Procedure Qualification Record No. Date
Welding Procedure Spec No.
Welding Process (es) Type (s)
JOINTS (QW-402)
BASE METALS (QW-403) POSTWELD HEAT TREATMENT (QW-407)
SECT. NO. 1 MAT'L Temperature
SECT. NO. 2 MAT'L Time
P-No. 8 Group No. 1 to P-No 1 Group No. 1 OtherThickness of Test Coupon
Diameter of Test Coupon
Maximum Pass Thickness
Other GAS (QW-408)
Shielding
SFA Specification Trailing
AWS Classification Backing
Filler Metal F-No. Other
Weld Metal Analysis A-No.
Size of Filler Metal
Filler Metal Product Form Current
Supplemental Filler Metal PolarityElectrode Flux Classification Amps. SEE WELDING PARAMETER
Flux Type Volts SEE WELDING PARAMETER
Brand Trade Name Tungsten Electrode Size -
Weld Metal Thickness Mode of Metal Transfer for GMAW (FCAW) -
Other Heat Input
Other -
POSITION (QW-405)Position of Groove TECHNIQUE QW-410Weld Progression (Uphill, Downhill) Travel Speed
Other - String or Weave Bead
Oscillation
PREHEAT (QW-406)Preheat Temperature Other -
Interpass temperature
Other `
Single or Multiple Electrodes
UPHILL
ELECTRICAL CHARACTERISTICS (QW-409)
Multipass or Single Pass (Per Side)
Percent Composition
60
SECTION 1 - SS SECTION 2 - CS
1 MM
3 MM
Groove Design of Test Coupon
( For combination qualifications, the deposited weld metal thickness shall be recorded for each filler metal and process used. )
PROCEDURE QUALIFICATION RECORDS (PQR)
As per ASME IX
Company Name :
(Automatic, Manual, Machine or Semi-Auto)
12.7 MM
FILLER METALS (QW-404)
Page 1 of 3
8/10/2019 Pqr.asme.Blank
2/3
PQR No.
% Shear
-
-
-
--
-
-
-
-
-
-
No Yes - No
SATISFACTORY - REFER REPORT NO. :-
Type of Test VICKERS HARDNESS TEST (HV 10) - REFER REPORT NO.:-
Deposit Analysis -
Other -
Welder's Name Welder ID
Test conducted by : Laboratory Test No.(Detail of record of tests are illustrative only and may be modified to conform to the type and number of tests required by the Code.)
CERTIFIED BY
SIGNATURE / DATE
Macro - Results
Other Tests
I/C or Passport No.
-
Comments
Fillet-Weld Test (QW-180)
Result - Satisfactory : Yes - - Penetration into Parent Metal : -
- - - - - -
-
- - - - - - -
- - - - - -
-
- - - - - - -
- - - - - -
-- - - - - - -- - - - - -
- - - - - - -
-
- - - - - - -
- - - - - -
S 3
S 4
Toughness Tests (QW-170)
Specimen No. Notch LocationSpecimen
Size
Test
Temparature
Impact ValuesDrop Weight Break (Y/N)
ft-lb or J Mils (in.) or mm
Guided-Bend Tests (QW-160)
Type and Figure No. Result
S 1
S 2
T 2
T 1
Tensile Test (QW-150)
Specimen
No.Width Thickness Area
Ultimate Total
Load
Ultimate Unit Stress, (psi
or Mpa)Type of Failure and Location
Page 2 of 3
MSI/PQR/002-14
PROCEDURE QUALIFICATION RECORDS PQRSection IX, ASME Boiler and Pressure Vessel Code
8/10/2019 Pqr.asme.Blank
3/3
PQR No.
= 300 MM
TIME SPEED
(min & sec) (mm/min)
SECTION 1 SECTION 2
1 MM
COUPON
LENGTH
SMAW
SMAW
SMAW
AWS
CLASS /
BRAND
PASS NO. PROCESS SIZE AMPERAGE VOLTAGE
ROOT1
Page 3 of 3
WELDING PARAMETER
PROCEDURE QUALIFICATION RECORDS (PQR)
Section IX, ASME Boiler and Pressure Vessel Code
FILLER METALWELD WELD CURRENT TRAVEL
POLARITY
DCEN / DCEP
HOTPASS2
DCEP
DCEP
DCEPHOTPASS
3
HEAT INPUT
(kJ/mm)
INTERPASS
TEMP. ( C )
SMAW
SMAW
SMAW
SMAW
DCEP
DCEP
DCEP
DCEP
4
5
6
7
FILL
FILL
CAPPING
CAPPING
3 MM
60
12 MM
1
2
3
4
5
6 7