Filler metals for welding, brazing and braze-welding
www.fsh-welding.com
Panorama
TIG, MIG, MICRO-LASER* WIRES Low-alloyed steels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4Low-alloyed aeronautical steels. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4Stainless steels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4Nickel alloys. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5Aluminium alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5Magnesium alloys. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 6Copper alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 6Hardfacing. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 6Mould hardfacing . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 6Cobalt alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7Titanium alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7Metallizing wires. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7Locking & Breaking wires. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 7
BRAZING Zinc-aluminium brazing . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 8Aluminium brazing . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 8
SCOURING FLUXES for welding, brazing and braze-welding. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9
CUSTOMISING ON DEMAND . . . . . . . . . . . . . . . . . . . . . . . . .10
TECHNICAL INFORMATION . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .11
SUMMARY
* Available as micro-laser from Ø 0,3 mm unless stated otherwise. Please consult us.
low-alloyed steels
DENOMINATION EN AWS WERKSTOFF MICRO N° C Mn Si Cr Ni Mo S P Ti Al N V TIG MIG LASER Zingafil CTA 0.08 1.15 0.40 0.10 0.10 0.01 0.01 0.01 l l l
70 S3 G2Si
A5-18 ER70S3 0.10 1.20 0.65 ≤ 0.035 ≤ 0.025
l l l
80 SB 2 CrMo1Si
A5-28 ER80SB2 1.7339 0.11 1.00 0.60 1.10 0.5
l l l
90 SB 3 CrMo1Si A5-28
ER90SB3 1.7384 0.08 1.10 0.60 2.80 1.0 l l l
CR 5 Mo 6 CrMo20
A5-9 ER502 1.7373 ≤ 0.06 0.50 0.45 5.80 0.6 l l l
classification chemical composition forrm
classification chemical composition forrm
low-alloyed aeronautical steels
*AUBERT & DUVAL steels.
DENOMINATION EN AFNOR WERKSTOFF MICRO N° C Mn Si Cr Ni Mo S P Ti Al N V TIG MIG LASER A 60 ≤ 0.12 1.00 ≤ 0.6 ≤ 0.06 ≤ 0.06 l l l
S.C.V.S.* 15 CrMoV6 15 CDV6 1.7734 ≤ 0.15 1.00 ≤ 0.2 1.40 0.95 ≤ 0.06 ≤ 0.06 0.25 l l l
B.M.S.* 8 CrMo12 8 CD12 ≤ 0.10 1.00 ≤ 1.0 3.00 0.90 ≤ 0.06 ≤ 0.06 l l l
F 66S* 25 CrMo4 25 CD4 ≤ 0.25 0.60 ≤ 0.25 1.00 < 0.3 0.23 ≤ 0.06 ≤ 0.06 l l l
* Higher Si content for MIG welding.**AUBERT & DUVAL steels.
