www.allnex.com Energy Curable Coatings for Automotive Interior - Marcus Hutchins and Jennifer McClung

Transcript of Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung....

Page 1: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

www.allnex.com

EnergyCurableCoatingsforAutomotiveInterior

- MarcusHutchinsandJenniferMcClung

Page 2: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Content

2

• Technology/ProcessComparison• ChallengesofUVCure• Products– 100%SolidsandWaterborneUV• Experimentation• Results• Conclusion– 100%SolidsUVandWaterborneUV• NextGeneration• TechnologyComparison• Experimentation• Results• Conclusion

Page 3: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

AutomotiveInteriorTechnologyComparison

4May2018 3

1Kor2KConventional(NCO- OH)

+Fullcurefordifficultshapeofpart+Lowershrinkage+Outstandingweatherability

- Spaceandtime- Slowcure- Highenergyconsumptionfordrying

UVCuring

+Fastcure(highproductivity)+Highscratch&chemicalresistance+Smallfootprint&easylineretrofits

- 3Dshape=>NOUV=NOCure- Volumetricshrinkage- Adhesionisnotrobust

Page 4: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Water-orSolvent-borne(1K/2K,UV)

• Water orSolventevaporation• Physical drying• Higher MW – Low Viscosity

Heat

TechnologyComparison

Tackyor

Tack-free !

UVorEB

Liquidmixture

DRYFILM

UVorEBOligomersMonomersPhotoinitiator

100%Solids

UV/EB:Readyforimmediateuseaftercure 1K/2K:Oktohandle,hoursanddaysbeforefullproperties

Page 5: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

TechnolgoyComparison

5

0

5

10

15

20

25

30

35

40

1K/2KSolventborne 1K/2KWaterborne SolventborneUV WaterborneUV

Minutes

Coat(Spray) SolventorWaterRemoval Cure

CureTemperature80oCAdditional4,000minutesbeforefullpropertiesdevelop

Page 6: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

ChallengesofUVCure

6

UV-AUV-BUV-C UV-V

Coating

Substrate

100– 280nm280– 315nm

315– 400nm400– …nm

Electrons(EB)

• DifferentpartsoftheUVspectrumcanpenetratetodifferentdepthsofthecoating.• Therightphotoinitiatorchoicewillinitiatethereactionintheentirecoating.• UVLEDistypically385nm,395nm,405nm.(365nmisavailableatlowenergy

output)

O2O2

O2O2

O2

O2O2 O2

O2O2

O2O2

O2 O2 O2O2

O2

O2O2

O2

O2

O2

O2

O2

O2O2O2O2

O2 O2

O2O2 O2 O2

O2O2

O2O2

O2

O2

O2

O2

O2O2

O2

O2O2

O2

O2O2

O2

–O–C–CH=CHO

Page 7: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Products

Functionality,Acrylate

HydroxylValue(NCO,%)

Viscosity,cPat25oC Non-volatile,%

Bio-basePolyester 2 - 450 100

UrethaneHexa-acrylate 6 - 85000 100

RX 81100 4 - 1500 100

UVCurablePUD 6 - 50 40

Hexa-acrylate Emulsion 6 - 500 65

1K PolycarbonatePUD - 170 200 40

1KThermal Silicone - 10 20

Page 8: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Testing

- Abrasion: TaberHaze- 100cyclesonPCsheetwith500gload,CS10Fwheels

- Scratch:SteelWool- 0000and1kgweight

- AutomotiveChemicalTesting- Sunlotionandhandcreamareappliedonabandage

- Thesampleisputinaventilatedovenfor24hoursat80°C- Lotionandcreamremovedandsampleareleftfor4hoursatroomtemperature

beforemakinganassessment- Visualassessmentandrating

- 0noattack- 1visualglosschange- 2changeinsurfaceappearance- 3delamination,blistering,lossofadhesion

Page 9: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

FormulationsforTesting

• 100%resin• UVcuredsystemsinitiated- 100%solids:4%basedontotalweightofsolids,1-hydroxy-cyclohexylphenyl-ketone- WaterborneUV:4%basedontotalweightofsolidsofablendof1-hydroxy-cyclohexylphenyl-ketoneandbenzophenone (1:1)

- Dryfilmtarget12-14g/m2

• WaterandSolventremoval- 80oCfor10minutesforwaterremoval- 80oCfor10minutesforsolventremoval

• 1K/2KandThermalSilicone:ThermalCuring- 80oCfor30minutes- Sampleskeepatroomtemperaturefor72hoursbeforetesting

9

Page 10: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

%HazeAfterAbrasion(CS10F,500g,100cycles)

Sun LotionandHandCream

(80oC,24hr)

SteelWoolScratch

(0000,1kg)

Bio-basePolyester 10 1 100doublerubs

UrethaneHexa-acrylate 7 0 100doublerubs

RX81100 15 0 3double rubs

Thermal Silicon 6 0 100doublerubs

1K:PCPUD 25 3 0

2K:PCPUD +HDITrimer 15 0 3

Results:UVCurableResins– 100%Solids

Page 11: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

PercentHazeAfterAbrasion

(CS10F,500g,100cycles)

