Ensayo Triaxial CID (ASTM D2850-70)

Muestra: Cenizas

Ds [cm] 5.04 Hm [cm] 10.29Dm [cm] 5.04 Peso [g] 340.38Di [cm] 5.04 winicial [%] 5 Dens seca

Dens Hum

Consolidación CorteTiempo Volumen Pres. Poros Deform. Anillo Volumen

[min] 0,01mm Carga Kgf0 20 2.86 0 0.5 16.9

0:00:06 19.6 10 12.6 16.80:00:15 19.4 20 15 16.70:00:30 19.25 30 17.3 16.60:01:00 19.15 40 18.4 16.50:02:15 19.1 50 20.4 16.40:04:00 19 60 22 16.30:06:15 19 70 23.7 16.20:09:00 18.9 80 24.6 16.1

90 26 16.0100 27.9 15.9150 33.5 15.4200 38.5 15.0250 42.8 14.6300 45.5 14.3350 48.7 14.0400 50.7 13.8450 52.3 13.6500 54.3 13.4600 57 13.1700 58.6 12.9800 60.3 12.7900 61.3 12.5

1000 62.2 12.41100 63.3 12.21200 63.8 12.11300 64.5 12.01400 64.9 11.91500 65.4 11.81600 65.8 11.71700 66.2 11.61800 66.5 11.51900 66.9 11.52000 66.9 11.4

s3'

[cm3] [kg/cm2] [cm3]

Ensayo Triaxial CID (ASTM D2850-70)

[kg/cm2] 1

1.5791.658

Ensayo Triaxial (ASTM D2850-70)

Muestra: Cenizas

Ds [cm] 5.04 Hm [cm] 10.29 [kg/cm2]Dm [cm] 5.04 Peso [g] 340.38Di [cm] 5.04 w [%] 5 Dens seca 1.579

Dens Hum 1.658

Consolidación CorteTiempo Volumen Pres. Poros Deform. Anillo Volumen

[min] 0,01mm Carga Kgf0 20.0 4.76 0 0.1 15.0

0:00:06 18.1 10 20.1 14.80:00:15 17.1 20 26.6 14.70:00:30 16.4 30 31.5 14.50:01:00 15.9 40 35.2 14.40:02:15 15.6 50 39.0 14.30:04:00 15.4 60 43.1 14.10:06:15 15.2 70 46.3 14.00:09:00 15.1 80 50.1 13.90:12:15 15 90 53.8 13.7

100 57.7 13.5150 72.5 13.0200 86.3 12.5250 98.6 11.8300 109.6 11.3350 118.8 10.9400 126.8 10.5450 133.9 10.1500 140.2 9.8600 151.4 9.2700 159.5 8.7800 166.3 8.3900 171.6 8.0

1000 175.3 7.71100 178.6 7.41200 181.1 7.21300 184.0 7.01400 186.0 6.91500 187.4 6.71600 189.0 6.51700 190.5 6.41800 191.9 6.31900 193.8 6.2

s3'

[cm3] [kg/cm2] [cm3]

2000 194.6 6.0

3