stainless steelsclassification chemical composition forrm
DENOMINATION EN AWS WERKSTOFF MICRO 14343 AMS N° C Mn Si Cr Ni Mo Nb Cu N2 V MIG TIG LASER 307 Si 18 8 Mn ER 307 1.4370 0.09 7 ≤ 1.0 19 9 l l l
308 L* 19 9 L ER 308 L 1.4316 ≤ 0.03 1.75 ≤ 0.6 20 10 l l l 309 L* 23 12 L ER 309 L 1.4332 ≤ 0.03 1.75 ≤ 0.6 24 13 l l l
310 25 20 ER 310 1.4842 0.095 1.75 ≤ 0.6 26 20 l l l
312 29 9 ER 312 1.4337 0.12 1.75 ≤ 0.6 30 9.5 l l l
316 L* 19 12 3 L ER 316 L 1.4430 ≤ 0.03 1.75 ≤ 0.6 19 13.5 2.5 l l l
318* 19 12 3 Nb ER 318 1.4576 ≤ 0.08 1.75 ≤ 0.6 18 12 2.5 8xC/1 l l l
321 Z 19 9 Ti ER 321 < 0.08 1.75 0.48 19.5 9.75 0.75 0.75 < 0.04 Ti 9xC/1.0 l l l
347*
19 9 Nb
ER 347 1.4551 ≤ 0.06 1.75 ≤ 0.6 20 10 10xC/1 l l l AMS 5680 385 20 25 5 Cu L ER 385 1.4539 ≤ 0.015 1.25 ≤ 1.0 20 25 4.5 1.5 0.15 l l l
2209 22 9 3 NL ER 2209 1.4462 ≤ 0.02 1.3 0.5 24 8 3 0.13 l l l
410 13 ER 410 AMS 5776 1.4009 ≤ 0.10 0.55 ≤ 0.6 13 l l l
410 NiMo ER 410 NiMo 0.02 0.5 0.45 12.3 4.2 0.5 0.08 l l l
430 17 ER 430 1.4015 ≤ 0.10 ≤ 1.00 ≤ 0.75 17 l l l
52 N ≤ 0.030 1 0.5 25 9 3 1.7 0.20 l l l
17-4 Mo Z 16 5 1 0.04 0.7 0.25 16 5 1 l l l
17-4 CU Z 17 4 Cu ER 630 AMS 5825
≤ 0.05 0.5 0.5 16 5 0.2 3.5 l l l
Z 12 CNDV 12 0.12 0.7 0.5 12 3 1.5 0.3 l l l
16.8.2 16 8 2 ER 16.8.2 ≤ 0.10 1.75 0.5 16 8 2 l l l
FINOX N 155
0.10 1.5 ≤ 1 21 20 3 1 Co
0.15 w
l l l AMS 5794 19.5 2.5 Z 6 NTC 25 AMS 5804 0.03 0.15 0.25 14 25 1.2 Ti 2.25 0.28 l l l
4 77, rue de la Maïre - Z.I. Les Paluds - BP 1023 - F 13781 AUBAGNE Cedex - Tel. +33 (0)4 42 18 60 60 - Fax +33 (0)4 42 18 60 61
577, rue de la Maïre - Z.I. Les Paluds - BP 1023 - F 13781 AUBAGNE Cedex - Tel. +33 (0)4 42 18 60 60 - Fax +33 (0)4 42 18 60 61
nickel alloys
DENOMINATION AFNOR AWS A5.14 WERKSTOFF MICRO AMS N° Ni Cr Cu Mn Fe Ti Nb Mo Co Al W TIG MIG LASER Ni 059 NCD 22.16 ≈ ERNiCrMo-13 2.4607 balance 25 ≤ 0.5 ≤ 1.0 15 ≤ 0.3 0.15 l l l
Ni 60 NU 25 M ER NiCu-7 2.4377 65 balance 3.5 ≤ 2.5 2 ≤ 1 ≤ 1.25 l l l
Ni 82 NC 20 Nb
ER NiCr-3 2.4806 ≥ 67 20 3 ≤ 3 ≤ 0.75 2.5 ≤ 1 l l l
AMS 5836 Ni 90 NC 20 KTA 2.4632 balance 19 ≤ 1 ≤ 3 2.4 18 1.4 l l l
Ni 263 NCK 20 D AMS 5966 2.4650 balance 20 0.4 ≤ 0.7 2.2 5.8 20 0.4 l l l
Ni 276 NCD 16.16 Fe ER NiCrMo-4 2.4886 balance 16 ≤ 1 5 16 ≤ 2.5 4 l l l
Ni 601 NC 22 F ER NiCrFe-11 2.4626 60 23 ≤ 1 ≤ 1 balance 1.4 l l l
Ni 625 NC 22 DNb ER NiCrMo-3
AMS 5837 2.4831 ≥ 58 22 ≤ 5 ≤ 0.4 3.5 9 ≤ 0.4 l l l
Ni 718 NC 19 FeNb ER NiFeCr-2 AMS 5832
2.4667 52 19 balance 0.9 5 3 ≤ 1 ≤ 0.5 l l l
NiCr 80.20 NC 20 2.4639 ≥ 93 20 ≤ 1.2 ≤ 0.5 ≤ 1 l l l
