Vacancy Diffusion on Ge(111)-c(2x8)
14
Vacancy Diffusion on Ge(111)-c(2x8) Maksim Skorobogatiy, John Joannopoulos MIT, Physics
description
Vacancy Diffusion on Ge(111)-c(2x8). Maksim Skorobogatiy, John Joannopoulos MIT, Physics. Ge(111)-c(2x8). Restatoms. Adadoms. Hybridization of MO. DFT++ calculations of Ge(111)-c(2x8). E cutoff = 12 Ry, k-point 6 layers of Ge + 4 adatoms + termination by H N atoms = 100 Ge + 16 H - PowerPoint PPT Presentation
Transcript of Vacancy Diffusion on Ge(111)-c(2x8)
Vacancy Diffusion on Ge(111)-c(2x8)
Maksim Skorobogatiy, John Joannopoulos
MIT, Physics
Ge(111)-c(2x8)
Restatoms
Adadoms
Hybridization of MO
DFT++ calculations of Ge(111)-c(2x8)
E cutoff = 12 Ry, k-point
6 layers of Ge + 4 adatoms+ termination by H
N atoms = 100 Ge + 16 HZ vacuum = 7.5 A
UMO of Ge(111)-c(2x8)
OMO of Ge(111)-c(2x8)
Vacancies on Ge(111)-c(2x8)
E barrier = 0.08 ev
UMO for a Vacancy on Ge(111)-c(2x8)
OMO for a Vacancy on Ge(111)-c(2x8)
Diffusion of Vacancies on Ge(111)-c(2x8)
Vacancy Diffusion Along (t L) Direction
Vacancy Diffusion Along (t R) Direction
Vacancy Diffusion Along (t) Direction
Vacancy Diffusion Along (p) Direction