TEST REPORT Mechanical & Hardgoods Laboratory Report No.: TH50159B/2014

Page: OF 6 Date: JUN. 11 ,2014

PRO LITE 5F-128, FU CHIANG ST., TAICHUNG- TAIWAN

The following merchandise was submitted and identified by the applicant as: Product Description: Frame Style/Item No.: CDS-233 ManufacturerNendor: PRO-LITE Quantity: 3 pes of Frames

We have tested the submitted sample(s) as requested and the following results were obtained: Test Requested: For compliance with Clause 4.8.2.2, Clause 4.8.3.2, Clause 4.8.4.2 and Clause 4.8.5.2

of EN 14 781 :2005 Racing bicycles - Safety requirements and test methods.

Test Method: According to Clause 4.8.2.3, Clause 4.8.3.3, Clause 4 .8.4.3 and Clause 4.8.5.3 of EN 14781:2005 Racing bicycles - Safety requirements and test methods.

Sequence ofTesting: Sample No. # 1 :Clause 4.8.5.3. Sample No. #3 :Clause 4.8.4.3 , Clause 4.8.2.3 and Clause 4.8.3.3.

Test Result: --See following sheet(s)--

Date of Receipt: MAY 19,2014, MAY 22, 2014, JUN. 05,2014

Testing Period: MAY 19, 2014 - JUN. 11, 2014 --- See Next Page ---

Testing Place: No. 9, 14th Rd., Taichung Ind. Park, Taichung City 40755, Taiwan

Signed for and on behalf of SGS Taiwan Ltd.

Kaini Chen Team Leader

Th1s document i~ issued by the Company_ sub1ect to its General C~nd1tions of Service printed overleaf, available on reQuest or accessible ~~;t!Jtto;!Jwww sos.com/enfTecms:and·l;;onqitions aspx and. for electromc format documents, subject o Terms and ConditiOns for Electromc Documents at http·Uwww sgs co!!!len!Terms-and-Coqdii•~-!!:.Q!:>Ql!!i!!nt'JJ;JllL Attent1on IS drawn to the limitaUon of liability, Indemnification and jurisdiction Issues defined !herem. Any holder of this document is advised that information contained hereon reflects the Company's findings at the time of 1ts .Intervention only and Within the lim1ts of Client's instructions, if any. The Company's sole responsibility is to its Client and this document does not exonerate parties to a transaction from exercising all their rights and obligations under the transaction documents. This document cannot be reproduced except In full. without prior written approval of the Company. Any unauthorized alterat,on, forgery or falsification of the content or appearance of this document is unlawful and offenders may be prosecuted to the fullest extent of the law. Unless otherwise stated the results shown in this test report refer only to the sample(s) tested. T 3 5 Q g 3 2 7

, 1 l I. 127. Wu Kung Road, NewTa1pei Industrial Park, NewTaip01 City. Taiwan/N!f:JI:. rpfffr:JI:.J.i "t'OO g.n..:r:.4127*. ~ ~ .ft.l!a#41~fif ;t) m,;~ J) t 1886·2) 2299-3279 f (886·2) 2299·2920 www.sgs.tw

Member ol SGS Group

TEST REPORT Mechanical & Hardgoods Laboratory Report No.: TH50159B/2014

Page: 2 OF 6 Test Result: Clauses: 4.8.2 Frame and front fork assembly- impact test (falling mass) 4.8.2.2 Requirement When tested by the method described in 4.8.2.3, there shall be no visible cracks or fractures in the assembly and there shall be no separation of any parts of any suspension system. The permanent deformation measured between the axes of the wheel axles (the wheel-base see 3.23) shall not exceed the following values:

a) 30 mm where a fork is fitted; b) 15 mm where a solid-steel bar is fitted in place of a fork.

4.8.2.3 Test method Figure:

A t IF' d ' c ua m m~: Test clause

Clause 4.8.2.3

5

Requirement < 15mm

Test Result 0.4mm

Remark There was no visible crack on the sample after testing.

Note: 1. Information of sample: Material (Carbon), Mass (1 ,670 g), Frame (560 mm). 2. The rigid fork which is needed to conduct the test was provided by SGS Taiwan

and rigid fork is 357 mm in length. 3. Sample No. #3.