NiTi 61 NT 3 ER Ni-1 2.4155 balance ≤ 1 ≤ 1 3 ≤ 1 ≤ 1.5 l l l
Ni W ND 24 Fe C ER NiMo-3 AMS 5786
balance 5 ≤ 1 6 24 ≤ 2.5 ≤ 1 l l l
Ni X NC 22 Fe D ER NiCrMo-2
AMS 5798 balance 22 ≤ 1 18.5 9 1.5 0.6 l l l
FENI 50 NF 45 2.4472 55 0.6 balance l l l
classification chemical composition forrm
aluminium alloysclassification chemical composition forrm
DENOMINATION AFNOR AWS A5.10 WERKSTOFF MICRO A 81331 AMS N° Mn Fe Si Mg Al Zn Cr Ti TIG MIG LASER Al 99.5 A 5 ER 1100 3.0259 0.3 0.2 ≥ 99.5 l l l
AlMg3 AG 3 ER 5654 3. 3536 0.3 0.4 0.2 3 balance ≤ 0.1 0.1 0.1 l l l
AlMg5
AG 5 ER 5356 3.3556
0.15 0.4 0.2 4.7 balance ≤ 0.1 0.15 0.15
VERITAS l l
l
accredited
AlMg4Mn
AG 4 MC ER 5183 3.3548
0.7 0.4 0.2 4.7 balance ≤ 0.1 0.1 0.1 GIAT
l l l accredited
AlCu6
AU 6 ER 2319
0.3 0.3 0.2 balance ≤ 0.1 0.15 Cu
l l l AMS 4191 6.3 AlMg4Z2 AG 4Z2 0.4 0.4 0.1 4 balance 2 l l
AlSi7G0.6
AS 7 G0.6
ER 357 AMS 4246
0.1 7 0.55 balance 0.1 l l l
AlSi10
AS 5
ER 4043 AMS 4190
3.2245
0.4 5.2 balance ≤ 0.1
l l l
AlSi12
AS 12
ER 4047 AMS 4185
3.2585 0.1 0.5 12 balance ≤ 0.1 l l l
6
magnesium alloysclassification chemical composition form
DENOMINATION AFNOR AMS AWS MICRO A 5-19 AL Zn Mg Mn Zr Rare Earth Be TIG MIG LASER AZ 92 A MA 9 4395 AZ 92 A 8.3/9.7 1.7/2.3 Balance 0.15/0.5 0.0002/0.0008 l l l
EZ 33 A MZ 3 4396 EZ 33 A 2/3 Balance 0.4/1 2.5/4 l l l
copper alloys
hardfacing
classification chemical composition
DENOMINATION EN AWS WERKSTOFF MICRO A5.7 N° Fe Si Mn Sn Al Ni Cu Ag P Ti TIG MIG LASER Cu110 CuSn1 ER Cu 2.1006 0.2 0.4 0.9 balance l l l
CuSi3 CuSi3 ER CuSi-A 2.1461 3 1 balance l l l
CuAg CuAg1 2.1211
98.5 1
l l l
CuAl9 CuAl9Fe ER CuAI-A2 ≤ 1.5 9 balance l l l
CuAl8 CuAl8 ER CuAI-A1 2.0921 0.2 0.4 8 balance l l l
CuAl9Mn CuAl9MnNiFe 1.3 ≤ 1.5 8.5 2.3 balance l l l
Cu118 CuMn12AlNiFe ER CuMnNiAI 2.1368 1.5 12 7 2 balance l l l
CuAl9Ni CuAl9NiFeMn ER CuNiAI 2.0927 3 1.5 8.75 4.5 balance l l l
Cu114 CuSn6 ER CuSn-A 2.1022 6 ≥ 93 0.2 l l l
CuSn8 CuSn8 2.1025 8 balance l l l
CuNi30 CuNi30 ER CuNi 2.0837 0.6 ≤ 1 30 balance 0.4 l l l
CuNi90.10 CuNi10Fe 2.0873 1.0 11 balance 0.4 l l l
1733 W
MICRODENOMINATION EN 14700 WERKSTOFF N° C Si Mn Cr Al Ti TIG MIG LASER
R 250 B SFe1 1.8401 0.3 0.5 1.1 1.0 0.1 0.2 l l
R 600 B SFe6 1.4718 0.45 3.0 0.4 9.0 l l
classification chemical composition applications form
Hardfacing of rails, shafts, rollers, HB 225-275. Easy to use. Hardfacing of tools for civil engineering equipment such as crunching hammers, chain links, excavators, etc.
hardfacing for toolingclassification base metal applications form
*AUBERT & DUVAL steels.
