Processing

2

JointingDrilling holes for jointing see page 8

• with drill bits for aluminium sheet and plastic panels (for larger holes use a drill bit with locating point)

Riveting see page 16

• with normal tools and rivets or blind rivets

Screwing see page 17

• with normal stainless steel screws or boltsfor wood, sheet or metal

Welding see page 18

• the PE core material with hot-air weldingdevices and PE welding rod

Glueing see page 19

Outdoor use• adhesive sealing compound

Indoor use• metal adhesives for aluminium• double-sided adhesive tape

Clamp connections see page 19

• with toothed butt joint and corner sectionsfor 3, 4 and 6 mm

Surface treatment

Lacquering see page 21• overlacquering of ALUCOBOND®

surfaces possible with suitable lacquer qualities

Note:For processing ALUCOBOND® A2 and ALUCOBOND® PLUS please refer toseparate leaflet.

Processing at aglance

Cutting to shapeSawing see page 7

• with vertical panel saw, circular or jig saw

Cutting see page 8

• with guillotine shears (slight drawing of the panel cover sheet), cushion clamp

Punching / Decorative workPunching see page 8

• with conventional sheet punching machines.For clean cuts please use evenly groundtools. Drawing of the panel cover sheet

Contour cutting see page 8

• with water torches, CNC machining centresand jig saws

ShapingBending see page 9

• with folding machine or bending press, min. inner radius r = 10 x t ALUCOBOND® and

ALUCOBOND® PLUSr = 25 x t ALUCOBOND® A2(t = panel thickness)return travel greater than with solid sheet

Roll bending see page 9

• with roll bending machines. Make sure to use ground rolls.

Folding (routing technique)see page 11

• manually after routing a V-groove using a panel saw with routing device, a CNCmachining centre or a panel routingmachine

Page

Transport / Storage / Handling 4 /5

Cutting and Fabricating 6 - 9

Routing and Folding Technique 10 - 13

Jointing / Fixing Technique 14 - 19

Surface Treatment 20 /21

Cleaning and Maintenance 22 /23

Technical Data sheets 24-26

ALUCOBOND® Information 27

Contents

4

Transport

HandlingStorage

5

ALUCOBOND® is a prefabricated panellingmaterial, i.e. the surface of the standard panelis either lacquered, anodised or mill-finished.These surfaces are protected by a special foilduring transport, storage and processing.Nevertheless, the following information mustbe observed when storing and handling thepanels:

• The pallets must be handled carefullyduring transport and unloading.

• Upon delivery the pallets must be examinedfor any damage due to moisture (ALUCOBOND®

panels that have become wet must be dried toavoid any spots or corrosion forming). Anydamage must be reported immediately andconfirmed by the forwarding agent.

• Store the pallets so that they are protectedagainst any wetness penetrating due to rainand spray water and avoid any condensationforming (e.g. when transporting cold panels towarmer rooms).

• Store the pallets stacked one over the other(do not store ALUCOBOND® panels standingvertically), with a maximum of 6 pallets of thesame format stacked on top of each other(heavy pallets at the bottom).

• Individual panels must be lifted off the pal-let by two people holding all four corners andnot drawn over each other. Carry the panelsvertically. Wear gloves to avoid making anymarks on them.

The following should be observed asregards the ALUCOBOND® protective foil:

• Storage exceeding 6 months should beavoided.

• Strong fluctuations in temperature reducethe long-term durability.

• Should the protective foil partially come offduring processing, dirtied edges can occur inthe course of time.

6

7

Jig saw bladesfor wood or plastics, e.g. T101 B (Bosch), tooth thickness 2.5 mm for precision cuts

Saw blades for ALUCOBOND® A2 and ALUCOBOND® PLUSfor max. number of revs 2,500 RpmTooth geometry see aboveSaw blade dia. D = 300 mm(for Striebig Saw Standard II)Number of teeth t = 72Speiser Code No. 804030333Saw blade dia. D = 250 mm(for Holz-Her Saw 1255)Number of teeth t = 60Speiser Code No. 02040151

Manufacturer / supplierand Sharpening serviceSpeiser Werkzeugtechnik Salzstetter Straße 29D-72221 HaiterbachPhone +49 74 56 94 49 0Fax +49 74 56 94 49 11

For further information on machines and toolsplease refer to the separate leaflet on ‘Processingof ALUCOBOND® A2 and ALUCOBOND® PLUS’.

