ULTEM™ 9085 Resin
FDM® Thermoplastic FilamentFit for High-Performance Applications
The information presented are typical values intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes.
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
2
OverviewULTEM™ 9085 resin filament is a PEI (polyetherimide) thermoplastic FDM material. It features a high strength-to-weight ratio, high
thermal and chemical resistance, and meets multiple aerospace and railway industry standards for flame, smoke and toxicity (FST)
characteristics.
ULTEM™ 9085 resin CG (Certified Grade) meets more stringent test criteria and possesses documented traceability from filament back
to raw material lot number. Included documentation:
• Certificate of Analysis – for both raw material and filament are supplied, documenting test results and identification to match
filament manufacturing lot number to raw material batch number.
• Certificate of Conformance – confirms that the material is manufactured in compliance to approved Stratasys and industry
specifications.
Typical applications include production parts and functional prototypes. Available colors are natural and black.
Contents:Overview …………………………………………………………………………………...........................................…………............… 2
Ordering Information ……………………………………………………………....................................................……………………… 3
Physical Properties .......................................................................................................................................................................... 4
Mechanical Properties …………………………..……………………................................……...................…………………………..... 5
Flame, Smoke, and Toxicity Test Results .............……................................................................…….........……………………........ 10
Outgassing .........................................................….………….……................................................................……....…................... 13
Fire Protection for Railway Vehicles .................................................................................................................................................. 13
Appendix ………………………………………………………………………………................................……………...........……..…… 14
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
3
Part Number Description
Filament Canisters(1)(2)
355-02310 ULTEM™ 9085 resin natural, 92 cu in – Plus
355-08310 ULTEM™ 9085 resin natural, 184 cu in – Plus
355-23101 ULTEM™ 9085 resin CG, 92 cu in – Plus
355-02311 ULTEM™ 9085 resin black, 92 cu in – Plus
355-03220 ULTEM™ 9085 resin BASS, 92 cu in – Plus
312-20001 ULTEM™ 9085 resin CG, 92 cu in – Classic
312-20000 ULTEM™ 9085 resin natural, 92 cu in – Classic
312-20018 ULTEM™ 9085 resin natural, 184 cu in – Classic
312-20200 ULTEM™ 9085 resin black, 92 cu in – Classic
310-30600 ULTEM™ 9085 resin BASS, 92 cu in - Classic
Printer Consumables
511-10401 T16 tip, 0.010 in. (0.254 mm) layer height
511-10410 T16A tip, 0.010 in. (0.254 mm) layer height
511-10701 T20 tip, 0.013 in. (0.330 mm) layer height
325-00475(3) 900 high temperature build sheet, 0.02x26x38 in (0.51x660x965 mm)
325-00275(4) 900 & 450 high temperature build sheet, 0.02x16x18.5 in (0.51x406x470 mm)
310-00300(5) High Temperature build sheet, 0.03x16x18.5 in. (0.76x406x470 mm)
Ordering Information
Table 2. ULTEM™ 9085 Resin Ordering Information
(1) Classic canisters are compatible with all Fortus 400mc and Fortus 900mc printers prior to s/n L502(2) Plus canisters are compatible with all Fortus 450mc, all Stratasys F900, and Fortus 900mc printers s/n L502 and up(3) Compatible with Stratasys F900 and Fortus 900mc(4) Compatible with Fortus 450mc, Stratasys F900 and Fortus 900mc(5) Compatible with Fortus 400mc
Build Sheet
High temperature
0.03 x 26 x 38 in. (0.76 x 660 x 965 mm)
0.03 x 16 x 18.5 in. (0.76 x 406 x 470 mm)
0.02 x 16 x 18.5 in (0.51 x 406 x 470 mm)
Table 1. Printer and Support Material Compatibility
Printer Model Tip Support Material Support Tip
Fortus 400Fortus 400 T16T16
T20T20
9085 Support9085 Support T16 (all slices)T16 (all slices)
Fortus 450Fortus 450 T16T16
T20T20
9085 Support9085 Support T16 (all slices)T16 (all slices)
Fortus 900mcFortus 900mc T16T16
T16AT16A
T20T20
9085 Support9085 Support T16 (all slices)T16 (all slices)
F900F900 T16T16
T16AT16A
T20T20
9085 Support9085 Support T16 (all slices)T16 (all slices)
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
4
Values are measured as printed. XY, XZ, and ZX orientations were tested.
