Resins for coatings / Epoxyester - Synthopol
Transcript of Resins for coatings / Epoxyester - Synthopol
Page 1 of 27
Resins for coatings / Epoxyester
Product Fields of use nvc (%) solv. AV Iod-col. Flowtime in s.
SYNTHALAT ER 402 air-drying primer and anti-rust primer withamine resins for oven-drying undercoats
60 X < 3 (nfA) < 10 (50% X) 150 - 220 (50% X)
SYNTHALAT ETH 419 zinc-rich paints, air- and oven-drying anti-rust and adhesive primer, paints fortropical climates
50 X max. 5 (nfA) max. 20 (40% X) 75 - 85 (40% X)
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 2 of 27
Resins for coatings / Acrylic resins
Product
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 3 of 27
Resins for coatings / Acrylic resins /
Product Fields of use nvc (%) solv. AV Flowtime in s. Visc. mPas OH value OH cont. (%)
LIOPTAL A 424 stoved enamels, highly reactive, from98¡C
50 S 150/But. (2:1) 30 - 40 200 - 300 (Lffm.)
LIOPTAL A 453-60 stoved enamels with good weatherresistance and colour stability
60 X/But. (3:1) 9 - 13 (Lffm.) 50 - 80 (40%X)
LIOPTAL A 453-65 stoved enamels with good weatherresistance and colour stability
65 X/But. (3:1) 9 - 13 (Lffm.) 50 - 80 (40% X)
LIOPTAL A 470 stoved enamels with good weatherresistance and colour stability
70 SSA/But (20:10) 8 - 12 1.000 - 1.500
LIOPTAL A 471 use and properties as LIOPTAL A 470with higher elasticity and lower VOCs
69 - 71 SSA / But. 8 - 12 1.100 - 1.500
SYNTHALAN LS60-037 T
For masonry protection paints (for waterrepellence)
50 TB K30 5.500 - 8.000
SYNTHALAN LS64-129T
for masonry protection (for waterrepellence)
50 X/Buac (3:2) 3.000 - 5.000
SYNTHALAN LS 768 Acrylic resin specifically as a paste binderparticularly for use with hard to dispersepigments
60 Buac 5.500 - 7.000 46 - 53 1,5
SYNTHALAT A 045 2-pack primers and top coats, highlyelastic, weather-resistant and veryadhesive, even on difficult substrates
60 X/Buac (9:1) 70-100 (50% X) 45 - 55 1,4
SYNTHALAT A 045 2-pack primers and top coats, highlyelastic, weather-resistant and veryadhesive, even on difficult substrates
60 SSA 70-100 (50% X) 45 - 55 1,4
SYNTHALAT A 045 2-pack primers and top coats, highlyelastic, weather-resistant and veryadhesive, even on difficult substrates
60 Buac 100-150 (50% X) 40 - 50 1,4
SYNTHALAT A 055 primarily as a component for givingelasticity to SYNTHALAT A 150, A 151and A 191, highly elastic, weather-
60 X/Buac (3:1) 200-300 (50% X) 55 - 65 1,7
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 4 of 27
Product Fields of use nvc (%) solv. AV Flowtime in s. Visc. mPas OH value OH cont. (%)
resistant with good universal adhesion
SYNTHALAT A 060 2-pack industrial coatings with highelasticity, adhesion and weatherresistance
60 SSA 95-115 (50% SSA) 50 - 65 1,8
SYNTHALAT A 065 2-pack primers and top coats on wood,steel and plastics, high surface hardness,good chemical resistance, fast drying
50 X/Buac (9:1) 250-300 (Lffm.) 60 - 70 2,0
SYNTHALAT A 065 2-pack primers and top coats on wood,steel and plastics, high surface hardness,good chemical resistance, fast drying
50 SSA 200-350 (Lffm.) 60 - 70 2,0
SYNTHALAT A 065 2-pack primers and top coats on wood,steel and plastics, high surface hardness,good chemical resistance, fast drying
50 Buac 220-300 (Lffm.) 60 - 70 2,0
SYNTHALAT A 077 use and properties as SYNTHALAT A085, suitable for railways
60 SSA 50-60 (50% SSA) 80 - 100 2,6
SYNTHALAT A 077 use and properties as SYNTHALAT A085, suitable for railways
60 X 2.600 - 3.600 80 - 100 2,6
SYNTHALAT A 078 2-pack coatings which are air- and oven-drying in combination with aliphaticpolyisocyanates for industrial coatingsoffering good mechanical properties plusresistance to chemicals and weather
60 SSA 2.000 - 2.500 80 - 95 2,6
SYNTHALAT A 078 HV 2-pack coatings which are air- and oven-drying in combination with aliphaticpolyisocyanates for industrial coatingsoffering good mechanical properties plusresistance to chemicals and weather
65 SSA 10.000 - 15.000 80-95 2,6
SYNTHALAT A 085 2-pack primers, top coats and one-coatpaints. Elastic, good adhesion even todifficult substrates
60 X 100-160 (50% X) 85 - 105 2,6
SYNTHALAT A 085 2-pack primers, top coats and one-coatpaints. Elastic, good adhesion even todifficult substrates
60 Buac 100-130 (50% X) 85 - 105 2,6
SYNTHALAT A 085 2-pack primers, top coats and one-coat 65 SSA 70 - 90 (50% X) 85 - 105 2,6
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 5 of 27
Product Fields of use nvc (%) solv. AV Flowtime in s. Visc. mPas OH value OH cont. (%)
paints. Elastic, good adhesion even todifficult substrates
SYNTHALAT A 090 2-pack coatings in combination withaliphatic polyisocyanate additives withgood adhesion to plastics, especially ABScopolymer
60 X/Buac (1:1) 600 - 900 80 - 100 2,7
SYNTHALAT A 120 E 2-pack coatings which are air- and oven-drying in combination withpolyisocyanates, offering high abrasionresistance and high resistance to weatherand chemicals
61 X/SSA/Buac (2:1:1) 2.500 - 3.500 125 - 130 3,8 - 3,9
SYNTHALAT A 135 2-pack industrial coatings for metal andplastics, air- and oven-drying, goodresistance to chemicals and weather
70 Buac 70-100 (50% Buac) 125 - 140 4,0
SYNTHALAT A 150 2-pack top coats for high-capacityvehicles, cars etc. with high abrasionresistance, build, resistance to chemicalsand water
60 X/SSA/Buac (2:1:1) 140-180 (50% X) 130 -150 4,5
SYNTHALAT A 150 2-pack top coats for high-capacityvehicles, cars etc. with high abrasionresistance, build, resistance to chemicalsand water
60 Buac 150-180 (50% Buac) 130 -150 4,5
