A simple chemical treatment for easy dispersion of carbon nanotubes in epoxy
matrix for improving mechanical properties
Anil Suri1,*, Santosh Kumar Yadav2, and Aravind Dasari1
1 School of Materials Science and Engineering, Nanyang Technological University, Block N4.1 Nanyang Avenue,
Singapore 639798.2 Chemical and Biological Engineering Department, Drexel University, 3141 Chestnut Street, Philadelphia PA
19104, USA.
E-mail: [email protected]
Fax: +65-6790 9081
SUPPLEMENTARY INFORMATION
Raman spectroscopy
0 500 1000 1500 2000 2500 3000 3500
Shift (cm-1)
Inte
nsity
(a.u
.)
Figure S1 Raman spectra of as-received HiPco SWNTs (blue line) and SWNTs after chemical
treatment with sodium hydroxide / ethanol solution (red line). The Raman spectra were recorded
at an excitation wavelength of 633 nm.
Transmission electron microscopy
Figure S2 Transmission electron micrographs (JEOL-JEM 3010) of the P2 SWNTs subjected to chemical treatment by NaOH / ethanol.
Tensile testing
Figure S3 Average stress-strain curves for neat epoxy and epoxy-treated SWNT composites.