For full details refer to the Stratasys Materials Test Procedure on www.stratasys.com.
DSC and TMA curves can be found in the Appendix.
Property Test Method Typical Values
HDT @ 66psiASTM D648
Method B176.9 °C (350.4 °F)
HDT @ 264psiASTM D648
Method B172.9 °C (343.2 °F)
TgASTM D7426
Inflection Point177.32 °C (351.18 °F)
Mean CTEASTM E831
(-50C to 80C)44.89 µm/[m·°C] (24.94 µin/[in·°F])
Mean CTEASTM E831
(80C to 160C)31.35 µm/[m·°C] (17.42 µin/[in·°F])
Volume Resistivity ASTM D257 > 6.89*1015 Ω·cm
Dielectric ConstantASTM D150
1 kHz test condition2.84
Dielectric ConstantASTM D150
2 MHz test condition2.69
Dissipation FactorASTM D150
1 kHz test condition0.002
Dissipation FactorASTM D150
2 MHz test condition0.010
Specific GravityASTM D792
@ 23C1.27
UL Flammability(1) ANSI/UL 746B V0 – Blue Card #E345258
Table 3. ULTEM™ 9085 Resin Physical Properties
(1) Applies to the natural version of ULTEMTM 9085 resin only
Physical Properties
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logohttp://www.stratasys.comhttps://iq.ul.com/plastics/
ULT
EM
TM 9
085
Res
in D
ata
She
et
5
Samples, natural and black, were printed with 0.010 in. (0.254 mm) and 0.013 in. (0.330 mm) layer heights.
For the full test procedure please see the Stratasys Materials Test Procedure on www.stratasys.com.
Mechanical Properties
Print Orientation
Parts created using FDM® are anisotropic as a result of
the printing process. Below is a reference of the different
orientations used to characterize the material.
Tensile Curves
Due to the anisotropic nature of FDM, tensile curves look
different depending on orientation. Below is a guide of the two
types of curves seen when printing tensile samples and what
reported values mean.
Z
Y
X
Flat (XY) On Edge (XZ) Upright (ZX)
A = Tensile at break, elongation at break (no yield point)
STRAIN
ST
RE
SS
YIELD POINT
B = Tensile at yield, elongation at yield
C = Tensile at break, elongation at break
A
BC
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
6
XZ Orientation(1) ZX Orientation(1)
Tensile Properties: ASTM D638
Yield StrengthMPa 69.2 (1.0) No yield
psi 10000 (150) No yield
Elongation @ Yield % 5.4 (0.50) No yield
Strength @ BreakMPa 68.1 (1.6) 39.4 (8.7)
psi 9870 (230) 5710 (1300)
Elongation @ Break % 5.4 (0.50) 1.9 (0.51)
Modulus (Elastic) GPa 2.52 (0.062) 2.41 (0.15)
ksi 365 (8.9) 350 (22)
Flexural Properties: ASTM D790, Procedure A
Strength @ BreakMPa 104 (2.2) 73.1 (13)
psi 15000 (320) 10600 (1900)
Strain @ Break % No break 3.67 (0.55)
ModulusGPa 2.40 (0.032) 2.13 (0.081)
ksi 348 (4.6) 309 (12)
Compression Properties: ASTM D695
Yield Strength MPa 139 (9.4) 342 (27)
psi 20100 (1400) 49600 (390)
ModulusGPa 2.22 (0.047) 2.28 (0.080)
ksi 321 (6.8) 331 (12)
Impact Properties: ASTM D256, ASTM D4812
