Morbond 170 Description Morbond 170 is a two component system that forms a rapid setting, easily placed castable on mixing, which can be brought quickly into service. Morbond 170 is a chamotte/bauxite composition exhibiting excellent thermal shock resistance. Specifically developed for heat containment applications, it is particularly recommended for burner quarls. Characteristics Bond Type Chemical Raw Material Base Chamotte/Bauxite Maximum Grain Size (mm) 4 Maximum Service Temperature °C 1700 Bulk Density Dried to 110°C kg/m 3 2500 Net Material Required kg/m 3 2450 Physical Properties Test Temperature (°C) Cold Crushing Strength (N/mm 2 ) Permanent Linear Change (%) 110 30 815 30 -0.1 1000 30 -0.1 MST 65 (1600) +/-0.5 (1600) Thermal Conductivity ASTM C417 (W/mK) @ mean temp 200°C Typical Chemical Analysis (%) Al 2 O 3 75 SiO 2 15 Fe 2 O 3 0.6 TiO 2 1.4 CaO 2 MgO 0.1 Na 2 O, K 2 O 0.2 P 2 O 5 5.4 BaO Modulus of Rupture (N/mm 2 ) 110°C 815°C Abrasion Resistance C704 (cm 3 ) 815°C Packaging Size (kg) Bag Weight 25 Pallet Size 1200 Water Addition % by Weight Accelerator Volume per Bag (l) 1 Bottle The values given herein are typical values obtained in accordance with accepted test methods and are subject to normal manufacturing variations. They are supplied as a technical service and are subject to change without notice. Therefore the data contained herein should not be used for specification purposes. Check with your Morgan Thermal Ceramics office to obtain current information or a Compliance Data Sheet where guaranteed property specifications are required.Before using these materials, it is strongly recommended that the installer consults Morgan Thermal Ceramics' storage and installation manual, copies of which are obtainable from Morgan Thermal Ceramics offices or distributors. Powered by TCPDF (www.tcpdf.org)
description
Morgan Ceramics
Transcript of Morbond 17
Morbond 170
Description
Morbond 170 is a two component system that forms a rapid setting, easily placed castable on mixing, which can be brought quickly into service.Morbond 170 is a chamotte/bauxite composition exhibiting excellent thermal shock resistance. Specifically developed for heat containmentapplications, it is particularly recommended for burner quarls.
Characteristics
Bond Type Chemical
Raw Material Base Chamotte/Bauxite
Maximum Grain Size (mm) 4
Maximum Service Temperature °C 1700
Bulk Density Dried to 110°C kg/m3 2500
Net Material Required kg/m3 2450
Physical Properties
Test Temperature (°C) Cold Crushing Strength (N/mm2) Permanent Linear Change (%)
110 30
815 30 -0.1
1000 30 -0.1
MST 65 (1600) +/-0.5 (1600)
Thermal Conductivity ASTM C417 (W/mK)
@ mean temp 200°C
Typical Chemical Analysis (%)
Al2O3 75
SiO2 15
Fe2O3 0.6
TiO2 1.4
CaO 2
MgO 0.1
Na2O, K2O 0.2
P2O5 5.4
BaO
Modulus of Rupture (N/mm2)
110°C
815°C
Abrasion Resistance C704 (cm3)
815°C
Packaging Size (kg)
Bag Weight 25
Pallet Size 1200
Water Addition
% by Weight Accelerator
Volume per Bag (l) 1 Bottle
The values given herein are typical values obtained in accordance withaccepted test methods and are subject to normal manufacturing variations.They are supplied as a technical service and are subject to change withoutnotice. Therefore the data contained herein should not be used forspecification purposes. Check with your Morgan Thermal Ceramics office toobtain current information or a Compliance Data Sheet where guaranteedproperty specifications are required.Before using these materials, it isstrongly recommended that the installer consults Morgan ThermalCeramics' storage and installation manual, copies of which are obtainablefrom Morgan Thermal Ceramics offices or distributors.