MIOX – Technical Information 02 / 02Pliolite S 5E – Solution weight % Aromat 100 40,0 Pliolite S...

REZEPTUREN

STARTING FORMULATIONS

KÄRNTNER MONTANINDUSTRIE GMBH

SCHLOSS 1

A-9400 WOLFSBERG

TEL: +43 (4352) 54535

FAX: +43 (4352) 54535-35

E-MAIL: [email protected]

WWW.KMI.AT

mailto:[email protected]

http://www.kmi.at/

MIOX – Technical Information 01 / 02

Alkyd-MIOX-Flowcoat

green weight % 1) Alftalat AM 649/60 30,0 2) White Spirit 3,0 3) MIOX SG 27,0 4) Talc ST 15 2,0 5) TiO22160 3,0 6) Chrome Oxide Green GN-M 3,0 7) Antifloat D 14 1,0 8) Thixatrol ST 0,7 _____________________________________________ 9) Alftalat AM 649/60 15,0 10) n-Butanol 2,0 11) Byketol spez. 2,0 12) Silres KX 0,3 13) White spirit 9,5 14) Drier 173 1,0 ____________________________________________ 15) Borchinox M2 0,5 100,0 Thinner weight % White Spirit 90,0 n- Butanol 10,0 100,0 The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.

MIOX – Technical Information 01 / 02 Manufacturing instructions: Stir 2) -8) into the resin solution and disperse for about 30 minutes at a peripheral speed of about 20 m/sec with high speed disperser (dissolver), temperature should not exceed 60 °C After cooling below 40 °C stir 9)-14), then 15). Typical properties: Colour green Solid matter % m/m 64,0 Binder % m/m 28,0 Pigment % m/m 36,0 VOC % m/m 36,0 Viscosity DIN-4-sec 90,0 Application Flow coating: Viscosity DIN-4-sec: 25 – 30


Pliolite-MIOX-Topcoat

(Acrylated Rubber) green

weight % Pliolite AC 80 Solution 40,0 Sojalecithin 0,7 MIOX SG 27,0 Talc ST 15 2,0 TiO2 3,0 Chrome Oxide Green GN-M 3,0 Thixatrol ST 1,0 ___________________________________________ Aromat 100 23,3 100,0 Plitolite AC 80 Solution weight % Aromat 100 40,0 Pliolite AC 80 40,0 Hordaflex LC 50 17,0 Epikote 828 3,0 100,0 The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.

MIOX – Technical Information 02/02

Typical properties: Colour green Solid matter % m/m 64,0 Binder % m/m 28,0 Pigment % m/m 36,0 VOC % m/m 36,0 Viscosity (Krebs) KU 85,0 – 95,0 Surface dry KU 2,0 Hard dry KU 6,0 Application - brush, airless spray - film thickness (dry) 80 µm - thinner, if necessary Aromat 100


Pliolite-MIOX-Primer (Acrylated Rubber)

red weight % Pliolite S 5E – Solution 33,0 Sojalecithin 0,7 Aromat 100 5,0 Zincphosphate ZNP/S 10,0 MIOX SG 20,0 Talc ST 15 4,0 Bayferrox Red 130 M 10,0 Thixatrol ST 1,0 ___________________________________________ Aromat 100 16,3 100,0 Pliolite S 5E – Solution weight % Aromat 100 40,0 Pliolite S 5E 40,0 ___________________________________________ Hordaflex LC 50 17,0 Epikote 828 3,0 100,0 The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.

MIOX – Technical Information 03/02

Typical properties: Colour red Solid matter % m/m Binder % m/m 21,5 Pigment % m/m 44,0 VOC % m/m 34,5 Viscosity (Krebs) KU 85,0 – 95,0 Surface dry KU 1,0 Hard dry KU 5,0 Application - brush, airless spray - film thickness (dry) 80 µm - thinner, if necessary Aromat 100


Topcoat for bituminous surfaces weight % 1) Asphalt solution (70 %) 40,0 2) MIOX SG 12,0 3) Minifiber 1,5 4) Perlite 3,0 5 Thixatrol ST 4,0 ___________________________________________ 6) Aluplaste (65 %) leafing 6,0 7) Mineral spirits 36,5 100,0 The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


2-Pack PUR Topcoat white

Component 1 1) Desmophen A 160/60 20,0 2) Methoxypropylacetate (MPA) 3,0 3) Acronal 700 L / 10 % MPA 0,5 4) TiO2 Kronos 2160 28,0 5) Thixatrol ST 0,8 ___________________________________________ 6) Desmophen A 160/60 33,0 7) Methoxypropylacetate (MPA) 4,0 8) Aromatic 100 9,7 9) Modaflow 1,0 100,0 Component 2 1) Desmodur N 75 90,0 2) Methoxypropylacetate (MPA) 10,0 100,0 Mixing ratio Component 1 : Component 2 = 7 : 1 (weight) The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


1-Pack PUR- Zinc-MIOX Primer grey

moisture curing (MC-PUR)

weight % 1) Additive MT 3,0 2) Desmodur E 14 2,5 3) Methoxypropylacetate (MPA) 4,0 4) Xylol 4,0 5) Acronal 700 L/10 % in MPA 0,2 6) Talc ST 15 3,0 7) MIOX SG 18,0 8) Zinc dust 48,0 9) Aerosil R972 0,8 ____________________________________________ 10) Desmodur E 14 6,0 11) Xylol 8,5 ____________________________________________ 12) Incozol 2 2,0 100,0 Manufacturing instructions: Stir 3) – 9) into the resin solution and disperse for about 20 minutes at a peripheral speed of about 20 m/sec in a high speed disperser, temperature should rise to 60 °C but not exceed. After cooling below 40 °C stir in 10) and 11), then add 12). Stir in 12) just before fill out to cans. Avoid contact with air moisture as far as possible. Use nitrogen atmosphere.

