MOLDING
ROTATIONAL
Disclaimer:
- It is the customer’s responsibilities to inspect and test the product for sustainability of the customer’s own use and purpose. The customer responsible for appropriate, safe,
legal use, processing and handling of the product.
- To the best of our knowledge, the information contained herein is accurate and reliable as of the publication. We however do no assume any liability whatsoever for the accuracy t
and completeness of the information contained herein.
- We make no warranties which extend beyond the description herein. Nothing herein shall constitute any implied warranty of merchantability or fitness for a particular purpose.
- No liability can be accepted in respect of the use of the product in conjunction with other materials. The information contained herein relates exclusively to the product when it is
not used in conjunction with any third party’s materials.
Rev. Jan 2018 valid until next revision
- The application specified for reference only.
INTRODUCTION
01
Our Production Capacity (As of 2018)
(PE / PP / PVC)
Total Capacity : 2,878 KTA
Polyolefin
Total : 1,912 (KTA)
PVC
Total : 966 (KTA)
HDPE 920
PP 720
LLDPE 120
LDPE 152
PVC Resin 850
PVC Compound 80
PVC Paste Resin 36
SCG Chemicals is one of the largest integrated petrochemical companies in Asia and a key industry leader.
We manufacture and supply a full range of petrochemical products ranging from upstream monomers to
downstream polymer including PE, PP, PVC, PS and MMA
To better serve customers’ requirements, SCG Chemicals assign prime importance to development of new
technology and innovation for the creation of high value-added products and services (HVA).
Widely recognized for product quality as well as for excellent management and world-class operation
efficiency, SCG Chemicals has joint ventured with a number of the world’s leading chemical companies,
including the DOW Chemical Company, Mitsui Chemicals and Mitsubishi Rayon.
SCG Chemicals rotational molding resin has been well formulated for excellent all-round properties to suit
various types of rotational molding applications; water tank, cooler box, kayak, playground equipment,
flower pot, fuel tank, automotive part, etc.
We offer various forms of products as follows:
1. Natural PE pellets and powder
2. Color compound (Standard and Color-matched)
3. Special-effects (Granite, Wood, Terracotta)
The highlighted features include wide processing window, easy demolding, good dimensional stability,
good mechanical properties, UV resistance, and durability.
SCG Chemicals can tailor to customer demands from ready-to-mold- color to special-effect color compound
powder, which can be specifically matched to your individual needs to keep you ahead of the competition.
Rotational MoldingKeep you ahead
03
Automotive Application
C8
Natural
8
Color
UV Level
ASTM G155
Density
[g/cm3]
ASTM D1505
Grade M3504DXP
C8
Color Compound
8
0.935
M50
C4
Natural
8
0.932
Melt Index
[g/10 min]
ASTM D1238 @190°C, 2.16 kg46
Flexural Modulus
[kg/cm2 (MPa)]
ASTM D7906,400 (630)5,800 (570)
Tensile Strength at Yield
[kg/cm2 (MPa)]
ASTM D638180 (18)170 (17)
Elongation at Break
[%]
ASTM D6381,1001,000
ARM Impact Strength at -40°C
[J/mm]
ARM Method (5 mm part)
Optimum PIAT*
[°C]
TPE Method**
2825
M735RW
C4
Natural
4
M735RU
C4
Color Compound
8
Key Characteristic
RecommendedApplication
- Excellent ESCR
- Good chemical resistance
- Excellent impact resistance
- Low warpage
- Fair processing
- TUV certified
M70
Resin Type
235 225220200 220
- Suitable for intricate parts
- Good impact resistance
- Excellent surface finishing
- Good dimensional stability
- Diesel tank - AdBlue tank
- Roofing
- Interior parts
Remarks: * Optimum PIAT can vary, depending on color strength and molding condition.
** Oven temperature 280°C, oven time 15-30 minutes, rotomolded part thickness 5 mm.
Values quoted here are representative of tested specimens only. This data is not intended for specification purposes.
For technical assistance, please contact SCG Chemicals representative near you.
04
Building & Infrastructure Application
C4
Natural
8
Color
UV Level
ASTM G155
Density
[g/cm3]
ASTM D1505
Grade M3804RW
C4
Natural
2
M3804RU
C4
Color Compound
8
0.938
M10
Melt Index
[g/10 min]
ASTM D1238 @190°C, 2.16 kg4
Flexural Modulus
[kg/cm2 (MPa)]
ASTM D7907,200 (700)
Tensile Strength at Yield
[kg/cm2 (MPa)]
ASTM D638200 (20)
Elongation at Break
[%]
ASTM D638800
ARM Impact Strength at -40°C
[J/mm]
ARM Method (5 mm part)
Optimum PIAT*
[°C]
TPE Method**
27
Key Characteristic
RecommendedApplication
- High stiffness
- Good processing
- Good impact resistance
Resin Type
220180 220
- Domestic water tank (Up to 5,000 L.)