Carbide tipped (CT) saw blades

Blade geometry Tooth thickness approx. 2 – 4 mm, tapered to the inside to prevent jamming

Tooth geometry trapezoid tooth / flat thooth

Pitch t 10 – 12 mmClearance angle a 15 °Rake angle g 10 ° positive

Maximum cutting speed v 5,000 m/min

Maximum feed s 30 m/min

Carbide tipped (CT) saw blades for HOLZ-HER and Striebig circular panel saws

Trapezoid/flat tooth saw blade, flat teeth 45° chamfered for burr-free edges

Saw blade dia. D = 300 mm (for Striebig vertical panel saw Standard II)

Number of teeth t = 72 (for cuts of up to 5 panels)LEUCO Code No. 188389t = 96 (for single cuts without burrs)LEUCO Code No. 188390

Saw blade dia. D = 250 mm (for Holz-Her vertical panel saw 1255 ALUCOBOND®)

Number of teeth t = 60 (for cuts up to 5 panels) LEUCO- Code No. 188939t = 80 (for cuts without burrs) LEUCO- Code No. 188940

Bore dia. D = 30 mmTooth thickness 3.2 mmClearance angle 15 °Rake angle 10 ° positive

Manufacturer / supplier: LeucoLedermann GmbHPostfach 1340D-72153 HorbPhone +49 74 51 93 0Fax +49 74 51 93 500www.leuco.com

Sawing

Sketch showing the edge geometry for professional resharpening:

Cutting andFabricating

8

RoutingALUCOBOND® can be easily routed on conven-tional routing machines and CNC machiningcentres. To avoid pressure marks on the ALUCOBOND®

surface, please use plastic or wood vice jawswhen chucking the workpieces. High-speed steel or carbide tipped cutterssuitable for aluminium and ALUCOBOND®

have a wide tooth pitch, radiused and smoothgrooves and small lip angles.They produce perfect cuts, e.g. under thefollowing conditions:

• High-speed steel max. cutting speed max. 3,000 m/min.feed max. 25 m/min.

• Carbide tipped cutter max. cutting speed max. 5,000 m/min. feed max. 30 m/min.

Suitable end milling cutters for ALUCOBOND®:

HSS end milling cutter, shank dia. 8 mm

Dim. 5 x 12 x 60 mmArt. No. 100 56 0008

Dim. 3 x 12 x 60 mmArt. No. 100 36 0008

Manufacturer / supplier:Werner Albrecht KGBe We PräzisionswerkzeugeIm Öhrlach 11bD-75417 MühlackerPhone +49 70 41 41 940 310Fax +49 70 41 41 414 31

Carbide end milling cutter series F 113

Manufacturer / supplier: Gienger IndustrieserviceWeimarstraße 15D-78532 TuttlingenPhone +49 74 61 16 20 20Fax +49 74 61 16 20 21www.gis-tec.de

DrillingALUCOBOND® can be drilled with twist drillsnormally used for aluminium and plastics onmachines common for metals.Drill material: High-speed steel (HSS)Tool geometry: Lip angle: 100 ° – 140 °Drilling without burr is possible using the fol-lowing drills:spot facing cutter with centre-point.Angle of whist: 30 ° – 45 °e.g. Extreme 2TM HSS-G Metal drill DIN 338 ofDe WALT, D-Idstein

CountersinkThree-lipped core drills and counterborescommon for aluminium are used for counter-sinking pre-drilled holes. Counterbored holesare less out of centre than those produced bytwist drills. Countersinks for aluminium can beused for countersinking flat head screws intoALUCOBOND®. Head and shank counterboresfor aluminium are mainly used for countersink-ing screw heads or for making holes throughALUCOBOND®.

Contour cuttingALUCOBOND® can be cut to size with jigsaws, CNC machining centres and watertorches. Please cut abrasively when using awater torch. Pre-drilling of the panels is nec-essary when starting the cut in the middle ofa panel as it is not possible to drill throughwith a water torch.

ShearingALUCOBOND® is easily sheared with a guillo-tine. A slight drawing of the aluminium coversheet caused at the impact side should benoted. The clamp on the shear should be fittedwith a shock-absorbing rubber pad to preventdamage to the cover sheet.

PunchingALUCOBOND® panels of any thickness can bepunched with conventional sheet punchingmachines. For clean cuts please use evenlyground tools and the narrowest possible cut-ting gap (0.1 mm). This punching method alsocauses a slight drawing of the panel coversheet. Holes of a minimum diameter of 4 mmcan be punched. The minimum width of webbetween hole edges is also 4 mm.

BendingALUCOBOND® can be formed by conventionalmetal and plastic fabrication methods. Certainspecific points should be noted relating to themultilayer structure combining materials ofdifferent characteristics:

• The minimum radius isfor ALUCOBOND® and ALUCOBOND® PLUS r = 10 x tfor ALUCOBOND® A2 r = 25 x tt = panel thickness

The spring-back effect experienced when fold-ing sheet metal is larger with ALUCOBOND®.For production series a prototype should bemade.The surface should be protected from damageby affixing plastic film or inserting polyethyleneof 1 – 2 mm thickness or plastic film stripsduring processing.The panel surface must be free from anyadhesive material (e.g. labels, etc.).Important:When bending ALUCOBOND® with ananodized surface, the bent area is brighter.