MIOX Technical Information 06 / 02

Typical properties Colour grey Solid matter % m/m 82,5 PVC % v/v 41,0 Binder % m/m 12,5 Pigment % m/m 70,0 VOC % m/m 17,5 Viscosity KU 60,0 – 70,0 Surface dry h 1,0 Hard dry h 4,0 Application: - airless spray - film thickness (dry): 75 – 100 µm - dilution, where necessery: Aromatic 100 Field of application: Primer for steel surfaces. Suppliers: 1) Bayer 2) Bayer 3) BASF 4) Naintsch/Luzenac 5) Kärntner Montanindustrie 6) Degussa 7) Bayer Industrial Copolymers Ltd (ICL) The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.

MIOX – Technical Information 06 A / 02

1 Pack PUR-Zinc-MIOX-Primer grey


weight % 1) Additive XP 7084 3,0 2) Desmodur XP 7080 2,5 3) Methoxypropylacetate (MP) 4,0 4) Xylene 4,0 5) Acronal 700 L/10 % in MPA 0,2 6) Vertal 3,0 7) MIOX SG 18,0 8) Zinc dust # 64 48,0 9) Aerosil R972 0,8 ___________________________________________ 10) Desmodur XP 7080 6,0 11) Xylene 8,5 ___________________________________________ 12) Incozol 2 2,0 100,0

Manufacturing instructions: Stir 3) – 9) into the resin solution and disperse for about 20 minutes at a peripheral speed of about 20 m/sec in a high speed disperser, temperature should rise to 60 °C but not exceed. After cooling below 40 °C stir in 10) and 11), than add 12). Stir in 12) just before fill out to cans. Avoid contact with air moisture as far as possible. Use nitrogen atmosphere.

MIOX – Technical Information 06 A / 02 Typical properties: Colour grey Solid matter % m/m 82,5 PVC % v/v 41,0 Binder % m/m 12,5 Pigment % m/m 70,0 VOC % m/m 17,5 Viscosity KU 60,0 – 70,0 Surface dry h 1,0 Hard dry h 4,0

Application: airless spray film thickness (dry): 3–4 mil dilution, where necessary Aromatic 100 Field of application: Primer for steel surfaces. Suppliers: 1) Bayer 2) Bayer 3) BASF 4) Vermont Talc 5) Kärntner Montanindustrie 6) Degussa 7) Bayer 8) Industrial Copolymers Ltd (ICL) The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


1-Pack-Pur-MIOX Sealer red

moisture curing (MC-PUR) weight % 1) Additive MT 10,0 2) Methoxypropylacetate (MPA) 7,0 3) Aromatic 100 2,0 4) Acronal 700 L/10 % in MPA 0,3 5) Talc ST15 7,0 6) Bayferrox Red 130 M 6,0 7) MIOX SG 17,0 8) Aerosil R972 1,0 ___________________________________________ 9) Desmodur E 14 3,5 10) Desmodur E 21 30,0 11) Aromatic 100 14,2 ___________________________________________ 12) Incozol 2 2,0 100,0 Manufacturing instructions: Stir 2) – 8) into the resin solution and disperse for about 30 minutes at a peripheral speed of about 20 m/sec in a high speed disperser, temperature should rise to 60 °C but not exceed. After cooling below 40 °C stir in 9) – 11) Stir in 12) just before fill out in cans. Avoid contact with air moisture as far as possible. Use nitrogen atmosphere.

MIOX – Technical Information 07 / 02 Typical properties: Colour red Solid matter % m/m 76,0 PVC % v/v 17,0 Binder % m/m 46,0 Pigment % m/m 30,0 VOC % m/m Viscosity KU 60,0 – 70,0 Surface dry h 1,0 Hard dry h 4,0 Application - brush - film thickness (dry) 25 - 40 µm - dilution, where necessary Aromatic 100 Field of application: Suitable on steel surfaces after power tool cleaning or manual cleaning as well as on old paint layers for maintenance coatings. This sealer penetrates into residue of rust, seals pores and reinforces the old paint layer. Suppliers: Bayer BASF Naintsch/Luzenac Bayer Kärntner Montanindustrie Degussa Bayer Bayer Industrial Copolymers Ltd. ( ICL) The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


Typical properties:

Colour red Solid matter % m/m 76,0 PVC % v/v 17,0 Binder % m/m 46,0 Pigment % m/m 30,0 VOC % m/m Viscosity KU 60,0 – 70,0 Surface dry h 1,0 Hard dry h 4,0 Application - brush - film thickness (dry) 1 mil - dilution, where necessary Aromatic 100 Field of application: Suitable on steel surfaces after power tool cleaning or manual cleaning as well as on old paint layers for maintenance coatings. This sealer penetrates into residue of rust, seals pores and reinforces the old paint layer. Suppliers: Bayer BASF Bayer Kärntner Montanindustrie Degussa Bayer Industrial Copolymers Ltd. ( ICL) The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


1-Pack-PUR-MIOX Sealer red


weight % 1) Additive XP 7084 10,0 2) Methoxypropylacetate (MPA) 7,0 3) Aromatic 100 2,0 4) Acronal 700 L/10 % in MPA 0,2 5) Talc 7,0 6) Bayferrox Red 130 M 6,0 7) MIOX SG 17,0 8) Aerosil R972 0,8 ___________________________________________ 9) Desmodur XP 7080 33,0 10) Aromatic 100 15,0 ___________________________________________ 11) Incozol 2 2,0

100,0

Manufacturing instructions: Stir 2) – 8) into the resin solution and disperse for about 30 minutes at a peripheral speed of about 30 m/sec in a high speed disperser, temperature should rise 60 °C but not exceed. After cooling below 40 °C stir in 9) – 10). Stir in 11) just before fill out to cans. Avoid contact with air moisture as far as possible. Use nitrogen atmosphere.