SYNTHALAT A 150 S use and properties as SYNTHALAT A 150but with faster drying
60 X/SSA/Buac (2:1:1) 160-220 (50% X) 130 - 150 4,5
SYNTHALAT A150-XMPA
2-pack top coats for high-capacityvehicles, cars etc. with high abrasionresistance, build, resistance to chemicalsand water
59 - 61 X/MPA (2:1) 2500 - 4500 130 - 150 4,5
SYNTHALAT A 151 2-pack top coats for industrial areas;properties include good abrasionresistance, good build and pigmentuptake, resistance to chemicals andweather
60 X/SSA/Buac (1:1:1) 300-450 (50% X) 130 - 150 4,5
SYNTHALAT A 1613 2-pack coatings for furniture with goodgrain enhancement of dark woods
45 Buac 2.000 - 4.000 40 - 65 1,5
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 6 of 27
Product Fields of use nvc (%) solv. AV Flowtime in s. Visc. mPas OH value OH cont. (%)
SYNTHALAT A 1633 2-pack furniture coatings for industrialapplications, super-fast drying, earlystacking resistance
50 SSA/EPA (3:1) 2,8 - 3,4 60 - 75 2,0
SYNTHALAT A 1633 2-pack furniture coatings for industrialapplications, super-fast drying, earlystacking resistance
50 X/Buac (1:1) 160-200 60 - 75 2,0
SYNTHALAT A 1633 2-pack furniture coatings for industrialapplications, super-fast drying, earlystacking resistance
50 Buac 100-140 60 - 75 2,0
SYNTHALAT A 1653 use and properties as SYNTHALAT A1633, but low-viscosity for high-solidswood varnishes, environmentally friendly
65 X/Buac (1:2) 90-120 (50% X/Buac) 50 - 75 2,0
SYNTHALAT A 190 2-pack top coats for areas which musthave a high resistance, very abrasion-restant, good build and resistance tochemicals and weather
60 SSA/Buac (1:1) 140-190 (50% Buac) 175 - 185 5,7
SYNTHALAT A 191 use and properties as SYNTHALAT A 190but with improved elasticity
60 SSA/Buac (1:1) 3.600 - 4.600 175 - 185 5,7
SYNTHALAT A 192 use and properties as SYNTHALAT A 191but with improved elasticity
60 EPA 200-250 (45% EPA) 180 - 200 5,7
SYNTHALAT A 333 sole binder, primarily for plastics 40 X/But (2:1) 30 - 35 90 - 150 (Lffm.)
SYNTHALAT A 397 industrial coatings, fast drying, resistanceto weather, air drying and forced drying
60 TB K30 < 5 80 - 120 (45% TB K30)
SYNTHALAT A 526 HS-B
for low-solvent, high-solids road markingpaints
60 Buac/A (1:1) 10 - 15 430 - 570
SYNTHALAT A 587 cement plaster setting agent and infillprimers with hard paint films
60 TB K 30 < 5 40 - 70 (40% TB K30)
SYNTHALAT A 597 sole binder for primers on problematicsubstrates such as zinc
60 X 8 - 12 2.500 - 3.000
SYNTHALAT A 597 sole binder for primers on problematicsubstrates such as zinc
60 Buac 9 - 12 (Lffm.) 3.400 - 4.000
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 7 of 27
Product Fields of use nvc (%) solv. AV Flowtime in s. Visc. mPas OH value OH cont. (%)
SYNTHALAT A-TS1400
2-pack coatings for furniture, extremelyfast drying
40 Buac 1.800 - 2.400 35- 45 1,2
SYNTHALAT A-TS1558
for aerosols, plastics and metals; goodresistance to petroleum and weather; fastdrying
50 Buac 27 - 37 7.000 - 10.000
SYNTHALAT A-TS1857
solvent-based version of Synthalat A TS1558
50 SSA 27 - 37 20.000 - 26.000
SYNTHALAT A-TS2104
Sole binder for primers on problematicsubstrats such as zinc
60 Buac 8 - 12 7.000 - 11.000
SYNTHALAT A-TS3277
use and properties as SYNTHALAT A077, improved resistance to weather
60 SSA 7.000 - 10.000 80 - 100 2,6
SYNTHALAT A-TS3392
highly elastic high-solids polyacrylic resinfor sealing compounds in the architecturalsector
75 Eac/Buac < 5 12.000 - 18.000
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 8 of 27
Resins for coatings / Acrylic resins / high solid
Product Fields of use nvc (%) solv. OH value OH cont.(%)
Visc.mPas
Flowtimein s.
VOC(g/L)
hardener ratio resin/hardener
Base AV Gard-col. Sustainable Parts(%)
Hazen-col.
SYNTHALAT A 086 HS 2-pack coatings with highabrison-,chemical- and weather-resistancefor industrial coatings.
75 Buac 80 - 100 2,6 14.000 -22.000
SYNTHALAT A 125 HS in association with polyisocyanates, air-and oven-drying 2-pack paints with highmechanical resistance, good resistance tochemicals and weather, high-solidsindustrial coatings
70 SSA/Buac (1:2)
120 -140
3,9 200 -240(60%Buac)
SYNTHALAT A 141 HS 2-pack high-solids top coats for examplefor cars, large-capacity vehicles and theindustrial sector; properties asSYNTHALAT A 125 HS
70 SSA/Buac (2:1)
130 -140
4,2 800 -1.400(60%Buac)
SYNTHALAT A 147 HS 2-pack high-solids top coats for examplefor cars, large-capacity vehicles and theindustrial sector; use and properties asSYNTHALAT A 125 HS with lower VOCs
70 Buac/BGA (1:1)
140 -160
4,5 1.500 -2.500
SYNTHALAT A 149 HS 2-pack high-solid top coats for i.e. cars,vehicles, and industrial coatings
77(Lffm) Buac 140 -160(Lffm)
4,5 5.000 10.000(Lffm)
< 420
SYNTHALAT A 156 HS in association with polyisocyanates air-and oven-drying high-solids 2-packcoatings, suitable for automotive andindustrial coatings; HS variant of SA 150
70 SSA/EPA/Buac/BGA(2:2:3,5:1)
135 -150
4,5 60 - 80(60%Buac)
SYNTHALAT A 200 2-pack primer extenders, outstandingextender properties, good adhesion tosteel, aluminium, zinc and fast drying withgood condensed moisture and salt spraytest results
72 X/ SSA/Butoxyl(2:2:1)
200 -250
6,0 12.000 -17.000
SYNTHALAT A-HD8199
2-pack high-solids top coats for furniturewith high initial gloss
70 SSA/Buac (2:1)
105 -115
3,3 8.000 -12.000
SYNTHALAT A-TH 2-Pack high-solid clear- and pigmented 77 Buac/Sol 140 - 4,5 10.000 - < 420
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 9 of 27
Product Fields of use nvc (%) solv. OH value OH cont.(%)
Visc.mPas
Flowtimein s.
