ISOMAT_Repairs & maintenance

Repairs& Maintenanceof Dwellings

Step by step presentation of repairing and constructional solutions

Repairs and Maintenance of DwellingsThe maintenance and repair of dwellings often cause problems not only to individuals, but also to professionals. The choice of the appropriate materials and their proper application are crucial for the solution of these problems.

Therefore, in ISOMAT we have developed a wide range of repairing and constructional solutions, based on our experience and our know-how, for a variety of cases regarding repairs and maintenance of dwellings.

This particular brochure, in which a step by step photographic presentation of solutions is demonstrated, shall constitute a comprehensive guide for everyone.

However, every repairing or maintaining work has its own particularity, while the factors causing these problems vary. This situation renders impossible describing and tackling all sub-cases. For this reason, if you need more information you can consult the Technical Support Department of ISOMAT. Our highly specialized and experienced engineers are ready to provide you with the proper technical solution to any difficulty arising in your repairing works.

2

1

4

5

3

6

7 8

9

10

1

PAINTS REPAIRRepair of damaged paint

PLASTERS REPAIRRepair of random cracks on plasterRepair of hair cracks on plaster Repair of intense multiple cracks on plasterRepair of crumbled plasterRepair of detached plaster

MASONRY REPAIRRepair of cracked or detached masonry

REINFORCED CONCRETE REPAIRSmoothening of exposed concreteRepair of cavities on concreteRepair of peeled concrete due to corrosion of the steel reinforcement

MINOR REPAIRSRepair of cracks between door frame and wallRepair of rusty stanchionsFixing of detached ridge polesFixing of stair rails to wall

INTERIOR SPACES RENOVATIONPuttying and painting of surfacesRelocation of electrical installationsRepair of o in wallsPuttying of walls

TILES FIXINGFixing new tiles on old tile layersFixing tiles on wood and gypsum boardFixing tiles on metal surface

LEVELING AND SMOOTHING OF Repairing uneven surfaces or inclinations using floor leveling cement mortarLeveling and smoothing using self-leveling cementitious screed

SURFACES CLEANINGCleaning cement residuesCleaning oils

SURFACES PROTECTIONWall protection from graffitiProtection of unpolished marbleProtection of walls made of natural or artificial stones

penings

FLOORS

of uneven surfaces

floors fromfloors from

2

1

4

5

3

3

3445

9910

1314

1515

1616

171718

C O N T E N T S

5

6

77

6

7

8

9

10

8

10

11111212

14

2

1 PAINTS REPAIRREPAIR OF DAMAGED PAINT

FLEXCOAT FLEX-PRIMER

2 2 Elastic waterproofing coating (consumption: 125 ml/m /layer or totally 250 ml/m )2 High quality acrylic water-based emulsion (consumption: 0.1-0.2 kg/m )

MATERIALS

Paint detachment may be due to wrong application (lack of priming, wet substrate), to its bad quality (very low strength, absorptivity) or to the moisture coming from the back side of the wall.

The second layer of FLEXCOAT follows, after the first has dried.

After the primer has dried, the surface is painted with FLEXCOAT in two layers.

Then, the surface is cleaned off very thoroughly of any dust.

Priming with FLEX-PRIMER follows.

After all possible moisture problems have been restored, the old paint is rubbed off by putty knife in order for the bulges to be removed.

1 PAINTS REPAIR

REPAIR OF RANDOM CRACKS ON PLASTER

2 PLASTERS REPAIR

Random cracks on plaster can be restored easily, as long as they are on the surface and not been caused due to masonry cracks.

FLEX-COVER is prepared, adding A-component (cementitious powder) into B-component (acrylic polymer dispersion) under continuous stirring.

The crack is sealed using FLEX-COVER by a putty knife.

After the sealing material has dried, the surface is primed with FLEX-PRIMER and then painted with FLEXCOAT.

Light dampening of the crack follows.Then the crack is cleaned off of any dust.The crack is initially opened and all loose particles are removed.

TIP: In this particular application, instead of FLEX-COVER, it can also be used the elastoplastic acrylic sealant ISOMASTIC-A.

3

FLEX-COVERFLEXCOATFLEX-PRIMERISOMASTIC-A

2-component, flexible putty (consumption for sealing joint of 5 mm x 5 mm: 40 g/m of joint)2 2 Elastic waterproofing coating (consumption: 125 ml/m /layer or totally 250 ml/m )

2 High quality acrylic water-based emulsion (consumption: 0.1-0.2 kg/m ) Elastoplastic acrylic mastic

MATERIALS

REPAIR OF HAIR CRACKS ON PLASTER

The existence of hair cracks on plaster, in case they are not tackled in time, is possible to lead to more serious problems.

After the primer has dried, the painting of the surface with FLEXCOAT in two layers follows.

The second layer follows after the first one has dried.

TIP: In case the cracks are multiple and intense, it is recommended that the first FLEXCOAT layer be reinforced, while still wet, with the polyester cloth (TREVIRA) of 1 m width. Then, for the TREVIRA embodiment, two more FLEXCOAT layers are needed. Alternatively, repairing multiple and intense cracks, could take place with the use of the elastic 2-component elastic putty FLEX-COVER, as this is described below.

Firstly, the surface needs to be cleaned off of dust, etc.

Then, the dry surface is primed with FLEX-PRIMER.

MATERIALS 2 High quality acrylic emulsion (consumption: 0.1-0.2 kg/m )FLEXCOATFLEX-PRIMER TREVIRA

2 2 Elastic waterproofing coating (consumption: 125 ml/m /layer or totally 250 ml/m )water-based

2Polyester reinforcement textile for waterproofing layers (30 g/m )

REPAIR OF INTENSE MULTIPLE CRACKS ON PLASTER

MATERIALSFLEX-COVERFLEXCOAT FLEX-PRIMER

2-component, flexible putty (consumption for sealing joint of 5 mm x 5 mm: 40 g/m of joint)

2 High quality acrylic water-based emulsion (consumption: 0.1-0.2 kg/m )

2 2 Elastic waterproofing coating (consumption: 125 ml/m /layer or totally 250 ml/m )

Intense hair cracks on plaster may be due to its wrong application (deficient dampening during summer months, lack of plaster reinforcement when applied on thermo-insulating boards etc.) as well as to its bad quality.

FLEX-COVER is prepared after A- is added into under continuous stirring.

componentB-component

After the primer has dried, FLEX-COVER is applied by putty knife on the cracked surface in one layer.

