Phosphate Stabilization by Non-Chromate Post-Rinse Treatment
by
Tae-Ho Yoon
Thesis submitted to the Faculty of the
Virginia Polytechnic Institute and State University
in partial fulfillment of the requirements for the degree of
Master of Science
J. L.0 Lytton
in
Materials Engineering
7 W. J':" van Ooij, Jhairman
/
June, 1987
Blacksburg, Virginia
J. G. Dillard \
Phosphate Stabilization by Non-Chromate Post-Rinse Treatment
by
Tae-Ho Yoon
W. J. van Ooij, Chairman
Materials Engineering
(ABSTRACT)
Zinc phosphate conversion coating has been applied to improve the corrosion resistance and
paint adhesion. However, zinc phosphate crystals dissolve in a highly alkaline environment,
which reduces the corrosion resistance of base metal. To improve the phosphate stability in
a highly alkaline environment, a post-rinse treatment has been applied to phosphate coating
by rinsing with an aqueous solution which contains certain anions or cations. Chromate-
post-rinse treatment is the most widely used method and has shown a great improvement in
corrosion resistance. But, due to the environmental problems caused by chromate ions,
non-chromate post-rinse treatment should be developed, which has equal or better corrosion
resistance than does chromate post-rinse treatment. In this research, inorganic silicate with
addition of Ca2+, Ba2 +, Ni2+, Mg2 +, has been extensively evaluated together with silane sol-
ution, y -aminopropyltriethoxysilane ( y -A.P.S., NH2(CH 2) 3Si(OC2H5) 3), which was applied after
the post-rinse treatment. The evaluation was carried out by the highly advanced surface
analysis techniques such as SEM/EDX, AES, SIMS, and XRD and polarization measurements.
Acknowledgements
The author would like to express his gratitude to Dr. W. J. van Ooij for his contributions
and suggestions throughout this research effort and to Amchem Products Inc. for their spon-
sorship.
The author would also like to extend his thanks to Dr. J. L. Lytton, and Dr. J. G. Dillard for
serving on his committee. The author wishes to acknowledge the helpful suggestions from
Dr. Woo Jin Choi, Dr. Hee Young Lee and Regina H. Kim.
The author wish to express special thank to Bob McGrew at Colorado School of Mines for
the SEM and the EDX works.
Finally, the author would also like to express his sincere thanks to his parents, Mr. and
Mrs. D. S. Yoon, and Mr. and Mrs. C. K. Lee for their support.
Acknowledgements iii
Table of Contents
Chapter I. Introduction ................................................... 1
Chapter II. Literature Review .............................................. 4
2 - 1. Phosphate Conversion Coatings. . .................................... 5
2 - 1 - 1. Introduction. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5
2 - 1 - 2. Mechanisms of Phosphate Conversion Coatings. . . . . . . . . . . . . . . . . . . . . . 6
2 - 1 - 3. Effects of Phosphate Coatings on Corrosion Protection. . . . . . . . . . . . . . . . . 7
2 - 1 - 4. Dissolution of Phosphate Coatings. . .............................. 8
2 - 2. Post-rinse Treatment. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9
2 - 2 - 1. Introduction .................................................. 9
2 - 2 - 2. Effect of Post-rinse Treatment on Corrosion Protection. . . . . . . . . . . . . . . . . 9
2 - 2 - 3. Possible Non-chromate Post-rinse Treatment. . . . . . . . . . . . . . . . . . . . . . . 10
2 - 3. Silane Coupling Agent. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 12
2 - 3 - 1. Bonding Theory of Silane Coupling Agent. . . . . . . . . . . . . . . . . . . . . . . . . . 12
2 - 3 - 2. Chemistry of Silane Coupling. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13
2 - 4. Principle of Surface Analysis Techniques . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 14
2 - 4 - 1. Basic Principles ............................................. 15
Table of Contents iv
2 - 4 - 2. Scanning Electron Microscope. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 15
2 - 4 - 3. Energy Dispersive X-ray Analysis. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 17
2 - 4 - 3. Auger Electron Spectroscopy. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 18
2 - 4 - 4. Secondary Ion Mass Spectrometry. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 18
Chapter Ill. Experimental ................................................ 22
3 - 1. Sample Preparation. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 24
3 - 1 - 1. Raw Materials. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 24
3 - 1 - 2. Experimental Conditions. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 24
3 - 1 - 3. Solution Preparation. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .. . . . . . . . . . . . 27
3 - 1 - 4. Experimental Procedure. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 30
3 - 2. Sample Analysis. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 32
3 - 2 - 1. SEM/EDX Analysis. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 32
3 - 2 - 2. AES/SIMS Analysis. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 32
3 - 2 - 3. X-Ray Diffraction Analysis. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 33
3 - 2 - 4. Polarization Measurement. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 33
Chapter IV. Results and Discussion ••••••••••••••••••••.•.••.•.••.••.••.••• 35
4 - 1. SEM/EDX Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 36
4 - 1 - 1. Post-rinse Treatment. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 36
4 - 1 - 2. Variability and Brittleness. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 58
4 - 1 - 3. Silane Treatment. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 64
4 - 1 - 4. Heat Treatment. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 70
4 - 2. AES/SIMS Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 71
4 - 3. X-ray Diffraction Analysis Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 87
4 - 4. Polarization Measurement Results. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 87
Chapter V. Summary and Conclusions • • • • • • • • • • • • • • • • • • . • • • • • • . • • • • • • • . . . • • 91
Table of Contents v
Bibliography 96
Vita 100
Table of Contents vi
List of Illustrations
Figure 1. Variety of signals produced by electron bombardment. . . . . . . . . . . . . . . . . . 16
Figure 2. General procedure of treatment . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 23
Figure 3. Schematic diagram of treatment setting . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 26
Figure 4. Schematic diagram of polarization measurement setting. . ...... : . . . . . . . . 34
Figure 5. Leaching of phosphate in a solution of pH 12.0. . . . . . . . . . . . . . . . . . . . . . . . 37
Figure 6. Leaching of phosphate in a solution of pH 12.5. . . . . . . . . . . . . . . . . . . . . . . . 38
Figure 7. Phosphate crystals of as-received sample . . . . . . . . . . . . . . . . . . . . . . . . . . . 39
Figure 8. Phosphate crystals after treatment in a solution of pH 12.0 for 30minutes(a) and one hour(b). . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 40
Figure 9. Phosphate crystals after treatment in a solution of pH 12.5. for 10(a) and 20 minutes(b). . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 41
Figure 10. Effect of waterglass on the stabilization of phosphate in a solution of pH 12.0 for 30 minutes. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 43
Figure 11. Dissolution of phosphate crystals after treatment in solution WG (a) and WZ (b) for 30 min. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 44
Figure 12. Change of silicon content by the post-rinse treatment and followed by immersion test for 10 and 20 min. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 45
Figure 13. Effect of post-rinse treatment on the phosphate stabilization in the immersion test. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 47
Figure 14. Effect of zinc sulfate on the stabilization of phosphate in solution WZ. . . . . . . 48
Figure 15. Effect of calcium on the phosphate stabilization . . . . . . . . . . . . . . . . . . . . . . . 50
Figure 16. Morphology change by the treatment in· solution WC (a) and WB (b) at pH 12.0 for 30 min. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 52
Figure 17. Dissolution of phosphate crystals in the immersion test for 10(a) and 20 min.(b) after treatment in solution WC. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 53
List of Illustrations vii
Figure 18. Effect of the post-rinse treatments in solution WB, WCN, WCM and WCB on the phosphate stabilization in the immersion test. . . . . . . . . . . . . . . . . . . . . . . . 55
Figure 19. Dissolution of phosphate crystals of samples treated in solution WB in the immersion test for 10 (a) and 20 min.(b). . . . . . . . . . . . . . . . . . . . . . . . . . . . . 56
Figure 20. Variability of P, Si and Ni in as-received sample. . . . . . . . . . . . . . . . . . . . . . . 60
Figure 21. Relationship between P, Si and Ni in as-received sample. . . . . . . . . . . . . . . . 61
Figure 22. Effect of treatment on variability . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 62
Figure 23. Effect of immersion test on variability . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 63
Figure 24. Cracks formed by the punching. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 65
Figure 25. Change of silicon content by the silane treatment and followed by the immersion test. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 66
Figure 26. Effect of the silane treatment on the phosphate stabilization in the immersion test. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 68
Figure 27. Effect of the silane treatment on the dissolution of phosphate crystals in the immersion test for 10 (a) and 20 min.(b)(pretreated in WCB) . . . . . . . . . . . . . 69
Figure 28. Effect of heat treatment on the phosphate stability in the immersion test. 72
Figure 29. Degradation of phosphate crystals by heat treatment followed by the immersion test for 10 (a) and 20 min.(b). . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 73
Figure 30. AES spectrum of as-received sample. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 75
Figure 31. AES spectrum of the sample treated in solution WG for 30 min. . . . . . . . . . . . 76
Figure 32. AES depth profiling spectrum of the sample treated in solution WG. . . . . . . . 77
Figure 33. AES spectn,im of the sample treated in solution WC without water rinse. 78
Figure 34. Effect of water rinse on the retention of elements in the coating surface. 79
Figure 35. Depth profiling result of the sample treated in solution WC for 30 min (no rinse). 80
Figure 36. AES spectrum of the sample treated in solution WCB. . . . . . . . . . . . . . . . . . . 81
Figure 37. AES spectrum of the sample treated in solution WCB followed by the silane treatment. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 82
Figure 38. SIMS survey spectra of the sample treated in solution WCB for 30 min. . . . . . 85
Figure 39. SIMS spectrum of the sample treated in solution WCB followed by the silane treatment. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 86
Figure 40. X-ray diffraction spectra of the samples after post-rinse treatment followed by the immersion test for 20 min. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 88
List of Illustrations viii
Figure 41. Cathodic polarization curves of post-rinse treated and/or silane treated samples and as-received smple. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 90
Figure 42. Proposed model of thin film formed by the post-rinse treatment in solution WB. 94
List of Illustrations ix
List of Tables
Table 1. Analytical characteristics of AES (70). . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 19
Table 2. Analytical characteristics of SIMS (74) . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 21
Table 3. The specification of sample panel . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 25
Table 4. List of chemicals . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 28
Table 5. Solutions used in post-rinse treatment . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 29
Table 6. Average and standard deviation value of the variability treatment. . . . . . . . . . 59
List of Tables x
Chapter I. Introduction
Recently, the need to improve corrosion resistance of automotive steel became more
important than ever due to hostile environment such as the increasing use of de-icing salts in
winter (1). A number of investigations have been carried out to improve corrosion resistance
of automotive steel with more research focusing on the pre- and post-treatment (2, 3) rather
than developing new anti-corrosive materials. Powerful surface analysis techniques have
become increasingly valuable for corrosion studies, for example SEM/EDX, AES and SIMS, in
combination with other tools (4).
Zinc (6-9) and its alloy coating (10-13) have been widely applied to steel surface to im-
prove corrosion resistance by the sacrificial action of zinc to steel. The phosphate conversion
coatings have also been extensively used by themselves or in combination with other coatings
to improve the corrosion resistance (14-16), which provide good barrier for corrosion pro-
tection and base for paint coating. However, phosphated and electrocoated steel corrodes
readily in salt spray, scab and filiform conditions. Recent studies using modern surface
analysis tools such as XPS, AES and EDX have indicated that such corrosion is initiated by the
transformation in the phosphate layers (17,18).
Chapter I. Introduction 1
Since phosphate coatings have some degree of porosity (19, 20) and damage from han-
dling, corrosion cell can be established under the paint coating. As corrosion reaction go on,
the pH of corrosion cell increases generally upto 12-14. As reported in literature (21, 22)
phosphate coatings dissolve in a highly alkaline environment; hence corrosion protection by
phosphate coatings reduce. The stabilization of phosphate coatings and hence the corrosion
protection can be further enhanced by the post-rinse treatment in a solution which contains
certain cations or anions, such as CrH, Pb2+ or Cro~- (17, 18, 21). This treatment forms a
protective skin with a much reduced solubility by ion exchange of certain cations or anions
with either Zn2+ or POl- ion. This treatment was found to be effective only at high pH condi-
tion (salt spray test). The post-rinse treatment with solution containing chromate ions has
shown great improvement of corrosion protection (19), however, due to the environmental
problems caused by chromate ions, non-chromate post-rinse treatment should be developed,
which has equal or better corrosion resistance than chromate post-rinse treatment.
