•The laser always irradiates the sample vertically to obtain a Raman image without distortion
•Accurate image information also obtained when using 3-D imaging
•A wide area sample measurement using only laser scanning (50 µm x 50 µm using a 100X objective lens)
Laser
Objective lens
Sample
‘‘VertiScan’ Laser ScanningVertiScan’ Laser Scanning
VertiScan Conventional Laser scan
‘‘VertiScan’ Laser ScanningVertiScan’ Laser Scanning
Sample Raman image
VertiScan
Laser spot shape
Laser
Objective lens
Sample Sample
Consistently complete circle
No distortion, wide range Raman imaging
Conventional Laser scan
Objective lens
Sample area far from the center of the objective lens is irradiated from an ‘oblique’ laser beam. A measurement point of the internal sample can be greatly distorted.
Spot far from center is ellipsoidal with low spatial resolution
Distorted Raman imaging for outside sample positions, distortion-free imaging in center of sample
Laser spot shape
Sample Raman image
Laser always irradiates the sample vertically
SPRIntS High Speed ImagingSPRIntS High Speed Imaging
Peak height at 520 cm-1
Polymer Laminate – Cross Section Polymer Laminate – Cross Section Spectral Images Spectral Images
Polyvinyl acetate – 1297 cm-1
Polyethylene – 849 cm-1
Nylon/Polyamide – 1639 cm-1
Polymer Laminate – Image Overlay Polymer Laminate – Image Overlay
Polymer Laminate – 3-D Image Polymer Laminate – 3-D Image (1639 cm(1639 cm-1-1))
Polymer Laminate – 3-D Image Polymer Laminate – 3-D Image (1639 cm(1639 cm-1-1))
Polymer Laminate – 3-D Image (1077 cmPolymer Laminate – 3-D Image (1077 cm-1-1) )
Polymer Laminate – 3-D Composite ImagePolymer Laminate – 3-D Composite Image
Polyvinyl alcohol
Polyethylene
Nylon/Polyamide
Polymer Laminate – Cross Section Polymer Laminate – Cross Section Analysis Analysis
Polymer Laminate – 3-D Image Polymer Laminate – 3-D Image (1608 cm(1608 cm-1-1))
Polymer Laminate – 3-D Image (1626 cmPolymer Laminate – 3-D Image (1626 cm-1-1) )
Polymer Laminate – 3-D Image (868 cmPolymer Laminate – 3-D Image (868 cm-1-1) )
Polymer Laminate – 3-D Composite ImagePolymer Laminate – 3-D Composite Image
Acknowledgements Acknowledgements