VOC(g/L)
hardener ratio resin/hardener
Base AV Gard-col. Sustainable Parts(%)
Hazen-col.
1141 top coats for metals and plastics with highmechanical properties, quick physicallydrying, high gloss and body, excellentweather- and chemical resistance
ventnaphtha(13:10)
160 16.000 (21 sec)
SYNTHALAT A-TH1561
Quick drying 2 pack-HS polyurethanecoatings with high gloss and wetting,especially for furniture paints.
65 Buac 50 - 75 2 800 -1600
357 Polyisocyanate
1 : 1 Acrylat
6 - 10 max. 1 50
SYNTHALAT A-TH2712
Air- and forced-drying 2 pack coatingswith high abrasion-, Chemical- undWeather-resistance for automotive andgeneral industrial coatings.
70 MPA/Buac
140 -160
4,5 3000 -7000
310 1 : 1 Acrylat
8 - 12 40 < 100
SYNTHALAT A-TS3737
2-pack coatings with high abrison-,chemical- and weather-resistance forindustrial coatings.
70 Buac 90 - 110 3 1.000 -2.000
SYNTHALAT A-TS4399
In combination with aliphaticpolyisocyanates for 2 pack soft feelingcoatings.
75 Xylol 120 -130
3,8 3.500 -4.500
< 420
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 10 of 27
Resins for coatings / Acrylic resins / water-thinnable
Product Fields of use nvc (%) solv. OH value Visc. mPas pH value OH cont. (%)
SYNTHALAT A-JB 772 for waterborne1pack- und 2pack-, clear-and top-coats with good chemicalresistance and exellent ovendryingproperties
40 H2O/But(54:6) ca. 140 200 - 1.500 7,5 - 9,0
SYNTHALAT WA 146 contains hydroxyl groups, for generalindustrial and automotive top coats andextenders, with fast drying and goodresistance to weather and chemicals
42 H2O / DMEA 140 - 160 50 - 2.000 7,0 - 9,0 4,4
SYNTHALAT WA TH2188
2 pack coatings and filler, stovingenamels, onelayer coat on differentsubstrates
45 H2O/DMEA/PnB 85 50 - 2000 7,0 - 9,0 2,6
SYNTHALAT WA TH2189
2 pack coatings and filler, stovingenamels, onelayer coat on differentsubstrates
45 H2O/DMEA 110 7,0 - 9,0 3,3
SYNTHALAT WA TH2202
2 pack coatings and filler, with highresistance
45 H2O/DMEA 200 2000-6000 7,0 - 9,0 6
SYNTHALAT WA TH2242
2 pack coatings and filler, with very highresistance
42 H2O/DMEA 220 7,0 - 9,0 6,7
SYNTHALAT WA TH2358
2 pack coatings and filler, for flexiblesubstrates
45 H2O/DMEA 135 7,0 - 9,0 4,1
SYNTHALAT WA TH2569
2 pack coatings and filler, with goodresistance, gloss and body.
42 H2O/DMEA/PnB 150 7,0 - 9,0 4,5
SYNTHALAT WA TH2595
2 pack coatings and filler, stovingenamels, onelayer coat on differentsubstrates
45 H2O/DMEA/PnB 75 7,0 - 9,0 2,3
SYNTHALAT WA TH2598
2 pack coatings and filler, stovingenamels, onelayer coat on differentsubstrates
45 H2O/DMEA/PnB 65 7,0 - 9,0 2
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 11 of 27
Resins for coatings / Alkyd resins
Product Fields of use nvc (%) solv. Oil cont.(%)
Oil type AV Iod-col. Flowtimein s.
Sustainable Parts(%)
Gard-col. Visc.mPas
pH value solv. % Base MFFT(°C)
LIOPTAL 541 air- and oven-drying primers, surfacers,industrial coatings
60 X 38 talloil/woodoil 20%mod.resins
< 25 < 25(50% X)
140 - 200(50% X)
67
LIOPTAL 836 air-drying primers and industrial paints,good dipping bath stability
60 X 27 dryingfattyacids
< 20 < 10(50% X)
100 - 150(50% X)
27
LIOPTAL B 49 machinery, automotive, radiator paints,80¡C refinish paints, completely TB-soluble
55 TBK30/X(6:1)
49 veg. fattyacids lowinlinolenicacid
< 12 < 5 (40%TB K30)
40 - 55(40% TBK30)
41
LIOPTAL ES 43 stoved enamels, industrial use, SH woodvarnishes
70 Buac 43 mix ofnon-dryinganddryingfattyacids
< 10 < 5 (50%Buac)
25 - 30sec.(50%Buac)
59
LIOPTAL TH 406 primers, surfacers with reduced aromaticscontent, thinnable in petroleum
55 TB K21 talloil/woodoil 20%mod.resins
< 15(nfA)
90 - 130(40% TBK21)
56 max. 7(40% TBK21)
SYNTHALAT AEM 700TC
used as co-binder and sole binder forwood-preserving glazes for interior andexterior, with good penetration
55 H2O 70 tall oil/cottonseedoil
70 30 - 200 7,0 - 9,0
SYNTHALAT D 272 printing inks, gloss inks, heatset inks,quickset inks
100 74 linseedoil/soyabean oil
< 12 < 10(50% TBK30)
69 15.000 -20.000
SYNTHALAT E 405 NC wood varnishes with especially goodbuild, good sandability and release ofsolvelnts, SH wood varnishes
75 Buac 41 peanutfatty acid
< 10 < 5(Lffm.)