1-Pack PUR-MIOX Intermediate Coat grey


weight % 1) Desmodur E 21 16,0 2) Methoxypropylacetate (MPA) 4,0 3) Aromat 100 4,0 4) Incozol 2 2,0 5) Talc ST 15 9,0 6) MIOX SG 34,0 7) TiO2 Kronos 2160 3,5 8) Acronal 700 L/10 % in (MPA) 0,2 9) Aerosil R 972 1,3 _________________________________________

10) Desmodur E 14 4,5 11) Incozol 4 2,5 12) Methoxypropylacetate (MPA) 6,0 13) Aromat 100 12,0

14) Incozol 2 1,0

100,0 Manufacturing instructions: Stir 2) – 9) into the resin solution and disperse for about 20 minutes at a peripheral speed of about 20 m/sec in a high speed disperser, temperature should rise to 60 °C but not exceed. After cooling below 40 °C stir in 10) – 13). Stir in 14) just before fill out of cans. Avoid contact with air moisture as far as possible. Use nitrogen atmosphere.

MIOX – Technical Information 08 / 02 Typical properties:

Colour silver-grey Solid matter % m/m 72,0 PVC % v/v 31,0 Binder % m/m 27,0 Pigment % m/m 45,0 VOC % m/m 28,0 Viscosity (Krebs) KU 80,0 – 90,0 Surface dry h 2,0 Hard dry h 6,0 Application: brush, spray, airless spray film thickness (dry): 80 – 100 µm thinner, where necessary Aromatic 100 Field of application: Intermediate coat on Sealer FG 38/I (38/II) or Primer FG 39/I (39/II) or Primer DrP 090298. Suppliers: 1) Bayer 4) Industrial Copolymers Ltd (ICL) 5) Naintsch (Luzenac) 6) Kärntner Montanindustrie 7) Kronos 8) BASF 9) Degussa 10) Bayer 11) Industrial Copolymers Ltd. (ICL) The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.

MIOX Technical Information 09 / 02

MIOX-Primer red

for galvanized steel and aluminium weight % 1) Plexisol PM 559/50 40,0 2) Soyalecithin 0,5 3) Adhesion Resin LTH 3,0 4) Resamin HF 450 2,0 5) MIOX SG 13,0 6) Talc 5,0 7) Heucophos ZP0 10,0 8) Bayferrox Red 130 M 8,0 9) Thixatrol ST 0,8 ___________________________________________

10) Aromat 100 17,7

100,0 Manufacturing instructions: Stir 2) – 9) into the resin solution 1) and then disperse for about 20 – 30 minutes at a peripheral speed of about 20 m/sec with a high speed disperser (dissolver). Caution: The temperature must not exceed 50 °C After cooling below 35 °C stir in 10). The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


MIOX- Topcoat green

for galvanized steel and aluminium weight % 1) Plexisol PM 559/50 40,0 2) Soyalecithin 0,5 3) Adhesion Resin LTH 3,0 4) Resamin HF 450 2,0 5) MIOX SG 30,0 6) Talc 2,0 7) Chrome Oxide Green GN-M 2,0 8) TiO2 Kronos 2160 2,0 9) Thixatrol ST 0,8 ___________________________________________ 10) Aromat 100 17,7 100,0 Manufacturing instructions: Stir 2) – 9) into the resin solution 1) and then disperse for about 20 – 30 minutes at a peripheral spend of about 20 m/sec with a high speed disperser (dissolver) Caution: The temperature must not exceed 50 °C After cooling below 35 °C stir in 10). The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


Thinner: Aromat 100 or Xylene Typical properties: Colour green Solid matter % m/m 61,1 Binder % m/m 25,1 Pigment % m/m 36,0 VOC %m/m 38,9 Viscosity (Krebs) KU 80,0 – 90,0 Surface dry h 2,0 Hard dry h 6,0 Application: - brush, airless spray - film thickness (dry): 2 x 80 µm (=160µm) Field of application: Galvanizded steel and aluminium The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.

MIOX-Technical Information 11 / 02

Micaceous Iron Oxide Alkyd-MIOX-Flowcoat

green

weight % 1) Alftalat AM 649/60 30,0 2) White Spirit 3,0 3) MIOX SG 27,0 4) Talc ST 15 2,0 5) TiO2 2160 3,0 6) Chrome Oxide Green GN-M 3,0 7) Antifloat D 14 1,0 8) Thixatrol ST 0,7 ___________________________________________ 9) Alfalat AM 649/60 15,0

10) n-Butanol 2,0 11) Byketol spez. 2,0 12) Silres KX 0,3 13) White spirit 9,5 14) Drier 173 1,0

___________________________________________

15) Borchninox M2 0,5

100,0 Thinner weight % White spirit 90,0 n-Butanol 10,0 100,0 The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.

MIOX – Technical Information 11 / 02 Manufacturing instructions: Stir 2) – 8) into the resin solution and disperse for about 30 minutes at a peripheral speed about 20 m/sec with a high speed disperser (dissolver), temperature should not exceed 60 °C. After cooling below 40 °C stir 9) – 14), then 15). Typical properties: Colour green Solid matter % m/m 64,0 Binder % m/m 28,0 Pigment % m/m 36,0 VOC % m/m 36,0 Viscosity DIN-4-sec 90,0 Application: Flow coating: Viscosity DIN-4-sec: 25 – 30


Epoxyester – MIOX Topcoat silvergrey

1) Duroxyn EF 900 / 50 X 20,0 2) MIOX SG 30,0 3) Talc ST 15 5,0 4) Alupaste Stapa 4 3,0 5) Thixatrol ST 0,5 ___________________________________________ 6) Duroxyn EF 900 / 50 X 35,0 7) Aromatic 100 5,5 8) Co-Siccativ 6 % 0,5 9) Antiskin Borchinox M 2 0,5 100,0 The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