Bending with a brake press(Fig. 1) ALUCOBOND®, like sheet metal, is easilyformed with a brake press. The air-bendingprocess is used when forming with a brakepress. The ALUCOBOND® panel rests on the edges ofthe die (rails, channels) and is bent by thepunch (tube or shaft). The bending angle isdetermined by the width of the die and thestroke of the punch. The die edges should berounded and smooth.Ideal die width:2 x t + 2 x protective foil thickness + punch diameter + 15 mmThe minimum side length of the bent partshould be 5 times the ALUCOBOND® thickness.

Bending with a folding machine(Fig. 2) When working with folding machines, thepanel to be bent is clamped between twocheeks. The projecting edge is bent aroundthe upper clamping cheek and former usingthe movable swivel bar. The bending radius isdetermined by interchangeable formersattached to the upper clamping cheek.

Bending with a roll bending machine

ALUCOBOND® can be bent with sheet metalroll bending machines – mainly with three andfour-roll machines. Please make sure that thefeeder does not exert too much pressure.Bending rolls which are also used for bendingother metals must be thoroughly cleaned fromswarf before processing ALUCOBOND®. Werecommend ground rolls to avoid damagingthe cover sheets.

9

Note:For processing ALUCOBOND® A2 and ALUCOBOND® PLUS please refer to the separate leaflet.

Fig.1 Bending with a brake press

Fig.2 Bending with folding machine

l min. = 5xdr min.:

ALUCOBOND® and ALUCOBOND® PLUS = 10xtALUCOBOND® A2 = 25xt

Protective foil

Die widthDie

Upper clamping cheek

Swivel barFormer

Lower clamping cheek

Protective foil

10

11

Routing and Folding Technique

and Designfor individual Shaping

AdvantagesThe convincing advantages of the routing andfolding techniques are:• Minimum investment• Simple operating technique• Folding need not be done in the workshop,

it can be done on site; this means lowtransport and storage costs

• Low-cost manufacture of shaped parts likefascia claddings, roof edgings, corner pieces,column casings and many more are possible

• Versatile formability• Good economy• Shapes are not restricted by machine

dimensions• Folding without cutting, therefore no

buckling in the corner area and thus evenelements

Rectangular groove for edges up to 150° depending on panel thickness

Groove 135° (V-shaped) for edges up to 135°

MethodALUCOBOND® composite panels can beshaped by means of a simple processing tech-nique. This procedure, the routing and foldingtechnique, enables a variety of shapes andsizes to be manufactured.V-shaped or rectangular grooves are routed onthe rear of the panels with disk or end millingcutters, whereby the aluminium cover sheet atthe front and part of the polyethylene core areretained. The small thickness of the remainingmaterial then allows folding by hand. A brakepress is not required. The groove shape deter-mines the radius of the bend.The grooves can be produced with a panel sawwith routing device for ALUCOBOND®, on aCNC machining centre, with a panel routingmachine or a hand routing machine. The rout-ing and folding technique can be used forcomposite panels of all standard surfaces.Important:When folding ALUCOBOND® with an anodizedsurface, the edges are brighter.

Tracing roller for exact groove-depth-adjustment

Disc milling cutter

not suitable for ALUCOBOND® A2

Groove (V-shaped) for edges up to 90°

ALUCOBOND®

12

Tools and machinery for routing and folding technique

For special machines and dust extractor systems please refer to the separate leaflet “Processing ALUCOBOND® A2 and ALUCOBOND® PLUS”.

1

2

Panel saws ALUCOBOND® routing device(special accessory)

Holz-Her vertical panel saw PK 1255 ALUCOBOND®

Code No. 278.6133Striebig Vertical panel saw Standard II for composite panels

Manufacturers / suppliers:Reich Spezialmaschinen GmbH Plochinger Straße 65 D-72622 Nürtingen Phone +49 70 22 7 02 – 0www.holzher.deStriebig AG Maschinenbau Großmatte 26a CH-6014 Littau Phone +41 41 25 9 53 53www.striebig.comOther panel saws can subsequently be providedby the manufacturer with an additional routingdevice. Please ask for details.

CNC machine centres

Manufacturers / suppliers:On request.

Panel routing machinePF 1200 E-Plus ALUCOBOND®

(Fig. 1)Supplied with:• Tracing roller for 4 mm• Cutter disk for V-grooves 90°• Adjustment template• Transport box

Supplier:TTS Tooltechnic Systems Deutschland GmbHMarketing sales: FESTOOLWertstrasse 20D-73240 Wendlingen Phone +49 7024 804 640Fax +49 7024 804 724ebg@tts-festool.comwww.festool.com

Hand routing machines (Fig. 2)Commercially available hand routing machineswith a minimum rating of 800 W are suitable. Collet chucks 8 mm dia.