After the FLEX-COVER layer has dried,it is needed to prime with FLEX-PRIMER and paint with FLEXCOAT.

Firstly, the surface needs to be cleaned off of dust etc.

Then, priming with FLEX-PRIMER follows. Especially when plasters are relatively unstable, FLEX-PRIMER is needed to stabilize their surfaces.

4

REPAIR OF CRUMBLED PLASTER

If a plaster is not water repellent, it becomes crumble and it finally gets detached.

Repairing takes place using UNICRET or UNICRET-FAST, improved with the addition of ADIPLAST.

Firstly, all crumbling parts of the plaster are removed by putty knife.

Products are applied with a float, after the primer has dried.

Then, the surface is cleaned off of any dust.

After the plaster has slightly dried, it is treated (rubbed) with a sponge-faced float.

Since the plaster has dried, the surface is primed with FLEX-PRIMER and it can be painted with FLEXCOAT.

Next, priming the surface with FLEX-PRIMER or NANO-SEAL takes place, in order to stabilize it.

UNICRETUNICRET-FASTADIPLAST

NANO-SEAL

2 Plastering mortar (consumption: 15.5 kg/m /cm of layer thickness)2 Fast-setting, white, repairing mortar (consumption: 15 kg/m /cm of layer thickness)

Mortar improvement polymer latex2 2 Elastic waterproofing coating (consumption: 125 ml/m /layer or totally 250 ml/m )

2 High quality acrylic emulsion (consumption: 0.1-0.2 kg/m )

FLEXCOAT FLEX-PRIMER water-based

2Waterproofing and stabilisation of surfaces (consumption: 0.1-0.2 kg/m )

MATERIALS

REPAIR OF DETACHED PLASTER

DUROCRET DUROCRET-FAST

NANO-SEAL

2 Polymer modified repairing cement mortar (consumption: 15 kg/m /cm of layer thickness) Fast-setting, repairing cement mortar

2 2 Elastic waterproofing coating (consumption: 125 ml/m /layer or totally 250 ml/m )

2(consumption: 17 kg/m /cm)

2High quality acrylic water-based emulsion (consumption: 0.1-0.2 kg/m )2Waterproofing and stabilisation of surfaces (consumption: 0.1-0.2 kg/m )

FLEXCOAT FLEX-PRIMER

MATERIALS

Plaster falling off the wall may be due to its intense corrosion by water.

Restoring, after the primer has dried, takes place using DUROCRET or DUROCRET-FAST. Their preparation requires only the addition of water.

The material is applied with a trowel. After the material has slightly dried, rubbing with a sponge-faced float can take place.

After DUROCRET has dried, the surface is primed with FLEX-PRIMER and it can be painted with FLEXCOAT.

Firstly, all crumble parts of the plaster are removed by putty knife.

Then, the surface is cleaned off of any dust.

Priming the surface with FLEX-PRIMER or NANO-SEAL, in order to stabilize it, follows.

5

MASONRY REPAIRREPAIR OF CRACKED OR DETACHED MASONRYThe existence of single cracks on plasters, which are present in a height of 30-40 cm below the ceiling, is caused usually by masonry bricks' movements. Sealing the cracks on the surface would most probably lead to a new crack. A complete solution consists of the steps presented below.

REPAIR OF CRACKED OR DETACHED MASONRY

3

A cracked or detached masonry results to cracks on plaster.

The entire area of the detachment is thoroughly cleaned with a brush.

Subsequently, the substrate is thoroughly dampened.

After the mortar has hardened, the surface is cleaned off of any dust etc and is dampened.

After the first layer has dried, the surface is dampened and the second layer follows with UNICRET or UNICRET-FAST.

After the plaster has slightly dried, it is being rubbed with a sponge face-float.

After the surface has dried, priming with FLEX-PRIMER follows and finally painting with FLEXCOAT takes place.

While the first coat is still fresh, a strip of glass mesh is placed and it is lightly pressed onto the first coat.

Firstly, the plaster is removed to a total width of 30 cm (15 cm on each side) along the entire length of the detachment.

Finally, DUROCRET, DUROCRET-FAST or RAPICRET fill the widened crack as deeply as possible using a gauging trowel.

A first coat of plaster, using UNICRET or UNICRET-FAST, improved with ADIPLAST polymer latex is applied.

Then, the area of the detachment is widened by breaking the surrounding bricks with a sharp tool.

DUROCRETDUROCRET-FASTRAPICRETUNICRET UNICRET-FASTFIBER-GLASS MESH

2 Polymer modified repairing cement mortar (consumption: 15 kg/m /cm of layer thickness) Fast-setting, repairing cement mortar

2(consumption: 17 kg/m /cm)2Fast-setting repairing cement mortar (consumption: 17.5 kg/m /cm of layer thickness)

2Plastering mortar (consumption: 15.5 kg/m /cm of layer thickness)2Fast-setting, white, repairing mortar (consumption: 15 kg/m /cm of layer thickness)

High-strength plaster reinforcement

MATERIALS

A more detailed description of the products mentioned in this guide, can be found in pages 17-20. 6

Imperfections on exposed concrete can easily be smoothened with the use of polymer modified cement putties PLANFIX or PLANFIX-FINE.

Firstly, the surface is cleaned off of any dust and is thoroughly dampened.

After the surface has been hardened, it is being rubbed with a thin sand paper.

Finally, follows the priming and painting of the surface.

The cement putty is gradually added into water under continuous stirring, until uniform pasty putty is formed, proper for stuccoing.

The material is applied using a putty knife in one or two layers, depending on the imperfections of the surface. The second layer follows after the first has dried.

4Repairs of concrete elements (smoothening, filing cavities, rusted reinforcement, destroyed parts etc.) need special attention and knowledge, as wrong choice of materials along with wrong application, depending on the severity of the situation, may render the repair ineffective.

REINFORCED CONCRETE REPAIRTHE PROBLEM

SMOOTHENING OF EXPOSED CONCRETE

PLANFIX PLANFIX-FINE

2Polymer modified cement putty (consumption: 1.3 kg/m /mm of layer thickness)2 Polymer modified, extra fine-graded, cement putty (consumption: 1.3 kg/m /mm of layer thickness)

MATERIALS

DUROCRET Fast-setting, repairing cement mortar

2Polymer modified repairing cement mortar (consumption: 15 kg/m /cm of layer thickness)2(consumption: 17 kg/m /cm)

2Fast-setting polymer modified repairing cement mortar (consumption: 17.5 kg/m /cm of layer thickness)DUROCRET-FASTRAPICRET

MATERIALS

REPAIR OF CAVITIES ON CONCRETE

The appearance of cavities on concrete is a rather common phenomenon.

