PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater....
Transcript of PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater....
![Page 1: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/1.jpg)
Bridging model and real systems with laboratory experiments: dynamic retention of deuterium in tungsten
Régis Bisson
PIIM laboratory Aix-Marseille Université - CNRS
Marseille, France
Trieste ICTP-IAEA, November 2014
![Page 2: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/2.jpg)
Bridging model and real systems with laboratory experiments: summary of common laboratory experiments
Trieste ICTP-IAEA, November 2014 1
• same parameters, similar retention but different TPD profile: sample preparation?
Ogorodnikova et al. J. Nucl. Mater. 313-316, 469 (2003)
Tian et al., J. Nucl. Mater. 399, 101 (2010)
200 eV/D F=3.1024 D/m2
Ogorodnikova et al., Phys. Scr. T138, 014053 (2009)
![Page 3: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/3.jpg)
Ogorodnikova et al. J. Nucl. Mater. 313-316, 469 (2003)
Bridging model and real systems with laboratory experiments: summary of common laboratory experiments
• same parameters, similar retention but different TPD profile: sample preparation?
• different apparatuses used for D implantation and TPD retention measurement
air exposure generates many deuterated products than cannot all be recorded
underestimation of retention [Wang et al. Nucl. Instr. Meth. Phys. Res. B 300, 54 (2013)]
Tian et al., J. Nucl. Mater. 399, 101 (2010)
200 eV/D F=3.1024 D/m2
Ogorodnikova et al., Phys. Scr. T138, 014053 (2009)
Trieste ICTP-IAEA, November 2014 2
![Page 4: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/4.jpg)
3
• Retention measurement best approach: all-in-situ apparatus (no air exposure)
• a rare example in the literature: Ogorodnikova et al. J. Nucl. Mater. 313-316, 469 (2003)
Flux: 1019 D.m-2.s-1
Fluence: 1021-1024 D.m-2 Ts: 300 K Ek: 200 eV/D
Ogorodnikova et al.
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: selecting “ideal” conditions
![Page 5: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/5.jpg)
4
• Retention measurement best approach: all-in-situ apparatus (no air exposure)
• a rare example in the literature: Ogorodnikova et al. J. Nucl. Mater. 313-316, 469 (2003)
Flux: 1019 D.m-2.s-1
Fluence: 1021-1024 D.m-2 Ts: 300 K Ek: 200 eV/D
Ogorodnikova et al. this work
1016 D.m-2.s-1
1017-1021 D.m-2 300 K 250 eV/D
• in Aix-Marseille University (AMU): our W samples present a single low temperature
desorption peak (low defect density)
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: selecting “ideal” conditions
![Page 6: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/6.jpg)
5
Polycrystalline sample with low defect concentration - Annealed at (1573 K ; 1h) in vacuum by A.L.M.T. (Japan) - Electro-polished in-house for mirror finish - Annealing at 1300 K in ultra-high vacuum
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: selecting “ideal” conditions
this work
1016 D.m-2.s-1
1017-1021 D.m-2 300 K 250 eV/D
![Page 7: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/7.jpg)
6
Polycrystalline sample with low defect concentration - Annealed at (1573 K ; 1h) in vacuum by A.L.M.T. (Japan) - Electro-polished in-house for mirror finish - Annealing at 1300 K in ultra-high vacuum
differentially pumped
QMS chamber
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: the AMU apparatus
![Page 8: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/8.jpg)
7
differentially pumped
QMS chamber
D2+
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: the AMU apparatus
![Page 9: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/9.jpg)
8
differentially pumped
QMS chamber
D2
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: the AMU apparatus
![Page 10: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/10.jpg)
9
• Absolute calibration of the TPD in desorption rate (D2/s) and retention (D/m2) checked with NRA measurements (JSI, Slovenia)
•Absolute retention sensitivity down to 1017 D.m-2
differentially pumped
QMS chamber
D2
