Magnetism in Welding
Transcript of Magnetism in Welding
-
7/25/2019 Magnetism in Welding
1/4
Tubular structures and pipelines are commonly fabricatedby using one of several different arc welding processes.
This type of work is routine, takes place everyday, and
proceeds in a reliable and predictable manner. Yet once in
a while, sufficient magnetism arises within the components
being fabricated that welding becomes seriously disrupted,threatening to cause expensive delays in the programme of
work.
This article examines the origins of magnetic arc blow and
discusses practical remedies which allow fabricators tominimise any subsequent delays in the welding schedule.
A practical example in solving problems associated withhigh levels of magnetism at a work site in Hungary is also
described.
Introduction
Welding arcs consist of a stream of electrons travelling from
the welding electrode to the workpiece which heat up thejoint preparation and melt filler metal to form a molten weld
pool which is directed along the joint to form a weld. If,
however, significant levels of magnetism are present in the
material being welded, then the interaction between the
magnetic field and the welding arc causes the arc to bedeflected sideways with subsequent disturbance of the weld
pool, see figure 1. This deflection is called magnetic arc
blow and can lead to the possible introduction of defects inthe weld, an increase in the time required to complete the
work, and a frustrated team of welders.
Often the interference with the welding arc is small and
welders can make the necessary adjustments required to
complete the job . Occasionally, however, the arc
becomes unstable or is completely blown out causing
defective welds and greatly increased welding times. The
cost implications of increased welding times or late deliverycan be significant.
The solution to the problem is to demagnetise the weldpreparation to enable welding to proceed. To do this
properly requires a means of measuring the magnetic field
in order to assess the magnitude of the problem, and thento confirm that successful demagnetisation has taken
place. Measurement of the residual magnetic field in thejoint preparation is important to ensure that demagnetising
procedures reduce rather than increase the value. Since
the magnetism in the steel can arise, in part, from the
welding current itself, demagnetisation has to take this intoaccount and a suitable procedure is described below.
Some level of magnetism is normally present within steel
(except stainless steel.) The key factor in determiningwhether or not this will cause problems is the strength of the
magnetic field at the point of welding. This should be
measured as shown in figure 2. In general, where the
magnetism in a joint preparation is found to be above 20gauss (2mT) , then disruption of the welding arc can be
expected. When the value is over 40 gauss (4mT) then arc
blow will be a problem. Demagnetisation techniquesshould aim to reduce the magnetic field in the joint
preparation to below 10 gauss (1mT). It is not unknown to
find magnetic fields of several thousand gauss which
completely prevents any welding from taking place.
Once magnetic arc blow has begun to disrupt the weldingarc, it is important to deal correctly with the problem to avoid
unnecessary delays in the fabrication programme; it isimportant not to waste time with attempted remedies which
cannot remove the high levels of magnetisation. Byapplying the correct demagnetisation procedures, welding
can usually proceed at the normal production rate.
Magnetism - A Blow to Welding
The origins of magnetic arc blow are examinedSolving problems associated with high levels of magnetism at a
Hungarian site is used as a practical example. (Publ ished in Welding & Metal
Fabrication, May 1999)
Fig 1
Fig 2
-
7/25/2019 Magnetism in Welding
2/4
Factors affecting arc blow
A range of factors are responsible for the presence and
strength of magnetism within materials. The most
significant are listed as follows.
1. The Earth's Magnetic FieldThis becomes particularly important when pipelines orstructures are laid in a North/South direction rather than
East/West. The effect can also be greater as the length of
the pipeline increases. Although the Earth's magnetic field
is less than 0.1mT, this can become concentrated to a
much greater value by steel alloys.
2. MaterialMagnetism can become a problem in materials with a
ferrite crystal structure. This microstructure produces
ferromagnetism which is found mainly in alloys with iron,nickel, or cobalt including steels but excluding most
stainless steels. Arc blow is frequently encountered when
welding steels with a high nickel content.
3. Weld preparationThe magnetic field in a weld preparation is higher where
the two butting faces are close together. Therefore,
magnetic arc blow tends to be worse at the root of a weld
where the gap between the faces is at its smallest. It is
also more of a problem in deeper , narrower V preps wherethe arc has to travel farther in the proximity of the faces of
the preparation .
4. Presence of longitudinal seamsWhere tubes have been manufactured using longitudinal
welds, there can be a high magnetic field associated with
the seams. Often, magnetism which is directed North on
one side of the seam becomes strongly South on the otherside. The location of these seams therefore causesparticular difficulties when circumferential butt welds areattempted, since the welding arc will be deflected in one
direction as the welder approaches the seam and will be
abruptly deflected in the opposite direction as soon as the
seam is passed by.
5. D.C. Welding currentD.C. welding current tends to cause or intensify magneticfields within steel whereas A.C. welding currents are much
less prone to this. Where the magnetism in steel isproduced entirely by the effect of the welding current, then
switching to A.C. should be considered if that is possible.
