perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
i
PENGARUH KOMPOSISI AGREGAT DAUR ULANG TERHADAP
SUSUT PADA BETON NORMAL DANBETON MUTU TINGGI
“The Influence of Recycled Aggregate Composition on the Shrinkage ofNormal
and High Strength Concrete”
SKRIPSI
Disusunsebagai Salah SatuSyaratMemperolehGelarSarjana
PadaJurusanTeknikSipilFakultasTeknik
UniversitasSebelasMaret
Surakarta
Oleh :
BIMO HARIOSETO
NIM. I0107056
JURUSAN TEKNIK SIPIL FAKULTAS TEKNIK
UNIVERSITAS SEBELAS MARET
SURAKARTA
2013
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
ii
LEMBAR PERSETUJUAN
PENGARUH KOMPOSISI AGREGAT DAUR ULANG TERHADAP
SUSUT PADA BETON NORMAL DANBETON MUTU TINGGI
“The Influence of Recycled Aggregate Composition on the Shrinkage ofNormal
and High Strength Concrete”
Disusun Oleh :
BIMO HARIOSETO
NIM. I0107056
Telah disetujui untuk dipertahankan dihadapan Tim Penguji Pendadaran
Jurusan Teknik Sipil Fakultas Teknik Universitas Sebelas Maret
JURUSAN TEKNIK SIPIL FAKULTAS TEKNIK
UNIVERSITAS SEBELAS MARET
SURAKARTA
2013
DosenPembimbing I
Dr.Techn.Ir.SholihinAs’ad, MT
NIP. 19671001 199702 1 001
DosenPembimbing II
Kusno Adi Sambowo, ST, PhD
NIP. 19691026 199503 1 002
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
iii
LEMBAR PENGESAHAN
PENGARUH KOMPOSISI AGREGAT DAUR ULANG TERHADAP
SUSUT PADA BETON NORMAL DANBETON MUTU TINGGI
“The Influence of Recycled Aggregate Composition on the Shrinkage ofNormal
and High Strength Concrete”
SKRIPSI
Disusun oleh:
BIMO HARIOSETO
NIM. I0107056
Dipertahankan dihadapan Tim Penguji Pendadaran Jurusan Teknik Sipil Fakultas
Teknik Universitas Sebelas Maret Surakarta dan diterima guna memenuhi
persyaratan untuk mendapatkan gelar sarajana teknik
Pada Hari : Rabu
Tanggal : 13 November 2013
Tim Penguji Pendadaran :
1. Dr.Techn.Ir.SholihinAs’ad, MT ……………………………
N I P . 19671001 199702 1 001
2. Kusno Adi Sambowo, ST, MSc, PhD …………………………....
N I P . 19691026 199503 1 002
3. Ir. Sunarmasto, MT ……………………………
N I P . 19560717 198703 1 003
4. Achmad Basuki, ST, MT ……………………………
N I P . 19710901 199702 1 001
Disahkan
Ketua Jurusan Teknik sipil
Fakultas Teknik UNS
Ir. Bambang Santosa, MT
NIP. 19590823 198601 1 001
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
iv
LEMBAR PENGESAHAN SEMENTARA
PENGARUH KOMPOSISI AGREGAT DAUR ULANG TERHADAP
SUSUT PADA BETON NORMAL DANBETON MUTU TINGGI
“The Influence of RecycledAggregate Composition on the Shrinkage ofNormal
and High Strength Concrete”
SKRIPSI
Disusun Oleh :
BIMO HARIOSETO
NIM. I 0107056
Pembimbing :
1. Dr.Techn.Ir.SholihinAs’ad, MT ……………………………
N I P . 19671001 199702 1 001
2. Kusno Adi Sambowo, ST, MSc, PhD ……………………………
N I P . 19691026 199503 1 002
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
vii
ABSTRAK
Bimo Harioseto, 2013. Pengaruh Komposisi Agregat Daur Ulang Terhadap
Susut pada Beton Normal dan Beton Mutu Tinggi. Tugas Akhir. Jurusan
Teknik Sipil Fakultas Teknik Universitas Sebelas Maret Surakarta.
