MURDOCH RESEARCH REPOSITORY
This is the author’s final version of the work, as accepted for publication following peer review but without the publisher’s layout or pagination.
The definitive version is available at http://dx.doi.org/10.1016/j.materresbull.2013.04.093
Huang, W., Li, D., Zhu, Y., Xu, K., Li, J., Han, B. and Zhang, Y. (2013) Phosphate adsorption on aluminum-coordinated functionalized macroporous–mesoporous silica: Surface
structure and adsorption behavior. Materials Research Bulletin, 48 (12). pp. 4974-4978.
http://researchrepository.murdoch.edu.au/15728/
Copyright: © 2013 Elsevier Ltd.
It is posted here for your personal use. No further distribution is permitted.
Accepted Manuscript
Title: Phosphate Adsorption on Aluminum–coordinatedFunctionalized Macroporous–mesoporous Silica: SurfaceStructure and Adsorption Behavior
Author: Weiya Huang Dan Li Yi Zhu Kai Xu Jianqiang LiBoping Han Yuanming Zhang
PII: S0025-5408(13)00379-6DOI: http://dx.doi.org/doi:10.1016/j.materresbull.2013.04.093Reference: MRB 6699
To appear in: MRB
Received date: 20-1-2013Revised date: 30-4-2013Accepted date: 30-4-2013
Please cite this article as: W. Huang, D. Li, Y. Zhu, K. Xu, J. Li, B.H.</sup>,Yuanming Zhang, Phosphate Adsorption on Aluminum–coordinatedFunctionalized Macroporous–mesoporous Silica: Surface Structureand Adsorption Behavior, Materials Research Bulletin (2013),http://dx.doi.org/10.1016/j.materresbull.2013.04.093
This is a PDF file of an unedited manuscript that has been accepted for publication.As a service to our customers we are providing this early version of the manuscript.The manuscript will undergo copyediting, typesetting, and review of the resulting proofbefore it is published in its final form. Please note that during the production processerrors may be discovered which could affect the content, and all legal disclaimers thatapply to the journal pertain.
Page 1 of 21
Accep
ted
Man
uscr
ipt
1
Phosphate Adsorption on Aluminum–coordinated Functionalized
Macroporous–mesoporous Silica: Surface Structure and Adsorption
Behavior
Weiya Huang1,2, Dan Li3, Yi Zhu1, Kai Xu1, Jianqiang Li1, Boping Han4,Yuanming
Zhang 1,*
1Department of Chemistry, Jinan University, Guangzhou 510632, P.R. China
2Department of Materials Science and Engineering, Taizhou University, Linhai
317000, P.R. China
3Environmetal Engineering, School of Engineering and Information Technology,
Murdoch University, Murdoch, Western Australia 6150, Australia
4Institute of Hydrobiology, Jinan University, Guangzhou 510460, P.R. China
* To whom correspondence should be addressed. E-mail: [email protected] (Y.M.
Zhang);
Fax: +86-20-85221264; Tel: +86-20-85221264.
Page 2 of 21
Accep
ted
Man
uscr
ipt
2
Abstract:
In this study, Al(Ш)-coordinated diamino-functionalized macroporous-mesoporous
silica was synthesized and characterized by X-ray diffraction, N2
adsorption-desorption, Fourier transform infrared spectroscopy, scanning and
transmission electron microscopy. Because of well-defined and interconnecting
macroporous-mesoporous networks, the resulting adsorbent (MM-SBA) exhibited a
significantly better phosphate adsorption performance and faster removal rate, as
compared with the mesoporous adsorbent (M-SBA). Based on the Freundlich and
Langmuir models, the phosphate adsorption capacity and the maximum adsorption
capacity of MM-SBA were 7.99 mg P/g and 23.59 mg P/g, respectively. In the kinetic
study of MM-SBA, over 95% of its final adsorption capacity reached in the first 1 min;
whereas that of M-SBA was less than 79%.