Subsequently, the surface is thoroughly dampened.

The cavity is filled with DUROCRET. The material is applied by pressure using a trowel.

If fast work is required, DUROCRET-FAST or RAPICRET (fast-setting patching mortar) can be used instead.

Firstly, the surface is cleaned off of any loose particles, by mechanical means.

Then, the surface is cleaned off of any dust with the use of a hard brush.

7

REPAIR OF PEELED CONCRETE DUE TO CORROSION OF THE STEEL REINFORCEMENT

FERROSEALMEGACRET-40RAPICRET

Cement based, anti-corrosive coating for reinforcement elements (consumption: 70-130 g/m of reinforcement bar)2 High-strength, fiber-reinforced, repairing cement mortar (consumption: 17.5 kg/m /cm of layer thickness)

2 Fast-setting polymer modified repairing cement mortar (consumption: 17.5 kg/m /cm of layer thickness)MATERIALS

A more detailed description of the products mentioned in this guide, can be found in pages 17-20.

The corrosion in reinforcement, which has led to the detachment of concrete parts, endangers the whole structure.

Next, the surface is cleaned thoroughly off of any dust.

FERROSEAL is applied using a brush in two layers. Its preparation requires only the addition of water.

After FERROSEAL has dried, the surface is dampened thoroughly.

The final surface should be well protected from dehydration for 48 hours, e.g. repeating dampening.

If fast work is required, RAPICRET (fast-setting patching mortar) may be used instead.

After the material has hardened, plastering and painting of the surface follows.

The peeled area of the concrete is repaired by the application of MEGACRET-40 (high performance patching mortar). Its preparation requires only the addition of water.

The material is applied by pressure using a trowel.

Initially, all broken and loose particles of the peeled concrete should be removed thoroughly, and the corroded steel reinforcement should be completely uncovered.

Subsequently, the corroded steel is cleaned and scrubbed, grinded etc. with an appropriate tool in order for the rust to be completely removed.

The second layer is applied after the first one has dried.

8

FLEX-COVER is prepared after A-component is added into B-component under continuous stirring.

The surface is slightly dampened and FLEX-COVER is applied by a putty knife in the joint.

Finally, the stanchion is painted after FLEX-COVER has dried.

Firstly, the joint between the marbles is cleaned thoroughly with a sharp tool. The base of the stanchion is cleaned from any rust and checked if the metal is completely destroyed.

If the stanchion is not destroyed from the rust and its replacement is not necessary, it is painted with an anticorrosive paint.

The joint is sealed by the acrylic mastic ISOMASTIC-A.

The acrylic sealant is smoothened, while it is still fresh.

Right afterwards, the paper tape is removed with caution.

After ISOMASTIC-A has dried, the joint is painted alongside.

Firstly, the crack is widened to a width of 3 mm.

Thorough cleaning of any dust follows. The use of paper adhesive tape is necessary in order to prevent any smear of the door frame.

The wrong choice of materials for sealing the joint between the door frame and the wall, led to crack appearance.

5Minor repairs are not required only in old structures, which may demand maintenance, but also in new ones, where there has been made wrong choice of materials or bad application of them. Following are presented some of the most common problems that can appear in a structure.

MINOR REPAIRSTHE PROBLEM

REPAIR OF CRACKS BETWEEN DOOR FRAME AND WALL

REPAIR OF RUSTY STANCHION

MATERIALS FLEX-COVER 2-component flexible putty (consumption for sealing joint of 5 mm x 5 mm: 40 g/m of joint)

9

MATERIALS ISOMASTIC-A Elastoplastic acrylic mastic

The influence of water resulted to the rusting of the base of the stanchion, a situation that needs to be confronted immediately, as it makes the whole construction dangerous.

Fixing rails into wall is an application that requires speed and great stability.

The material is applied by pressure using a trowel as usual.

Firstly, the surface is cleaned off of any dust, etc.

Subsequently, the surface is smoothened by a moist brush.

Subsequently, the surface is thoroughly dampened.

RAPICRET starts to harden after 15 minutes and the rail is almost stabilized.

The next day the surface is ready to be painted.

RAPICRET is added into water under continuous stirring, until a mixture with the desired workability is formed.

The detachment of ridge poles is a problem that usually occurs when their fixing is made by a low quality cement mortar.

DUROCRET is applied using a trowel as usual.

Subsequently, the ridge pole is fixed and is leveled using a thread.

Finally, any DUROCRET leftovers are removed and the surface is well smoothened.

The use of DUROCRET in red-brown color improves the appearance of the roof.

Firstly, the surface is cleaned by any loose materials or dust.

Subsequently, the surface is well dampened.

DUROCRET (red-brown colour) is added into water under continuous stirring, until a mixture with the desired workability is formed.

FIXING OF DETACHED RIDGE POLES

FIXING OF STAIR RAILS TO WALL


MATERIALS DUROCRET Polymer modified repairing cement mortar in red-brown 2(consumption: 15 kg/m /cm of layer thickness)

MATERIALS RAPICRET 2Fast-setting repairing cement mortar (consumption: 17.5 kg/m /cm of layer thickness)

10

Small imperfections on plaster (e.g. cracks, breaks) are very common and they can be repaired relatively quickly.

FAST-COVER is applied with a putty knife at the desired spot and it is pressed to fill completely the gap.

The surface is smoothed out immediately by a putty knife.

After the repaired surface has dried (in approx. 30 minutes), painting can follow.

Firstly, the surface is cleaned off of any loose materials, etc.

Subsequently, the surface is cleaned of any dust.

Finally, when the surface has dried (approximately after 3 hours) the surface can be painted.

After the plaster has slightly dried (approx. after 45 minutes), it is being rubbed with a sponge-faced float.

The puttying is being made using UNICRET-FAST. Its preparation requires only the addition of water.

Changing use of a room, normally leads to the relocation of the electrical installations.

Firstly, the electric channel (path) is cleaned off of any dust and the location of the wire holder follows.

Subsequently, the surface is slightly dampened.

6The renovation of a room will probably include a range of repairs, from minor to large scale ones. Hereunder are represented a few common minor problems, which can be tackled fast and easy, taking for granted that the appropriate materials have been chosen.