--- See Next Page---

Result

Pass

This document is issued by the Company sub1'ect to its General Conditions of Service printed overleaf, available on re uest or accessible at · . • · · and for electronic format documents, subject o Terms and Conditions for Electronic Documents at · • • · . • Attention is drawn to the limitation of liability, indemnification and jurisdiction issues defined therein. Any holder of this document is advised that information contained hereon reflects the Company's findings at the time of its .intervention only and within the limits of Client's instructions, if any. The Company's sole responsibility is to its Client and this document does not exonerate part1es to a transaction from exerc1s1ng all their rights and obligations under the transaction documents. This document cannot be reproduced except in full, without prior written approval of the Company. Any unauthorized alteration, forgery or falsification of the content or appearance of this documenl is unlawful and offenders may be prosecuted to the fullest extent of the law. Unless otherwise stated the results shown in this test report refer only to the sample(s) tested. 3 5 Q 9 3 2 8

127. Wu Kung Road, New Taipe1lndusmal Park. New Taipei City. Taiwan /HiT ;1:. rp HiT ;1:.,4.1: 00 g Ji...I-~127~ ~ ~:lk~H~UH};t) ~~ .i) t 1886-2) 2299-3279 f (886·21 2299-2920 www.sgs.tw

Member of SGS Group

TEST REPORT Mechanical & Hardgoods Laboratory Report No.: TH50159B/2014

Page: 3 OF 6 Test Result: Clauses: 4.8.3 Frame and front fork assembly- impact test (falling frame) 4.8.3.2 Requirement When tested by the method described in 4.8.3.3, there shall be no visible cracks or fractures in the assembly and after the second impact, the permanent deformation measured between the axes of the wheel axles (the wheel-base - see 3.23) shall not exceed 15 mm for a frame-fork assembly and there shall be no separation of any parts of any suspension system.

4.8.3.3 Test method Figure:

A IF" d. ctua m mg: Test clause

Clause 4.8.3.3 Requirement

< 15mm I I

\ \

-~j \ I I I

3

Test Result 0.2 mm

Remark There was no visible crack on the sample after testing.

Note: 1. Infonnation of sample: Material (Carbon), Mass (1,670 g), Frame (560 mm). 2. The rigid fork which is needed to conduct the test was provided by SGS Taiwan

and rigid fork is 357 mm in length. 3. Sample No. #3.

--- See Next Page ---

Result

Pass

This document is issued by the Company sub1"ect to its General Conditions of Service printed overleaf, available on re uest or accessible at · • • · · and for electronic format documents, subject o Terms and Conditions for Electronic Documents at · . • · · . • Attention 1s drawn to the lim1tation of liability, indemnification and jurisdiction issues defined therein. Any holder of this document is advised that infonmation contained hereon reflects the Company's findings at the time of its .intervention only and within the limits of Client's instructions, if any. The Company's sole responsibility is to its Client and this document does not exonerate parties to a transaction from exerc1s1ng all their nghts and obligations under the transaction documents. Th1s document cannot be reproduced except in full, without prior written approval of the Company. Any unauthorized alteration, forgery or falsification of the content or appearance of this document is unlawful and offenders may be prosecuted to the fullest extent of the law. Unless otherwise stated the results shown in this lest report refer only to the sample(s) tested. 3 5 Q g 3 2 g

127. Wu Kung Road. New Tatpei Industrial Park. New Ta1pei City, Taiwan/ -8JT ;t, rp -liT;!:,;.{ 1: 00 g Ji.I.~l27~ {; ~oltAkH4Ul:{st.:tf ffl./~ J) t (886·21 2299 3279 f (886-2) 2299 2920 www.sgs.tw

Member of SGS Group

TEST REPORT Mechanical & Hardgoods Laboratory Report No.: TH50159B/2014

Page: 4 OF 6 Test Result: Clauses: 4.8.4 Frame - fatigue test with pedalling forces 4.8.4.2 Requirement When tested by the method described in 4.8.4.3, there shall be no visible cracks or fractures in the frame, and there shall be no separation of any parts of any suspension system. For carbon- fibre frames, the peak deflections during the test at the points where the test forces are applied shall not increase by more 20% of the initial values.

4.8.4.3 Test method Figure:

A IF. d. ctua m mg:

Test clause

Clause 4.8.4.3

c

r~7

Force

1,100 N

A

Test conditions Frequency Cycles

3Hz 100,000

Remark There was no visible crack on the sample after testing.

-----------Peak deflections during_ the test

Initial values Final values Left 20.55 mm 22.19 mm

Right 22.59mm 24.34mm

Test Result (Cycles)

100,000

Test Result Pass Pass

Remark The peak deflections was no more than 20% of the initial values.

Note: 1. lnfonnation of sample: Material (Carbon), Mass (1 ,670 g), Frame (560 mm). 2. The rigid fork which is needed to conduct the test was provided by SGS Taiwan

and rigid fork is 357 mm in length. 3. Sample No. #3.

---See Next Page---

Result

Pass

This document Is ISsued by the Company sub!·ect to its General Conditions of Service printed overleaf, available on re uest or accessible at · - - · · and. for electronic format documents. subject o Terms and Conditions for Electronic Documents at · . - - · · - - Attent on 1s rawn to the l1mitation of liability, indemnification and jurisdiction issues defined therein. Any holder of this document is adv1sed that information contained hereon reflects the Company's find1ngs at the time of its intervention only and w1thin the limits of Client's instructions, If any. The Company's sole responsibility is to its Client and this document does not exonerate parties to a transaction from exercising all their nghts and obligations under the transaction documents. This document cannot be reproduced except in full, without prior written approval of the Company. Any unauthorized alteration, forgery or falsification of the content or appearance of this document is unlawful and offenders may be prosecuted to the fullest extent of the law. Unless otherwise stated the results shown in this test report refer only to the sample(s) tested.

