Edition 5 / Revision 2 TRANSPORT FOR NSW
June 2020
TRANSPORT FOR NSW (TfNSW)
QA SPECIFICATION B310
COMPRESSION SEAL EXPANSION JOINTS
NOTICE
This document is a Transport for NSW QA Specification. It has been developed for use with
roadworks and bridgeworks contracts let by Transport for NSW or by local councils in NSW. It is not
suitable for any other purpose and must not be used for any other purpose or in any other context.
Copyright in this document belongs to Transport for NSW.
REVISION REGISTER
Ed/Rev
Number
Clause
Number Description of Revision
Authorised
By Date
Ed 1/Rev 0 First Issued. GM,CMS 04.03.91
Ed 2/Rev 0 Reformatted and converted to MS Word 6.0c
References updated.
GM, RNIC
(W Ho)
25.07.97
1.3 Refer to Special Conditions.
Ed 3/Rev 0 All Major changes. Samples for testing to be
taken from lengths of seal, not from raw
material of elastomer. Requirements for
lubricant adhesive added.
GM, RNIC 04.05.00
Ed 3/Rev 2 1.3 Reference to Conditions of Contract changed
to suit C1.
GM, RNIC 30.05.01
Ed 4/Rev 0 1.2 Revised Standards. Details transferred to
annexure B310/M
GM, RNIC 11.03.03
2 & 4 Revised elastomer properties.
3 to 5 Clauses renumbered 4 to 6
Annexure
B310/C
Schedule of Identified Records added.
Ed 4/Rev 1 Fonts changed GM, RNIC 07.08.03
Ed 5/Rev 0 Various Text revised to direct imperative style.
”Superintendent” replaced by “Principal”.
Reformatting and minor editing
“Shall” replaced by “must”
GM, RNIC
(P
Bamford)
01.11.06
Foreword New clause after the Table of Contents
Various Additional requirements
Ed 5/Rev 1 1.3 Use of approved seals mandated and link to
lists of RMS approved bridge proprietary
products added.
GM, IC 20.04.12
1.4 Warranty requirement added.
Ed 5/Rev 2 Global References to “Roads and Maritime
Services” or “RMS” changed to “Transport
for NSW” or “TfNSW” respectively.
DCS 22.06.20
Edition 5 / Revision 2 TRANSPORT FOR NSW
June 2020
QA SPECIFICATION B310
COMPRESSION SEAL EXPANSION
JOINTS
Copyright – Transport for NSW
IC-QA-B310
VERSION FOR:
DATE:
Compression Seal Expansion Joints B310
Ed 5 / Rev 2 i
CONTENTS
CLAUSE PAGE
FOREWORD ............................................................................................................................................... II TfNSW Copyright and Use of this Document ............................................................................... ii Revisions to Previous Version ....................................................................................................... ii Project Specific Changes ............................................................................................................... ii
1 GENERAL ........................................................................................................................................ 1 1.1 Scope .............................................................................................................................. 1 1.2 Structure of the Specification ......................................................................................... 1 1.3 Approved Bridge Components and Systems .................................................................. 1 1.4 Warranty ......................................................................................................................... 1
2 MATERIALS .................................................................................................................................... 2
3 DESIGN ........................................................................................................................................... 3
4 MANUFACTURE .............................................................................................................................. 3
5 ADHESIVE LUBRICANT ................................................................................................................... 4
6 INSTALLATION ............................................................................................................................... 4
ANNEXURES B310/A AND B310/B – (NOT USED).................................................................................... 5
ANNEXURE B310/C – SCHEDULE OF IDENTIFIED RECORDS .................................................................... 5
ANNEXURES B310/D TO B301/L – (NOT USED) ...................................................................................... 5
ANNEXURE B310/M – REFERENCED DOCUMENTS .................................................................................. 5
LAST PAGE OF THIS DOCUMENT IS ............................................................................................................ 6
B310 Compression Seal Expansion Joints
ii Ed 5 / Rev 2
FOREWORD
TFNSW COPYRIGHT AND USE OF THIS DOCUMENT
Copyright in this document belongs to Transport for NSW.