Izod, NotchedJ/m 88.5 (21) 39.2 (4.3)
ft*lb/in 1.66 (0.40) 0.735 (0.080)
Izod, UnnotchedJ/m 647 (66) 187 (42)
ft*lb/in 12.1 (1.2) 3.51 (0.79)
Table 4. ULTEM™ 9085 Resin Natural Mechanical Properties (T16 tip)
(1) Values in parentheses are standard deviations
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
7
XZ Orientation ZX Orientation
Tensile Properties: ASTM D638
Strength @ 0.2% offset yieldMPa 45 .2 38 .2
psi 6560 5540
Ultimate StrengthMPa 77 .1 59.0
psi 11200 8600
Modulus (Elastic) GPa 2.62 2.39
ksi 377 347
Flexural Properties: ASTM D790, Procedure A
Ultimate StrengthMPa 98.3 80.3
psi 14300 11600
ModulusGPa 2.63 2.26
ksi 381 328
Compression Properties: ASTM D695
Strength @ 0.2% offset yieldMPa 78.9 60.1
psi 11400 8710
ModulusGPa 2.98 266
ksi 433 386
Impact Properties: ASTM D256, ASTM D4812
Izod, NotchedJ/m 73.7 69.3
ft*lb/in 1.4 1.3
Table 5. ULTEM™ 9085 Resin Natural Mechanical Properties (T16A tip)(1)
(1) For full details refer to the Stratasys ULTEM™ 9085 resin report published on the NIAR website
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logohttps://www.wichita.edu/research/NIAR/Research/ultem9085.php
ULT
EM
TM 9
085
Res
in D
ata
She
et
8
XZ Orientation(1) ZX Orientation(1)
Tensile Properties: ASTM D638
Yield StrengthMPa 68.5 (0.46) No yield
psi 9930 (67)
Elongation @ Yield % 5.8 (0.044) No yield
Strength @ BreakMPa 67.8 (0.66) 38.9 (3.7)
psi 9840 (95) 5640 (530)
Elongation @ Break % 5.7 (0.32) 2.5 (0.35)
Modulus (Elastic) GPa 2.31 (0.056) 1.98 (0.16)
ksi 335 (8.1) 287 (23)
Flexural Properties: ASTM D790, Procedure A
Strength @ BreakMPa 102 (1.0) 58.8 (8.8)
psi 14800 (150) 8530 (1300)
Strain @ Break % No break 3.25 (0.57)
ModulusGPa 2.39 (0.021) 1.93 (0.045)
ksi 346 (3.1) 280 (6.5)
Compression Properties: ASTM D695
Yield Strength MPa 86.5 (2.8) 209 (6.6)
psi 12500 (410) 30400 (960)
ModulusGPa 1.60 (0.046) 2.00 (0.072)
ksi 232 (6.7) 290 (10)
Impact Properties: ASTM D256, ASTM D4812
Izod, NotchedJ/m 124 (35) 36.6 (7.6)
ft*lb/in 2.31 (0.66) 0.685 (0.14)
Izod, UnnotchedJ/m 952 (130) 141 (35)
ft*lb/in 17.8 (2.4) 2.65 (0.66)
Table 6. ULTEM™ 9085 Resin Natural Mechanical Properties (T20 tip)
(1) Values in parentheses are standard deviations
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
9
Table 7. ULTEM™ 9085 Resin Black Mechanical Properties (T16 tip)
(1) Values in parentheses are standard deviations
XZ Orientation(1) ZX Orientation(1)
Tensile Properties: ASTM D638
Yield StrengthMPa 71.7 (1.6) No yield
psi 10,400 (240)
Elongation @ Yield % 5.5 (0.27) No yield
Strength @ BreakMPa 69.8 (1.7) 41.4 (9.0)
psi 10100 (240) 6000 (1300)
Elongation @ Break % 5.4 (0.65) 2.1 (0.58)
Modulus (Elastic) GPa 2.54 (0.050) 2.42 (0.16)
ksi 368 (7.2) 351 (23)
Flexural Properties: ASTM D790, Procedure A
