Product Brochure UPS 240 HD Heavy Duty Ceramic Carbide Unique Polymer Systems LTD – [email protected] - +44(0)1531 636300 UPS 240 HD Heavy Duty Ceramic Carbide Is a two component solvent free epoxy coating metal repair compound incorporating ceramic beads. The product has been designed for use in harsh operating environments subject to heavy wear, abrasion and impact. The material can be used for repairs and resurfacing of equipment such as chutes, hoppers, pipe bends, pump casings and other process equipment in contact with aggregates and slurries. Unique Properties Mechanical Properties Two component solvent free epoxy Adhesion Tensile Shear Adhesion (ASTM D1002) 13.79Mpa (2000psi) 3:1 mixing ratio by volume Compressive Strength Tested to ASTM D695 103.5Mpa (15000psi) Useable life 60 minutes (20°C) Abrasion Resistance CS17 Wheel (ASTM D4060) 11mgm (0.006ml) loss per 1000 cycles – 1kg load Initial Set 3 hours (20°C) Flexural Strength Tested to ASTM D790 41.5Mpa (6000psi) Hard Dry for Machining 8 hours (20°C) Maximum Operating Temperatures Dry Heat Wet Heat 120°C (248°F) 70°C (158°F) (Post cured) Hardness (Rockwell R) 100 Coal Fire Power Station Feed Pipes Resurfaced With UPS 240 HD Dredger Pumps Resurfaced With UPS 240 HD
Transcript of UPS 240 HD Heavy Duty Ceramic Carbide - Unique … Brochure UPS 240 HD Heavy Duty Ceramic Carbide...
Product Brochure UPS 240 HD Heavy Duty Ceramic Carbide
Unique Polymer Systems LTD – [email protected] - +44(0)1531 636300
UPS 240 HD Heavy Duty Ceramic Carbide Is a two component solvent free epoxy coating metal repair compound incorporating ceramic beads. The product has been designed for use in harsh operating environments subject to heavy wear, abrasion and impact. The material can be used for repairs and resurfacing of equipment such as chutes, hoppers, pipe bends, pump casings and other process equipment in contact with aggregates and slurries. Unique Properties Mechanical Properties Two component solvent free epoxy
Adhesion Tensile Shear Adhesion (ASTM D1002)
13.79Mpa (2000psi)
3:1 mixing ratio by volume Compressive Strength Tested to ASTM D695
103.5Mpa (15000psi)
Useable life 60 minutes (20°C) Abrasion Resistance CS17 Wheel (ASTM D4060)
11mgm (0.006ml) loss per 1000 cycles – 1kg load
Initial Set 3 hours (20°C) Flexural Strength Tested to ASTM D790
41.5Mpa (6000psi)
Hard Dry for Machining 8 hours (20°C)
Maximum Operating Temperatures Dry Heat Wet Heat
120°C (248°F) 70°C (158°F) (Post cured)
Hardness (Rockwell R) 100
Coal Fire Power Station Feed Pipes Resurfaced With UPS 240 HD
Dredger Pumps Resurfaced With UPS 240 HD