When this document forms part of a contract
This document should be read with all the documents forming the Contract.
When this document does not form part of a contract
This copy is not a controlled document. Observe the Notice that appears on the first page of the copy
controlled by TfNSW. A full copy of the latest version of the document is available on the TfNSW
Internet website: http://www.rms.nsw.gov.au/business-industry/partners-
suppliers/specifications/index.html
REVISIONS TO PREVIOUS VERSION
This document has been revised from Specification TfNSW B310 Edition 5 Revision 1.
All revisions to the previous version (other than minor editorial and project specific changes) are
indicated by a vertical line in the margin as shown here, except when it is a new edition and the text
has been extensively rewritten.
PROJECT SPECIFIC CHANGES
Any project specific changes are indicated in the following manner:
(a) Text which is additional to the base document and which is included in the Specification is
shown in bold italics e.g. Additional Text.
(b) Text which has been deleted from the base document and which is not included in the
Specification is shown struck out e.g. Deleted Text.
(TfNSW COPYRIGHT AND USE OF THIS DOCUMENT - Refer to the Foreword after the Table of Contents)
Ed 5 / Rev 2 1
TfNSW QA SPECIFICATION B310
COMPRESSION SEAL EXPANSION JOINTS
1 GENERAL
1.1 SCOPE
This Specification sets out the requirements for the design, supply and installation of preformed
elastomeric compression seals of the open-cell type and the adhesive lubricant used for their insertion
into concrete or steel faced bridge deck joints.
The seal must have multiple webs and accommodate compression by folding inwards at the top.
1.2 STRUCTURE OF THE SPECIFICATION
This Specification includes a series of annexures that detail additional requirements.
1.2.1 Schedule of Identified Records
The records listed in Annexure B310/C are Identified Records for the purposes of Specification
TfNSW Q Annexure Q/E.
1.2.2 Referenced Documents
Unless specified otherwise or is specifically supplied by the Principal, the applicable issue of a
referenced document must be the issue current at the date one week before the closing date for tenders,
or where no issue is current at that date, the most recent issue.
Standards, specifications and test methods are referred to in abbreviated form (e.g. AS 1234). For
convenience, the full titles are given in Annexure B310/M.
1.3 APPROVED BRIDGE COMPONENTS AND SYSTEMS
Unless approved otherwise by the Principal, use only TfNSW approved compression seal expansion
joints. Details of TfNSW approved bridge proprietary products can be found at:
http://www.rms.nsw.gov.au/business-industry/partners-suppliers/documents/tenders-
contracts/listofapprovedbridgecomponentssystems.pdf
1.4 WARRANTY
The supply of each proprietary compression seal expansion joint must be accompanied with a
warranty from the joint supplier in the name of Transport for NSW on the serviceability of the joint for
a minimum period of five years from the date of installation. Any joint that becomes defective within
this period must be rectified by the supplier at no cost to the Principal.
(TfNSW COPYRIGHT AND USE OF THIS DOCUMENT - Refer to the Foreword after the Table of Contents)
B310 Compression Seal Expansion Joints
2 Ed 5 / Rev 2
2 MATERIALS
Make the seal from vulcanised compound having polymerized chloroprene as the only base polymer.
The material of the seal, as manufactured, must conform to Table B310.1. Cut or buff all test
specimens from a length of preformed seal.