35 - 50(60%Buac)
65
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 12 of 27
Product Fields of use nvc (%) solv. Oil cont.(%)
Oil type AV Iod-col. Flowtimein s.
Sustainable Parts(%)
Gard-col. Visc.mPas
pH value solv. % Base MFFT(°C)
SYNTHALAT F 330 air-drying, overpaintable industrial andsynthetic resin coatings, universal primerswith good adhesion to steel, wood,aluminium and zinc
60 X 34 dryingfattyacids
< 20 < 20(50% X)
145 - 170(50%X)
30
SYNTHALAT F 334 universal primers and one-coat finisheswith good adhesion to steel, wood,aluminium and zinc and no need forspecial labelling
60 SSD40/Solv. PM(1:1)
34 dryingfattyacids
< 20 < 15(50% X)
110 - 150(50%SSD40/PM, 1:1)
30
SYNTHALAT F 477 fast-drying synthetic resin paints, withgood gloss retention, industrial paints, low-yellowing radiator paints
55 TBK30/X(3:1)
50 dryingfattyacids
< 10 < 7 (40%TB K30)
70 - 95(40% TBK30)
44
SYNTHALAT F 477 fast-drying synthetic resin paints, withgood gloss retention, industrial paints, low-yellowing radiator paints
55 SS D40 50 dryingfattyacids
< 12 <10(Lffm.)
90 -130(55% SSD40)
44
SYNTHALAT HL 30 - X rust protection primers, fast-drying, goodadhesion to light metal
60 X 38 wood oil,linseedoil 20%mod.resins
< 25 < 25(50% X)
110 - 170(50% X)
67
SYNTHALAT HS 80 high-solid decorative paints above 85%solids content, optimum properties, usedfor paints with "blue angel" mark
100 80 specialmodifiedfattyacids
< 15 < 15 (80% TBK30)
70 - 75(80% TBK30)
74
SYNTHALAT PL 754 Fast drying industrial and anti-corrosivelacquers for steel and metallic substrates(checked for DB TL 918 300 paper 93)
60 SSD60 ca. 60 <3 58 2,500 -8,000
SYNTHALAT PWK1227
For fast drying universal primers and air-drying one-coat enamels recoatable withstoving enamels and two componentacrylic lacquers. Suitable for matt or semi-gloss and also for high gloss coatings.Good adhesion on steel and on aluminiumor zinc after 7 days of through-drying
53 H2O 40 linseedoil/tall oil
28 30 - 200 6,0 - 8,0
SYNTHALAT PWK1542
Fast drying waterbased industrial lacquerswith good anti-corrosion properties using
41 wässrig 33 specialdrying
32 50 - 500 7,0 - 9,0 < 0,3 Urethanalk
< 20
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 13 of 27
Product Fields of use nvc (%) solv. Oil cont.(%)
Oil type AV Iod-col. Flowtimein s.
Sustainable Parts(%)
Gard-col. Visc.mPas
pH value solv. % Base MFFT(°C)
low amount of dryers fatty acid yd
SYNTHALAT PWL 819 Synthalat PWL 819 is recommended forpigmented interior or exterior air-dryinglacquers with faster drying behaviour andhigher pendulum hardness
55 H2O 65 dryingfattyacids
55 20 - 500 7,0 - 9,0
SYNTHALAT PWL 926 used as co-binder and sole binder forarchitectual paints with good glossretention
53 H2O 63 specialdryingfattyacids
60 20 - 300 7,0 - 9,0
SYNTHALAT PWM1394
High-grade decorative and architecturalpaints with particularly fast dryingcapacity, anti-corrosive paint.
55 H2O linolicpoor fattyacids
30 - 400 7,9 - 9,0
SYNTHALAT PWM 883 solventpoor instustrial coatings withreduced amount of siccatives VOC-conform decorative coataings incombination with medium oil alkydemulsions
45 specialdryingfatty acid
< 30 52 200 - 700 7 - 9 < 20
SYNTHALAT QL 1910 High quality decorative paint for internaland external application. High glossretention and little yellowing.
90 ShellD60
70 veg. fattyacids
< 10 < 10 66 4000 -7000
SYNTHALAT QL 2060 For High-Solid wood stains and as co-binder in decorative paints in order
100 N/A 78 veg. fattyacids
< 15 < 10 1500 -4000
SYNTHALAT SF 260 fast-drying primers and synthetic resinpaints
55 X 30 spec.dryingfattyacids (triglyceride)
< 15 < 10(50% X)
100 - 150(50% X)
26
SYNTHALAT SF 653 high-grade decorative and architecturalpaints with particularly fast drying,corrosion protection paints
60 TB K30(HV)
63 specialdryingfattyacids
< 10 < 10(50% TBK30)
130 - 150(50% TBK30), HV
60
SYNTHALAT SF 653 high-grade decorative and architecturalpaints with particularly fast drying,corrosion protection paints
60 TB K60 63 specialdryingfatty
< 10 < 10(50% TBK60)
100 - 130(50% TBK60)
60
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 14 of 27
Product Fields of use nvc (%) solv. Oil cont.(%)
Oil type AV Iod-col. Flowtimein s.
Sustainable Parts(%)
Gard-col. Visc.mPas
pH value solv. % Base MFFT(°C)
acids
SYNTHALAT SF 653 high-grade decorative and architecturalpaints with particularly fast drying,corrosion protection paints
70 TB K60 63 specialdryingfattyacids
< 10 < 10(50% TBK60)
160 - 180(50% TBK60)
60
SYNTHALAT SF 653 high-grade decorative and architecturalpaints with particularly fast drying,corrosion protection paints
60 SSD40 63 specialdryingfattyacids
< 10 < 10(50%SSD40)
100 - 130(50%SSD40)
60
SYNTHALAT SF 653 high-grade decorative and architecturalpaints with particularly fast drying,corrosion protection paints
60 SSD60 63 specialdryingfattyacids
< 10 < 10(50%SSD60)
100 - 130(50%SSD60)
60
SYNTHALAT SF 690 high-grade full-build decorative paints,very easily brushable, very low darkyellowing
75 TB K30 68 mix ofspecialdryingveg. fattyacids (triglyceride)
< 10 < 10(50% TBK30)
20 - 25(50% TBK30)
60
SYNTHALAT SF 690 high-grade full-build decorative paints,very easily brushable, very low darkyellowing
75 TB K60 68 mix ofspecialdryingveg. fattyacids (triglyceride)
< 10 < 10(50% TBK60)
28 - 32(50% TBK60)
60
SYNTHALAT SF 690 High grade decorative paints for indoorsand outdoors; very good brushability; verylittle dark yellowing.
