EXPERIENCE WITH

NSL CHEMICALS

INTRODUCTION

1

FOUNDED IN

PRODUCTS

Calcium Hydroxide

Steel Slag

Monolithic Refractories materials

PRODUCTION

PROCESS CaO

SUPPLY/FEED STORAGE HYDRATOR

BALL MILL

Finer Products

LIME STORAGE

AIR SEPARATOR

AIR SEPARATOR

Coarser Products

PRODUCTION

PROCESS Limestone to quicklime: -Calcium carbonate ---heat---> calcium oxide (QUICKLIME) + carbon dioxide -Chemical formula: CaCO3 ---heat---> CaO + CO2

Quicklime to slaked lime: -Calcium oxide (QUICKLIME) + water ---> calcium hydroxide (SLAKED LIME) -Chemical formula: CaO + H20 ---> Ca(OH)2

PRODUCTION

PROCESS

CaC2(s) + 2 H2O(l

Calcium Carbide reacts with water to form acetylene gas and Calcium hydroxide (slurry).

C2H2(g) + Ca(OH)2(s)

GREEN CAUSE

EXPERIENCE

1 attachment

TESTING

LAB

SIEVING

DRY

SIGNIFICANCE

-Customer Requirement

-Coarser particles will choke pipelines

PROCEDURE

- Weigh out 5g of sample

- Weigh the residue left on the mesh

after 10 mins of vacumn

- Calculate the percentage passing

EQUIPMENT

OPERATION

PROJECT

3

SAMPLE

COLLECTION

UNCONFINED PRESSURE TEST

SIEVING WET

SIGNIFICANCE

-Determine the amount of material finer than a given sieve size

-Used on adhesive/sticky soils

PROCEDURES

-Wet Sample Weighed Out -Placed on Sieve and washed down -Care taken to ensure accurate results

ANALYSIS

DATA

Marine Clay Moisture analysis Sample 1 (g) Sample 2 (g)

Initial Weight (sample only)

Weight of Container

Sample weight + container

Sample weight + container (after 2 hrs in oven)

Sample weight + container (30 mins extra heating)

Sample weight + container (30 mins extra heating)

Sample weight + container (30 mins extra heating)

Constant weight achieved at 3hrs 30 mins in the oven

Using given Moisture Formula Sample 1 Sample 2

Water mass Content of sample/ dry weight 55.88% 58.88%

MOISTURE ANALYSIS

Contributions

4

MANPOWER ADDITIONAL

LOGISTICS

SOLUTIONS

SAFETY

SOLUTIONS

TEAMWORK

RECODING DATA

EFFICIENT

DATA SAMPLE

1. GENERAL INFORMATION Tested by: Date Tested: Lab partners/organisation: Client: Project:

Boring no: Recovery Depth:

Recovery Date: Recovery Method:

Soil Description:

2. Test Details Scale type/serial no./precision:

Oven Temperature: Duration of oven drying:

Concentration of sodium hexametaphosphate solution: Duration of soaking period: Notes,observations, and deviations from ASTM D1140 test standard:

3. Measurements and Calculations: Net dry mass of soil before sieving (B): Net dry mass of soil retained by #200 sieve (C ): Percent fines (A):

BENEFITS

5

RESPONSIBILITY

TIME MANAGEMENT

COOPERATION

COMMUNICATION

RECAP

1 Introduction 2

3 4

5 Benefits

Contributions

Experience

Project

THANK YOU!