13

Carbide tipped disk milling cutters fo vertical panel saws

Suppliers for profile cutters(not available ex stock)KWO-Werkzeuge GmbH Postfach 1363 D-73444 Oberkochen Phone +49 73 64 951 - 8Fax +49 73 64 951 - 749www.kwo.de

MAWEX GmbHMaschinen und Werkzeuge Postfach 1314D-75417 MühlackerPhone +49 70 41 95 82 - 0Fax +49 70 41 95 82 - 11www.mawex.de

The diameters of tracing rollers and cutterdiscs are adjusted so as to leave a residualcore thickness of 0.3 mm (V-groove) or 1 mm(rectangular groove). The dimensions given inthe drawings show the cover panel thicknessof 0.5 mm plus the corresponding residual corethickness.

Carbide tipped cutter No. 79 803 (KWO)HSS cutter No. 201 00 83 08 (MAWEX)

Please address all enquiries relating to• new machines with accessory parts for

milling of ALUCOBOND®

• possible retrofitting of existing machines(stating machine type/No. and year ofconstruction)

• accessories such as cutter disks, tracingrollers, etc.

directly to the manufacturer of the panel saws.

Disk milling cutter for V-grooves 90 ° Disk milling cutter for V-grooves 135 °

End milling cutter for V-grooves 90 ° End milling cutter for V-grooves 135 ° End milling cutter for rectangular grooves

Carbide tipped cutter No. 79 804 (KWO) HSS cutter ø 10 mm No.79800(KWO)HSS cutter ø 15 mm No.79801(KWO)

Important:Please state the following in your enquiry ororder “for processing ALUCOBOND® compositepanels”.

Milling cutters with cylindrical shank for hand routing machines

Disk milling cutter for rectangular grooves

up to4 mm

up to 4 mm

14

15

Jointing /

TechniqueFixing

ALUCOBOND® can be joined by means ofstandard processes used in metal and plasticstechnology. If ALUCOBOND® is to be joined to structuralparts of metals other than aluminium, or iffasteners (e.g. bolts, screws) are to be used,the following material guidelines should beobserved:Fasteners and structural parts made of alu-minium, plastic or stainless steel should besuitable for the assembly with ALUCOBOND®.When using other materials please insertinsulating washers etc. or apply protectivecoating to prevent corrosion.

Please take the thermal expansion of the panelinto account for outdoor use of ALUCOBOND®

to avoid jamming or deformation.The minimum gap depends on the expectedexpansion of the panel.Please refer to processing recommendationsfor rivets and bolts for additional measures toprevent jamming.The linear thermal expansion of ALUCOBOND®

is determined by the aluminium cover sheets. At a temperature difference of 100°C thethermal expansion is 2.4 mm/m.

16

ALUCOBOND® panels can be fastened togetheror joined to other materials with rivets commonto aluminium constructions.For outdoor use and for use in areas of highhumidity, aluminium blind rivets with stainlesssteel mandrils should be used to prevent uglycorrosive edges. When using aluminium blindrivets with steel mandrils, the mandril shoulddrop out after riveting (detachable version).Countersunk rivets are suitable for indoor useonly.

For outdoor use please note:• For outdoor use aluminium blind rivets thathave been approved for construction with a 5 mm shaft diameter and an attachment headdiameter of 11 or 14 mm are used.• Please take the thermal expansion of thepanel into account (2.4 mm/m/100°C). Toavoid jamming, the hole in the panel must belarge enough to allow for expansion.• With the shaft of the rivet fitting closely tothe edge of the hole, the attachment headmust cover over 1 mm of the area surroundingthe hole.• Multi-step drills or sleeves having corre-sponding diameters are used for centricallydrilling holes into the panel and the substruc-ture and for centrically fitting the rivet.• Rivet attachment jigs are used for fittingblind rivets without jamming allowing for atolerance of 0.3 mm. Make sure to use rivetattachment jigs and rivets from the samemanufacturer, as the height of the attachmenthead according to DIN 7337 may vary.• The clamping thickness results from thethickness of the material to be riveted plus anadditional value of 2 mm to ensure that theclosing head is perfectly formed. In accor-dance with this clamping thickness the corre-sponding shaft length is determined in thetables provided by the rivet manufacturers.(lmin. = 14 mm)

Important:Since during riveting many factors may havean influence on the exact tolerance of therivets of 0.3 mm (e.g. rivet head tolerance), werecommend that you make a test on a façadepanel. Please always remove the protective foil in theriveting area prior to riveting.

