![Page 1: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/1.jpg)
Angular dependence of FMR measurements in exchange coupled
NiFe/NiO bilayers: Experiment and Theory
B.W. Southern*N. Grenda*#, P. Hyde*, Y.S. Gui*, M.P. Wismayer*,
C.‐M. Hu*, K.‐W. Lin&, and J. van Lierop*
*Department of Physics and Astronomy, University of Manitoba, Winnipeg, Manitoba, Canada
# Institut fur Angewandte Physik und Zentrum furMikrostrukturforschung, Universitat Hamburg, Hamburg, Germany
& Department of Materials Science and Engineering, National Chung HsingUniversity, Tiachung,Taiwan
1
Magnetic North III
![Page 2: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/2.jpg)
Outline
• Introduction • Experimental results• Theoretical Interpretation• Summary
2
![Page 3: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/3.jpg)
• Ferro (F) and Anti‐ferro (AF) films in contact exhibit the phenomenon of exchange‐bias first observed by Meiklejohnand Bean (1956) in CoO
• Usually characterized by a shifted hysteresis loop after field cooling.
• Attributed to a unidirectional anisotropy
• Applications in information storage technologies and was first practical application of AF in spin valves
3
770K
Cooled in 1T
![Page 4: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/4.jpg)
4
Easy (00) Hard(900)
See review articles by• Nogues and Schuller JMMM 192,203(1999)• Berkowitz and Takano JMMM 200,552 (1999)• Stamps J. Phys. D. 33, 247 (2000)• Kiwi JMMM 234,584 (2001)
Hc=( hR‐hL)/2Hex=(hR+hL)/2
![Page 5: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/5.jpg)
5
• Different experimental techniques yield different values for the coupling field Hex at the interface
• Hysteresis loops involve irreversible switching of the magnetization
• FMR and BLS generally involve small pertubations of the magnetization about equilibrium and are reversible
• In this talk I will discuss a particular NiFe/NiO bilayer systemwhere both magnetization and FMR measurements have been performed by research groups in Manitoba.
![Page 6: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/6.jpg)
• The bilayer was prepared by the group of Ko‐Wei Lin at the National Chung Hsing University in Taiwan using a dual ion‐beam sputtering technique at room temperature. Lin et al Appl. Phys. Lett. 100, 122409(2012)
• The NiFe/NiO film was fabricated on a SiO2 substrate and no external field was applied during any stage of the growth
6
epoxy
SiO2
Fabrication
![Page 7: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/7.jpg)
7
• NiO film layers had crystallitesizes between 5 and 20 nm indiameter that penetrated the16 nm thickness (XRD)
• ZFC and FC DC susceptibilitymeasurements indicated ablocking temperature TB=360K
• NiO has a cubic fcc structure with alternating ferromagneticsheets along the [111] direction
• Since no field was applied during fabrication, many AF domain configurations could be present.(there 4 possible [111]directions as well as perhapsthree in each plane)
Analysis
![Page 8: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/8.jpg)
8
McCord: Adv in Solid State Physics 48, 157 (2009)
• The presence of exchange bias and coercivitydepends on the thickness of the AF layer
• For 16 nm thickness, Hc and Hex could be of the same order of magnitude with Hex larger
![Page 9: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/9.jpg)
9
McCord: Adv in Solid State Physics 48, 157 (2009)Easy
Hard
![Page 10: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/10.jpg)
10
• Magnetometry measurements by Van Lierop’s group on a sampleof length 6 mm and width 2 mm for both a single and bilayer wereperformed
• Films were heated to 400K and cooled in a field of 2T
• Single NiFe layer exhibited negligble coerciviity and no exchange bias
• Bilayer sample exhibited both coercivity and exchange bias shift Hex ~ 2.0 mT along the cooling field direction
• Hc ~ 1.1 mT @ 300K
Magnetometry
NiFe
NiFe/NiO
![Page 11: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/11.jpg)
11
FMR Measurements
• FMR measurements on the same samples were performed by the group of Can‐Ming HuNiFe: L=21 mm W=20.0 mm T=9nmNiFe/NiO:L=16.3 mm W=13.8 mm T=9 nm
• Broadband microwave absorption spectroscopy was used to detectthe FMR frequency as evidenced by a transmission minimum
• A reference measurement at 150 mTis used to perform a subtraction at lower fields
30mT
150mT
![Page 12: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/12.jpg)
12
FMR
• External field is applied in‐plane atvarious angles φ with respect to thelong direction
• For each φ, a reference measurementis made at ± 150 mT and then either an up sweep or a down sweep is carried out between ±30 mT at intervals of 0.4 mT
• No heating or cooling in a field performed• Two distinct types of behaviour are observed for the FMRfrequency as a function of the field which depend upon thedirection of the field.