Sun LotionandHandCream(80oC,24hr)

SteelWoolScratch(0000,1kg)

UVCurablePUD 12 1 5doublerubs

Hexa-functionalUrethaneAcrylateEmulsion 6.5 0 100doublerubs

1KWater-basedPolycarbonatePUD 25 3 0rubs

1KPCPUD+HDITrimer 15 0 5doublerubs

1K PCPUD+UVPUD(DualCure) 18 1 0rubs

Results:UVCurableResins– Waterborne

Page 12: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Conclusion:100%SolidsandWaterborneUV

• UV/EBsystemcanmeetmorestringentautomotivechemicaltest• WaterborneUVcanbedesignedtohaveequivalentperformancetohigherfunctionalacrylatesystem

• Bio-basedresincanbedesignedtodeliverynotonimprovesustainabilitywithoutsacrificingperformance

⁻ Ideaforflatsubstrates⁻ Glasstransitionandcross-linking(higher)importantforsunlotionandhandcreamresistance

⁻ Adhesionvariedbasedonsupplierandtype⁻ 100%solidsisnotidealforcurrentcoatingprocessingconditionsØDualCuretechnologycouldpossiblebridgethebetweenconventionalandenergycurablechemistries

12

Page 13: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

NextGeneration:DualCure

13

Conventional1Kor2KSB(NCO- OH)+Fullcurefordifficultshapeofpart+Lowershrinkage+Outstandingweatherability

- Spaceandtime- Slowcure- Highenergyconsumptionfordrying

UVCuring+Fastcure(highproductivity)+Highscratch&chemicalresistance+Limitedspaceneeded

- 3Dshape=>NOUV=NOCure- Moreshrinkage(adhesionsometimeschallenging)

+Fastcure(highproductivity)+Lowshrinkage– goodadhesion+Goodscratch&chemicalresistance+3Dshape:NOUV=Cure(NCO-OH)+Lessspaceoccupation

Page 14: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

NextGeneration:DualCure

14

Page 15: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

ProcessingComparison

15

0

5

10

15

20

25

30

35

1K/2KSolventborne 1K/2KWaterborne SolventborneUV WaterborneUV DualCureUVSolventborne

Minutes

Coat(Spray) SolventorWaterRemoval Cure UVCure

CureTemperature80oCfor25minutesAdditional4,000minutesbeforefullpropertiesdevelop

DualCureCuringTemperature80oCfor5minutesAdditional5minutesbeforefullpropertiesdevelop

Page 16: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Products

Functionality,Acrylate(NCO)

HydroxylValue(NCO,%)

Viscosity,cPat23oC Non-volatile,%

OHFunctional Acrylic - 100 3000 55

NCOAcrylate 1.5(1.5) - 20000 90

Urethane acrylate 6 - 8500 (25oC) 100

Page 17: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Testing

- Abrasion: TaberHaze- 100-300-500cyclesonPCsheetwith500gload,CS10Fwheels

- Curl uponcure- CoatingwasappliedtoPETfilm(12.5microns)at12microns- 4”x4”samplewastakenandtheheightofcurlwasmeasuredateachcornerand

fourcornerswereaveraged

- Adhesion:crosshatch- 0=noadhesion,5=fulladhesion

- Erichsen (pen318withtipof0.75mm)pass/fail

Page 18: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Testing

- DoublebondandNCOconversion- MeasuredusingFTIRspectrophotometer

- ~810cm-1 absorbancefordoublebondconversion- ~2270cm-1 absorbanceforisocyanateconversion

- AcceleratedOutdoordurability(ASTMG154-UVA)- 8hoursat60oCatanirradianceof0.89W/cm2

- 4hoursdarkat50oC

- Humidityresistance:VWTL226Agingstability- hydrolysis(72h,90°C,95%humidity)- Crosshatchadhesionafterhumiditytest

Page 19: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Testing

- AutomotiveChemicalTesting- Sunlotionandhandcreamareappliedonabandage

- Thesampleisputinaventilatedovenfor24hoursat80°C- Lotionandcreamremovedandsampleareleftfor4hoursatroomtemperatureandretested

- Crosscutadhesion- Glossmeasured- Erichsen penhardness

Page 20: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

StartingPointFormulation

4May2018 20

*1-hydroxy-cyclohexylphenyl-ketone**Dibutyltindilaurate(DBTL)

• ComponentsIand IIaremixedjust beforeapplication

• Viscosity@25°C~200mPa.s• Solidcontent~58%• Substrate:plasticpanel• Targetdryfilmthickness(DFT):20g/m²• 30’@80°C:flashoffandthermalstep***• UVcuring:2x10m/min.with120W/cmHglamp(~2000mJ/cm²)

• Testingafter1weekstorageatroomtemperature

wt% wt%ComponentI IV.1 IV.2OHFunctionalAcrylic 38.9 31.9Alphatic urethane acrylate 7.8Butylacetate 15.0 15.0Flow andLevelingadditive 0.5 0.5Photoinitiator* 4.2 4.2Catalyst** 0.02 0.02