Manufacturers / suppliers:

Blind rivetsIn the trade or from

GESIPA-Blindniettechnik GmbH Nordendstr. 13-39 D-64546 Mörfelden-Walldorf Phone +49 61 05 962 0Fax +49 61 05 962 287www.gesipa.com

Gebr. Titgemeyer GmbH & Co. KG Postfach 4309 D-49033 Osnabrück Phone +49 541 58 22 – 0 Fax +49 541 58 22 – 490www.titgemeyer.de

VVG-Befestigungstechnik GmbH & Co. Haber Straße 29D-24537 NeumünsterPhone +49 43 21 96 71 71Fax +49 43 21 96 71 96www.vvg-befestigungstechnik.de

Blind rivets lacqueredMBE GmbH Postfach 2525 D-58685 Menden Phone +49 23 73 17 430 – 0Fax +49 23 73 17 430 – 11www.mbe-gmbh.com

SFS intec GmbH & Co. KG In den Schwarzwiesen 2 D-61440 OberurselPhone +49 61 71 70 02 0Fax +49 61 71 70 02 46www.sfsintec.biz

Multi-step drills (not available ex stock) KWO Werkzeuge GmbHPostfach 1363D-73444 Oberkochen Phone +49 73 64 95 18 Fax +49 73 64 95 749www.kwo.de

Hole gaugesPlease refer to blind rivets lacquered: MBE GmbH

Rivet attachement jigsAppropriate rivet attachment jigs are availablefrom the manufacturers or suppliers of rivets.

Riveting

Blind rivet Distancemin. 15 mm

Pop blind rivet(Gebr. Titgemeyer)

Countersunk rivet(for indoor use only)

Stainless steelmandril

Steel mandril Stainless steelmandril

Detachable headversion

Rivet attachment jig

Distancemin. 15 mm

Aluminium substructure

Aluminium blind rivet dia. 5 mmwith stainless steel mandril

Attachement head dia. 11 or 14 mm

Rivet attachment jig for screwingto the riveting device

(for fixing ALUCOBOND® panelswithout jamming)

dia. 7.0 mm – Rivet K11dia. 8.5 mm – Rivet K14

Multi-step drill withadjustable stop

Countersink screw head with cover sheet depressed

Tallow-drop screws with tapered washer

Fascia screw thread-cutting Fascia screw self-tapping

17

Manufacturers /Suppliers:Fascia screwsEJOT Baubefestigungen GmbH Postfach 11 35 D-57323 Bad Laasphe Phone +49 27 52 9 08 – 0Fax +49 27 52 9 08 – 731www.ejot.de

Fascia screws, lacqueredMBE GmbH Postfach 2525 D-58685 Menden Phone +49 23 73 17 430 – 0Fax +49 23 73 17 430 – 11www.mbe-gmbh.com

SFS intec GmbH & Co. KG In den Schwarzwiesen 2 D-61440 OberurselPhone +49 61 71 70 02 0Fax +49 61 71 70 02 46www.sfsintec.biz

Threaded fasteners

1

22

22

Sheet metal / wood screws Countersunk bore

Plastic covers for fascia screwsKU-FA Befestigungs GmbH Obere Espen 2D-57334 Bad Laasphe Phone +49 27 54 37450 Fax +49 27 54 81 19

Multi-step drills (not available ex stock) KWO Werkzeuge GmbHPostfach 1363D-73444 Oberkochen Phone +49 73 64 95 18 Fax +49 73 64 95 749www.kwo.de

Distancemin. 15 mm

Distanzmin. 15 mm

Screws for indoor use – no outdoor use

1

Wood screw with washer and plastic cover

2

Fascia screws for metal substructuresThreaded fasteners for outdoor use

Please take the thermal expansion of thepanel into account when using threaded fas-teners outdoors. To avoid jamming, the holediameter in the panel must allow for theexpansion.Fastening without jamming is possible withfascia screws made of stainless steel withsealing washer (Fig. 1) that have beenapproved for construction. The screws mustbe suitable for the corresponding substructure(please note the information given by themanufacturer). The screws should be tight-ened with a torque wrench or screwdriver sothat the sealing washer is placed on the panelfor sealing the bore hole without exertingpressure onto the panel.Multi-step drills or sleeves having correspon-ding diameters are used for centrically drillingholes into the panel and the substructure andfor centrically fitting the rivet.

Important: Make sure to remove protective foil prior toscrewing.

Threaded fasteners for indoor use

Screws for sheet metal and wood with differ-ent head-shapes are suitable for indoor use(Fig. 2). They do not normally allow for anypanel expansion.Countersunk screws can be inserted by theusual countersinking method or by depressingthe aluminium surface into the panel. Whendepressing the aluminium surface, the holediameter in the panel must be larger than thescrew diameter..

Hot-air welding has proved useful for joiningthermoplastic plastics and for weldingALUCOBOND®. The plastic core and the plasticwelding rod are heated and welded withelectrical hot-air welding sets. The followingconditions are essential for good results:• Well prepared welding joint• Good quality welding rod• Clean hot air• Correct temperature• Correct contact pressure• Welding speed

Welding with rapid welding nozzle

(Fig. 1) The rapid welding nozzle method ensuresuniform heating of the core material and thewelding rod and thus results in a betterwelding quality. Rod A is inserted manually through nozzletongue B. By applying constant pressure to thenozzle tongue, the rod is pressed into the joint.