It is certain that corrosion protection can be improved by reducing the dissolution of
phosphate coating in a highly alkaline environment. In this research, to develop non-chromate
post-rinse treatment widely used corrosion inhibitors were tried as a post-rinse treatment
agents, such as silicate, calcium, barium and magnesium, and nickel which is well known
coating material. Silicate which is inexpensive, non-toxic, well known corrosion inhibitor (25,
26) and causes no serious problems was extensively evaluate together with other ions. The
silane treatment was also performed to improved the paint adhesion and reduce the dissol-
ution of phosphate. The analysis of the samples was carried out with SEM/EDX, AES and
SIMS, and confirmation of results was made by the application of XRD and polarization
measurements.
It is proposed to optimize the conditions in terms of pH, temperature, time, concentration
of the silicate and the presence of other ions in the solution by observing the effect of these
factors on the rate of phosphate attack. The objectives of this research were as follow;
Chapter I. Introduction 2
1. to understand the mechanism by which zinc and zinc-iron phosphate exchange cations
and/or anions in highly alkaline media and to formulate a model,
2. to develop a post-rinse treatment which is fast, cheap, effective at both high and low pH,
and which does not involve the use of chromium or chromate ions by using the funda-
mental knowledge acquired from step 1,
3. to further improve the corrosion protection by incorporating a suitably selected silane in
the inorganic silicate film.
Chapter I. Introduction 3
Chapter II. Literature Review
To improve the corrosion resistance of automotive steel panels, numerous research has
been carried out on the various aspects of phosphate conversion coating and post-rinse
treatment. The availability and usefulness of highly advanced surface analysis techniques
have led to the fundamental studies of the mechanism of corrosion protection by the post-
rinse treatment and phosphate coating. The silane treatment has emerged as a very impor-
tant method in enhancing paint adhesion to metal or inorganic coating and corrosion
protection.
Due to the demand a good quality coating to minimize the corrosion damage, numerous
versions of phosphate coating system and post-rinse treatment technique have been devel-
oped and some have been utilized widely in the industries. To have a better knowledge of
the protection mechanism, it is important to understand the basic principles of phosphate
coating and post-rinse treatment.
Chapter II. Literature Review 4
2 - 1. Phosphate Conversion Coatings.
2 - 1 - 1. Introduction.
The protective coatings are applied to the steel surface to enhance the corrosion re-
sistance, durability and appearance. A number of protective coating systems have been de-
veloped and can be classified into three groups; (i). metallic coatings, (ii). non-metallic and
inorganic coatings and (iii). organic coatings. In recent years, however, a mixture of metallic
and inorganic coating has been introduced (27).
Prior to the application of protective coatings, it is necessary to clean the surface of steel
very carefully to enhance the adhesion of coating to the base metal(28, 29). The effect of
surface contamination on coating has been investigated (19, 30). The adhesion of coating to
the metal surface is a key to the coating effectiveness and thus, the surface preparation be-
comes even more critical for coatings applied in corrosive areas.
The phosphate conversion coatings, belonging to the inorganic coating category, have
been applied to steel surfaces to improve the corrosion protection since the beginning of this
century. Since then, a number of investigations have been carried out to improve the quality
and application technique of phosphate coatings. The phosphate coatings are usually applied
to provide a barrier for corrosion protection and a base for paint coating, and are readily ap-
plied to the articles of all size by spray or immersion. The general aspects of phosphating
were reviewed by Lorin (31).
Chapter II. Literature Review 5
2 - 1 - 2. Mechanisms of Phosphate Conversion Coatings.
All conventional phosphate coating processes are based on dilute phosphoric acid sol-
ution of iron, manganese or zinc phosphate either separately or in combination. The chemical
reactions are proposed by several authors (31-33). Zinc phosphate coating is accomplished
by treating the materials in an aqueous solution of acidic zinc phosphate, Zn3(H2P04h to form
a thin film of zinc phosphate crystals, Zn3(P04h , on the surface by spraying or dipping.
The formation of the phosphate crystal in an aqueous solution of acidic zinc phosphate
is represented by the following reactions.
However, when a steel panel is immersed in the phosphate solution its surface is im-
mediately attacked by the free phosphoric acid. Thus ferrous phosphate and hydrogen are
produced as follows;
If the steel panel is coated with zinc (no source of iron), equation (4) may be replaced by the
following reaction,
Chapter II. Literature Review 6
Reaction (5) produces a acidic zinc phosphate solution and the driving force of reaction (2),
which shifts the reaction toward the right, is the neutralization of free phosphoric acid by re-
action (4) and (5). Therefore, the relative amount of free phosphoric acid is very important in
order to obtain a precipitation of phosphate coating(34).
In the phosphating process, chemical activators such as nickel ions are generally added
to make phosphate crystals finer (35). O~idizing agents are also added to accelerate the
overall reaction. Since the chemical activator absorbs on the surface, called surface condi-
tioning, prior to phosphate coating, they provide the sites for crystal nucleation.
2 - 1 - 3. Effects of Phosphate Coatings on Corrosion Protection.
In the automotive industry, the zinc phosphate coatings are generally used. The zinc
phosphate coatings usually consist of two types of crystals; hopetite (Zn3(P04) 2-4H20) and
phosphophyllite (Zn2Fe(P04}z-4H20). The former is more likely obtained by spray and the latter
by immersion. Even though phosphophyllite is more desirable due to its superior alkaline
resistance (36), it is hard to get phosphophyllite even in immersion application if the steel
surface was already treated with other coatings, like zinc.
The phosphate coatings provide a barrier for the corrosion protection. Protectability of
the phosphate coatings without sealing treatment is not good enough because usually the
phosphate coatings have some degree of porosity and defects (20, 21). It is generally ac-
cepted that corrosion protection of phosphate coatings is directly related to the thickness and
porosity of coating, and the ratio of phosphophyllite to hopetite. The porosity of phosphate
coatings has been investigated (37).
Chapter II. Literature Review 7
2 - 1 - 4. Dissolution of Phosphate Coatings.
Recent studies have shown that the phosphate coatings dissolve in a wide range of pH
(19,38). At high pH the phosphate ions are leached out of the phosphate crystals, while at
moderate pH zinc and phosphate ions dissolve, and at very low pH the entire phosphate
coating dissolves. The phosphate dissolution is due to the corrosion reaction which increases
the pH of the corrosion cell beneath the coating(39, 40).
Due to the porosity and the damage from the handling, the corrosion cell might be es-
tablished beneath the coating by the diffusion of oxygen, water and ions. As the corrosion
reactions proceed, the pH of the corrosion cell increases due to the OH- ions produced by
cathodic reaction. The increased pH has an adverse effect on the corrosion protection be-
cause of the dissolution of phosphate coatings in a high alkaline solution which results in a
greater surface porosity and additional coating defects (41), hence less corrosion protection
(42).
Since the dissolution of phosphate coatings is directly related to corrosion protection,
the corrosion resistance can be improved by preventing the dissolution of phosphate, espe-
cially in a high pH solution.
Chapter II. Literature Review 8
2 - 2. Post-rinse Treatment.
2 - 2 - 1. Introduction.
The post-rinse treatment is another very important procedure to obtain increased cor-
rosion protection. After phosphating, the water rinse is a necessary step to remove the sol-
uble salts and unreacted phosphate ions. The improved corrosion resistance can be obtained
by water rinse which contains suitable corrosion inhibitors; certain cations or anions. In the
water rinse step, care should be taken to ensure that the water itself is sufficiently free from
the harmful salts.
The most commonly used compound in the post-rinse treatment is chromate which has
shown an excellent corrosion protection properties (18). Even though trivalent chromium is
regarded as the safer form and its use as a final rinse was more widely accepted by the in-
dustry than hexavalent compound, recently chromic acid has been labeled as a suspected
carcinogen by the EPA. As a result, metal product finishers are being forced to take another
look at the safer form of chromium or develop new materials for the post-rinse treatment.
2 - 2 - 2. Effect of Post-rinse Treatment on Corrosion Protection.
The post-rinse treatment is usually applied by immersion in a solution or spray, which
contains the desired ions. This treatment forms a rarely soluble film on the phosphate coating
by incorporating with ions in solution. The formation of the film seems to be related to the ions
used and phosphate coating itself. Even though the phosphate coating may look complete and
uniform, there is a certain amount of porosity in the coating. The porosity may come from the
Chapter II. Literature Review 9
poor surface preparation and/or the phosphate itself. Two mechanisms are proposed to ex-
plain the improvement of corrosion protection by the post-rinse treatment; the chemical and
the physical effects.
These two effects can be explained by the chromate post-rinse treatment. During the
post-rinse treatment, the chromate ions precipitates into the pores and on to the surface of
phosphate crystals. It is assumed that the precipitates adhere to the coating surface phys-
ically and act as a gel that fills the pores and results in a sealing effect by forming a thin film
of chromate compound which acts as an effective barrier for corrosion protection.
The action of post-rinse treatment is not confined solely to the precipitation of the insol-
uble film on the coating surface but also involves reactions with the phosphate coating itself.
The solution penetrates the coating to some degree and reacts with the phosphate ions in the
crystal resulting in the formation of a very insoluble compound, for example, chromium
phosphate. The insoluble phosphate film covers the coating and thus provides a sealing ef-
fect. Hence, it is thought that almost inhibiting effect is attributed to physical absorption of
precipitate, and chemical reactions provide improved adhesion of film to coating.
2 - 2 - 3. Possible Non-chromate Post-rinse Treatment.
Even though chromate post-rinse treatments have been applied to a wide range of in-
dustrial metals and show a great improvement in corrosion protection, they should be re-
placed by non- chromate post-rinse treatments due to the possible environmental problems
caused by chromate. For this purpose, several kinds of materials have been tried such as
inorganic silicate and other metallic ions . However, no treatment has yet been developed to
replace the chromate post-rinse treatment. In this research, to develop non-chromate post-
Chapter II. Literature Review 10
rinse treatment, well known corrosion inhibitors were tried as a treatment agent, such as
silicate in combination with calcium, barium, magnesium and nickel. The corrosion inhibition
of those elements has been reviewed (43).
Silicate is inexpensive, non-toxic and causes no serious environmental problems. It is
very stable in acidic solution except in hydrofluoric acid. Silica and silicate have been used
for corrosion protection because they provide a good barrier and act as inhibitors (44,45). One
of the widely used soluble silicates is sodium silicate, waterglass Na2 O-nSi02• The aqueous
solution of this is more or less polymeric depending on the ratio of silica to alkali. Soluble
silicate has been reviewed extensively (46) and recently, the effects of silicate on human
health have also been studied (47).
Calcium is one of the metallic elements used as a corrosion inhibitor (48,49) and calcium
phosphate has already been commercialized. This is the fifth abundant element in the earth's
crust and not toxic. Barium, belonging to the alkaline earth element group like calcium, has
almost the same chemical characteristics as calcium , but most barium compounds are toxic
except barium sulfate. Barium salts have been also used as a corrosion inhibitor (50).
Magnesium is another element in alkaline earth group. Magnesium has good resistance
to atmospheric attack and to certain chemicals because of its ability to acquire a protective
film, insoluble hydroxide film (51). Due to this ability, it has been used as a corrosion inhibitor
(52). However, despite its resistance to alkaline environment. it is susceptible to acids and
does not promote the formation of an insoluble film in an acidic environment.
Nickel has been used as anti-corrosive coating material, such as Zn-Ni alloy coating
(53,54), and as an activator in phosphating (35). Nickel is not readily oxidized in air at ordinary
temperatures. Nickel and its salts are not generally considered poisonous except nickel
carbonyl which is extremely toxic.
Chapter II. Literature Review 11
2 - 3. Silane Coupling Agent.
In recent years, the use of silane coupling agents has increased dramatically in the in-
dustries to obtain high strength plastic composites and to improve the bond strength of or-
ganic coatings to inorganic surfaces (55-61) and corrosion protection (62,63). In the
automotive industry, paint delamination is one of the major problems and is generally as-
sumed to be alkaline saponification of the polymer adjacent to the interface of metal as a re-
sult of cathodic corrosion reaction. The paint adhesion to metal or to inorganic coatings is
very important in corrosion protection. A number of investigations have been carried out and
the the application of silane coupling agents has dramatically increased recently.
2 - 3 - 1. Bonding Theory of Silane Coupling Agent.
Since minute proportions of coupling agents at the interface have a great effect on ad-
hesion promotion, it is necessary to understand the mechanism of adhesion promotion by a
silane coupling agents and the fundamental nature of them. The function of silane coupling
agent is to provide a stable bond strength between two different surfaces.