ComponentII wt%NCOFunctionalAcrylate 56.2

***tobeadjustedbytheamountofcatalysttotherequirementsoftheline/machine

Page 21: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Results– LowCurlUponCure

0

0.2

0.4

0.6

0.8

1

1.2

AliphaticUrethaneAcrylate

NCO-Acrylate+OHFunctionalAcrylic(Thermal+UV)

NCO-Acrylate+OHAcrylic(Thermal)

AverageCu

rl,m

m

21

Page 22: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Results:HazeafterAbrasion

0

10

20

30

40

50

60

OHFunctionalAcrylic OHFunctionalAcrylic+NCO-Acrylate(Thermalonly)

OHFunctionalAcrylic+NCO-Acrylate(Thermal+UV)

UrethaneAcrylate

Percen

tHaze

100cycles 300cycles 500cycles

22

Page 23: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Results:HazeafterAbrasion– AdditionalProcessingTime

IV.1 IV.2

2x5m/m 2x10m/m 2x5m/m 2x10m/m

after1week

+48hrs60°C

after1week

+48hrs60°C

after1week

+48hrs60°C

after1week

+48hrs60°C

Uncoated

%start 0 0.2 0.2 0.1 0.2 0.2 0.2 0.2 0.2

%after100cycles 24.5 6.4 6.1 6.2 6.2 6 5.9 6.5 5

%after200cycles 25.8 9.1 8.8 9 9 8.7 8 8.8 7.4

%after300cycles 28 11.8 11.5 12.5 11.5 11.3 11 12.4 10.6

%after500cycles 30 15.6 15.4 16 14.9 14.5 15.1 15.6 13.9

23

Page 24: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Results:NCOandDouble(=)Conversion

24

Page 25: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Results:DualCure– StainResistance

IV.1 IV.2 UrethaneAcrylate

2x5m/m 2x10m/m 2x5m/m 2x10m/m 2x10m/m

mustard 4 3 5 3 5

eosine 5 4 5 4 5

coffee 5 5 5 5 5

isobetadine 4.5 3.5 4.5 4 5

NH10% 5 5 5 5 5

ethanol50% 5 5 5 5 5

N70blackmarker 5 5 5 5 5

Average 4.8 4.4 4.9 4.4 5

NCOconv(1week) 86 90 81 82 Notapplicable

=conv(1week) 86 79 81 76 79(nochange)

25

Page 26: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Results:ChemicalResistance

IV.1 IV.2 UrethaneAcrylate

2x5m/m 2x10m/m 2x5m/m 2x10m/m 2x10m/m

SUNcreamlotion

Initialgloss20° 85.6 87.8 88.9 88.5 100

60° 93.2 93 93.1 92.6 100

Gloss(aftertest)

20° 87.2 86.6 87.7 87.2 99.32

60° 92.1 92.8 92.8 92.5 98.83

InitialAdhesion(crosshatch) 5 5 5 5 5

Adhesion(crosshatch) 5 5 5 5 5

Erichsenpen10N pass pass pass pass pass

26

Page 27: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Results:DualCure– ChemicalResistance

27

IV.1 IV.2 UrethaneAcrylate

2x5m/m 2x10m/m 2x5m/m 2x10m/m 2x10m/m

Handcreamlotion

Initialgloss20° 85.6 87.8 88.9 88.5 100

60° 93.2 93 93.1 92.6 100

Gloss(aftertest)

20° 84.1 83.9 83.8 82.9 97.62

60° 91.8 91.5 91.3 91.6 94.74

InitialAdhesion(crosshatch) 5 5 5 5 5

Adhesion(crosshatch) 5 5 5 5 5

Erichsenpen10N pass pass pass pass pass

Page 28: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Results:DualCure– Weathering

0

20

40

60

80

100

120

0 100 300 500 750 1000 1250 1500 2000 2500 3000 3500Hours

OHAcrylic

Hexa-functionalUrethaneAcrylate

NCO-Acrylate+OHAcrylic

UncoatedPanel

Percen

tGlossReten

tion

28

Page 29: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

Conclusions

•DifferentcombinationsofUVcurableproductsenableformulatorstocreatingidealcoatingsolutionsforautomotiveinteriorbenefitingfromintrinsicnatureoftheUVchemistry

•DualCureexpandsthetoolbox;benefitingfromthebestofbothworlds

29

• Dryingconditions(e.g.catalystamount,thermaltemperature)caninfluenceperformance!

DuctilebehaviorforhighscratchresistancecoatingsExcellentadhesiontoABS,PC,ABS/PCblendsShorterprocessingtimeincludingfasterfinalpropertydevelopment

Outstandingscratch,abrasionandchemical(sunlotionandhandcream)ExcellentWeatherability

• NCOfunctionalacrylatesNOTimpactedbyNCOrestrictions!

Page 30: Hutchins-Marcus-Energy Curable Coatings for Automotive ...€¦ · Jennifer McClung. Hutchins-Marcus-Energy Curable Coatings for Automotive Interior ...

www.allnex.com

MarcusHutchins([email protected],770-280-8391)JoinusatBooth301