Table B310.1 - Material Properties
Property Requirement Test Method
Tensile Strength 13.8 MPa minimum AS 1683.11 (Dumb-bell test pieces)
Elongation at Break 250% minimum AS 1683.11 (Dumb-bell test pieces)
Hardness IRHD 59 ± 5 AS 1683.15.1
Compression Set 40% maximum AS1683.13 (72 hrs at 100°C)
Ageing: AS 1683.26 (Method A for 72 hours
at 100°C)
Change in Tensile Strength –20% to 0 AS 1683.11 (Dumb-bell test pieces)
Change in Elongation at Break –20% to 0 AS 1683.11 (Dumb-bell test pieces)
Change in Hardness IRHD 0 to +10 AS 1683.15.1
Resistance to Ozone No visible cracking AS 1683.24 (Ozone concentration
100 pphm in air, 20% strain,
100 hours at 40°C)
Low Temperature Stiffening
(Change in Hardness)
IRHD 0 to +15 AS 1683.15.1 (After 7 days
at –10°C)
Change in Volume in Oil +70% maximum AS 1683.23 (Using Oil No. 3, after
72 hours at 100°C)
Note: The Principal may waive the requirement for testing as above provided that:
(a) The elastomer for the manufacture of the seal is supplied by a company which has a third party
certified quality management system to AS/NZS ISO 9001 for the manufacture and supply of
elastomer;
(b) Test certificates are supplied to prove that the elastomer meets the properties specified in Table
B310.1 in Type Tests not more than six months old;
(c) Day to day batch quality control on the manufacture of the elastomer is exercised by performing
a test which accurately measures the cure characteristics of the elastomer and highlights
variations resulting from incorrect ingredients or levels thereof; and
(d) The manufacturer establishes control points and limits on batches which have been Type Tested
and uses these control points and limits for subsequent quality control purposes.
Obtain a Certificate of Compliance from a laboratory with appropriate registration from NATA, or
from an organisation mutually recognised by NATA, to verify the conformity of the seal upon
delivery, with the seal identified by a specific batch number. Provide a Certificate of Compliance not
more than one year old with each size of each seal type/configuration delivered. Provide with the
Certificate a statement that the raw material and manufacturing process detailed in the Certificate have
not changed. When the supply of raw material or the manufacturing process changes, a new
Certificate will be required.
(TfNSW COPYRIGHT AND USE OF THIS DOCUMENT - Refer to the Foreword after the Table of Contents)
Compression Seal Expansion Joints B310
Ed 5 / Rev 2 3
3 DESIGN
The design of the joint must conform to Clause 7.3 of AS/NZS ISO 9001, AS 5100.4 and this Clause.
The compression seal selected must accommodate the specified range of movement on the Drawings.
The actual joint gap, as confirmed from site measurements, and the selected size of compression seal
must:
(a) Permit the compression seal to be inserted;
(b) Allow the seal to compress within the seal’s design movement range to the minimum gap width
at ultimate maximum bridge temperature;
(c) Allow the seal to expand within the seal’s design movement range to the maximum gap width at
ultimate minimum bridge temperature after allowing for ultimate remaining concrete shrinkage
and creep effects and live load rotations.
The joint gap must be configured to prevent the compression seal from being pushed down further into
joint gap than the depth specified for the selected size of compression seal.
4 MANUFACTURE
The seal must conform to Table B310.2.
Following manufacture, each seal must be completely uniform and homogeneous throughout. Reject
any seal showing imperfections, surface splits or indentations.
The permissible tolerances for the seal cross-section are:
Tolerance (mm) = 0.05 x dimension
where “dimension” is the relaxed width or overall depth of the seal in millimetres.
The longitudinal profile of the seal must match the bridge cross section, and be obtained either by
removing a portion of the seal to bend it to the required angle or by joining straight lengths using an
adhesive recommended by the seal manufacturer. The seal must not be field spliced except when
permitted specifically by the Principal.
Table B310.2 – Seal Properties
Property Requirement Test Method
Recovery of compression seal: ASTM D 3542, Clause 8.2
High temperature recovery
after 72 hours at 100°C
80% minimum
Low temperature recovery
after 72 hours at –10 °C
88% minimum
Notes: (a) Two test samples must be tested simultaneously for each recovery test. The recovery value must
be the average result of the pair of samples, provided that the lowest result does not exceed a
tolerance of 0 to –3% of the minimum specified recovery.
