NEXTERION® Microarray slides with barcodes and custom logos from SCHOTT
2
Schott Jena er Glas GmbH Microarray Solution Otto Schott Str. 13, 07745 Jena Tel.: +49 3641 68191971 Fax: +49 3641 681970 02.05.07 Laser etched foil barcodes and logos on SCHOTT Borosilicate glass slides Colour of foil Properties White Black Brown Blue Abrasion (1) / adhesion (2) No effect Temperature (3) and temperature change (4) stability No effect Water resistance (5) No effect Color stability after thermal stress (6) No effect slight fading Text is bleached Stability against acid (7) or alkaline (8) Solution Stable Not stable Maximum temperature without colour change (9) (dependent on type of glass) upto 1000 o C upto 500 o C 200 o C (1h) High pressure water spray test (10) No effect Not stable (1) Abrasion test (2) Adhesive tape test (3) 5 x 8 h at 200 °C, cooling to ambient between heating steps (4) 5 x 15 min to 200 °C samples cooled in water (20 °C) between heating steps (5) According to DIN ISO 719 (6) Recovery following manufacture’s recommendations (heat to 550°C, 30 min stops, depending on glass thickness) (7) According to DIN 12116 (8) Supported by DIN ISO 695 (9) Sample heated 100 to 500 degrees in 100 K stages, 1h holding time, slow cooling (10) 5 x 15 min at 200 °C, Spray the text with water at 20 °C Logos Graphic logos and company names may be applied at any location on the glass surface
-
Upload
schott -
Category
Technology
-
view
772 -
download
2
description
Details about the barcodes and custom logos SCHOTT can apply to borosilicate glass microarray slides.
Transcript of NEXTERION® Microarray slides with barcodes and custom logos from SCHOTT
Schott Jenaer Glas GmbHMicroarray SolutionOtto Schott Str. 13, 07745 JenaTel.: +49 3641 68191971 Fax: +49 3641 681970
02.05.07
Laser etched foil barcodes and logos on SCHOTT Borosilicate glass slides
Colour of foil
Properties White Black Brown BlueAbrasion(1)/ adhesion(2)
No effectTemperature (3) and temperature change (4)
stability
No effect
Water resistance(5)No effect
Color stability after thermal stress(6)
No effect slight fading Text is bleached
Stability against acid (7)or alkaline (8) Solution
Stable Not stable
Maximum temperature without colour change(9)
(dependent on type of glass)
upto 1000 oC upto 500 oC 200 oC (1h)
High pressure water spray test(10)
No effect Not stable
(1) Abrasion test
(2) Adhesive tape test
(3) 5 x 8 h at 200 °C, cooling to ambient between heating steps
(4) 5 x 15 min to 200 °C samples cooled in water (20 °C) between heating steps
(5) According to DIN ISO 719
(6) Recovery following manufacture’s recommendations (heat to 550°C, 30 min stops, depending on glass thickness)
(7) According to DIN 12116
(8) Supported by DIN ISO 695
(9) Sample heated 100 to 500 degrees in 100 K stages, 1h holding time, slow cooling
(10) 5 x 15 min at 200 °C, Spray the text with water at 20 °C
Logos
Graphic logos and company names may be applied at any location on the glass surface
Schott Jenaer Glas GmbHMicroarray SolutionOtto Schott Str. 13, 07745 JenaTel.: +49 3641 68191971 Fax: +49 3641 681970
02.05.07
Seite 2 von 2
Type of Barcodes available using laser etched foil barcodes:
DataMatrix: 2-Dimensional barcodes Alphanumeric barcodes
ID Matrix ECC 100 two-dimensional
ID Matrix ECC 130 two-dimensional
ID Matrix ECC 140 two-dimensional
ID Matrix ECC 200 two-dimensional
ID Matrix ECC 200 rectangular
Code 39 (full ANSI)
Code 39 (Alphanumeric)
Code 93 (Alphanumeric)
Code 128 (Alphanumeric)
Codabar (numeric)
EAN/OCC 128 (Alphanumeric)
EAN-8 (numeric 8)
EAN-13 (numeric 13)
UPC-A (numeric 12)
UPC-E (numeric 6)
Interleaved 2/5 (numeric)
PDF417(full ansi)
Barcodes can be applied to upper or lower slide surface. Barcodes on lower surface can
be reversed so they are read correctly from top surface.
Examples of barcodes