C4
Natural
20
M9001RW
0.939
Color Compound
8/20
3.2
7,500 (740)
210 (21)
1,100
29
C4
- High stiffness
- Excellent impact resistance
- Long durability
- Good processing
- Meet the requirement of AS/NZS 4766
M90
200
- Septic tank
- Underground water tank
- Medium-to-large size water
tank (Up to 22,500 L.)
Remarks: * Optimum PIAT can vary, depending on color strength and molding condition.
** Oven temperature 280°C, oven time 15-30 minutes, rotomolded part thickness 5 mm.
Values quoted here are representative of tested specimens only. This data is not intended for specification purposes.
For technical assistance, please contact SCG Chemicals representative near you.
05
C4
Natural
8
C4
Natural
4
Color
UV Level
ASTM G155
Density
[g/cm3]
ASTM D1505
Grade M735RU M735RW
Melt Index
[g/10 min]
ASTM D1238 @190°C, 2.16 kg
Flexural Modulus
[kg/cm2 (MPa)]
ASTM D790
Tensile Strength at Yield
[kg/cm2 (MPa)]
ASTM D638
Elongation at Break
[%]
ASTM D638
ARM Impact Strength at -40°C
[J/mm]
ARM Method (5 mm part)
Optimum PIAT*
[°C]
TPE Method**
0.932
6
5,800 (570)
170 (17)
1,000
25
Color Compound
8
C4
Key Characteristic
RecommendedApplication
M70
Building & Infrastructure Application
Resin Type
220200 220
- Suitable for intricate parts
- Good impact resistance
- Excellent surface finishing
- Good dimensional stability
- Industrial cleaning machine
- Air blower
- Industrial parts
Remarks: * Optimum PIAT can vary, depending on color strength and molding condition.
** Oven temperature 280°C, oven time 15-30 minutes, rotomolded part thickness 5 mm.
Values quoted here are representative of tested specimens only. This data is not intended for specification purposes.
For technical assistance, please contact SCG Chemicals representative near you.
C4
Natural
2
M3204RU
C4
Color Compound
8
0.932
4
5,800 (570)
170 (17)
1,100
28
M40
220180
- Excellent impact resistance
- Suitable for low temperature service
- Good processing
- Low warpage
- Good dimensional stability
- Road barrier
- Traffic cone
06
Living & Lifestyle Application
Color
UV Level
ASTM G155
Density
[g/cm3]
ASTM D1505
Grade
0.9380.932
Melt Index
[g/10 min]
ASTM D1238 @190°C, 2.16 kg44
Flexural Modulus
[kg/cm2 (MPa)]
ASTM D7907,200 (700)5,800 (570)
Tensile Strength at Yield
[kg/cm2 (MPa)]
ASTM D638200 (20)170 (17)
Elongation at Break
[%]
ASTM D6388001,100
ARM Impact Strength at -40°C
[J/mm]
ARM Method (5 mm part)
Optimum PIAT*
[°C]
TPE Method**
2728
Key Characteristic
RecommendedApplication
- High stiffness
- Good processing
- Good impact resistance
Resin Type
220180 220220
- Excellent impact resistance
- Suitable for low temperature service
- Good processing
- Low warpage
- Good dimensional stability
- Trash bin- Trash bin
- Playground equipment
Remarks: * Optimum PIAT can vary, depending on color strength and molding condition.
** Oven temperature 280°C, oven time 15-30 minutes, rotomolded part thickness 5 mm.
Values quoted here are representative of tested specimens only. This data is not intended for specification purposes.
For technical assistance, please contact SCG Chemicals representative near you.
M3804RWM3204RU M3804RU M10M40
C4
Natural
8
C4
Natural
2
C4
Natural
2
C4
Color Compound
8
C4
Color Compound
8
07
C4 C4
Natural
4 8
Color
UV Level
ASTM G155
Density
[g/cm3]
ASTM D1505
Grade M735RU
C4
Natural
8
M735RW
0.932 0.939
Color CompoundColor Compound
8/20
Melt Index
[g/10 min]
ASTM D1238 @190°C, 2.16 kg6 3.2
Flexural Modulus
[kg/cm2 (MPa)]
ASTM D7905,800 (570) 7,500 (740)
Tensile Strength at Yield
[kg/cm2 (MPa)]
ASTM D638170 (17) 210 (21)
Elongation at Break
[%]
ASTM D6381,000 1,100
ARM Impact Strength at -40°C
[J/mm]
ARM Method (5 mm part)
Optimum PIAT*
[°C]
TPE Method**
25 29
C4
Key Characteristic
RecommendedApplication
- Suitable for intricate parts
- Good impact resistance
- Excellent surface finishing
- Good dimensional stability
- High stiffness- Excellent impact resistance- Long durability- Good processing- Meet the requirement of AN/NZS 4766
M90M70
Living & Lifestyle Application
Resin Type
220200 220 200
- Decorative item
- Flower pot
- Furniture
- LED lamp cover
- Kayak
Remarks: * Optimum PIAT can vary, depending on color strength and molding condition.