Agregat daur ulang merupakan material yang berasal dari hasil daur ulang limbah
beton yang bisa dipergunakan kembali didalam konstruksi bangunan dan memiliki
nilai ekonomis. Limbah padat hasil dari pembongkaran bangunan yang tidak
terpakai bila tidak diolah dapat mencemari lingkungan. Jika diolah dengan benar,
limbah konstruksi dapat menghasilkan beton bermutu tinggi dan ramah
lingkungan. Pemanfaatan agregat daur ulang ini diharapkan mampu menjadi salah
satu penerapan yang dapat mendukung adanya program green concrete. Penelitian
ini bertujuan untuk mengetahui karakteristik beton dengan penggantian sebagian
atau seluruh agregat daur ulang jika dibandingkan beton dengan agregat alam
ditinjau dari nilai susut beton.
Penelitian ini menggunakan metode eksperimen dengan total 72 benda uji. Benda
uji terdiri atas beton normal dan beton mutu tinggi dengan variasi komposisi
agregat daur ulang 0%, 20%, 40%, 60%, 80% dan 100%. Setiap jenis campuran
beton dibuat 3 benda uji. Benda uji yang digunakan adalah prisma beton dengan
panjang 28 cm, tinggi 7,5 cm, dan lebar 7,5 cm. Pengujian shrinkage dilakukan pada
umur 1 hari hingga umur 90 hari. Data yang diamati berupa nilai penyusutan yang
selanjutnya dianalisis dan didapat besar penyusutan dan prediksi shrinkage jangka
panjang menggunakan persamaan ACI 209.
Dari analisis diperoleh hasil bahwa agregat daur ulang menambah besarnya nilai
susut yang terjadi. Shrinkage terbesar terjadi pada sampel beton normal dengan
pemakaian agregat kasar daur ulang sebanyak 100% yaitu sebesar 1014,5
microstrain. Sedangkan shrinkage terendah terdapat pada sampel beton mutu
tinggi dengan pemakaian agregat alami sebanyak 100% yaitu sebesar 595,83
microstrain. Hasil pengujian menunjukkan bahwa besarnya drying shrinkage
yang terjadi pada beton mutu tinggi lebih kecil dibandingkan beton normal. Hasil
penelitian ini juga menunjukkan bahwa semakin banyak kadar agregat daur ulang
yang digunakan, besarnya nilai susut pada beton akan semakin besar.
Kata kunci: agregat daur ulang, susut, dan prediksi susut.
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
viii
ABSTRACT
Bimo Harioseto, 2013. The Influence of Recycled Aggregate Composition on
the Shrinkage of Normal and High Strength Concrete. Final Project. Civil
Engineering Department of Engineering Faculty of Surakarta Sebelas Maret
University.
Recycled aggregate is material derived from recycled concrete waste that can be
reused in the construction of buildings and have economic value. Solid waste from
the demolition of unused buildings if not treated can pollute the environment. If it
is processed properly, construction waste can produce high strength concrete and
environmentally friendly. Utilization of recycled aggregates is expected to be an
application that can support the green concrete program. This study aims to
determine the characteristics of concrete with a replacement part or all of the
recycled aggregate in comparison with natural coarse aggregate in terms of
shrinkage of concrete.
This study used experimental method with 72 specimens. The specimens consisted
of normal concrete and high strength concrete with a variation of the composition
of recycled aggregate 0%, 20%, 40%, 60%, 80% and 100%. Each type of
concrete mix was made with 3 specimens. The tested object used was beam with
28 x 7,5 x 7,5 cm3 size. The shrinkage tests were carried out in the first day until
the 90th days. The data observed was the shrinkage value that furthermore was
analyzed and the shrinkage value and long-term shrinkage prediction were
obtained using ACI 209 equation.
From the result of analysis, it can be found that the use of recycled aggregate
increase the drying shrinkage. The greatest shrinkage occurs in normal concrete
samples with the use of recycled coarse aggregate as much as 100% in the
amount of 1014.5 microstrain. While the lowest shrinkage found in a sample of
high quality concrete with natural aggregate consumption as much as 100% in
the amount of 595.83 microstrain. The results shows that the magnitude of drying
shrinkage that occurs in high strength concrete is smaller than normal concrete.
The result of research also shows that the more recycled aggregate is used, the
magnitude of shrinkage of concrete with recycled aggregates becomes greater.
Keywords: recycled aggregate, shrinkage, and prediction of shrinkage.
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
iv
MOTTO
Kegagalan adalah ketika kita berhenti untuk
berusaha.
