8/2/2019 Wind Turbine Rotor
1/14
INTRODUCTION
This report explains briefly about the design procedure and the
fabrication of a wind turbine blades. The design procedure has two
main steps.
I. CALCULATION OF THE POWER FROM THE WIND.II. BLADE DESIGN
I. CALCULATION OF THE POWER FROM THE WIND.Calculation of the power from the wind includes the calculation
of the following parameters.
1.Diameter of the rotor.2.Power from the rotor.3.Mean power output.4.Tip speed ratio (TSR).5.Shaft speed.
1.DIAMETER OF THE ROTOR.Diameter, D = (P/(Cp*/2*/4*V
3))
O.5(m)
Where,
, density of air, (kg/m3) = 1.2 ( Temperature Dependent )
Cp, Power co-efficient = Cp< 0.6, say 0.4
V, Wind speed (m/s) = 9 m/s ( Rated Wind Speed )
P, power (Watts) = 1200 ( considering the
losses )
To find the diameter lets substitute the input parameters in the
equation, with the power rating of 1KW.
Diameter, D = ( 1200/(0.4*(1.2/2)*(/4)*(93))
0.5
= 2.95 m.
The rotor may be designed for diameter up to 3 meters.
-
8/2/2019 Wind Turbine Rotor
2/14
2.POWER FROM THE ROTOR.Power (in watts) is the rate of capture of energy, at any given
instant.
Power, P = Cp*1/2**A*V3
i.e.,
Power, P(watts) = Cp*/2*/4*D2*V
3
= 0.4*(1.2/2)*/4*2.952*9
3
= 1236.7 Watts.
If the windmill catches 40% of the raw power in the wind. Then
percentage caught is known as the 'power coefficient', Cp.
The raw power in the wind depends on the following.
1.The density of air.2.The speed of the wind.3.The size of the rotor.
Wind speed is critical, Stronger winds carry a greater mass of air
through the rotor per second and the kinetic energy per kilogram of
air depends on the square of its speed, so the power in the wind will
increase dramatically with wind speed.
3.MEAN POWER OUTPUT.Pm= 0.14*D
2*Vm
3
Where,Pm = Mean Wind speed.
Vm = Mean Wind velocity.
Let us consider a mean wind velocity, Vm = 9 m/s.
Pm = 0.14*(2.952)*(9
3)
= 0.14*2.95
2
*9
3
= 888.17 watts on average.
-
8/2/2019 Wind Turbine Rotor
3/14
4.TIP SPEED RATIO (TSR).TIP SPEED RATIO (TSR) =(tip speed of blade)/(wind speed).
The tip speed ratio is a very important factor in the different formulasof blade design.
Generally can be said, that a three bladed wind turbine use 5-7 as tip
speed ratios.
We can calculate the rotor tip speed ratio.
TSR = RPM**D/60/V
we calculate the rpm we can get with TSR = 7
RPM = 60*V*TSR/(*D)
= ( 60*9*7 )/( *2.95 )
= 407.8
All this is based on a 9 m/s wind speed. We must also consider the
power and speed conditions at low winds like 4m/s.
P = Cp*/2*/4*D2*4
3= 104.9 Watts.
Rpm = 60*V*TSR/(*D)
= 60*4*6/(3.14*2.95)
= 181.2 rpm
(So, the generator must produce some power at speeds under 200rpm, if it is to work well in low winds.)
5.Shaft speed.Rpm = 60*V*TSR/( x D) = 407.8 rpm
Shaft must be designed for up to 500 RPM.
-
8/2/2019 Wind Turbine Rotor
4/14
II. BLADE DESIGN.The 'Blade Design' section suggests the shape of the blade at
each station. Say we use 5 stations along the blade length, at radius'Rs' = 0.29, 0.58, 0.87, 1.16, and 1.47 metre.
We choose,
B = 3 blades.
'CI' = 0.8.
'Alpha' = 4.Length = 1.47 m.
At each station we should find the setting angle 'Beta', and thechord width 'Cw'
Blade setting angle, Beta = ATAN(D/3/Rs/TSR)-4
Chord width, Cw = 5.6*L/(B*CI*Rs*TSR2)
Drop = Cw*SIN(Beta)
Thickness = 0.15 *Cw (or 0.12 *Cw at the tip).
CALCULATIONS
i. For Rs = 0.294Beta = ATAN(2.95/3/0.294/7)-4
= 21.64
Cw = 5.6*1.47/(3*0.8*0.294*72)
= 0.210 m.
Drop = 0.210*SIN(21.64)
= 0.077 m.
Thickness = 0.15*0.210
= 0.0315 m.
