Slide 1

Specifying and Selecting Coatings Presented by: Troy Fraebel, Sherwin Williams

Slide 2

Introduction This webinar will provide guidance on how to properly specify and select a coating system for a specific substrate (carbon steel, other metals, concrete, previously coated), structure, and environment.

Slide 3

Painting Project Specification A statement of particulars, describing the dimensions, details, or peculiarities of any work to be undertaken.. Legal document. Part of a contract. Provides the (technical) rules. Practical document. Requires thorough planning. What, where, when, but NOT so much on how!

Slide 4

Painting Project Specification Contents Scope of work. Areas to be coated and not coated. Site specific requirements. Paint materials and suppliers. Surface preparation, application, and inspection requirements using standard methods.

Slide 5

Specification Writing Goals Clear. Complete. Concise. Consistent. Correct.

Slide 6

Specification Writing Techniques Use short sentences. One requirement per sentence. Place action words at the beginning. Use strong verbs. Never repeat descriptions or requirements. Define words that may be misunderstood. Use the same writing style throughout.

Slide 7

Important Word Meanings Shall. Essential requirement. Should. Preference or strong recommendation. May. Used when alternatives are acceptable.

Slide 8

Coating Specification Formats Construction Specification Institute (CSI) SSPC modified CSI format Major Sections General Products Execution

Slide 9

Coating System Selection Coating mechanisms and types Type of substrate (steel, concrete, etc.) Prevailing service environment (immersion?) Level of surface preparation possible Access to the work Owners desires and expectations: Intended service life of structure Desired service life of coating Worker skills and equipment availability Aesthetics (gloss & color retention) Timing Economics

Slide 10

Making Steel Corrode Anode Cathode Metallic Pathway Electrolyte

Slide 11

How Coatings Protect Surfaces Barrier Inhibitive Sacrificial Corrosion Prevention Stop the deterioration of a substrate. Corrosion is a natural process that displays the tendency of materials to give up energy and return to its natural state.

Slide 12

Zinc-Rich Primers Contain High Percentage of Zinc Dust in the Dried Film So That There Is Direct Contact Between Zinc Particles and Steel Sacrificial / Galvanic Protection (like galvanizing) Corrosion Protection Prevention of Undercutting

Slide 13

Solvent Based Epoxies Excellent Alkali, Solvent, and Water Resistance Good Abrasion Resistance Good Acid Resistance Good Exterior Durability but... Low Temperature Application Available Typical Dry Heat Resistance to 250 F

Slide 14

Solvent Based Alkyds Application as low as 40F Single Package / Ease of Application Heat Resistance to 200-250 F Embrittle With Age Prone to Yellow / Saponify Require modification for exterior topcoats

Slide 15

Waterborne Acrylics Single Component Water Based Fast dry and fast re-coat Good color and gloss retention Primers must contain inhibitors Low stress

Slide 16

Polyurethanes / Polyureas / Polyaspartics Aliphatic Excellent Color Retention Excellent Gloss Retention Primarily Used as Finish Coats More Expensive than Aromatics Aromatic Yellows & Chalks in Sunlight Yellows & Chalks in Bright Artificial Light Used as Primers & Intermediate Coat Less Expensive than Aliphatics

Slide 17

Moisture Cured Urethanes Can be surface tolerant Can be applied during high humidity Easy to application Fast cure / fast recoat Low temperature application to 20 F. Single component Reinforce with micaceous iron oxide Aliphatic topcoats

Slide 18

Types of Substrates Coated

Slide 19

Types of Steel Cold-rolled Hot-rolled Stainless steel

Slide 20

Cold-Rolled Steel Typically steel coils; typically thin sheet steel. Produces a denser, smoother surface than hot-rolling. Phosphating may be used to promote coating adhesion; otherwise coatings may not bond well.

Slide 21

Hot-Rolled Steel Typical of structural steel used in construction. Manufacturing process creates a bonded layer of iron oxide called mill scale. Smooth Cathodic Differential expansion

Slide 22

Slide 23

Stainless Steel Better mechanical properties and greater resistance to corrosion than mild steel. Numerous grades of stainless steel (add chromium and... ) Harder than mild steel Prone to stress corrosion cracking (SCC)

Slide 24

Hot Dip Galvanized Surfaces Application of a zinc coating to steel by dipping it in molten zinc or by depositing zinc on the steel through electrolytic means. Post-treated with oil or a chromate conversion coating to protect from white rust, a wet-storage stain. Post-treatments must be removed before coating. Alkaline substrate. Oil-based alkyds may saponify.

Slide 25

Aluminum May require chemical treatment, wash priming, and/or brush off blasting with a soft abrasive. SSPC-SP 16

Slide 26

Ductile Iron Use Standard NAPF 500-03 Applying steel surface preparation specifications to ductile iron is inappropriate, and may actually result in damage to the pipe surface with subsequent reduced coating effectiveness and life expectancy.

Slide 27

Concrete A composite material comprised of a Portland cement and water mixture that serves as a binder for embedded particles of coarse and fine aggregate.

Slide 28

Concrete Characteristics Alkalinity (pH range of 9 to 12) Porosity Moisture Movement of concrete (i.e., cracking)

Slide 29

Concrete Types and Finishes Concrete (tilt-up, cast-in-place, block) Finish (broom, steel trowel, sacked, stoned, wood floated) Curing compounds / Sealers (paintable?)