75 SSD60 68 veg. fattyacids
< 10 60
SYNTHALAT SF 740HS
High quality decorative paint for internaland external application. Excellentbrushability and filling capacity.
90 SSD60 74 veg. fattyacids
< 10 66 3.500 -6.500
SYNTHALAT SR 46 high-quality, bloom-free top coats for theagricultural machinery sector
50 TBK30/X(41:9)
47 dryingfattyacids
< 10 < 5 (40%TB K30)
50 - 70(40% TBK30)
39
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 15 of 27
Product Fields of use nvc (%) solv. Oil cont.(%)
Oil type AV Iod-col. Flowtimein s.
Sustainable Parts(%)
Gard-col. Visc.mPas
pH value solv. % Base MFFT(°C)
SYNTHALAT TH 30 HS Air-drying and oven-drying primer coatingsfor industrial appication such asmachinery and steel constructions.
80 X < 20 < 20(50% X)
49 15.000 -22.000
SYNTHALAT TH 30 HS Air-drying and oven-drying primer coatingsfor industrial appication such asmachinery and steel constructions.
75 SSD25/Solv PM
< 20 49 2.000 -8.000
SYNTHALAT W 30 water-thinnable priming paints, goodhardness and elasticity
75 But./BG(2:1)
30 dryingfattyacids
37 - 40 < 3 (50%BG)
100 - 140(50%BG)
24
SYNTHALAT W 46 water-thinnable top coats, very goodresistance to water, top coats foragricultural machinery
40 BG/ Ammoniak/H2O (7:2,5:50,5)
46 dryingfattyacids
opak 38 1.000 -4.000
8,0 - 9,0(10% inH2O)
SYNTHALAT W 48 water-thinnable top coats, very goodresistance to water, low yellowing, topcoats for agricultural machinery
35 BG/ Ammoniak/H2O (8:0,5:56,5)
42 dryingfattyacids
opak 37 2.000 -5.000
7,5 - 9,0(10% inH2O)
SYNTHALAT ZM 1133 Decorative paints 65 SSD40 57 dryingfattyacids
< 15 51 4.000 -6.000
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 16 of 27
Resins for coatings / Dispersions
Product Fields of use nvc (%) Visc. mPas pH value MFFT (°C) Base SustainableParts (%)
solv. % solv. hardener ratioresin/hardener
LIOCRYL AM 432 concrete coating, tile adhesive 46 < 1.500 7,5 - 9,0 ca. 5
LIOCRYL AM 483 2-pack softfeeling and flexible substrates 50 20 - 500 6,5 - 8,5 < 3
LIOCRYL AM 903 facades, glazes, acrylic paints; APEO freeversion of Liocryl AM 900
45 20 - 500 7,0 - 8,5 < 5
LIOCRYL AM 907 wood/plastics coatings, high blockingresistance
42,5 < 300 6,5 - 8,0 < 5
LIOCRYL AM 912 facades, glazes, acrylic paints 50 100 - 300 7,5 - 8,5 ca. 17
LIOCRYL AM 920 wood and furniture coatings for one-packand two-pack applications
40 20 - 200 7,0 - 8,0 ca. 40
LIOCRYL AM 921 wood and furniture coatings for one-packand two-pack applications
40 20 - 500 6,5 - 8,5 42 - 45
LIOCRYL AM 923 wood and furniture coatings for one-packand two-pack applications
40 20 - 500 6,5 - 8,0 ca. 46
LIOCRYL AM 951 hard coatings with high blockingresistance and low solvent requirement
40 20 - 500 7,0 - 8,0 ca. 10
LIOCRYL AM 955 industrial coatings, very high blockingresistance
40 20 - 500 7,0 - 8,5 ca. 45
LIOCRYL AM 982 plastics coatings; polystyrene, audio,automotive
50 20 - 500 7,0 - 8,0 > 80
LIOCRYL AS 320 N interior and exterior paints, constructionadhesives
50 (Lffm.) 150 - 400 7,2 - 7,9 ca. 21
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 17 of 27
Product Fields of use nvc (%) Visc. mPas pH value MFFT (°C) Base SustainableParts (%)
solv. % solv. hardener ratioresin/hardener
LIOCRYL AS 603 Industrielacke für Holz/Kunststoffe/Metall 42 (Lffm.) 40 - 200 8,5 - 9,5 ca. 30
LIOCRYL AS 610 parquet varnishes, industrial paints forwood/plastics
42 (Lffm.) 40 - 200 6,5 - 7,5 ca. 50
LIOCRYL AS 615 primers and top coats for metal and wood 42 (Lffm.) 20 - 300 7,8 - 8,3 ca. 43
LIOCRYL AS 640 fast drying aqueous 2-pack top coats withhigh gloss und good chemical resistance
45 (Lffm.) 20 - 500 7,0 - 9,0 ca.60
LIOCRYL AS 680 parquet varnishes, industrial paints forwood/plastics
40 (Lffm.) 20 - 300 6,5 - 8,0 ca. 65
LIOCRYL DRR 2084 aqueous wood stains and pigmentedcoatings with high elasticity
47 20 - 500 7,0 - 8,5 ca. 16
LIOCRYL DRR 2459 primer for metal, high water resistance 50 100 - 500 8,0 - 10,0 ca. 22 Wasser/water
LIOCRYL DRR 2574 coatings for paper foils 45 max. 500 2,0 - 5,0 ca. 60
LIOCRYL XAM 2714 paints for wood/plastics 42 20 - 500 7,0 - 8,5 ca. 65
LIOCRYL XAM 2827 furniture and parquet coatings 42 20 - 500 7,2-7,9 ca. 56
LIOCRYL XAM 2867 coatings, self crosslinking at 130-160°C 57 < 400 2,5 - 6,0 ca. 5
