Temperature Reading in API 510 Exam Alterr
Click here to load reader
description
Transcript of Temperature Reading in API 510 Exam Alterr
TEMPERATURE READING IN API 510 EXAMS
1. Corrosion Engineer Shall Be Consulting When Developing The Inspection Plan Of Vessels Operating At Elevated Temp
Above 750◦ F(400◦ C) (General)
2. Cui Externally Insulated Vessel Intermittent Service Or Operate Between
10◦ F to 350◦ F(-12◦ C to175◦ C) – For Carbon And Low Alloy Steel
140◦ F to 400◦ F (60◦ C to 185◦ C) – Austenic Stainless Steel And
280◦ F to 350◦ F (138◦ C to 185◦ C)- Duplix Stainless Steel
3. Ut(Thick )
Above 150◦ F (65◦ C) Not Use
4. Minimize The Brittle Fracture Keep The Metal Temp
30◦ F (17◦ C)Mdmt – Above 2”Thick (API 510 -5.8.7.2)
5. Minimize The Brittle Fracture Keep The Metal Temp
10◦ F (6◦ C)Mdmt – Below 2”Thick (API 510 -5.8.7.2)
6. In Alternative Of Pwht – Alteration Or Repair Preheat Temp Min
300◦ F (150◦ C) (API 510 -8.1.7.4.2)
7. In Alternative Of Pwht – Alteration Or Repair Interpass Temp Max
600◦ F (315◦ C) (API 510 -8.1.7.4.3.2)
8. Operating Temp Of Vessel In Cui
-4◦ C To 120◦ C (Api 572)
9. Local Pwht Substituted For 360◦ banding-Local Repair
Pre Heat 300◦ F (150◦ C) Are Higher (API 510 -8.1.7.4.2)
10. Shielding Gas Shall Exhibit A Dew Point No Higher Than
-60◦ F (-50◦ C) (API 510 – 8.1.7.4.3.3)
11. Design Temp Of Pressure Vessel Not Exceeded
210◦ F (99◦ C) (Sec VIII- U1)
12. Caustic Stress Corrosion Cracking (Caustic Embrittlment) – Crack Or High Stress Occur When Temp Over 400◦ F (204◦ C)(API
571)
13. High Temperature Sulfide Corrosion
Over 400◦ F (204◦ C) (API 571 – Table of content)
14. Temper Embrittlement (Structural Change)
Temp Exceed 650◦ F To 1100◦ F (345◦ C – 595◦ C) (API 510 – 3.1.69)
15. Thermal Fatigue
Cyclic Stress Caused By Variation In Temp Exceed 200◦ F (93◦ C) (API 571 – 4.2.9)
16. Cooling Water Corrosion Process Side Temp Is Above 140◦ F (60◦ C) & Brackish And Salt Water Outlet Temp Above 115◦ F
(46◦ C) (API 571 – 4.3.4)
17. Sulfidation
Metal Temp Above 500◦ F (260◦ C) (API 571 – 4.4.2)
18. CL Stress Corrosion Cracking (CLSCC)
Metal Temp Above 140◦ F (60◦ C) (API 571 – 4.5)
19. Atmospheric Corrosion
250◦ F (121◦ C) (API 571 – 4.3.2)
20. In Temper Bead Welding The Heat Consideration Is
500 ◦ F +/- 50◦ F (260 ◦ C +/- 30◦ C) (API 510 – 8.1.7.4.3.3)
21. Lamination Found heat Approximately 200◦ F to open (API 572)
22. Hydro Testing Solid Or Clad Austenitic Stainless Steel Water Temp Upto 120◦ F (50◦ C)