ToughMet ® 3 The Readily Available Alloy for Demanding Service ToughMet ® provides high strength, corrosion resistance, lubricity and wear resistance under severe loading conditions. ToughMet ® has a highly uniform composition in all product forms and is available in a wide range of sizes and shapes. Design flexibility offered by these attributes, combined with ToughMet’s excellent machinability, delivers the best total cost solution for high wear and severe service components. ToughMet ® is Materion Brush Performance Alloys’ solution to your severe service materials problems. By applying our proprietary EquaCast ® process, tailored alloying addition and spinodal hardening technology, we have engineered ToughMet ® to provide attributes beyond those typically found in a high strength copper alloy.
Transcript of ToughMet 3 The Readily Available Alloy for Demanding ServiceNACE MR0175/ISO 15156, ASTM B865, DIN...
-
ToughMet® 3The Readily Available Alloy for Demanding Service
ToughMet® provides high strength, corrosion resistance, lubricity and wear resistance under severe loading conditions. ToughMet® has a highly uniform composition in all product forms and is available in a wide range of sizes and shapes. Design flexibility offered by these attributes, combined with ToughMet’s excellent machinability, delivers the best total cost solution for high wear and severe service components.
ToughMet® is Materion Brush Performance Alloys’ solution to your severe service materials problems. By applying our proprietary EquaCast® process, tailored alloying addition and spinodal hardening technology, we have engineered ToughMet® to provide attributes beyond those typically found in a high strength copper alloy.
-
BRUSH PERFORMANCE ALLOYS6070 Parkland BoulevardMayfield Heights, OH 44124 USAp 800.375.4205 +1.216.486.4200www.materion.com/brushalloys
MATERION CORPORATION Materion (NYSE: MTRN) is a global advanced materials company dedicated to providing solutions that enable our customers’ technologies and drive their growth. Our products include precious and non-precious specialty metals, precision optical filters, inorganic chemicals and powders, specialty coatings, specialty-engineered beryllium alloys, beryllium and beryllium composites, and engineered clad and plated metal systems. www.materion.com
0 50 100 150 200 250 300
Ni-‐alloy
Stainless
Alloy Steel
Cu-‐Be 25
ToughMet
Machinability Index (FC Steel=100)
Make this in parens under the chart or on the y axis
MATERION BRUSH PERFORMANCE ALLOYs is the world’s leading supplier of high-performance alloys, providing high-strength, high-conductivity copper and nick-el beryllium products, and non-beryllium-containing specialty alloy products. With unparalleled technical expertise and global service, we are your first choice for the most demanding applications.
CT0010 3.12
Alloy (UNS) Temper Applicable Standards & Specifications
Ultimate Tensile
Strength (ksi)
Yield Strength
(ksi)
Tensile Elongation
(%)
Hardness(HV)
Maximum Hardness by
NACE *
ToughMet® 3 (C72900)
CX 105 NACE MR0175/ISO 15156, ASTM B505 105 + 90+ 3 + HRC 27 No Restriction
ToughMet® 3 (C72900)
AT 90NACE MR0175/ISO 15156, MIL-STD-167,
ASTM B249, ASTM B251110 + 90 + 12 + HBN 260 No Restriction
ToughMet® 3 (C72900)
AT 110NACE MR0175/ISO 15156, AMS 4596, BMS 7-373, MIL-S-
901D, ASTM B249, ASTM B251125 + 110 + 8 + HRC 30 No Restriction
ToughMet® 3 (C72900)
TS 120U (Rod)
NACE MR0175/ISO 15156, ASTM B249 120 + 110 + 15 + HRC 23 No Restriction
ToughMet® 3 (C72900)
TS 150(Tube)
NACE MR0175/ISO 15156 ASTM B251 158 + 150 + 5+ HRC 36 No Restriction
ToughMet® 3 (C72900)
TS 160UNACE MR0175/ISO 15156, AMS 4597,
ASTM B249, ASTM B25160 + 150 + 3 + HRC 36 No Restriction
6AL-4V Titanium (R56400)
Annealed NACE MR0175/ISO 15156, AMS 4928 130 + 120 + 10 + HRC 36 HRC 36
INCONEL® alloy 625 (N06625)
AnnealedNACE MR0175/ISO 15156, ASTM B446, AMS 5666, AMS
5581, ASTM B444, ASTM B829120 + 60 + 30 + HRB 95 HRC 35
INCONEL® alloy 718 (N07718)
Annealed & Aged
NACE MR0175/ISO 15156, AMS 5589, AMS 5663, ASTM B637
170 (nom.) 145 (nom.) 15 (nom.) HRC 35 HRC 35
Nitronic® 50 (S20910)
High Strength
NACE MR0175/ISO 15156, AMS 5681, AMS 5764, ASTM A 182, ASTM A 193, ASTM A 194, ASTM A 240, ASTM A 249, ASTM A 269, ASTM A 312, ASTM A 3134, ASTM A
358, ASTM A 403, ASTM A 412, ASTM A 479
150 126 29 HRC 33 No Restriction
MONEL® alloy K-500 (N05500)
Annealed & Aged
NACE MR0175/ISO 15156, ASTM B865, DIN 17751, DIN 17752, QQN 286, AMS 4676, ISO 9723, MIL-N-24549
130 + 85 + 20 + HRC 30 HRC 35
MONEL® alloy 400 (N04400)
Hard DrawnNACE MR0175/ISO 15156, ASTM B164, ASTM B165, DIN
17551, DIN 17752, QQ-N-281, AMS 4574, AMS 4675, MIL-N-24106
110 + 90 + 3 + HRC 20 HRC 40
Aluminum Nickel Bronze
(C63000)Hard Drawn AMS 4640, ASTM B124, ASTM B150 110 60 20 HRB 100 No Restriction
Manganese Bronze (C67500)
Hard Drawn ASTM B138, ASTM B124 80 + 56 + 8 + B 80 No Restriction
ToughMet® is a registered trademark of Materion Brush Inc. MONEL® and INCONEL® are registered trademarks of Special Metals Corporation, Nitronic® is a registered trademark of AK Steel Corp.* Maximum hardness as suggested in NACE MR0175/ISO 15156 to safeguard against sulfide stress corrosion cracking. Please refer to this standard for details.
Advantages of ToughMet® 3n High Strengthn Anti Gallingn Corrosion, erosion and wear resistancen Non-magneticn Non-sparkingn Low coefficient of frictionn Excellent machinability
Machinability Index (FC Steel = 100)
ASTM E618 Machinability Index of ToughMet® Suggests Part Production Rates 5X versus Other High-Strength Corrosion Resistant Materials