LIOCRYL XAM 3972 coatings e.g. wood stains with earlyblocking resistance and high elasticity
45 < 500 7,0 - 9,0 ca. 8
LIOCRYL XAM 4107 facades, glazes, acrylic paints 45 < 500 7,0 - 9,0 ca. 8
LIOCRYL XAM 5134 wood and furniture coatings for one-packapplications with very good chemicalresistance
40 20 - 500 7,5 - 8,5 ca. 33
LIOCRYL XAM 6979 Flexible coatings with early blockingresistance e.g. lasures for wood, harderthan XAM 7574
45 < 500 7,0 - 9,0 ca. 8
LIOCRYL XAM 7252 A dispersion with low particle size forwood and furniture lacquers with very
41 20 - 500 7,5 - 9,0 ca. 33
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 18 of 27
Product Fields of use nvc (%) Visc. mPas pH value MFFT (°C) Base SustainableParts (%)
solv. % solv. hardener ratioresin/hardener
good chemical resistance
LIOCRYL XAM 7440 Paints for wood/plastics, partiallysustainable version of Liocryl XAM 2714
42 20 - 500 7,0 - 8,5 65 27
LIOCRYL XAM 7452 Furniture and parquet coatings, partiallysustainable version of Liocryl XAM 2827
42 20 - 500 7,0 - 8,5 56 36
LIOCRYL XAM 7574 Flexible coatings with early blockingresistance e.g. lasures for wood, moreelastic than XAM 6979
44 < 500 7,0 - 9,0 ca. 0
LIOCRYL XAM 7876 Flexible coatings with early blockingresistance e.g. lasures for wood, partiallysustainable version of Liocryl XAM 6979
41 < 500 7,0 - 9,0 < 10 20
LIOCRYL XAS 4940 cost-effective wood and furniture coatings 35 20 - 500 7,0 - 9,0 ca. 48 Wasser/water
LIOPUR 2004-119 1-pack formulations for coatings on wood,especially parquet and furniture
33 10 - 300 7,0 - 8,5 < 0 7% DMM
LIOPUR 2004-140 1-pack formulations for wood finishes 38 30 - 300 7,0 - 9,0 < 5 16 < 0,5
LIOPUR 2004-151 2-pack coatings for wood, especially forparquet floors
33 10 - 400 7,0 - 9,0 ca. 5 8% DMM
LIOPUR PFL 1154 2-pack coatings for wood 35 20 - 500 7,0 - 8,5 ca. 40 < 0,5
LIOPUR PFL 1284 NMP-free 1-pack formulation for wood andplastics
35 20 - 500 7,0 - 9,0 ca. 45 < 0,5
LIOPUR PFL 1908 1-pack and 2-pack systems for highquality wood and plastic coatings
35 30 - 500 7,0 - 9,0 > 80 < 0,5
LIOPUR PFL 1964 2-pack formulation for elastic plastic 38 20 - 500 7,0 - 9,0 < 10 < 0,5
LIOPUR PFL 2075 plastic coatings 34 +/- 2 20 - 400 7,0 - 9,0 < 20 0 wässrig/watery
BayhydrolXP 2655
10 : 1
LIOPUR PFL 2104 1-pack formulations for elastic coatings 40 20 - 500 7,0 - 9,0 < 0 < 0,5
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 19 of 27
Product Fields of use nvc (%) Visc. mPas pH value MFFT (°C) Base SustainableParts (%)
solv. % solv. hardener ratioresin/hardener
LIOPUR PFL 2315 2-pack formulation for wood coatings,especially parquet flooring
35 20 - 400 7,0 - 9,0 ca. 20 < 0,5
LIOPUR PFL 2366 1- and 2 pack formulations for woodcoatings, TEA-free
35 20 - 500 7,0 - 9,0 ca. 35
LIOPUR PFL 2392 1- and 2 pack formulations for plasticcoatings, TEA-free
40 10 - 400 7,0 - 9,0 < 20 15
LIOPUR PFL 2634 For stoving enamels, stable to overbakeand also 2 pack Systems
33 20 - 1000 7,0 - 9,0 < 5 < 0,5
LIOPUR PFL 2900 1K –Holz- u. Parkettlacken, die nach 1-2Stunden schleifbar sind u. eine guteAnfeuerung auf hellen Hölzern wie Eichebesitzen.
39 20 - 300 7,0 - 9,0 ca. 80 44
LIOPUR PFL 2966 1- and 2 pack systems for elastic textileand plastic coatings
50 30 - 500 6,5 - 8,5 < 5 < 0,5
LIOPUR PFL 3046 1- and 2 pack formulations for plasticcoatings and wood, TEA-free
34 +/- 2 30 - 750 7,0 - 9,0 ca. 20 25 < 0,5
LIOPUR PFL 3526 Coatings for plastics and wood withadditional flame retardant properties
40 10 - 300 6,5 - 8,5 ca. 55 < 0,5
LIOPUR PFL 3531 One- and two-component coatings forplastics and glass
40 20 - 800 7,9 - 9,0 < 5 < 0,5
LIOPUR PFL 3678 Coatings for flexible coatings, esp. leather 35 50 - 500 7,0 - 9,0 ca. 30 < 0,5 %
LIOPUR PFL 3864 Coatings for plastics and textile withadditional flame retardant properties
40 10 - 400 6,0 - 8,5 < 5 Polyesterurethan
< 0,5 %
LIOPUR PFL 4177 1C / 2C wood coatings 37 20 - 300 7,0 - 9,0 < 20 15 0
LIOPUR PFL 4225 1K systems for wood coatings 30 +/- 1 20 - 500 7 - 9 < 20
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 20 of 27
Resins for coatings / Polyester resins, saturated
Product Fields of use nvc(%)
solv. OHvalue
OHcont.(%)
AV Iod-col.
Flowtime ins.
Visc.mPas
solv.%
AVtypical
Hazen-col.