INTERIOR SPACES RENOVATIONTHE PROBLEM

PUTTYING AND PAINTING OF SURFACES

RELOCATION OF ELECTRICAL INSTALLATIONS

MATERIALS UNICRET-FAST 2Fast-setting, white, repairing mortar (consumption: 15 kg/m /cm of layer thickness)

MATERIALS FAST-COVER Ready-to-use, light weighted acrylic putty for patching and filling cracks and holes

11

The creation of smoothed surfaces on interior spaces is a very common demand in new buildings.

The mixture is applied by putty knife in two layers. The second layer follows after the first one has dried (after 2-3 hours).

After the material has hardened (in approximately 12 hours) the grinding of the surface follows.

Finally, the surface is being primed and painted.

Firstly, the surface of the plaster is cleaned off of any dust, etc. No priming or preparation using oil before the application is needed.

The content of STUCCOCRET is added to water under continuous stirring until a uniform mixture with the desired workability is formed.

REPAIR OF OPENINGS IN WALLS

PUTTYING OF WALLS


During the renovation of a space it may be necessary the dismantlement of some old installations.

Plastering is being made using UNICRET or UNICRET-FAST, improved with ADIPLAST polymer latex.

After the plaster has slightly dried, it is being rubbed with a sponge-faced float.

Finally, when the plaster has dried, the painting of the surface follows.


Subsequently, the repaired area is being primed using the ready-made primer PL-BOND.

The surface is dampened and the plaster is applied using a trowel.

After the primer has dried, the bricks are being built using UNICRET or UNICRET-FAST. Their preparation requires only the addition of water.

UNICRET UNICRET-FAST ADIPLAST PL-BOND

2Plastering mortar (consumption: 15.5 kg/m /cm of layer thickness)2Fast-setting, white, repairing mortar (consumption: 15 kg/m /cm of layer thickness)

Mortar improvement polymer latex2Adhesion primer (consumption: 0.3-0.35 kg/m )

MATERIALS

MATERIALS STUCCOCRET 2Spatula putty for interior use (consumption: 1.1 kg/m /mm of layer thickness)

12

7The latest tendency is for tiles to substitute the rest of the floor and wall coatings. Hereunder, there are presented some particular cases of applications, which if not tackled properly, can cause problems to the construction.

TILES FIXINGTHE PROBLEM

FIXING NEW TILES ON OLD TILE LAYERS

The wrong choice of tiles leads to their destruction. Thus, a new layer of tiles is necessary.


After the surface is walkable, tile grouting follows either with MULTIFILL 3-15, enriched with resin DS-99, or with MULTIFILL SMALTO 1-8.

The grout is spread onto the joints, using a rubber float in a diagonal direction to the joints, in order to fill them completely.

Finally, with a bubble level and a rubber hammer we arrange their desirable leveling (position).

Then, the tiles should be fixed by pressing them to the desired position by keeping them stable and locating crosses for grouting.

The tile adhesive should be spread (combed) on the substrate using a notched trowel, in order to be uniformly applied on the whole surface.

The excess material should be wiped after a while, using a slightly wet sponge.

Finally, the surface may be cleaned with a slightly wet cloth after the tile grout has completely dried.

Fixing new tiles on old tiles is an easy application without any removal of the old tiles layer.

ISOMAT AK-22 is gradually added into water under continuous stirring, until a uniform paste is formed. The mixture should be left about 10 minutes to settle and stirred slightly again.

13

ISOMAT AK 22MULTIFILL 3-15MULTIFILL SMALTO 1-8DS-99

2 Flexible, high quality, polymer modified, tile adhesive for difficult substrates (consumption: 1.5-4.0 kg/m ) Colored tile grout for joint width 3-15 mm

Water-repellent, polymer modified tile grout with porcelain effect for joint width 1-8 mm Additive for tile adhesives and joint grouts

MATERIALS

FIXING TILES ON WOOD AND GYPSUM BOARD

MATERIALSISOMAT AK-ELASTIC MULTIFILL SMALTO 1-8UNI-PRIMER

Elastic, 22-component, tile adhesive (consumption: 1.5-4.0 kg/m ) Water-repellent, polymer modified tile grout with porcelain effect for joint width 1-8 mm

2 Acrylic water-based primer (consumption: 0.1-0.2 kg/m )

FIXING TILES ON METAL SURFACE



After the tile adhesive has been dried, follows the tile grouting with MULTIFILL SMALTO 1-8.

ISOMAT AK-ELASTIC is prepared by adding A-component to B-component under continuous stirring.

Fixing tiles on wood and gypsum board is nowadays a very common application.

The tiles should be then fixed by pressing them to the desired position.

After UNI-PRIMER has dried, the tile adhesive is “combed” on the substrate using a notched trowel.

Firstly, the surface is cleaned off of any dust and is primed with UNI-PRIMER.

ISOMAT AK-ELASTIC MULTIFILL SMALTO 1-8

2Elastic, 2-component, tile adhesive (consumption: 1.5-4.0 kg/m ) Water-repellent, polymer modified tile grout with porcelain effect for joint width 1-8 mm

MATERIALS

Metal surfaces comprise a difficult substrate for fixing tiles.

The tiles should be then fixed by pressing them to the desired position.


After the tile adhesive has been dried, tile grouting with MULTIFILL SMALTO 1-8 follows.

Firstly, the surface is cleaned off of any dust, rust, etc.

ISOMAT AK-ELASTIC is prepared by adding A-component to B-component under continuous stirring.

The tile adhesive should be combed on the substrate using a notched trowel, so as to be uniformly applied on the surface.

14

8Floor filling may be required for new building structures (covering water or heating pipes) as well as for the repair of old ones (e.g. dismantlement of old wood floors and leveling in order to fix tiles or marble). The creation of a sloped surface in terraces or balconies may also be another significant requirement.

LEVELING AND SMOOTHING OF FLOORS THE PROBLEM

REPAIRING UNEVEN SURFACES OR INCLINATIONS USING FLOOR LEVELING CEMENT MORTAR

Dismantlement of old wood floors and leveling in order to fix tiles, leads to height differences in comparison with other floors.

SCREED-100 is added into water under continuous stirring, until a homogenous mass is formed.

Then, the substrate surface must be well dampened, but without creating water puddles.

The laying procedure of SCREED-100 is the same as for concrete up to 10 cm thickness.

For thin application layers (up to 3-4 cm) a bonding layer of ADIPLAST mixed with water, cement and sand is required, after dampening, in order to achieve a stronger bonding of SCREED-100 to the existing cement based substrate. Otherwise, FERROSEAL can be applied instead.

