Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
-
Upload
jagabandhupatra -
Category
Documents
-
view
215 -
download
0
Transcript of Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 1/16
See discussions, stats, and author profiles for this publication at: https://www.researchgate.net/publication/290452976
Ionic liquids and their solid-state analogues asmaterials for energy generation and storage
ARTICLE · JANUARY 2016
DOI: 10.1038/natrevmats.2015.5
READS
241
12 AUTHORS, INCLUDING:
Mega Kar
Monash University (Australia)
6 PUBLICATIONS 55 CITATIONS
SEE PROFILE
Jennifer M Pringle
Deakin University
92 PUBLICATIONS 3,192 CITATIONS
SEE PROFILE
Hiroyuki Ohno
Tokyo University of Agriculture and Techno…
525 PUBLICATIONS 13,480 CITATIONS
SEE PROFILE
Masayoshi Watanabe
Yokohama National University
350 PUBLICATIONS 14,367 CITATIONS
SEE PROFILE
All in-text references underlined in blue are linked to publications on ResearchGate,
letting you access and read them immediately.
Available from: Maria Forsyth
Retrieved on: 30 January 2016
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 2/16
Ionic liquids (ILs) possess unique properties thatmake them highly attractive for a range of applications(BOX 1). As solvent media for materials synthesis, theirhigh thermal stability and their ability to dissolve awide range of metal and organic compounds providenew preparative directions. In the context of electro-chemical applications and devices, these properties,coupled with high intrinsic ion conductivity, makethem attractive as high-stability electrolyte materials.Their strong electrostatic interactions render them vir-tually non-volatile and therefore of low flammability.On the other hand, the structural variety in their com-ponent molecular ions provides an enormous range of
solvency properties, which are unparalleled in otherliquid media.
In this Review, we highlight recent developments inthe application of ILs and their solid-state analogues,organic ionic plastic crystals (OIPCs), in the field ofenergy materials. Without question, sustainable gener-ation and storage of energy is one of the great challengesof our time. There are many alternative technologiesunder active development, in particular for ‘distributed’generation and storage at the community and house-hold levels. These developments demand electroactivematerials and electrolytes with high energy-storageand power-delivery capacity, and safety of operation.
In this context, ionic materials have much to offer, andthe breadth of their ‘designable’ properties creates newpossibilities in materials synthesis and design.
We focus on recent developments in the use of ILsas media for the preparation of electroactive materialsand on the electrochemical application of ILs in a rangeof sustainable energy technologies. Because the litera-ture is voluminous, we focus our attention on importantdevelopments in the period since 2012; readers inter-ested in delving further into earlier work can accessthe literature via these recent papers. Several reviewshave appeared in recent years, and we refer the readerto these for a more historical account of each field1–3. A
glossary of nomenclature abbreviations and molecularstructures of the compounds described in this Reviewis provided in TABLE 1.
Space limitations preclude discussion of two impor-tant areas of energy technology in which ILs have thepotential to have a considerable impact: CO
2 capture
and nuclear fuel processing. Both of these require spe-cific and unique functionality in the IL and are there-fore most appropriately discussed in dedicated reviews.We also set aside the interesting, but distinctly sepa-rate, topic of ILs used as salts in solvent-based media,in which the IL nature of the salt is often insignificant,and behaviour is dominated by the solvent properties.
1 ARC Centre of Excellence for
Electromaterials Science,
School of Chemistry, Monash
University, Clayton, Victoria
3800, Australia.2 ARC Centre of Excellence for
Electromaterials Science,
Institute for Frontier Materials,
Deakin University, Burwood,
Victoria 3125, Australia.3Helmholtz Institute Ulm,
Helmholtzstraße 11, 89081
Ulm, Germany and Karlsruhe
Institute of Technology, PO
box 3640, 76021 Karlsruhe,
Germany.4Functional Ionic Liquid
Laboratories (FILL), Graduate
School of Engineering, Tokyo
University of Agriculture and
Technology, 2-24-16
Nakacho, Koganei, Japan.5Department of Chemistry and
Biotechnology, Yokohama
National University, 79–5
Tokiwadai, Hodogaya-ku,
Yokohama 240–8501, Japan.6 Department of Polymer
Science and EngineeringCollege of Chemistry,
Chemical Engineering and
Materials Science, Soochow
University, Suzhou, 215123,
China.7 Department of Materials
Chemistry, Nankai University,
Tianjin, 300071, China.
Correspondence to D.R.M.
douglas.macfarlane@
monash.edu
Article number: 15005
doi:10.1038/natrevmats.2015.5
Published online 12 Jan 2016
Ionic liquids and their solid-stateanalogues as materials for energygeneration and storageDouglas R. MacFarlane1, Maria Forsyth2, Patrick C. Howlett 2, Mega Kar 1,
Stefano Passerini 3, Jennifer M. Pringle2, Hiroyuki Ohno4, Masayoshi Watanabe5,
Feng Yan6 , Wenjun Zheng 7 , Shiguo Zhang 5 and Jie Zhang 1
Abstract | Salts that are liquid at room temperature, now commonly called ionic liquids, have
been known for more than 100 years; however, their unique properties have only come to lightin the past two decades. In this Review, we examine recent work in which the properties of
ionic liquids have enabled important advances to be made in sustainable energy generation
and storage. We discuss the use of ionic liquids as media for synthesis of electromaterials,
for example, in the preparation of doped carbons, conducting polymers and intercalation
electrode materials. Focusing on their intrinsic ionic conductivity, we examine recent reports
of ionic liquids used as electrolytes in emerging high-energy-density and low-cost batteries,
including Li-ion, Li–O2, Li–S, Na-ion and Al-ion batteries. Similar developments in electrolyte
applications in dye-sensitized solar cells, thermo-electrochemical cells, double-layer
capacitors and CO2 reduction are also discussed.
NATURE REVIEWS | MATERIALS ADVANCE ONLINE PUBLICATION | 1
REVIEWS
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 3/16
Electrode materials synthesis in IL media
In this section, we review the IL-based synthesis of elec-troactive materials, including conducting polymers,doped carbons, battery anode and cathode intercalationcompounds, and electrocatalysts. Although the ‘green’credentials of ILs as reaction media have been widelydiscussed, our emphasis is on the special properties ofthe resultant materials that can be obtained owing totheir IL origins.
Conducting polymers. Conducting polymers (CPs) areunique materials in that their synthesis and electrochem-ical cycling (from the neutral, non-conductive state to thecharged, ‘doped’ conductive state) rely on ion insertionor de-insertion from the electrolyte. Thus, the nature ofthe ions, their high concentration and the extent of inter-calation into the polymer, can influence properties such
as the morphology, electrochemical activity, conductivityand stability 4. Interestingly, the anions that are effectivein forming ILs, such as [NTf
2]−, [OTf]−, [PF
6]−, [fsi]− and
[fap]−, are also those that dominate the family of inter-calating ions (also known as dopants) for CPs; this com-monality stems from the fact that some properties, suchas charge delocalization and electrochemical stability,are key to both families of materials. The advantages ofsynthesizing CPs in ILs often include improved mono-mer solubility, and access to higher monomer oxidationpotentials and higher polymer n- and p-doping potentials.CP films electrodeposited from ILs are also commonlysmoother than those from molecular solvents4. A detaileddiscussion of electro-polymerization of CPs in IL mediahas recently been published5.
Poly(3,4-ethylenedioxythiophene), PEDOT, has acentral role in applications including actuators, electro-chromics, organic light-emitting diodes and organicsolar cells. The nature of both the anion and cation ofthe IL electrodeposition medium from which PEDOTis synthesized can influence its resistance, as recently
demonstrated for deposition onto a Pt(111) surface6;the resistance of the IL/PEDOT interface for the oxi-dized film and the total resistance of the reduced filmwere observed to follow the trend [C
4mmim][NTf
2] >
[C4mim][OTf] > [C
2mmim][NTf
2] > [C
2mim][NTf
2],
whereas the effect on the ion-exchange rate duringredox switching followed the trend [C
4mmim][NTf
2] <
[C2mmim][NTf
2] < [C
4mim][OTf] < [C
2mim][NTf
2].
This study also demonstrated the presence of two poly-mer redox processes and the high doping levels that canbe achieved by growth in ILs. Alternatively, the propertiesof PEDOT can be enhanced by chemical functionaliza-tion with an IL moiety, such as an imidazolium group, orby combination with polymerized ILs to form more sta-ble IL–CP materials7. PEDOT, with good catalytic activityfor the oxygen reduction reaction (ORR), has recentlybeen electrochemically deposited onto flexible carboncloth from [C
4mpyr][NTf
2] using a sandwich-cell con-
figuration8, producing better polymer film coverage andimproved performance compared with analogous filmsgrown in acetonitrile.
The synthesis of CPs in ILs is also a viable route toenhancing optical and electrical properties. For exam-ple, poly(pyrrole) and PEDOT have recently beencopolymerized in [C
4mim][BF
4] at different ratios to
alter the resultant morphologies and spectro-electro-chemical behaviour9, which is pertinent to applica-
tion in electrochromics. New monomers continue tobenefit from electro-polymerization in ILs, as exem-plified by the asymmetric sulfur analogue of PEDOT,poly(thieno[3,4-b-]-1,4-oxathiane) — grown in [C
4mim]
[PF6] — which shows very promising electrochromism10.
The monomer oxidation potential is advantageouslylower in the IL, and the polymer displays a smoother andmore uniform morphology than that grown from dichlo-romethane, as well as higher electrochemical activity,conductivity, doping levels and stability (10,000 cycles).
Inevitably, given the burgeoning field of nanotech-nology, attention is turning to the development of CPswith nanometre-scale morphologies. For example,
Box 1 | Turning a salt into a liquid
120°187°
115 pm
131 pm
N –
N
N+ N
N
a b
Ionic liquids (ILs), also known as room-temperature molten salts, are a large family
of recently discovered liquid salts usually comprising organic cations and various
anions, such as I−, BF4
− and CF3SO
3−. They have many features in common with
simple, often very-high-melting-point salts, such as NaCl. However, the separation
between the large molecular ions in an IL weakens and shields the electrostaticforces between the ions, lowering the melting point. Another molecular feature
that assists in lowering the melting point is delocalized charges. For example, in the
dicyanamide ion (see the figure, panel a) the bond lengths and angles determined
from crystal structures indicate that the negative charge is spread over all three
nitrogen atoms, further weakening the electrostatic interactions. Similarly, the
positive charge in the imidazolium cation (see the figure, panel b) is delocalized
across the N–C–N bonds of the five-membered ring.
The combination of these two ions produces a very well-known IL, ethylmethylim-
idazolium dicyanamide ([C2mim][dca]), which has a melting point of −21 °C. The
weakening of the electrostatic interactions between the ions by the charge
delocalization effect also increases the mobility of the ions in the liquid state;
[C2mim][dca] is thus one of the most fluid ILs known. Low symmetry, or preferably a
complete lack of symmetry, in one or both of the ions is also a common feature of
IL-forming ions, as this prevents efficient packing into a low-energy crystal
structure, thereby further lowering the melting point. The rich variety of N- andP-based cations available, coupled with an equally vast family of inorganic and
organic anions, creates a potentially enormous family of ILs, with the different ions
producing a wide range of tunable properties.
As liquid salts, ILs typically exhibit significant ion conductivity that makes them
ideal as electrolytes. They also exhibit very low vapour pressure and low
flammability. The mix of electrostatic, hydrogen-bonding and hydrophobic types of
interaction that exist in an IL create powerful and tunable solvency properties; they
can be water soluble or miscible, or strongly water repellent. Equally, they can be
excellent solvents for inorganic salts and for proteins.
For applications in which a solid form of the IL is more desirable, several soft
material versions of ILs have been developed, including poly(ILs) and gels,
sometimes known as ionogels. Moreover, solid-state analogues, so-called organic
ionic plastic crystals (OIPCs), are an emerging alternative (BOX 2).
