Transcript of Making of Rolled Threaded Pipes
www.panchinafs.com
GREEN SAFE STEEL NIPPLES
An Brief Introduction to
Rolled Pipe Threads on Galvanized and Black Carbon Steel Pipe
SHANGHAI PAN-CHINA FASTENING SYSTEM CO.,LTD CHITHREAD ROLLING TECHNOLOGY CO., LTD
www.panchinafs.com
By 2, 3 or more rollers, at room temperature, to roll the pipe placed in the rollers’ central axle into the NPT、BSPT or other pipe thread. It is a kind of mature cold forming, a no- material-cut-away technology, widely used in modern industry. But IT has been specially developed by our Chinese Patent since 2003.
Rolling Thread Technology Via. Cutting
Rolling Thread Technology
What is the
Cutting Thread Technology
? is
www.panchinafs.com
1. Perfect Mating Between Male & Female Thread Increases Leak Tightness Greatly 100% Perfect Thread Teeth Profile – Excellent Teeth Surface Enhance Mating – Zinc Coating Kept – More “Thickness” of Pipe.
2. Excellent Rust-Resistance on Rolled Thread Pipe 1.Original hot-dip zinc coating of the galvanized pipe remains intact, and is not cut away as with lathe cut ones. 2.The density of the rolled thread pipe is increased greatly and makes, at least, the “same thickness” as the original pipe itself, and forms an anti-oxidization layer of high metallic density against rusty.
3. Pipe Material Not Cut Away Makes Thread Mechanical Connection Much Better The mechanical properties of the pipe thread are greatly improved as no material is cut away and the weight per unit length of
rolled thread pipe remains unchanged, and further more the metal density is increased.
I. Rolled Thread Nipples Are Safe Steel Nipples
PCFS – CHITHREAD Green Safe Steel Nipples - Rolled Thread Pipe Steel Nipples
www.panchinafs.com
Perfect Thread – Excellent Surface Enhance Mating – Zinc Coating Kept – More “Thickness”
1. No Leaking Point Any More
Galvanized Pipe Rolled Thread Nipple Connection with Standard Cast Iron Coupling popular in the Market
www.panchinafs.com
1.1.1 . Perfect Thread: 100% perfect teeth profile (geometry size), produced by long-life rollers (tools), fundamentally guarantees the excellent integrity with female cut thread. The cut teeth, by easy- worn knife (tools), varies in profile time to time, can’t guarantee it. 1.1.2 . Excellent Surface Enhance Mating: Surface roughness of rolled thread is improved dramatically by 5 – 7 levels to Ra < 0.4 due to the thread to be formed by the roller rolling on the pipe, and the cut thread is by, knifing in the pipe, Ra > 3.2. Rolling makes much better mating between the male and the female thread. 1.1.3 . Zinc Coating Kept: Rolled thread of galvanized pipe is sealed mainly by original zinc coating which is metallic layer (hard) sealing & very good for suffering the weight of the pipe, plus traditional tape(soft) sealing. And the cut thread is sealed 100% by tapes(soft) which are un- appropriate for suffering the weight and can’t be 100% sure for lasting a period of years. 1.1.4. More “Thickness” of The Pipe: As no material is cut away, the weight per unit length remains same, plus a rolled teeth surface is much harder, those bring improvement in mechanical properties.
1.1 Perfect Thread - Enhance Mating – Zinc Coating Kept – More “Thickness”
Rolled Thread Cut Thread
www.panchinafs.com
--- The pressure capacity of rolled thread nipple connection without any sealant, after fracture, is up to 17Kgs
1.2 Factory Lab Max. Working Pressure Test
Water Pressure C
apacity Test
After tensile fracture test,
the pressure capacity of
the rolled thread nipple
connection is up to 17kgs.
After bend fracture test,
the pressure capacity of
the rolled thread nipple
connection is up to 16kgs.
Stainless steel 304 coupling connection with rolled thread nipples without any sealant & tape.
The broken end is sealed by bolt fastened with sealing tape.
www.panchinafs.com
1.3 Factory Lab Temperature Test from - 20℃ to + 175℃
The test procedure: Fill in the gas into the rolled thread nipple
connection of piping system without any sealing tapes at 16Kgs pressure for 24 hrs to check the
changing of the pressure under condition that the temperature was varied from - 20℃ to + 175℃.
