Ultrabond® 365Low Temperature Cure Acrylic Adhesive

Ultrabond® 365 is a two-component, (10:1 ratio), methylmethacrylate adhesive. It is a high strength, moistureinsensitive, non-sag paste adhesive system. Ultrabond 365Acrylic Adhesive is a low temperature cure product that isformulated for anchoring threaded rods, bolts, and fastenersinto concrete, grout filled block, hollow block, andunreinforced masonry as well as anchoring rebar dowels and

smooth dowels into pavement/concrete. Ultrabond 365 hasbeen tested in accordance with AC-58 for creep, seismic,freeze-thaw, in-service temperature and damp/wet-holeapplications.

GENERAL USES• Grouting dowel bars and tie bars for full-depth concretepavement repairs

• Anchoring/Fastening into solid-base materials: Stadiumseating, Pallet racking & Airport runway/taxi-way expansion

• Anchoring/Fastening into hollow-base materialswith screen)

ADVANTAGES & FEATURES• Moisture insensitive and can be used in damp holes• Non- sag adhesive

• Exceptional strength• Extended temperature range allows for setting of anchorsin extreme environments for both elevated and lowtemperature applications

Ultrabond® 1300Epoxy Anchoring Adhesive

Ultrabond® 1300 Epoxy Anchoring Gel is a two-component(1:1 ratio), 100% solids, high modulus, structural, epoxy gel.It is a solvent free, no odor, high strength, moistureinsensitive, non-sag epoxy system.

.GENERAL USES• Fastening in grout filled block and unreinforced masonry• Anchoring and bracing for short term tensile load wheredynamic, vibratory, wind or intermittent loads exist

• Doweling applications for rebar and tie bars for full depthconcrete pavement repairs

• Bulk dispensing flowability for efficient application

ADVANTAGES & FEATURES• High strength• Moisture insensitive• Non-sag epoxy system• Easy to use (1:1 ratio) system


Ultrabond® 2 Epoxy Anchoring Gel is a two component(1:1 ratio), 100% solids, high modulus epoxy gel. It is asolvent free, high strength, moisture insensitive, non-sagepoxy system. Ultrabond® 2 Epoxy Anchoring Gel isformulated for anchoring threaded rod, bolts, rebar and

smooth dowels into concrete, grout filled block, andunreinforced masonry. Ultrabond® 2 has been tested inaccordance with AC58 and is acceptable for long term tensileloads. It may also be used for short term tensile loadanchors, which includes wind and seismic forces.

GENERAL USES• Seismic anchoring and bracing• Grouting dowel bars and tie bars for full-depth concretepavement repairs

ADVANTAGES & FEATURES• High strength epoxy system• Non-Sag formula• Easy to use (1:1 ratio) system

• Long working time• Moisture insensitive• Great for setting anchors in elevated temperatureenvironments


Ultrabond® 1 Epoxy Anchoring Gel is a two component(1:1 ratio), high modulus, structural epoxy gel. It is a solventfree, no odor, high strength, moisture insensitive, non-sagepoxy system.

GENERAL USES• Anchoring threaded rod, bolts, rebar dowels and smooth dowelsinto concrete, grout filled block and unreinforced masonry

• Seismic anchoring and bracing• Grouting dowel bars and tie bars for full-depth concretepavement repairs

ADVANTAGES & FEATURES• Exceptional strength• Long working time (20 minutes at 75°F)• Easy to use & can be used with any standard caulking gun• Load time in as little as 4 hrs

ANCHORING & DOWELING

Color When Mixed Gray

Viscosity Non-Sag gel

Gel Time 14 minutes

Load Time (75°F) 4 hours

Temperature Range 35°F – 115°F

Quick Selection Guide

Color When Mixed Concrete Gray


Gel Time (60gm @ 75°F) 15 minutes

Load Time 10 hours





Working Time (75°F) 6 min.

Load Time (75°F) 30-35 min.





Gel Time (60gm @ 75°F) 14 min.