REV IEWS
2 | ADVANCE ONLINE PUBLICATION www.nature.com/natrevmats
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 4/16
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 5/16
graphitization and conductivity 24,25. Interestingly, a sim-ple relationship between the N/C molar ratio and theN content of the doped carbons was observed, and theupper limit of N content was found to be strongly relatedto the carbonization temperature26.
IL-based carbonaceous materials have found applica-tion as ORR electrocatalysts24,27,28. The high N content isbelieved to provide abundant electrocatalytically activesites, as the N-dopants can induce charge delocalizationand change the chemisorption mode, which effectivelyweakens the O–O bonding and facilitates the ORR 29.The excellent activity is reflected by onset and half-wavepotentials, and kinetic current density comparable tothose of commercial Pt/C fuel-cell materials24,27,28.
Electroactive materials by ionothermal synthesis in ILs. Since the concept of ‘ionothermal’ synthesis of materi-als using an IL solvent was proposed by Morris30, themethod has been extensively used for the fabrication ofinorganic nanomaterials and IL–inorganic hybrids31–35;Eshetu et al.33 recently provided a useful review of the
field. In general, the IL acts as a reaction medium withhigh thermal and chemical stability 36, and it can also actas a structure-directing agent owing to its highly struc-tured architecture37. Recently, open-framework fluoridematerials for Li and Na battery cathodes were prepared bythis method38, whereby the dehydration process was facil-itated by infiltration of, and capping by, the IL [C
4mim]
[BF4], resulting in FeF
3·0.33H
2O with a conversion yield
of 100%. Jana et al.39 prepared flowerlike hierarchicalarchitectures of layered SnS
2 using [C
2mim][BF
4] as the
reaction medium to produce nanosheet-petals of SnS2.
Mali et al.40 synthesized TiO2 with a nanoflower morphol-
ogy using an imidazolium IL, achieving a high degree ofcrystallization even at mild annealing temperatures. Theuse of ultrasonic irradiation for materials synthesis in ILshas also been reviewed recently 41.
Another excellent example of the tunable morpholog-ical and electrochemical features made possible by thissynthetic approach, Choi et al.42 reported the [C
4mim]
[BF4]-based synthesis of IL–Co(OH)
2 hybrid electrode
materials with tailored geometric morphology for appli-cation in supercapacitors. The Co(OH)
2 hybrids exhib-
ited surface areas of up to 400 m2 g−1 (with a mesoporesize of 4.8 nm) and retained a surface adsorbed layer ofIL; this layer enhances the pseudo-capacitance of theelectrode, which allowed specific capacitance as high as859 F g−1 to be achieved. Density functional theory (DFT)calculations were used to probe the effect of the IL onthe pseudo-capacitive redox reactions of Co(OH)
2 at
the molecular level; under anodic potentials, the processwas found to involve the loss of a f irst electron–hydro-gen pair and then a second pair, ultimately producingCoO
2. The optimized structures of [C
4mim][BF
4] on the
Co(OH)2 surface are shown in FIG. 1; the [C
4mim]+ cation
facilitates hydrogen desorption from the surface. Thehydrogen desorption energies are smaller than that of abare Co(OH)
2 surface, thus lowering the energy barrier
to the pseudo-capacitive process. Such hybrid materialsproduced by ionothermal synthesis hold considerablepromise for enhanced electrochemical properties.
Electrocatalyst deposition from IL media. ILs are widelyrecognized as media for the electrodeposition of met-als and semiconductors. The general methodologyand advantages of electrodeposition in IL media havebeen reviewed elsewhere5. Deposition of various semi-conducting materials has been explored, in particularby the Endres43 group, as exemplified by their recentdescription of the preparation of crystalline Ga-dopedGe and Si
x Ge
1−x from an IL medium. IL media have also
been used for the electrodeposition of a broader rangeof electrocatalytic materials; for example, birnessite-typeMnO
x has been used as a water oxidation catalyst 44,45.
Similarly, ILs have recently been used to deposit highlycatalytically active forms of Pd46,47 for the ORR in fuelcells and MoS
x for the hydrogen evolution reaction48.
CoNi@Pt core–shell mesoporous nanorods with veryhighly active surfaces for methanol electro-oxidationhave also been developed using IL electrodepositionmethods49. Thus, IL-based synthesis is opening up newapproaches to prepare electroactive materials with newmorphologies and excellent electrochemical properties.Further understanding of the roles of the ILs in these pro-cesses via systematic studies and theoretical simulationswould greatly facilitate progress in this field.
ILs as electrolyte materials
With their intrinsic ion conductivity, high metal-saltsolubility and high electrochemical stability, some IL
a
b
c
Box 2 | Organic ionic plastic crystals as solid-state ionic liquid analogues
Most ionic liquids (ILs) will, eventually, at some sufficiently low temperature, form a
crystalline solid. In certain families of organic salts, multiple crystal structures form as
a function of temperature, and the higher-temperature structures exhibit soft, plastic
mechanical properties and significant ion conductivity. These are often referred to as
organic ionic plastic crystals (OIPCs). The molecular structure of the ions is often
closely related to IL-forming ions; for example, [C4mpyr]+ often forms ILs, whereas the
smaller and more symmetrical [C2mpyr]+ forms OIPCs. The mechanical and transport
properties of OIPCs originate in rotational motions of one or both of the ions in the
crystal (see the figure); in other words, the ions can exhibit some of the motional
properties that are characteristic of the liquid without losing their 3D ordered
structure. This can produce ion conduction in the material, which thereby becomes
interesting and useful as a solid-state electrolyte.
REV IEWS
4 | ADVANCE ONLINE PUBLICATION www.nature.com/natrevmats
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 6/16
types are a natural fit to most battery electrochemistries,as long as the cost is not prohibitive. Several excellentreviews highlight the significant role that ILs can havein high-energy-density batteries, including Li-ion50,Na-ion51, Li–S (REF. 52,53) and Li–air54,55 systems; Karet al.56 have recently reviewed the broad application ofILs in metal–air battery systems.
Lithium batteries. Although ILs have not achieved large-scale application in commercial Li batteries, after morethan a decade of intense research, interest in their prop-erties as safe electrolytes continues unabated50. This hasbeen encouraged by growing recognition of the needto improve the charge–discharge cycling performanceof Li metal electrodes to enable the next generation ofhigh-energy-density batteries, such as Li–S or Li–air(also written as Li–O
2) batteries54,55. In Li–air configura-
tions, a high-specific-capacity anode is needed to matchthe enormous capacities of the air cathode; Bruce et al.54 provide an excellent review of this area. Research con-tinues to focus on small quaternary ammonium cations,particularly cyclic pyrrolidinium and piperidinium cat-ions, owing to their high chemical and electrochemicalstability (higher than [C
nmim]+) and relatively high con-
ductivity. For example, Elia et al.57 recently reported aLi–air cell based on [C
4mpyr][NTf
2] that exhibited an
82% charge–discharge energy efficiency.Enhancing the oxidative stability of the IL will ena-
ble the use of new high-voltage cathodes55. For example,Wu et al.58 recently reported stable cycling of a range ofhigh-voltage cathodes (notably Li
1.2Ni
0.2Mn
0.6O
2at 4.8 V)
in [C4mpip][NTf
2] using additives to stabilize both the
anode and cathode solid electrolyte interphases (SEIs).The SEI is typically a layer of breakdown products,which allows facile transport of Li ions, but otherwiselimits further breakdown reactions, thereby stabilizingthe interphase and increasing the cycle life of the bat-tery. The SEI may form entirely as a result of trace-levelimpurities (for example, water, oxygen and nitrogen),
but it may also involve the electrolyte and electrode com-ponents. Stable cycling of a 4.7-V LiNi
0.5Mn
1.5O
4 cell59
and a 4.5-V LiFe0.1
Co0.9
PO4 cell60 using [C
4mpyr][NTf
2]
electrolytes has also been reported. Recent reports ofsmall phosphonium cation ILs61,62 exhibiting propertiescomparable or superior to the best N-based electrolytesshould prompt a considerable expansion of studies usingthese cations. Theoretical investigations are also begin-ning to provide insights into the origins of the superiorconductivity and fluidity of these ILs63.
Anion choice is largely dominated by [NTf 2]− and
[fsi]−, again owing to their stability and conductivity,as well as their well-known SEI-forming properties.However, the cost of some anions is a limiting factor,especially for [NTf
2]−. Recent work 64 has shown that
Li cycling can be achieved in [dca]− ILs by doping witha small amount of water as an SEI-forming component.These ILs, which contain only H, C and N atoms, areintrinsically cheaper and also have superior transportproperties.
The [fsi] anion has attracted considerable attention as
a potentially less expensive ion65, with properties compa-rable or superior to those of [NTf
2]− (REF. 66). Matsui et al.67
demonstrated charge–discharge cycling of high-volt-age LiNi
1/3Mn
1/3Co
1/3O
2 cathodes in [C
2mim][fsi].
The benefits of high Li-ion concentrations have also beenrevealed in reports of high-performance Li cycling ininorganic–organic salt mixtures based on [C
3mpyr][fsi]
(REF. 68) or [P1,1,1,i4
][fsi] (REF. 61), in which the Li-salt con-centration can exceed 60 mol% (3.8 mol kg−1). Theseapproaches to the goal of a ‘liquid lithium salt’ supportthe notion that extremely high Li-salt concentrationscan be used to manipulate Li-ion transport properties69 to produce higher-rate charging than previously thoughtpossible (FIG. 2). At present, the [fsi] anion is unique inallowing the creation of these ambient-temperatureinorganic–organic IL mixtures; further investigationinto the reasons for this is required and may lead to thediscovery of other anions with similar properties.
Interest has also been driven by reports of enhancedLi-battery cycling performance in ILs compared withconventional electrolytes70. This is further highlightedby reports of inadequate Li-metal cycling performancein the ether-based electrolytes used for most Li–airstudies71. Grande et al.70 recently performed a carefulexamination of [C
4mpyr][NTf
2] in this context, reveal-
ing once again that the SEI-forming properties of the ILdictate the long-term cycling performance. Piper et al.72
demonstrated the stable cycling (77% capacity reten-tion after 100 cycles) of a high-capacity Si nanocom-posite anode architecture in a [C
3mpyr][fsi] electrolyte.
Theoretical simulations and surface analysis indicatedthe key role of the [fsi] anion in the formation of a sta-ble SEI, which promoted the structural integrity of thenanocomposite anode.
A key property in the context of Li–S cells is theability of the IL to limit the solubility of polysulfides,thereby reducing capacity loss due to the formation ofhigh-impedance phases and redox shuttle mechanisms.Excellent summaries of electrolytes used for Li–S cellshave recently been published73,74. The solubility of
N H O
O
FF
F
Box 3 | Mixing acids and bases to make protic ionic liquids
Protic ionic liquids (ILs) are liquid
organic salts prepared by the
neutralization of an organic base with
an acid. The acids can be any of the
very common (and inexpensive) acids
such as nitric, sulfuric or phosphoric
acid. Their ease of preparation and
inexpensive starting materials make
them some of the most easily utilized
ILs. A well-known example is
ethylammonium nitrate prepared by
the mixing of ethylamine and nitric
acid. The transferred proton remains chemically active and can participate in
synthetic and electrochemical applications, such as the hydrogen fuel cell and water
splitting. The proton can also be highly mobile, as desired in these applications and,
in some cases, it is transported via a water-like Grotthus mechanism. Proton acidity
tends to be lower in protic ILs, resulting in lower proton transfer than would be
expected on the basis of aqueous behaviour. The dynamic nature of the proton
transfer equilibrium also makes these ILs slightly volatile and potentially distillable.
Proton transfer between trifluoroacetic acid and methyl pyrrolidine, depicted in the
figure, produces another well-known example of a protic IL.