Firstly, the surface is cleaned off of any dust, oils, loose materials, etc. and an elongated beam for leveling is located.

MATERIALSSCREED-100 ADIPLASTFERROSEAL

2Cementitious screed for filling floors (consumption: 14 kg/m /cm of layer thickness)Mortar improvement polymer latex

2Cementitious bonding layer (consumption: 2 kg/cm )

FLOWCRET 1-10FLOWCRET 1-10 EXPRESSFLOWCRET 3-30 EXPRESSUNI-PRIMER

2 Self-leveling, polymer modified, cementitious screed for leveling floors (consumption: 1.65 kg/m /mm) Fast-setting, self-leveling, polymer modified, cementitious screed for leveling floors Fast-setting, self-leveling, polymer modified, cementitious screed for leveling floors

2 Acrylic, water-based primer (consumption: 0.1-0.2 kg/m )

MATERIALS

LEVELING AND SMOOTHING OF UNEVEN SURFACES USING SELF-LEVELING CEMENTITIOUS SCREED

After the primer has dried, FLOWCRET 1-10 can be applied. The material is added to water under continuous stirring, until a homogenous mass is formed.

In case it is desirable for the floor to be walkable after 3 hours or to be covered within 24 hours, it is recommended the use of FLOWCRET 1-10 EXPRESS. Alternatively, for floor thickness from 3 mm up to 30 mm it is recommended the use of FLOWCRET 3-30 EXPRESS.

Firstly, the surface is cleaned off of any dust, oils, loose materials, etc.

The surface of concrete floors is usually uneven, making it difficult to fix tiles, carpet, plastic flooring etc.

Subsequently, the surface is primed with UNI-PRIMER.

The FLOWCRET 1-10 mixture should be spread in a single layer, with the aid of a large spatula, at a thickness of up to 10 mm. After the FLOWCRET 1-10 has dried it can be covered with various floorings such as tiles, carpet, plastic flooring etc.

15

SURFACES CLEANINGTHE PROBLEMCement residues (cement grouts, plasters, cement dirt, lime dirt, etc.) which have been dried on surfaces of ceramic tiles, natural stones, and unpolished marbles have to be cleaned with special cleaning liquids and not by mechanical means, as this procedure may cause some serious problems to the surface. Surfaces which have been impregnated with oils, grease, etc. can also be cleaned with special cleaning liquids.

CLEANING FLOORS FROM CEMENT RESIDUES

9


Tiles, old mosaics, unpolished marbles etc., with cement residues, can be cleaned easily with CL-CLEAN.

The liquid should act for 2-3 minutes and then the surface should be brushed with a hard (non metallic) brush.

The surface should be washed with plenty of water.

In difficult cases it might be necessary to repeat the procedure.

On vertical surfaces, it is applied with a brush.

CL-CLEAN is spread on the surface to be cleaned as it is or diluted with water, up to 1:1.

MATERIALS CL-CLEAN 2Tile and natural stone cleaning liquid (consumption: 0.15-0.2 kg/ml )

CLEANING FLOORS FROM OILS

MATERIALS FD-CLEAN 2Oil and grease remover from concrete floors (consumption: 0.8-1.0 kg/m )

Floors which have been impregnated with oils is a common phenomenon on garages, food industries etc.

Subsequently, the surface is rubbed meticulously with a hard wire-brush in order to penetrate the substrate pores.

Let FD-CLEAN at least 30 minutes to emulsify the oils. The change of colour shows that the chemical reaction has begun.

Finally the emulsified oil is removed by high pressure and high temperature water blast. In difficult cases it might be necessary to repeat the procedure.

Firstly, the floor surface is cleaned from superficial dirt by using high pressure and high temperature water blast.

After the surface is cleaned from these residues, FD-CLEAN is then spread on the floor.

16

Cleaning a surface is easily done by using hot water under pressure or rubbing with a sponge.

After cleaning, the surface must be protected again by the application of ISOMAT AG-77 in 1-2 layers.

The substrate is cleaned off of any dust etc, before the application of ISOMAT AG-77.

ISOMAT AG-77 protects the surface from graffiti, environmental impurities, etc. without changing the surface appearance.

The material is then applied in 1-2 layers, depending on the absorptivity of the surface. The second layer follows after the first one has dried.

Cleaning a surface from graffiti is easily done after treated with ISOMAT AG-77.

NANOPRO-M has impregnated into the pores of the marble without altering its appearance.

The final cleaning of the surface can be done after 6 hours.

Then the surface is cleaned with a slightly wet cloth.

Stains that have impregnated into marbles can be removed in a rather difficult way. Thus, proactive protection is critical in order to avoid such situations.

NANOPRO-M is poured onto the cleaned surface and is applied by squeegee.

The material is left to act for 5 minutes and then the excessive material is removed using a squeegee.

Alternatively, PS-21 can be used instead of NANOPRO-M.

10With a few simple and easy applications, the appearance and the life cycle of certain coatings (stones, marbles, painted surfaces, decorative coatings etc.) can be enhanced.

SURFACES PROTECTION THE PROBLEM

WALL PROTECTION FROM GRAFFITI

PROTECTION OF UNPOLISHED MARBLES

MATERIALS ISOMAT AG-77 2Anti-graffiti, protection emulsion (consumption: 50-100 ml/m )

NANOPRO-M PS-21

2Nano-impregnation for protecting marbles (consumption: 50-70 ml/m )2Ready-to-use, silicone based solution without solvents for waterproofing (consumption: 200-400 ml/m )

MATERIALS

17

If altering the appearance of the surface is not desirable, then the ideal solution for its waterproofing is PS-20.

PS-20 is applied with brush, roller or spray in two layers. The second layer is applied once the first layer has completely dried.

PS-20 impregnates to the pores of the surface and prevents it from rain water absorption without altering its appearance.

Firstly, the surface where PS-20 is going to be applied on, should be clean, dry and have open pores.

Waterproofing of walls, which are made of or are decorated with natural stones or coatings, prevents the appearance of white stains (salt) on them, while simultaneously protects them from frost and pollution. Hereunder, two different ways of dealing with the same problem are presented: 1) Waterproofing with the transparent water-repelling impregnation PS-20 and 2) waterproofing with the acrylic stone varnish VS-1.

st1 Solution: Waterproofing of surfaces with the transparent water-repellent solution PS-20.

VS-1 brings out the natural color of the material on which it is applied, protecting at the same time the surfaces from the influence of rainwater.