Preparing of welding jointFor butt-welding, the edges of theALUCOBOND® panels must be chamfered (Fig. 2).Before folding and welding ALUCOBOND®

panels, grooves have to be routed into thepanels using corresponding milling cutters(Fig. 3).As the plastic core oxydizes relatively quicklywhen exposed to air, welding should be com-pleted within 24 hours after chamfering.

Welding rodPlease use the following quality:Polyethylene, soft, Type: 1800-hColour: black, diameter: 3-4 mmThe outer layer (oxide layer) of the weldingrod should be removed with emery clothimmediately before welding. Please chamferthe starting end of the rod to approx. 45°.

TemperatureThe following air temperature is required forhot-air welding:ALUCOBOND®: 265°C +/- 5°CThe temperature must be continuouslyadjustable and is measured with a mercurythermometer or bimetal measuring unit 5 mmfrom the nozzle point. To measure the temper-ature, please take off the rapid welding nozzle.

Contact PressureThe required pressure to the nozzle shoe(rapid welding nozzle) should be approx. 3 kp.

Hot-air welding setsWe recommend that the Leister hot-airwelding set, Type DIODE PID, be used inconnection with the ventilator, Type MINOR.

Skimming the welding seamA scraper blade or knife is used at a very flatangle to shave the welding seam as soon as ithas cooled down. For visible welding joints,the seam on butt and corner welds is removedusing a crescent-shaped knife (Fig. 4).

18

Hot-air welding (for ALUCOBOND® with PE core only)

Manufacturer / Suppliers:

Hot-air welding sets, temperaturemeasuring devices, crescent-shapedknives and welding rodHeißlufttechnik GmbH & Co Leister Vertrieb Dültgentaler Str. 11 D-42719 SolingenPhone +49 2 12 3 82 60 – 0 Fax +49 2 12 31 23 24www.heisslufttechnik.deHerz GmbH Leister-Vertrieb Biberweg 1 D-56566 Neuwied Phone +49 26 22 8 10 86 Fax +49 26 22 8 10 80www.herz-gmbh.comWelding rodKetterer + Liebherr GmbH & Co KG Gündlinger Str. 20 D-79111 Freiburg Phone +49 7 61 4 78 14 – 0 Fax +49 7 61 4 78 14 – 90www.ketterer-liebherr.deMilling cutters (not available ex stock)KWO Werkzeuge GmbHPostfach 1363D-73444 Oberkochen Phone +49 73 64 95 18 Fax +49 73 64 95 749www.kwo.de

1

2

4

adjacent

Crescent shaped knife

3

Grooving with milling cutter

For t = 3 mm Code No. 79805For t = 4 mm Code No. 79806For t = 6 mm Code No. 79807

r = 2 to 3 mm

t

r

Metal adhesives / Universal adhesives

For indoor use, trade fair/exhibition standstructures and machines, most metal oruniversal adhesives are suitable.

Tapes / Velcro tapesDouble-sided tapes (such as the 3M-VHB highcapacity jointing systems) can be used for theabove applications with low tensile or trans-versal strength requirements. Velcro tapes areavailable for detachable joints, for exampleSCOTCHMATE or tapes marketed under theDual Lock trademark. Both products are also available from 3M Deutschland GmbHCarl-Schurz-Straße 1D-41460 NeussPhone +49 21 31 14 - 0Fax +49 21 31 14 26 49www.3m.com

19

Clamp connections incorporating aluminium or plastics are particularly suitable forALUCOBOND®. They generally consist of twoparts with the clamping effect achieved bybolting.Various designs of clamping elements areused for display and store fitting purposes (no outdoor use). Suppliers:“Klemetric” system:KlemProducts®Gesellschaft für Werbemittel mbHTalangerstrasse 3aD-82152 Krailing/MünchenPhone +49 89 857 72 80Fax +49 89 895 83 48www.klemproducts.de“Voluma” system:MERO Raumstruktur GmbH & Co.KGAusstellungssystemePostfach 6169D-97064 WürzburgPhone +49 931 66 70 – 571Fax +49 931 66 70 – 189www.mero.de

Adhesive sealing compoundsFor high-strength and elastic connections werecommend the following one-componentadhesive sealing compound:Sika Bond-T2 (polyurethane base) Sika GmbH Stuttgarter Straße 139 D-72574 Bad Urach Phone +49 71 25 9 40 - 0 Fax +49 71 25 9 40 - 321www.sika.deFor outdoor use, this adhesive can be used forfastening parts of minor static importance.

Important:Please observe the manufacturer’s instructionsregarding the application and use of adhe-sives/tapes.Adhesives and sealing compounds do notadhere to the ALUCOBOND® plastic core (cut edges).Laminating of ALUCOBOND® panels to othermaterials may result in deformation of thelaminates (differing expansion/bimetal effect).

