VIETNAM MINING CORPORATION
Sample ProtocoleRaw MaterialSample Name
With reference to the Offer/Order nr. for performing laboratory
tests on the materials as above identified and received on CIMPROGETTI S.p.A. submits the present Raw Material Suitability Report as guidelines for the
preliminary evaluation of the project feasibility and of the plant performance guarantees.
RAW MATERIAL CHARACTERISTICSCaratteristiche della materia prima
Suitable for the use in the proposed plantIdoneità per l'utilizzo proposto
Comments on chemical compositionCommenti sulla composizione chimica
Comments on physical propertiesCommenti sulle proprietà fisiche
ReactivityReattività
Filled by:
ACCEPTABLE
HIGH BUT THE LIMESTONE OVERBURNS EASILY
T.CHRISTIANSEN
Technological Test Laboratory
03/09/2009date
ACCEPTABLE
YES
5-001157-K-09-1
548LIMESTONESample 2
Sample identificationIdentificazione campione
Raw Material Suitability ReportRapporto di idoneità materia prima
NotesAnnotazioni
CIMPROGETTI S.p.A. - Via Pasubio, 5 - (I) Dalmine - ph.+39.035.4550.111 - fax +39.035.4550.336 - Email [email protected]
Sample ProtocoleRaw MaterialSample Name
LIMESTONECalcare
LIMECalce
Lime after 3 hours at 1050°C Lime after degradation test
Technological Test Laboratory
03/09/2009date548
LIMESTONESample 2
Sample identificationIdentificazione campione
PHYSICAL APPEARANCEAspetto fisico
CIMPROGETTI S.p.A. - Via Pasubio, 5 - (I) Dalmine - ph.+39.035.4550.111 - fax +39.035.4550.336 - Email [email protected]
Sample ProtocoleRaw MaterialSample Name
COMPONENTS METHOD FORMULA %Componenti Metodo Formula
Loss on ignition / Perdita a fuoco TM-01 P.a.F. 43,53Silicon dioxide / Diossido di silicio TM-10 SiO2 0,47Aluminium dioxide / Ossido di alluminio TM-10 Al2O3 0,18Iron oxide / Ossido di ferro TM-10 Fe2O3 0,00Calcium oxide / Ossido di calcio TM-10 CaO 55,01Magnesium oxide / Ossido di magnesio TM-10 MgO 0,72Sulphur trioxide / Anidride solforica TM-12 SO3 0,01Sodium oxide / Ossido di sodio TM-13 Na2O
Potassium oxide / Ossido di potassio TM-13 K2O
Manganesium oxide / Ossido di manganese TM-10 Mn2O3
Chromium / Cromo TM-10 CrBarium / Bario BaPhosphorus / Fosforo TM-10 PTin / Stanno TM-10 SnStrontium / Stronzio TM-10 SrSulphur (H2S) / Anidride solforosa 0,008
Halogens / Alogeni TM-14 F,Cl,Br,I 0,010(Fluorine,Chlorine,Bromine,Iodine / Fluoro,Cloro,Bromo,Iodio )
TOTAL 99,94
Water / Acqua TM-03 H2O 0,41Carbonates (calculated as CO2) /Carbonati (calcolato come CO2) TM-15 CO2
Degradation % in mech. test TM-32 Perdita al test meccanico TM-32
Contents % of dirt on stone TM-36 Contenuto % di sporcizia TM-36
Max. moisture TM-35 Umidità massima TM-35
Maximum moisture % TM-35 Massima umidita` TM-35
Cohesion (visual evaluation) Coesione (valutazione visiva)
Physical aspect (visual evaluation) Aspetto fisico (valutazione visiva)
Structure (visual evaluation) Struttura (valutazione visiva)
Sample 2
Grey, dry
<2%
Microcristallinic, quite homogenous
LIMESTONE
Technological Test Laboratory
03/09/2009date548
Sample identificationIdentificazione campione
CHEMICAL ANALYSISAnalisi chimica
Limestone physical analysisAnalisi fisiche del calcare
CIMPROGETTI S.p.A. - Via Pasubio, 5 - (I) Dalmine - ph.+39.035.4550.111 - fax +39.035.4550.336 - Email [email protected]
Sample ProtocoleRaw MaterialSample Name
Loss on ignition % after 2 h at t °C% perdita a fuoco dopo 2 ore a t °C
