P.K. Lin
1
![Page 2: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/2.jpg)
Outline• Introduction• Experiments• Results and Discussion• Conclusion• References
2
![Page 3: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/3.jpg)
Introduction
• Over the past few years, people have proposed numerous physics mechanisms to explain the phenomenon of efficiency droop, such as Auger recombination ,electron leakage , poor hole injection efficiency , polarization effect , and the quantum confined stark effect.
• Up to now, however, the approaches to improve efficiency droop are still mainly to suppress the electron overflow, enhance the hole injection efficiency, and reduce the polarization field.
3
![Page 4: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/4.jpg)
Introduction
• Such as the usage of staggered quantum wells (QWs) ,AlGaN barriers , indium graded last barrier , p-InGaN hole reservoir layer , graded electron blocking layer (EBL) , and AlGaN/GaN superlattice EBL of gradual Al mole fraction.
• In this paper, the idea of InGaN barriers and dip-shaped last barrier is proposed with reduced polarization effect, decreased electron current overflow, and increased hole injection efficiency.
4
![Page 5: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/5.jpg)
Experiments
C-plan Sapphire
2um-undoped GaN Layer
2μm Si-doped N-GaN(n = 5 x1018cm-3)
MQW
20nm Al0.15Ga0.85NEBL (p = 5x1017cm-3)
170nm Mg-doped P-GaN(p = 7x1017cm-3)
N contact
ITO
P contact
LED MQWComposition In0.16Ga0.84N/
GaNPair six-period
Thickness 3nm/10nm
Chip size: 300x300(um2)
5
The structue of the conventional (Original structure)
![Page 6: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/6.jpg)
6
FIG. 1. Schematic view of InGaN LEDs with conventional GaN barrier(original structure), InGaN barriers (structure A), and InGaN barriers anddip-shaped last barrier (structure B).
![Page 7: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/7.jpg)
Fig. 2. (a) Light output power, (b) I –V curves, and (c) IQE for the three LEDs.
7
Results and Discussion
At 200mA Efficiency droopOriginal structure 40.9%
Structure A 27.7%
Structure B 23.5%
![Page 8: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/8.jpg)
Fig. 3. Electrostatic fields and band wavefunctions of the three LEDs at200 mA.
8
![Page 9: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/9.jpg)
Fig. 4. Energy band diagrams of the three LEDs at 200 mA.
9
![Page 10: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/10.jpg)
Fig. 5. (a) Electron concentrations, (b) hole concentrations,and (c) electron current density of the three structures at 200 mA.
10
![Page 11: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/11.jpg)
Fig. 6. Radiative recombination rate inset with spontaneous emission rate of the three structures at 200 mA.
11
![Page 12: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/12.jpg)
• In summary, it is found that the electron leakage is markedly reduced, the hole injection efficiency is greatly enhanced.
• In addition, the electrostatic fields in the MQWs are relieved effectively when the conventional GaN barriers are replaced by InGaN barriers and dip-shaped last InGaN barrier .
• Therefore, the optical and electrical performances of the newly designed LED acquired a significant improvement.
Conclusion
12
![Page 13: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/13.jpg)
• R.M.Lin,S.F.Yu,S.J.Chang, T.H.Chiang,S.P.Chang,andC.H. Chen, “Inserting a p-InGaN layer before the p-AlGaN electron blocking layer suppresses efficiency droop in InGaN-based light-emitting diodes,” Appl. Phys. Lett., vol.101,no.8,pp.081120-1–081120-3,Aug.2012.
• T.Lu,S.Li,C.Liu,K.Zhang,Y.Xu,J.Tong,L.Wu,H.Wang, X.Yang,Y.Yin,G.Xiao,andY.Zhou,“Advantages of GaN basedlight-emitting diodes with a p-InGaN hole reservoir layer,” Appl. Phys. Lett.,vol.100,no.14,pp. 141106-1–141106-3,Apr.2012.
• C.S.Xia,Z.M.Simon Li,W.Lu,Z.H.Zhang,and L.W.Cheng,“Droop improvement in blue InGaN/GaN multiple quantum well light-emitting diodes with indium graded last barrier,”Appl. Phys. Lett.,vol.99,no.23,pp.233501-1–233501-3, Dec. 2011.
References
13
![Page 14: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/14.jpg)
Thanks for your attention!
![Page 15: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/15.jpg)
References
![Page 16: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/16.jpg)
The advanced physical model of semiconductor devices simulation software
The key parameters Set on The radiative 2.0 x 10-11 cm3/s
Internal absorption 2000m-1
Auger cofficients 1.0 x 10-31 cm3/s
SRH recombination lifetime 100ns
Operating temperature 300K
![Page 17: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/17.jpg)
![Page 18: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/18.jpg)
![Page 19: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/19.jpg)
References
![Page 20: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/20.jpg)
My Designed EBL structure of LED
p-GaNn-GaN
p-AlGaN
MQW(GaN/InGaN)Original structure
p-GaNn-GaN
p-AlGaN
MQW(GaN/InGaN)New structure
透過在MQW與 EBL間插入一層 AlGaN superlattice ,做為緩衝 last barrier 與 EBL lattice mismatch 所帶來能帶傾斜的效應 !!進而增加 EBL有效的能障高度…
![Page 21: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/21.jpg)
My Designed EBL structure
p-GaNn-GaN
p-AlGaN
MQW(GaN/InGaN)Original structure
在 last barrier 做一 n參雜,目的在於行程一空乏區內建電場 !透過 PN面空乏區電場來去抵補極化場 !!
n-GaN
New structure
p-GaN
p-type
n-type
![Page 22: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/22.jpg)
極化場方向內建電場方向
![Page 23: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/23.jpg)
![Page 24: P.K. Lin](https://reader035.fdocuments.in/reader035/viewer/2022070501/56816937550346895de09ade/html5/thumbnails/24.jpg)
My Designed EBL structure
n-GaN
New structure
p-GaN
p-type
n-type
p-type GaN barrier
n-type EBL
p-type EBL
p-GaN