Epoxy-MIOX Primer high solid

grey Component 1 weight % 1) Epikote 828 14,0 2) Plastopal EBS 400 1,5 3) n-Butanol 3,0 4) Xylene 6,0 5) MIOX SG 37,0 6) Zincphosphate 15,0 7) Talc ST 15 5,0 8) TiO2 Kronos 216C 5,0 9) Thixatrol ST 1,0 ___________________________________________ 10) n-Butanol 2,0 11) Xylene 10,5 100,0 Component 2 /1 Versamid 115/70 Mixing ratio: Comp. 1 : Comp. 2 = 4 : 1

or

/2 Euredur 43 S Mixing ratio: Comp: 1 : Comp. 2 = 12 : 1

or

/3 Cardolite NC 541/90 X 65,0 Necires EPXL 35,0 100,0 Mixing ratio: Comp. 1 : Comp. 2 = 6 : 1

or

/5 Euredur 30/55 Mixing ratio: Comp. 1 : Comp. 2 = 3,6 : 1 The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


1-Pack PUR-MIOX Top Coat green


weight % Vesticoat UT 994 22,0 Methoxypropylacetate (MPA) 4,0 Incozol 2 2,0 Talc ST 2 3,0 MIOX SG 34,0 TiO2 Kronos 2160 2,0 Chrome Oxide Green GNM 2,0 Acronal 700 L/10 % in MPA 0,3 Aerosil R972 1,5 Vesticoat UT 994 15,0 Incozol 4 2,0 Aromatic 100 11,2 Incozol 2 1,0 100,0 Manufacturing instructions: Stir 2) – 9) into the resin solution and disperse, for about 20 minutes at a peripheral speed of about 20 m/sec in a high speed disperser. Temperature should not exceed 60 °C. Then stir in 10) – 13). Stir in 14) just before fill out to cans. Avoid contact with air moisture as far as possible. Use nitrogen atmosphere.

MIOX-Technical Information 14 / 02

Typical properties: Colour green Solid matter % m/m 74,0 Binder % m/m 22,0 Pigment % m/m 33,0 VOC %m/m 41,0 Viscosity KU 80,0 – 90,0 Surface dry h 2,0 Hard dry h 6,0 Application: brush, spray, airless spray film thickness (dry): 80 µm thinner, where necessary: Aromatic 100 Field of application: Topcoat on intermediate coat FG 40/I or DrP 100298 Suppliers: 1) Hüls 3) Industrial Copolymer Ltd. (ICL) 4) Naintsch (Luzenac) 5) Kärntner Montanindustrie 6) Kronos 7) Bayer 8) Basf 9) Degussa 11) Industrial Copolymers Ltd. (ICL) The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


Alkyd-MIOX Topcoat carline thistle green

weight % 1) Alftalat AM 649/60 30,0 2) White Spirit 3,0 3) MIOX SG 32,5 4) Talc ST 15 2,0 5) Chrome Oxide Green GN-M 3,5 6) Thixatrol ST 0,7 7) Alupaste Stapa 4 2,5 8) Alftalat AM 649/60 15,0 9) White Spirit 9,3 10) Octa Soligen 173 1,0 11) Borchinox M2 0,5 100,0 Binder % m/m 28,- Pigment % m/m 39,5 Solid matter % m/m 67,5 VOC % m/m 32,5 PVC % v/v 26,0 Viscostiy DIN-6-mm 50 – 60 Surface dry h 2 Hard dry h 8 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


MIOX Top Coat decorative based on acrylic emulision

water reducible black

weight % I II III 1) Acronal S760 18,0 18,0 18,0 2) H2O deion. 2,0 2,0 2,0 3) Korrosionsinhibitor L1 0,2 0,2 0,2 4) Butyl glycol 1,0 1,0 1,0 5) White Spirit (180-210°C) 2,0 2,0 2,0 6) Agitan 280 0,3 0,3 0,3 7) Borchigen ND 0,5 0,5 0,5 8) MIOX SG 32,0 - - 9) MIOX DB - 32,0 -

10) MIOX ME - - 32,0 11) Grafit MP 88/92 5,0 5,0 5,0 12) Acronal S 760 32,0 32,0 32,0 13) Agitan 295 0,3 0,3 0,3 14) NH4OH conc. 0,2 0,2 0,2 15) H2O deion. 5,5 5,5 5,5 16) Borchigel LW 44/50% Butyl glycol 1,0 1,0 1,0

100,0 100,0 100,0 Solid matter % m/m 57,0 % PVC 28,0 % Binder % m/m 25,0 % Pigment % m/m 37,0 % Viscosity 70 – 80 KU (Krebs Unit) pH 9,5 I: fine structure II: medium structure III: coarse structure The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


Topcoat waterbased

green

weight %

Acronal S 760 18,0 H2O VE 5,0 Korrosionsihibitor L1 0,2 Texanol 2,0 Agitan 280 0,3 Borchigen ND 0,5 TiO2 Kronos 2190 3,0 Chromoxidgrpn GN-M 3,0 MIOX SG 30,0 Talk ST 15 3,0 Acronal S 760 32,0 Agitan 295 0,3 Butylglykol 1,0 Borchigel LW 44 0,4 NH4OH konz. 0,3 H2O VE 1,0 100,0 Binder 25 % Pigment 39 % FK 64 % PVK 25 % PH 8–9 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Primer based on acrylic emulsion

water reducible red

weight % Acronal S 760 18,0 H2O deion. 7,0 Borchigen ND 0,5 Korrosionsinhibitor L1 0,2 Texanol 2,0 Agitan 295 0,3 Talc ST 15 3,0 Heucophos ZPZ 9,0 Bayferrox Red 130 M 7,0 MIOX SG 15,0 Acronal S 760 32,0 Agitan 295 0,3 Borchigel LW 44 0,4 NH4OH conc. 0,3 H2O deion. 5,0 100,0 Binder 25 % Pigment 34 % Solid matter 59 % PVC 24 % pH 8,5 – 9,5 The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