Load Time (75°F) 2 hrs.



22 - 24See rendering of building in this brochurefor applications.

For more product details including Technical Data, Catalog, MSDS and Instructions refer to our website at www.atc.ws

Rail AnchoringRunway DowelingD.O.T. Doweling

with

Deep Embedment Anchors


Ultrabond® 2300 is a two-component, 100% solids, highstrength epoxy bonding adhesive. It is a solvent free, highmodulus, moisture insensitive, non-sag epoxy system.Ultrabond 2300 is ideal for use in temperatures ranging from

60°F - 110°F. Acceptable uses for the Ultrabond 2300include rebar dowel and anchor installations where dynamic,vibratory or intermittent loads exist. Ultrabond 2300 can alsobe used for bonding fresh/plastic concrete to hardenedconcrete and other substrates or projects that require a non-sag epoxy with a long working time.

GENERAL USES• Bonding fresh concrete to hardened concrete• Bonding hardened concrete to hardened concrete• Anchoring threaded rod fasteners and rebar dowels• Mortar Repair Material (when mixed with dry silica sand)

ADVANTAGES & FEATURES• High Strength Epoxy Adhesive• Non-Sag Epoxy System• Easy to Use (1:1 ratio)• Moisture Insensitive Epoxy

Ultrabond® SpeedSet2Doweling Adhesive

Ultrabond® SpeedSet2 Doweling Adhesive is a two-component, (10:1 ratio), polyester blend adhesive. It is asolvent free, high modulus, high strength, non-sag adhesivesystem Ultrabond® SpeedSet2 can be applied attemperatures ranging from 25° F to 120° F.

GENERAL USES• Rebar dowel installations where dynamic, vibratory orintermittent loads exist

• Vertical, horizontal and screen applications• Use in concrete, hollow block, brick, clay and stone

ADVANTAGES & FEATURES• Exceptional strength• Moisture insensitive allowing usage in dampenvironments

• Minimum loading time of 1 hour at 78° F, which is greatfor applications that require minimum down times

Ultrabond® HS200Doweling Adhesive

Ultrabond® HS200 EpoxyAnchoring Gel is a two component(2:1 ratio), 100% solids, high modulus, structural epoxy gel.It is a solvent free, no odor, high strength, moistureinsensitive, non-sag epoxy system. HS-200 has been testedin accordance with ICC - AC58 and is acceptable for longterm sustained loads as well as short term loading.

GENERAL USES• Anchoring threaded rod and rebar doweling wheredynamic, vibratory or intermittent loads exist

• Seismic anchoring and bracing for long term sustainedloads in accordance to ICC AC-58

• Grouting dowel bars and tie bars for full-depth concretepavement repairs

ADVANTAGES & FEATURES• Tested for long term creep at elevated temperatures,static loads, seismic / wind loading.• Freeze-thaw conditions, damp holes• A solvent free system means low VOC content• High Strength

Ultrabond®RT66Rebar and Doweling Adhesive

Ultrabond® RT66 is a new 2-component Hybrid Ester-Blendformula designed for doweling applications in both cold andelevated temperatures, 25°F to 120°F. It is a high strength,high modulus and moisture insensitive adhesive forinstallations in damp environments.

GENERAL USES• Perfect for horizontal, vertical and screen applications• May be used in concrete, brick, stone, clay and hollow block• Rebar dowel installations where dynamic, vibratory orintermittent loads exist

ADVANTAGES & FEATURES• High strength, non-sag structural Hybrid Ester blend system• Minimum down time with a very fast cure time• Moisture insensitive for installations in damp holes• 100% solvent free system means low VOC content

Ultrabond® 4CCRebar and Doweling Adhesive

Ultrabond® 4CC is a high performance epoxy adhesive foranchoring and doweling applications in both cracked and un-cracked concrete. It’s TESTED IN ACCORDANCE TOICC-ESAC-308 and Meets 2009 IBC requirements. Refer toICC-ES ESR-3218 Evaluation Report.