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: the AMU apparatus
![Page 11: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/11.jpg)
10
[1] Ogorodnikova et al., J. Nucl.Mater. 313-316, 469 (2003)
• retention orders of magnitude smaller than implantation probability from SRIM model
• non-linear dependence of Retention α Fluence0.50-0.66
Bridging model and real systems with laboratory experiments: retention measurements: extending to low fluences
Trieste ICTP-IAEA, November 2014
![Page 12: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/12.jpg)
[1] Ogorodnikova et al., J. Nucl.Mater. 313-316, 469 (2003)
Bisson et al., in preparation 11
• retention orders of magnitude smaller than implantation probability from SRIM model
• non-linear dependence of Retention α Fluence0.50-0.66
Retention α Fluence0.40-0.60
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: retention measurements: extending to low fluences
![Page 13: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/13.jpg)
12 Bisson et al., in preparation
• retention similar to SRIM implantation probability when reaching low fluences
• non-linear dependence of Retention α Fluence0.50-0.66
Retention α Fluence0.40-0.60
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: retention measurements: extending to low fluences
[1] Ogorodnikova et al., J. Nucl.Mater. 313-316, 469 (2003)
![Page 14: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/14.jpg)
• discrepancy in the 1021 D/m2 range where different fluxes were used
Bridging model and real systems with laboratory experiments: retention measurements: explaining discrepancies
13 Bisson et al., in preparation
• retention similar to SRIM implantation probability when reaching low fluences
• non-linear dependence of Retention α Fluence0.50-0.66
Retention α Fluence0.40-0.60
Trieste ICTP-IAEA, November 2014
[1] Ogorodnikova et al., J. Nucl.Mater. 313-316, 469 (2003)
![Page 15: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/15.jpg)
• discrepancy in the 1021 D/m2 range where different fluxes were used … i.e. different implantation duration
• could it be that release (desorption) of deuterium occurs during implantation ?!
2 min
24 hour
14 Bisson et al., in preparation
• retention similar to SRIM implantation probability when reaching low fluences
• non-linear dependence of Retention α Fluence0.50-0.66
Retention α Fluence0.40-0.60
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: retention measurements: explaining discrepancies
[1] Ogorodnikova et al., J. Nucl.Mater. 313-316, 469 (2003)
![Page 16: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/16.jpg)
• could it be that release (desorption) of deuterium occurs during implantation ?!
15 Bisson et al., in preparation
repeated this implantation many times with different storage time
between the end of implantation and
the TPD measurement
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: retention measurements: explaining discrepancies
[1] Ogorodnikova et al., J. Nucl.Mater. 313-316, 469 (2003)
![Page 17: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/17.jpg)
Deuterium release on the time scale of hours and days
Release of deuterium during long implantation (explains the discrepancy in the 1021 D/m2 range between our data and
Ogorodnikova et al. data)
16 Bisson et al., in preparation Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: dynamic retention of deuterium in tungsten
![Page 18: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/18.jpg)
17 Bisson et al., in preparation
Deuterium release on the time scale of hours and days
Best fit obtained with a double exponential decay (with a constant): at least 3 populations of traps… but a single desorption peak !
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: dynamic retention of deuterium in tungsten
![Page 19: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/19.jpg)
Deuterium release on the time scale of hours and days
Best fit obtained with a double exponential decay (with a constant): at least 3 populations of traps… but a single desorption peak !