PRIMER

waterbased red brown

weight % Acronal S 760 18,0 H2O VE 7,0 Borchigen ND 0,5 Korrosionsinhibitor L1 0,2 Texanol 2,0 Agitan 295 0,3 Talk ST 15 3,0 Heucophos ZPZ 9,0 Bayferrox Rot 130 M 7,0 MIOX SG 15,0 Acronal S 760 32,0 Agitan 295 0,3 Borchigel LW 44 0,4 NH4OH konz. 0,3 H2O VE 5,0 ______ 100,0 Binder 25 % Pigment 34 % FK 59 % PVK 24 % PH 8 – 9 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Stoving enamel for alu black

1. 2. Viacryl SC 420/50 24,0 24,0 Solvesso 100 6,0 6,0 MIOX AS 22,0 - MIOX SG - 22,0 Grafit MP 88/92 3,0 3,0 Thixatrol ST 0,5 0,5 Viacryl SC 420/50 20,0 20,0 Solvesso 100 14,0 14,0 Haftharz LTW/60 3,0 3,0 Modaflow 0,5 0,5 100,0 100,0 Variation 1: fine structur Variation 2: middle coarse structur Stoving conditions: 25 min/160 °C Binders: 25 % Pigment 25 % FK 50 % Viscosity: 60 – 90 DIN-4-Sek As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility.The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Alkyd – MIOX Topcoat Antique effect dark grey

weight %

1) Vialkyd AL 633/60 43,0 2) MIOX SG 40,0 3) Talc ST micro 5,0 4) Thiaxotrol ST 0,7 5) White Spirit 8,5 6) Octa Soligen Drier 173 1,0

7) White Spirit 0,7 8) Stapa Bronze 300 Pale Gold (03) 0,6

9) Borchinox M2 0,5 100,0 Manufacturing instructions: Stir 2) – 4) into the resin solution 1) and then disperse for about 20–30 minutes at a peripheral speed of about 15–20 m/sec in a high speed disperser. Then let down under stirring 5) and 6). Stir 8) into 7) and stir it into 1) – 6) . Then let down 9) As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Typical properties: Colour dark grey Solid matter % m/m 72,5 % Binder % m/m 26,5 % Pigment % m/m 46,0 % VOC % m/m 27,5 % Viscosity sec (DIN 53211) 50 – 60 (DIN 6 mm) Surface dry 3 h Hard dry 10 h Application - brush, air spray, airless spray, roller coating - film thickness (dry): 50–80 µm Suppliers: 1) Vianova Resine 2) Kärntner Montanindustrie 3) Naintsch 4) Rheox 5) Borchers 6) Eckart Werke 7) Borchers As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


2-Pack-Ethylsilicate Zinc/MIOX Primer grey

Component 1 A B 1) Hydrolysate 4 16,0 14,0 (Silicate 2253) 2) Pioloform solution BN18/25% 3,0 3,0 3) Fumed Silica HDK H 15 2,0 1,5 4) MIOX SF 27,0 15,0 5) Hydrolysate 4 2,0 4,0 6) Methoxypropylacetate 3,0 3,0 7) Xylene 2,0 2,0 55,0 42,5 Component 2 8) Zinc dust (Zincoli 601) 45,0 57,5

100,0 100,0 Manufacturing instructions Stir 3) and 4) into the resin solution 1) and 2) and disperse for about 20 – 30 minutes at a peripheral speed of about 20 m/sec in a high speed disperser, then stir in 5) – 7). Zinc dust 8) as component 2 is to be stirred into component 1) short before using the paint. The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.


Alkyd – MIOX Single coat

green weight %

1) Alftalat AM 649/60 15,0 2) Bentone 34 – Antiterra 203 – Xylene 3,0

10 : 5 : 85 3) Resamin HF 450 3,0 4) Talc ST 15 5,0 5) Zinc Phosphate Sicor ZNP/M 10,0 6) MIOX SG 18,0 7) Chrome Oxide Green GN-M 4,0 8) TiO2 Kronos 2160 6,0 9) Thixatrol ST 0,8

10) Alftalat AM 649/60 27,0 11) Co-drier 6% 0,3 12) Pb-drier 24 % 0,8 13) White spirit 6,6

14) Borchinox M2 0,5 100,0 Manufacturing instructions: Stir 2) – 9) into the resin solution 1) and then disperse for about 30 minutes at a peripheral speed of about 15 – 20 m/sec in a high speed disperser. Caution: The temperature must not exceed 60 °C. Add then 10) – 13) while stirrling and then stir in 14) As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.

MIOX – Technical Information 22 / 02 Thinner: White Spirit Typical properties: Colour green Solid matter % m/m 72,0 Binder % m/m 29,0 Pigment % m/m 43,0 VOC % m/m 28,0 Viscosity (DIN Flow Cup 6mm) sec 50–60 Surface dry h 3,0 Hard dry h 10,0 Application: - brush, air spray, airless spray, - film thickness (dry): 80–100µm Field of Application: General purpose painting both on steel surfaces and on old paint layers for maintenance coatings. As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


2-Pack Epoxy-Zinc/MIOX Primer grey

Component 1 weight % Epikote 1001/75 7,7 Plastopal EBS 400 B 0,5 Aerosil R 972 1,0 n-Butanol 1,0 Zinc dust 58,0 MIOS AS 25,0 Xylene 6,8 100,0 Component 2 Euredur 424 100,0 Mixing ratio Component 1 : Component 2 = 10 : 1 Thinner: Xylene Typical properties: Colour grey Solid matter % m/m 86,0 Binder % m/m 10,0 Pigment % m/m 76,0 VOC % m/m 14,0 Viscosity ( DIN 53211) 60 – 80 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Alkyd-MIOX Primer red

weight %

1) Alftalat AM 440/60X 27,0 2) Talc 8,0 3) Zinc Phosphate 10,0 4) MIOX SG 22,0 5) Bayferrox Red 130 M 10,0 6) Thixatrol ST 0,8 7) n-Butanol 3,0