6. Assembly of componentsWhen the magnetic field is measured at the end of a stand-
alone tube or other components, this will be much lowerthan when tube ends are butted together. The strength of
the magnetism normally increases, often by a factor of 10,
when the pipes are assembled for welding.
7. Welding process.Magnetic arc blow is more likely to occur with lower
voltage arcs. Therefore TIG welding which uses a lowvoltage arc, and which is often used for the root pass of
multi-pass welds, is particularly susceptible to arc blow.
Manual metal arc welding using small diameter electrodes
also calls for low currents and voltages resulting in atendency to arc blow. Where possible, it is advisable to
"stiffen" the welding arc by increasing the current and
hence the welding voltage.
8. Magnetic particle inspection
Tubes which have been subjected to magnetic particleinspection can retain magnetism which subsequentlycontributes to the problems of arc blow.
9. Magnetic clampsThese can be used to lift steel components, or to attach
items to a steel surface. They tend to leave magnetic
patches in the steel which may contribute towards the
residual magnetism in the joint region.
10. Large structuresLarge structures such as those where pipes are used to
link large vessels as frequently found in a refinery or
chemical reactor are prone to becoming magnetic,
particularly where the pipes are linking structures on thenorth of a site to those on the south. This occurs because
large steel structures pull in the Earth's magnetic field andthis becomes concentrated in the pipes which link the
main parts together. Magnetic fields of several thousand
gauss have been measured in pipes in these locations.Pipework being assembled or repaired under these
conditions is very susceptible to magnetic arc blow.
11. Hyperbaric weldingHyperbaric welding carried out with high ambient gaspressures is more prone to arc blow than welding at
atmospheric pressure. This is because the electrons
which make up the welding arc are slowed down by the
high gas pressure allowing the arc more time to bedeflected by any magnetic field which may be present.
Magnetism - A Blow to Welding
-
7/25/2019 Magnetism in Welding
3/4
REMEDIES FORMAGNETIC ARC BLOW
Several techniques can be used to reduce or remove the
problem of arc blow.
Consider the joint designMake the weld preparation wider if possible. A J
preparation is better than a V.
Check the assembly procedureWhen making several circumferential welds to fabricate a
tube assembly, it is better to carry out the central weld first,
and work towards the ends. If welding proceeds by making
the outer joints first, the final closing weld in the centre of
the assembly involves welding two large structurestogether. A closing weld near the centre of a structure canresult in arc blow problems.
Select the welding processIf possible, an A.C. welding process should be used. This
avoids the welding current from significantly magnetising
the steel. If a D.C. process has to be used, then the
susceptibility to arc blow can be reduced by using thehighest arc voltage possible.
Demagnetisation prior to welding
It is possible to reduce the magnetism within a steel tube bycarrying out a demagnetisation procedure. This requires
the tube to be passed through a coil which is carrying an
alternating electric current. The coil length should be at
least equal to the diameter of the pipe. The peak value ofthe current multiplied by the number of turns should be
10,000 ampere turns per metre length of coil. The
frequency of the alternating current used depends on the
wall thickness and material of the tubes . Typical values forthe demagnetisation of steel pipes are 0.3 Hz for inch
wall thickness and 0.1 Hz for 1 inch.
Although this demagnetisation procedure is sometimes
carried out, it is time consuming and requires expensivehardware and power supplies. Moreover, demagnetising
prior to welding may not solve the problem of arc blow.Firstly, this is because it may not be possible to
demagnetise tubes with linear seams which possess
residual magnetism with both north and south polarity.Secondly, individual tubes may be successfullydemagnetised to an acceptable level but once ends are
butted together to form a weld preparation, the magnetic
field can increase by a factor of 10. Thirdly, the magnetism
which causes arc blow, may be caused by the weldingcurrent, rendering any prior demagnetisation useless.
Demagnetising During WeldingThe most reliable method of demagnetising is to carry this
out whilst welding is taking place. This is the only way totake account of variations in the level and polarity of the
magnetic field which occur during welding.
The Zeromag system available from Diverse Technologies
carries out this demagnetising process automatically. A
sensor is positioned near the welding electrode and theZeromag unit ensures that the magnetic field in the joint
preparation remains below 1 mT enabling welding to
proceed as normal. The Zeromag technique removes the
magnetic field within seconds and maintains the field closeto zero throughout the weld. Any changes in the polarity of
the magnetic field which occur as the weld proceeds are
detected by the Zeromag sensor which immediately makes
the necessary adjustments to the demagnetising current.Diverse also operates an on-site demagnetisation service
to enable fabricators to deal with occurrences of arc blow.
REMOVAL OF
MAGNETISM IN NI STEEL
TUBES
Manufacturing of welded tubular structure from Ni
alloyed steel.A de-ethaniser column was ordered from DKG-EAST RT
(Hungarian pressure vessel manufacturer) in the second
half of 1998. Due to the low working temperature (-110C), 12Ni19 (WNr. 1.5680, DIN 17280) material was chosen
for the vessel base metal. The material belongs to the 5%Ni alloyed carbon steel category.