-
8/2/2019 Wind Turbine Rotor
5/14
ii. For Rs = 0.588Beta = ATAN(2.95/3/0.588/7)-4
= 9.43
Cw = 5.6*1.47/(3*0.8*0.588*72)
= 0.16 m.
Drop = 0.160*SIN(9.43)
= 0.026 m.
Thickness = 0.15*0.160
= 0.024 m.
iii. For Rs = 0.882Beta = ATAN(2.95/3/0.882/7)-4
= 5.04
Cw = 5.6*1.47/(3*0.8*0.882*72)
= 0.140 m.
Drop = 0.140*SIN(5.04)
= 0.012 m.
Thickness = 0.15*0.140
= 0.021 m.
iv. For Rs = 1.176Beta = ATAN(2.95/3/1.176/7)-4
= 2.81
Cw = 5.6*1.47/(3*0.8*1.176*7
2
)
-
8/2/2019 Wind Turbine Rotor
6/14
= 0.110 m.
Drop = 0.110*SIN(2.81)
= 0.005 m.
Thickness = 0.15*0.110
= 0.016 m.
v. For Rs = 1.47Beta = ATAN(2.95/3/1.47/7)-4
= 1.45
Cw = 5.6*1.47/(3*0.8*1.47*72)
= 0.09 m.
Drop = 0.09*SIN(1.45)
= 0.0022 m.
Thickness = 0.15*0.09
= 0.0135 m.
Naca 23015 profile was chosen
-
8/2/2019 Wind Turbine Rotor
7/14
FABRICATION OF THE BLADE
EQUIPMENT REQUIRED
The blades are made from fibre glass. This fibre glass has great strength intension and compression. The various chemicals required are listed here.
Chemicals required
Resin
Resin Type R 10-03
This is a general purpose rigid orthopthalic (FRP)
polyester resin. It is relatively inexpensive and isused for the majority of the wind turbine blades.
Resin Type Polymer 31-441
This is called a gel coat polyester resin. It is
100% isophthalic with Neo-Pentyl Glycol (NPG).
It is very hard wearing and is scratch and
chemical resistant. It is more expensive than the
other type of resin therefore its use is limited tojust the outer layers of the blade.
STYRENE MONOMER
This is mixed with the resin to reduce the viscosity
of the resin. This makes the resulting mixture more
workable and easier to paint onto the fibre glasscloth.
HARDENER
Hardener is added to the resin mix to start the
solidification (or curing) process. The time taken
before the resin sets is controlled by the amount of
hardener and accelerator (cobalt) added. Once the
hardener is added to the resin it must be worked
quickly into the fibreglass as the resin will solidifyquickly.
-
8/2/2019 Wind Turbine Rotor
8/14
COBALT
Cobalt is an 'accelerator' that speeds up the
hardening process when added to the resin.This can be used to help control the setting time
of the resin.
TONER
This only adds colour to the resin. It has no
structural properties. It is used to colour the
outer layers of resin, rather than paint the
blades afterwards. This can be obtained inmany different colours. Approx 5 to 10% by
weight is added to the resin mixture until the
correct colour is reached. Adding a greater
amount than this may inhibit the solidification
process. Adding toner makes the lay-up stage
easier as you can clearly see where the resin is,
however this makes the foam filling stage more
difficult as the blade is then opaque.
LOWILITE
This is a UV stabilizer and must be used on the
outer layers of resin. It helps to prevent material
degradation by sunlight. It is supplied in powder
form.
DURAWAX
This is a release agent. It is applied to the mould
before each lay-up to ensure that the itemproduced does not stick to the mould.
Sometimes a thin non-stick film is added to
moulds to avoid the part sticking given the
complex curved shape of the moulds a wax
release agent was selected.
-
8/2/2019 Wind Turbine Rotor
9/14
FIBRE GLASS CHOPPED STRAND
FIBRE GLASS MAT (CSM)
The fibres within CSM are in random
orientation. This means that it has thesame strength in every direction. It is the
cheapest and easy to work with, as its
orientation does not matter. It used to
produce the moulds and a thin veil of
100gsm is used to join the sides and
protect the leading edge.
WOVEN CLOTH FIBRE GLASS (WC)
This consists of woven strands. It is very
strong in the direction of the weave but is
slightly more expensive and harder to
work with as the orientation of the weave
when the piece is cut must be carefully
chosen. The cut weave has a tendency to
unravel when it is handled in a dry state.
THINNERS
Lacquer thinners are required to remove excess resin and to clean up
any spills, paint brushes, pots and tools.
It is extremely flammable.