![Page 13: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/13.jpg)
13
• Irreversible switching is observed in the range ‐6mT < H < 6mT• For all angles < 450 a single peak is found• Frequency range is 2.0 < f < 2.5 GHz
![Page 14: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/14.jpg)
14
• Irreversible switching is observed in the range ‐8mT < H < 8mT• For all angles >600 a two peaks are found• Suggests a two step reversal process• Frequency range is 2.7 < f < 3.4 GHz
![Page 15: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/15.jpg)
15
0
2r sf H M H
μ0Ms=963 mT, γ= 176 GHz/T
![Page 16: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/16.jpg)
16
• For 4.5 GHz we can plot the resonant field Hr as a function of φ• Can be fit to the form Hr= a0 + a1 cos(φ) + a6 cos(6φ)a0= 25.306 mT, a1= .345 mT and a6=‐0.133 mT for up sweep (a)a0= 25.338 mT, a1= .296 mT and a6=‐0.237 mT for down sweep (b)
• Suggests that there may be a unidirectional anisotropy as well asa six‐fold anisotropy
Up sweep Down sweep
![Page 17: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/17.jpg)
17
? Theory
![Page 18: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/18.jpg)
18
• In order to model this behaviour we treat the NiFe as a single domain and include the effect of the NiO as introducing anisotropies at the interface
• The energy of the system can be written as
2 2 2 2 2 2 2 22 4
6 6 4 2 2 46
1.2 2 4
15 15
z x x y y z z x
x y x y x y x
x xE H M M S S S S S S S
x S S S S S S jS
• Use spherical coordinates to find extrema of E as function ofthe field direction φH and magnitude
• Calculate FMR frequencies using Smit‐Beljers formula (1955)
21sins
E E EM
![Page 19: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/19.jpg)
19
90 degrees x2=3 mT x4= ‐8mT x6= 0.1 mT
![Page 20: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/20.jpg)
20
0 degrees x2=3 mT x4= ‐8mT x6= 0.1 mT
![Page 21: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/21.jpg)
210 degrees 90 degrees
![Page 22: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/22.jpg)
22
45 60 80
![Page 23: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/23.jpg)
23
Downsweep90 degrees
![Page 24: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/24.jpg)
24
Downsweep0 degrees
![Page 25: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/25.jpg)
25
• Bilayers were fabricated in zero field and no field cooling wasperformed for the FMR measurements
• Minor hysteresis loops appear as the field direction is rotatedfrom 0 to 90 degrees with respect to the longer sample side
• The single domain model is too simple to make detailedcomparisons with experiment but does indicate thatanisotropies contribute to the angular dependence of theresonant frequencies
• F layer may not be homogeneous at interface• Micromagnetic results indicate that reversal is not single domain• AF layer is treated as being static and providing an effectiveanisotropy
• The micromagnetic calculations need to be extended to multiplelayers which would allow some dynamics in the AF
Summary
![Page 26: Magnetic North III dependence of FMR measurements NiFe ......4 Easy 0)(0 Hard(900) See review articles by • Nogues and Schuller JMMM 192,203(1999) • Berkowitz and Takano JMMM 200,552](https://reader033.fdocuments.in/reader033/viewer/2022060918/60aae84dc75d46058c2efe50/html5/thumbnails/26.jpg)
26
The End