Strength @ BreakMPa 107 (3.4) 72.1 (5.9)
psi 15500 (490) 10500 (860)
Strain @ Break % No break 3.78 (0.39)
ModulusGPa 2.47 (0.059) 2.11 (0.039)
ksi 358 (8.6) 305 (5.7)
Compression Properties: ASTM D695
Yield Strength MPa 142 (9.1) 349 (24)
psi 20600 (1300) 50600 (350)
ModulusGPa 2.27 (0.043) 2.37 (0.097)
ksi 329 (6.3) 343 (14)
Impact Properties: ASTM D256, ASTM D4812
Izod, NotchedJ/m 94.8 (22) 37.0 (8.3)
ft*lb/in 1.78 (0.4) 0.693 (0.16)
Izod, UnnotchedJ/m 771 (140) 169 (54)
ft*lb/in 14.4 (2.7) 3.16 (1.0)
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
10
ULTEM™ 9085 resin, natural (T20 tip and T16A tip) and black (T16 tip), printed on the Stratasys F900 and tested per 14 CFR 25.853,
BSS 7238 and 7239, and AITM 2.0007B and 3.0005. The testing done establishes that this material meets requirements for:
Table 8. ULTEM™ 9085 Resin Flame, Smoke, and Toxicity Test Results
Flame, Smoke, and Toxicity
Avg Time to Extinguish (seconds)
Avg Burned Length (inches)
Drip Time to Extinguish (seconds)
12 Second Vertical Ignition per 14 CFR 25.853(a), Appendix F, Part I, Paragraph (a)(1)(ii)
ULTEMTM 9085 Resin, Natural, T20 Tip, Build XZ 1.6 0.2 0 (no drips)
ULTEMTM 9085 Resin, Natural, T20 Tip, Build ZX 1.7 0.5 0 (no drips)
ULTEMTM 9085 Resin, Natural, T16A Tip, Build XY 2.0 0.2 0 (no drips)
ULTEMTM 9085 Resin, Natural, T16A Tip, Build XZ 1.5 0.2 0 (no drips)
ULTEMTM 9085 Resin, Natural, T16A Tip, Build ZX 2.0 0.2 0 (no drips)
ULTEMTM 9085 Resin, Black, T16 Tip, Build XZ 1.1 0.3 0 (no drips)
ULTEMTM 9085 Resin, Black, T16 Tip, Build ZX
ULT
EM
TM 9
085
Res
in D
ata
She
et
11
Test Mode Average DS (maximum) within 4 minutes, (4Dmax)
Smoke Density per BSS 7238, Rev. C
ULTEMTM 9085 Resin, Natural, T20 Tip, Build XZ Flaming 4
ULTEMTM 9085 Resin, Natural, T20 Tip, Build ZX Flaming 5
ULTEMTM 9085 Resin, Natural, T16A Tip, Build XY Flaming 4
ULTEMTM 9085 Resin, Natural, T16A Tip, Build ZX Flaming 4
ULTEMTM 9085 Resin, Black, T16 Tip, Build XZ Flaming 10
ULTEMTM 9085 Resin, Black, T16 Tip, Build ZX Flaming 15
Smoke Density per AITM 2.0007B, Issue 3
ULTEMTM 9085 Resin, Natural, T20 Tip, Build XZ Flaming 5
ULTEMTM 9085 Resin, Natural, T20 Tip, Build ZX Flaming 5
ULTEMTM 9085 Resin, Natural, T20 Tip, Build XZ Non-Flaming 0
ULTEMTM 9085 Resin, Natural, T20 Tip, Build ZX Non-Flaming 0
ULTEMTM 9085 Resin, Natural, T16A Tip, Build XY Flaming 5
ULTEMTM 9085 Resin, Natural, T16A Tip, Build ZX Flaming 6
ULTEMTM 9085 Resin, Natural, T16A Tip, Build XY Non-Flaming 0
ULTEMTM 9085 Resin, Natural, T16A Tip, Build ZX Non-Flaming 0
ULTEMTM 9085 Resin, Black, T16 Tip, Build XZ Flaming 12
ULTEMTM 9085 Resin, Black, T16 Tip, Build ZX Flaming 14
ULTEMTM 9085 Resin, Black, T16 Tip, Build XZ Non-Flaming 0
ULTEMTM 9085 Resin, Black, T16 Tip, Build ZX Non-Flaming 0