KEYWORDS: A. amorphous materials; A. structural materials; B. chemical
synthesis; D. diffusion
Page 3 of 21
Accep
ted
Man
uscr
ipt
3
1. Introduction
Phosphorus is an important nutrient for living species, which is typically present
at a low concentration in environment serving as the limiting factor for aquatic plant
growth. To date, the increasing discharge of contaminating nutrients, e.g. phosphate,
into the aquatic system has resulted in serious environmental problems around the
world, such as eutrophication and consequent algal bloom [1]. Hence, it is necessary
to decrease the concentration of phosphate in wastewater before its discharge. The
typical discharge limit for phosphorus in wastewater is less than 1 mg P/L [2];
however, this still causes the problem of eutrophication. Therefore, methods which are
capable to remove phosphate efficiently and rapidly at a relatively low concentration
are urgently needed. A series of methods have been studied to remove phosphate from
water [3], in which the adsorption-based process has attracted great interest, due to the
high removal efficiency and fast removal rate, especially at low phosphate
concentrations [4]. Among various types of adsorbents, including inorganic, organic
and inorganic-organic hybrid materials [5-7], well-ordered mesoporous silica
materials are useful in adsorption for their unique features, such as highly ordered
structures, ultrahigh surface areas, narrow mesopore size distributions, and tunable
pore size and structure [8,9]. However, the pure mesoporous silicas exhibit extremely
low or even immeasurable phosphate adsorption capacities, which are attributed to the
poor capacity of surface groups Si-OH capturing phosphate anions from aqueous
solution [10]. So far, organic-functionalization has been considered as an effective
Page 4 of 21
Accep
ted
Man
uscr
ipt
4
strategy to precisely control the chemical properties of silica materials and generate
specific binding sites for phosphate ions, which can enhance the adsorption capacity
and removal rate of resulting adsorbents. For example, Chouyyok and co-workers
reported that Fe(III)-coordinated ethylenediamine-functionalized MCM-41 silica had
a phosphate adsorption capacity of 14.13 mg P/g with 99% of phosphate removal
within 1 min [9]. Zhang et al. utilized Fe(III) and La(III)-coordinated
diamino-functionalized MCM-41 adsorbents for phosphate removal, which showed
the maximum adsorption capacities of 16.90 mg P/g and 17.72 mg P/g, respectively
[11, 12]. Recently, we reported the synthesis of functionalized SBA-15 adsorbents
with various loadings of diamino group via a new NH4F-assisted co-condensation
method for the first time [13]. With 0.5:1 molar ratio of
N-(2-aminoethyl)-3-aminopropyltrimethoxysilane and tetraethoxysilane, the resulting
Fe(III)-coordinated sample showed the maximum phosphate capture capacity of 20.7
mg P/g and reached almost 90% of the final adsorption capacity in 10 min.
However, it is noted that the attachment of functional groups on the silica pore
surfaces decreased pore sizes of mesoporous silicas and subsequently limited the
diffusion [14]. Previous research has shown that the introduction of macropores into
mesoporous materials may act as rapid transport conduits to the active sites on the
surfaces of mesopores, thus favoring mass transfer and reducing transport limitations
[15]. The objective of our work is to investigate the utilization of Al(III)-coordinated
diamino-functionalized macroporous-mesoporous SBA-15 silica material for
phosphate removal. Herein, a dual-templating approach was applied to generate
Page 5 of 21
Accep
ted
Man
uscr
ipt
5
mesopores and macropores by using P123 and polystyrene beads in the preparation of
adsorbent. Afterwards, the diamino-functional groups were post-grafted onto the
macroporous–mesoporous SBA-15 supports, followed by the immobilization of Al(Ш)
active sites. The fabrication, characterization and phosphate adsorption performance
of Al(Ш)-coordinated diamino-functionalized macroporous-mesoporous SBA-15
silicas are detailed in this paper. The presence of interconnected macroporous and
mesoporous structures in our prepared adsorbent is expected to promote mass transfer
and enhance phosphate removal.
2. Experimental
2.1 Preparation and characterization of adsorbents
Monodisperse polystyrene (PS) beads with an average size of 380 ± 10 nm were
synthesized via the emulsion polymerization approach as reported [16].
Macroporous-mesoporous SBA-15 silica was prepared with the use of Pluronic P123
triblock co-polymer (PEO20-PPO70-PEO20, Aldrich) and our prepared PS beads as
templates which generated mesopores and macropores [17]. 1.0 g of P123 was
dissolved in a solution consisting of 7.5 mL of deionized (DI) water and 25.0 mL of
2.0 M HCl under stirring at 35 °C. After well dispersing 8.7 g of PS beads, 2.3 mL of
tetraethoxysilane (TEOS, Aladdin Reagent Inc., 95%) was added to the mixture,
which was continuously stirred at 35°C for 24 h and subsequently reacted at 100 °C
for another 24 h. Solid powder was filtered and washed with DI water 3 times,
followed by calcination in air at 550°C for 6 h to remove P123 and PS beads.