Jadikan kemarin sebagai pelajaran dan
pengalaman, sekarang sebagai usaha dan esok
sebagai cita-cita dan harapan.
Orang yang sukses bukan yang tak pernah kalah,
tetapi yang tak pernah menyerah.
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
v
PERSEMBAHAN
Syukur Alhamdulillah saya panjatkan kepada Allah SWT atas rahmat dan hidayah-
Nya, dengan segala kerendahan hati izinkan saya mempersembahkan karya ini
seraya berucap terima kasih kepada:
Kedua Orang Tuaku (Sugiharto dan Sulastri)
Terima kasih atas do’a dan kasih sayang yang tak pernah putus, serta kepercayaan
dan dukungan yang tulus. Bimo akan selalu berusaha tuk bisa membahagiakan dan
menjadi kebanggaan Papa dan Mama.
Saudaraku (Dewo Arihutomo)
Terima kasih Bro atas dukungannya. Semoga kamu bisa menjadi sarjana yang lebih
baik dari abang.
Dosen Pembimbingku
(Dr.Techn.Ir. Sholihin As’ad, M.T. dan Kusno Adi Sambowo, ST, MSc, PhD.)
Terima kasih pak atas bimbingan, arahan serta sarannya. Bapak yang sangat sabar,
teliti, dan telaten dalam membimbing saya.
Dosen Penguji Skripsi
(Ir. Sunarmasto, MT dan Achmad Basuki, ST, MT)
Terima kasih pak atas kritik, saran, serta arahan selama siding akhir. Hal tersebut
sangat bermanfaat dalam perbaikan isi skripsi saya.
Rekan seperjuangan (Wahyu dan Hari)
Terima kasih atas kerjasama dan bantuannya. Dari mulai NGULI sampai asistensi
bareng. Sukses selalu buat kalian. Maaf, saya telat menyusul.
Para Sahabat
(Adhit, Alfian, Anas, Anggi, Butet, Chandra, Herry, Ijul, Sheiza, Kamplenk,
Bolang, Wahyu, Dion, Rizal, Yuda, Mas Bol, Bacil, Didit, Tenyom, Kunyil,
Gendut, Ali, Hakim 1, Hakim 2, Mas Angga, Ajik, Fathir, dan lain-lain)
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
vi
Terima kasih atas kebersamaan dan keceriaan yang selalu ada selama ini. Semoga
kita tetap menjadi keluarga yang ‘wollu’.
Keluarga besar Sipil UNS 2007
Terima kasih atas persahabatannya selama ini, sukses slalu buat kalian.
B 6221 KLE
Yang udah nemenin gw dari awal kuliah sampai sekarang, mulai dari nganterin ke
kampus serta jalan-jalan menjelajahi Solo dan sekitarnya.
Girl behind the script
Terima kasih atas semua support, nasihat, saran dan semuanya yang telah kau beri
untukku.
Dosen-dosen Jurusan Teknik Sipil FT UNS
Semua pihak yang telah membantu yang tidak mungkin aku sebutin satu persatu.
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
ix
KATA PENGANTAR
Puji syukur kehadirat Allah SWT yang telah melimpahkan rahmat serta hidayah-
Nya sehingga penulis dapat menyelesaikan penyusunan skripsi dengan judul
“ Pengaruh Komposisi Agregat Daur Ulang Terhadap Susut Pada Beton Normal
dan Beton Mutu Tinggi” guna memenuhi syarat memperoleh gelar Sarjana Teknik
dari Jurusan Teknik Sipil Fakultas Teknik Universitas Sebelas Maret Surakarta.
Penulis menyadari sepenuhnya bahwa tanpa bantuan dari berbagai pihak maka
banyak kendala yang sulit untuk penyusun pecahkan hingga terselesaikannya
penyusunan skripsi ini. Untuk itu, Penulis ingin menyampaikan ucapan
terimakasih kepada :
1. Pimpinan Fakultas Teknik Universitas Sebelas Maret Surakarta,
2. Pimpinan Jurusan Teknik Universitas Sebelas Maret Surakarta,
3. Dr. Techn. Ir. Sholihin As’ad, MT selaku dosen pembimbing I,
4. Kusno Adi Sambowo, ST, MSc, PhD selaku dosen pembimbing II,
5. Ir. Sunarmasto, MT dan Achmad Basuki, ST, MT selaku dosen penguji siding
akhir.