Test Mode
CO ppm
SO2 ppm
NOX ppm
HCN ppm
HCI ppm
HF ppm
Toxic Gas Emission per BSS 7239, Rev. A
ULTEMTM 9085 Resin, Natural, T20 Tip, Build XZ Flaming 50 0 (NI) 2 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T20 Tip, Build ZX Flaming 50 0 (NI) 2 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T16A Tip, Build XY Flaming 50 0 (NI) 2 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T16A Tip, Build ZX Flaming 50 0 (NI) 2 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Black, T16 Tip, Build XZ Flaming 100 0 (NI) 1 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Black, T16 Tip, Build ZX Flaming 75 0 (NI) 1 0 (NI) 0 (NI) 0 (NI)
Table 8. ULTEM™ 9085 Resin Flame, Smoke, and Toxicity Test Results
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
12
Test Mode
CO ppm
SO2 ppm
NOX ppm
HCN ppm
HCI ppm
HF ppm
Toxic Gas Emission per AITM 3.0005, Issue 2
ULTEMTM 9085 Resin, Natural, T20 Tip, Build XZ Flaming 92 0 2.8 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T20 Tip, Build ZX Flaming 102 0 4 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T20 Tip, Build XZNon-Flaming
2.6 0 0 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T20 Tip, Build ZXNon-Flaming
2.2 0 0 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T16A Tip, Build XY Flaming 61 0 2.3 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T16A Tip, Build ZX Flaming 78 0 3.2 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T16A Tip, Build XYNon-Flaming
4 0 0 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Natural, T16A Tip, Build ZXNon-Flaming
5 0 0 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Black, T16 Tip, Build XZ Flaming 93 0 1 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Black, T16 Tip, Build ZX Flaming 103 0 3 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Black, T16 Tip, Build XZNon-Flaming
2 0 0 0 (NI) 0 (NI) 0 (NI)
ULTEMTM 9085 Resin, Black, T16 Tip, Build ZXNon-Flaming
2 0 0 0 (NI) 0 (NI) 0 (NI)
Peak HRR (kW/m2)
Time to Peak Heat Release (seconds)
2 Minute Total HRR (kW-min./m2)
Heat Release Rate of Cabin Materials per 14 CFR 25.853(d), Appendix F, Part IV
ULTEMTM 9085 Resin, Natural, T20 Tip, Build XZ 54.5 73 35.5
ULTEMTM 9085 Resin, Natural, T20 Tip, Build ZX 48.2 66 41.0
ULTEMTM 9085 Resin, Natural, T16A Tip, Build XY 57.0 57 43.7
ULTEMTM 9085 Resin, Natural, T16A Tip, Build ZX 56.6 57 52.8
ULTEMTM 9085 Resin, Black, T16 Tip, Build XZ 55.4 48 32.7
ULTEMTM 9085 Resin, Black, T16 Tip, Build ZX 41.8 51 34.1
Table 8. ULTEM™ 9085 Resin Flame, Smoke, and Toxicity Test Results
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
13
ULTEM™ 9085 resin, natural and black, was printed with a T20 and T16 tip on the Stratasys F900 and tested per ASTM
E595. Full report available upon request.