Afterwards, the resulting silica sample was functionalized via the post-grafting
Page 6 of 21
Accep
ted
Man
uscr
ipt
6
method, by refluxing in the mixture of 30.0 mL of toluene and 3.0 mL of
N-(2-aminoethyl)-3-aminopropyltrimethoxysilane (AAPTS, 95%, Aladdin Reagent
Inc.) at 130°C for 24 h. Following that, the diamino-functionalized sample was
filtered, washed with ethanol 3 times and mixed in 0.1 M AlCl3 aqueous solution for 2
h. The solid was separated, washed with DI water and 2-propanol, and dried under
vacuum at 60 °C for 12 h. The final product, Al(III)-coordinated
diamino-functionalized macroporous–mesoporous silica, is denoted as MM-SBA. For
comparison, by using the similar synthetic method, the Al(III)-coordinated
diamino-functionalized mesoporous silica which was fabricated without the addition
of PS beads is denoted as M-SBA.
Surface morphologies of samples were examined by scanning electron
microscopy (SEM, JSM-7401F, JEOL Ltd., Japan) and transmission electron
microscopy (TEM, JEM2010-HR, JEOL Ltd., Japan). X-ray powder diffraction (XRD)
patters were recorded in the 2θ range of 0.6–6° at a scan speed of 1°/min by using a
diffractometer (Bruker D8 Advance diffractometer, Germany) with Cu Kα radiation
(40 mA, 45 kV). Fourier transform infrared (FT-IR) measurements were performed
between 400 cm−1 and 4000cm−1 by using Shimadzu IR Prestige-21 instrument, in
which KBr pellets containing 0.50 % of the samples were used. Nitrogen
adsorption-desorption isotherms were measured at 77 K using ASAP2010
(Micromeritics Inc., USA). Prior to analysis, the samples were degassed at 120 °C for
12 h under vacuum. The specific surface area (SBET) was determined from the linear
part of the BET plot (P/P0 = 0.05-0.20). The pore size (DBJH) was calculated from the
Page 7 of 21
Accep
ted
Man
uscr
ipt
7
desorption branch of isotherm by using Barrett-Joyner-Hallenda (BJH) method. The
total pore volume (VTotal) was evaluated from the adsorbed nitrogen amount at a
relative pressure 0.98.
2.2 Phosphate adsorption of adsorbents
A series of batch tests were conducted to investigate the phosphate adsorption
performances of adsorbents. In the equilibrium experiment, 0.025 g of adsorbent was
added into 25.0 mL of phosphate solution with various initial concentrations in a
polypropylene bottle, which was prepared by dissolving anhydrous K2HPO4
(analytical grade, Sinopharm Chemical Reagent Co., Ltd) in DI water. After shaking
for 2 h, the solution was removed by filtering through a syringe nylon-membrane
filter (pore size 0.45 μm; Shanghai Xinya Purification Devices Factory). The
concentraiton of phosphate in filtrate was analyzed by Autoanalyzer 3 (Bran and
Luebbe Inc., Germany). The amount of phosphate adsorbed on the sample at
equilibrium (qe) was calculated by Eq. (1),
m
VCCq e
e
!!!
)( 0 (1)
where C0 and Ce are the initial and equilibrium phosphate concentrations in solution
(mg P/L), respectively; V is the volume of solution (L) and m is the mass of adsorbent
(g).
The equilibrium data were fitted to the well-known Langmuir and Freundlich
isotherm models, as shown in Eqs. (2) and (3), respectively [18],
Langmuir model: 00
1qC
KqqC e
Le
e !! (2)
Freundlich model: eFe Cn
Kq log1
loglog !! (3)
Page 8 of 21
Accep
ted
Man
uscr
ipt
8
where q0 (mg/g) and KL (L/mg) are constants in the Langmuir isotherm model which
are related to maximum adsorption capacity and energy or net enthalpy of adsorption,
respectively; KF (mg/g) and n are the constants in the Freundlich isotherm model,
which measure the adsorption capacity and intensity, respectively.
The adsorption kinetic experiment was conducted as follows: 0.10 g of adsorbent
was added in 100.0 mL of phosphate solution with initial concentration of 50.0mg P/L.