GENERAL USES• Anchoring threaded rods, bolts and fasteners into grout filledmasonry, solid brick or either cracked or uncracked concrete

• Anchoring rebar dowels and smooth dowels intopavement/concrete

• Suitable for long term sustained loads and seismic bracing• Can be used dry, water-saturated or water-filled andsubmerged applications with no load reductions

• Airport runways and taxi-way expansions, stadium seating,pallet racking

• Concrete traffic barriers to concrete bridge decks

ADVANTAGES & FEATURES• Non-sag epoxy gel anchoring• High strength• Moisture insensitive



Gel Time (75°F) 32 minutes






Gel Time (60g sample @ 75°F) 7 minutes

Load Time (75°F) 60 minutes



Color When Mixed Medium Gray


Gel Time (60g sample @ 75°F) 8 min.

Load Time (75°F) 1 hr.



Color Concrete Gray


Gel Time (60gm @ 75°F) 10 minutes


Temperature Range 35° F – 110° F


Color Gray


Working Time (70°F) 15 minutes

Cure Time 24 hours



Used for the seismic retrofit of the Golden Gate Bridge.


Miracle Bond®1350Multi-Purpose Repair Epoxy

Miracle Bond® 1350 is a two-component, high strength, highmodulus, moisture insensitive, non-sag, ceramic blend epoxysystem. It’s ideal for use as a bonding agent for almost anymaterial, including metal, concrete, brick, wood, stone, blockand other substrates.

GENERAL USES• Repairing holes and spalls in concrete• Repairing rotted wood• Bonding fresh concrete to hardened concrete• Bonding hardened concrete to hardened concrete• Capping paste sealer around ports and cracks for crackinjection process

• Non-sag patching material for cracks and small spalls• Bonds to a multitude of substrates

ADVANTAGES & FEATURES• Non-sag, high strength epoxy makes it great foroverhead and vertical repair

• Easy to use (1:1 ratio) system• 100% solvent free system means low VOC content• Moisture insensitive system-can be used ondamp surface

Color Concrete Gray

Viscosity Non-Sag Gel

Gel Time (75°F) 8 minutes

Cure Time 2 hours @ 75°F



Crackbond® JF311Polyurea Joint Filler

Crackbond® JF-311 is a 2-component, rapid curing,elastomeric, polyurea joint filler. It is designed for heavy dutytraffic and freezer applications.

GENERAL USES• Joint filler for control joints or new construction saw joints• Specifically formulated for industrial floor applicationsreceiving heavy-duty vehicle traffic.

ADVANTAGES & FEATURES• Self leveling• 100% solids• Flexible system that provides 10-15% movement ofinstalled joint width

• Can be used at temperatures between -40°F - 120°F• Rapid cure allows repaired joints to be opened to trafficwithin 90 minutes (at 72°F)

Crackbond® LR-321Low Viscosity Epoxy

Crackbond® LR-321 is formulated for use as an injectionresin for cracks in structural concrete, masonry & wood. It’salso perfect for an epoxy grout, healer/sealer or as a mortarwhen mixed with sand. It has the viscosity of light oil and lowsurface tension, allowing it to deeply penetrate fine cracks.It cures to a solid with no shrinkage, bonds to both surfacesof the crack, bonding the structure back to its originalmonolithic strength.

GENERAL USES• Pressure injection of fine to medium size cracks(3mm to ¼”)

• Primer for industrial coatings• Bonding agent for new to old concrete repair• Resin binder for epoxy mortar patching using additionof aggregate

• Sealer for interior slabs and exterior above-ground slabsfrom water, chlorides and mild chemical attack

• Gravity feed structural crack repair in horizontal concrete,masonry and wood in fine to medium size cracks

ADVANTAGES & FEATURES• High strength• Moisture insensitive system-can be used ondamp surfaces

• 100% solvent free system means zero VOC content• Low Viscosity epoxy system ideal for gravity feedcrack injection applications

BONDING & COATING


Viscosity of Resin 525cps @ 77°F

Gel Time (72°) 3 minutes

Cure Time (72°) 90 minutes

Temperature Range -40°F – 120°F


Color When Mixed Amber

Viscosity When Mixed 350 – 450cps

Gel Time (ASTM 60g mass) 20 minutes

Initial Cure Time (30 mil thin film) 6 hrs. and 30 min.