Several adhesion theories have been proposed but chemical bonding theory is the old-
est and predominant (64). Coupling agents contain two different types of reactive groups that
provide an ability to bond chemically to inorganic surfaces and organic polymers. The bond-
ing to the surface is made by chemical bonds, usually covalent bond, but, sometimes, van der
Waals forces or ionic bonds. Assuming that all this occurs, the coupling agents may act as
a bridge to bond the metal surface to paint coating. The bridge could be expected to lead to
strong chemical bonds.
Chapter II. Literature Review 12
2 - 3 - 2. Chemistry of Silane Coupling.
Silane coupling agents have two functional groups : organo and inorganic silicate to form
a bridge between inorganic substrate and organic polymer. The performance of
organofunctional silanes depends on the stable link between the organofunctional group (R)
and hydrolyzable group (X) in compounds of the general formula X3-SiR (64,65).
The organofunctional groups (R) usually react with the polymer surface while the
hydrolyzable groups (X) are merely intermediate in formation of silanol groups for bonding to
inorganic surfaces. In many commercial applications the silanes are pre-hydrolyzed and ap-
plied from dilute aqueous solution. Therefore, the nature of hydrolyzable group is not impor-
tant to the performance of the coupling agent, if adequate moisture is available for hydrolysis.
Silane coupling agents interact with receptive inorganic surfaces forming strong chemi-
cal bond at the interface. Receptive inorganic surfaces are characterized by the presence of
hydroxyl groups attached to certain elements, such as silicon and aluminum, in the formation
of hydrated oxides having absorbed water of hydration as their outermost layer. The coupling
agent is first converted to the reactive silanol form by hydrolysis;
R SiX3 + 3H20 -+ R-Si(OH)3 + 3HX
This reaction may occur on the surface or already brought in a previous step during prepa-
ration of solution of the coupling agent. The reaction is rapid in the presence of slightly
acidified water around pH 3 to 6.
The silanol form of the coupling agent now reacts with hydroxyl group in the inorganic
surface. Self condensation of the silanol forming siloxane polymer is an important side re-
Chapter II. Literature Review 13
action. When silica or alumina is present in the surface layer, the coupling reaction is readily
obtained since they are inherently receptive to coupling with silane.
-OH ----OH+(OH)3 Si(CH2)3 R_. ~-OH
OH 0Si(OH)2 (CH2)3 R+ H2 0 OH
Glasses, silicates and other Si-OH bearing siliceous materials share receptivity in pro-
portion to their silicon content. The coupling reaction of silane to the organic surface is easier
than to the inorganic surface. The organic chemistry predicts the formation of chemically
covalent bonds between the organofunctional group of silane and the reactive species in the
polymer matrix.
~ OH /1 I /Si-0-Si-R /~ I ~ OH
~ OH /o I ~1-0-Si-R ,,~ I ~ OH
2 - 4. Principle of Surface Analysis Techniques
In recent years, surface analysis techniques in combination with traditional tools for
corrosion research have become widely adapted to examine and solve many problems. It is
believed that such use will increase with time. A number of review papers are available on
Chapter II. Literature Review 14
the applications and basic principles of surface analysis techniques (66-75). In this research,
several surface analysis techniques were used such as SEM, EDX, AES, SIMS. In this section
the basic principles of these instruments will be reviewed briefly.
2 - 4 - 1. Basic Principles
In the instrument chamber, a sample is bombarded with the electron or ion beam which
was accelerated through an electric field and hence has acquired kinetic energy. The dissi-
pation of electron beam yields a variety of signals for the analysis of sample as depicted
schematically in Fig. 1. Auger and secondary electrons escape from the surface layers of the
sample. The secondary electrons which emerge from near the sample surface are detected
to form an image of the sample in the SEM while Auger electrons are for the AES analysis.
The characteristic X-rays having much greater escape depth than electrons, provide ele-
mental information; therefore, they are used for EDX or WDX to identify the elements.
2 - 4 - 2. Scanning Electron Microscope.
SEM is by far the most powerful instrument for obtaining topological information. In the
corrosion research SEM is widely applied usually in combination with EDX, WDX or others
such as AES. The principle of and the applications of this on corrosion research have been
published (66,67). A fine probe electron beam is used for rastering the sample. The SEM
image is obtained by scanning the beam across the sample and by detecting the low energy
secondary electrons or high energy backscattered electrons returning from the surface of the
sample. The detection of electrons is achieved by means of a scintillator -photomultiplier ar-
rangement, that is positively biased by several hundred volts. The signal is fed to a cathode
Chapter II. Literature Review 15
Cathodoluminescence (visible light)
lncldlent Electron Beam
Bremsstrahlung
Characteristic X-rays
-.
Specimen Current
Auger Electrons
Secondary Electrons
Elastically Scattered Electrons
Transmitted Electrons and lnelastlcally Scattered Electrons
Figure 1. Variety of signals produced by electron bombardment.
Chapter II. Literature Review 16
ray tube (CRT) and surface topology and elements give rise to different signal intensity
;therefore, contrast is obtained on the CRT.
The SEM has a remarkable depth of field and better resolution compared to optical
microscopy providing a three-dimensional image. One of advantages is large samples can be
analyzed. However, the major problem is the charging of insulating materials which can be
overcome by applying thin conductive coating on the surface of the sample.
2 - 4 - 3. Energy Dispersive X-ray Analysis.
When the primary beam bombards the sample, the characteristic x-ray as well as
electrons are generated. However, it was not utilized until the solid state detector (Li or Si)
had become available to resolve the x-ray peaks of adjacent elements in the periodic table.
In EDX, the characteristic x-rays are detected by the liquid nitrogen-cooled Si (or Li )
detector. The energy of x-rays are translated proportionally to the pulse mode which is fed
to a multichannel analyzer. By accumulating the pulse, x-ray spectrum is processed by a
computer.
EDX techniques have many advantages, such as a satisfactory compromise between a
multi-element character, ~conomy, speed and ease of operation. Also EDX offers a fairly uni-
form detection limit across a large portion of periodic table. However, it is at most a semi-
quantitative analysis technique. The details of EDX have been reported in the literature
(68,69).
Chapter II. Literature Review 17
2 - 4 - 3. Auger Electron Spectroscopy.
During the past decades, the technique of AES has emerged as one of the most widely
used analytical tools for acquisition of the chemical information. The fundamental mechanism
involved in AES are ionization of core level atom by the bombardment of electrons. Auger
electrons escape from near the surface of the sample and are characteristic of the target
materials, and the measured energy of Auger electrons is not dependent on the primary en-
ergy. Since Auger electrons have well defined energies, they are manifested as small peaks
in the total energy distribution function { N{e)). The differential spectrum is usually recorded
by removing the background.
The peak positions are characteristic of particular elements allowing qualitative analysis
of all elements except H, He and sometimes Li. AES is particularly sensitive to light elements
and the analytical characteristics of AES are listed in Table 1(70). The depth profiling in AES
can be performed during the analysis. The one disadvantage is that quantification is difficult.
The mechanisms and applications of AES have been reported in detail {71,72).
2 - 4 - 4. Secondary Ion Mass Spectrometry.
SIMS is one of the true surface analysis techniques, which has higher sensitivity, ability
to detect all elements and information from the outermost layers {73-75). The principle
mechanism of SIMS is almost the same as that of AES. In SIMS, however, an ion beam instead
of an electron beam is used for bombardment, which is usually an inert gas ion such as Ar+,
o;, Ga+ or cs+. By bombardment with an ion beam of 2 to 20 keV, considerable disruption
occurs by transfer of momentum to lattice atoms, which result in the eruption of atomic and
molecular fragments from the several atomic layers deep, consisting of mainly neutral and a
Chapter II. Literature Review 18
Table 1. Analytical characteristics of AES (70).
Kinetic energy : 50 - 2500 eV Energy range Escape depth : 20 A0
Peak location : ± 1eV
Chemical information Marginal
Elements : Z > 2 Elemental sensitivity Signinificity : good
Sensitivity variations : SOX
Absolute : ± 30 percent Quantitative analysis Relative : ± 5 percent
Detection limit : 0.005 monolayer Matrix effect : some
Vacuum : 10-1 - 10- 11 torr Depth profiling: yes, rapid, multiplex
Other aspects X-Y resolution : 0.5µ Elemental mapping : yes Speed : fast, most spectra takes minutes Sample destruction : particularly bad for organics
Chapter II. Literature Review 19
few percent of positively and negatively charged fragments. In SIMS analysis, only positively
or negatively charged ions are collected to form the mass spectrum which gives rise to the
peaks presenting elemental species and cluster ions.
SIMS has two variations depending on the operating conditions; dynamic and static
mode. Even though SIMS is a very sensitive surface analysis technique, it has limitations.
Charge builds up when insulators are analyzed, which could be eliminated by compensating
the charge ionization with appropriate low energy electron flux. The analytical characteristics
of SIMS are shown in Table 2 (74).
Chapter II. Literature Review 20
Table 2. Analytical characteristics of SIMS (74)
Spectral range 1 - 500 amu
Analysis depth 40 A0 (dynamic), monolayer (static)
Chemical information Mass spectrum from surface layer
Element - all Elemental sensitivity Specificity - good (some overlap)
Sensitivity variation - 10- 5
Absolute - not possible Relative - ± 50 percent
Quantitative analysis Detection limit - 10- 4 percent nomolayer Matrix effect - severe
Vacuum : 10- 5 torr of ionizing gas Depth profiling : Yes, rapid, 'dynamic' SIMS
Other aspects X - Y resolution : 1 µ with ion microprobe Elemental mapping : As a microprobe Speed : fast, most spectra take minutes Sample destruction : yes, sputtering of surface
Chapter II. Literature Review 21
Chapter Ill. Experimental
The phosphate ions are leached out in a high pH solution (32), which is directly corre-
lated with the corrosion protection (34) and paint adhesion failure (25). In this investigation,
a non-chromate post-rinse treatment was applied to the phosphate coating in order to reduce
the amount of leaching of phosphate ions in a high pH solution; hence to improve the corro-
sion protection and paint adhesion.
Seven different solutions were tried as post-rinse treatment agent. After the post-rinse
treatment, some samples were immersed in a KOH solution of pH 12.5 to see how effective
this treatment was, named as an immersion test, and others were submitted to the silane
treatment or the heat treatment. The general procedure of the experiment is shown in Fig.
2. The variability and brittleness of the phosphate coating were also evaluated before and after
the post-rinse treatment. Heat treatment was performed at 110° C for 24 hours and at 180° C
for 30 minutes after the post-rinse treatment. The silane treatment was applied to the selected
samples.
For the characterization of the treated samples, the surface analysis techniques, such
as AES and SIMS, were applied, and X-ray diffraction analysis and polarization measurements
Chapter Ill. Experimental 22
POST RINSE TREATMENT
SI LANE TREATMENT
ANALYSIS
Figure 2. General procedure of treatment
Chaper Ill. Experimental
HE AT TREATMENT
23
were also used for further evaluation. However, most of analysis was performed by Scanning
Electron Microscopy(SEM) and Energy Dispersive X-ray Analysis (EDXA or EDX).
3 - 1. Sample Preparation.
3 - 1 - 1. Raw Materials.
The as-received steel panel was cold-rolled, electrogalvanized, type GM-16-20E, and one
side sprayed phosphated using Granodine 902, which is the same material used in the auto-
motive industry. The panels were supplied by the project sponsor, Amchem Porducts Inc. of
Ambler, Pa.. The specification of the panels is listed in Table 3. The sample panels were
sheared to 1x2 inch rectangular pieces and a hole of 1/8 inch in diameter was punched at the
top center of th·e sample.
3 - 1 - 2. Experimental Conditions.
During the treatments, a magnetic stirrer, Corning Pc-351, was used at a speed of 240
RPM. All samples were treated in 500 ml of solution at 25° C in 600 ml beaker. In the post-
rinse treatment, pH of all solutions was adjusted to 12.0 and in the immersion test, to 12.5. A
pH-meter, Beckman 4500, was calibrated with buffer solutions of pH 7 and 10 prior to the ex-
periments. The treatment was carried out for 30 minutes in the post rinse treatment, for 10
or 20 minutes in the immersion test and for 5 minutes in the silane treatment, respectively.
The pH of all solutions was adjusted by dissolution of the reagent KOH. Usually, two samples
were treated simultaneously but sometimes they were treated for different time duration. Fig.
3 shows the schematic diagram of the treatment setting.
Chapter Ill. Experimental 24
Table 3. The specification of sample panel
Material Cold rolled steel
Thickness 0.030 inches
Size 4x12 inches
Hardness B 60-45 Re
Carbon SAE 1008
Coating 0.54 mils Electrogalvanized
Phosphate Granodine 902 sprayed
Chapter Ill. Experimental 25
Water in
®0
Figure 3. Schematic diagram of treatment setting 1. Thermometer 2. Sample 3. Heat control 4. Speed control
Chapter Ill. Experimental
Water out
0®
26
The heat treatment was carried out for the elected samples either at 180° C for 30 min-
utes or at 110° C for 24 hours. Before the heat treatment, the oven was calibrated and stabi-
lized by waiting for one hour. The immersion test was performed before or after the heat
treatments at both temperatures. After the heat treatment, the samples were cooled to room
temperature.