t °C 750 800 850 900 950 1000 1050 1100LoI % 14,41 33,93 43,75% calcined 32,94 77,55 100,00
CONSIDERATIONS ON BEHAVIOUR DURING HEATING AND BURN INGConsiderazioni sul comportamento durante il riscaldo e la cottura
Optimum > 95%Good/buono 85-95%Fair/suffic. 75-85%Scarce/scarso 65-75%Poor/scadente < 65%
Degradation % in mech. test TM-32 Perdita al test meccanico TM-32
Visual aspect Aspetto fisico
Notes Note
Whitish/greenish 11,64 gr = 27,7%X
7,3% (at 10 mm) 31,7% (at 19 mm)
Valutazione a 950° C Attitudine cottura Valutazione visiva allo shock termico Test ad alta temperatura TM-31
Evaluation at 950° C Burning attitude Visual inspection of thermal shock High temperature test TM-31
Technological Test Laboratory
03/09/2009date
Sample 2
548LIMESTONE
Sample identificationIdentificazione campione
BURNING TESTProva cottura
0,00
5,00
10,00
15,00
20,00
25,00
30,00
35,00
40,00
45,00
50,00
850 950 1050t°C
LoI%
Lime physical analysisAnalisi fisiche del la calce
CIMPROGETTI S.p.A. - Via Pasubio, 5 - (I) Dalmine - ph.+39.035.4550.111 - fax +39.035.4550.336 - Email [email protected]
Sample ProtocoleRaw MaterialSample Name
x The limestone sample is burnt in muffle at 1.050°C for 3 hours.Calcare cotto in muffola a 1.050°C per 3 ore.
The limestone is burnt in kiln type: Calcare cotto in forno tipo
Maximum temperature ºC Temperatura massima
40°C temperature increase min Aumento temperatura di 40°C
Notes Note
73,8
2,16
Technological Test Laboratory
03/09/2009date
SLAKING METHOD (EN 459-2.5.10)
Sample 2
548LIMESTONE
Metodo di spegnimento
150 gr of lime is added at time = 0 to a thermos containing 600 cc of water at 20°C; the water with li me is kept in movement by an agitator at the speed of 400 rpm.150 g di calce sono aggiunti al tempo = 0 in un termos contenente 600 cc di acqua a 20°C; l'acqua/calc e è tenuta in movimento da un agitatore alla velocità di 400 rpm.
Sample identificationIdentificazione campione
REACTIVITY TESTTest di reattività
19,9
41,5
51,0
59,3
63,8
66,9
69,3
71,0
72,172,9
73,473,6
73,873,7
0
10
20
30
40
50
60
70
80
0 2 4 6 8 10 12 14
Min
°C
NotesAnnotazioni
CIMPROGETTI S.p.A. - Via Pasubio, 5 - (I) Dalmine - ph.+39.035.4550.111 - fax +39.035.4550.336 - Email [email protected]
Sample ProtocoleRaw MaterialSample Name
x The limestone sample is burnt in muffle at 1.150°C for 3 hours.Calcare cotto in muffola a 1.150°C per 3 ore.
The limestone is burnt in kiln type: Calcare cotto in forno tipo
Maximum temperature ºC Temperatura massima
40°C temperature increase min Aumento temperatura di 40°C
Notes Note
Technological Test Laboratory
03/09/2009date
SLAKING METHOD (EN 459-2.5.10)Metodo di spegnimento
150 gr of lime is added at time = 0 to a thermos containing 600 cc of water at 20°C; the water with li me is kept in movement by an agitator at the speed of 400 rpm.150 g di calce sono aggiunti al tempo = 0 in un termos contenente 600 cc di acqua a 20°C; l'acqua/calc e è tenuta in movimento da un agitatore alla velocità di 400 rpm.
548LIMESTONE
67,5
12,75
Sample 2
Sample identificationIdentificazione campione
REACTIVITY TESTTest di reattività
20,0
30,6
34,0
41,1
45,7
48,8
51,252,9
54,4
56,757,7
58,659,4
60,261,0
61,762,3
62,963,5
64,164,7
65,365,7
66,166,5
66,867,1
67,367,4
67,567,5
55,6
0
10
20
30
40
50
60
70
80
0 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32
Min
°C
NotesAnnotazioni