8) Xylene 8,2 9) Alftalat AM 440/60X 10,0

10) Octa Soligen Lead 24 0,5 11) Octa Soligen Cobalt 6 0,2

12) Borchinox M2 0,3 100,0 Manufacturing instructions: Stir 2) – 7) into the resin solution and disperse for about 20 minutes at a peripheral speed of about 15–20 m/sec in a high speed disperser, temperature must not exceed 55 °C. After cooling below 40 °C stir in 8) – 11), than add 12). Caution: Do not use a perl- or sandmill for grinding MIOX, the lamellar platelets of MIOX would be destroyed in such a milling process. As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Alkyd-MIOX Primer red

weight %

1) Alftalat AM 440/60 X 27,0 2) Bentone 34 – Borchigen PB 60 – Xylene 3,0

10 : 5 : 85 3) Talc ST 20 8,0 4) Zinc Phosphate Sicor ZNP/M 10,0 5) MIOX AS 22,0 6) Bayferrox Red 130 M 10,0 7) Thixatrol ST 0,3 8) n-Butanol 3,0

9) Xylene 5,7 10) Alftalat AM 440/60x 10,0 11) Octa Soligen Lead 24 0,5 12) Octa Soligen Cobalt 6 0,2

13) Borchinox M2 0,3 100,0 Manufacturing instructions: Stir 2) – 8) into the resin solution and disperse for about 20 minutes. at a peripheral speed of about 15 – 20 m/sec in a high speed disperser, temperature must not exceed 55 °C. After cooling below 40 °C stin in 9) – 12), then add 13).58--0 Caution: Do not use a perl- or sandmill for grinding MIOX, the lamellar platelets of MIOX would be destroyed in such a milling process. As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.

MIOX – Technical Information 25 / 02 Suppliers: 1) Hoechst 2) Bentone 34 Rheox 3) Borchigen PB 60 Borchers 4) Naintsch 5) BASF 6) Kärntner Montanindustrie 7) Bayer 8) Rheox 9) Hoechst 10) Borchers 11) Borchers 12) Borchers As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Topcoat heat resistant Silicone-MIOX

weight % Silres REN 60 45,0 Aerosil R 972 1,0 MIOX AS 30,0 Talc 5,0 Aluminium paste n. 1. 4,0 Xylene 15,0 100,0 Typical properties: Solid matter % m/m 66 Binder % m/m 27 Pigment % m/m 39 VOC % m/m 34 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.

MIOX – Technical Inforamtion 27 / 02

Intermediate Coat heat resistant Silicone-MIOX

weight % Silres REN 60 40,0 Aerosil R 972 1,0 MIOX AS 35,0 Talc 7,0 Aluminium paste n. 1. 1,0 Xylene 16,0 100,0 Typical properties: Solid matter % m/m 68 Binder % m/m 24 Pigment % m/m 44 VOC % m/m 32 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Primer heat resistant Silicone-zinc dust

weight % Silres REN 60 10,0 Aerosil R 972 1,5 Zinc dust 65,0 Xylene 24,5 100,0 Typical properties: Solid matter % m/m 72,5 Binder % m/m 6,0 Pigment % m/m 66,5 VOC % m/m 33,5 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the enduser to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


HIGH BUILD VINYL

Micaceous Iron Oxide High Performance Coating

HIGH BUILD VINYL (Copolymers of vinyl chloride and vinyl isobutyl ether)

Top coat. Single pack. weight % MIOX SG 38,0 Aluminium paste 1,5 Talc 6,0 Chromium oxide green 2,5 Zinc oxide 2,5 Thixotrope gel 0,3 Laroflex MP 15 (BASF) 20,0 Phtalopal LR8686 (BASFf) 3,0 Chlorinated paraffin plasticiser 1,7 (e.g. Cereclor 42, ICI) Xylene 8,5 Ethoxypropylacete 5,0 Butylacetate 11,0 100,0 Dissolve resins and plasticiser in bulk of solvent blend. Incorporate pigments and thixotorpe in high speed disperser but add aluminium pigment by slow mixing. Pigment volume concentration (mixed) = 36 % Volume solids (mixed) = 48 % As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


URETHANE – ALKYD

Micaceous Iron Oxide High Performance Coating URETHANE-ALKYD Intermediate and top coat. Single pack.

weight % MIOX SG 47,0 Aluminium Paste or titanium dioxide 3,0 Talc 7,0 Thixotrope gel 2,0 Resins solids* 18,0 White spirit 21,0 Driers and antiskin 2,0 100,0

*A 2.5/1 blend of medium/long oil alkyd and urethane alkyd (eg. Unithane 655W – Cray Valley) is recommended.

Process in high speed disperser. Add aluminium paste by slow mixing. Pigment volume concentration = 41% Volume solids = 50% As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


EPOXY-POLYAMIDE

Micaceous Iron Oxide High Performance Coating

EPOXY – POLYAMIDE (high solids) Intermediate and top coat. Two pack. weight % BASE MIOX SG 45,0 Titanium dioxide 4,0 Talc 7,2 Thixotrope gel 1,7 Liquid epoxy (Epoxy-molar mass 235-263) 22,5 e.g. Epikote 834-X80, 80% in xylene, Shell Xylene 7,2 ACTIVATOR Polyamide resin ( 70% in xylene) 12,4 (amine value 210-220) (e.g. Versamid 115X, Cray Valley) 100,0 Mix epoxy resin in half xylene. Incorporate pigments and thixotrope in high speed disperser. Add remaining solvent by slow mixing. Base and activator are mides together immediately before application. Pigment volume concentration (mixed) = 35% Volume solids (mixed) = 69% As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