3 - 1 - 3. Solution Preparation.
The seven different solutions were prepared for the post-rinse treatment, as listed in
Table 2. The waterglass solution was first made by diluting waterglass with deionzed water
to 0.05M concentration and then futher diluted to the molarity needed. The other solutions
were prepared by dissolving the chemical(s) into the 0.005M waterglass solution. The general
procedure of preparing the solutions is as follow except that of the silane solution which will
be described later.
1. Weighing the exact amount of chemical(s)
2. Dissolving the chemical(s) in a solution of 0.005M waterglass
3. Adjusting pH and temperature
The research or reagent grade chemicals were used, which are listed in Table 5. To get
the optimun result, one or more chemicals were dissolved in the 0.005M waterglass solution.
When the chemical(s) were dissolved completely, pH and temperature were adjusted to 12.0
and 25° C.
Chapter Ill. Experimental 27
Table 4. List of chemicals
Chemical Grade Manufacturer
Waterglass 40-42 Be Fisher
Zinc Sulfate Reagent Fisher
Calcium Nitrate 99.5 percent Mallinckrodt
Nickel Sulfate 97.1 percent Baker
Magnesium Sulfate 99.5 percent Baker
Barium Nitrate 99.4 percent Baker
Chapter Ill. Experimental 28
Table 5. Solutions used in post-rinse treatment
Solution Chemical Rinse
WG 0.005M waterglass Yes
wz 0.005M waterglass + 0.01 M zinc sulfate Yes
WC 0.005M waterglass + 0.005M calcium nitrate Yes/No
WB O.OOSM waterglass + 0.005M barium nitrate No
WCB Solution WC + 0.005M barium nitrate No
WCN Solution WC + O.OOSM nickel sulfate No
WCM Solution WC + 0.005M magnesium sulfate No
Chapter Ill. Experimental 29
A wide range of molarity was tried to find the optimum molarity of solution such as
waterglass, 0.005M waterglass + zinc sulfate and 0.005M waterglass + calcium nitrate sol-
ution. For the immersion test, the solution of pH 12.5 was made by dissolving KOH in
deionized water.
y -Aminopropyltriethoxysilane ( y-A.P.S.) was used for the preparation of the silane
solution. y -A.P.S. was hydrolized by 100 parts of y -A.P.S., 5 parts of acetic acid and 25 parts
of deionized water, and stirred for about 30 minutes until a clear solution was obtained. This
silane solution containing about 30 percent of active ingredient was diluted with deionized
water again to 0.5 percent of active solution (76).
3 - 1 - 4. Experimental Procedure.
The post-rinse treatment was carried out right after the solutions were prepared to avoid
the deterioration, such as precipitation. As soon as the post-rinse treatment was completed,
some samples were rinsed with deionized water and dried by air blown at room temperature
while others were just dried in air. The post-rinse treatment was followed by either the
immersion test, the heat treatment, the silane treatment or the analysis. The general proce-
dure of post-rinse treatment is as follow.
1. Treating samples for 30 min. in solution
2. Rinsing with deionized water ( optional; see Table 5 )
3. Drying by air blown at room temperature
Chapter Ill. Experimental 30
4. Immersing some of the samples in a solution of pH 12.5 for 10 and 20 min. ( others sub-
jected for analysis, heat treatment or silane treatment)
5. Repeating step 2) and 3)
6. Analyzing
The brittleness test of the phosphate crystals was carried out for selected samples. The
samples, 1/8 inche, were punched from the sample panels before and after the post-rinse
treatment in solution WC, and after the immersion test for 10 min.
Heat treatment was carried out for the samples treated in a solution WC and WCB at 110
0c and at 180 °c for 24 hours and 30 minutes, respectively. In the first stage of heat treatment.
Heat Treatment I, the treatment steps are i) post-rinse treatment, ii) immersion test, iii) heat
treatment, while in the second stage, Heat Treatment II, the steps ii) and iii) are switched.
After the heat treatment, the samples were cooled down to room temperature in air.
The silane treatment was applied to the samples treated in solution WC, WB and WCB.
The samples were treated in 0.5 percent silane solution for 5 minutes and dried by air blown
at room temperature. After the silane treatment, the samples were aged at room temperature
for 24 hours before further treatment. Some of the silane treated samples were analyzed and
others were immersed in a solution of pH 12.5 for 10 and 20 minutes and rinsed, dried and
analyzed.
Chapter Ill. Experimental 31
3 - 2. Sample Analysis.
3 - 2 - 1. SEMIEDX Analysis.
The samples for the SEM/EDX analysis were prepared by punching a piece , 3/8 inches
in diameter, from the treated sample panels and were carbon coated with Denton Vacuum
Evaporator, DV-502, to avoid charging problem since the zinc phosphate is not a good con-
ductor. SEM, Jeol JAX-840 Scanning Microanalyzer, combined with a Tracoer Northern EDX
analysis sytem, TN-5500, was used at 15 kV. The EDX data was acquired for 60 seconds of
live acquisition time from the area of 1.2 mm x 0.9 mm. The EDX analysis was performed three
times per sample. The spectra obtained were analyzed quantitatively and qualitatively.
3 - 2 - 2. AES/SIMS Analysis.
For a better understanding of mechanism of phosphate stabilization by post-rinse treat-
ment, AES/SIMS as well as SEM/EDX were applied in this research. A Perkin-Elmer PHl-610
Scanning Auger Microprobe was used for AES/SIMS analysis of selected samples, which was
equipped with a quadrupole mass analyzer with a mass range of 1 to 511 amu. A defocused
beam was used for a survey scan of AES at 7kV, and depth profiling was performed with
Ar+ ion sputtering. In SIMS analysis, 1 kV Ar+ ion source was used for the survey scan.
Chapter Ill. Experimental 32
3 - 2 - 3. X-Ray Diffraction Analysis.
The X-ray diffraction analysis was utilized to ascertain the protection of phosphate
coating by the treatment. The diffraction spectra were obtained from the samples which were
immersed in a solution of pH 12.5 for 20 minutes after the post-rinse treatment and/or the
silane treatment. The spectra were obtained by using Cu Ka radiation with a Rigaku-200. The
experimental conditions were 40kV, 80mA, 2 degree per minute of scan rate and time con-
stant of 1.
3 - 2 - 4. Polarization Measurement.
An open "L" shaped plastic cylinder was used for sample mounting where a 0-ring
gasket was placed between the cylinder and the sample surface to avoid leakage of salt sol-
ution. At the open end of the cylinder, 1.54 cm2 of treated sample surface was exposed to an
aerated and stirred 5 percent NaCl solution for one hour before measurements. The anodic
and cathodic polarization curves were obtained with Potentiostat, Princeton Applied Research
Model-173, in a broad potential range at a scan rate of 1mV per second. A saturated calomel
electrode ( S.C.E.) and a platinum electrode were used as a reference and a counter
electrode, respectively. The schematic diagram of polarization measurement setting is shown
in Fig. 4.
Chapter Ill. Experimental 33
w E
R E
c E
Figure 4. Schematic diagram of polarization measurement setting. I = Ampere meter E = Volt meter
Chapter Ill. Experimental 34
Chapter IV. Results and Discussion
The phosphate stability in a highly alkaline solution was improved by the post-rinse
treatment, especially in the solutions containing Ca2+ and Ba2+. Barium added waterglass
solution showed the best result in the prevention of phosphate dissolution in the immersion
test. The silane treatment, applied to post-rinse treated sample, improved the phosphate
stability further. However, the heat treatment did not reduce the dissolution of phosphate
crystals in the immersion test but rather accelerated.
The data from the SEM/EDX and AES/SIMS indicated that thin film had formed by the
post-rinse treatment and the silane treatment. The thin film, which should be a silicate com-
pound film containing zinc and other metallic ions, increased the stability of phosphate due
to the very low solubility and high alkaline resistance. The results from x-ray diffraction and
polarization measurements confirmed that the leaching of phosphate crystals was reduced
and corrosion resistance was improved by the post-rinse treatment as well as by the silane
treatment.
Chapter IV. Results and Discussion 35
4 - 1. SEM/EDX Results.
4 - 1 - 1. Post-rinse Treatment.
The leaching of phosphate ions was observed by SEM/EDX. The relative percentage of
phosphorus in a coating layer decreased rapidly with time in a high pH solution. Fig.5 and 6
show the change of relative percentage of phosphorus in coating layer with time in a solution
of pH 12.0 and 12.5 respectively. Almost all phosphate crystals were leached out in an hour
in a solution of pH 12.0 and in 30 minutes in a solution of pH 12.5, respectively.
Fig. 7 shows the phosphate crystals of as-received sample before any treatment. The
needle-like crystals, ( hopetite, Zn3(P04) 24H20 ), are presented, which are usually produced
by spray application (6). As expected , the dissolution of phosphate crystals was observed in
the solution of pH 12.0 and 12.5 as shown in Fig. 8 and 9, respectively. These micrographs
show that all phosphate crystals disappeared in an hour in a solution of pH 12.0, and in 30
minutes in a solution of pH 12.5. The leaching of phosphate ions is directly related to pH and
length of treatment time. Therefore, the investigation aimed at the prevention of phosphate
dissolution in an alkaline media by non-chromate post-rinse treatment.
The samples treated in a wide molarity range of the waterglass solution of pH 12.0 for
30 minutes showed that the leaching of phosphate ions varied depending on the molarity of
waterglass. Fig. 10 shows the phosphate stabilization in the waterglass solution treatment.
The leaching of phosphate decreased with increasing molarity of waterglass up to the molarity
of 0.0075 and increased at the higher molarity than 0.0075M. The relative percentage of silicon
increased with the waterglass treatment from about 2 percent of as-received sample to as
high as 7.5 percent, but the increasement of silicon did not depend on the molarity of
waterglass in the treatment solution. It is suggested that only certain amount of silicate
Chapter IV. Results and Discussion 36
20
-~ 0 -0 -0..
10
0 15 30 45 60 Tl ME(mi n)
Figure 5. Leaching of phosphate in a solution of pH 12.0.
Chapter IV. Results and Discussion 37
30 ,...----------------------
20
-~ ... 0 -a..
10
0 5 10 TIME(min)
Figure 6. Le~ching of phosphate in a solution of pH 12.5.
Chapter IV. Results and Discussion
15 20
38
Figure 7. Phosphate crystals of as-received sample
Chapter IV. Results and Discussion 39
a
b Figure 8. Phosphate crystals after treatment in a solution of pH 12.0 for 30minutes(a) and one
hour(b).
Chapter IV. Results and Discussion 40
a
b
Figure 9. Phosphate crystals after treatment in a solution of pH 12.5. for 10(a) and 20 minutes(b).
Chapter IV. Results and Discussion 41
(silicon) precipitated on the phosphate crystals regardless of the molarity of waterglass in the
solution and silicate content is related to some degree to the stabilization of phosphate coat-
ing in a high pH solution.
The waterglass solution (0.005 M) was chosen for the later post-rinse treatments since
the result obtained at this molarity was almost same as that obtained at the molarity of 0.01
and 0.0075. The degree of destruction of phosphate crystals in the waterglass treatment
showed the same trend as that of the leaching of phosphate ions in the wide molarity range
of waterglass solution.
The relative percentage of phosphorus of the sample treated in a solution WG, 0.005 M
waterglass solution of pH 12.0, for 30 minutes was about 22 percent and that of as received
sample immersed in a solution of pH 12.0 for 30 minutes was about 7 percent, while that of
as-received sample without any treatment was around 28 percent. Fig. 11-a shows the
morphology of the sample treated in a solution WG for 30 minutes.
The dissolution of phosphate crystals by the post-rinse treatment in a solution WG for
30 minutes was much less than that by immersion in a solution of pH 12.0 for the same time
duration. The addition of waterglass reduced the dissolution of phosphate crystals. The
waterglass treatment improved the stabilization of phosphate coating in a solution of pH 12.5,
especially when the concentration of waterglass was optimum. One of the graphs in Fig. 12
shows the change of silicon content by the treatment in solution WG followed by the
immersion test. The relative percentage of silicon increased significantly with the waterglass
treatment. It suggests that the increasing silicon content improved the stabilization of
phosphate ions in a high pH solution. The possible mechanism of this is a formation of a thin
film of silicate or silicate compound with zinc and/or phosphate ions in solution. Due to the
higher alkaline resistance of the thin film and hence, the reduced phosphate dissolution, better
corrosion protection would be obtained.