SustainableParts(%)
Gard-col.
pHvalue
hardener
ratio resin/hardener
Base VOC(g/L)
stoving condition
SYNTHOESTER 1018 two-pack coatings in association withaliphatic or aromatic polyisocyanates, airand oven-drying, good resistance toweather
75 X 155 -175
ca.5,0
< 15 < 3(50%X)
130 -250(50%X)
SYNTHOESTER 1080 two-pack air- and oven-drying coatings inassociation with aromatic polyisocyanates,hard films, resistant to chemicals
85 MPA 280 -320
8,8 < 4 < 5(70%MPA)
1.200-1.600(70%MPA)
SYNTHOESTER 1110 two-pack air- and oven-drying coatings inassociation with aromatic polyisocyanates
100 220 -240
ca.6,5
< 4 < 4(70%MPA)
300 -600(70%MPA)
SYNTHOESTER 1130 in combination with isocyanateprepolymers such as Desmodur L or N forair-drying two-pack PU coatings
75 X 128 -152
ca.4,3
< 15(Lffm.)
< 4(Lffm.)
50 -95(50%X)
SYNTHOESTER 1130 in combination with isocyanateprepolymers such as Desmodur L or N forair-drying two-pack PU coatings
75 Buac 128 -152
ca.4,3
< 15 < 4(Lffm.)
1.300-1.500
SYNTHOESTER 1165 two-pack air- and oven-drying coatings inassociation with aliphatic polyisocyanates,excellent resistance to weather
65 MPA/X(1:1)
240 -290
ca.8,0
< 4 < 3(50%MPA)
350 -750(50%MPA)
SYNTHOESTER 1170 gives elasticity to SYNTHOESTERcombinations for coatings on highly elasticmaterials
100,MV
40 -50
ca.1,5
< 3 < 2(Lffm.)
400 -650(70%EGA)
SYNTHOESTER 1179 soft-feel coatings 100 50 - ca. < 4 < 4 15.00
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 21 of 27
Product Fields of use nvc(%)
solv. OHvalue
OHcont.(%)
AV Iod-col.
Flowtime ins.
Visc.mPas
solv.%
AVtypical
Hazen-col.
SustainableParts(%)
Gard-col.
pHvalue
hardener
ratio resin/hardener
Base VOC(g/L)
stoving condition
65 1,8 (Lffm.)
0 -25.000
SYNTHOESTER 1402 In combination with suitable isocyanatesfor so-called soft-feeling paints
100 120 -140
ca.4,0
< 15 < 3(Lffm.)
15.000 -25.000
SYNTHOESTER 1680 fast-drying, air- and oven-drying two-packcoatings in association with aliphaticpolyisocyanates, for industrial andautomotive paints, excellent resistance toweather
60 X 110 -130
10 -25
max.3(Lffm.)
2.000-3.000
SYNTHOESTER 1680 fast-drying, air- and oven-drying two-packcoatings in association with aliphaticpolyisocyanates, for industrial andautomotive paints, excellent resistance toweather
70 Buac 110 -130
10 -25
max.3(Lffm.)
SYNTHOESTER 1690 air- and oven-drying two-pack coatings inassociation with aliphatic polyisocyantes,little curing agent required, good glossretention and colour stability, compatiblewith alkyd resin pastes
60 X ca.60
ca.1,8
< 30 max.3(Lffm.)
2.000-3.000
SYNTHOESTER 186HS
in combination with amino resins and CABfor base coats and stoving paints. Incombination with aliphaticpolyisocyanates, air- and oven-drying two-pack high-solids top coats and extenderswith good mechanical values, high gloss,good adhesion, very good resistance tochemicals, and very good gloss retentionand colour stability.
80 Buac 200 6 14 -20
1.000-1.600(70%Buac)
SYNTHOESTER 215HS
In combination with melamine resins andCAB for base-coat enamels. Incombination with aliphatic polyisocyanatesair- and oven-drying 2 pack high-solidlaquers and fillers with high mechanicalproperties, high gloss and body, very goodchemical- and weatherresistance.
80 Buac 205 -235
6,7 14 -20
16.000 -24.000
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 22 of 27
Product Fields of use nvc(%)
solv. OHvalue
OHcont.(%)
AV Iod-col.
Flowtime ins.
Visc.mPas
solv.%
AVtypical
Hazen-col.
SustainableParts(%)
Gard-col.
pHvalue
hardener
ratio resin/hardener
Base VOC(g/L)
stoving condition
SYNTHOESTER CC 55 For can- and coil coating and as hydrofillerfor 1 pack water- and convertional stovingdrying coatings
70 BG 40-45
max.10(Lffm.)
20.000 -30.000
SYNTHOESTERHD-080
soft-feel coatings and low-temperatureelastic two-pack coatings
100 80 -90
2,4 3 - 5 15.000 -20.000
SYNTHOESTERHD-165
hydroxyl group-containing polyesters forgiving elasticity or for two-pack coatings,low-temperature elasticity
80 SSA 160 -180
ca.5,0
< 2(60%EPA)
40 -60(60%EPA)
SYNTHOESTERHD-170 HS
hydroxyl group-containg polyesters,especially for giving elasticity withpolyisocyanate-curing acrylic resincombinations
80 SSA/EPA(1:4)
145 -170
ca.5,1
14 -18(nfA)
60 -75(60%EPA)
SYNTHOESTER TC1995
In combination with melamin resins forcan - und coil coating with goodweathering, elasticity and adhesion.
70 Solv. DPM/Solv.PM(2:1)
95 -115
2,9 -3,5
15000 -25000
30 40 -55
< 8 30
Synthoester TH 2325 Hydroxyl group-containing polyester resinfor 1k and 2k scratch-resistant and self-healing paints for the automotive sector
65 Buac 200 -240
6,1 -7,3
< 6 2000-5000
< 1
Synthoester TH 2532 Hydroxyl group-containing polyester resinfor 1k and 2k scratch-resistant and self-healing paints for industrial paints
70 Buac 200 -240
6,1 -7,3
< 6 1200-3400
< 1
Synthoester TH 2844 Hydroxyl group-containing polyester resinfor 1k and 2k scratch-resistant and self-healing paints for industrial paints
70 Buac 180 -220
5,5 -6,7
< 6 700 -1700
< 1
SYNTHOESTER TS1713
use and properties as SYNTHOESTER186 HS with lower VOC value and higherhydroxyl value
80 Buac 225 -265
7,4 14 -20(nfA)
500 -1.000(70%Buac)
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 23 of 27
Product Fields of use nvc(%)
solv. OHvalue
OHcont.(%)
AV Iod-col.
Flowtime ins.
Visc.mPas
solv.%
AVtypical
Hazen-col.