77, rue de la Maïre - Z.I. Les Paluds - BP 1023 - F 13781 AUBAGNE Cedex - Tel. +33 (0)4 42 18 60 60 - Fax +33 (0)4 42 18 60 61
form
MICRODENOMINATION EN TIG MIG LASER HBCrMo17.1 X40CrMo17.1 Z55CrNiMoV12 - Z55Cr14 - Z160 CrMoV12......... l l l
HBC 82 100 MoCrVW8 85 W MoCrV 6.5.4.2 l l
CuBe2 Cu Be 2 Cu Be 2 l l
819 B.S.* 36NiCrMo16 45 NiCrMo18 - 60 NiCrMo11 - 36 NiCrMo16 - 40 NiCrMo20 - 40 NiCrMo16........
l l
l
B.M.S* 8CrMo12 30 CrMoV12 - 55 NiCrMoV7 - 55 CrNiMo4.......... l l l
MARVAL 18 S* X2NiCoMoTi18-8 X2NiCoMo18 - X35CrMoV5 - X38CrMoV5...... l l l
MARVAL X12 S* X1CrNiMoAlTi12.9 X40CrMo15 - X1CrNiMo12.9 - X1CrNiMoAlTi12.10......... l l l
MV5S* X50CrMoWV5 X50CrMoWV5 - X100CrMoV5...... l l l
S.M.V3S* X38CrMoV5 X38CrMoV5 - X32MoCrV2S - X30CrMoV12 - X40CrMoV12....... l l l
X.S.H.S* CoCr20WNi X38 Cr MoV5 - X38 CrMoV5.3......... l l l
Tools for cold working.
Tools for cold working.
Welding & hardfacing of copper-berylium.
Bolster for forcing & stamping. Moulds for plastic moulds.
Moulds for plastics.
Boring tools, cutting-press blades, injections moulds for light metals & plastics.
Moulds for plastics.
Moulds & cold working tools.
Bolster for piercing & stamping, extrusion dies, injection moulds for light alloys.
Bolsters & inserts.
777, rue de la Maïre - Z.I. Les Paluds - BP 1023 - F 13781 AUBAGNE Cedex - Tel. +33 (0)4 42 18 60 60 - Fax +33 (0)4 42 18 60 61
cobalt alloysclassification chemical composition form
MICRODENOMINATION AFNOR AMS C Fe Cr Ni W Co Si Mn La V Mo TIG MIG LASER Co 25 KC 20 WN 5796 0.1 ≤ 3 20 10 15 balance 1 1.5 l l l
Co 188 KCN 22 W 5801 0.1 ≤ 3 22 22 14 balance 0.35 1.25 0.04 l l l
Co 694 KC 28 W 0.85 ≤ 3 27 5 20 balance ≤ 1 ≤ 1 1 l
Co T 800
KD 28 C 0.01 18
+Fe balance 3 29
2.5 l
Co 1 KC 29 W13 2.5 3 29.5 3 12.5 balance 2 1 1 l
Co 6 KC 29 W5 5788 1.15 3 29 3 4.5 balance 2 1 1 l
Co 12 KC 29 W9 1.45 3 29 3 8.3 balance 2 1 1 l l
Co 21 KC 27 D 5385 0.25 3 27 2.75 balance 1 1 5.5 l l l
Co 31 KC 26 NW 5789 0.5 2 25.5 10.5 7.5 balance 1 1 l
Co 414 KC 29 NW 0.12 1 29.5 10.5 7 balance 0.75 0.7 l l l
Co 918
KC 20 NTa
0.07 20 20 balance 0.2 0.2
Ta l l l
7.5
titanium alloysclassification chemical composition form
DENOMINATION ASTM AWS A5.16 WERKSTOFF MICRO AMS N° C N2 H2 O2 Fe Ti Pd Al V Sn TIG MIG LASER
T 40
Grade 2 ER TI-2
AMS 4951 3.7035
≤ 0.05 ≤ 0.02 ≤ 0.008 ≤ 0.10 ≤ 0.20 balance l l l
T 60 Grade 4 ER Ti-4 3. 7065 ≤ 0.05 ≤ 0.02 ≤ 0.008 ≤ 0.20 ≤ 0.30 balance l l T Pd 0,2 Grade 7 ER Ti-0.2 Pd ≤ 0.05 ≤ 0.02 ≤ 0.008 ≤ 0.15 ≤ 0.25 balance 0.20 l l