1 3 5 Q g 3 3 Q

127. Wu Kung Road, New Tatpetlndusmal Park. New Tatpei City, Taiwan /-$f 31:. 'f1 -$f 31:....! "f l!J I;& Ji..J.4127*. ~ ~4t-lla~HUHr;tr ffi_J~ J] t (886 2) 2299-3279 f (886·2) 2299-2920 www.sgs.tw

Member ol SGS Group

TEST REPORT Mechanical & Hardgoods Laboratory Report No.: TH50159B/2014

Page: 5 OF 6 Test Result: Clauses: 4.8.5 Frame- fatigue test with horizontal forces 4.8.5.2 Requirement When tested by the method described in 4.8.5.3, there shall be no visible cracks or fractures in the frame and there shall be no separation of any parts of any suspension system. For carbon- fibre frames, the peak deflections during the test in either direction from the mean position shall not increase by more than 20% of the initial values.

4.8.5.3 Test method Figure:

A tu I F. d. c a m mg:

Test clause

Clause 4.8.5.3

2

Test conditions Force Frequency Cycles

+ 600N 3Hz 100,000

- 600N Remark There was no visible crack on the sample after testing.

------------Peak deflections during the test

Initial values Final values

s· 1 I Pull(+) 3.25 mrn 3.29 mrn mg e I Push(-) 4.65 mrn 4.70 mrn

Test Result (Cycles)

100,000

Test Result Pass Pass

Remark The peak deflections was no more than 20% of the initial values.

Note: 1. Information of sample: Material (Carbon), Mass (1 ,557 g), Frame (535 mm). 2. The rigid fork which is needed to conduct the test was provided by SGS Taiwan

and rigid fork is 353 mrn in length. 3. Sample No. #1.

--- See Next Page---

Result

Pass

This document is issued by the Company subl'ect to its General Conditions of Service printed overleaf, available on re uest or accessible at · • • · · and for electronic format documents, subject o Terms and Conditions for Electronic Documents at · - - · · - - ttent1on IS drawn to the limitation of liability, indemnification and jurisdiction issues defined therein. Any holder of this document is advised that information contained hereon reflects the Company's findings at the time of its .Intervention only and withil) th~ llm1ts of Ghent's instructions, if any. The Company's sole responsibility is to its Cli~nt and this docu.ment does not exonerate ~Jarties to a transaction from exerCISing all the1r nghts and obhgat1ons under the transaction documents. Th1s document cannot be reproduced except 1n full, w1thout pnor written approval of the Company. Any unauthorized alteration, forgery or falsification of the content or appearance of this document is unlawful and offenders may be prosecuted to the fullest extent of the law. Unless otherwise stated the results shown 1n th1s lest report refer only to the sample(s) tested. 3 5 Q 9 3 3 1

127, Wu Kung Road, New Taipei Industrial Park, New Taipei City, Taiwan I mr :11:. rfr mr :!I:. A. ;t 00 !& Ji..I.~ 127tt f:; JJ\';It~#~Uli~;IJ *'~ .ij t 1886·2) 2299 3279 f 1886·2) 2299-2920 www.sgs.tw __ _

Member of SGS Group

TEST REPORT Mechanical & Hardgoods Laboratory Report No.: TH50159B/2014

Page: 6 OF 6 - Picture( s) -

--- End of Report ---

This document is issued by the Company sub1'ect to its General Conditions of Service printed overleaf, available on re uest or accessible at · s com/encrerms-and-Condltjons aspx and. for electronic format documents, subject o Terms and Conditions for Electronic Documents at · - - · - - AHention is drawn to the limitation of liability, mdemnificat1on and jurisdiction issues defined therein. Any holder of this document is advised that information contained hereon reflects the Company's findings at the time of its intervention only and within the limits of Client's instructions, if any. The Company's sole responsibility is to its Client and this document does not exonerate f)arties to a transaction from exercising all their rights and obligations under the transaction documents. This document cannot be reproduced except in full, without prior wriHen approval of the Company. Any unauthorized alteration, forgery or falsification of the content or appearance of this document is unlawful and offenders may be prosecuted to the fullest extent of the law. Unless otherwise stated the results shown in this lest report refer only to the sample(s) tested. 3 5 Q 9 3 3 2

127. Wu Kung Road. New Ta1pci lndustnal Park. New Taipei City. Taiwan /SIT ;1::. rp i/f;l::..ii 1: 00 g Ji_.:L~l27*. f; ~:lt-l!a-:H4Ul:1;r .:tf RV~ .>] t (886-2) 2299-3279 f (886·2) 2299-2920 www.sgs.tw

Member of SGS Group