Chapter IV. Results and Discussion 42
:E ~(Jl f"T1 :::a G> r l> CJ) CJ) -3· 0 (1)
~o 0.
c;I -
(Jl
P ( Q f 0/o)
0
0
(JJ 0
Figure 10. Effect of waterglass on the stabilization of phosphate in a solution of pH 12.0 for 30 minutes.
Chapter IV. Results and Discussion 43
a
b Figure 11. Dissolution of phosphate crystals after treatment in solution WG (a) and WZ (b) for 30
min.
Chapter IV. Results and Discussion 44
Si ( 0 f 0/o) 0 N (>J
l> ::u
~ G')
N CJ) :: : :.:::::·1----
() z ::u () I I II 111 z CD z
I I II Ill
~ D () '1) '1) -0 3: CJ)
:I: :I: 0 CJ)
N N ~ () z CJ)
() CD
. 01 01 :::0 N z 0 0 CJ)
~ ~ rii 11111 11 11 I z
Figure 12. Change of silicon content by the post-rinse treatment and followed by immersion test for 10 and 20 min.
Chapter IV. Results and Discussion 45
Even though the phosphate stabilization was improved dramatically by the treatment in
solution WG for 30 minutes, this treatment improved the phosphate stabilization slightly in the
immersion test for 10 minutes but not for 20 minutes compared to the result from the as-
received sample. The results of the immersion test of the samples treated in solution WG are
shown in Fig. 13. The phosphate crystals of sample treated in solution WG totally disappeared
in 20 minutes in the immersion test. The immersion test shows that the post rinse treatment
in solution WG is not effective enough to protect the phosphate coating in a high pH solution.
On the other hand, the silicon content decreased slightly by the immersion test of the
samples treated in solution WG but was still high as shown in Fig. 12. It indicates that the
post-rinse treatment in waterglass solution had a limited effect on phosphate stabilization in
a high pH solution and that the leachability of phosphate ions in a high pH solution is different
from that of silicon.
Fig. 14 shows the results of treatment in a solution of varied molarity of zinc sulfate
added 0.005 M waterglass solution at pH 12.0 for 30 minutes. The relative percentage of
phosphorus decreased slightly with the increasing zinc sulfate molarity. However, Fig. 11-b
shows that the phosphate crystals of samples treated in a solution WZ for 30 minutes were
destroyed less than those treated in solution WG for the same time. Even though the relative
percentage of phosphorus decreased with the increasing zinc sulfate molarity, the phosphate
crystals did not follow the same trend as that shown in the waterglass treatment. It is as-
sumed that the zinc ions in the solution adhered to the surface of the sample, which decreased
the relative intensity of phosphorus.
The results of the immersion test of the samples, treated in solution WZ for 30 minutes,
are shown in Fig. 13. Even though the relative percentage of phosphorus decreased, the
treatment slightly improved the phosphate stabilization in the immersion test compared to the
treatment in solution WG. After the immersion test for 20 minutes, the relative percentage of
Chapter IV. Results and Discussion 46
-~ 0 +-0 -a..
20
10
0 5
-0- ·AR -0- WG -0- WG+ZS -ts- WG+CN(R) -0- WG+CN
10 TIME(min)
15 20
Figure 13. Effect of post-rinse treatment on the phosphate stabilization in the immersion test.
Chapter IV. Results and Discussion 47
()1
N -z n en c-ro ,, l> -I rr1 -3 0 (1)
x 0 ~ -
()1
N 0
N ()1
P (at 0/o)
0 N 0
0
Figure 14. Effect of zinc sulfate on the stabilization of phosphate in solution WZ.
Chapter IV. Results and Discussion
(JJ 0
48
phosphorus was about 1 percent; however, all the crystals disappeared. The post-rinse treat-
ment in solution WZ did not have a positive effect on the stabilization of phosphate coating in
a solution of pH 12.5.
After the treatment in solution WZ for 30 minutes, almost the same amount of silicon was
detected as that in the sample treated in solution WG as shown in Fig. 12. However, the silicon
content decreased significantly in the immersion test for 20 minutes but not less than 1 per-
cent. The improvement of phosphate stability might be explained by the same hypothesis as
that used in the waterglass solution treatment; the formation of a thin film of silicate or silicate
compound. The addition of zinc to waterglass solution increased the phosphate stability very
little in a high pH solution. The reachability of silicate (silicon) was increased by addition of
zinc in the immersion test.
The phosphate stabilization of samples treated in 0.005 M waterglass + varied molarity
of calcium nitrate solution of pH 12.0 for 30 minutes is presented in Fig.15. The relative per-
centage of phosphorus was greatly improved up to that of the as-received sample, and did
not depend on the molarity of calcium nitrate in a solution. Even a very small amount of
calcium added to waterglass solution of pH 12.0 protected the phosphate completely.
The phosphate crystals of samples treated in solution WC look similar to those in the
as-received sample, shown in fig. 16-a. However, the silicon content was less than that in the
sample treated in solution WC, while the calcium content was increased; the amount of in-
crease in the calcium content is much less than the amount of decrease in silicon. Calcium
together with silicate is very effective in improving the phosphate stability in a high pH sol-
ution. It is suggested that a thin film formed by calcium added waterglass solution treatment
is much more effective in the phosphate stabilization than that formed by waterglass or zinc
added waterglass solution treatments. The added calcium seems to decrease the solubility
Chapter IV. Results and Discussion 49
0
nCJl )> r ()
c 3:: -~o -i ::0 l> ~ m -3 01 0 CD )C
~N 0
0
P (at 0/o) N 0
Figure 15. Effect of calcium on the phosphate stabilization
Chapter IV. Results and Discussion
0
(>J 0
~ 0
50
of thin film and increase the alkaline resistance ;hence, increase the stability of phosphate
ions in a high pH solution.
As described in the experimental section, two different options were applied to the
samples treated in solution WC; deionized water rinse and no rinse. The observed differences
between the deionized water rinsed sample and the non-rinsed sample after the post-rinse
treatment in solution WC were the relative percentages of silicon and calcium, and the degree
of the stabilization of phosphate ions in the immersion test. The less relative percentages of
phosphorus and silicon were detected with deionized water rinse, therefore, the less stability
of phosphate ions in the immersion test.
The post-rinse treatment in solution WC is much more effective in the stabilization of
phosphate in the immersion test than the treatments in solution WG or WZ, which is shown in
Fig. 13. It is also shown that rinsing with deionized water gave poorer protection. Even after
20 minutes in the immersion test, the non-rinsed sample showed about 5 percent of
phosphorus while the rinsed one showed only about 0.5 percent. The addition of calcium to the
waterglass solution improved the phosphate stability even in the immersion test for 20 min-
utes.
The leaching of the phosphate crystals in the immersion test of the sample treated in
solution WC for 30 minutes (non-rinsed) is shown in Fig. 17. The non-rinsed sample showed
some crystals even after the 20 minute immersion test, while the rinsed one did not show any
crystals (micrographs are not included, see Fig. 9-b). This is due to the increased resistance
of the thin film to alkali by addition of calcium and much less protection is obtained by
deioninzed water rinse which removed added elements partly on the surface of phosphate
coatings.
Chapter IV. Results and Discussion 51
a
b Figure 16. Morphology change by the treatment in solution WC (a) and WB (b) at pH 12.0 for 30
min.
Chapter IV. Results and Discussion 52
.a
b Figure 17. Dissolution of phosphate crystals In the Immersion test for 10(a) and 20 min.(b) after
treatment in solution WC.
Chapter IV. Results and Discussion 53
As shown in Fig. 12, the silicon content of the non-rinsed sample decreased slightly while
that of the rinsed sample decreased significantly by the immersion test. This also indicates
that the silicon content is related to the stabilization of phosphate in a high pH solution. The
relative percentage of silicon of the non-rinsed sample treated in solution WC is less than that
of samples treated in solution WG and WZ. It could be due to the added calcium which de-
creased the reactivity of silicate in solution to the phosphate coating.
Solution WB was made by substituting calcium with the stoichiometric amount of barium
nitrate in solution WC. All samples treated in solution WB were dried by air blown at room
temperature without deionized water rinse. The relative percentage of phosphorus detected
by the EDX analysis is similar to that from the sample treated in solution WC, which is almost
the same as that of the as-received sample. The treatment in barium added waterglass sol-
ution (WB) completely prevented the dissolution of phosphate crystals in a solution of pH 12.0,
just as in the calcium added waterglass treatment. In the immersion test, however, the barium
added waterglass solution treatment showed the best protection of the phosphate coating than
any other treatment, as presented in Fig 18. The micrographs of the smples treated in solution
WB followed by the immersion test are shown in Fig. 19. Even after 20 minutes of immersion,
fairly good phosphate crystals were observed and about 13 percent of phosphorus was de-
tected by EDX analysis.
The silicon content after treatment in solution WB was almost the same as that after
treatment in solution WC, and was decreased slightly by the immersion test, as shown in Fig.
12. The decreased dissolution of silicate(silicon) from the phosphate coatings in the
immersion test seems to arise from the added barium and can be related to the phosphate
stability. The results of the post-rinse treatments in solutions WCB, WCM, and WCN ·followed
by the immersion test are also shown in Fig. 18. These post-rinse treatments did not show
any difference among themselves in the relative percentage of phosphorus, which was same
as that of the as-received sample, consequently, they prevented the dissolution of phosphate
Chapter IV. Results and Discussion 54
-~ 0 ... 0 -CL
20
10
0
-0- WG+BN -6- WG+CN+NS -<)- WG +CN +MS -0- WG+CN+BN
5 10 15 20 TI ME(m in)
Figure 18. Effect of the post-rinse treatments in solution WB, WCN,WCM and WCB on the phosphate stabilization in the immersion test.
Chapter IV. Results and Discussion 55
a
b Figure 19. Dissolution of phosphate crystals of samples treated in solution WB in the immersion
test for 10 (a) and 20 min.(b).
Chapter IV. Results and Discussion 56
crystals completely. However, The immersion test showed significant differences in terms of
the relative percentage of phosphorus and the phosphate crystals.
The samples treated in solutions WCM and WCN showed poorer results than those
treated in solution WC in the immersion test. However, the samples treated in solution WCB
showed the same result as those treated in solution WC in the immersion test. Even though
the separate use of calcium and barium improved the stability of phosphate coating in the
immersion test, as discussed before, the improvement from the mixture of these did not ex-
ceed that obtained by the use of barium nitrate alone. This suggests that barium nitrate could
not make insoluble film if calcium nitrate is dissolved in the same solution or vice versa.
These results also indicate that magnesium sulfate and nickel sulfate had a negative effect
on the stabilization of phosphate in a high pH solution.
The analytical data by SEM/EDX reveal that the best post rinse treatment carried in this
research is the treatment in solution WB, 0.005M waterglass + 0.005M barium nitrate solution
of pH 12.0. The possible mechanism to explain this result is the formation of silicate com-
pound film on the phosphate coating by the post-rinse treatment. The improved stability of
phosphate coating in a high pH solution is due to the higher resistance of film to alkaline
solution and the sealing effect of the film.
The different results from the different treatments are related to the nature and the re-
activity of the chemicals. Some chemicals, such as barium, make a virtually soluble film with
silicate, which has higher alkaline resistance, while others such as nickel do not. One thing
to be pointed out here is that nickel and magnesiulTI, which are well known corrosion
inhibitors like calcium, did not improve the stability of phosphate coating in a high pH solution.
Chapter IV. Results and Discussion 57
4 - 1 - 2. Variability and Brittleness.
During the experiment, it was found that the relative percentage of phosphorus varied
from one sample to another. Therefore, the analysis with SEM/EDX was carried out on ten
randomly selected sample panels. The samples were treated in solution WC and immersion
tested for 10 minutes. The analysis was carried out at all stages of the treatments.
In the study of as received samples, the relative percentage of phosphorus varied from
25.68 to 30.26. Other statistical data are listed in Table 6. The analytical data show that the
percentage of phosphorus was high whenever those of nickel and silicon were high. Among
them, silicon was more directly related to the phosphorus content. Fig. 20 shows the vari-
ability of phosphorus, silicon and nickel of as-received sample. The relationships between
these elements are shown in Fig. 21 where a slight relationship exists between phosphorus
and silicon, and nickel.
The relative percentage of elements in the phosphate coating was changed by the
post-rinse treatment in solution WC for 30 minutes, which is shown in Fig.22. After the post-
rinse treatment, the relative percentage of phosphorus and nickel was unchanged, but the
relative percentage of silicon and calcium increased.