18 Bisson et al., in preparation Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: dynamic retention of deuterium in tungsten
![Page 20: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/20.jpg)
19 Bisson et al., in preparation
Deuterium release on the time scale of hours and days
The single desorption peak has a structure “evolving” with storage time: it is composed of several sub-peaks
Several trapping energies are related to the low desorption temperature peak (at least 3 trapping energies from previous retention decay analysis)
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: dynamic retention of deuterium in tungsten
![Page 21: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/21.jpg)
Bridging model and real systems with laboratory experiments: origin of the dynamic retention of deuterium
a single TPD peak =
at least 3 trapping energies
Bisson et al., in preparation Fernandez, Kato, Ferro, in preparation
“a single trap: the W vacancy” =
at least 4 groups of trapping energies for 300 K implantation
DFT calculations + statistical model PIIM lab + NIFS (D. Kato) 20 Trieste ICTP-IAEA,
November 2014
![Page 22: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/22.jpg)
Bridging model and real systems with laboratory experiments: double checking the origin of the dynamic retention of deuterium
21 Trieste ICTP-IAEA, November 2014 Bisson et al., in preparation
At low fluences: retention = SRIM implantation probability:
dynamic retention is non operative
Why? deuterium density is low (10-5 at. density)
mostly 1H or 2H-vacancy complexes (VH1-2)
![Page 23: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/23.jpg)
Fernandez, Kato, Ferro, in preparation
22
VH1-2 complexes: binding energy is high desorption temperature should be higher for low fluences…
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: double checking the origin of the dynamic retention of deuterium
Bisson et al., in preparation
At low fluences: retention = SRIM implantation probability:
dynamic retention is non operative
Why? deuterium density is low (10-5 at. density)
mostly 1H or 2H-vacancy complexes (VH1-2)
![Page 24: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/24.jpg)
Fernandez, Kato, Ferro, in preparation
23
VH1-2 complexes: binding energy is high desorption temperature should be higher for low fluences… this is verified
At low fluences: retention = SRIM implantation probability:
dynamic retention is non operative
Why? deuterium density is low (10-5 at. density)
mostly 1H or 2H-vacancy complexes (VH1-2)
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: double checking the origin of the dynamic retention of deuterium
Bisson et al., in preparation
![Page 25: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/25.jpg)
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: summary
• all-in-situ apparatus • implantation at 300 K ; TPD up to 1300 K • retention measured down to 1017 D/m2
• observation of D release at 300 K • on at least 3 time scales • with an evolution of the TPD peak • consistent with W vacancy trap filling
![Page 26: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/26.jpg)
R. Bisson, C. Grisolia (CEA), T. Angot Researchers O. Saïdi, F. Ghiorghiu PhD students S. Markelj (JSI, Slovenia) visiting scientist (Euratom) O. Mourey Master student J.-B. Faure Mechanical engineer
€ from ANR, CNRS, AMU, EFDA/EUROfusion
Trieste ICTP-IAEA, November 2014
• all-in-situ apparatus • implantation at 300 K ; TPD up to 1300 K • retention measured down to 1017 D/m2
Bridging model and real systems with laboratory experiments: summary
• observation of D release at 300 K • on at least 3 time scales • with an evolution of the TPD peak • consistent with W vacancy trap filling
![Page 27: PIIM laboratory Aix-Marseille Université - CNRS Marseille ...Ogorodnikova . et al. J. Nucl. Mater. 313-316, 469 (2003) Bridging model and real systems with laboratory experiments:](https://reader034.fdocuments.in/reader034/viewer/2022050304/5f6d37943a4dbe598e3e4443/html5/thumbnails/27.jpg)
Starting 2015 an extensive “model experiment – theory” collaboration on D retention in tungsten through a project supported by the A*MIDEX foundation (Aix-Marseille Université)
a large set of samples (single and poly-crystals)
surface and bulk preparation techniques (e-/p+/Wn+ accelerators, surface science) complete set of analysis tools (TPD, XPS, SEM, TEM, NRA, SIMS, PAS…)
multi-scale modeling approach (DFT, OKMC, MRE)
Trieste ICTP-IAEA, November 2014
Bridging model and real systems with laboratory experiments: perspectives
Y. Ferro, C. Becquart, C. Grisolia, B. Rousseau, R. Bisson, T. Angot, G. Cartry, C. Pardanaud, C. Martin, P. Roubin, M.-F. Barthe, L. Gallais… PIIM, Fresnel, CEA, CEMHTI, UMET, LSPM…
Thank you for your attention