(b) If, after a recovery test, any test sample exhibits adhesion between any internal faces, cracking in
any walls or splitting, reject the batch of seal represented by the sample.
(TfNSW COPYRIGHT AND USE OF THIS DOCUMENT - Refer to the Foreword after the Table of Contents)
B310 Compression Seal Expansion Joints
4 Ed 5 / Rev 2
5 ADHESIVE LUBRICANT
The adhesive lubricant must provide sufficient lubrication for insertion of the seal into the joint gap at
ambient temperatures. It must be a moisture cured or chemically cured single or multi component
compound compatible with the seal and substrate and not be affected by moisture. It must bond the
seal to the face of the joint gap and seal the joint against infiltration of moisture.
Use only a lubricant that conforms to Table B310.3 and is recommended by the seal manufacturer.
Verify compliance of the lubricant by submission of a test report issued by the manufacturer or, if
required by the Principal, by a NATA accredited test report.
Table B310.3 – Adhesive Lubricant Properties
Property Requirement Test Method
Solids content 60% minimum ASTM D 4070, Clause 9.1
Viscosity 20,000 to 300,000 cP ASTM D 4070, Clause 9.2
Lubricating life 2 hours minimum ASTM D 4070, Clause 9.3
Sag No sagging ASTM D 4070, Clause 9.4
Peeling strength test:
500 g load
1000 g load
zero
12 mm
ASTM D 4070, Clause 9.5
6 INSTALLATION
Verify that the joint gap and selected size of compression seal conform to Clause 3.
The compression seal must not be inserted into the joint gap until all deck concrete work in adjacent
spans or abutments is complete, except in the case of seals which are pre-compressed between
permanent steel sections with the assembly fixed in position prior to placing the concrete.
Install the seal in accordance with the manufacturer’s instructions.
The sides of the joint gap must be sound, dry and blast cleaned of all grit and loose particles before
installation of the seal unless required otherwise by the Principal.
Insert the seal into the joint gap using the adhesive lubricant and an insertion tool recommended by the
seal manufacturer.
(TfNSW COPYRIGHT AND USE OF THIS DOCUMENT - Refer to the Foreword after the Table of Contents)
Compression Seal Expansion Joints B310
Ed 5 / Rev 2 5
ANNEXURES B310/A AND B310/B – (NOT USED)
ANNEXURE B310/C – SCHEDULE OF IDENTIFIED RECORDS
Refer to Clause 1.2.1.
The records listed below are Identified Records for the purposes of TfNSW Q Annexure Q/E.
Clause Description of Identified Record
2 Certificate of Compliance that the elastomer used complies with the specified
requirements.
4 Test results showing that the seal complies with the specified requirements.
5 Test results showing that the adhesive lubricant complies with the specified
requirements.
ANNEXURES B310/D TO B301/L – (NOT USED)
ANNEXURE B310/M – REFERENCED DOCUMENTS
Refer to Clause 1.2.2.
TfNSW Specifications
TfNSW Q Quality Management System
Australian Standards
AS 1683.23 Methods of test for elastomers – Method 23: Rubber - Vulcanized –
Determination of resistance to liquids
AS 1683.24 Methods of test for elastomers – Method 24: Determination of the resistance of
vulcanized or thermoplastic rubbers to ozone cracking – Static strain test
AS 1683.26 Methods of test for elastomers – Method 26: Rubber, vulcanized or
thermoplastic - Accelerated ageing and heat resistance tests
AS 5100.4 Bridge design – Bearings and deck joints
AS/NZS ISO 9001 Quality management systems – Requirements
ASTM Standards
ASTM D 3542 Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals
for Bridges
(TfNSW COPYRIGHT AND USE OF THIS DOCUMENT - Refer to the Foreword after the Table of Contents)
B310 Compression Seal Expansion Joints
6 Ed 5 / Rev 2
ASTM D 4070 Standard Specification for Adhesive Lubricant for Installation of Preformed
Elastomeric Bridge Compression Seals in Concrete Structures