The sealed polypropylene bottle was then placed in the shaker bath for 4 h. About 2.0
mL of suspension was taken out of bottle over a given period of time, and the
phosphate concentration was analyzed as in the equilibrium experiment.
3. Results and discussion
3.1 Characterization of adsorbents
The X-ray diffraction patterns of M-SBA and MM-SBA are presented in Fig. 1.
In the XRD pattern of M-SBA, three well-resolved SBA-15 reflections, one intense
diffraction peak (100) and two relatively weak diffraction peaks (110) and (200),
suggest the presence of well-ordered hexagonal arrangement of mesoporous silica
framework [19]. In the XRD pattern of MM-SBA, the characteristic reflections of
SBA-15 peaks are relatively lower; however, all the peaks are distinguishable. This
indicates that the synthesized MM-SBA adsorbent has a well-ordered hexagonal
mesoporous silica framework as well.
Fig. 2 shows FT-IR spectra of M-SBA and MM-SBA. The bands at 1082 cm−1,
803 cm−1, and 466cm−1 are attributed to the Si-O-Si asymmetric and symmetric
vibrations of condensed silica network. The peak at 961cm−1 is ascribed to the
Page 9 of 21
Accep
ted
Man
uscr
ipt
9
non-condensed silanol Si-OH groups [20, 21]. The bands observed at 1408 cm−1 and
1635 cm−1 are corresponding to the NH2 vibrations [21, 22], which confirms the
successful incorporation of organic functional groups into the synthesized adsorbents
via the post-grafting method.
Fig. 3 shows N2 adsorption-desorption isotherms of M-SBA and MM-SBA, and
their corresponding Barrett-Joyner-Halenda (BJH) pore size distribution plots (the
inset). Table 1 summarizes the textual property of samples, including BET surface
area (SBET), pore diameter (DBJH) and total pore volume (VTotal). The N2
adsorption-desorption isotherm of M-SBA exhibits a type IV isotherm model with a
H1 hysteresis loop according to IUPAC classification standard, suggesting the sample
with uniform and even mesopores [23]. The BET surface area, pore diameter and total
pore volume of M-SBA are 219 m2/g, 4.98 nm and 0.32 cm3/g, respectively. Its BET
surface area is smaller than that (514 m2/g) of the corresponding parent SBA-15
without amino-functionalization and metal-impregnation; that is also observed in the
comparison of SBET between MM-SBA (187 m2/g) and its parent
macroporous-mesoporous SBA-15 (432 m2/g), which can be explained by the
diamino-functionalization on the silica and the Fe-coordination [9,11]. As compared
with M-SBA, MM-SBA exhibits a similar N2 adsorption-desorption isotherm as well
as textual properties. However, in the N2 adsorption-desorption isotherm of MM-SBA,
there is an additional prominent hysteresis above P/P0 = 0.9, which is attributed to the
presence of high concentration of macropores in the sample [24].
Fig. 4a-d shows SEM and HR-TEM images of M-SBA and MM-SBA. In Fig. 4a,
Page 10 of 21
Accep
ted
Man
uscr
ipt
10
the sample M-SBA exhibits a uniform and ropelike shape, which is the typical
SBA-15 morphology as reported in literature [19]. In MM-SBA, the addition of PS
beads modifies the SBA-15-like organization and creates a new macroporous network
(the inset of Fig. 4b). The formed macroporous network is open and interconnected
with SBA-15 mesoporous framework, which is expected to induce a rapid adsorption
through particle diffusion. The HR-TEM images (Fig. 4c and d) further confirms the
change of morphology between these two samples. As seen in Fig. 4c, M-SBA shows
a typical SBA-15 morphology with 2D periodically hexagonal mesostructure, which
are indicated by white arrows and lines. In Fig. 4d, the introduction of macropores,
which are highlighted by the yellow line, breaks up the extended mesoporous
channels. The size of observed macropore is approximately 350 nm, which is close to
the size of PS beads (Fig. 4e; 380 ± 10 nm). Moreover, the highly-organized
concentric mesoporous channels solely locate in the walls of macroporous framework
of MM-SBA, which are shown with white arrows and lines in Fig. 4d.
3.2 Phosphate adsorption of adsorbents
Fig. 5 shows the Langmuir (Fig. 5a) and Freundlich adsorption isotherms (Fig.