TA 6 V 4*
Grade 5 ER Ti-5 AMS 4954
3.7165 ≤ 0.05 ≤ 0.02 ≤ 0.008 ≤ 0.15 ≤ 0.25 balance 6 6 l l l
* TA6V4 can also be delivered as ELI (Extra Low Interstitial)
DENOMINATION AFNOR WERKSTOFF N° Si Fe Cu Mn Mg Zn Ti Al MV A5 1050 A 3.0255 ≤ 0.3 ≤ 0.4 ≤ 0.05 ≤ 0.05 ≤ 0.05 ≤ 0.07 ≤ 0.05 ≥ 99.5 MV A8 1080 A 3.0285 ≤ 0.15 ≤ 0.15 ≤ 0.03 ≤ 0.02 ≤ 0.02 ≤ 0.06 ≤ 0.02 ≥ 99.8 MV A99.90 1090 A 3.0305 ≤ 0.06 ≤ 0.05 ≤ 0.01 ≤ 0.01 ≤ 0.01 ≤ 0.04 ≤ 0.006 ≥ 99.9 MV A99.98 1098 3.0385 ≤ 0.01 ≤ 0.006 ≤ 0.003 ≤ 0.015 ≤ 0.003 ≥ 99.98 MV A99.99 1199 3.0400 ≤ 0.06 ≤ 0.005 ≤ 0.005 ≤ 0.005 ≤ 0.002 ≥ 99.99
metallizing wiresclassification chemical composition
DENOMINATION NFL 23320 AMS RE A5 (1050) Pur aluminium Used for holding pieces during surface treatment. EC A5 Used for holding pieces during surface treatment. RE UZ40 Used for holding pieces during surface treatment. Z 2 CN 18.10 23320 CA 5697 Ready to use locking wire for aeronautical industry. Z 6 CNT 18.10 23320 VQ 5689 Ready to use locking wire for aeronautical industry. NC 15 Fe 23320 TC 5687 Ready to use locking wire for aeronautical industry.
locking wires & breaking wiresclassification applications
8
zinc-aluminium brazing
aluminium brazing
denomination
denomination
420° - 450°C
590° - 610°C
580°C
440° - 460°C
600° - 620°C
TBW ZINAL 4
TBW HARASIL 7.5
ZINAL 30 NCS
TBW HARASIL 10
TBW HARASIL 12
fusion temperature according to NF A 81-362
fusion temperature according to NF A 81-362
form
TBW / FCW Preforms
l l
l l
form
TBW Preforms
l l
l l
l l
chemical composition
Zn Al
98 2
85 15
chemical composition
Zn Al
balance 7,5
balance 10
balance 12
*TBW : Tubular brazing wire.
77, rue de la Maïre - Z.I. Les Paluds - BP 1023 - F 13781 AUBAGNE Cedex - Tel. +33 (0)4 42 18 60 60 - Fax +33 (0)4 42 18 60 61
977, rue de la Maïre - Z.I. Les Paluds - BP 1023 - F 13781 AUBAGNE Cedex - Tel. +33 (0)4 42 18 60 60 - Fax +33 (0)4 42 18 60 61
scouring flux for welding, brazing & flame-brazingDENOMINATION
recommended filler metalsfusion point
references applications
HARAKIRI ROSE
SCOURING FLUX FOR FLAME WELDING
Al 99.5%658°C NF EN 1045 Ensures exceptional ease for welding aluminium with aluminium-alloys, except AlMg
(for which, use MALG-HARA). Universally reknowned
HARA-CUIVRECu 99.9 %
1083°C NA For flame-brazing of copper, bronze-tin, and high-speed brazing of steel reinforce-ments on semi-hard steel tools.