REV IEWS
NATURE REVIEWS | MATERIALS ADVANCE ONLINE PUBLICATION | 5
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 7/16
redox-active sulfur species (S8 and Li
2S
m) is reported to
be mainly dependent on the anion, with low solubilityresulting from the relatively weak coordination abilityof anions such as [NTf
2]− (REF. 75). Studies of SEI for-
mation in Li–S cells with [C4mpyr][NTf
2] also indicate
the importance of [NTf 2]− in maintaining a stable SEI,
although it is made more resistive by the presence of anouter, polysulfide-derived layer76.
Recently, ‘solvate’ ILs77, based on glyme–Li-saltmixtures, have attracted attention as safe, inexpen-sive electrolytes and have been shown to support thereversibility of the cathodic reaction in Li–air cells78.Blurring the lines further are reports of conceptuallysimilar, high-concentration ‘solvent-in-salt’ systems,which suppress polysulfide solubility in Li–S cells whileexhibiting excellent cycling performance79. For example,a 4 mol l−1 Li[fsi] in dimethoxyethane electrolyte exhib-its high Coulombic efficiencies and an excellent rateperformance of over thousands of cycles80.
New forms of Li-IL electrolytes include nanopar-ticle hybrids (cations tethered to SiO
2 nanoparticles).
For example, enhanced Li cycling was achieved when11 wt% [C
3mpip][NTf
2]–nanoparticle hybrid was added
to a standard electrolyte81. Solid electrolytes based on[C
3mpyr][NTf
2] confined inside a SiO
2–polymer matrix
also exhibit comparable performance to that of the pureIL in a Li–LiFePO
4 cell82.
Several ILs that exhibit OIPC phases have beenshown to support cycling in solid-state Li–LiFePO
4
cells83–85. These materials are solid-state analogues ofILs (BOX 2), in which there is substantial ion conductiv-ity due to crystal defects. These solid electrolytes offerconsiderable manufacturing advantages compared withliquid electrolytes in high-volume battery manufactureand are attracting increasing attention for this reason.
Sodium batteries. Room-temperature Na and Na-ionbatteries have recently attracted attention as a low-costenergy-storage technology 86. Researchers have typicallyused carbonate electrolytes to evaluate the electrodes87;however, these cause corrosion of the Na-metal anode,resulting in unstable cycling performance87. To avoidthis problem, IL-based electrolytes have been inves-tigated, with the additional benefit of their improvedsafety characteristics. Early work focused on inorganicsystems based on K[fsi] and Na[fsi] mixtures (m.p. ≈65 °C); cells using this electrolyte could be operatedat 90 °C using NaCrO
2 and Na
2FeP
2O
7 cathodes with
capacities close to 100 mAh g−1 (REF. 88). More recently,IL electrolytes composed of NaNTf
2 in [C
nmpyr][NTf
2]
or Na[fsi] in [C3mpyr][fsi] have been shown to facili-
tate stable Na deposition and stripping at temperaturesof up to 100 °C (REFS 89–91). Chagas et al.92 demon-strated a Na
0.45Ni
0.22Co
0.11Mn
0.66O
2 cathode operating
Figure 1 | Ionothermal synthesis of hybrid IL–Co(OH)2 capacitor materials. Optimized structures42 of free [C
4mim]
[BF4] (panel a) and [C
4mim][BF
4] on the Co(OH)
2 surface (panel b). Labels 1–4 in panel b represent the surface hydrogen
atoms beneath the [C4mim]+ cation or [BF
4]− anion. Adapted with permission from REF. 42, American Chemical Society.
a b
Side view
Top view
N F
Co
O H
CB
4
3
2
1
REV IEWS
6 | ADVANCE ONLINE PUBLICATION www.nature.com/natrevmats
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 8/16
at 4.6 V versus Na/Na+ with a Na[NTf 2]/[C
4mpyr][fsi]
electrolyte; this showed superior cycling stability incomparison with a carbonate-based electrolyte.
Similar to the high-concentration Li[fsi]-based sys-tems discussed above, excellent performance has beenreported for a Na-ion battery based on high-concentra-tion Na[fsi]–[C
3mpyr][fsi] electrolytes at 90 °C (REF. 93).
Current work indicates that the marked enhancement inNa electrochemistry arises from an unexpectedly high
transference number of Na ions90. Once again, such con-centrated metal–ion systems, in which [M+] > [IL
cation],
show great promise for energy-storage devices.There is also some evidence that mixed anions may
provide additional benefits in Na electrolyte systems94,95.Wang et al.75 investigated the effect of adding NaBF
4,
NaClO4, Na[NTf
2] or NaPF
6 to [C
4mpyr][NTf
2] and dis-
covered that NaBF4 produced remarkably higher ionic
conductivities than the other salts; however, the deviceperformance with a Na
0.44MnO
2 cathode was best with
NaClO4 and worst with NaPF
6, which correlated with
measurements of the interfacial resistance. Conversely,the mixture with NaBF
4 was optimal with a NaFePO
4
cathode95. Current understanding of these phenomena isthat metal speciation (the way in which the metal ion iscoordinated to the anions in the electrolyte) is crucial indetermining the ion transport, and the electrochemicaland interfacial behaviour at both the anode and cathode.Speciation has been explored in NaNTf
2/[C
nmim][NTf
2]
electrolytes, revealing that the coordination of Na isdifferent from Li, with sixfold coordination by three
anions96. Recent molecular dynamics simulations of aphosphonium PF
6− OIPC also demonstrated significant
differences between Na and Li coordination and theirresultant conduction mechanisms. Na+ has a preferencefor a higher coordination number in PF
6− electrolytes
compared with Li+, and rearrangement of this solvationenvironment dominates metal–ion transport97.
Magnesium, aluminium and zinc batteries. The depo-sition of Al and Mg from ILs has gained attention inthe past decade as the basis for emerging rechargeablemetal battery technologies. Both metals have very neg-ative reduction potentials (−2.3 and −2.4 V versus thestandard hydrogen electrode (SHE), respectively) andare cheaper and safer than Li or Na as battery materials.Based on the early work of Wilkes98,99 on chloroalumi-nate-based ILs such as AlCl
3/[C
2mim]Cl, Lin et al.100
recently developed an ‘ultrafast’ rechargeable Al battery.It demonstrated high currents (4 A g−1; more than 7,500cycles) at an energy density of 40 Wh kg−1, which is com-parable to lead–acid batteries. Unfortunately, these ILsare highly moisture sensitive and relatively expensive.Use of air-stable ILs that incorporate cations such as4-propylpyridine101 could increase the stability of thesesystems. Despite their high cost, these ILs show greatpromise for Al electrochemistry.
Investigation of ILs for Mg electrochemistry is at a
relatively early stage. Considerable work has been doneon establishing an efficient Mg primary cell, but furtherwork is required to develop rechargeable Mg batteries.Kakibe et al.102 demonstrated Mg cycling by the substi-tution of alkyl groups on cations such as [C
2mim]+ to
avoid unwanted reactions of the Mg surface with the C2proton on the imidazolium ring. By mixing the ILs withadditives103, Mg cycling can be enhanced, and undesir-able side reactions, such as hydrogen formation, can besuppressed. Studies on Mg electrochemistry using molec-ular solvents have been useful in the design of suitableILs. Recent work by Mohtadi et al.104 and Shao et al.105 has shown, in the case of Mg[BH
4]
2 in ethereal solvents,
Figure 2 | High rate cycling of lithium. a | Schematic of ionic liquid (IL)-based Li-ion
battery cell. b | LiCoO2 cells in an inorganic–organic IL at different charging rates from
1C (1-hour rate) to 5C (12-minute rate) for [C3mpyr][fsi] electrolyte (blue lines) and
organic electrolyte (red lines). The [C3mpyr][fsi] electrolyte comprises 50 mol%
(3.2 mol kg−1) Li[fsi] in [C3mpyr][fsi] and the organic electrolyte comprises 1 M LiPF
6 in
EC:DMC = 50:50 vol%. Panel b reprinted with permission from REF. 68. Copyright (2013),
The Electrochemical Society.
+
–
a
V o l t a g e d u r i n g c h a r g i n g ( V )
Charging capacity (mAh g–1)
4.20
4.15
4.10
4.05
4.00
4.95
0 20 40 60 80 100 120 140
b
Constant current cut-off: 4.2 V
[C3mpyr][fsi] electrolyte
Organic electrolyte
Hermeticallysealed case
Li metal anode
Ionic-liquid-impregnatedseparator membrane
LiCoO2 cathode layer
1C
2C
3C
4C
5C
REV IEWS
NATURE REVIEWS | MATERIALS ADVANCE ONLINE PUBLICATION | 7
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 9/16
that the electrochemical reversibility of Mg is improvedwhen THF is replaced by dimethoxyethane. This suggeststhat the presence of multiple ether oxygens, which candisplace the anion from metal-centred associated spe-cies, may be important for Mg deposition and stripping.Preliminary electrochemical studies have already demon-strated Mg cycling from ether-functional ILs106. The workof Mohtadi et al.104 also indicates that the anion must beweakly coordinating to Mg2+ to enable its release at theelectrode; earlier studies showed that NTf
2− complexes
with Mg2+ and ultimately degrades to form a passivatingfilm on Mg that hinders anodic dissolution107. Thus, ILswith very reductively stable but weakly coordinating ani-ons are a promising avenue of investigation in this area.
Although the reduction potential of Zn is not asnegative as Al or Mg (−0.76 V versus SHE), its electro-chemistry is still of interest owing to its low cost andhigh abundance. Much progress has been made onlong-term cycling of Zn in [N(CN)
2]− (REFS 108–110)
and [NTf 2]−-based111 ILs in the presence of co-solvents
such as water and dimethyl sulfoxide. Purpose-designedalkoxy-functionalized cations also hold promise asoptimized electrolytes for rechargeable Zn batteries,with more than 800 charge–discharge cycles havingbeen demonstrated112. Fluidic Energy Inc. has patenteda rechargeable Zn–air battery based on IL electrolytesand is currently commercializing these for large-scaleapplications113,114.
Dye-sensitized solar cells and thermocells
Dye-sensitized solar cells (DSSCs) are attractive photo-electrochemical devices because of their relatively highlight-to-electric conversion efficiencies and low pro-duction costs. In 2014, a record conversion efficiencyof 13% was achieved using a porphyrin-based dye in a
liquid electrolyte (acetonitrile)115. The non-volatility ofILs makes them ideal candidates for improving the long-term stability of DSSCs. Various ILs, especially from theimidazolium family, have been extensively studied; forexample, [C
2mim][B(CN)
4] and [C
2mim][N(CN)
2]
have exhibited efficiencies of more than 8%, althoughthe long-term stability still needs to be improved116.ILs based on triazolium cations have been studiedrecently 117, and the potential of ILs to operate effectivelywith porphyrin dyes has also been demonstrated118.
Recent developments in the application of ILs inDSSCs include functionalization of redox electrolytes.Among the alternative couples to the classic iodide/triiodide couple, cobalt complexes have attracted greatattention119; however, their limited solubility hindersapplication. Functionalization of CoII/III(bpy)
3 with
imidazolium cations improves both the redox poten-tial and solubility in IL electrolytes, with an overallpower conversion efficiency of 7.3% reported120 in a[C
3mim]I/[C
2mim][SCN] mixture at 1 sun (where
1 sun corresponds to standard illumination at AM1.5,
100 mW cm–2). Imidazolium-cation-functionalized2,2,6,6-tetramethylpiperidine-N -oxyl (TEMPO) wasalso synthesized and applied in DSSCs; this dual-redox-couple electrolyte gives a higher efficiency thanthose with a single redox couple121.