6. Staf pengelola/laboran Laboratorium Bahan Bangunan dan Struktur Jurusan
Teknik Sipil Fakultas Teknik Universitas Sebelas Maret,
7. Rekan-rekan mahasiswa Teknik Sipil Angkatan 2007 dan semua pihak yang
telah membantu penulis secara langsung maupun tidak langsung yang tidak
dapat penulis sebutkan satu persatu.
Penulis menyadari bahwa skripsi ini masih jauh dari sempurna. Oleh karena itu,
saran dan kritik yang membangun sangat penulis harapkan untuk kesempurnaan
skripsi ini. Semoga skripsi ini dapat berguna bagi pihak-pihak yang
membutuhkan, khususnya bagi penulis sendiri.
Wassalamu’alaikum Wr. Wb.
Surakarta, November 2013
Penulis
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
x
DAFTAR ISI
HALAMAN JUDUL ................................................................................... i
HALAMAN PERSETUJUAN .................................................................... ii
HALAMAN PENGESAHAN ..................................................................... iii
MOTTO DAN PERSEMBAHAN .............................................................. iv
ABSTRAK ................................................................................................. vii
KATA PENGANTAR ............................................................................... ix
DAFTAR ISI ............................................................................................... x
DAFTAR TABEL ....................................................................................... xiii
DAFTAR GAMBAR .................................................................................. xv
DAFTAR LAMPIRAN ............................................................................... xvii
DAFTAR NOTASI DAN SIMBOL ........................................................... xviii
BAB 1. PENDAHULUAN
1.1.Latar Belakang ...................................................................................... 1
1.2.Rumusan Masalah ................................................................................. 4
1.3.Batasan Masalah.................................................................................... 4
1.4.Tujuan Penelitian .................................................................................. 4
1.5. Manfaat Penelitian ............................................................................... 5
BAB 2. TINJAUAN PUSTAKA DAN DASAR TEORI
2.1.Tinjauan Pustaka ................................................................................... 6
2.2.Landasan Teori ...................................................................................... 7
2.2.1. Beton ................................................................................................ 7
2.2.2. Beton Mutu Tinggi ........................................................................... 7
2.2.3. Beton Daur Ulang ............................................................................. 8
2.2.4. Material Penyusun Beton Daur Ulang dan Beton Mutu Tinggi
Daur Ulang ...................................................................................... 9
2.2.4.1. Semen Portland .............................................................................. 9
2.2.4.2. Agregat ........................................................................................... 11
2.2.4.3. Air .................................................................................................. 26
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
xi
2.2.4.4. Bahan Tambah ............................................................................... 26
2.2.5. Susut Pada Beton ............................................................................. 28
2.2.5.1. Mekanisme Terjadinya Susut ....................................................... 30
2.2.5.2. Efek Susut pada Struktur .............................................................. 32
2.2.5.3. Prediksi Susut Jangka Panjang ..................................................... 32
2.2.5.4. Prinsip Pengukuran Susut ............................................................ 33
BAB 3. METODE PENELITIAN
3.1. Tinjauan Umum ................................................................................... 35
3.2. Benda Uji ............................................................................................. 35
3.3. Alat Uji Penelitian ................................................................................ 37
3.4. Bahan .................................................................................................. 38
3.5. Pembuatan Agregat Daur Ulang .......................................................... 38
3.6. Tahap Penelitian ................................................................................... 38
3.7. Pengujian Bahan Dasar Beton .............................................................. 42
3.7.1. Agregat Halus.................................................................................... 42