It has been found in practice that the higher the carbon
and/or the Ni content of the steel, the more it tends to retain
magnetism. These types of steels are categorised as
magnetically hard materials and it is suggested that any
order placed on a plate manufacturer specifies themaximum permitted magnetic field strength.
Details of the pressure vesselThe vessel is a vertically installed pressure vessel
supported by a conical skirt. Vessel ends are closed by
elliptical heads. The shell diameter is ID 1500 mm and ID
2500 mm, while wall thickness varies from 16 to 20mm forthe ID 1500 mm part and 25 mm for the ID 2500 mm part.
The transition cone between the two parts also has 25 mm
wall thickness. The column's overall height is 35.4 m (See
figure 3 for column details).Due to the column dimensions, the vessel body was
manufactured from 16 shell sections. Shell sections were
welded by longitudinal joints (having 1800 to 2200 mmlength) and the entire shell is fabricated by assembling andwelding the circumferential joints between the sections.
Magnetism - A Blow to Welding
Fig 4. Welding of a circumfrential joint being carried out
while demagnetisation is in process
-
7/25/2019 Magnetism in Welding
4/4
Welding technique and parameters
Almost all the joints of the vessel were welded in the flat
position including the circumferential joints which wererotated during welding. The nozzle-shell welds were also
made as horizontal joints
The Longitudinal joints of the vessel were "V" beveled, background and rewelded from the other side. Two supporting
layers were welded by GMAW process, all other layers by
the SAW process.
The Circumferential joints had symmetrical "X" bevels withdouble side welding. As before two supporting layers were
welded by GMAW process and all other layers by SAW.
For the nozzle-shell joints, the shell opening was "half V"
bevelled, and the welding performed by back grinding and
rewelding from the other side using the SMAW process. Thenozzle circumferential welds were "V" beveled with welding
taking place from one side. The GTAW process was used forthe root pass welding, the filling and covering layers arcwelded using the SMAW process.
The welding material used for all processes was the
austenite-ferrite type high alloyed material ensuring
compliance with the high impact test requirements.
Magnetic build up in weld prep
Manufacturing of pressure vessels started with cutting andbevelling of the steel plates and rolling the shell sections. It
appeared that the above procedures resulted in an increase
in the magnetic field found in the material. However, the
magnetism was of a low level and did not interfere with the
longitudinal welding.It was only after the longitudinally welded sections were
subsequently rolled and assembled in preparation forcircumferential welding, that a serious increase in the
magnetic field was detected. Measurements showed thatthe magnetic field strength was about 10 times greater in the
weld preparation than at the components' bevelled edges .
This caused arc blow which at some locations was sufficient
to prevent arc striking.
Attempts were made to solve the problem, using AC welding
processes or to demagnetise the material prior to welding,but did not prove successful. At some locations where the
magnetism was lower, it was possible to weld successfullyonly by stiffening the arc through the use of larger diameter
electrodes and higher arc voltages. With such high levels of
magnetism in the joint, it was necessary to reduce the
magnetic field strength to acceptable levels during the
welding process.
Demagnetising procedure during welding
Smaller components can be demagnetised easily and
routinely by passing them through a demagnetising coilpowered from the mains. For bigger components such as
the above vessel, the only way was to use a localised
demagnetising technique during the welding process. Toaccurately monitor the magnetic flux, it was essential to use
a magnetic field meter capable of measuring the magnetismin the root of the weld preparation. This enabled the
magnetic field in the vicinity of the joint preparation to be
cancelled out and the manufacturing of the column wascompleted.
1. The magnetic field around the circumferential butt
joints was not constant and varied significantly, particularly
near the longitudinal joints. This necessitated continual
monitoring of the magnetic field strength and continual
adjustment of the demagnetising current to cancel out the
residual field. Of course, after finishing welding andswitching off the demagnetising equipment, the magnetic
field returned to the components but was of no further
concern. Figure 4 shows a circumferential joint beingwelded whilst demagnetisation is taking place.
Conclusions
1 Low levels of magnetism caused by the Earth's field orthe welding current can result in much higher magneticfields when tubes are assembled for the welding ofcircumferential butt joints.
2 It is worthwhile being prepared for the possibility ofmagnetic arc blow since there are some simple changesto the welding process which can be made to relieve theproblem.
3 Demagnetisation whilst welding is taking place is themost reliable method of ensuring that welding can
proceed with the minimum time delay.4 Propriety equipment is available which reducesmagnetism in weld preparations to the low levelsrequired by arc welding.
Jzsef Takcs, EWE is a welding engineer with DKG-EAST
Oil and Gas Equipment Manufacturing Company, at
Nagykanizsa, Hungary.
Further information on Zeromag
Diverse Technologies Ltd., Cambridge, U.K.
Tel +44 (0) 1223 84 44 44Email [email protected]
Zeromag ZM100A De-Magnetiser
Magnetism - A Blow to Welding