HARA-FONTECast Iron1200°C NA For flame-brazing of cast iron. Ensures perfect scouring of parts to be welded while not
hardening cast iron. An energetic remover of metal oxides, particularly iron oxide.
MALG-HARAAlMg3, AlMg5, AlMg4Mn,
AlMg5Mn, AlSi7G0.6610° - 650°C
NF EN 1045Special flux for light alloys containing magnesium. Simultaneously attacks & dissolves alumina, magnesia and their combinations. Used as powder or as paste. The only flux used in aerospace construction for AlMg5.
FLUX ODAL
SCOURING FLUX FOR BRAZE-WELDING
AlSi5, AlSi10, AlSi12520° - 550°C NF EN 1045 FL 10 Flux for aluminium alloys except aluminium-magnesium alloys (for which, use MALG
HARA). Exceptional wetting with energetic deoxidising action.
ALUNOX 13 LCAlSi10, AlSi12520° - 540°C NF EN 1045
Neutral & non-corrosive flux for manual braze-welding and automatic brazing of aluminium to aluminium or to stainless steel and copper. Prevents in-depth attack of parts in the event of overheating.
MALG ODALAlSi10, AlSi12520° - 540°C FD/4.F.1, NF EN 1045 Scouring flux for braze-welding of aluminium-magnesium alloys. Wets perfectly. Often
used in food & dairy industries.
HARAKIRI BLEUE
SCOURING FLUX FOR SOFT-BRAZING
AlSi12, ZINAL 4,ZINAL 30 NF EN 1045 Flux for strong & soft brazing of aluminium alloys, except aluminium-magnesium (for
which, use BRAZ-ALMAG or MALG ODAL). Exceptional scouring and wetting action.
BRAZ-ALMAG ZINAL 4, ZINAL 30 NF EN 1045 Flux for brazing aluminium-magnesium alloys. Excellent scouring and wetting action on AlMg3 and AlMg5.
HARA-FLUX Tin-Lead Brazing NALiquid flux for soft brazing of all ferrous and copper metals, or parent metals of Zinc, Lead, Tin, etc. except light alloys. Also suitable for low temperature brazing of bronze-aluminium and chrome-nickel stainless steels.
ALUNOX NCS ZINAL 4, ZINAL 30 NA Flux brazing of aluminium-aluminium alloys or with stainless steel. Active temperature is about 15°C lower than those of ALUNOX NC and ALUNOX 13 LC.
BORINOX
SCOURING FLUX FOR SILVER BRAZING
Brazing of Cadmium-bearing Silver alloys, with active temperatures below
730°C : - OD 90-4- OD 80-4- OD 60-4- OD 100-4
FD/4.B.1, NF EN 1045Non-brilliant, general purpose flux for silver brazing, with active temperature between 590°-730°C. Recommended for stainless steels, copper & brass. Excellent wetting action, does not overheat. Employed dry or diluted in water.
BORINOX PUR FD/4.S.1, NF EN 1046 Controlled grain-size of BORINOX powder for high-frequency brazing and delicate jobs, i.e. aerospace, pipes & fittings, high-pressure joints, etc.
BORINOX PATE FD/4.B.3, NF EN 1047 BORINOX in paste-form, ready to use. Very effective in small amounts. Recommended on copper pipes.
FLUX-BORE
SCOURING FLUX FOR SILVER BRAZING & BRAZE-WELDING ALLOYS
Brazing of Cadmium-free Silver alloys, with active
temperature above 730°C :brass & nickel silver
- BRASOL 71- BRASOL 10
FD/7.S.1, NF EN 1045Flux for strong brazing (above 730°C) and braze-welding of all copper and ferrous metals. Ensures excellent wetting capability and prefect bonding. Excellent results with tempered steels. Deformations reduced to a minimum. Can be employed as powder or in water-diluted form. Perfect adhesion to preheated strips.
NEO-FLUX FD/7.A.4, NF EN 1045 Washing product for braze-welding of all copper and ferrous metals. Assures better wetting and penetration than FLUX-BORE.