The results of the immersion test for 10 minutes after the post-rinse treatment in solution
WC for 30 minutes are shown in Fig. 23. The relative percentage of phosphorus and silicon
decreased by more than 50 percent based on the average value. However, that of nickel, less
than 1 percent, did not decrease. As a result, it is believed that not only phosphorus but also
silicon was leached out in the immersion test. The same relationships among phosphorus,
silicon and nickel exist after treatment in solution WC as those in the as-received samples.
Chapter IV. Results and Discussion 58
Table 6. Average and standard deviation value of the variability treatment.
As-received
p Si Ni Ca
AVG. 27.61 1.75 0.80 0.17
S.D. 1.58 0.11 0.10 0.02
Waterglass +Calcium nitrate
p Si Ni Ca
AVG. 28.01 2.21 0.75 0.36
S.D. 1.37 0.43 0.18 0.12
After immersion test for 10 min.
p Si Ni Ca
AVG. 9.61 1.08 0.53 1.09
S.D. 3.04 0.18 0.05 0.04
Chapter IV. Results and Discussion 59
J\)
(>I CJ)
~~ -c r 01 fT1
z cm ~ CD -J fT1 :::0
CD
a
0 0
0
P (at 0/o) N 0
(>J 0
J\) (>J
S i a N i { O t 0/o )
Figure 20. Variability of P, SI and Ni In as-received sample.
Chapter IV. Results and Discussion
~ 0
~~9 zcn-c -· -·
60
S i a N i ( a t 0/o)
-c -~ 0 -
t> ~~ z Cf) -· -·
Figure 21. Relationship between P, Si and NI in as-received sample.
Chapter IV. Results and Discussion 61
0
N
(>J
CJ) l>~ ~ -0 r 01 f'T'1
Zm c ~ CD -J rT'1 :0 CX>
0
0
0
P (at 0/o) N 0
(>J 0
N (>J
Si a Ni (at 0/o}
~ 0
~~9 ~~-0
Figure 22. Effect of treatment on variability: Variability of P, Si and Ni after treatment in a sol-ution WC for 30 min. at pH 12.0.
Chapter IV. Results and Discussion 62
0
0
P(at 0/o)
0
N (>I
Si Ni (at 0/o}
N 0
Figure 23. Effect of Immersion test on variability: Variability of P, Si and Ni after treatment in a solution WCB followed by the immersion test for 10 min.
Chapter IV. Results and Discussion 63
The phosphate stability in a high pH solution is, in some degree, related to the content
of silicate(silicon) and calcium in the coating layers. Due to the limited detectability of EDX,
which is only a semi-quantitative analysis technique, it is difficult to give full credit to the re-
sults, especially on the content of nickel and calcium which are less than 2 percent.
When the samples were analyzed with SEM, some cracks were found on the edges of
the sample. In Fig. 24, the cracks in the phosphate crystals of as-received sample is shown.
Since the samples were hole punched to be analyzed in the SEM, the cracks in the phosphate
crystals were formed by the punching. The formation of cracks indicated that the phosphate
crystals were brittle. The number of and length of crack per unit area were decreased slightly
by the post-rinse treatment in solution WC, 0.005 M waterglass + 0.005 M calcium nitrate
solution of pH 12.0. This is probably due to the post-rinse treatment which decreased the
brittleness of phosphate coatings.
Since cracks increase the surface area of phosphate crystals and provide more chances
for the solution to access the steel surface, it should have a negative effect on the stabilization
of phosphate in a high pH solution. Therefore, more investigation is needed to understand the
mechanism.
4 - 1 - 3. Silane Treatment.
The silane treatment was applied to the samples treated in solutions WC, WB and WCB.
The analytical data from EDX did not show any change with the silane treatment in the relative
intensity of the elements present except that of silicon which increased with the silane treat-
ment as expected. However, the increased silicon content by the silane treatment is less than
1.5 percent.
Chapter IV. Results and Discussion 64
Figure 24. . Cracks formed by the punching.
Chapter IV. Results and Discussion 65
5
4
-3 ~ 0
..... 0 -·- 2 (/)
0
I I POST RINSE
~ SI LANE I: : : I pH 12.5 ICM ~ pH 12.5 20M
WG+CN WG+CN+BN WG+BN
Figure 25. Change of silicon content by the silane treatment and followed by the Immersion test.
Chapter IV. Results and Discussion 66
The change of the relative percentage of silicon by the silane treatment followed by the
immersion test is presented in Fig. 25. The relative percentage of silicon increased slightly
with the silane treatment. The highest increase was obtained with the sample treated in sol-
ution WB. There should be a relationship between the amount of silane precipitated on the
phosphate crystals and the elements present on the phosphate crystals. The immersion test
of the silane treated samples decreased slightly the content of silicon. Compared to the results
from the post-rinse treatments in solution WC, WB and WCB followed by immersion test, the
stability of film formed by silane treatment is generally higher than that formed by the post
rinse treatments. The treatment in solution WB followed by silane treatment showed the
highest silicon content in the immersion test for 20 minutes. It is assumed that a thin silane
layer was formed on the surface of the sample by the silane treatment, actually on the thin film
of silicate compound coating according to the hypothesis, and that the thin film containing
barium had a higher reactivity to silane than any other elements used in this experiment since
the dissolution of silane decreased in the immersion test when only barium was added.
The leaching of phosphate ions in the immersion test was reduced significantly by the
silane treatment as shown in Fig. 26. The relative percentage of phosphorus was still more
than 20 percent even after 20 minutes immersion test. The samples treated in solution WB
and WCB showed better protection than those treated in solution WC after the silane treat-
ment. Even though the treatment in solution WCB followed by the silane treatment showed the
less silicon content than that in solution WB followed by the silane treatment, the protection
of the phosphate coating by these treatments was almost the same in the immersion test. The
added barium might produce a highly insoluble film with silane; hence, the samples treated
in solution WCB and WB followed by the silane treatment showed almost the same result in
the immersion test. The film formed by the post-rinse treatment in cooperating with the film
by the silane treatment had a higher alkaline resistance than that by post-rinse treatment by
itself.
Chapter IV. Results and Discussion 67
-~ 0 .... 0 -
30 r--------r-------------
20
10
0
-0--• • -6--
WG+CN WG+CN~SLN
WG+CN+BN ~sLN WG+BN~SLN
5 10 TIME (min)
15 20
Figure 26. Effect of the silane treatment on the phosphate stabilization In the immersion test.
Chapter IV. Results and Discussion 68
a
b
Figure 27. Effect of the silane treatment on the dissolution of phosphate crystals in the immersion test for 10 (a) and 20 min.(b)(pretreated in WCB)
Chapter IV. Results and Discussion 69
The phosphate crystals of samples treated in solution WB followed by the silane treat-
ment and immersion test are shown in Fig 27. After the immersion test for 20 minutes, the
phosphate crystals were slightly destroyed. It indicates that the silane treatment was effective
on the phosphate stabilization in a high pH solution.
4 - 1 - 4. Heat Treatment.
The results from the heat treatment of samples treated in solution WC, O.OOSM
waterglass + O.OOSM calcium nitrate, are shown in Fig. 28. The analytical data with EDX dis-
played that the relative percentage of phosphorus from the Heat Treatment I at 180° C is little
higher than that from at 110° C. The results obtained at both temperatures are similar to that
from the immersion test without the heat treatment. However, the results from the Heat
Treatment II showed different phosphate content and morphology of the phosphate crystals
from the samples without the heat treatment and those from the Heat Treatment I. The rela-
tive percentage of phosphorus decreased by 3 to 4 percent with the Heat Treatment II com-
pared to that without the heat treatment. The samples treated in solution WCB showed the
same trend as those treated in solution WC at 110° C and at 180° C.
The micrographs of samples, treated in a solution WC followed by Heat Treatment II at
110° C for 24 hours, are shown in Fig 29. The phosphate crystals were changed by heat
treatment at 110° C as well as at 180° C. However, the micrographs taken from the Heat
Treatment I did not show any change compared to those taken from the samples immersion
tested only, which are not included here.
The results indicate that the heat treatments at 180° C and at 110° C after the immersion
test did not affect the phosphate coating while the heat treatment before the immersion test
Chapter IV. Results and Discussion 70
did have a significant effect. It is suggested that the heat treatment had evaporated the water
in the coating layers which might result in the degradation of the phosphate coating. It was
reported (34) that the zinc phosphate coatings heated in the absence of air lose their corrosion
resistance between 150 and 163° C. At these temperatures, about 75 percent of the water of
hydration is lost and it results in a volume decrease of the coating which causes voids and
thereby lowers the corrosion resistance. The loss of water from the zinc phosphate coating
heated in air is 10 to 20 percent higher than the loss on heating in the absence of air. The
change of phosphate crystals by heating, as shown in Fig. 29, should be due to the loss of
water.
The results obtained from this experiment are not consistent with the literature as de-
scribed. The degradation of phosphate coatings by Heat Treatment II at both temperatures
was observed. On the other hand, the Heat-Treatment I at 180° C did not show any degrada-
tion of the phosphate coating. The difference in observation between literature and experiment
is probably due to the post-rinse treatment which decreased the transition temperature of the
phosphate coating but is not certain.
4 - 2. AES/SIMS Results.
The analysis by AES and SIMS was carried out only on selected samples. The survey
spectra of AES were taken from the samples treated in solution WG, WC, WCB and as-received
sample, and depth profiling spectra were taken from the samples treated in solution WG and
WC. The SIMS analysis was performed only on the sample treated in solution WCB before
and after the silane treatment. The AES spectra are shown in Fig. 30 to 37 and those of SIMS
in Fig. 38 and 39, respectively.
Chapter IV. Results and Discussion 71
30 ------,-----r-----,-----,
20
-~ +-0 -a..
10
0 5
-0---0--• --6-•
10 TIME( min)
WG+CN pH -.1 so0 c 1so0 c~pH pH-+110°C 110°c~pH
15
Figure 28. Effect of heat treatment on the phosphate stability in the immersion test.
Chapter IV. Results and Discussion
20
72
a
b Figure 29. Degradation of phosphate crystals by heat treatment followed by the immersion test
for 10 (a) and 20 min.(b).
Chapter IV. Results and Discussion 73
In the survey spectrum of as-received sample, as shown in Fig. 30, the data from AES is
fairly consistent with that from EDX. The silicon peak not present in the AES spectrum might
be explained by the sensitivity factor of silicon or by that silicon is not in the outermost surface
layers.
However, the samples treated in solution WG for 30 minutes showed clear silicon peaks
which are shown in Fig. 31, while some other peaks such as calcium and iron disappeared.
It also shows that the peak intensity of phosphorus decreased with the treatment in solution
WG, which was fairly consistent with the EDX results. The increased intensity of the silicon
peak by the waterglass treatment supports the hypothesis of the thin film formation and also
indicates that the thickness of the film is ,less than the probing depth of AES at the exper-
imental condition.
The result from depth profiling of the sample treated in solution WG is shown in Fig. 32.
The silicon content decreased significantly in the first three minute sputtering and decreased
slightly after that. This fact clearly indicates that the silicon content was increased by the
waterglass treatment. It is assumed that silicon might diffuse to some degree to the surface
layer of phosphate coating and/or react with ions in the solution, such as phosphate, zinc or
iron ions, which led to the formation of thin film of silicate compound. Based on the depth
profiling data, the thickness of the film should be few hundred A0
The survey spectra of samples treated in solution WC without and with deionized water
rinse are shown in Fig. 33 and 34, respectively. A much higher silicon peak was recorded from
the sample without deionized water rinse and the calcium peak was also detected. The depth
profiling data of sample treated in solution WC, 0.005 M waterglass + 0.005 M calcium nitrate,
and dried by air blown at room temperature is shown in Fig. 35. The calcium peak increased
sharply until about 1.5 minute sputtering time and decreased sharply, while the silicon peak
showed the opposite trend.
Chapter IV. Results and Discussion 74
IT1 ~
r IT1 () -i :0 0 CX> z rn z rn :0 -G>f\) -< -Cl) < )(
0 o-- ())
N
0
N :J
11 Cl)
d!/dE ~
z
Figure 30. AES spectrum of as-received sample.
Chapter IV. Results and Discussion 75
fT1 r o fT1 () -; ::uoo 0 z fT1 z f"Tl-:::oN G)
-< -Cl)
< )( (j) 0 0 -
dl/d E ~
Figure 31. AES spectrum of the sample treated in solution WG for 30 min.