The result: No pressure drops down during
& after the 24 hr. continuous test.
-- The pressure capacity of rolled thread nipple connection without any sealant is up to 16Kgs
without any sealing tapes
www.panchinafs.com
The Safety Of Rolled Thread Connection Is Much Better Than Traditional Cut Thread Connection, and its leak tightness is 100% Assured.
Conclusion: No Leaking Point Any More If female good
Practical、Theory and Test have proven that there is
no leaking point any more in rolled thread cconnection if female thread is qualified.
www.panchinafs.com
2. Rust Resistance of Rolled Thread Greatly Improved
1.Original hot-dip zinc coating remains intact. 2.After rolling thread, no metal material is cut away, the weight per unit length is as same as the original pipe, and further more it increases the metal pipe density on thread proportion accordingly. High density metal layer forms a metallic anti-oxidization layer against rusty.
The Rolling Thread Technology improves the rust resistance
on thread proportion very greatly.
The metal grain is not cut off by rolling
The metal grain is cut off by cutting
www.panchinafs.com
After 130hr. salt acid spray
1. Steel Brand:
Tianjin Youfa DN15 Q195
2. Product: Rolled Thread Galvanized
Welded Steel Nipples.
3. Testing in 50g/L±5g/L Nacl. solution.
4. There is no any corrosion spot appeared after salt acid
spray on the rolled galvanized steel nipples up to 100 hrs.
continuously.
2.1. MA & ML SALT ACID SPRAY TEST ON ROLLED NIPPLES
MA & ML Test Report on July 18th, 2008.
After 130 hr. continuous salt acid spray, corrosion spots
appear both on thread & pipe.
www.panchinafs.com
2.2. MA SALT ACID SPRAY TEST ON ROLLED & CUT THREAD
Rolled Thread
Cut Thread
Painted Cut Thread
Before Salt Acid Spray Test
Rolled Thread
After Salt Acid
Spray 175hrs.
Cut Thread
After Salt Acid
Spray 5hrs.
Painted Cut Thread
After Salt Acid
Spray 24hrs.
After Salt Acid Spray Test
Rolling & cutting pipe thread nipples BSP on galvanized steel pipe DN32 of Shanghai Yinhe.
Corrosion spots appear on rolled thread nipple & cut one after salt acid spray 175 hrs. vs. 5 hrs.
Rust-resistance of rolled pipe nipple is 35 times better than cut thread.
MA Salt Acid Spray Report 11-03-2010
www.panchinafs.com
Conclusion: Rust Resistance Greatly Improved By Rolling
Original Zinc Coating remains intact .
After the zinc coating has been rusted off, the higher density, instead of cut-thinner-wall-thickness, of the pipe thread still owns stronger rust-resistance.
1 2
Total in all, the rust-resistance of the rolled thread
pipe nipples is 40 times higher than cut thread pipe nipples.
Plus
Cut Thread Nipple
Rolled Thread Nipple
Not-Cut-Away Metal to be rolled into Higher Density Metal Pipe.
Cut-Thinner-Wall-Thickness by Cut Thread makes the pipe 50% weak than original pipe.
+
www.panchinafs.com
3. Thread Mechanical Connection Greatly Improved
Continuous line-like kept ,instead of being cut off, and further more the metal grains are compressed & are more close to each other.
The pipe becomes harder by Rolling Thread Technology instead of thinner by cutting.
1.Tensile strength by 150% -1 80%; 2.Flexural strength by 150% - 170%; 3.Shear strength by 140% - 170%; 4.Surface hardness by 130%; 5.Fatigue strength by 250% - 400%. These percentage will be varied on different pipe thickness, size, material & etc.
Continuous Grain
Cut Grain Off
The metallograph of Micro Fiber of Pipe Metal Grain Before Rolling. Grade 6
The metallograph of Micro Fiber of Pipe Metal Grain After Rolling. Grade 8.5
It improves the organization of original metal fiber grain allocation & makes the pipe much stronger.
www.panchinafs.com
3.1 Rolled Thread Don’t Loss the Material for Teeth Profile and Taper
Teeth height + Taper are cut away by cutting process.
The cold rolling process doesn’t cut the metal fiber off, instead the rolling compresses the metal fiber and make it stronger. Therefore the strength of tension, bend, shear and fatigue are increased, as well as the surface hardness. Chi-Thread nipples act very good mechanical connection performance, and could protect the piping system well from subsidence, drift and lateral displacement & etc. under stress.