Glueing

Clamp connections“Klemetric” system

“Voluma” system

Any suitable connection or shock-resistantframe can easily be made with aluminiumsections.The inevitable tolerances signify differentretention forces. A uniform and solid fit of thesections is obtained by pressing the sectionsides together prior to inserting the panels.Butt joint, corner and edge sections are avail-able for panels of 3, 4 and 6 mm. Please askfor our stock list. For fascia cladding applications specialaluminium sections are provided for clampconnections.For further information on ALUCOBOND®

special sections and types for fasciacladdings please ask for the respectivedocumentation.

20

Lacquering of mill-finished ALUCOBOND® surfaces

21

Surfacetreatment

Customer requirements for special colourshades of ALUCOBOND® composite panels are met in small amounts by overlacqueringstandard stove-lacquered ALUCOBOND®

surfaces or mill-finished surfaces.

The composition of lacquer coating forALUCOBOND® is basically the same as thosefor mill-finished aluminium surfaces. However,it is advisable to be familiar with coatingsystems and materials as well as workingmethods for aluminium.

Please note:

• For general information on painting,lacquering and coating of aluminium werecommend the leaflets on ”02, 03, 012,015 surfaces” issued by

Gesamtverband der Aluminiumindustrie e. V.Postfach 105 463D-40045 DüsseldorfPhone +49 211 47 96 0Fax +49 211 47 96 408www.aluinfo.de

Please note:• The maximum permissible temperature

of the material (ALUCOBOND® panels)must not exceed 70°C when applyingfast-drying methods. During the dryingprocess at high temperatures theALUCOBOND® panels must be posi-tioned with great care to preventdeforming.

• ALUCOBOND® cut edges should not be incontact with organic solvents for a pro-longed period of time to avoid weakeningthe bond.

• ALUCOBOND® panels lacquered or overlac-quered at a later stage should not be bentor folded. The lacquer in the bends or foldsmay be damaged due to the low elasticityof the top coat.

• Upon request, we can name you lacquersuppliers who are able to apply lacquer thatcan be bent and folded.

• Only inferior lacquer adhesion can beachieved on core material exposed at cutedges.

• Please make a test prior to overlacqueringand follow the instructions of the lacquersuppliers.

Overlacquering of stove-lacquered ALUCOBOND®

surfaces

22

Non-suitable cleaning agentsPlease do not use any powerful alkalinecleaning agents such as potassium hydroxide,sodium carbonate or caustic soda, or anypowerful acidic products or heavily abrasivescouring agents or lacquer-dissolving cleaningagents.

23

Cleaning and Maintenance

Surfacesof stove-lacquered

Cleaning agentsA list of neutral cleaning agents for organicallycoated or anodized aluminium components isavailable at

Gesamtverband der Aluminiumindustrie e. V.Postfach 105 463D-40045 Düsseldorf Phone +49 211 47 96 0Fax +49 211 47 96 408www.aluinfo.de

Please observe the manufacturer’s cleaningand safety instructions!

For further information such as addresses ofapproved and recommended cleaning compa-nies, please contact

Gütegemeinschaft für die Reinigung vonMetallfassaden e.V. (GRM)Irrerstrasse 17 - 19 D-90403 Nürnberg Phone +49 9 11 20 44 41 Fax +49 9 11 22 67 55www.grm-online.de

Expert and regular cleaning not only maintainsthe aesthetic and representative finish ofstove-lacquered surfaces but also maintainstheir quality through the removal of dirt andaggressive deposits.Cleaning intervals depend on local environ-mental conditions and the resulting amount ofsoiling. Surfaces should be cleaned eithermanually or with a suitable cleaning devicefrom top to bottom.Please do not use any abrasive pads on lac-quered surfaces. We recommend that thecleaning agent be tried on an unobtrusive partof the object to be cleaned to check whetherthe surface is affected.Do not clean hot surfaces (>40° C) as the quick drying process may causeblemishes.

Panel-Thickness: Standard Unit 3 mm 4 mm 6 mm

Thickness of Aluminium Layers [mm] 0.50Weight [kg/m2] 4.5 5.5 7.3Width [mm] 1000 / 1250 / 1500

Technical properties:Section modulus W DIN 53293 [cm3/m] 1.25 1.75 2.75Rigidity (Poisson’s ratio µ = 0,3) E·I DIN 53293 [kNcm2/m] 1250 2400 5900Alloy/Temper of Aluminium Layers EN 573-3 EN AW 5005A (AlMg1), H22/H42Modulus of Elasticity EN 1999 1-1 [N/mm2] 70’ 000Tensile Strength of Aluminium EN 485-2 [N/mm2] Rm ≥ 1300.2 % Proof Stress EN 485-2 [N/mm2] Rp0,2 ≥ 90Elongation EN 485-2 A50 ≥ 5Linear Thermal Expansion EN 1999 1-1 2.4 mm/m at 100°C temperature difference

Core:Polyethylene, Type LDPE [g/cm3] 0.92

Surface:Lacquering Coil Coating

Fluorocarbon based (e.g. PVdF)Gloss (initial value) ECCA T2 [%] 30 - 80Pencil Hardness ECCA T4 HB - F