Devices based on liquid electrolytes generally suffer
from leakage issues. Incorporating ILs into a poly(IL)material or physically gelling them in inorganic nano-materials to form quasi-solid electrolytes has the poten-tial to eliminate leakage122–124. In addition, OIPCs havebeen shown to perform well, with efficiencies exceed-ing ~5%123–126 (FIG. 3). However, effective sealing is stillnecessary to ensure long-term stability, especially inhumid environments for hydrophilic OIPCs. Yanet al.124 recently reported water-resistant, solid-state DSSCsbased on a hydrophobic OIPC, [C
2mpyr][NTf
2],
which
produced >5% efficiency at 1 sun; the unsealed deviceexhibited long-term stability (>800 h) at 100% relativehumidity at 50 °C. Thus, looking to the future in this
Figure 3 | OIPC-based dye-sensitized solar cells. a | Current–voltage profiles of
various organic ionic plastic crystal (OIPC) materials, the optimum being [C1mpyr]
[N(CN)2] at around 5% solar efficiency. b | Differential scanning calorimetry (DSC)
thermogram and crystal structure of [C2mpyr][NTf
2] in phases IV and III, indicating a
greater extent of rotatory motion at the higher temperatures (the melting point of
this compound is 91 °C, at which point it becomes a highly conductive ionic liquid
(IL)). Adapted with permission from REF. 125, the Royal Society of Chemistry.
100 200 300 400 500 700 900 1,000
0
8
10
6
4
2
Voltage (mV)
C u r r e n t d e n s i t y ( m A
c m – 2 )
[C1mpyr][N(CN)
2]
[C1mpyr][I]
[Et4N][N(CN)
2]
[C2mpyr][BF
4]
[C1mpyr][PF
6]
[C1
mpyr][NTf 2
]
[C1mpyr][SCN]
a
b
–100 50–50 100 1500
Phase IV
Phase IV
Phase III
Phase III
Phase II Phase I Melt
Temperature (°C)
600 800
REV IEWS
8 | ADVANCE ONLINE PUBLICATION www.nature.com/natrevmats
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 10/16
field, IL gels and OIPCs offer considerable advantages,not only in improving the long-term stability of DSSCs,but also in offering the possibility of fabricating flexibledevices via reel-to-reel printing.
ILs are also enabling advances in thermo-electrochem-ical cells (TECs). TECs are devices that generate a voltagebetween two electrodes operating at different tempera-tures. Typically, these involve a redox couple in an elec-trolyte, similar to the DSSC electrolytes discussed above;in this case, it is the Seebeck coefficient, S
e = dE / dT , of
the redox couple (where E is the associated equilibriumpotential) that is the key thermodynamic property. Wasteheat-harvesting from industrial power stations is anattractive application; however, the typical temperatureregime (T
hot ≈ 130–150 °C; T
cold ≈ ambient temperature)
rules out most solvent-based electrolyte systems. Recentwork 127 has shown that IL electrolytes are well suited tothis application. S
e relates to the entropy change in the
redox reaction, which involves both the reaction entropyand the solvent reorganization entropy. The latter dependson the nature of the IL; S
e for the same redox couple can
range from 1.54 to 1.82 mV K−1 for CoII/III(bpy)3, indicat-ing a relatively subtle effect of the ion structure on thereorganization entropy 128–130. Effects of longer-range ILstructures may also contribute to this and are worthy offurther investigation. Similar to the other device appli-cations discussed, the transport properties, especially atT
cold, and thermal conductivity of the IL are crucial in
determining the overall efficiency 131; transport-propertylimitations at low temperatures can be overcome by rais-ing T
cold to 50–70 °C. Finally, mixtures of ILs with high-
boiling-point solvents such as methoxypropionitrile canenhance the transport properties. Under these conditions,with T
hot = 130 °C, a power output as high as 800 mW m−2
was obtained in an IL–solvent mixture132.
Electric double layer capacitors
ILs are also under intense investigation as safety- andenergy-enhancing electrolytes for electric double layercapacitors (EDLCs). This type of high-power devicestores energy in the electric double layer at the electrode/electrolyte interface, with the electrodes usually consist-ing of high-surface-area activated carbon. The electro-chemical stability imparted by ILs could considerablyincrease the operating voltage and thus the energy storagedensity (proportional to the square of the voltage)133,134.Conventional electrolytes for EDLCs predominantly con-sist of organic salts (for example, N
2,2,2,2BF
4) dissolved in
low-viscosity solvents, such as acetonitrile. Thus, as forthe other devices discussed above, the low flammabil-ity and negligible vapour pressure of ILs are attractiveproperties. The high ionic concentration of ILs is alsobeneficial in terms of weight-specific performance135.Unlike battery systems, the formation of SEIs is avoidedto improve internal resistance136; hence the voltage rangemust stay within the window of electrolyte stability: forexample, with [C
4mpyr][NTf
2], EDLCs are limited to
3.7 V (REF. 135), whereas, as discussed in the previous sec-tions, this IL can be used with cathode materials reaching4.6 V versus Na/Na+ (REF. 92). It has also become clear thatthere are capacitance-reducing ‘sieving’ effects with ions
that are too large for the pores of the activated carbon134;hence, there is considerable scope to tune the carbonmaterial to suit the chosen ions. ILs have also beensuccessfully used with high-volumetric-energy-densitygraphene in EDLCs137,138.
Mainly imidazolium and pyrrolidinium cations havebeen investigated for low-viscosity and cathodically sta-ble IL-based electrolytes134. More recently, sulfonium andazepenium cations have been considered — the formerfor its physicochemical properties and the latter owingto the reduced cost of the raw materials139,140. In mostcases, these cations are combined with fluorinated ani-ons such as [NTf
2]−, [fsi]−, [BF
4]− and [PF
6]−. As a result
of their increased anodic stability and size compatibilitywith activated carbons, high-performance EDLCs withhigh operating voltages between 3.0 and 3.5 V can berealized134,141. For cost and environmental reasons, theperformance of low viscosity, [dca]-based ILs was exam-ined, and it was found that these ILs exhibited highercapacity at increased current densities than the more
viscous [NTf 2]-based ILs142.
Carbon dioxide reduction and water splitting
Chemical or electrochemical conversion of CO2 is a
potentially effective means of energy conversion andstorage. By mimicking photosynthesis in nature, it isseen as part of a suite of globally important ‘artificialphotosynthesis’ technologies143,144. However, despitethe worldwide research effort to develop commercially
viable technologies for CO2 utilization, little progress
has been made because of the high kinetic stability ofCO
2 and the complexity of CO
2 conversion reactions. In
protic media, some routes for CO2 reduction are ther-
modynamically reasonable via proton-coupled elec-tron-transfer pathways. However, because hydrogenevolution is often thermodynamically and kineticallyfavoured, the Faradaic efficiency of CO
2conversion can
be very low. Thus, finding efficient and highly selectivecatalyst and media combinations for CO
2 reduction
is widely recognized as one of the grand challenges ofthe twenty-first century 145. A wide range of electrolytemedia with different levels of proton availability has beeninvestigated for CO
2 reduction; however, ILs have been
relatively little explored despite their attractive prop-erties (for example, high CO
2 solubility)146. ILs based
on the imidazolium cation have been the most widelystudied owing to the unique interaction between theelectroreduced form of imidazolium (that is, carbene)
and CO2 (or between imidazolium and CO2•−
) throughthe formation of a carbene–CO
2 complex147,148. Masel
and co-workers148 reported the electrocatalytic reduc-tion of CO
2 to CO in a [C
2mim][BF
4]–water mixture
with Faradaic efficiency greater than 96%. They postu-lated the formation of a more easily reducible carbenecomplex between CO
2•− and [C
2mim]+, with [C
2mim]+
acting as a co-catalyst for the reduction of CO2. An
in situ investigation of the reaction mechanism usingsum frequency generation spectroscopy 149 suggestedthat surface-adsorbed [C
2mim]+ plays an important
role via the formation of an adsorbed carbene–CO2
complex and by suppressing the hydrogen evolution
REV IEWS
NATURE REVIEWS | MATERIALS ADVANCE ONLINE PUBLICATION | 9
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 11/16
reaction. The role of [C2mim]+ has also been investi-
gated by Sun et al.147 in acetonitrile at a lead electrode.
It was found that the major products for CO 2 reductionwere CO and an imidazolium carboxylate species when[C
2mim][NTf
2] was used as the supporting electrolyte.
By contrast, the onset potential for CO2 reduction shifted
negatively and oxalate was the main product when[N
2,2,2,2][ClO
4] was used. Mechanisms for CO
2 reduction
(FIG. 4) have been proposed to explain the differences inproducts obtained; these are supported by the findings ofWatkins and Bocarsly 150 who studied the electrochemicalreduction of CO
2 at post-transition metal electrodes in
[C2mim][tfa]. No voltammetric process associated with
1,3-dimethylimidazolium carboxylate was detectedin the potential region in which CO
2 reduction was
observed. It was concluded that imidazolium carboxy-late does not contribute directly to the CO
2 reduction
current observed in [C2mim][tfa]. In other words, the
C2 position of the imidazolium ring is not catalyticallyactive under the conditions of the experiment. By con-trast, well-defined reduction processes associated withimidazolium carboxylates were reported by Cheeket al.151 in [C
4mpyr][OTf] at a Pt electrode. Clearly, the
medium and electrode materials affect the role of theimidazolium C2 position in the catalytic reduction ofCO
2, and further studies are required to understand and
optimize the role of the IL cation.During CO
2electroreduction, an accompanying and
sustainable oxidation reaction is needed. Water oxida-tion to O
2 is ideal because the amount of O
2 produced
would be negligible compared with atmospheric O2;
oxidation of water also produces the protons needed toreduce CO
2. However, in comparison with water oxida-
tion in aqueous media, this reaction has not been widelyexplored in ILs. It has been suggested that this processmay require a lower activation energy in ILs owing to
the disruption of the hydrogen bonding network oth-erwise present in liquid water 152. Investigation of wateroxidation in protic IL–water mixtures, based on butylammonium cations and various anions, has shown thatwater oxidation in these mixtures is diverted from itsusual (and energetically costly) four-electron pathwayinto the two-electron pathway that leads to H
2O
2 at
lower overpotentials44,153 (FIG. 5). Thus, this energeticallyefficient process offers an important direction for cost-effective CO
2 reduction. H
2O
2 is a valuable chemical,
but, if necessary, could be decomposed into water andoxygen to produce a completely sustainable process. Thismechanism also considerably enhances the photoactivityof the MnO
x
catalyst45.It is also noteworthy that ILs have been used as reac-
tion media for electrosynthesis reactions using CO2 as
a carbon source154,155. However, an important drawbackof using ILs in these applications is their relatively lowmass-transport rates. Miniaturized devices may offer asolution; for example, a gas-diffusion electrode with aprotic-IL membrane156 can be used for CO
2 conversion or
water splitting157. To optimize protic ILs for this purpose(that is, enhancing the proton conductivity), extensivemechanistic studies are needed158.
Fuel cells
Proton-conducting electrolyte materials are much sought
after for proton exchange membrane (PEM) fuel cells.Diaz et al.159 recently provided a useful review of this area.Conventional hydrated-Nafion membranes are limitedby the volatility of the water, which is crucial to their con-ductivity. This could be circumvented in protic-IL-basedmembranes, which would allow access to higher temper-atures. The labile protons typically create high protonconductivity, even in an anhydrous state, which enablestheir function in fuel cells158. It has been suggested thatsome cations, such as the protonated imidazolium cation,may also allow movement of protons via the water-like,Grotthuss conduction mechanism156. Various electrolytemembranes that incorporate ILs are being investigated;
Figure 4 | Reaction pathways for the electrochemical reduction of CO2 at a lead
electrode in acetonitrile. a | Reduction of CO2 in the absence of [C
2mim][NTf
2].
b | Catalytic mechanism based on the involvement of the imidazolium cation.
c | Non-catalytic mechanism based on the production of an imidazolium carboxylate
zwitterion147. Adapted with permission from REF. 147, American Chemical Society.