Mechanical properties of the cut thread is lower than the original pipe by 30% - 50%.
Cut thread Rolled thread
www.panchinafs.com
3.2 Not Cut-Away-Material Thread & Its Continuous Grain
After rolling it hardens the teeth bottom by cold compressing micro solid metal fiber from grade 6 to grade 8.5.
Surface of teeth becomes m
ore harder. .
Thicker, harder & more solid
Continuous Grain
Cut Grain Off
www.panchinafs.com
3.3 Mechanical Property Performance Test
Test Material : Pipe Material Brand: Tianjin Youfa, China; Galvanized Steel Pipe: DN15, Q195; Wall-Thickness: 2.2mm; With Stainless Steel 304 Pipe Coupling.
Test Requirement: Rolled Thread Nipples connection with stainless Steel 304 pipe coupling without any sealing tapes. Turnaround 3 circles by hand, and turnaround 2 circles by tool to fasten the connection.
Experimental Basis: 1. For Tensile Strength Test: <<GB/T228>> Tensile Strength Test Methods for Metal Material at Room Temperature; 2. For Bend Test: <<GB/T244>> Bend Test Methods for Metal Pipe.
Test Institute: Shanghai Quality Supervision & Inspection Station Of Building Materials & Components.
Pull Off Two Rolled Thread Nipples until one of carbon steel nipples is fractured.
Bending Two Rolled Thread Nipples until one of carbon steel nipples is fractured.
Force
Force
Force
Tensile Strength Test
Bend Test
www.panchinafs.com
3. 4 AL & MA Mechanical Property Performance Test Report
After Mechanical Fracture
Test at 54 kN & 70°
AL & MA Test Report
One of the two rolled thread nipples is fractured, as showed in yellow circle,
when the tensile load 54.2kN was applied.
The other of the two rolled thread
nipples is still connected well with the stainless steel 304 coupling.
One of the two rolled thread nipples is fractured, as showed in yellow circle, when the bend test at 70° (d=6a ).
The other of the two rolled thread
nipples is still connected well with the stainless steel 304 coupling.
54.2kN
70° (d=6a )
Broken Nipple
Broken Nipple
Without Any Sealing Tapes in the Connection between the
Rolled Thread Nipple & Coupling.
Un-Broken Nipple
www.panchinafs.com
3.5 Working Pressure Test after Fracture in Tensile and Bend Test
After Tensile Fracture Test
it still can afford 17kgs pressure .
After Bend Fracture Test
It still can afford 16kgs pressure.
One end of the broken nipple is sealed by a fastener with enough sealing tape to be sure no leaking from this end. And filling in water to the pipe from the one end of un-broken nipple up to a certain working pressure. It shows that both coupling connection with broke & un-broken nipples, without any sealing tapes, have a no leaking at 17 kgs for the one of tensile fracture test and 16 kgs for the bend fracture test respectively.
No leaking at both rolled thread nipple connected with the coupling either for tensile fracture or bend fracture test
Broken Nipple Broken Nipple
Un-broken Nipple Un-broken Nipple
No tapes No tapes
www.panchinafs.com
3.6 Mechanical Properties Comparison Among Pipe, Cut & Rolled Thread
Com
parison Basis <<GB / T3091-2008>>
<<GB/T3091-2008>>
Welded Pipe For Low -
Pressure Fluid Flow
Transportation
Cut Thread Bend
(Earthquake) Test made by
National Association of
Manufacturers, USA.
Items
Objective
Tensile Fracture
Load (kN)
Bend Fracture(Degree)
Test Institution
Pipe 41.65 90°
Shanghai Quality Supervision &
Inspection Station Of Building Materials
& Components.
Rolled Thread Nipples
54.2 70°
Shanghai Quality
Supervision & Inspection Station
Of Building Materials & Components.
Cut Thread Nipples
10.1°, 12.3°, 14.4°.