Slide 30

Other Substrates Wood or plywood Polyvinyl Chloride (PVC) Fiberglass Reinforced Plastic (FRP)

Slide 31

Demands of Environments on Coating Systems

Slide 32

Questions to Ask Is the coating being applied to an interior or exterior space? What is the atmospheric service environment? Will the coating be exposed to abrasion and impact? What is the surface temperature once in service? Will there be a cleaning or cyclic exposure?

Slide 33

Questions to Ask Will the coating be immersed in chemicals? Type Concentration pH Temperature Primary or secondary containment What are the application conditions? Is the coating being applied in a climate- controlled shop environment or in the field? What is the surface temperature during application?

Slide 34

Interior Service Environment Coatings Coatings need not withstand sunny conditions. Maybe climate controlled.

Slide 35

Exterior Service Environment Coatings Designed to withstand sun, rain, and snow. Remain flexible after curing; wont crack or peel as it expands and contracts with changes in temperature and humidity. Additives enhance mildew-, fungus-, and UV-resistance.

Slide 36

Service Locations What are some different service locations? How might location affect the type of coating you would select? What factors should be considered?

Slide 37

Inland, Rural Free from the corrosive influence of airborne salt; polluted air and rain may still be present.

Slide 38

Heavy Industrial High corrosion rates High atmospheric chemical concentration (i.e., sulphur dioxide, nitrous oxide)

Slide 39

Marine High concentration of salt mist (chlorides). Not always in direct contact with salt spray or splashing waves. Often in conjunction with heavy industrial environments.

Slide 40

Immersion Better surface preparation. More impermeable. Typically not UV stable. Must resist constant exposure to the cargo.

Slide 41

Alternating Immersion Any area in which immersion in water is combined with period of exposure to the atmosphere just above it. Steel in a tidal range. High waterline in a tank.

Slide 42

Condensing Humidity Service Example: Headspace in a tank Indoor pool with condensation on ceiling Cold pipes

Slide 43

Chemical Environments Strong concentrations of highly corrosive gases, fumes, and chemicals that come in direct contact with the coated surface. Mild to severe; direct immersion or splash.

Slide 44

Underground Buried surfaces in direct contact with soil. Possibly highly acidic. Compatible with cathodic protection.

Slide 45

Abrasion and Impact Coatings exposed to particle objects that rub, scrape, impact, or erode the surface by friction (i.e., pipeline, dam gate).

Slide 46

Final Service Temperature Certain coatings are prone to limited chemical resistance and early failure when exposed to high in-service temperatures.

Slide 47

Other Factors to Consider What else might impact your choice of coating selection beyond the service environment?

Slide 48

Application Temperature Apply coating system only when the air and substrate temperature are within the range indicated by the manufacturers written instructions on the product data sheet (PDS).

Slide 49

Coatings and Moisture Not applied to wet or damp surfaces unless formulated by the manufacturer for this type of application. Not applied on frosted or ice-coated surfaces. Typically not applied when surface temperature is less than 5 o F (3 o C) above the dew point.

Slide 50

Previously Coated Substrates Generic Type Assessment of Current Paint Percentage (%) of corrosion Adhesion to substrate and other coats Thickness (DFT) Number of coats Chalking, blistering, etc. Test Patch!

Slide 51

Adhesion Test adhesion of existing coating to itself and to the substrate. Low adhesion values can indicate possible delamination during overcoating.

Slide 52

Multiple Coating Layers High internal stress possible. Can cause delamination and reduce intercoat adhesion when overcoated. Delaminated and cracked coatings are not good candidates for overcoating.

Slide 53

Chalking and Erosion Typical of aging epoxy and alkyd coatings.

Slide 54

Coating Compatabilty Small field patch tests. Apply proposed repair system to small deteriorated areas using same surface treatment planned for repairs. Visual defects and adhesion testing can detect incompatibilities.

Slide 55

Coating Compatabilty Patch tests are described in ASTM D5064 Standard Practice for Conducting a Patch Test to Assess Coating Compatibility and SSPC-Guide 9 Guide for Atmospheric Testing of Coatings in the Field.

Slide 56

Coating System/Structure Life Expectancy Expected service life of structure and coating or overcoat system. Economics of overcoating versus remaining years of service life.

Slide 57

Site-Specific Concerns Noise and emission considerations. Permissible surface preparation and application methods that meet all requirements and are suitable for the coating product selected. Return to service time.

Slide 58

Budget and Time Constraints Some examples: An aliphatic polyurea cures faster than an acrylic, a good selection when turnaround time is short and resistance to sunlight is desirable. An epoxy is less expensive than a polyurethane and works just as well in interior environments.

Slide 59

Summary A coating system is applied to a structure to prevent corrosion and perhaps impart color and gloss. Each layer (primer, intermediate coat, and/or topcoat) provides a specific protective function. There are a variety of substrates that are protected using coatings and coating systems. The various substrates have inherent characteristics that impact the degree of surface preparation and coating system selection. A review of coating types available, substrates, service environment, the condition of the existing coating system if any, and budget and time constraints are the means by which the proper coating system can be selected to provide the maximum corrosion protection.

Slide 60

???????ANY QUESTIONS ????????