Quick Selection Guide For LR-321




Healer/Sealers, Injection Repairs, Grouting & Patching

KEY USES• Crack injection• Concrete crack and spall repair• Bonding concrete to concrete• Patching Material• Primer for industrial coatings• Healer Sealer• Epoxy Grouting• Gravity fed structural crack repair• Mortar when mixed with sand• Capping paste sealer• Fix Cracks• Rotted Wood• Loose Railing• Broken Steps• Broken Concrete

Crack-KitCrack Injection and Concrete Repair Kit

Our new and improved patented T-Port System with observationwindows is everything you need to perform crack injection andconcrete repair to multiple applications.

KEY CRACK-KIT ADVANTAGES• Latex Storage Pod delivers constant injection pressure andindicates if more injection is required

• Flexible T-Port absorbs disturbances during installation helping toeliminate reattaching ports

• Leak free direct port /nozzle connection keeps epoxy resin inwhile allowing air and water to escape

• Observation windows allows installer to view and confirm the flowof resin within the injected crack


Crackbond® LR-321GLow Viscosity Thixotropic Formula

This unique formula will flow as a liquid when being pumpedwith a dispensing tool but will cease flowing within (or out) ofthe crack when pumping stops. This characteristic makes itperfect for blind side crack repairs. Visit our website for all thecomplete technical data.

AlsoAvailable

Crackbond® SLV-302Super Low Viscosity Epoxy Resin

Crackbond® SLV-302 is formulated for use as an injectionresin for cracks in concrete/wood structures and as apenetrating healer/sealer/primer. It has the viscosity of a verylight oil, and low surface tension, allowing it to deeplypenetrate fine/hairline cracks. It cures to a solid with noshrinkage, bonds to both surfaces of the crack, bonding thestructure back to its original monolithic strength.

GENERAL USES• Pressure injection of hairline to fine cracks• Primer for industrial coatings• Gravity feed structural crack repair in horizontal concrete,masonry and wood in fine cracks

• Epoxy resin binder for epoxy mortar patching and overlayof interior surface using addition of aggregate

• Sealer for interior slabs and exterior above-ground slabs,decks, patios, driveways, parking garages and otherstructures from water, chlorides and mild chemical attack

• Shear fracture repairs on interior/exterior concrete slabs• Bonding agent for new to hardened or hardened tohardened concrete

ADVANTAGES & FEATURES• Crackbond SLV-302 is a moisture insensitive product andcan be used in damp environments

• Super low viscosity and low surface tension allows it todeeply penetrate hairline to fine cracks

• Cures to a solid with no shrinkage and bonds to allsurfaces of the crack bonding the structure back to itsoriginal monolithic strength

• 100% solids, solvent free system with zero VOC content.

Crackbond®CSRRapid Cure Polyurethane Crack/Spall Repair

Crackbond® CSR is a specially formulated very low viscositytwo-part hybrid polyurethane rapid cure concrete repairmaterial.

GENERAL USES• Repair spalls & cracks in high traffic areas• Repair floors prior to floor grinding/polishing• Rebuild spalled floor joints and concrete edges• Repair concrete on bridge & parking decks• Repair of interior and exterior hairline cracks

ADVANTAGES & FEATURES• Penetrating super low viscosity provides high bond strength• Reaches 4,900 psi in 1 hour• Use in temperatures down to 0°F• Cures in 20 minutes• Self-leveling

• Provides excellent results when polished• Add aggregate for use as mortar

Crackbond® FE-2315Flexible Pick-Proof Epoxy

Crackbond® FE-2315 is a pick-proof, two component(1:1 ratio), semi-flexible, epoxy adhesive. It is a solvent-free,no odor, moisture insensitive, non-sag epoxy adhesive.