National Association
of Manufacturers, USA
www.panchinafs.com
3.7 Rolled Thread Nipples Almost Double The Maximum Working Pressure
The calculations are quoted from the Wheatland Tube Company U.S.A. and it shows that the pipe after cutting thread significantly decreases the max. working pressure by 32% - 57% on different size and wall thickness of the welded pipe. In other word, as per previous information in this PPT, the pipe after rolling thread will not reduces the max. working pressure, and in another word, under same condition, we can save a huge (12% up) pipe material if we use the rolled thread on the pipe.
www.panchinafs.com
3.8 Sch.40 Pipe May Replace Sch.80 By Rolling Thread Technology
Take the ¾” DN20 Sch.80 Cutting Pipe Thread as an example: The ¾” NPT teeth height is 0.057inch(1.45mm) + The taper (1:16) loss is from0.006 – 0.021inch, therefore after cutting, the original nominal wall thickness was cut off and varies from the min. 0.076inch / 1.93mm (0.154 – 0.057 – 0.021) to the thickest 0.091inch / 2.295mm (0.154 – 0.057 – 0.006). The thickest after cut thread is only 0.091inch (2.295mm), 19.47% less than the Sch.40 one and the max. working pressure is only 1150 psi as per the calculations last page. Take the ¾” DN20 Sch.40 Rolled Pipe Thread as comparison: The weight (mass) per unit length after rolling (the wall thickness is rolled and compressed) is same as the plain end pipe itself. i.e. the max. working pressure is 1450 psi as per the calculations from Wheatland Tube Co., last page. The max. working pressure of rolled thread ¾” DN20Sch40 pipe or nipple is 26% higher than the cut one of Sch80. And at meantime we can easily get the material saved by 0.35 lb/ft ( =1.48 -1.13 ) or 24% ( = 0.35 / 1.48 ).
Pipe Size (inches)
Outside Diameter (inches)
Identification
Wall Thickness
- t - (inches)
Inside Diameter
- d - (inches)
Carbon Steel
Nominal Weight (Mass) Per Unit
Length Plain End (lb/ft) Iron Pipe
Size Schedule
No.
3/4 1.050 STD XS
40 80
1.13(1.69kg/m) 1.48(2.20kg/m)
.113
.154 .824 .742
¾” NPT Cut Thread Steel Nipple Sch. 80
www.panchinafs.com
3.9 Saving Material on Different Size by Sch.40 Replacing Sch. 80
GREEN CONCLSION: If rolling thread on the pipe, ¾” SCH.40 pipe
can replace ¾” SCH.80 pipe with 26% higher
max. working pressure as per following table.
The Cut Loss of Pipe Material NPT Thread Sch.80 vs.Sch.40 Rolled Thread
NPS DN Schedule Nominal Wall
Thickness Teeth Height Max. Taper Cut Loss
Min. Taper Cut Loss
Thinnest Wall Thickness After Cut
Thread
Thickest Wall Thickness After Cut
Thread
Nominal Weight (Mass) Per Unit
Length
Rolled Thread on Sch.40 Better
Than Cut Thread On Sch.80 In
Pressure Capacity
(mm) (Inch) (mm) (Inch) (mm) (Inch) (mm) (Inch) (mm) (Inch) (mm) (Inch) (kg/m) (lb/ft)
1/2 15 Sch.40 2.77 0.109 1.451 0.057 1.27 0.85
25% Sch.80 3.73 0.147 1.451 0.057 0.517 0.020 0.164 0.006 1.762 0.070 2.115 0.084
3/4 20 Sch.40 2.87 0.113 1.451 0.057 1.69 1.13
26% Sch.80 3.91 0.154 1.451 0.057 0.529 0.021 0.164 0.006 1.930 0.076 2.295 0.091
1 25 Sch.40 3.38 0.133 1.767 0.070 2.50 1.68
29% Sch.80 4.55 0.179 1.767 0.070 0.636 0.025 0.199 0.008 2.147 0.084 2.584 0.101
1-1/4 32 Sch.40 3.56 0.140 1.767 0.070 3.39 2.27
22% Sch.80 4.85 0.191 1.767 0.070 0.649 0.026 0.199 0.008 2.434 0.095 2.884 0.113
1-1/2 40 Sch.40 3.68 0.145 1.767 0.070 4.05 2.72
18% Sch.80 5.08 0.200 1.767 0.070 0.649 0.026 0.199 0.008 2.664 0.104 3.114 0.122
2 50 Sch.40 3.91 0.154 1.767 0.070 5.44 3.66
6% Sch.80 5.54 0.218 1.767 0.070 0.659 0.026 0.199 0.008 3.114 0.122 3.574 0.140
2-1/2 65 Sch.40 5.16 0.203 2.540 0.100 8.63 5.80
20% Sch.80 7.01 0.276 2.540 0.100 0.902 0.036 0.286 0.011 3.568 0.140 4.184 0.165
3 80 Sch.40 5.49 0.216 2.540 0.100 11.29 7.58
14% Sch.80 7.62 0.300 2.540 0.100 0.958 0.038 0.286 0.011 4.122 0.162 4.794 0.189
3-1/2 90 Sch.40 5.74 0.226 2.540 0.100 13.57 9.12
8% Sch.80 8.08 0.318 2.540 0.100 0.994 0.039 0.286 0.011 4.546 0.179 5.254 0.207
4 100 Sch.40 6.02 0.237 2.540 0.100 16.07 10.80
Same Sch.80 8.56 0.337 2.540 0.100 1.009 0.040 0.286 0.011 5.011 0.197 5.734 0.226
