ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Welded Joint Category: First of all welding engineer shall pre-describe the welded joint category to ensure proper identification for Joint Efficiency which is a part of joint configuration, Position, Thickness. As these parameters lately used as prescribed the tables shown below for Determination of % of Radiographic test requirements and / or Hydro static test requirements as per material specification.
Joint Efficiency:
As shown table after determination of the joint category it will be easy to determine the joint eff. Which used lately.
Prepared By: Mohammed AbdulfattahPage 1
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Prepared By: Mohammed AbdulfattahPage 2
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Heat Treatment Operation: A care must be taken for heat treatment process as per Div.1 requirements for determining the Heat treatment requirements and /or exemption the following should be taken into considerations: Holding temp., Material THK., Material Specification and hydro-static test interference finally the MAWP Limitation.
Prepared By: Mohammed AbdulfattahPage 3
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Prepared By: Mohammed AbdulfattahPage 4
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
If deviations at soaking temp. occurred during general processing from recommended min. temp requirements shown below table shall be used for Gr.1,2,3 P1. For ensuring min. stress relief requirement.
Prepared By: Mohammed AbdulfattahPage 5
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
General Testing Requirements and fabrication hints:
UT RT Interference
Welder I.D & Traceability
Finalizing Circumferential / Longitudinal welds
Prepared By: Mohammed AbdulfattahPage 6
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Weld Metal Build Up
Prepared By: Mohammed AbdulfattahPage 7
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
RT & UT Exemption
Welding Butt joints of Unequal Thickness within transition ration 1:3
Prepared By: Mohammed AbdulfattahPage 8
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Welding For Unequal Thickness:
Prepared By: Mohammed AbdulfattahPage 9
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Inspection During Fabrication:
Prepared By: Mohammed AbdulfattahPage 10
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
NON DESTRUCTIVE EXAMINATION ACCEPTANCE CRITERIA
PENETRANT TESTING
Prepared By: Mohammed AbdulfattahPage 11
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
NON DESTRUCTIVE EXAMINATION ACCEPTANCE CRITERIA
MAGNETIC TESTING
Prepared By: Mohammed AbdulfattahPage 12
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
NON DESTRUCTIVE EXAMINATION ACCEPTANCE CRITERIA
ULTRASONIC TESTING
Amp
20%
Prepared By: Mohammed AbdulfattahPage 13
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
NON DESTRUCTIVE EXAMINATION ACCEPTANCE CRITERIA
RADIOGRAPHIC TESTING
FOR INDICATION THK LESS THAN 25 MM
Prepared By: Mohammed AbdulfattahPage 14
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Prepared By: Mohammed AbdulfattahPage 15
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Prepared By: Mohammed AbdulfattahPage 16
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Prepared By: Mohammed AbdulfattahPage 17
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Prepared By: Mohammed AbdulfattahPage 18
ASME AUTHORITYTesting & Fabrication Tips ASME VIII DIV.1
Prepared By: Mohammed AbdulfattahPage 19