CHLORINATED RUBBER Micaceous Iron Oxide High Performance Coating

CHLORINATED RUBBER Intermediate and top coat. Single pack. weight % MIOX SG 25,0 Aluminium paste or titanium dioxide 4,0 Talc 5,0 Zinc oxide 1,0 Chlorinated rubber (low viscosity grade) 14,5 Chlorinated paraffin plasticiser (e.g. Cereclor S52, ICI) 5,7 Thixotrope gel 1,5 Epoxy stabiliser (e.g Epikote 828, Shell) 0,5 Xylene 33,8 Solvesso 100 9,0 100,0 Dissolve resin in bulk of solvent Incorporate pigment in high speed disperser but add aluminium pigment by slow mixing. Pigment volume concentration = 35 % Volume solids = 35 % As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


ACRYLATED RUBBER

high performance coating

ACRYLATED RUBBER (Styrene-acylic copolymer) Intermediate and top coat. Single pack. weight % MIOX SG 39,5 Aluminium paste or titanium dioxide 3,0 Talc 7,0 Pliolite AC 80 (Goodyear) 10,0 Pliolite AC 4 (Goodyear) 4,0 Chlorinated paraffin plasticiser 4,0 (eg. Hordaflex LC 60 – Hoechst) Xylene 6,0 Naphtha solvent 10,5 Mineral spirit 140-170 16,0 100,0 Dissolve resins and plasticisers in bulk of solvent. Incorporate pigments in high speed disperser but add aluminium pigment by slow mixing. Pigment volume concentration = 40 % Volume solids = 40 % As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


MOISTURE CURED POLYURETHANE Micaceous Iron Oxide High Performance Coating

MOISTURE CURED POLYURETHANE (Aromatic polyisocyanate) Intermediate and top coat. Single pack. N.B. The production process has to be strictly controlled to avoid instability. Please also refer to detailed notes provided by Bayer AG, D – Leverkusen. weight % I. 1-Methoxypropylacetate-2 12,30 White spirit 6,15

Additive MT (Bayer) 6,32 HDK-H15 (Wacker Chemie) 1,47 Desmodur E 14 (Bayer) 4,18 Accronal 700L (BASF) 0,22 (10% in ethyl acetate) MIOX SG 34,38 Titanium dioxide * 4,00 Talc 12,20 II. Desmodur E1361 (Bayer) 17,21 (61 % in solvent mixture) III. Additive OF (Bayer 1,57 100,00 * Alternatively, aluminium paste if specification allows. Aluminium should be mixed in with (2)

Process in high speed disperser in the following sequence: I. Run for 15 – 30 mins at 20 m/s. A temperature of 50–60°C is necessary for dewatering. Hold back a small amount of solvents for final viscosity adjustment. II. Mix in the resin at low speed. III. Finally, mix in Additive OF (viscosity stabiliser) and leave to stand in sealed container for 24 hrs blankened with inert gas. It is then stirred, adjusted for viscosity and filled into an airtight container using a blanket or inert gas. Pigment volume concentration = 40 % Volume solids = 50 % As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


WATER BORNE ACRYLIC BASED ON GOODYEAR PLIOTEC LS1

GUIDE FORMULATION FOR HIGH PERFORMANCE COATING WATER BORNE PAINT BASED ON GOODYEAR PLIOTEC LS1 For application over primed steelwork. % w / w Raw Material Supplier BINDER PLIOTEC LS 1 49,0 Goodyear Chemicals RHEOLATE 255 0,1 NL Chemicals RHEOLATE 278 0,4 NL Chmicals KODAFLEX TX 1 B 3,0 Eastmann Kodak PIGMENT / EXTENDER MIOX SG 24,0 KMI TIOXIDE RHD2 2,0 Tioxide BLANC FIXE N 8,0 Sachtleben TALC OR MICA POWDER 5,0 Omya UK ADDITIVES DISPERBYK 181 0,2 BYK Chemie SURFYNOL 104 E 0,3 Air Products NOPCO 8034 0,1 Henkel COALESCENTS DOWANOL DPNB 2,5 Dow Chemicals DOWANOL DPM 0,5 Dow Chemicals DIMETHYLAMINO ETHANOL 0,5 Union Carbide WATER 4,4

MANUFACTURING PROCEDURE Use high speed disperser (dissolver)

1. Charge vessel with Pliotec LS1 2. Premix Disperyk 181 with Surfinol 104E and stir into Pliotec.

Add Nopco 8034 and rapid mix until homogenous. 3. At low speed add pigment/extender. Increase rate gradually and run until fully

dispersed.

Temperature must not exceed 50 °C 4. Mix in remaining Pliotec. 5. Premix coalescents and Kodaflex TX1B. Add to bulk while stirring. 6. Add water and Rheolate and run at high speed until completely dispersed. Properties: PVC = 30 % Solids content, wt = 59,55 Density = 1,4 % Volume = 45 % As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Viscosity for flow-coating: 30 – 40 DIN-4-sek (Ford cup No. 4) Note: It would be useful to use the pigments 7), 8) and 9) in form of pastes. The whole batch then can be produced only by using a high speed disperser (no grinding) Suppliers: 1) Jäger 2) Röhm 3) Bentone Rheox

Antiterra 203 Byk 4) Degussa 5) Langer 6) Kronos 7) Bayer 8) Bayer 9) Degussa

10) Naintsch 11) Kärntner Montanindustrie 12) Benda-Lutz 13) Wacker 14) Byk 15) Borchers 16) Borchers As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Alkyd/Acryl-MIOX Topcoat concrete-grey, ca. RAL 7033

Flow coat paint

weight %

1) Jägalyd spez. BB/60 38,0 2) Plexigum P28/40 in Solvesso 100 20,0 3) Bentone 34 – Antiterra 203 – Xylene 3,0

10 : 5 : 85 4) Aerosil R972 0,3 5) Antifloat D14 0,4 6) TiO2 Kronos 2160 5,0 7) Chrome oxide green GN-M 1,0 8) Bayferrox yellow 920 0,5 9) Carbon black Printex A 0,1