www.panchinafs.com
1. Minimizing the Leakage in Rolled Thread Nipple Connection.
2. For Galvanized Pipes and Nipples, Original Zinc Coating remains
Intact &, at meantime, Strengthen the Metal Protective Layer.
3. The Performance of Mechanical Connection Greatly Increased.
Conclusion: A Safe Pipe Connection Technology - Rolled Thread
www.panchinafs.com
II. Rolled Thread Nipples Are Green Steel Nipples
Minimizing possibilities of the leaking in the thread connection of pipe network;
Saving valuable natural gas, water resources & etc.;
Saving valuable steel material & saving the sealant & tapes in installation;
Create a friendly environment for workers both in production and in installation;
Further enhance the city safety.
www.panchinafs.com
Much improving in quality of piping network installation and safety
Saving Both in Production and Installation
MANUFACTURING No metal waste scraps is from rolling thread, material saving; Production environment is clear and friendly;
INSTALLATION ON SITE More Safety; Easy & convenient tightening; 50% - 70% saving of sealant and tapes; A trial test of piping system 100% successful pass in 1st time; No re-call work; Over 50% efficiency up in installation; Daily maintenance on thread connection of piping system zero.
& saving a lot of material and labor.
www.panchinafs.com
Shanghai Pan-China Fastening System Co., Ltd. Chi-Thread Rolling Technology Co., Ltd.
Room502, Nr.1122, XinJinQiao Road, Shanghai, China 201206 Tel: +86-21-61462100 Fax: +86-21-61462118 [email protected]
Limbiate Italy Mississauga, Ontario, Canada 1307 Souter Dr. Troy, MI, USA Trigolo, CR, Italy
Creating Value Together with You
www.panchinafs.com
Shanghai Pan-China Fastening System Co., Ltd. Chi-Thread Rolling Technology Co., Ltd.
Room502, Nr.1122, XinJinQiao Road, Shanghai, China 201206 Tel: +86-21-61462100 Fax: +86-21-61462118 [email protected]
In 2009, Chi-Thread Rolling Technology Co., Ltd was found to focus on developing new applications of this Chinese Rolling Thread Technology in many industry sectors in order to benefit our human being.
Creating Value Together with You
www.panchinafs.com
Shanghai Pan-China Fastening System Co., Ltd. Chi-Thread Rolling Technology Co., Ltd.
Room502, Nr.1122, XinJinQiao Road, Shanghai, China 201206 Tel: +86-21-61462100 Fax: +86-21-61462118 [email protected]
PCFS (Chi-Thread) G.S.S.N., with BSP and NPT threads are supplied in several types of surface finishing according to domestic and international standards, and guarantees long- lasting applications in the most diverse usage conditions as the special strong pipe thread.
Creating Value Together with You
www.panchinafs.com
Shanghai Pan-China Fastening System Co., Ltd. Chi-Thread Rolling Technology Co., Ltd.
Room502, Nr.1122, XinJinQiao Road, Shanghai, China 201206 Tel: +86-21-61462100 Fax: +86-21-61462118 [email protected]
ありがとう
Thank You!
谢 谢!
Vielen Dank
Спасибо
Merci
감사합니다
Ευχαριστούμε
Grazie
धन्यवा
Teşekkür ederiz
Gracias
Creating Value Together with You