Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Aluminum A356.0-T6, Sand Cast
Categories: Metal; Nonferrous Metal; Aluminum Alloy; Aluminum Casting Alloy
Material Notes: Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN.
Composition Notes: Composition information provided by the Aluminum Association and is not for design.
Key Words: Aluminium A356.0-T6; UNS A13560; AAA356.0-T6
Vendors: No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
Physical Properties Metric English Comments
Density 2.67 g/cc 0.0965 lb/inMechanical Properties Metric English Comments
Hardness,Brinell 70.0 - 105 70.0 - 105 AA; Typical; 500 g load; 10 mm ballHardness,Knoop 112 112 Estimated from Brinell Hardness.Hardness,RockwellA 37 37 Estimated from Brinell Hardness.Hardness,RockwellB 55 55 Estimated from Brinell Hardness.Hardness,Vickers 99 99 Estimated from Brinell Hardness.TensileStrength,Ultimate >= 234 MPa >= 34000 psi AATensileStrength,Yield >= 165 MPa >= 24000 psi AA; 0.2% OffsetElongationatBreak >= 3.50 % >= 3.50 % AA; in 2 in. (50 mm) or 4DModulusofElasticity 72.4 GPa 10500 ksi In Tension; elastic modulus in compression is typically about 2%
higher for aluminum alloys.
PoissonsRatio 0.330 0.330Machinability 50 % 50 % 0-100 Scale (100=best)ShearModulus 27.2 GPa 3950 ksiShearStrength 143 MPa 20700 psi CalculatedElectrical Properties Metric English Comments
ElectricalResistivity 0.00000440 ohm-cm 0.00000440 ohm-cmThermal Properties Metric English Comments
HeatofFusion 389 J/g 167 BTU/lbCTE, linear 21.4 m/m-C
@Temperature 20.0 - 100C11.9 in/in-F
@Temperature 68.0 - 212F
23.2 m/m-C@Temperature 20.0 - 300C
12.9 in/in-F@Temperature 68.0 - 572F
SpecificHeatCapacity 0.963 J/g-C 0.230 BTU/lb-FThermalConductivity 151 W/m-K 1050 BTU-in/hr-ft-FMeltingPoint 557 - 613C 1030 - 1140FSolidus 557C 1030FLiquidus 613C 1140FProcessing Properties Metric English Comments
MeltTemperature 677 - 816C 1250 - 1500FSolutionTemperature 535 - 540.6C 995 - 1005F holdattemperaturefor12hrcoolinwaterat150to212FAgingTemperature 152 - 157C 305 - 315F hold at temperature 2 - 5 hrs; start with solution heat-treated materialCastingTemperature 677 - 788C 1250 - 1450FComponent Elements Properties Metric English Comments
Aluminum,Al 91.1 - 93.3 % 91.1 - 93.3 % As remainderCopper,Cu
-