GENERAL USES• Seals joints in facilities requiring pick-proof andtamper resistance

• Adhesive for marine applications• Hollow block joint repairs• Sealing joints in concrete to prevent water intrusion• Crack sealer/ filler• Capping gel for crack-injection

ADVANTAGES & FEATURES• Pick-proof, tamper resistance (windows, doors, etc.),Ideal for correctional facilities

• Great for bonding metal to metal

Color When Mixed Amber

Viscosity 190 cps

Gel Time (ASTM 60g mass at 75°F) 10 minutes

Initial Cure Time (30 mil thin film) 7 hours



Color When Mixed Black, then light gray

Viscosity 60cps mixed

Gel Time (75°F) 2.5 minutes

Cure Time 20 minutes



Color When Mixed Off-White


Gel Time (60g mass @ 75°F) 35 minutes

Full Cure Time (Pick-Proof) 72 hours




25See rendering of building in this brochurefor applications.


Ultrabond 2100, Crackbond LR321 LPL,Ultrabond 2100 LPLEpoxy Bonding/Coating Adhesives -Extended tack free time

PRODUCT DESCRIPTIONThe three featured products in this section are all two component, solvent free,high strength, moisture insensitive self leveling epoxies. The main differencesbetween the products can be found in their color, mixing ratios, viscosity, cureand tack free times.

GENERAL USES• Bonding fresh concrete to hardened concrete• Bonding hardened concrete to hardened concrete• Mortar repair material (when mixed with dry silica sand)• Gravity feed crack repairs• Deep hole anchoring

Ultrabond 2100 Crackbond LR321 LPL Ultrabond 2100 LPL

Viscosity Mixed (cps) 3,600 525 4,000

Gel time (60 gm sample at 75°F) min. 37 50 90

Tack Free Time 30 mil thin film 3 hrs, 40 min 8-10 hrs 5 hrs, 15 min.

Tensile Strength psi 7 days-ASTM D638 7,210 8,000 3,511

Heat Deflection Temperature °F ASTM D648 135° 121° 122°

Compressive Strength-psi 7 days ASTM D695 10,100 10,800 9,146

Bond Strength-psi 14 day ASTM C882 1,690 3,300 2,600

Mixing Ratio 1:1 2:1 1:1

Color Gray Amber Gray

ASTM C881, Type I, II, IV & V, Grade 2, Class B & C X

ASTM C881, Type I, II, IV & V, Grade 1, Class B & C X

ASTM C881, Type I, II & V, Grade 2, Class C X


The Cracker®Non-Explosive Cracking Agent

The Cracker® is a non-explosive cracking agentthat can crack any hard rock or reinforced concrete.The Cracker is a universal product which may notonly be substituted for explosives, hydraulicwedges, rock-breakers, and concrete-crackers, butcan also be used in many places where othermethods are impractical. Produced in powder form,The Cracker need only be mixed with water andpoured into predrilled holes for dramatic results.

KEY USAGE FACTSYou’ll need to know the following to determine howmuch product you’ll need. What is the size andshape of the object to be demolished? What sizepieces are you looking to create? Is there a freeedge? Will the substrate be over or under 72°F? Isthe substrate reinforced? What is the substrate psi?For complete info, watch our Cracker video on ourwebsite and download the Cracker technicalmanual.

ADVANTAGES & FEATURES• SAFE - High safety factor when compared toother methods of demolition

• QUIET - Ideal for use in or near occupied buildings• NON-TOXIC - 100% biodegradable after activated• POWERFUL - Breaks concrete from 8 inches to10 feet thick

Hard-RokAnchoring Cement

HARD-ROK Anchoring cement is a high strength, fast setting,non-shrink, nonmetallic cementitious product used foranchoring and grouting applications. This hydraulic cement isquickly and easily mixed with water to either a pourable orputty-like consistency.