Chapter IV. Results and Discussion 76
A. C, ( 0/o) p ~ co rv N
(j) 0 -J _..., ~ ~ ~ ~ 0
' ' ' \ I
(JJ I (/) I
""O I c I -i I
-i O'> I rn I ::0 I
I -i I 3: (.!) I rn I - I 3 I :::> I I -
N I I I I (/'I -0 I I
U1 I
Figure 32. AES depth profiling spectrum of the sample treated in solution WG.
Chapter IV. Results and Discussion 77
0
~ fTI r rn () _, :::0 CX) 0 z fTI z fTl-:::0 N G') -< -ct> < )< -_()')
0 0 -
N 0
0
N ::::>
en
"'O
dI/dE ~
z
Figure 33. AES spectrum of the sample treated In solution WC without water rinse.
Chapter IV. Results and Discussion 78
~ rn r fT1 (") -i ::a 0 00 z rn z rn ::a -G> I\) ~ -Cl) < x o_ Om - '
dl/dE ~ (j)
0
CJ)
Figure 34. Effect of water rinse on the retention of elements in the coating surface.
Chapter IV. Results and Discussion 79
A C. (0/o)
°' <.O . . <.O . .
ow <.O <.O -----
en VJ \ \
"U \ c \
I -f I -f mm \
I
::0 I
-f I I - I ~
~<.O I I I 3
I :J - I
I I
f\) I "U () (./)
I I 0 -·
. I
(Jl
Figure 35. Depth profiling result of the sample treated In solution WC for 30 min (no rinse).
Chapter IV. Results and Discussion 80
dl/dE N ~
~
rr1 r 0 IT1 CD () 0
-i :::0 CX> 0 z
N rr1 :J
z 1"11-:::0 N G) -< -Cl> < x -en ~ 0 0 -
N o--~~~~--~~~-'---~~~~--~---'
Figure 36. AES spectrum of the sample treated in solution WCB.
Chapter IV. Results and Discussion 81
~ rn r rn () -; :::0 ooo z rn z rn :::0 N G> -< -Cl> < >< --om 0 -
N
dI/dE N ~
0
()--~~~~--~~~----~~~~~.-~-
Figure 37. AES spectrum of the sample treated In solution WCB followed by the silane treatment.
Chapter IV. Results and Discussion 82
These data indicate that the thin film formed by the treatment in solution WC consists
of two parts; the silicon rich outer layer and the calcium rich inner layer of the film. This is
supported by comparison with the spectra in Fig. 33 and 34, where the sample rinsed with
deionized water gives rise to the less intense peak of silicon than the sample without rinse,
while the peak intensity of calcium in both spectra is alike. The two layer film formation might
be due to the different reactivity of silicon(silicate) and calcium to the phosphate coating.
The spectra of the sample treated in solution WCB and this treated in solution WCB fol-
lowed by the silane treatment are shown in Fig 36 and 37, respectively. A fairly large barium
peak was detected from the sample treated in solution WCB. However, it disappeared by the
silane treatment. According to these results, the treatment in solution WCB increased the peak
intensity of barium compared to the treatment in solution WC, and the silane treatment after
the treatment in solution WCB reduced the intensity of this peak. The reduced intensity of
barium peak by the silane treatment should be the result of silane film formation on the
silicate compound film.
Since AES is a surface analysis techniques with a probing depth of 10 to SO 0A, the
spectra taken by AES indicates that the thin film of silicate(silicon) compound, consisting of
calcium, barium, phosphate, zinc and Iron, was formed by the post-rinse treatment and the
thin layer of silane film was also formed by the silane treatment. Even though the formation
of the thin film by the treatment is well known, the mechanism of the film formation and the
protection of phosphate in a high pH solution need more investigation in detail.
The SIMS spectra of samples treated in solution WCB, and in the silane solution after
treatment in solution WCB are shown in Fig. 38 and 39 respectively. In the spectrum of
sample treated in solution WCB, 0.005 M waterglass + 0.005 M calcium nitrate + O.OOSM
barium nitrate, the peak intensity of silicon and calcium were relatively low and that of barium
Chapter IV. Results and Discussion 83
was relatively high. This may be due to the different sensitivity factor of these elements since
the data taken by EDX showed almost the same amount of calcium and barium.
In the spectrum of the sample treated in solution WCB followed by the silane treatment,
the intensity of silicon increased while that of barium and calcium decreased compared to that
in the spectrum of the sample treated in solution WCB. Since the probing depth of SIMS is
usually 3 to 10 A0 , the silane layer should be thicker than 10 A0 because the barium peak was
not detected in SIMS analysis of the silane treated sample.
Based on the data taken by SEM/EDX and AES/SIMS, which are in mutual agreement,
the formation of the thin film by the post-rinse treatment and the silane treatment is confirmed.
The assumed thickness of films are few hundred A0 by the post-rinse treatment and several
A0 by the silane treatment.
It is generally accepted that a coherent oxide film on the coating surface was formed by
the chromate post-rinse treatment, which provides the passivation. The increased stabiliza-
tion of phosphate coating in this experiment could be explained by the same theory. The thin
film formed by the post-rinse and silane treatment provides a passivation as well as high alkali
resistance. Based on the AES/SIMS results, it is proposed that the film formed by the post-
rinse treatment in solution WB consists of Ba, Zn and Si03 • As a result, the proposed model
of film is the compound of those elements; (Ba, Zn)Si03-Zn(OH), which has very low solubility
in alkaline solution and hence, protects the phosphate coatings from the alkaline attack.
Chapter IV. Results and Discussion 84
6
en
ci 4
(j 2
6
cri
.4 a..
(.)
2
0
H+ Na+
0 20
100 120
K+
ca+
+ + K+C3H5
+ Si(C~)
40 60 A. M. U.
+ + BaO BaOH
\ ,/
140 160 A. MU.
80 100
180 200
Figure 38. SIMS survey spectra of the sample treated In solution WCB for 30 min.
Chapter IV. Results and Discussion 85
6 H+
en
a.: 4
u 2
0
6
cL 4
2
0 100
~+
CH+ 3
20
liO
Si+
SiH+ + + C3H5+K
+ K fiCH:
Si OH Fe+
+ SiH
40 60 A. M U.
120 A. M.
130 u.
80 100
140 150
Figure 39. SIMS spectrum of the sample treated in solution WCB followed by the silane treat-ment.
Chapter IV. Results and Discussion 86
4 - 3. X-ray Diffraction Analysis Results.
X-ray diffraction spectra are shown in Fig. 40. Many zinc phosphate and zinc peaks were
recorded in the spectrum of the as-received sample. However, most zinc phosphate peaks
disappeared in the spectrum of the sample immersion tested for 20 minutes, while the peak
intensity of zinc increased ( at 20 = 36°). After the treatment in solution of WZ, WC and WCB
followed by the immersion test, the intensity of zinc phosphate peaks increased from treat-
ment in WZ to WCB while that of zinc peaks decreased. The silane treatment followed by the
immersion test increased the intensity of zinc phosphate peaks more than any other treat-
ments did, as expected according to SEM/EDX and AES/SIMS results.
Therefore, it is corroborated again that the post-rinse treatments carried out in this re-
search retarded the leaching of phosphate ions in a solution of pH 12.5. The treatment in sol-
ution WCB showed the best result, which was further improved by the silane treatment. Even
though the EDX analysis revealed that there is more than 20 percent of phosphorus after the
immersion test, the peak intensity in the XRD spectrum is low. This might be resulting from
the reduced X-ray intensity by the film on the surface, which was formed by the post-rinse or
silane treatment.
4 - 4. Polarization Measurement Results.
The cathodic polarization curves of samples treated in solution WG, WZ, WC, WB, and
in the silane solution after treatment in solution WB, and as received sample are shown in Fig.
41. Even though the anodic polarization curves, which are not shown in this report, were alike,
the cathodic polarization curves were different from one another depending on the treatment.
Chapter IV. Results and Discussion 87
INTENSITY
I\) f\) (>J
CD -0.. (1)
cO .., Cl> (1) -
f\) ~
(>J
VJ CX>
Figure 40. X-ray diffraction spectra of the samples after post-rinse treatment followed by the Immersion test for 20 min. 1) as-received(no treatment). 2) 0.005M waterglass treated, and immersion test. 3) 0.005M waterglass and 0.01M zinc sulfate, and immersion test. 4) 0.005M of waterglass and calcium nitreate, and immersion test. 5) 0.005M of waterglass, calcium nitrate and barium nitrate solution treated and immersion tested. 6) silane treatment of #5.
Chapter IV. Results and Discussion 88
The lowest dissolution phosphate coating in a pH 12.5 solution was obtained by the
treatment in solution WB followed by the silane treatment, which was slightly better than that
obtained by the treatment in solution WB only. The improvement by the silane treatment was
noticeable but not to a great extent in the polarization measurement even though the stability
of phosphate crystals was greatly improved. The results from the other post-rinse treatments
listed in the order of descending improvement are the samples treated in solution WC, WZ,
WG and the as-received sample.
Since the phosphate stabilization is directly related to the corrosion protection, it is as-
sured that there should be better protection after the post-rinse treatments according to the
data revealed by SEM/EDX and AES/SIMS. The polarization measurements confirmed that the
post-rinse treatments improved the corrosion protection by depressing the reaction of oxygen
depolarization.
Chapter IV. Results and Discussion 89
POTENTIAL vs S. C. E. ( mV x -100) ~ N 0 CD
r 0 G')
("") c :::0 . :::0 ~ f"Tl z --i 0 f"Tl z c.n ---i -< -:J (J1 l> ~ 3 "' -
Figure 41. Cathodic polarization curves of post-rinse treated and/or silane treated samples and as-received smple. 1). as-received. 2). O.OOSM waterglass 3). O.OOSM waterglass and 0.01M zinc sulfate. 4). O.OOSM waterglass and calcium nitrate. 5). 0.005M waterglass and barium nitrate. 6) .. silane treatment of #5.
Chapter IV. Results and Discussion 90
Chapter V. Summary and Conclusions
The dissolution of the phosphate crystals in a highly alkaline environment, which is
mainly caused by the corrosion reaction under the organic coating, has a negative effect on
the corrosion resistance and paint adhesion. This problem is wide-spread in industry, and
many investigations have been carried out in order to understand the mechanism of dissol-
ution and to minimize this effect. One of widely utilized methods is post-rinse treatment with
a solution which contains metallic or non-metallic ions. Due to the environmental problems
generated by the use of chromate ions, which showed great improvement of corrosion pro-
tection in a highly alkaline solution, the chromate post-rinse treatment should be replaced by
the non-chromate post-rinse treatment.
The objective of this research was the development of a non-chromate post-rinse treat-
ment with equal or better corrosion protection than the chromate post-rinse treatment. The
basic consideration was that zinc phosphate could be exposed to an alkaline solution con-
taining certain additives which would precipitate onto the phosphate crystals and arrest fur-
ther attack of the crystals. Silicate (sodium silicate) was extensively used due to low cost of
Chapter V. Summary and Conclusions 91
materials. The silicate treatment would produce a silicated and silanized phosphate which
reduced the sensitivity of phosphate coating to alkaline environment and in addition, provide
a highly stabilized phosphate-paint interface against hydrolysis and rehydration. The addition
of other ions such as Ca2+, Ba2+ , Ni2+ and Mg2+ to waterglass solution was utilized.
The analysis of treated samples were carried out by SEM/EDX, and AES/SIMS were uti-
lized to understand the mechanism of prevention of phosphate dissolution in highly alkaline
environment. The additional data by XRD and polarization measurement revealed that the
post-rinse treatment as well as the silane treatment are effective in stabilization of phosphate
coating and in corrosion protection. The observed results are as follow.
1. The post-rinse treatment in a solution of O.OOSM waterglass + O.OOSM barium nitrate
showed the best result in the immersion test, followed by the treatment in a solution of
O.OOSM waterglass + O.OOSM calcium nitrate and O.OOSM waterglass + O.OOSM calcium
nitrate + O.OOSM barium nitrate. (by SEM/EDX)
2. A further improvement was obtained by the silane treatment. The samples treated in
solution of O.OOSM waterglass + O.OOSM barium nitrate and of O.OOSM waterglass +
O.OOSM calcium nitrate + O.OOSM barium nitrate showed almost the same result which
were much better than that taken in step 1). (by SEM/EDX)
3. The analytical data from AES/SIMS showed that (a) the thin silicate compound film was
formed by the post-rins treatment, (b) silane is covering the surface of the sample, and
(c) added elements are present in the surface layer, which were removed partly by the
deionized water rinse.
4. The heat treatment both at 180° C and 110° C did not improve the stability of phosphate
but had a negative effect.