Desorption
Desorption
Oxalate desorption
N
N
N
N
N
N
N
NO
CO
NN
O ONN
N
N
N
N
CO C
O
O
O
C
O
NN
OO
N
N
O O
OO
a
b
c
Lead electrode2CO
2
+ 2e–
CO2
+ e–
CO2 adsorption
CO2 dimerization to oxalate
2H+
+ e–
H2O
0.5H2
Carboxylate formation
between CO2 and C
2mim
O
C
O O
C
C C
O
OC
O
CO2 coordination
with C2mim
• –
CO2 coordination
with C2mim
• –
• –
• –
CO2
+ e–
• –
CO
REV IEWS
10 | ADVANCE ONLINE PUBLICATION www.nature.com/natrevmats
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 12/16
for example, protic IL–polymer composites that useNafion or alternative polymers as a support can reachpower densities as high as 400 mA cm−2 (REFS 156,160).Efficient application of OIPCs in fuel cells has also beenreported recently 161. Further advances, particularly inimproving performance and reducing costs, are stillrequired to realize commercial devices. Nonetheless,there is a potentially bright future for IL-based materialsin PEM-based fuel cells.
There are several different strategies being pursued toproduce practical biofuel cells based on microbial spe-cies or enzymes as the electrocatalytic species. A par-ticularly interesting example is a microbial biofuel cell
that operates in wastewater to simultaneously generateenergy and treat the wastewater162 (FIG. 6). SupportedIL-based membranes have been explored in this contextas alternatives to Nafion as the separator between thetwo aqueous chambers163.
ILs are also being explored as candidate reactionmedia for enzyme-based biofuel cells owing to theirstrong enzyme-stabilizing effect. For example, Fujitaand co-workers164–168 have explored ‘hydrated’ ILsbased on [Ch][H
2PO
4]–water mixtures as excellent
solvents for proteins. The electron-transfer activity ofcytochrome C dissolved in this medium was maintainedfor at least one year164. This exceptionally long shelf life
Figure 5 | Photo-driven water oxidation in butylammonium protic ILs. a | Schematic of the formation process of
H2O
2. b | Oxidation currents in protic ionic liquid (IL)/water electrolytes. c | Ab initio calculation of the protic IL solvation
environment stabilizing H2O
2 (in this case, ethylammonium cations). d | Photocurrent dependence on potential on
MnO x-coated fluorine-doped tin oxide (FTO) electrodes. Organic electrolyte, 1 M butylammonium nitrate. SCE,
standard calomel electrode; SHE, standard hydrogen electrode. Panel b adapted from REF. 153 with permission of
the Royal Society of Chemistry. Panel d adapted from REF. 45 with permission of the Royal Society of Chemistry.
e–
e–
e–
h+
2H2
4H+
O2+2H+
H2O
2+2H+
2H2O
7
6
5
4
3
2
1
0
0.6 0.7 0.8 0.9 1.0 1.1 1.2
Borate buffer, pH 9
Organic electrolyte, pH 9
Borate buffer/organic
electrolyte, pH 9
Potential vs SCE (V)
N e t p h o t o c u r r e n t ( m A c m – 2 )
FTO glass
Anodea
b
c
C u r r e n t d e n s i t y ( m A c m –
2 )
1.4 120
100
80
60
40
20
0
1.2
1.0
0.8
0.6
0.4
0.2
0
1.2 1.61.00.80.6 1.4Potential vs SHE (V)
1 M butylammonium sulfate
1 M butylammonium
methanesulfate
d
1 M diethylammonium sulfate
1 M butylammonium
ethanesulfate
Cathode
F ar a d ai c effi ci en c y ( % )
REV IEWS
NATURE REVIEWS | MATERIALS ADVANCE ONLINE PUBLICATION | 11
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 13/16
demonstrates the applicability of this IL in enzyme-based biofuel cells, as confirmed recently for the oxida-tion of cellobiose by cellobiose dehydrogenase169. Theeffectiveness of hydrated [Ch][H
2PO
4] in solubilizing
and stabilizing enzymes is thought to result from itsstructural similarity to the surface of cell membranes165;hence, the medium is, to an extent, biomimetic withrespect to certain enzymes. The optimal water contentfor these mixtures has been explored and suggestedto be around seven water molecules per ion-pair forassured biological activity 167.
Future directions and challenges
As the field of energy storage and conversion contin-ues to grow, both in global importance and in tech-nological sophistication, it is apparent that IL-basedsystems can provide a platform for safe, durable andhigh-energy-density materials. In addition, alterna-tive chemical and electrochemical mechanisms thatare often supported by IL systems provide opportu-nities for new directions in these fields. For example,the concentrated-metal-ion/organic-salt systems arean interesting new approach to enhance performance.
Similarly, solvate–IL systems are likely to have an effecton post-Li-ion battery applications.
There is much scope to better understand howstructure and dynamics in IL electrolytes correlate withelectrochemical and transport behaviour. Despite thefact that millions of combinations of ILs are possiblewith the currently available cations and anions, onlya handful have been studied in any great depth; in thefield of energy storage, this focus has been mainly onfluorinated anions owing to their stability. Given thepower of theoretical modelling, ab initio methodsshould provide further insights into the molecular fea-tures that lead to high (electro)chemical stability and
potentially help design new, perhaps non-fluorinatedanions. Although ab initio and DFT techniques havegreatly helped us to understand the origins of the struc-tures of ILs and how they develop into heterogeneity onthe nanometre scale, a detailed approach to predictingtransport properties ab initio remains elusive. This isparticularly important for electroactive ions that areoften present as solutes in the IL; details of their solva-tion, speciation and mobility are invaluable, and com-putational approaches could have an important role inoptimization of their transport properties in particular.This approach will support the power demands of newapplications and large-scale devices, for which theseproperties need to be substantially improved.
The ‘green’ credentials of ILs are widely discussed;however, these claims are often not well substantiated.In the context of energy science and technology, con-
ventional electrolytes or synthetic media are often usedas the sole basis for comparison; in many cases, ILscompare favourably. However, it is also necessary toquantitatively assess toxicity, recyclability and biodeg-radability, for which there is, in most cases, scant infor-mation available. We commend this task to researchers
with the requisite skills to derive such information forthese important materials.
Cost is another issue for most applications of ILs,especially for those that have high electrochemicalstability because of the need for fluorinated anions.Recent work has detailed new IL-based electrolyte sys-tems that avoid fluorinated anions by providing alter-native pathways to SEI formation and that representan important area for future development. The abilityto maintain high performance and thermal stabilityeven in the presence of small amounts of volatile addi-tives provides tremendous scope to tune SEI formationusing these additives, while at the same time improving
Figure 6 | Wastewater-driven microbial fuel cell. a | Fuel cell design162. b | Practical multi-element immersion design16.
PEM, proton exchange membrane. Reproduced with permission from REF. 162, Elsevier.
H+
Microorganisms
Catalyst
e– e–
a b
Anode
PEM
Effluent
Influent
Air
Cathodic chamber Separator Anodic chamber
Organic matter
Oxygen
Cathode: 6O2
+ 24H+ + 24e–
12H2O
Anode: C6H
12O
6
+ 6H2O
6CO2
+ 24H+ + 24e–
Cathode
REV IEWS
12 | ADVANCE ONLINE PUBLICATION www.nature.com/natrevmats
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 14/16
the transport properties. More broadly, there is hugepotential to optimize properties of IL-based mixtures,and we encourage researchers to pursue this researchdirection. A better understanding of the properties ofmixtures of ILs, as well as mixtures with molecular sol-
vents and high concentrations of inorganic salts, willopen up possibilities for further development.
Our vision of this field for the next decade featuresan expanding base of materials that retain the fun-damentally unique suite of properties offered by ILand OIPC salts. These will be increasingly optimizedand tuned for a widening range of applications andpotentially lead to entirely new directions in energygeneration and storage.
1. Smiglak, M. et al. Ionic liquids for energy, materials, and
medicine. Chem. Commun. 50, 9228–9250 (2014).
2. MacFarlane, D. R. et al. Energy applications of ionic
liquids. Energy Environ. Sci. 7, 232–250 (2014).3. Ohno, H. Electrochemical Aspects of Ionic Liquids 2nd
edn (Wiley, 2011).
4. Pringle, J. M., Forsyth, M. & MacFarlane, D. R. in
Electrodeposition from Ionic Liquids (eds Endres, F.,
Abbott, A & MacFarlane, D. R.) 167–211
(Wiley-VCH, 2008).
5. Endres, F., MacFarlane, D. R. & Abbott, A. P.
Electrodepositon from Ionic Liquids 1st edn (2008).
6. Sandoval, A. P., Feliu, J. M., Torresi, R. M. &
Suarez-Herrera, M. F. Electrochemical properties of
poly(3,4-ethylenedioxythiophene) grown on Pt(111)
in imidazolium ionic liquids. RSC Adv. 4,
3383–3391 (2014).
7. Dobbelin, M., Marcilla, R., Pozo-Gonzalo, C. &
Mecerreyes, D. Innovative materials and applications
based on poly(3,4-ethylenedioxythiophene) and ionic
liquids. J. Mater. Chem. 20, 7613–7622 (2010).8. Abdelhamid, M. E., Snook, G. A. & O’Mullane, A. P.
Electropolymerisation of catalytically active PEDOT
from an ionic liquid on a flexible carbon cloth using a
sandwich cell configuration. ChemPlusChem 80,
74–82 (2015).
9. Astratine, L., Magner, E., Cassidy, J. & Betts, A.
Electrodeposition and characterisation of copolymers
based on pyrrole and 3,4-ethylenedioxythiophene in
BMIM BF4 using a microcell configuration.
Electrochim. Acta 115, 440–448 (2014).
10. Wang, Z. P. et al. Poly(thieno[3,4-b]-1,4-oxathiane):
medium effect on electropolymerization and
electrochromic performance. Langmuir 30,
15581–15589 (2014).
11. Kannan, B., Williams, D. E., Laslau, C. & Travas-Sejdic, J. The electrochemical growth of highly
conductive single PEDOT (conducting polymer):BMIPF6
(ionic liquid) nanowires. J. Mater. Chem. 22,
18132–18135 (2012).
12. Carstens, T., Prowald, A., El Abedin, S. Z. & Endres, F.
Electrochemical synthesis of PEDOT and PPP
macroporous films and nanowire architectures from
ionic liquids. J. Solid State Electrochem. 16,
3479–3485 (2012).
13. Lagoutte, S. et al. Poly(3-methylthiophene)/vertically
aligned multi-walled carbon nanotubes:
electrochemical synthesis, characterizations and
electrochemical storage properties in ionic liquids.
Electrochim. Acta 130, 754–765 (2014).
14. Descroix, S., Hallais, G., Lagrost, C. & Pinson, J.
Regular poly( para-phenylene) films bound to gold
surfaces through the electrochemical reduction of
diazonium salts followed by electropolymerization in
an ionic liquid. Electrochim. Acta 106,
172–180 (2013).15. Wallace, G. G., Moulton, S. E., Kapsa, R. M. I. &
Higgins, M. J. Organic Bionics (Wiley-VCH, 2012).
16. Du, Z. J., Luo, X., Weaver, C. L. & Cui, X. T.
Poly(3,4-ethylenedioxythiophene)-ionic liquid coating
improves neural recording and stimulation functionality
of MEAs. J. Mater. Chem. C 3, 6515–6524 (2015).
17. Fellinger, T. P., Thomas, A., Yuan, J. Y. & Antonietti, M.
25th anniversary article: ‘Cooking carbon with salt’:
carbon materials and carbonaceous frameworks from
ionic liquids and poly(ionic liquid)s. Adv. Mater. 25,
5838–5854 (2013).