** Oven temperature 280°C, oven time 15-30 minutes, rotomolded part thickness 5 mm.
Values quoted here are representative of tested specimens only. This data is not intended for specification purposes.
For technical assistance, please contact SCG Chemicals representative near you.
08
Color
UV Level
ASTM G155
Density
[g/cm3]
ASTM D1505
Grade
0.9380.932
Melt Index
[g/10 min]
ASTM D1238 @190°C, 2.16 kg44
Flexural Modulus
[kg/cm2 (MPa)]
ASTM D7907,200 (700)5,800 (570)
Tensile Strength at Yield
[kg/cm2 (MPa)]
ASTM D638200 (20)170 (17)
Elongation at Break
[%]
ASTM D6388001,100
ARM Impact Strength at -40°C
[J/mm]
ARM Method (5 mm part)
Optimum PIAT*
[°C]
TPE Method**
2728
Key Characteristic
RecommendedApplication
- High stiffness
- Good processing
- Good impact resistance
Container & Material Handling Equipment Application
Resin Type
220180 220220
- Excellent impact resistance
- Suitable for low temperature
service
- Good processing
- Low warpage
- Good dimensional stability
- Intermediate bulk container (IBC) - Cooler box
- Fish bin
Remarks: * Optimum PIAT can vary, depending on color strength and molding condition.
** Oven temperature 280°C, oven time 15-30 minutes, rotomolded part thickness 5 mm.
Values quoted here are representative of tested specimens only. This data is not intended for specification purposes.
For technical assistance, please contact SCG Chemicals representative near you.
M3804RWM3204RU M3804RU M10M40
C4
Natural
8
C4
Natural
2
C4
Natural
2
C4
Color Compound
8
C4
Color Compound
8
09
C8 C8
Natural
8 8
Color
UV Level
ASTM G155
Density
[g/cm3]
ASTM D1505
Grade M3504DXP
0.9350.939
Color Compound Color Compound
8/20
Melt Index
[g/10 min]
ASTM D1238 @190°C, 2.16 kg43.2
Flexural Modulus
[kg/cm2 (MPa)]
ASTM D7906,400 (630)7,500 (740)
Tensile Strength at Yield
[kg/cm2 (MPa)]
ASTM D638180 (18)210 (21)
Elongation at Break
[%]
ASTM D6381,1001,100
ARM Impact Strength at -40°C
[J/mm]
ARM Method (5 mm part)
Optimum PIAT*
[°C]
TPE Method**
2829
C4
Key Characteristic
RecommendedApplication
- Excellent ESCR
- Good chemical resistance
- Excellent impact resistance
- Low warpage
- Fair processing
- High stiffness
- Excellent impact resistance
- Long durability
- Good processing
- Meet the requirement of AN/NZS 4766
M90
Natural
20
C4
M9001RW M50
Container & Material Handling Equipment Application
Resin Type
235 225200
- Intermediate bulk container (IBC)
- Pallet
- Chemical container
- Army storage box
Remarks: * Optimum PIAT can vary, depending on color strength and molding condition.
** Oven temperature 280°C, oven time 15-30 minutes, rotomolded part thickness 5 mm.
Values quoted here are representative of tested specimens only. This data is not intended for specification purposes.
For technical assistance, please contact SCG Chemicals representative near you.
10
Agriculture & Marine Application
C8
Natural
8
Color
UV Level
ASTM G155
Density
[g/cm3]
ASTM D1505
Grade M3504DXP
C8
Color Compound
8
0.935
M50
C4
Natural
20
0.939
Melt Index
[g/10 min]
ASTM D1238 @190°C, 2.16 kg43.2
Flexural Modulus
[kg/cm2 (MPa)]
ASTM D7906,400 (630)7,500 (740)
Tensile Strength at Yield
[kg/cm2 (MPa)]
ASTM D638180 (18)210 (21)
Elongation at Break
[%]
ASTM D6381,1001,100
ARM Impact Strength at -40°C
[J/mm]
ARM Method (5 mm part)
Optimum PIAT*
[°C]
TPE Method**
2829
M9001RW
C4
Color Compound
8/20
Key Characteristic
RecommendedApplication
- Excellent ESCR
- Good chemical resistance
- Excellent impact resistance
- Low warpage
- Fair processing
- TUV certified
M90
Resin Type
235 225200
- High stiffness
- Excellent impact resistance
- Long durability
- Good processing
- Meet the requirement of AS/NZS 4766
- Chemical tank
- Pesticide tank
- Liquid fertilizer tank
- Diesel tank
- Large water tank (up to 22,500 L.)