VS-1 is applied with brush, roller or spray in two layers. The second layer is applied once the first layer has completely dried.

VS-1 impregnates into the pores of the surface and simultaneously brightens up its natural color.

Firstly, the surface where VS-1 is going to be applied should be clean, dry and have open pores.

Alternatively, NANOPRO-C can be used instead of PS-20.

PROTECTION OF WALLS MADE OF NATURAL OR ARTIFICIAL STONES

PS-20 NANOPRO-C

2Ready to use, silicone based, transparent solution with solvents for waterproofing (consumption: 200-400 ml/m )2Nano-impregnation for protecting porous surfaces (consumption: 100-200 ml/m )

MATERIALS

nd2 Solution: Brightening-up and protection of surfaces with the acrylic stone varnish VS-1.

MATERIALS VS-1 2 Acrylic stone varnish (consumption: 150-200 ml/m per layer)

A more detailed description of the products mentioned in this guide, can be found in pages 17-20. 18

PRIMERS

PL-BONDGypsum plaster adhesion primerAdhesion primer used for priming smooth or non-absorptive surfaces, instead of spatterdash, in order to increase the adhesion of the subsequent plaster. Ideal substrate for gypsum plasters. Suitable for indoor and outdoor use. Colour: Light red.

2Consumption: 0.3-0.35 kg/m . Packaging: Plastic buckets of 5 kg and 20 kg.

UNI-PRIMER Acrylic water-based primerReady-to-use acrylic water-based primer. Stabilizes weak, loose or crumbling plasters.Colour: White.

2Consumption: 0.1-0.2 kg/m . Packaging: Plastic containers of 1 kg, 5 kg and 20 kg.

MORTARS FOR LEVELING & FILLING FLOORS

FLOWCRET 1-10Self-leveling, polymer-modified cementitious screedSuitable for smoothing and leveling concrete or mortar floors, before laying finishing materials like carpet, parquet layers, tiles etc. Applied at a thickness of 1-10 mm per layer. Colour: Grey.

2Consumption: Approx. 1.65 kg/m /mm. Packaging: Bags of 25 kg.

SCREED-100

Ideal for filling and leveling floors to be covered with tiles, marble, parquet etc., as well as for forming slopes on terraces. It replaces non-reinforced concrete or gas-concrete. Applied at a thickness of up to 10 cm per layer.Colour: Grey.

2Consumption: Approx. 14 kg/m /cm. Packaging: Bags of 25 kg.

Floor leveling cementious screed

FLOWCRET 1-10 EXPRESSFast-setting, self-leveling, polymer-modified cementitious screed

It is applied in a thickness of 1-10 mm. Ideal for quick repairs, as it can be walkable after 3 hours and covered after 24 hours. Colour: White, grey.

2 Consumption: Approx. 1.65 kg /m /mm of layer thickness. Packaging: Bags of 25 kg.

Ideal for fast smoothening and leveling of concrete or mortar floors that are going to be covered with all kinds of tiles, carpet, parquet, vinyl tiles etc.

UNICRETMortar for plastering and masonry worksColour: Grey, white.

2Consumption: Approx. 15.5 kg/m /cm. Packaging: Bags of 25 kg.

UNICRET-FASTFast-setting, white repairing mortarIdeal for quick plaster repairs in old and new constructions. Replaces the use of gypsum in respective applications.Colour: White.

2Consumption: Approx. 15 kg/m /cm. Packaging: Bags of 5 kg and 25 kg.

REPAIRING MORTARS

RAPICRETFast-setting cement patching mortarIdeal for patching and repairing concrete elements, fixing, anchoring, cavity sealing, formation of grooves etc. and generally when considerable strength and fast work are needed.Colour: Grey.

2Consumption: Approx. 17.5 kg/m /cm. Packaging: Bags of 5 kg and 25 kg.

MEGACRET-40High-strength fibre-reinforced repairing mortarSuitable for highly demanding repairs of concrete elements. It is applied in layers up to 40 mm thick (per layer), by trowel or gunite machine.Colour: Grey.

2Consumption: Approx. 17.5 kg/m /cm. Packaging: Bags of 5 kg and 25 kg.

DUROCRET Polymer-modified cement mortarSuitable for patching and repairing concrete, masonry and plaster, formation of grooves or ridgepoles etc. Colour: Grey, white, redbrown.

2Consumption: Approx. 15 kg/m /cm. Packaging: Bags of 5 kg and 25 kg.

DUROCRET-FAST Fast-setting, repairing cement mortarSuitable for repairs on concrete, cement mortars, masonry, plasters and generally wherever high strength and fast application is necessary.Colour: Grey.

2Consumption: Approx. 17 kg/m /cm. Packaging: Bags of 25 kg.

FERROSEALCement-based anticorrosive coating for reinforcement elements - Bonding agentPolymer-modified brushable cement mortar used for protecting reinforcement elements from corrosion and for creating the bonding layer between old and new concrete or mortar. Colour: Redbrown. Consumption: As anticorrosive coating: 70-130 g/m of reinforcement element.

2As bonding agent: approx. 2.0 kg/m . Packaging: Containers of 1 kg, 5 kg and 15 kg.

FLOWCRET 3-30 EXPRESS

It can be used in a thickness of 3-30mm. Ideal for quick repairs, as it can be walkable after 3 hours. Moreover, it can be covered after 24 hours.Colour: Grey.

2 Consumption: Approx. 1.65 kg /m /mm of layer thickness. Packaging: Bags of 25 kg.

Fast-setting, self-leveling, polymer-modified compoundSuitable for smoothing and leveling of concrete or mortar surfaces before laying finishing materials like tiles, carpets, parquet, vinyl tiles, marbles etc.

19

FLEX-PRIMER High quality acrylic water-based primerIn combination with the highly elastic waterproofing paint FLEXCOAT, it forms an ideal system for the waterproofing of walls. Colour: White.

2Consumption: 0.1-0.2 kg/m . Packaging: Plastic containers of 1 kg, 5 kg, 10 kg and 20 kg.

FLEXCOAT High quality, elastic, waterproofing paintSuitable for painting and waterproofing walls, protecting of bituminous layers, coloring and waterproofing asbestos-cement roofs etc. For exterior and interior use. Colour: White and 1420 selected.

2Consumption: 125 ml/m /layer.Packaging: Plastic buckets of 3 lit and 10 lit.