3.7.2. Agregat Kasar.................................................................................... 45
3.8. Perencanaan Campuran Beton (Mix Design) ....................................... 47
3.9. Pembuatan Benda Uji ........................................................................... 47
3.10. Pengujian Nilai Slump ........................................................................ 47
3.11. Pengujian Susut Prisma Beton ........................................................... 48
BAB 4. HASIL PENGUJIAN DAN PEMBAHASAN
4.1. Hasil Pengujian Bahan ......................................................................... 51
4.1.1. Hasil Pengujian Agregat Halus Alam ............................................... 51
4.1.2. Hasil Pengujian Agregat Kasar Alam ............................................... 52
4.1.3. Hasil Pengujian Agregat Halus Daur Ulang ..................................... 54
4.1.4. Hasil Pengujian Agregat Kasar Daur Ulang ..................................... 56
4.2. Rencana Campuran Adukan Beton ...................................................... 58
4.2.1. Rencana Campuran Adukan Beton Normal ...................................... 58
4.2.2. Rencana Campuran Adukan Beton Mutu Tinggi .............................. 59
4.3. Hasil Pengujian .................................................................................... 60
4.3.1. Hasil Pengujian Slump ...................................................................... 60
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
xii
4.3.2. Pengujian Susut (Shrinkage) ............................................................. 62
4.3.3. Hasil Perhitungan Prediksi Susut ...................................................... 70
4.4. Pembahasan .......................................................................................... 75
4.4.1. Nilai Slump ........................................................................................ 75
4.4.2. Susut (Shrinkage) .............................................................................. 75
BAB 5. KESIMPULAN
5.1. Kesimpulan .......................................................................................... 78
5.2. Saran .................................................................................................. 79
DAFTAR PUSTAKA ................................................................................. 80
LAMPIRAN
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
xiii
DAFTAR TABEL
Tabel 2.1. Jenis semen portland di Indonesia sesuai SII 0013-81........... 10
Tabel 2.2. Batasan susunan butiran agregat halus ................................... 12
Tabel 2.3. Persyaratan gradasi agregat kasar .......................................... 14
Tabel 2.4. Standar agregat daur ulang Jepang ......................................... 23
Tabel 2.5. Persyaratan agregat daur ulang diijinkan untuk pembuatan
beton nonstruktural................................................................. 24
Tabel 2.6. Persyaratan agregat daur ulang diijinkan untuk pembuatan
beton struktural....................................................................... 25
Tabel 2.7. Persyaratan agregat daur ulang di Spanyol ............................ 25
Tabel 2.8. Chemical Admixture ............................................................... 27
Tabel 3.1. Perincian benda uji ................................................................. 36
Tabel 3.2. Tabel perubahan warna .......................................................... 43
Tabel 4.1. Hasil pengujian agregat halus alam........................................ 51
Tabel 4.2. Hasil pengujian gradasi agregat halus alam ........................... 52
Tabel 4.3. Hasil pengujian agregat kasar alam........................................ 53
Tabel 4.4. Hasil pengujian gradasi agregat kasar alam ........................... 53
Tabel 4.5. Hasil pengujian agregat halus daur ulang .............................. 54
Tabel 4.6. Hasil pengujian gradasi agregat halus daur ulang .................. 55
Tabel 4.7. Hasil pengujian agregat kasar daur ulang .............................. 56
Tabel 4.8. Hasil pengujian gradasi agregat kasar daur ulang .................. 57
Tabel 4.9. Proporsi campuran adukan beton normal ............................... 58
Tabel 4.10. Proporsi campuran adukan beton mutu tinggi ....................... 59
Tabel 4.11. Nilai slump dari beton normal dan beton mutu tinggi dengan
berbagai variasi komposisi agregat kasar daur ulang ............. 60
Tabel 4.12. Nilai slump dari beton normal dan beton mutu tinggi dengan
berbagai variasi komposisi agregat halus daur ulang ............. 60
Tabel 4.13. Data Pengukuran Susut Pada Benda Uji NA 100 .................. 62
Tabel 4.14. Hasil pengujian susut (shrinkage) pada beton normal dengan
penggunaan agregat daur ulang .............................................. 63
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
xiv