5b). In Fig. 5 and Table 1, both of the Freundlich model and Langmuir model can
well describe the experimental isotherm data, despite the use of the Freundlich model
(R2 ≈ 0.98) is slightly better as compared to the Langmuir model (R2 ≈ 0.94). As
shown in Table 1, the adsorption capacity (KF) of MM-SBA is 7.99 mg P/g, which is
40.42% greater than that of M-SBA. The quantitative Langmuir parameter q0 for
MM-SBA is 23.59 mg P/g, which is significantly greater than that of M-SBA (16.21
Page 11 of 21
Accep
ted
Man
uscr
ipt
11
mg P/g). These results can be explained by the incorporation of macropores into the
mesoporous adsorbent, which promotes the diffusion of phosphate to the active sites
of adsorbent, thus improving the adsorption efficiency as expected.
Fig. 6 shows the adsorption kinetic study with the use of M-SBA and MM-SBA.
In Fig. 6, over 95% of final adsorption capacity of MM-SBA reaches in the first 1 min.
In the following 10 min, the phosphate adsorption of MM-SBA slightly increases and
reaches the equilibrium for the rest of time. However, the adsorption rate of M-SBA is
slower as compared with that of MM-SBA; only 79% of final adsorption capacity is
recorded at 1 min and approximately 95% of final adsorption capacity of M-SBA
reaches at 3 min. The results of kinetic study suggest that faster diffusion of
phosphate to the active sites of the macroporous-mesoporous adsorbent MM-SBA
occurs, as compared with the single-sized mesoporous adsorbent M-SBA.
4. Conclusions
Al(III)-coordinated diamino-functionalized macroporous-mesoporous silica
adsorbent was synthesized by using a PS/TEOS weight ratio of 4:1. As compared with
the single-sized mesoporous M-SBA, MM-SBA possessed a
macroporous-mesoporous network, which exhibited an enhanced phosphate
adsorption performance, with a high maximum adsorption capacity (q0 = 23.59 mg
P/g) and a fast adsorption rate (> 95% of final adsorption capacity in the first 1min).
Therefore, the functionalized macroporous-mesoporous silica adsorbent shows great
potential for use in efficient phosphate removal.
Acknowledgements
Page 12 of 21
Accep
ted
Man
uscr
ipt
12
This work was supported by Natural Science Foundation of Guangdong (No.
S2011040001667), the Fundamental ResearchFunds for the Central Universities (No.
21611310), the National High Technology Research and Development Program of
China (863 Program) (No.2009AA064401), and the Key Laboratory of Mineralogy
and Metallogeny Cooperation Foundation (No. KLMM20110204). Support for Ms
Weiya Huang was partially provided by the program of China Scholarship Council
(No.201206780010).
References
[1] V.N.D. Jonge, M. Elliott, E. Orive, Hydrobiologia. 475-476 (2002) 1-19.
[2]A. Ugurlu, B. Salman, Environ. Int. 24 (1998) 911–918.
[3]G.K. Morse, S.W. Brett, J.A. Guy, J.N. Lester, Sci. Total Environ. 212 (1998)
69-81.
[4] S.K. Kang, K.H. Choo, K.H. Lim, Sep. Sci. Technol. 38 (2003) 3853-3874.
[5] L. Zeng, X.M. Li, J.D. Liu, Water Res. 38 (2004) 1318-1326.
[6] X.P. Liao, Y. Ding, B. Wang, B. Shi, Ind. Eng. Chem. Res.45 (2006) 3896-3901.
[7]B.K. Biswas, K. Inoue, K.N. Ghimire, H. Harada, K. Ohto, H. Kawakita, Bioresour.
Technol. 99 (2008) 8685-8690.
[8] E.W. Shin, J.S. Han, M. Jang, S.H. Min, J.K. Park, R.M. Rowell. Environ. Sci.
Technol. 38 (2003) 912-917..
[9]W. Chouyyok, R.J. Wiacek, K. Pattamakomsan, T. Sangvanich, R.M. Grudzien,
G.E. Fryxell, W. Yantasee, Environ. Sci. Technol. 44 (2010) 3073-3078.
Page 13 of 21
Accep
ted
Man
uscr
ipt
13
[10] R. Saad, K. Belkacemi, S. Hamoudi, J. Colloid Interface Sci. 311 (2007)
375-381.
[11] J. Zhang, Z. Shen, Z. Mei, S. Li, W. Wang, J. Environ. Sci. 23 (2011) 199–205.J.