CAR BODY FILLER
A two-part car body filler is used to fill
small blemishes and gaps on the final
blades. Usually is supplied as a tin of
resin with a small tube of hardener.
The resin is a thermal-set plastic. The
hardener, MEK peroxide, is a catalyst.
The two components are mixed in a proportion of approximately 1%
to 3% hardener to resin. Use a good quality brand.
-
8/2/2019 Wind Turbine Rotor
10/14
EXPANDING FOAM
A two-part expanding polyurethane low density foam is used to fill
the air gaps within the blade. The foam is initially two liquids which
must be mixed in a ratio of 1:1. This will then expand to 25 times its
initial volume. Such foam is used in boat building and construction.
This foam may not be required and the structure can be left empty but
it significantly improves the rigidity and strength of the blade.
BLADE MANUFACTURE
The blade is comprised of two blade halves, the windward half and
the backward half. Each blade half is built up from 16 layers of fibre
glass mat. Woven cloth (WC) is used for additional strength in the
direction the forces act on the blades.
Materials required:
For one blade:
The general process is as follows:
1.Preparation: Cut the layers of fibreglass WC. 16 layers are used ineach half.
2.Preparation:Prepare batches of resin mixture and the corresponding
batches of hardener.
4.Preparation: Wax the mould to ensure easy release.
-
8/2/2019 Wind Turbine Rotor
11/14
5.Procedure: Fill the moulds with a layer of resin, then a layer offibreglass WC until all 16 layers have been placed. The weave of
the WC must be rotated by 45 degrees between each layer.
6.Procedure: Leave to dry.BLADE JOINING
When set, the two halves of the blade need to be joined to form a
single unit. To do this they need to be accurately cut so that the two
pieces fit together. The join should be made with minimal impact on
the blades aerodynamic shape.
Also additional strength and rigidity is added to the blade through the
use of a stringer from the root to the tip. A wooden core is inserted
at the root. This is so the screws used to hold the blades to the wind
turbine have something to bite into. It also stops the blade rootcollapsing when the front blade assembly is bolted onto the generator
on the wind turbine.
BLADE TRIMMING
Firstly the excess (over lap from the mould) must be cut off. This was
done with a circular cutting saw. A jigsaw or a mini-cutter could also
be used. A line should be visible at the edge of the part, distinctly
showing the smooth section from the mould and the excess overlap.
Then grind down the inside edges at approximately 45 degrees. This
is to allow the two blade halves to fit just inside each other to make a
full blade. The two halves can be placed together for comparison to
check they fit well. This can be a long process and usually requires a
few attempts (additional grinding) until the two halves fit perfectly.
BLADE ROOT
A steel core is required at the blade root - where the blade is screwed
to the blade hub. The blade root should fit snugly in the root of the
blade and go far enough down the blade so that all the screws will bite
into the steel core.
-
8/2/2019 Wind Turbine Rotor
12/14
BLADE FINISHING
The blade halves have been stuck together and filled with foam, the
Last stage is the blade finishing. This involves filling any gaps on the
blade edges, adding a thin veil of fibre glass to the leading edge,sanding down any imperfections and painting.
Fill any gaps along the leading edge with good quality filler, such as
car body filler. Leave this to dry.
Sand the blade along the leading edge and ensure that the surface is
smooth. Add a narrow strip of CSM fibreglass to the leading edge.
Two layers should be applied. This is to help hold together the twoblade halves and also to add an additional layer to help protect the
leading edge.
Sand the blade to ensure that all the surfaces are smooth, especially
along the leading edge. The edge of the trailing edge should be thin,
approximately 1mm or less width. This will be the final sanding
process.
The final blades will look like this.
-
8/2/2019 Wind Turbine Rotor
13/14
CONCLUSION
Thus a wind turbine blade was successfully designed and fabricated,
for the given power and other requirements. The blade is designed to
ultimate perfection considering the loads and stresses acting on it.
The profile chosen for the blade was also analysed for its
aerodynamic properties and considered as best for the implementation
in the wind turbine.
ABSTRACT
-
8/2/2019 Wind Turbine Rotor
14/14
Roof Top Green Energy Generator is an emerging technology in the
wind energy conversion system.
With the immense encouragement from our college Management and
innovative guidance from our HOD and staff members, the focus is
given on Alternative Energy Resources [AER] such as the Solar
energy , wind energy, Biomass energy and the development of Roof
Top Green Energy Generator initiated and the dream come true, that
our college will have its own power generator.
Focus is given to Horizontal Axis Wind Turbines [HWAT] , the most
common and efficient type of wind energy conversion system.
This report deals with the designing and fabrication of a 1 KW wind
turbine blade.