VS-1Ready-to-use, transparent aUsed to impregnate and brighten up natural stones (slate or sinter stones etc.) and artificial building materials (decorative bricks, roof tiles etc). VS-1 brings out the natural color of the material on which it is applied, protecting at the same time from the influence of rainwater and atmospheric pollution. It is applied on walls and floors, indoors or outdoors. Colour: Transparent.

2Consumption: 150-200 ml/m per layer, depending on the absorptivity of the surface. Packaging: Cans of 1 lit and 4 lit.

crylic stone varnish

NANO-SEAL

Colour: Light blue.

2Consumption: 0.1-0.2 kg/m . Packaging: Plastic containers of 1 kg and 5 kg.

Waterproofing and stabilization of surfacesIt is used to protect porous substrates from moisture and salt strains, such as concrete, masonry, plaster, gypsum boards, chip boards, natural stone etc. It has also the ability to harden weak substrates, such as plasters etc. Suitable for indoor and outdoor application.

ISOMAT AG 77Brushable, aIt protects surfaces from sprays or paint graffiti, environmental impurities etc. Permitting easy cleaning of the surface, without affecting their structure appearance. Colour: White (transparent after drying).

2Consumption: 50-100 ml/m .Packaging: Plastic buckets of 1 lit and 3 lit.

nti-graffiti protection emulsion

PLANFIXPolymer-modified cement puttyIt is used for repairing and puttying exposed concrete, fixing of pores or cavities etc. Colour: Grey, white.

2Consumption: Approx. 1.3 kg/m /mm. Packaging: Bags of 5 kg and 25 kg.

STUCCOCRETSpatula puttySuitable for smoothing and preparing wall surfaces to be covered with paint or other coatings. It is applied on surfaces made of concrete or plaster. Replaces oil stuccos and other similar materials. Colour: White.

2Consumption: Approx. 1.1 kg/m /mm. Packaging: Bags of 4 kg, 10 kg and 20 kg.

FLEX-COVER2-component, flexible puttyIt consists of a cement-based powder (component A) and a resin emulsion (component B). Suitable for sealing and waterproofing joints and cracks, on walls or floors. It can be also used on window recesses, junctions between floors and walls, as well as for puttying surfaces with hair-cracks. To be applied on plaster, cement, gypsum boards, wood etc. Ideal for outdoor applications. Colour: White. Consumption: Joint 5 mm x 5 mm: 40 g/m of joint length.

2Puttying: 1.6 kg/m /mm.Packaging: Plastic buckets of 2.6 kg (A+B).

PAINTS & PROTECTIVE MATERIALS

PUTTIES

PLANFIX-FINEPolymer-modified cement putty, extra fine-gradedIt is uded for repairing and puttying exposed concrete. It can be also applied using a gunite machine. Colour: Grey, white.

2Consumption: Approx. 1.3 kg/m /mm. Packaging: Bags of 5 kg and 25 kg.

FAST-COVERReady-to use, lightweight acrylic spackling puttyIdeal for filling and patching cracks and holes of any kind, in a single step. It is applied on plaster, gypsum board, wood etc. at a maximum thickness of 5 cm. It does not crack and it doesn’t need to be rubbed. Painting follows after 30 minutes. For indoor and outdoor application. Colour: White. Packaging: Plastic buckets of 0,5 lit, 1 lit and 5 lit.

PS-21 (ex PROTESIL)Ready-to-use, silicone-based solution without solvents for waterproofingIt is suitable for waterproofing of tile joints and the protection against rain effect of various surfaces. It can be used even on slightly wet substrates. Colour: Transparent when dry.

2Consumption: 200-400 ml/m . Packaging: Plastic containers of 1 lit, 5 lit and 20 lit.

NANOPRO-M Nano-impregnation for protecting marblesWater-based emulsion with highly penetrating ability based on nano-molecular structure. It is used to protect from moisture and stains unporous substrates such as surfaces of polished marbles, granites, tiles, porcelain etc. Suitable for indoor and outdoor application. Color: White (transparent when dry).


NANOPRO-CNano-impregnation for protecting porous surfacesWater-based emulsion with high penetrating ability, based on nano-molecular structure. Ideal for protecting from moisture and salt stains porous substrates such as surfaces of concrete, masonry, plaster, tile grouts, natural stones etc. Suitable for indoor and outdoor application. Colour: White (transparent when dry).


PS-20 Ready-to-use, silicone-based, transparent solution for waterproofingIt ensures extremely high water-repellence and long term protection. It can be applied on various surfaces for their protection against rain effect. Also it is suitable for waterproofing of tile joints. Colour: Transparent.

2Consumption: 200-400 ml/m . Packaging: Cans of 1 lit, 3 lit and 20 lit.

(ex PROTESIL)

20

TILE ADHESIVES

ISOMAT AK 11 Polymer-modified, cement-based tile adhesive C2ESuitable for fixing granite tiles and generally absorptive or non-absorptive wall or floor tiles on various substrates such as concrete, brickwork, plaster etc. For indoor and outdoor applications. It is classified as type C2 E adhesive according to EN 12004. Colour: Grey, white.

2Consumption:1.5-4.0 kg/m .Packaging: Bags of 25 kg.

ISOMAT AK 12 High quality, polymer-modified, cement-based tile adhesive C2 TESuitable for fixing granite tiles and generally absorptive or non-absorptive wall or floor tiles on various substrates and especially where high adhesion and resistance to moisture are required. It is qualified as non-slip (zero slipping of the tile). For indoor and outdoor applications. It is classified as type C2 TE adhesive according to EN 12004. Colour: Grey, white.

2Consumption: 1.5-4.0 kg/m . Packaging: Bags of 25 kg.

ISOMAT AK 9 Cement-based tile adhesive C1Suitable for fixing ceramic tiles on walls or floors on surfaces made of concrete, brickwork, plaster etc. For indoor and outdoor applications. It is classified as type C1 adhesive according to EN 12004. Colour: Grey, white.

2Consumption: 1.5-4.0 kg/m . Packaging: Bags of 25 kg.

ISOMAT AK 10 High quality, cement-based tile adhesive C1 TSuitable for fixing ceramic tiles on walls or floors on surfaces made of concrete, brickwork, plaster etc. It is qualified as non-slip (zero slipping of the tile). For indoor and outdoor applications. It is classified as type C1 T adhesive according to EN 12004. Colour: Grey, white.

2Consumption: 1.5-4.0 kg/m .Packaging: Bags of 5 kg and 25 kg.