[12] Zhang, Z. Shen, W. Shan, Z. Mei, W Wang, J. Hazard. Mater. 186 (2011) 76---83.
[13] W. Huang, D. Li, J. Yang, Z. Liu, Y. Zhu, Q. Tao, K. Xu, J. Li, Y. Zhang,
Micropor. Mesopor. Mat. 170 (2013) 200-210.
[14] S. Garg, K. Soni, G. M.Kumaran, R. Bal, K. Gora-Marek, J.K. Gupta, L.D.
Sharma, G.M. Dhar, Catal. Today141(2009) 125-129.
[15] Z.Y. Yuan, B.L. Su, J. Mater. Chem. 16 (2006) 663-677.
[16] S. Vaudreuil, M. Bousmina, S. Kaliaguine, L. Bonneviot, Adv. Mater. 13 (2001)
1310-1312.
[17] J. Dhainaut, J.P. Dacquin, A.F. Lee, K. Wilson, Green Chem. 12 (2010) 296-303.
[18] P. Pengthamkeerati, T. Satapanajaru, P. Chularuengoaksorn, Fuel 87 (2008)
2469-2476.
[19] D.Y. Zhao, J.L. Feng, Q.S. Huo, N. Melosh, G.H. Fredrickson, B.F. Chmelka,
G.D. Stucky, Science 279 (1998) 548-552.
[20] L.D. White, C.P. Tripp, J. Colloid Interf. Sci. 227 (2000) 237-243.
[21] A.S.M. Chong, X.S. Zhao, J. Phys. Chem. B. 107 (2003) 12650-12657.
[22] X.G. Wang,K.S.K. Lin,J.C.C. Chan, S. Cheng, J. Phys. Chem. B. 109 (2005)
1763-1769.
[23] M. Kruk, M. Jaroniec, A. Sayari, Langmuir 13 (1997) 6267-6273.
[24] I. Nowak, Colloids Surf. A 241 (2004) 103-111.
Page 14 of 21
Accep
ted
Man
uscr
ipt
15
Table1. Textual property; and Langmuir and Freundlich isotherms parameters in the
phosphate adsorption by using MM-SBA and M-SBA.
Figure Captions:
Fig. 1. XRD patterns of M-SBA and MM-SBA.
Fig. 2. FT-IR spectra of M-SBA and MM-SBA.
Fig. 3. N2 adsorption-desorption isotherms of M-SBA and MM-SBA; and their
corresponding BJH pore size distribution plots (the inset).
Fig. 4. SEM images of M-SBA (a) and MM-SBA (b) at a low magnification (the inset
in (b) shows SEM image of MM-SBA at a high magnification); HR-TEM images of
M-SBA (c) and MM-SBA (d); TEM image of PS beads (e). The white arrows and
lines show the presence of mesopores; and the yellow line shows the observed
macropore in MM-SBA.
Fig. 5. (a) Langmuir adsorption isotherm and (b) Freundlich adsorption isotherm of
M-SBA and MM-SBA.
Fig. 6. Effect of contact time on the phosphate adsorption of M-SBA and MM-SBA.
Textual Property Langmuir Freundlich
Sample SBET
(m2/g)
DBJH
(nm)
VTotal
(cm3/g)
q0
(mg/g)
KL
(L/mg)
R2 n KF
(mg/g)
R2
M-SBA 219 4.98 0.32 16.21 0.449 0.944 3.88 5.69 0.978
MM-SBA 187 4.67 0.31 23.59 0.498 0.941 3.73 7.99 0.977
Page 15 of 21
Accep
ted
Man
uscr
ipt
16
Fig. 1.
Page 16 of 21
Accep
ted
Man
uscr
ipt
17
Fig. 2.
Page 17 of 21
Accep
ted
Man
uscr
ipt
18
Fig. 3.
Page 18 of 21
Accep
ted
Man
uscr
ipt
19
Fig. 4.
Page 19 of 21
Accep
ted
Man
uscr
ipt
20
Fig. 5.
Fig. 6.
Page 20 of 21
Accep
ted
Man
uscr
ipt
21
Research highlights
! ! Al-coordinated functionalized macroporous-mesoporous silica for phosphate removal
! ! It had the maximum adsorption capacity of 23.59 mg P/g
! ! Over 95% of the final adsorption capacity reached in the first 1 min