetrant residues can be removed by vapour

Dye penetrant process rinse waters should not be discharged to local authority waterways or sewers without some form of

Magnaflux can advise on suitable equipment for this purpose, for further information please contact Magnaflux.

Specification Compliance

Specification AMS 2644 ASME B & PV Code, Sec VASTM E-165 ASTM E-1417 MIL-STD-271 PRATT & WHITNEY ROLLS ROYCE RPS 702/CSS 232ROLLS ROYCE RRP 58003 SAFRAN Pr-5000/In-5000SNECMA DMC0010

Availability ZL-2C is available as follows: � 25 litre containers, part number 056C079.� 200 litre drums, part number 056C080. ZL-27A is available as follows: � 10 x 400ml aerosols, part number 008A002.� 25 litre containers, part number 066C017.� 200 litre drums, part number 066C016. ZL-37 is available as follows: � 25 litre containers, part number 066C020.� 200 litre drums, part number 066C019. Health and Safety � Safety Data Sheets for the individual

Magnaflux website (www.eu.magnaflux.com� Read the relevant Safety Data Sheets before use Magnaflux (A Division of ITW Ltd), Faraday Road, South Dorcan Industrial Estate,Swindon, Wiltshire, SN3 5HE, UK. Tel: +44 (0)1793 524566 Fax: +44 (0)1793 490459 Email: sales@magnaflux.co.uk www.eu.magnaflux.com Issue 3 15/12/2012

Product Data Sheet

Product Data Sheet

ZL-2C ZL-27A � �

ASME B & PV Code, Sec V � � � � � � � � � �

ROLLS ROYCE RPS 702/CSS 232 � � ROLLS ROYCE RRP 58003 – supersedes RPS 702 � �

5000 � � � �

Coverage

1 litre covers approximately 20-28 square metres.

79. 200 litre drums, part number 056C080.

10 x 400ml aerosols, part number 008A002. 25 litre containers, part number 066C017.

number 066C016.

25 litre containers, part number 066C020. 200 litre drums, part number 066C019.

heets for the individual products are available on request from your Magnaflux distributor or via the magnaflux.com).

heets before use.

Faraday Road, South Dorcan Industrial Estate,

Tel: +44 (0)1793 524566 Fax: +44 (0)1793 490459

Product Data Sheet

Product Data Sheet Zyglo ZL-2C, ZL-27A, ZL-37 page 4

ZL-37 � � � � � � � � � �

28 square metres.

are available on request from your Magnaflux distributor or via the