GENERAL USES• Anchoring Threaded Rods, Bolts and Rebar Dowels• Anchoring Railing, Signs, Posts and Parking Meters• Anchoring Machinery• Patching Holes and Cracks in Concrete

ADVANTAGES & FEATURES• High Strength• Fast cure anchoring cement: fast initial set of 15 minutes at75°F when mixed to fluid consistency

• Ideal for interior and exterior applications• Contains no metals to rust and cause unsightly stains• Compressive strength of 7,200 psi in 28 days insures a firmbed in grouting applications

• Mixed to a free flowing consistency: Flows like pancakebatter eliminating the labor required in Roding or vibratingto eliminate voids.

Hard-RokJet Patch

JET PATCH is a Portland Cement blend of specialtyaggregates and admixtures providing a rapid setting, highstrength, durable concrete repair for use on airport runways,taxiways, concrete floors, highway pavements, bridge decksand other applications requiring early resumption of traffic oruse. Jet Patch is formulated to meet the requirements ofASTM C928 Packaged, Dry, Rapid Hardening CementitiousMaterial for Concrete Repair.

GENERAL USES• Excellent for all types of concrete repair applications: bridgedecks, concrete pavements and joints, airport runways andtaxiways, industrial floors, loading docks, pre-stressed andprecast concrete

• Specifically designed for those applications requiring veryrapid strength gain

ADVANTAGES & FEATURES• For deeper spalls ( >3”) add pea gravel. See InstallationInstructions for details

• Thermal expansion & contraction similar to concrete,Freeze-thaw resistant

• For repairing depths between 1/2” to 3” use as packaged,mixed with water

• Flowable and Self Compacting• Sulfate resistant• High early strength with low permeability

SPECIALTY PRODUCTS

See rendering of building in thisbrochure for applications.

33

Hard-Rok Jet Patch used for runway repair.

This brochure is intended to be used as a quick reference guide only. Information is subject to change without notice.For more product details including Technical Data, Catalog, MSDS and Instructions refer to our website at www.atc.ws

Ultrabond® EGPHigh StrengthGrouting System

Ultrabond® EGP is a threecomponent, 100% solids, highperformance, high strength epoxygrouting system. It is a solvent-free,low-odor, moisture insensitive, pre-

packaged epoxy grout system. EGP is ideal for precisionseating of baseplates, and grouting under heavy-dutyequipment. It is ideal as an epoxy grout for concrete patchingand overlays. EGP can be mixed to three differentconsistencies:1) Trowelable2) Plastic /Flowable3) Pourable /Self-Leveling

GENERAL USES• High strength grouting – vibratory, high impact, heavyload conditions

• Patch and Spall repair• Patching / repairing warehouse, office and garage floors• Machine Base Grouting (heavy impact and vibratorymachinery, reciprocating engines, compressors and pumps)

• Grouting under crane rails

ADVANTAGES & FEATURES• Fast strength gain• Low exotherm• Oil and Chemical Resistant• Pre-proportioned kit• High strength epoxy grout• High effective bearing area• Corrosion and impact resistant

• High vibration resistance• Non-shrink• Moisture insensitive• Variable ratio fill system: ratio of special blend aggregateto total liquids

Color When Mixed Tan

Viscosity Thick Grout

Gel Time (60g mass @ 77°F) 35 – 60 minutes

Cure Time 24 hrs.



High Strength Grout, Cementitious Products, Concrete Demolition

© Copyright 2013, Adhesives Technology Corp. 0113

Ultrabond - ThomasNetcdn.thomasnet.com/ccp/10057515/172806.pdf · Ultrabond ®1300 Epoxy Anchoring...

Documents

Transcript of Ultrabond - ThomasNetcdn.thomasnet.com/ccp/10057515/172806.pdf · Ultrabond ®1300 Epoxy Anchoring...