WQT Format
4
WELDER PERFORMANCE QUALIFICATION TEST RECORD ( AWS D1.1 & 230/10/10/QA/PC/NA/0116) Certificate No.: 047 Form No.: 583-STR-008 Type of Welder Manual Welder ID : W - 1056 Using WPS No. 583-06 Date : 30.11.2011 The above mentioned welder is qualified for the following ranges. Variables Record Actual Values Qualification Range Used in Qualification Process/Type [Table 4.12, Item (1)] SMAW SMAW Electrode (single or multiple) [Table 4.12, Item (7) Single Single Current/Polarity DCEP DCEP Position [Table 4.12, Item (3)] 3G (V) 3G (F,V) Weld Progression [Table 4.12, Item (5)] Vertical Up Vertical Up Backing (YES or NO) [Table 4.12, Item (6)] Without With or Without Material/Spec. Base Metal BS EN 10025 S275JR BS EN 10025 S275JR or Equival Thickness: (Plate) Groove 12 mm 3 - 24 mm Fillet NA ALL Thickness: (Pipe/tube) Groove NA 3 - 24 mm (24" & above Dia Fillet NA All Thickness for 24" & above D Diameter: (Pipe) Groove NA Ø 24 inch & Above Fillet NA Ø 24 inch & Above Filler Metal (Table 4.12) Spec. No. SFA 5.1 SFA 5.1 Class E 7018-1 E 7018-1 F-No. [Table 4.12, Item (2)] F4 F4 Gas/Flux Type (Table 4.12) NA NA Other VISUAL INSPECTION (4.8.1) GUIDED BEND TEST RESULTS (4.30.5) Type Result Type Result NA FILLET TEST RESULTS (4.30.2.3 and 4.30.4.1) (Describe the location, nature, and size of any crack or tearing of the specimen.) RADIOGRAPHIC TEST RESULTS (4.30.3.2) Film Identificati Results Remarks Number ACCEPTED NA WQT- 78 V.R. ANJANEYULU Test Number:RT/WQT- 54 Medgulf Const. Co CAEL Qatargas Name Welder Name: Niraj Kumar Acceptable YES or NO: YES Report No.: VT/WQT-78 Appearance : ____________________NA_________ Fillet Size:______________NA__________________ Fracture Test Root Penetration:______ NA _________ Macroetch: _____________NA__________________ Interpreted by Organization: Sievert Date: 30.11.2011 PHOTO
-
Upload
abdul-khaliq -
Category
Documents
-
view
2.187 -
download
162
Transcript of WQT Format
WELDER PERFORMANCE QUALIFICATION TEST RECORD
( AWS D1.1 & 230/10/10/QA/PC/NA/0116)
Certificate No.: 047 Form No.: 583-STR-008
Type of Welder: Manual
Welder ID : W - 1056Using WPS No. 583-06 Date : 30.11.2011
The above mentioned welder is qualified for the following ranges.
Variables Record Actual Values Qualification Range
Used in Qualification
Process/Type [Table 4.12, Item (1)] SMAW SMAW
Electrode (single or multiple) [Table 4.12, Item (7)] Single Single
Current/Polarity DCEP DCEP
Position [Table 4.12, Item (3)] 3G (V) 3G (F,V)
Weld Progression [Table 4.12, Item (5)] Vertical Up Vertical Up
Backing (YES or NO) [Table 4.12, Item (6)] Without With or Without
Material/Spec.
Base Metal BS EN 10025 S275JR BS EN 10025 S275JR or Equivalent
Thickness: (Plate)
Groove 12 mm 3 - 24 mm
Fillet NA ALL
Thickness: (Pipe/tube)
Groove NA 3 - 24 mm (24" & above Dia.)
Fillet NA All Thickness for 24" & above Dia.
Diameter: (Pipe)
Groove NA Ø 24 inch & Above
Fillet NA Ø 24 inch & Above
Filler Metal (Table 4.12)
Spec. No. SFA 5.1 SFA 5.1
Class E 7018-1 E 7018-1
F-No. [Table 4.12, Item (2)] F4 F4
Gas/Flux Type (Table 4.12) NA NA
Other
VISUAL INSPECTION (4.8.1)
GUIDED BEND TEST RESULTS (4.30.5)
Type Result Type Result
NA
FILLET TEST RESULTS (4.30.2.3 and 4.30.4.1)
(Describe the location, nature, and size of any crack or tearing of the specimen.)
RADIOGRAPHIC TEST RESULTS (4.30.3.2)Film Identification Results RemarksNumber ACCEPTED NAWQT- 78
V.R. ANJANEYULU Test Number: RT/WQT- 54
Medgulf Const. Co CAEL Qatargas
Name
Welder Name: Niraj Kumar
Acceptable YES or NO: YES Report No.: VT/WQT-78
Appearance : ____________________NA_________ Fillet Size:______________NA__________________
Fracture Test Root Penetration:______ NA _________ Macroetch: _____________NA__________________
Interpreted by: Organization: Sievert Date: 30.11.2011
PHOTO
Signature
Date