SOUDO-BRAZINE FD/7.G.1, NF EN 1045 Flux for braze-welding of iron castings, as well as mixed constructions, i.e. steel, cop-per, brass, bronze. Suitability for machining, regardless of assembly type.
10
customising on demandWe also offer our clients the possibility to customise their products:
- Straightening : straight lengths of most types of wires between Ø 6.0 mm and Ø 0.3 mm.
- Spooling : on D300, D200 and D100 spools, also available are K400, K500 and SD400 type spools.
- Drawing : from Ø 5.5 mm up to Ø 0.3 mm, on most steels, stainless steels, nickel alloys, copper alloys, aluminium alloys and cobalt alloys.
- Pickling : chemical or mechanical.
- Pre-forming.
- Marking : either by stamping or flagging on one end of the rod.
- Packaging.
- Heat treatment : Ar, H2, water.
11
technical information ALLOYS ALUMINIUM TITANIUM STAINLESS STEEL COPPER d : 2,7 g/cm3 d : 4,5 g/cm3 d : 7,85 g/cm3 d : 8,9 g/cm3
Ø g/m m/kg g/m m/kg g/m m/kg g/m m/kg 0.5 1.54 649 0.6 2.22 450 0.8 1.36 735 2.26 442 3.94 254 4.47 224 1.0 2.12 472 3.53 283 6.16 162 6.98 143 1.2 3.05 328 5.08 197 8.87 113 10.06 100 1.6 5.42 184 9.04 111 15.77 63 17.88 56 2.0 8.48 118 14.13 71 24.65 41 27.95 36 2.4 12.21 82 20.34 49 35.48 28 40.23 25 3.0 19.07 52 31.79 31 55.46 18 62.88 16 3.2 21.70 46 36.17 28 63.10 16 71.54 14 4.0 33.91 29 56.52 18 98.59 10 111.78 9 5.0 52.99 19 88.31 11 154.06 7 174.66 6 6.0 76.30 13 7.0 103.85 10 8.0 135.65 7
d : density g/m : gram/meter m/kg : meter/kilogram
Ø in mm Ø in inches (fractions) Ø in inches
0.6 1/44 0.0236
0.8 1/32 0.0315
1.0 1/26 0.0393
1.2 3/64 0.0472
1.6 1/16 0.0629
2.0 5/64 0.0781
2.4 3/32 0.0945
3.2 1/8 0.1259
4.0 5/32 0.1574
1” = 1 inch = 25,4 mm
77, rue de la Maïre - Z.I. Les Paluds - BP 1023 - F 13781 AUBAGNE Cedex - Tel. +33 (0)4 42 18 60 60 - Fax +33 (0)4 42 18 60 61
FP Soudage (Fil Pour Soudage) was founded in 1974 to draw special filler metals from major foun-dries.
The company soon diversified into drawing of aluminium, copper, titanium and other metals for indus-tries pertaining to nuclear, energy, aeronautical and the tooling industry in particular.
In 1993, FP Soudage bought over the company Paul ODAM, which invents brazing fluxes. This com-pany was the first to make available a flux enabling flame-brazing of aluminium.
In 2000, FP Soudage obtained exclusive manufacturing rights to produce Aubert&Duval hardfacing steels for diameters of 4.0 mm and below.
In 2003, FP Soudage was bought by the FSH WELDING GROUP, integrating the company’s know-how into the group’s force and organization.
FP Soudage is certified ISO 9001:2000 and ISO 9100, accredited to supply to the nuclear and aeronau-tical industries, and ensuring high quality products and services.
Its experienced team of technical-salespeople, along with an exhaustive range of welding and brazing products, guarantees full service from conception to supply of the right product to a wide variety of applications.
Success at the heart of a
bi-centenary group
FSH WELDING GROUP Head Office.
77, rue de la Maïre - Z.I. Les PaludsBP 1023 - F 13781 AUBAGNE CedexTel. +33 (0)4 42 18 60 60Fax +33 (0)4 42 18 60 61Internet : www.fsh-welding.comE-mail : [email protected]
I S O 9 0 0 1VERSION 2000
EURO
SAG
A 3
3 (0
)3 8
4 21
01
12 -
12/
08