18. Lee, J. S., Wang, X. Q., Luo, H. M., Baker, G. A. &
Dai, S. Facile ionothermal synthesis of microporous
and mesoporous carbons from task specific ionic
liquids. J. Am. Chem. Soc. 131, 4596–4597 (2009).
19. Zhang, S. G., Dokko, K. & Watanabe, M. Carbon
materialization of ionic liquids: from solvents to
materials. Mater. Horiz. 2, 168–197 (2015).
20. Paraknowitsch, J. P., Zhang, J., Su, D., Thomas, A. &
Antonietti, M. Ionic liquids as precursors for nitrogen-
doped graphitic carbon. Adv. Mater. 22, 87–92 (2010).
21. Fulvio, P. F.et al. A new family of fluidic precursors for
the self-templated synthesis of hierarchical nanoporous
carbons. Chem. Commun. 49, 7289–7291 (2013).
22. Fellinger, T. P., Hasche, F., Strasser, P. & Antonietti, M.
Mesoporous nitrogen-doped carbon for the
electrocatalytic synthesis of hydrogen peroxide. J. Am.
Chem. Soc. 134, 4072–4075 (2012).
23. Fechler, N., Fellinger, T. P. & Antonietti, M. ‘Salt
templating’: a simple and sustainable pathway toward
highly porous functional carbons from ionic liquids.
Adv. Mater.25, 75–79 (2013).
24. Zhang, S., Miran, M. S., Ikoma, A., Dokko, K. &
Watanabe, M. Protic ionic liquids and salts as versatile
carbon precursors. J. Am. Chem. Soc. 136,
1690–1693 (2014).
25. Zhang, S., Dokko, K. & Watanabe, M. Direct synthesis
of nitrogen-doped carbon materials from protic ionic
liquids and protic salts: structural and physicochemical
correlations between precursor and carbon. Chem.
Mater. 26, 2915–2926 (2014).
26. Zhang, S. G., Tsuzuki, S., Ueno, K., Dokko, K. &
Watanabe, M. Upper limit of nitrogen content in
carbon materials. Angew. Chem. Int. Ed. Engl. 54,
1302–1306 (2015).
27. Yang, W., Fellinger, T. P. & Antonietti, M. Efficient
metal-free oxygen reduction in alkaline medium on
high-surface-area mesoporous nitrogen-doped
carbons made from ionic liquids and nucleobases.
J. Am. Chem. Soc. 133, 206–209 (2011).
28. Elumeeva, K., Fechler, N., Fellinger, T. P. &
Antonietti, M. Metal-free ionic liquid-derived
electrocatalyst for high-performance oxygen reduction
in acidic and alkaline electrolytes. Mater. Horiz.1,588–594 (2014).
29. Gong, K. P., Du, F., Xia, Z. H., Durstock, M. &
Dai, L. M. Nitrogen-doped carbon nanotube arrays
with high electrocatalytic activity for oxygen reduction.
Science 323, 760–764 (2009).
30. Cooper, E. R. et al. Ionic liquids and eutectic mixtures
as solvent and template in synthesis of zeolite
analogues. Nature 430, 1012–1016 (2004).
31. Barpanda, P., Djellab, K., Recham, N., Armand, M. &
Tarascon, J. M. Direct and modified ionothermal
synthesis of LiMnPO4 with tunable morphology for
rechargeable Li-ion batteries. J. Mater. Chem. 21,
10143–10152 (2011).
32. Duan, X., Ma, J., Lian, J. & Zheng, W. The art of using
ionic liquids in the synthesis of inorganic nanomaterials.
CrystEngComm 16, 2550–2559 (2014).33. Eshetu, G. G., Armand, M., Scrosati, B. & Passerini, S.
Energy storage materials synthesized from ionic liquids.
Angew. Chem. Int. Ed. Engl. 53, 13342–13359 (2014).
34. Liu, P. I. et al. Microwave-assisted ionothermalsynthesis of nanostructured anatase titanium dioxide/
activated carbon composite as electrode material for
capacitive deionization. Electrochim. Acta 96,
173–179 (2013).
35. Teng, F. et al. Synergism of ionic liquid and surfactant
molecules in the growth of LiFePO4 nanorods and the
electrochemical performances. J. Power Sources 202,
384–388 (2012).
36. Xiao, Z. H., Cui, Q. Q., Li, X. L., Wang, H. L. & Zhou, Q.
Ionothermal synthesis for Mg-doped LiMn1.5
Ni0.5
O4
spinel with structural stability and high-rate
performance. Ionics 21, 1261–1267 (2015).
37. Duan, X. C. et al. Ionic liquid-modulated preparation of
hexagonal tungsten trioxide mesocrystals for lithium-
ion batteries. Nanoscale 7, 2230–2234 (2015).
38. Li, C. L., Yin, C. L., Mu, X. K. & Maier, J. Top-down
synthesis of open framework fluoride for lithium and
sodium batteries. Chem. Mater. 25, 962–969 (2013).
39. Jana, M. K., Rajendra, H. B., Bhattacharyya, A. J. &
Biswas, K. Green ionothermal synthesis of hierarchical
nanostructures of SnS2 and their Li-ion storage
properties. CrystEngComm 16, 3994–4000 (2014).40. Mali, S. S., Betty, C. A., Bhosale, P. N., Patil, P. S. &
Hong, C. K. From nanocorals to nanorods to
nanoflowers nanoarchitecture for efficient dye-
sensitized solar cells at relatively low film thickness: all
hydrothermal process. Sci. Rep. 4, 5451 (2014).
41. Chatel, G. & MacFarlane, D. R. Ionic liquids and
ultrasound in combination: synergies and challenges.
Chem. Soc. Rev. 43, 8132–8149 (2014).
42. Choi, B. G. et al. Enhanced pseudocapacitance of ionic
liquid/cobalt hydroxide nanohybrids. ACS Nano 7,
2453–2460 (2013).
43. Lahiri, A., Olschewski, M., Carstens, T., Abedin, S. Z. &
Endres, F. Electrodeposition of crystalline gallium-
doped germanium and Si x Ge
1− x from an ionic liquid at
room temperature. ChemElectroChem 2,
571–577 (2015).
44. Izgorodin, A., Izgorodina, E. & MacFarlane, D. R. Low
overpotential water oxidation to hydrogen peroxide on
a MnO x catalyst. Energy Environ. Sci. 5,
9496–9501 (2012).
45. Zhou, F. et al. Enhanced photo-electrochemical water
oxidation on MnO x in buffered organic/inorganic
electrolytes. J. Mater. Chem. A 3,
16642–16652 (2015).46. Asnavandi, M., Suryanto, B. H. R. & Zhao, C. Controlled
electrodeposition of nanostructured Pd thin films from
protic ionic liquids for electrocatalytic oxygen reduction
reactions.RSC Adv. 5, 74017–74023 (2015).
47. Shrestha, S. & Biddinger, E. J. Palladium
electrodeposition in 1-butyl-1-methylpyrrolidinium
dicyanamide ionic liquid. Electrochim. Acta 174,
254–263 (2015).48. Murugesan, S. et al. Room temperature
electrodeposition of molybdenum sulfide for catalytic
and photoluminescence applications. ACS Nano 7,
8199–8205 (2013).
49. Serrà, A., Gómez, E. & Vallés, E. Novel
electrodeposition media to synthesize CoNi-Pt Core@
Shell stable mesoporous nanorods with very high
active surface for methanol electro-oxidation.
Electrochim. Acta 174, 630–639 (2015).
50. Kalhoff, J., Eshetu, G. G., Bresser, D. & Passerini, S.
Safer electrolytes for lithium-ion batteries: state of the
art and perspectives. ChemSusChem 8,
2154–2175 (2015).
51. Ponrouch, A. et al. Towards high energy density
sodium ion batteries through electrolyte optimization.
Energy Environ. Sci. 6, 2361–2369 (2013).52. Scheers, J., Fantini, S. & Johansson, P. A review of
electrolytes for lithium–sulphur batteries. J. Power
Sources 255, 204–218 (2014).
53. Rosenman, A. et al. Review on Li–sulfur batterysystems: an integral perspective. Adv. Energy Mater. 5,
1500212 (2015).
54. Bruce, P. G., Freunberger, S. A., Hardwick, L. J. &
Tarascon, J. M. Li–O2 and Li–S batteries with high
energy storage. Nat. Mater. 11, 19–29 (2012).
55. Shao, Y. Y. et al. Making Li–air batteries rechargeable:
material challenges. Adv. Funct. Mater. 23,
987–1004 (2013).
56. Kar, M., Simons, T. J., Forsyth, M. & MacFarlane, D. R.
Ionic liquid electrolytes as a platform for rechargeable
metal–air batteries: a perspective. Phys. Chem. Chem.
Phys. 16, 18658–18674 (2014).
57. Elia, G. A. et al. An advanced lithium–air battery
exploiting an ionic liquid-based electrolyte. Nano Lett.14, 6572–6577 (2014).
58. Wu, F.et al. Ionic liquid electrolytes with protective
lithium difluoro(oxalate)borate for high voltage lithium-
ion batteries. Nano Energy 13, 546–553 (2015).
REV IEWS
NATURE REVIEWS | MATERIALS ADVANCE ONLINE PUBLICATION | 13
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 15/16
59. Wongittharom, N. et al. Ionic liquid electrolytes for
high-voltage rechargeable Li/LiNi0.5
Mn1.5
O4 cells.
J. Mater. Chem. A2, 3613–3620 (2014).
60. Di Lecce, D., Brutti, S., Panero, S. & Hassoun, J. A new
Sn-C/LiFe0.1
Co0.9
PO4 full lithium-ion cell with ionic liquid-
based electrolyte. Mater. Lett. 139, 329–332 (2015).
61. Girard, G. M. A. et al. Electrochemical and
physicochemical properties of small phosphonium cation
ionic liquid electrolytes with high lithium salt content.
Phys. Chem. Chem. Phys. 17, 8706–8713 (2015).
62. Tsunashima, K., Sakai, Y. & Matsumiya, M. Physical
and electrochemical properties of phosphonium ionicliquids derived from trimethylphosphine. Electrochem.
Commun. 39, 30–33 (2014).
63. Scarbath-Evers, L. K., Hunt, P. A., Kirchner, B.,
MacFarlane, D. R. & Zahn, S. Molecular features
contributing to the lower viscosity of phosphonium
ionic liquids compared to their ammonium analogues.
Phys. Chem. Chem. Phys.17, 20205–20216 (2015).
64. Yoon, H. et al. Lithium electrochemistry and cycling
behaviour of ionic liquids using cyano based anions.
Energy Environ. Sci. 6, 979–986 (2013).
65. Singh, R. P., Martin, J. L. & Poshusta, J. C. Synthesis of
bis(fluorosulfonyl)imide. US Patent 8377406 (2013).
66. Lahiri, A., Schubert, T. J. S., Iliev, B. & Endres, F. LiTFSI
in 1-butyl-1-methylpyrrolidinium bis(fluorosulfonyl)
amide: a possible electrolyte for ionic liquid based
lithium ion batteries. Phys. Chem. Chem. Phys. 17,
11161–11164 (2015).
67. Matsui, Y.et al. Charge–discharge characteristics of a
LiNi1/3
Mn1/3
Co1/3
O2 cathode in FSI-based ionic liquids.
Electrochemistry 80, 808–811 (2012).
68. Yoon, H., Howlett, P. C., Best, A. S., Forsyth, M. &
MacFarlane, D. R. Fast charge/discharge of Li metal
batteries using an ionic liquid electrolyte.
J. Electrochem. Soc. 160, A1629–A1637 (2013).
69. Yoon, H., Best, A. S., Forsyth, M., MacFarlane, D. R. &
Howlett, P. C. Physical properties of high Li-ion content
N -propyl-N -methylpyrrolidinium bis(fluorosulfonyl)
imide based ionic liquid electrolytes. Phys. Chem.