ISOMAT AK 20 High quality, polymer-modified, cement-based, non-slip tile adhesive C2 TE S1Suitable for fixing absorptive or non-absorptive tiles (e.g. “gres porcelanato”), large tiles etc. on walls or floors on substrates with high demands for adhesion, elasticity and moisture resistance (e.g. old tile layers, floors with in-floor heating etc.). Possesses increased open time. For indoor and outdoor applications. It is classified as type C2 TE S1 adhesive according to EN 12004 and EN 12002. Colour: Grey, white.

2Consumption: 1.5-4.0 kg/m . Packaging: Bags of 5 kg, 15 kg and 25 kg in white and 5 kg and 25 kg in grey colour.

ISOMAT AK 22 Flexible, high quality, polymer-modified, cement-based, tile adhesive C2 TE S1It is suitable for fixing absorptive or non-absorptive tiles (e.g. “gres porcelanato”), large tiles, glass mosaic tiles etc. on walls or floors on substrates with particularly high demands for adhesion, elasticity and moisture resistance (e.g. floors with in-floor heating, metallic surfaces, swimming pools, gypsum board etc.). Possesses increased open time. For indoor and outdoor applications. It is classified as type C2 TE S1 adhesive according to EN 12004 and EN 12002. Colour: Grey, white.

2Consumption: 1.5-4.0 kg/m . Packaging: Bags of 5 kg, 15 kg and 25 kg in white and 5 kg and 25 kg in grey colour.

ISOMAT AK-ELASTIC Elastic, 2-component, tile adhesive for highly demanding applications C2 E S2

EN 12004 and EN 12002. Colour: White.

2Consumption: 1.5-4.0 kg/m . Packaging: Bags of

high quality

Suitable for fixing tiles of every type on walls or floors, on vibrative or dimensionally unstable substrates like gypsum board, chipboard, floors with in-floor heating, terraces, balconies, swimming pools etc. Combined with the elastic sealing slurry AQUAMAT-ELASTIC, it provides a perfect system for sealing and fixing. It is classified as type C2 E S2 adhesive according to

35 kg (25 kg A+10 kg B) and 7 kg (5 kg A+2 kg B).

ISOMAT AK-RAPID Fast-setting polymer modified, cement-based, tile adhesive C2 FTSuitable for fixing absorptive or non-absorptive tiles on walls or floors on surfaces made of concrete, brickwork, plaster etc. Ideal in cases where the surfaces have to be delivered fast for use, e.g. work areas etc. It is qualified as non-slip (zero slipping of the tile). For indoor and outdoor applications. It is classified as type C2 FT adhesive according to EN 12004. Colour: Grey, white.

2Consumption: 1.5-4.0 kg/m . Packaging: Bags of 5 kg and 25 kg in white and 25 kg in grey colour.

21

CLEANING AGENTS

CL-CLEANTile and natural stone cleanerRemoves lime residues, plaster, cement etc. Colour: Transparent.

2Consumption: 0.15-0.2 kg/m , depending on residue type.Packaging: Plastic containers of 1 kg, 5 kg and 20 kg.

FD-CLEAN Oil/grease remover from concrete floorsRemoves oil and grease residues from concrete floors by emulsification. Colour: Transparent.

2Consumption: 0.8-1.0 kg/m , depending on floor absorptivity and its fatigue by oils or fats. Packaging: Plastic containers of 4 kg and 18 kg.

IMPROVING RESINS

ADIPLASTPolymer latex for multiple improvements of mortarsImproves the properties of mortars in several ways offering, e.g. increased bonding to substrate, flexibility, shrinkage reduction, higher resistance to chemical effects and abrasion, enhanced water impermeability etc. Ideal for creating the bonding layer between old and new concrete or mortar. Colour: White. Consumption: Added to the mixing water in proportion of ADIPLAST : water = 1:1 to 1:5. Packaging: Plastic containers of 1 kg, 5 kg, 12 kg and 20 kg. Drum of 150 kg.

DS-99Additive for tile adhesives and joint groutsIt increases the bonding to the substrate, the flexural and compressive strength, the abrasion, the resistance to chemicals and frost. It also improves flexibility and offers water impermeability.Colour: white. Consumption: Added to the mixing water in proportion of DS-99 : water = 1:1 to 1:2. Packaging: Plastic containers of 1 kg, 5 kg and 20 kg.

ELASTIC JOINT SEALANTS

ISOMASTIC-A

Suitable for sealing work joints, thin expansion joints or plaster cracks in interior or exterior areas. Also suitable for slightly wet surfaces. Easily paintable.

Joint 10 mm x 10 mm: 1 cartridge/2.8 m of joint length. Joint 5 mm x 5 mm: 1 cartridge/11.2 m of joint length.

Cartridges of 280 ml.

Elastoplastic acrylic sealant

Colour: Grey, white.Consumption:

Packaging:

TILE GROUTS

MULTIFILL 2-5 classified as type CG2

Cement-based colored grout for pointing tile joints on walls or floors, for indoor and outdoor applications. Suitable for joint widths up to 5 mm. It is classified as type CG2 WA tile grout according to EN 13888. Colour: 34 color shades.

2Consumption: 0.2-2.0 kg/m .Packaging: Bags of 2 kg, 5 kg and 25 kg.

Coloured tile groutMULTIFILL 3-15

classified as type CG2Cement-based colored grout for pointing tile joints on walls or floors, for indoor and outdoor applications. Suitable for joint widths from 3 mm to 15 mm. It is classified as type CG2 tile grout according to EN 13888. Colour: 20 colour shades.

2Consumption: 0.2-2.0 kg/m . Packaging: Bags of 5 kg and 25 kg.

Coloured tile grout

MULTIFILL SMALTO 1-8Tile grout with porcelain effect, water-repellentColored, cement based tile grout enriched with resins. It offers high mechanical strength, superb color stability and great water-repellence. Contains special bacteriostatic agents, which block the formation of bacteria on the grout. It gives a smooth and glossy final surface. Suitable for joint width 1-8 mm. It is classified as type CG2 WA tile grout according to EN 13888.

2Colour: 34 colour shades. Consumption: 0.2-2.0 kg/m . Packaging: Bags of 2 kg, 5 kg and 25 kg.

22

0712

THESSALONIKI, GREECEth17 km Thessaloniki - Ag. Athanasios Road

P.O. BOX 1043, 570 03 AG. ATHANASIOS, GREECEΤ +30 2310 576 000, F +30 2310 722 475

ISOMAT S.A.ΒUILDING CHEMICALS & [email protected]

ISOMAT_Repairs & maintenance

Documents

Transcript of ISOMAT_Repairs & maintenance