Chapter V. Summary and Conclusions 92
5. X-ray diffraction analysis confirmed that the dissolution of phosphate coating was reduced
by the post-rinse treatment and also by the silane treatment.
6. The polarization measurement also confirmed that the post-rinse treatment improved the
corrosion protection. The cathodic polarization( oxygen reduction current) was improved
by the waterglass itself and more with additional ions such as Ca2+ and Ba2 +. The silane
treatment also led to a noticeable improvement in its own right.
From the results obtained in this research, the recommended treatment is that of 0.005M
barium added 0.005M waterglass solution which showed best results. However, it has been
reported that all barium compounds except barium sulfate are toxic. Therefore, the utilization
of barium added solution needs more investigation on the possible health problems. The ex-
perimental results can be accommodated in a simple model which is based on the solubility
parameter of the zinc phosphate in alkali and of films precipitated on to the crystals.
Zn3(P04h-4H2 0 dissolves readily at pH 12.0 and even faster at pH 12.5 under formation
of K3P04 and K2Zn02• In the presence of waterglass, however, a film of zinc compound is de-
posited in situ onto the phosphate. This film has to be dried in air in order to protect the
phosphate from the alkaline attack, e.g. in our test condition at pH 12.5. In the presence of
Ba2 + ions in the waterglass a slightly different film is formed with the tentative composition
(Ba, Zn)Si03-Zn (OH)z based on surface analysis data. This film is of much lower solubility
than ZnSi03, in agreement with zinc chemistry. The film has to be dried , too, in order for it
to form completely. The proposed model of thin film formed by the post-rinse treatment in
solution WB, 0.005fv1 waterglass + 0.005M barium nitrate, is shown in Fig. 42.
The silane treatment seems to lead to a surface compound which includes Zn, based
on surface analysis. Since silane needs OH- ions to react, it is reasonable to assume that it
reacts with the Zn(OH)z component of the surface film, forming a NH2(CH2)JSi(OC2H5h -0-Zn
Chapter V. Summary and Conclusions 93
( Ba, Z n) Si 0 3 - Zn ( OH )2
L~~--
·~····: . .... ;_ :..,-·.: " .... :--·:,-~·-·--·;· .... ·;.-:··--·~,,-~ .. :.-,-: .. '---. =. : · , - • , · · / , : s· T E E L.:.. · , , ·.. ~ .... .:. · , , '\ "··" J • ,. ···-,·.·.· .·,-•.: : --.·' .. ,:"~.,·:.~•,;. .i-.'
, I • • • I, t" • ;, • "' " ' •• • • I• "' r I • _. •: ~· • I"' - "' I r ,.I ,._,, " - • • "' ,, _ • ' • • .. • 1 • • ,. • • •" "' ,- • , • I 1 " " ,, ,
Figure 42. Proposed model of thin film formed by the post-rinse treatment in solution WB.
Chapter V. Summary and Conclusions 94
structure. Upon drying for at least 24 hours, this surface film crosslinks two-dimensionally. In
this treatment, the presence of the inorganic silicate is essential. It reduces the sensitivity of
the phosphate to alkali and also provides reaction sites for the silane.
The analytical data revealed that the treatment modifies a standard zinc phosphate
coating so as to improve its alkali resistance and hence its corrosion resistance. They also
provided a surface that will bond chemically to an electrocoat. This will reduce the sensitivity
of the interface to hydrolysis. In addition, the oxygen reduction sensitivity is less than that of
the standard.
However, more work needs to be done to understand the mechanism of film formation
better and to optimize the treatment for practical applications. The suggested works are as
follows;
1. Extensive testing of the recommended treatment in a variety of corrosion conditions (salt
spray, scab, water soak, cyclic tests, atmospheric tests, etc.)
2. By varying the parameters such as time, temperature and concentrations, the treatment
time should be reduced from 30 minutes to approximately 1-2 minutes without any loss
of performance.
3. Dip and spray versions should be tested on other phosphates and other substrates.
4. The mechanism of the exchange and Si-uptake should be studied in more detail as well
as role of other metallic ions.
5. The studies on the possible health or environmental problems are required in detail be-
fore utilization of this treatment in automotive industries.
Chapter V. Summary and Conclusions 95
Bibliography
1. H. Koyama, Corrosion Engineering, 31 (1), 1981, 34.
2. Shgetashi Ishihara, Trans ISIJ, 23, 1983, 897.
3. D. J. Blikwede, Trans ISIJ , 23, 1983, 687.
4. D. R. Bear, Applications of Surface Science, 19, 1984, 382.
5. W. C. Sivert and L. L. Frank, SAE Technical Paper Series #800146, Congress and Ex-position, Cobo Hall, Detroit, Feb. 25-29, 1980.
6. R. F. Higgs et al. SAE Technical Paper Series #800442, Congress and Exposition, Cobo Hall, Detroit, Ml., Feb. 25-29, 1980.
7. D. L. Dalton, Paint Manufacturer, Oct., 1977, 21.
8. J. H. Mock, ME, Jan. 1981, 33.
9. E. J. Kubel Jr., ME, Aug., 1985, 39.
10. A. Shibaya, T. Kurimoto, Y. Hoboh and N. Usuki, Trans ISIJ 23, 1983, 923.
11. R. Noumi et.al., SAE Technical Paper Series #820332 Int. Cong.and Expo., Detroit, Ml., Feb. 22-26, 1982.
12. A. W. Kennedy, H. K. Heringer and M. Tamura, Body Engineering Journal, Spring, 1981.
13. J. Samson,C. Bran and S. Mathieu, SAE Technical Paper Series #820335, Int. Cong. ·and Expo., Detroit, Ml., Feb. 22-26, 1982.
14. T. Yoshihara and H. Okita, Trans ISIJ 23, 1983, 984.
15. G. H. Nancollas, Corrosion, 39 (3), 1983, 77.
Bibliography 96
16. R. D. Wyvill, Product Finishing Nov., 1984, 77.
17. W. J. van Ooij, Pro. ACS Div. of PMSE, Chicago, IL., 1985, 698.
18. W. J. van Ooij andO. T. De Vries, IXth Int. Conf. on Org. Coat. Tech, Athen,Greece, 1984.
19. J. J. Wojtkowiak and H. S. Bender, J. fo Coating Tech., 50, 1978, 86.
20. R. W. Zurilla and V. Hospadaruk, SAE Tech. Paper Series #780187 , SAE Tech. Meeting, Detroit, Ml., March, 1978.
21. H. Leidheser Jr. ed. Proc. Corr. Contr. Org. Coatings Leh igh Univ., 1979, 225-241.
22. R. R. Wiggle, A. G. Smith and J. V. Petrocelli, J. of Paint Tech. , 40, 1968, 174.
23. R. W. Zurilla in Corrosion Control/ by Organic Coatings H. Leidheiser Jr. ed., Sceince Press, Princeton, 1979, 243.
24. N. J. Newhard Jr. in Corrosion Control/ by Organic Coatings H. Leidheiser Jr, ed., Science Press, Princeton, 1979, 225.
25. I. L. Rozenfeld, Corrosion Inhibitors, McGraw-Hill Inc., 1984.
26. H. Makishima and M. Hoshino, U.S. Patent #4011088, 1977.
27. M. Yamashita, T. Kubota and T. Adaniya, SAE Technical Paper Serises #862017
28. Gosta Waranglen, Introduction to Corrosion and Protection of Metals, New York, Champman Hill, 1985, 185.
29. C. M. Munger, Corrosion Prevention by Protective Coatings, NACE, 1984, 205.
30. J. J. Claus and R. P. Wenz, Corrosion SP-485, Int. Cong. and E epo., Cobo Hall, Detroit, Ml, Feb 23-27, 1981, SAE, 1981, 11.
31. G. Lorin, Phosphating of Metal, Finishing Publication LTD, 1974.
32. C. T. Yap, T. L. Tan, L. M. Gan and H. W. K Ong, Applied Surface Science, 27, 1986, 247.
33. S. Maeda, Pro. in Org. Coatings, 11, 1983, 1.
34. L. L. Shreir ed. Corrosion V.2, 2nd ed., Newnes-Butterworths, Boston, 1965, 16:19.
35. H. W. K. Ong,L. M. Gan and T. L. Tan, J. of Adhesion 20, 1986, 117.
36. T. Yoshihara and H. Okita Trans ISIJ 23, 1983, 984.
37. R. W. Zurilla and V. Hospadarak, Society of Automobile Engineers, Annual Meeting, No 780187, 1978.
38. S. Maeda, T. Asai and H. Okada, Corrosion Engineering (Boshoku Gijutu) 31, 1982, 268.
39. R. A. Rittar and H. Leidhisier, Corrosion, 37 (1), 1981, 28.
Bibliography 97
40. W. J. van Ooij, Surface and Interface Analysis 9, 1986, 367.
41. Y. Miyosh, J. Oka and S Maeda, Trans ISIJ, 23 (11), 1983, 974.
42. W. J. van Ooij, Spectrochemica Acta 39B (12), 1984, 1451.
43. F. Mansfeld ed., Corrosion Mechanisms Marcel Dekker Inc. New York, 1987, 119.
44. Encyclopedia of Chemical Engineering, V.20, John Wiley and Son, 1978, 748.
45. M. Yamashita et al., SAE Technical Paper Series #862017, Int. Cong. and Expo. Detroit, Ml., Feb. 1986.
46. J. G. Vail, Soluble Silicate Reinhold Pub. Co., New York, 1952.
47. J. S. Falcone Jr, ed. ACS Symposyum Series 194, ACS, 1982, 49.
48. Encyclopedia of Chemical Engineering, V.4, John Wiley and Son, 1978, 412.
49. A. M. Rosenberg and J. M. Gaidis, U.S. Patent #4355791, 1982.
50. E. Kuehn, U.S. Patent #4304707, 1981.
51. Metal Handbook V.5, ASM, 1986, 596.
52. J. W. Forsberg, U.S. Patent #4253976, 1981.
53. R. M. Burns and W.W. Bradley, Protective Coatings for Metals, 3rd ed. Reinhold Pub. Co. New York, 1967, 215.
54. H. H. Uhlig and R. W. Revie, Corrosion and corrosion Control, 3rd ed. John Wiley and Son, New York, 1985, 361.
55. P. Walker, J. of Coating Tech.,52 (670), 1980, 49.
56. E. P. Ebdon, J. of Paint Tech., 40 (516), 1968, 21.
57. M. Getting,F. S. Baker and A. J. Kinloch, J. of Appl. Poly. Sci., 21, 1977, 2375.
58. E. P. Plueddemam, J of Paint Tech. 42 (550), 1970, 600.
59. C.H. Chiang and J. L. Koenig, J. of Poly. Sci., Poly. Phys., 20 (11), 1982, 2135.
60. K. W. Allen, A. K. Hansrani and W. C. Wake, J of Adhesion, 12 (3), 1981, 199.
61. T. Furukawa, N. K. Elb, K. L. Mittal and H. R. Anderson, J. of Col/id and Interface Sci., 96 (2), 1983, 322.
62. M. Hoshino and T Shinohara, U.S. Patent #4098749, 1978.
63. R. W. Lerner, H. Hayati and J. R. Flasch, U.S. Patent #3776881, 1973.
64. E. P. Plueddemann, Silane Coupling Agents Plenum Press, New York, 1982, 29.
65. D. E. Leyden ed., Silylated Surfaces Carden and Breach Science Pub., 1978, 31.
Bibliography 98
66. J. I. Goldstein and H. Yakowitz ed. Practical Scanning Electron Microscopy, Plenum Press, New York, 1975.
67. M. J. A. van Green et al., Spectrochemica Acta, 398 (12), 1984, 1579-1581.
68. R. Jenkins, R. W. Gould and D. Gedcke, Quantitative X-ray Spec trometry, Marcel Dekker, New York, 1986.
69. R. van Grieken, Fresenius Z Anal. Chem.,324, 1986, 825-831.
70. D. M. Hercules and S. H. Hercules, J. Chem. Ed.,61 (6), 1984, 483.
71. D. Briggs and M. P. Seah ed., Practical Surface Analysis, John Wiley and Son, 1983, 217.
72. R. T. White and J. B. Malherbe, Applied Surface Sci., 25, 1986, 32-40.
73. D. M. Hercules and S. H. Hercules,, J. Chem. Ed., 61 (7), 1984, 593.
74. A. W. Czanderna ed., Methodes of Surface Analysis, Elsevier Scientific Pub. Co, 223.
75. L. A. Casper and C. J. Powell ed., Ind. Appl. of Surf. Analysis, 181th ACS Meeting, Aug. 23-28, 1981.
76. A guide to Dow Corning Silane Coupling Agents Dow Corning, 1987, 11.
Bibliography 99