Chem. Phys. 17, 4656–4663 (2015).
70. Grande, L., Paillard, E., Kim, G. T., Monaco, S. &
Passerini, S. Ionic liquid electrolytes for Li–air
batteries: lithium metal cycling. Int. J. Mol. Sci. 15,
8122–8137 (2014).
71. Jang, I.-C., Ida, S. & Ishihara, T. Lithium depletion and
the rechargeability of Li–O2 batteries in ether and
carbonate electrolytes. ChemElectroChem 2,
1380–1384 (2015).
72. Piper, D. M. et al. Stable silicon–ionic liquid interface
for next-generation lithium-ion batteries. Nat.
Commun. 6, 6230 (2015).
73. Barghamadi, M. et al. Lithium–sulfur batteries — thesolution is in the electrolyte, but is the electrolyte a
solution? Energy Environ. Sci. 7, 3902–3920 (2014).
74. Zhang, S., Ueno, K., Dokko, K. & Watanabe, M. Recent
advances in electrolytes for lithium–sulfur batteries.
Adv. Energy Mater. 5, 1500117 (2015).
75. Park, J.-W., Ueno, K., Tachikawa, N., Dokko, K. &
Watanabe, M. Ionic liquid electrolytes for lithium–sulfur
batteries. J. Phys. Chem. C 117, 20531–20541 (2013).
76. Xiong, S. Z., Xie, K., Blomberg, E., Jacobsson, P. &
Matic, A. Analysis of the solid electrolyte interphase
formed with an ionic liquid electrolyte for lithium–sulfur
batteries. J. Power Sources 252, 150–155 (2014).
77. Ueno, K. et al. Glyme–lithium salt equimolar molten
mixtures: concentrated solutions or solvate ionic
liquids? J. Phys. Chem. B 116, 11323–11331 (2012).
78. Li, F. J., Zhang, T., Yamada, Y., Yamada, A. & Zhou, H. S.
Enhanced cycling performance of Li–O2 batteries by the
optimized electrolyte concentration of LiTFSA in
Glymes. Adv. Energy Mater. 3, 532–538 (2013).
79. Suo, L. M., Hu, Y. S., Li, H., Armand, M. & Chen, L. Q. A new class of solvent-in-salt electrolyte for high-
energy rechargeable metallic lithium batteries. Nat.
Commun. 4, 1481 (2013).
80. Qian, J. F.et al. High rate and stable cycling of lithium
metal anode. Nat. Commun. 6, 6362 (2015).
81. Lu, Y. Y., Korf, K., Kambe, Y., Tu, Z. Y. & Archer, L. A.
Ionic-liquid–nanoparticle hybrid electrolytes:
applications in lithium metal batteries. Angew. Chem.
Int. Ed. Engl. 53, 488–492 (2014).
82. Guyomard-Lack, A. et al. Hybrid silica–polymer
ionogel solid electrolyte with tunable properties. Adv.
Energy Mater. 4, 1301570 (2014).
83. Jin, L. et al. An organic ionic plastic crystal electrolyte
for rate capability and stability of ambient
temperature lithium batteries. Energy Environ. Sci. 7,
3352–3361 (2014).
84. Howlett, P. C. et al. Thin and flexible solid-state
organic ionic plastic crystal-polymer nanofibre
composite electrolytes for device applications. Phys.
Chem. Chem. Phys. 15, 13784–13789 (2013).85. Iranipour, N. et al. Ionic transport through a
composite structure of N -ethyl-N -methylpyrrolidinium
tetrafluoroborate organic ionic plastic crystals
reinforced with polymer nanofibres. J. Mater. Chem. A3, 6038–6052 (2015).
86. Goodenough, J. B. Evolution of strategies for modern
rechargeable batteries. Acc. Chem. Res. 46,
1053–1061 (2013).
87. Slater, M. D., Kim, D., Lee, E. & Johnson, C. S. Sodium-
ion batteries. Adv. Funct. Mater. 23, 947–958 (2013).88. Fukunaga, A. et al. Intermediate-temperature ionic liquid
NaFSA-KFSA and its application to sodium secondary
batteries. J. Power Sources 209, 52–56 (2012).
89. Mohd, N. S. A., Gunzelmann, D., Sun, J.,
MacFarlane, D. R. & Forsyth, M. Ion conduction and
phase morphology in sulfonate copolymer ionomers
based on ionic liquid-sodium cation mixtures.
J. Mater. Chem. A 2, 365–374 (2014).
90. Noor, S. A. M., Yoon, H., Forsyth, M. &
MacFarlane, D. R. Gelled ionic liquid sodium ion
conductors for sodium batteries. Electrochim. Acta 169, 376–381 (2015).
91. Yoon, H. et al. Physicochemical properties of N -propyl-
N -methylpyrrolidinium bis(fluorosulfonyl)imide for
sodium metal battery applications. Phys. Chem. Chem.
Phys. 16, 12350–12355 (2014).
92. Chagas, L. G., Buchholz, D., Wu, L. M., Vortmann, B. &
Passerini, S. Unexpected performance of layered
sodium-ion cathode material in ionic liquid-based
electrolyte. J. Power Sources 247, 377–383 (2014).
93. Ding, C. et al. Na[FSA]-[C3C
1pyrr][FSA] ionic liquids as
electrolytes for sodium secondary batteries: Effects of
Na ion concentration and operation temperature.
J. Power Sources 269, 124–128 (2014).
94. Wang, C.-H. et al. Rechargeable Na/Na0.44
MnO2 cells
with ionic liquid electrolytes containing various sodium
solutes. J. Power Sources 274, 1016–1023 (2015).
95. Wongittharom, N., Wang, C. H., Wang, Y. C.,
Yang, C. H. & Chang, J. K. Ionic liquid electrolytes with
various sodium solutes for rechargeable Na/NaFePO4
batteries operated at elevated temperatures. ACS
Appl. Mater. Interfaces 6, 17564–17570 (2014).
96. Monti, D., Jonsson, E., Palacin, M. R. & Johansson, P.
Ionic liquid based electrolytes for sodium-ion
batteries: Na+ solvation and ionic conductivity.
J. Power Sources 245, 630–636 (2014).
97. Chen, F. F., Pringle, J. M. & Forsyth, M. Insights into the
transport of alkali metal ions doped into a plastic crystal
electrolyte. Chem. Mater. 27, 2666–2672 (2015).
98. Poetz, S. et al. Evaluation of decomposition products
of EMImCl·1.5AlCl3 during aluminiumelectrodeposition with different analytical methods.
RSC Adv. 4, 6685–6690 (2014).
99. Wilkes, J. S., Levisky, J. A., Wilson, R. A. &
Hussey, C. L. Dialkylimidazolium chloroaluminate
melts: a new class of room-temperature ionic liquids
for electrochemistry, spectroscopy, and synthesis.
Inorg. Chem. 21, 1263–1264 (1982).
100. Lin, M. C. et al. An ultrafast rechargeable aluminium-
ion battery. Nature 520, 325–328 (2015).
101. Fang, Y. et al. An AlCl3 based ionic liquid with a neutral
substituted pyridine ligand for electrochemical
deposition of aluminum. Electrochim. Acta 160,
82–88 (2015).
102. Kakibe, T., Hishii, J. Y., Yoshimoto, N., Egashira, M. &
Morita, M. Binary ionic liquid electrolytes containing
organo-magnesium complex for rechargeable
magnesium batteries. J. Power Sources 203,
195–200 (2012).103. Khoo, T. et al. Discharge behaviour and interfacial
properties of a magnesium battery incorporatingtrihexyl(tetradecyl)phosphonium based ionic liquid
electrolytes. Electrochim. Acta 87, 701–708 (2013).
104. Mohtadi, R., Matsui, M., Arthur, T. S. & Hwang, S. J.
Magnesium borohydride: from hydrogen storage to
magnesium battery. Angew. Chem. Int. Ed. Engl. 51,
9780–9783 (2012).
105. Shao, Y. et al. Coordination chemistry in magnesium
battery electrolytes: how ligands affect their
performance. Sci. Rep. 3, 3130 (2013).
106. Kar, M. et al. Stable zinc cycling in novel alkoxy-
ammonium based ionic liquid electrolytes. Electrochim.
Acta 188, 461–471 (2016).
107. Forsyth, M., Howlett, P. C., Tan, S. K., MacFarlane, D. R.
& Birbilis, N. An ionic liquid surface treatment for
corrosion protection of magnesium alloy AZ31.
Electrochem. Solid State Lett. 9, B52–B55 (2006).
108. Simons, T. J., Torriero, A. A. J., Howlett, P. C.,
MacFarlane, D. R. & Forsyth, M. High current density,
efficient cycling of Zn2+ in 1-ethyl-3-methylimidazolium
dicyanamide ionic liquid: the effect of Zn2+ salt and
water concentration. Electrochem. Commun. 18,
119–122 (2012).
109. Simons, T. J., Pearson, A. K., Pas, S. J. &
MacFarlane, D. R. The electrochemical cycling and
electrodeposition of lead from
1-ethyl-3-methylimidazolium
bis(trifluoromethanesulfonyl)imide ionic liquid.
Electrochim. Acta 174, 712–720 (2015).
110. Simons, T. J., MacFarlane, D. R., Forsyth, M. &
Howlett, P. C. Zn electrochemistry in 1-ethyl-3-methylimidazolium and
N -butyl-N -methylpyrrolidinium dicyanamides:
promising new rechargeable Zn battery electrolytes.
ChemElectroChem 1, 1688–1697 (2014).111. Kar, M., Winther-Jensen, B., Forsyth, M. &
MacFarlane, D. R. Chelating ionic liquids for reversible
zinc electrochemistry. Phys. Chem. Chem. Phys. 15,
7191–7197 (2013).
112. Kar, M., Winther-Jensen, B., Forsyth, M. &
MacFarlane, D. R. Exploring zinc coordination in novel
zinc battery electrolytes. Phys. Chem. Chem. Phys. 16,
10816–10822 (2014).
113. Friesen, C. A., Wolfe, D. & Johnson, P. B. Metal–air cell
with ion exchange material. World Patent
WO2012174558A1 (2012).
114. Friesen, C. A. & Hayes, J. Electrochemical cell, and
particularly a cell with electrodeposited fuel.
US Patent 8546028 (2013).
115. Mathew, S. et al. Dye-sensitized solar cells with 13%
efficiency achieved through the molecular engineering of
porphyrin sensitizers. Nat. Chem. 6, 242–247 (2014).116. Bai, Y., Zhang, J., Wang, Y., Zhang, M. & Wang, P.
Lithium-modulated conduction band edge shifts and
charge-transfer dynamics in dye-sensitized solar cells
based on a dicyanamide ionic liquid. Langmuir 27,
4749–4755 (2011).
117. Lau, G. P. S., Tsao, H. N., Zakeeruddin, S. M.,
Grätzel, M. & Dyson, P. J. Highly stable dye-sensitized
solar cells based on novel 1,2,3-triazolium ionic
liquids. ACS Appl. Mater. Interfaces 6,
13571–13577 (2014).
118. Armel, V.et al. Ionic liquid electrolyte porphyrin dye
sensitised solar cells. Chem. Commun. 46, 3146–3148
(2010).
119. Yella, A. et al. Porphyrin-sensitized solar cells with
cobalt (II/III)-based redox electrolyte exceed 12
percent efficiency. Science 334, 629–634 (2011).
120. Xu, D., Zhang, H., Chen, X. & Yan, F. Imidazolium
functionalized cobalt tris(bipyridyl) complex redox
shuttles for high efficiency ionic liquid electrolyte dye-
sensitized solar cells. J. Mater. Chem. A 1, 11933–11941 (2013).