Tabel 4.15. Hasil pengujian susut (shrinkage) pada beton mutu tinggi
dengan penggunaan agregat daur ulang ................................. 64
Tabel 4.16. Nilai Ultimate Shrinkage........................................................ 72
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
xv
DAFTAR GAMBAR
Gambar 1.1. Limbah beton dan agregat daur ulang ................................. 3
Gambar 2.1. Proses produksi agregat daur ulang di Tuen Mun Area 38
(Fong dan Yeung, 2003) ..................................................... 19
Gambar 2.2. Jaw crusher ......................................................................... 20
Gambar 2.3. Impact crusher .................................................................... 21
Gambar 2.4. Electromagnetic removing steel .......................................... 21
Gambar 2.5. Wet separation .................................................................... 22
Gambar 2.6. Cone crusher ....................................................................... 23
Gambar 2.7. Mekanisme susut ................................................................. 31
Gambar 2.8. Hubungan penyusutan terhadap waktu ............................... 34
Gambar 3.1. Bagan alir tahap-tahap penelitian ........................................ 41
Gambar 3.2. Pengujian nilai slump .......................................................... 48
Gambar 3.3. Setting pengujian dan alat uji susut kering .......................... 49
Gambar 4.1. Gradasi agregat halus alam ................................................. 52
Gambar 4.2. Gradasi agregat kasar alam ................................................. 54
Gambar 4.3. Gradasi agregat halus daur ulang ........................................ 55
Gambar 4.4. Gradasi agregat kasar daur ulang ........................................ 57
Gambar 4.5. Nilai slump pada beton normal dan beton mutu tinggi
dengan variasi komposisi agregat kasar daur ulang ............ 61
Gambar 4.6. Nilai slump pada beton normal dan beton mutu tinggi
dengan variasi komposisi agregat halus daur ulang ............ 61
Gambar 4.7. Hubungan shrinkage dan umur pengeringan pada beton
normal dengan penggunaan agregat halus daur ulang ....... 65
Gambar 4.8. Hubungan shrinkage dan umur pengeringan pada beton
normal dengan penggunaan agregat kasar daur ulang ........ 65
Gambar 4.9. Hubungan shrinkage dan umur pengeringan pada beton
mutu tinggi dengan penggunaan agregat halus daur ulang . 66
Gambar 4.10. Hubungan shrinkage dan umur pengeringan pada beton
mutu tinggi dengan penggunaan agregat kasar daur ulang . 66
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
xvi
Gambar 4.11. Hubungan shrinkage dan umur pengeringan dengan
pemakaian agregat daur ulang sebesar 20%........................ 67
Gambar 4.12. Hubungan shrinkage dan umur pengeringan dengan
pemakaian agregat daur ulang sebesar 40%........................ 67
Gambar 4.13. Hubungan shrinkage dan umur pengeringan dengan
pemakaian agregat daur ulang sebesar 60%........................ 68
Gambar 4.14. Hubungan shrinkage dan umur pengeringan dengan
pemakaian agregat daur ulang sebesar 80%........................ 68
Gambar 4.15. Hubungan shrinkage dan umur pengeringan dengan
pemakaian agregat daur ulang sebesar 100%...................... 69
Gambar 4.16. Hubungan shrinkage dan umur pengeringan dengan
pemakaian agregat daur ulang sebesar 0% dan 100% ........ 69
Gambar 4.17. Ultimate Shrinkage Sampel NA 100 ................................... 70
Gambar 4.18. Prediksi shrinkage pada beton normal dengan penggunaan
agregat halus daur ulang...................................................... 73
Gambar 4.19. Prediksi shrinkage pada beton normal dengan penggunaan
agregat kasar daur ulang...................................................... 73
Gambar 4.20. Prediksi shrinkage pada beton mutu tinggi dengan
penggunaan agregat halus daur ulang ................................. 74
Gambar 4.21. Prediksi shrinkage pada beton mutu tinggi dengan
penggunaan agregat kasar daur ulang ................................. 74
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
xvii
DAFTAR LAMPIRAN
Lampiran A. Data Hasil Pengujian Agregat
Lampiran B. Perhitungan Rencana Campuran Beton
Lampiran C. Data Hasil Pengujian Susut
Lampiran D. Data Prediksi Susut
Lampiran E. Dokumentasi Penelitian
Lampiran F. Surat-surat Skripsi
perpustakaan.uns.ac.id digilib.uns.ac.id
commit to user
xviii
DAFTAR NOTASI DAN SIMBOL
% = Persentase
oC = Derajat celcius
fc’ = Kuat tekan beton
in = Inchi
m = Meter
μm = Mikrometer
mm = Milimeter
cm = Centimeter
m³ = Meter kubik
gr = Gram
kg = Kilogram
lt = Liter
ml = Mililiter
W = Watt
MPa = Mega Pascal
𝜀𝑠ℎ(𝑡) = Nilai susut kering umur t (selama pengujian)
𝜀𝑠ℎ(𝑢) = Besar ultimate shrinkage
t = Umur pengujian ( hari )
ASTM = American Society for Testing and Material
PBI = Perencanaan Beton Bertulang Indonesia
ACI = American Concrete Institue
SNI = Standar Nasional Indonesia