10) Talc ST 20 5,0 11) MIOX SG 20,0 12) Alupaste Blitz 1041 0,2

13) K-Lack 0,5 14) Byketol spezial 2,0 15) n-Butanol 1,5 16) Drier 173 1,0 17) White spirit 1,0

18) Borchinox M2 0,5

100,0 Thinner: White spirit 93,- n-Butanol 7,- 100,- As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Alkyd-MIOX Top Coat black waterreducible

weight % Resydrol AY 586 W/38 d 50,0 NH4OH 10 % 1,0 Additol XL 270 0,4 Additol VXW 4990 0,6 Additol XW 329 0,3 Tego Foamex 1488 0,1 Bentone SD 2 0,4 Micaceous Iron Oxide MIOX SG 30,0 Special Black 100 0,5 Talcum ST 15 5,0 White spirit 3,0 H2O, deion 8,2 Borchinox M2 0,5 100,0 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


1-K-PUR-Zincdust-MIOX-Primer weight % Desmodur E14 3,5 Desmodur E1361 12,0 Additiv TI 1,0 Bentone 34 – Antiterra 203 – P. 5,0 Aerosil R 972 0,5 MIOX SF 25,0 ( - ) Zincdust VM4 P16 45,0 (82- ) Acronal 700 L/10% 0,15 Additiv OF 1,0 Methoxidpropylacetat 4,0 Solvesso 100 3,85 100,0 (112-) Bentone-Paste Xylol 85,0 Bentone 34 10,0 Antiterra 203 5,0 100,0 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Alkyd-MIOX Topcoat grey

water reducible weight % Resydrol AY 586 W / 38 d 50,0 NH4OH 10% 1,0 Additol XL 270 0,4 Additol VXW 4990 0,6 Additol XW 329 0,3 Borchinox M2 0,5 Tego Foamex 1488 0,1 Bentone SD 2 0,4 MIOX SG 27,5 TiO2 5,0 Talc (15 µm) 3,0 White spirit 3,0 Water, deion. 8,2 100,0 pH: 8,5–9,5 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


PVC- Acrylic-MIOX Primer red

High Build Coating weight %

1) Shell Sol A 4,00 2) Shell Sol AB 3,00 3) Dowanol PM 6,00 4) Laroflex MP 25 8,50 5) Palatinol AH 0,80 6) Plastigen G 0,40 7) Desavin 0,80 8) Haftharz LTW/60 4,00 9) Epikote 828 0,60

10) Unithane 373 SU/60 4,00 11) Plexisol P 627/50 6,50 12) Bentone 34–Borchigen PB 60–Shell Sol A 5,00

10 : 5 : 85 13) Thixatrol ST 0,60 14) MIOX SG 20,00 15) Zincphosphate 10,00 16) Talc ST micro 5,00 17) Bayferrox Red 130 M 10,00 18) Octa Soligen Lead 24 0,08 19) Shell Sol A 10,72

100,00 Manufacturing instructions: Stir 4) into 1) – 3) until it is dissolved. Then add 5) – 11) while strirring. Then add 12) – 17) while stirring. Then disperse for about 30 minutes at a peripheral speed of about 20 m/sec in a high speed disperser (no perl mill ), then add 18) and 19) As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


1-K-PUR-Zincdust-MIOX-Primer

Desmodur E14 3,5 Desmodur E1361 12,0 Additiv TI 1,0 Bentone 34 – Antiterra 203 – P. 5,0 Aerosil R 972 0,5 MIOX SF 25,0 Zincdust VM4 P16 45,0 Acronal 700 L/10% 0,15 Additiv OF 1,0 Methoxipropylacetat 4,0 Solvesso 100 3,85 100,0 Bentone-Paste Xylol 85,0 Bentone 34 10,0 Antiterra 203 5,0 100,0 As Kärntner Montanindustrie GmbH are not always aware of the conditions of use of this product, sufficient work should be carried out by the end user to ensure that the performance is adequate in each specific situation. KMI has taken every possible care to ensure that the information contained herein is correct in all aspects. However KMI cannot be held responsible for any errors or omminssions which may be found herein, nor will it accept responsibility for any use which may be made of the information, the same having been given in good faith, but without legal responsibility. The information presented above comprises typical data and should not be taken as representing a specification. Specification values are available separately.


Acrylic decorative topcoat, waterbased

weight % Component 1:

1) Acrilem IC20 5,0 2) Water 4,0 3) Benaqua 4000 0,4 4) Methylglycol 4,0 5) Orotan 165 3,0 6) Tegofoamex 825 0,5 7) AMP 90 0,3 8) MIOX AS 28,0 9) Calcitec M5 8,5 10) Wayncor 221 4,5 _____________________________________________

Component 2:

11) Acrilem IC20 34,5 12) Tegofoamex 825 0,3 13) Ser Ad Fa 179 1,0 14) Texanol 0,5 15) Rheolate 350 1,5 16) Water 1,5 17) Aquatint Nero 3110 1,0 18) Aluminium paste (see below) 1,5 ____________________________________________ 100,0 Aluminium paste: Hydroxal Stapa W 60 N.L. 0,5 Butylglycol 1,0 Disperse at high speed (dissolver) and add component 1 to premixed component 2 The information given here is based on our experience and tests and believed to be reliable. We can accept no liability regarding the suitability or use of any product for any particular purpose or for infringement of patents.

MIOX – Technical Information 42 / 02 Suppliers:

1) Icap-Sira Spa

3) Elementis 5) Rohm & Haas 6) Tego-Degussa 8) Kärntner Montanindustrie GmbH 9) Omya 10) Wayne Pigment corp 11) Icap-Sira Spa 14) Eastman 15) Rheox 17) Icap-Sira Spa 18) Eckart

MIOX – Technical Information 02 / 02Pliolite S 5E – Solution weight % Aromat 100 40,0 Pliolite S...