121. Chu, T.-C. et al. Ionic liquid with a dual-redox couple
for efficient dye-sensitized solar cells. ChemSusChem
7, 146–153 (2014).122. Zhao, J. et al. Solvent-free ionic liquid/poly(ionic liquid)
electrolytes for quasi-solid-state dye-sensitized solar
cells. J. Mater. Chem. 21, 7326–7330 (2011).
123. Zhang, Y. et al. Performance enhancement for quasi-
solid-state dye-sensitized solar cells by using acid-
oxidized carbon nanotube-based gel electrolytes.
Electrochim. Acta 61, 185–190 (2012).124. Lu, S. et al. Water-resistant, solid-state, dye-sensitized
solar cells based on hydrophobic organic ionic plastic
crystal electrolytes. Adv. Mater. 26, 1266–1271 (2014).
125. Armel, V., Forsyth, M., MacFarlane, D. R. &
Pringle, J. M. Organic ionic plastic crystal electrolytes;
a new class of electrolyte for high efficiency solid state
dye-sensitized solar cells. Energy Environ. Sci. 4,
2234–2239 (2011).
126. Pringle, J. M. Recent progress in the development anduse of organic ionic plastic crystal electrolytes. Phys.
Chem. Chem. Phys. 15, 1339–1351 (2013).
127. Abraham, T. J., MacFarlane, D. R. & Pringle, J. M.
High Seebeck coefficient redox ionic liquid electrolytes
for thermal energy harvesting. Energy Environ. Sci. 6,
2639–2645 (2013).
128. Jiao, N., Abraham, T. J., MacFarlane, D. R. &
Pringle, J. M. Ionic liquid electrolytes for thermal energy
harvesting using a cobalt redox couple. J. Electrochem.
Soc. 161, D3061–D3065 (2014).
129. Abraham, T. J., MacFarlane, D. R. & Pringle, J. M.
Seebeck coefficients in ionic liquids–prospects for
thermo-electrochemical cells. Chem. Commun. 47,
6260–6262 (2011).
130. Koerver, R., MacFarlane, D. R. & Pringle, J. M.
Evaluation of electrochemical methods for
determination of the Seebeck coefficient of redox
electrolytes. Electrochim. Acta 184, 186–192 (2015).
REV IEWS
14 | ADVANCE ONLINE PUBLICATION www.nature.com/natrevmats
© 2016 Macmillan Publishers Limited. All rights reserved
7/24/2019 Ionic Liquids and Their Solid-state Analogues as Materials for Energy Generation and Storage
http://slidepdf.com/reader/full/ionic-liquids-and-their-solid-state-analogues-as-materials-for-energy-generation 16/16
131. Abraham, T. J., Tachikawa, N., MacFarlane, D. R. &
Pringle, J. M. Investigation of the kinetic and mass
transport limitations in thermoelectrochemical cells
with different electrode materials. Phys. Chem. Chem.
Phys. 16, 2527–2532 (2014).
132. Lazar, M. A., Al-Masri, D., MacFarlane, D. R. &
Pringle, J. M. Enhanced thermal energy harvesting
performance of a cobalt redox couple in ionic liquid–
solvent mixtures. Phys. Chem. Chem. Phys. http://dx.
doi.org/10.1039/C5CP04305K (2015).
133. Arbizzani, C. et al. Safe, high-energy supercapacitors
based on solvent-free ionic liquid electrolytes. J. PowerSources 185, 1575–1579 (2008).
134. Béguin, F., Presser, V., Balducci, A. & Frackowiak, E.
Carbons and electrolytes for advanced supercapacitors.
Adv. Mater. 26, 2219–2251 (2014).135. Brandt, A. & Balducci, A. Theoretical and practical
energy limitations of organic and ionic liquid-based
electrolytes for high voltage electrochemical double
layer capacitors. J. Power Sources 250, 343–351
(2014).
136. Ruch, P. W., Cericola, D., Foelske, A., Kötz, R. &
Wokaun, A. A comparison of the aging of
electrochemical double layer capacitors with
acetonitrile and propylene carbonate-based
electrolytes at elevated voltages. Electrochim. Acta
55, 2352–2357 (2010).
137. Uesugi, E., Goto, H., Eguchi, R., Fujiwara, A. &
Kubozono, Y. Electric double-layer capacitance between
an ionic liquid and few-layer graphene. Sci. Rep. 3,
1595 (2013).
138. Yang, X., Cheng, C., Wang, Y., Qiu, L. & Li, D. Liquid-
mediated dense integration of graphene materials for
compact capacitive energy storage.Science 341,
534–537 (2013).
139. Coadou, E. et al. Comparative study on performances
of trimethyl-sulfonium and trimethyl-ammonium
based ionic liquids in molecular solvents as electrolyte
for electrochemical double layer capacitors. J. Phys.
Chem. C 117, 10315–10325 (2013).140. Pohlmann, S. et al. Azepanium-based ionic liquids as
green electrolytes for high voltage supercapacitors.
J. Power Sources 273, 931–936 (2015).
141. Pohlmann, S. & Balducci, A. A new conducting salt for
high voltage propylene carbonate-based
electrochemical double layer capacitors. Electrochim.
Acta110, 221–227 (2013).
142. Wolff, C., Jeong, S., Paillard, E., Balducci, A. &
Passerini, S. High power, solvent-free electrochemical
double layer capacitors based on pyrrolidinium
dicyanamide ionic liquids. J. Power Sources293,
65–70 (2015).
143. Faunce, T. et al. Artificial photosynthesis as a frontiertechnology for energy sustainability. Energy Environ.
Sci. 6, 1074–1076 (2013).
144. Faunce, T. A. et al. Energy and environment policy case
for a global project on artificial photosynthesis. Energy
Environ. Sci. 6, 695–698 (2013).
145. Cokoja, M., Bruckmeier, C., Rieger, B.,
Herrmann, W. A. & Kuhn, F. E. Transformation of
carbon dioxide with homogeneous transition-metal
catalysts: a molecular solution to a global challenge?
Angew. Chem. Int. Ed. Engl. 50, 8510–8537 (2011).
146. Ramdin, M., de Loos, T. W. & Vlugt, T. J. H. State-of-the-
art of CO2 capture with ionic liquids. Ind. Eng. Chem.
Res. 51, 8149–8177 (2012).
147. Sun, L., Ramesha, G. K., Kamat, P. V. & Brennecke, J. F.
Switching the reaction course of electrochemical CO2
reduction with ionic liquids. Langmuir 30,
6302–6308 (2014).148. Rosen, B. A. et al. Ionic liquid-mediated selective
conversion of CO2 to CO at low overpotentials. Science
334, 643–644 (2011).
149. Rosen, B. A. et al. In situ spectroscopic examination
of a low overpotential pathway for carbon dioxide
conversion to carbon monoxide. J. Phys. Chem. C
116, 15307–15312 (2012).
150. Watkins, J. D. & Bocarsly, A. B. Direct reduction of
carbon dioxide to formate in high-gas-capacity ionic
liquids at post-transition-metal electrodes.
ChemSusChem 7, 284–290 (2014).
151. Cheek, G. T., Roeper, D. F., Pearson, W. &
O’Grady, W. E. Electrochemical studies of imidazolium
carboxylate adducts in a room-temperature ionic liquid.
ECS Trans. 64, 161–169 (2014).
152. Bernardini, G., Wedd, A. G., Zhao, C. & Bond, A. M.
Electrochemical probing of the photoreduction of
molybdenum and tungsten Dawson-type
polyoxometalates in molecular and ionic liquid media
using water as an electron donor. Dalton Trans. 41,
9944–9954 (2012).153. McDonnell-Worth, C. & MacFarlane, D. R. Ion effects in
water oxidation to hydrogen peroxide. RSC Adv. 4,
30551–30557 (2014).
154. Zhao, S.-F., Horne, M., Bond, A. M. & Zhang, J.
Electrocarboxylation of acetophenone in ionic liquids:
the influence of proton availability on product
distribution. Green Chem. 16, 2242–2251 (2014).155. Zhang, S. et al. Ionic liquid-based green processes for
energy production. Chem. Soc. Rev. 43, 7838–7869
(2014).
156. Yasuda, T. & Watanabe, M. Protic ionic liquids: fuel cell
applications. MRS Bull. 38, 560–566 (2013).
157. Shironita, S., Karasuda, K., Sato, M. & Umeda, M.
Feasibility investigation of methanol generation by
CO2 reduction using Pt/C-based membrane electrode
assembly for a reversible fuel cell. J. Power Sources
228, 68–74 (2013).
158. Miran, M. S., Yasuda, T., Susan, M. A. B. H., Dokko, K.
& Watanabe, M. Binary protic ionic liquid mixtures as a
proton conductor: high fuel cell reaction activity and facile proton transport. J. Phys. Chem. C 118,
27631–27639 (2014).
159. Díaz, M., Ortiz, A. & Ortiz, I. Progress in the use of
ionic liquids as electrolyte membranes in fuel cells.
J. Membrane Sci. 469, 379–396 (2014).
160. Ye, Y.-S., Rick, J. & Hwang, B.-J. Ionic liquid polymer
electrolytes. J. Mater. Chem. A 1,
2719–2743 (2013).
161. Luo, J. et al. 1,2,4-Triazolium perfluorobutanesulfonate
as an archetypal pure protic organic ionic plastic crystal
electrolyte for all-solid-state fuel cells. Energy Environ.
Sci. 8, 1276–1291 (2015).
162. Hernández-Fernández, F. J. et al. Recent progress and
perspectives in microbial fuel cells for bioenergy
generation and wastewater treatment. Fuel Process.
Technol. 138, 284–297 (2015).
163. Hernández-Fernández, F. J. et al. New application ofsupported ionic liquids membranes as proton exchange
membranes in microbial fuel cell for waste water
treatment. Chem. Eng. J. 279, 115–119 (2015).
164. Fujita, K. et al. Solubility and stability of cytochrome c
in hydrated ionic liquids: effect of oxo acid residues
and kosmotropicity. Biomacromolecules 8,
2080–2086 (2007).
165. Fujita, K., Nikawa, Y. & Ohno, H. Cold crystallisation
behaviour of water molecules in ionic liquids as a
screening method to evaluate biocompatibility of the
hydrated ionic liquids. Chem. Commun. 49,
3257–3259 (2013).
166. Fujita, K., Murata, K., Masuda, M., Nakamura, N. &
Ohno, H. Ionic liquids designed for advanced
applications in bioelectrochemistry. RSC Adv. 2,
4018–4030 (2012).
167. Ohno, H., Fujita, K. & Kohno, Y. Is seven the
minimum number of water molecules per ion pair for
assured biological activity in ionic liquid–water
mixtures? Phys. Chem. Chem. Phys. 17,
14454–14460 (2015).168. Tamura, K., Nakamura, N. & Ohno, H. Cytochrome c
dissolved in 1-allyl-3-methylimidazolium chloride type
ionic liquid undergoes a quasi-reversible redox
reaction up to 140 °C. Biotechnol. Bioeng. 109,
729–735 (2012).
169. Fujita, K., Nakamura, N., Igarashi, K., Samejima, M.
& Ohno, H. Biocatalytic oxidation of cellobiose in an
hydrated ionic liquid. Green Chem. 11, 351–354
(2009).
AcknowledgementsD.R.M. and M.F. thank the Australian Research Council for
support from the Australian Laureate Fellowship programme
and J.M.P. and P.C.H. for support from the Discovery Projects
program and the Australian Centre for Electromaterials
Science. This work was supported in part by the National
Natural of Science Foundation of China (Grant Nos
21371101, 21421001), 111 Project (B12015) and MOE
Innovation Team (IRT 13022) of China. H.O. acknowledges
the financial support of the Grant-in-Aid for ScientificResearch from the Japan Society for the Promotion of Science
(KAKENHI, No. 26248049).
Competing interests statementThe authors declare no competing interests.
REV IEWS