Acoustical Properties:Sound Absorption Factor as ISO 354 0.05Sound Transmission Loss Rw ISO 717-1 [dB] 25 26 27Loss Factor d EN ISO 6721 0.0072 0.0087 0.0138

Thermal properties:Thermal Resistance R DIN 52612 [m2K/W] 0.0069 0.0103 0.0172Heat Transition Coefficient U DIN 4108 [W/m2K] 5.65 5.54 5.34Temperature Resistance [°C] -50...+80

24

Technical Data sheet

25

Technical Data sheet

plus

Panel Thickness: Standard Units 4 mm

Thickness of Aluminium Layers [mm] 0.50Weight [kg/m2] 7.6Width [mm] 1250 / 1500

Technical poperties:Section Modulus W DIN 53293 [cm3/m] 1.75Rigidity (Poisson’s ratio µ = 0,3) E·I DIN 53293 [kNcm2/m] 2400Alloy/Temper of Aluminium Layers EN 573-3 EN AW 5005A (AlMg1), H22/H42Modulus of Elasticity EN 1999 1-1 [N/mm2] 70’000Tensile Strength of Aluminium EN 485-2 [N/mm2] Rm ≥ 1300.2 % Proof Stress EN 485-2 [N/mm2] Rp0,2 ≥ 90Elongation EN 485-2 [%] A50 ≥ 5Linear Thermal Expansion EN 19991-1 2.4 mm/m at 100°C temperature difference

Core:Mineral material based on Aluminium-Hydroxide, polymer bonded

Surface:Lacquering Coil Coating

Fluorocarbon based (e.g. PVdF)Gloss (initial value) ECCA T2 [%] 30 - 80Pencil Hardness ECCA T4 HB - F

Acoustical Properties:Sound Absorption Factor as ISO 354 0.05Sound Transmission Rw ASTM E90 [dB] STC: 30 OITC: 24

Thermal properties:Thermal Resistance R ASTM C518 [m2K/W] 0.009Temperature Resistance [°C] -50...+80

Panel Thickness: Standard Units 3 mm 4 mm

Thickness of Aluminium Layers [mm] 0.50Weight [kg/m2] 5.7 7.2Width [mm] 1250 / 1500

Technical properties:Section modulus W DIN 53293 [cm3/m] 1.25 1.75Rigidity (Poisson’s ratio m = 0.3) E·I DIN 53293 [kNcm2/m] 1250 2400Alloy/Temper of Aluminium Layers EN 573-3 EN AW 5005A (AlMg1), H22/H42Modulus of Elasticity EN 1999 1-1 [N/mm2] 70’000Tensile Strength of Aluminium EN 485-2 [N/mm2] Rm ≥ 1300.2 % Proof Stress EN 485-2 [N/mm2] Rp0,2 ≥ 90Elongation EN 485-2 [%] A50 ≥ 5Linear Thermal Expansion EN 1999 1-1 2.4 mm/m at 100°C temperature difference

Core:Mineral material based on Aluminium-Hydroxide, polymer bonded

Surface:Lacquering Coil Coating

Fluorocarbon based (e.g. PVdF)Gloss (initial value) ECCA T2 [%] 30 - 80Pencil Hardness ECCA T4 HB - F

Acoustical Properties:Sound Absorption Factor as ISO 354 0.05Sound Transmission Loss Rw ISO 717-1 [dB] 27 27Loss Factor d EN ISO 6721 0.004 0.005

Thermal properties:Thermal Resistance R DIN 52612 [m2K/W] 0.002 0.003Temperature Resistance [°C] -50...+80

Technical Data Sheet

A2

26

Informations(Please request)

ALUCOBOND® Information folder

ALUCOBOND® Colours

ALUCOBOND® Product Catalogue: Aluminium Special Sections and Fittings

ALUCOBOND® Documentation filewith examples for fascia claddings and texts for tendering incl. CD ROM

27

Original samples with standard surfaces

Samples

1/07

/200

3 Pr

oces

sing

GB

www.alucobond.com

ALCAN COMPOSITESAlcan Singen GmbHD-78221 SingenPhone +497731/80–0 Fax +497731/80–2845composites@alcan.com

ALCAN COMPOSITES – a truly global playerOffices and manufacturing operations in Europe, theAmericas and AsiaWidest selection of sheet materialPartnerships with top distributorsDedicated salesforce

•

•••

•••••••

ALCAN COMPOSITES – a global organisationAlcan Airex AG, Sins, SwitzerlandAlcan Kapa GmbH, Osnabrück, GermanyAlcan Singen GmbH, Singen, GermanyAlcan Thermoplastics, Chelmsford, UKAlcan Composites USA Inc., St. LouisAlcan Composites Ltd., Shanghai, ChinaAlcan Composites Brasil S.A.