SustainableParts(%)
Gard-col.
pHvalue
hardener
ratio resin/hardener
Base VOC(g/L)
stoving condition
SYNTHOESTER TS2245
Siloxane modified polyester resin forscratch resistant low voc top coats. Incombination with melamines for bakingenamels or with polyisocyanates for aisdryin 2 K.
79-81 Buac 190 -250
6,4 <10(nfA.)
250 - 450(70%Buac)
SYNTHOESTER TS4309
very flexible 2pack-coating for soft-feeling-coatings, with amines even used forwaterdilutable coatings
99-100
80 -90
2,6 <20(nfA.)
15.000 -25.000
SYNTHOESTER W 142 for air- and forced drying top coats onmetal, glass, wood and plastic substrateswith very good adhesion, weathering andchemical resistance.
50 Wasser/PnB/DMEA
nicht messbar
3.000-8.000
7,7 -8,6
Synthoester W TE1900
Industrial, Can – and Coil – Coatings withhigh weather- and chemical resistances,tough elasticity, adhesion, hardness.
40 DMEA/Wasser
120 -150
3,6 -4,5
2000-6000
0 25 6,0 -8,0
Melaminharz/geblockte Polyisocyanate
80 :20
Polyester
< 10 >120°C20min
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 24 of 27
Resins for coatings / Radiation-curing resins
Product Fields of use nvc (%) OH value AV Iod-col. Visc. mPas solv. solv. % AV typical Gard-col.
SYNTHOLUX 197 PE primers and top coats for wood, paper andplastics, printing inks; resin is similar toSYNTHOLUX DRM 190 but lighter incolour
100 ca. 75 < 5 < 3 (Lffm.) 10.000 - 30.000
SYNTHOLUX 227 UA Difunctional Urethaneacrylate, diluted inHydroxy methyl methacrylate with a highflexibility on several substrates
2 - 4 Hydroxypropylmethacrylat
65 < 1 < 1
SYNTHOLUX 271 UA for versatile coating of substrates such aswood and paper, can be used as solebinder or together with other radiation-curing resins to increase elasticity.Polymer is identical to SYNTHOLUX 227UA.
65 < 2 (nfA) 9.000 - 18.000 < 0,5 (Lffm.)
SYNTHOLUX 291 EA wood, paper, glass, metal, ceramics andspecific plastics (PVC, polystyrene, ABS,polyethylene), giving elastic, hard filmswith very high resistance to chemicals
80 ca. 180 max. 7 23.000 - 33.000 max. 3(Lffm.)
SYNTHOLUX 432 PAA amine-modified, highly reactive, suitablefor monomer-free coating formulations inthe furniture and printing ink sector
100 ca. 60 < 4 (nfA) 200 - 500 < 3 (Lffm.)
SYNTHOLUX 475 PE UV- and electron beam-curing coatings forprinting inks with excellent pigmentwetting (paste resin)
100 ca. 50 13.000 - 16.000 < 6 (Lffm.)
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 25 of 27
Resins for coatings / Radiation-curing resins / water-thinnable
Product Fields of use nvc (%) Visc. mPas pH value solv. % Sustainable Parts (%)
SYNTHOLUX 1014 W water-based, physically drying and UV-curing aliphatic polyurethane dispersion,containing no emulsifiers or co-solvents;for coating susbtrates such as wood andplastics with good elasticity and resistanceto chemicals
40 10 - 300 7,0 - 8,5 (1:4 in H2O)
SYNTHOLUX BW 1964 Coatings for plastics, especially resilientflooring coatings based on PVC andlinoleum. Also for PC and metalsubstrates
40 10 - 300 7,0 - 8,5 (20% in H2O)
SYNTHOLUX BW 2025 water-based, physically drying and UV-curing aliphatic polyurethane dispersion,tinfree; for coating susbtrates such aswood and plastics with good elasticity andresistance to chemicals
40 10 - 300 7,0 - 8,5 (1:4 in H2O)
SYNTHOLUX BW 2096 waterborne physically drying, UV-curable,aliphatic polyurethane-dispersion
37 10 - 300 7,0 - 8,5 (20% in H2O)
SYNTHOLUX BW 2132 For waterborne wood application with avery good grain enhancement and verygood matting behaviour.
10 - 100 7 - 9
SYNTHOLUX BW 2182 Aqueous, physically drying and UV-curable, tin-free polyurethane dispersionwith increased functionality and highdouble bond equivalent.
40 20 -300 6,5 - 9,0 (50% in H2O)
SYNTHOLUX BW 2223 Aqueous, physically drying UV dispersionwith a very high chemical resistance,especially for high-quality pigmented UVcurable coatings. The dispersion isprepared without tin.
10 - 100 7,0 - 9,0 40
SYNTHOLUX BW 2361 Waterborn, weak physically drying, UV-curable PU-dispersion for very high glossapplication and very good grainenhancement, with 5 % of sustainable rawmaterials
40 10 - 300, 23°C 7 - 8,5 60 5
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 26 of 27
Resins for coatings / Radiation-curing resins / Inert acrylate
Product Fields of use nvc (%) solv. solv. % AV Gard-col. Visc. mPas Sustainable Parts (%)
SYNTHOLUX 708 IA Pure acrylic thermoplastic resin diluted inreactive diluent for primers on plastics andmetal with an excellent adhesion.
63 IBoA 37 max. 35 max. 3 1000 - 3000, 50% Buac, 23°C 29
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com
Page 27 of 27
Resins for coatings / Can and coil coating resins
Product Fields of use nvc (%) solv. OH value OH cont. (%) AV Iod-col. Visc. mPas
SYNTHOESTER C 455 In combination with melamine resin forhigh durable stoving enamels withexcellent weathering and colour stability.
65 Solvesso 150 ND/BG (3:1) 20 - 40 0,9 < 15 < 2 2.400 - 3.200
SYNTHOESTER CC 42 Combined with suitable melamine andbenzoguanamine resins, it is used in thecan and coil coating sector.
50 LM-Gem. (50%ig in DBE/Solvesso 150/ Butylglykol25:20:5)
< 5 < 3 (Lffm.) 3.500 - 4.000
Powered by TCPDF (www.tcpdf.org)
Synthopol Chemie Dr. rer. pol. Koch GmbH & Co. KG, Alter Postweg 35, D-21614 Buxtehude // Telefon: +49 (0) 4161 / 7071-0 // [email protected] // www.synthopol.com