- Silo
- Bouy
- Pontoon
Remarks: * Optimum PIAT can vary, depending on color strength and molding condition.
** Oven temperature 280°C, oven time 15-30 minutes, rotomolded part thickness 5 mm.
Values quoted here are representative of tested specimens only. This data is not intended for specification purposes.
For technical assistance, please contact SCG Chemicals representative near you.
DET1Dark Emerald
PGM1Panita Green
GNT1Milky Jade
FMM1Fog Mandarin
LLM1Lemon Lime
SLM1Sun Rise
SST6Sand Beach
RST1Rosetta
SST3Petra Gold
MST1Mill Stone
SST1Sand Stone
MST2Grey Granite
WMM1White Marble
SSM1Sand Marble
CRT1French Vanilla
GET2Green Tea
SOT1Sparkle Obsidian
BET1Smooth Cream
BRT1Beige
BRT3Wheat
BRM4Atras Sand
BET5Gobelin Beige
GRT1Mistgreen
GRU4Dark Forest
DBM1Blue Berry
RDM8Scarlet Red
GYT1Slate Grey
GYT3Light Grey
WTM1Creamy White
WTN5Rose White
WTT2Smoky White
BLM1Cyan Blue
RDN4Vermillion
WTN9Snow White
ORN7Scarlet Orange
ORM1Carrot Orange
WTT4Bluish White
BLT2Mountain Blue
ORN4Saffron Orange
GYM4Hot Spring
GYM6Posh Grey
GYN7Engine Grey
RDT2Western boots
YLM1Enoyable Yellow
DBN7Nautical Blue
YLN9Merry Yellow
DBO4Stained Glass Blue
GRT3Heritage Green
GYO4Contorail Silver
GRM1Health Green
GRO6Locomotive Green
GRU1Wild Fern
YLM9Vital Gold
YLN7Diver Yellow
YLO2Calf Skin Camel
YLN6Gold Medal
GRP1Green Emerald
BKM1Graphite Black
11
Shanghai
Guangzhou
Australia
Ho Chi Minh
Myanmar
Hanoi
Thailand
Overseas Offices & Contact Information
SOUTHEAST ASIA CHINA
196 Truong Chinh, Dong Da dist., Hanoi city
Tel. +84 439 744 354
Fax. +84 439 744 350
10th Floor, An Phu Plaza 117-119 Ly Chinh
Thang P7, Q3 Ho Chi Minh City, Vietnam
Tel. +84 988 804 672
Fax. +84 829 612 76
SCG Plastics Co., Ltd.
Gyi Gone, Yangon, Myanmar
Tel. +95 951 946 41, +95 973 183 332
MYANMAR
VIETNAM
RM 1012 Huarong Building No.1271-1289, South of Pudong
Road, Pudong New Area, Shanghai, China, 200122
Tel. +86 182 170 743 69
Fax. +86 216 888 6092
AUSTRALIA
SCG Trading Australia Pty Ltd.
Level 4, No.1 Chandos Street,
St. Leonards NSW 2065, Australia
Tel. +61 294 381 225, +61 411 022 231
Fax. +61 294 360 195
Unit 3207, Block B, China Shine Plaza, No.9 Lin He Xi
Road, Tianhe, Guangzhou, China 510610
Tel. +86 139 030 579 29
Fax. +86 203 810 1370
SCG Chemicals Co., Ltd.
1 Siam Cement Road, Bangsue, Bangkok,
Thailand 10800
Tel: +662 586 1111 Ext. 4116
Fax: +662 586 3676
Email: [email protected]
Head Office:
SCG Plastics Co., Ltd. (Ho Chi Minh Office)
2nd floor N. 136/137, Pyay Road, Saw Bea
SCG Plastics Co., Ltd. (Hanoi Office)
SCT Co., Ltd. (Hanoi) Representative Office
SCG Plastics (China) Co., Ltd. (Shanghai Office)
SCG Plastics (China) Co., Ltd. (Guangzhou Office)
SCG Chemicals Co., Ltd.
1 Siam Cement Road, Bangsue, Bangkok, Thailand 10800
Tel. +662 586 1111 Ext. 4116 Fax. +662 586 3676
www.scgchemicals.com
Top Related