Table 9. ULTEM™ 9085 Resin Outgassing Test Results
Outgassing
Sample TML (%) CVCM (%) WVR (%)
ULTEMTM 9085 Resin, Natural, T20 Tip 0.34 0.02 0.35
ULTEMTM 9085 Resin, Natural, T16A Tip 0.37 < 0.01 0.38
ULTEMTM 9085 Resin, Black, T16 Tip 0.33 < 0.01 0.22
(1) Observations apply to all tested samples
ULTEM™ 9085 resin was printed with a T16A tip on the Stratasys F900 and tested per EN-45545-2. The testing establishes
that this material meets requirements for:
• R1 HL1/2/3 at 25 mm thick in XY and XZ orientations and 5 mm in XZ orientation
• R2 HL1/2/3 at 5 mm thick in XY orientation.
Table 10. ULTEM™ 9085 Resin Fire Protection of Railway Vehicles Test Results
Fire Protection of Railway VehiclesEN-45545-2
Test Results 5mm XY 5mm XZ 25mm XY 25mm XZ
ISO 5659-2
Ds(4) - - 38 57
VOF4 - - 62 94
Dm - - 228 231
ISO 5659-2 + EN 45545-2 Appendix CITC 4 minutes - - 0.02 0.01
ITC 8 minutes 0.08 0.06
ISO 5660-1 MAHRE (kW/m2) - - 24.1 19.9
ISO 5658-2 CFE (kW/m2) 16.5 12.5 29.9 28.6
Testing Observations(1)
Visible Condensate No Opaque N/A
Percent Covered 0% Interference Fringes N/A
Thin N/A Colored Fringes N/A
Heavy N/A Sample appearance after test No change
Transparent N/A
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
14
Figure 1. 2nd heating scan DSC data for ULTEM™ 9085 resin, natural
Appendix
Figure 2. 2nd heating scan DSC data for ULTEM™ 9085 resin, black
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
15
Figure 3. Dimension change data as a function of temperature for ULTEM™ 9085 resin, natural, flat (XY)
Figure 4. Dimension change data as a function of temperature for ULTEM™ 9085 resin, natural, upright (XZ)
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
16
Figure 6. Dimension change data as a function of temperature for ULTEM™ 9085 resin, black, upright (XZ)
-50.00°C
24.55°CAlpha=47.79µm/(m·°C)
34.18°C
164.78°CAlpha=38.55µm/(m·°C) 177.45°C
-50
0
50
100
)mµ( egnah
C noisnemi
D
-50 0 50 100 150 200
Temperature (°C)
Sample: 126019, 9085BK UprightSize: 6.3796 mmMethod: In Cal, ß=5Comment: ß=5°C/min., -50 to 200°C, N2 = 150 cc/min.
TMAFile: E:\TMA Data\EH126019.002Operator: SCVRun Date: 25-Feb-2019 16:23Instrument: 2940 TMA V2.4E
Universal V4.5A TA Instruments
Figure 5. Dimension change data as a function of temperature for ULTEM™ 9085 resin, black, flat (XY)
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-stratasys-logo
ULT
EM
TM 9
085
Res
in D
ata
She
et
17
1 Holtzman St., Science Park, PO Box 2496 Rehovot 76124, Israel +972 74 745 4000+972 74 745 5000 (Fax)
© 2020 Stratasys. All rights reserved. Stratasys, the Stratasys Signet logo, FDM, and Fortus are registered trademarks of Stratasys Inc. Fortus 450mc, Fortus 900mc and F900 are trademarks of Stratasys, Inc. ULTEM™ is a registered trademark of SABIC or affiliates. All other trademarks are the property of their respective owners, and Stratasys assumes no responsibility with regard to the selection, performance, or use of these non-Stratasys products. Product specifications subject to change without notice. MDS_FDM_ULTEM9085_1020a
Stratasys Headquarters 7665 Commerce Way, Eden Prairie, MN 55344+1 800 801 6491 (US Toll Free)+1 952 937-3000 (Intl)+1 952 937-0070 (Fax)
stratasys.com ISO 9001:2015 Certified
Figure 7. Overlay of the dimension change data for all the ULTEM™ 9085 resin samples
http://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=footer-domain-linkhttp://www.stratasys.com/?utm_source=logos&utm_medium=pdf&utm_content=s-logoTop Related