How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling...
-
Upload
reynard-holmes -
Category
Documents
-
view
219 -
download
0
Transcript of How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling...
![Page 1: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/1.jpg)
How to Cause Scaling
• Two primary mechanisms and manifestations– Freeze-Thaw /
Deicer Scaling– Sealed Surface
Blistering and Delamination
![Page 2: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/2.jpg)
Key Players
• Specifier
• Ready Mix Concrete Producer
• Concrete Contractor
![Page 3: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/3.jpg)
Scaling from Freeze/Thaw Cycles and Deicers
• Disintegration of paste caused by:– the hydraulic
pressures from water in saturated pores and capillaries turning to ice.
– the osmotic pressures developed in the paste by the differential concentrations of alkali solutions as produced from the use of deicer salts.
![Page 4: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/4.jpg)
Key Factors Related to Freeze-Thaw & Deicer Scaling
• Entrained Air
• Paste Permeability (& Strength) Characteristics
• Degree of Pore Saturation
• Deicer Chemicals & Use
![Page 5: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/5.jpg)
Entrained Air
![Page 6: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/6.jpg)
Contributors to Improper Entrained Air
Specifier R/M Supplier Contractor
Specify inadequate air content limits
Failure to ask appropriate questions when receiving order
Failure to properly order
Omitting or putting inadequate Air-Entrainment dosage during batching
Adding water to surface and/or over-finishing surface (driving air out of surface)
![Page 7: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/7.jpg)
Paste Permeability (& Strength) Characteristics
Cement Particles
Mix Water Concentration (or Dilution) of Cement Particles in Paste
• W/C Ratio
•Space between cement particles directly determines paste pore structure and strength
![Page 8: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/8.jpg)
Paste Permeability (& Strength) Characteristics
Early Hydration
C-S-H Crystal Growth (Critical)
Later Hydration
CH Crystals (potential pores)
Pores and Capillaries
![Page 9: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/9.jpg)
Contributors to Poor Paste Characteristics
Specifier R/M Supplier Contractor
Failure to address issue-ACI- NMDOT
Failure to ask appropriate questions when receiving order
Failure to properly order
Disallow or inappropriately limit Supplementary Cementitious Materials (SCM’s)
Supply inappropriate mix
Add excessive water to mix at site
Deliver mix with excessive amount of mix water
Work bleed water or surface applied water into the surface
Inadequate curing requirements
Inadequate curing procedures
![Page 10: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/10.jpg)
Degree of Pore Saturation
• Reduced saturation lessens potential for expansive pressures– “Dry concrete doesn’t care about freezing
temperatures”
![Page 11: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/11.jpg)
Contributors to Undesirable Pore Saturation
Specifier R/M Supplier Contractor
Design site conditions with no or inadequate drainage off and away from concrete
Construct concrete members with no or inadequate drainage
Failure to address “Drying” period
Failure to assure drying conditions
![Page 12: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/12.jpg)
Deicer Chemicals & Use
• Frequently used deicers:– Sodium chloride (rock salt)– Calcium chloride– Urea– Magnesium chloride
• Magnesium chloride deicers have come under recent criticism for aggravating scaling.
• Deicers containing ammonium nitrate and ammonium sulfate rapidly attack and disintegrate concrete.
• Deicing chemicals should not be applied during first winter season.
![Page 13: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/13.jpg)
Contributors to Problems from Deicer Use
Specifier R/M Supplier Contractor
Failure to address the use and application of deicers
Failure to adequately instruct owner on the use and application of deicers
Failure to address “Drying” period
Failure to assure drying conditions
![Page 14: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/14.jpg)
Blisters and Delaminations
• Result from bleed water and bleed air being trapped below the prematurely closed (densified) mortar surface
![Page 15: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/15.jpg)
Key Factors Related to Blisters & Delaminations
• Surface Finish
• Bleeding
• Consolidation
• Finishing Conditions and Procedures
![Page 16: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/16.jpg)
Surface Finish
• Stainless Steel finishing tools close or seal a concrete surface
• Many (most) applications do not need a steel trowel surface
![Page 17: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/17.jpg)
Contributors to Problem of Finish
Specifier R/M Supplier Contractor
Requiring Steel Trowel Finish when unnecessary
Applying steel trowel finish when unnecessary
![Page 18: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/18.jpg)
Bleeding/Bleed Water
• Bleed capacity and bleed rate affect timing of finishing.
• Bleeding affected by:– Water content– Fine particles content
(Cement, SCM’s, and sand)
– Air content– Some admixtures– Slab thickness
![Page 19: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/19.jpg)
Contributors to Bleeding ProblemsSpecifier R/M Supplier Contractor
Requiring high cementitious content
Supplying concrete with excessive cementitious content
Requiring high sand content
Using sand with excessive amount of -#30 particles and/or having over-sanded mix
Requiring air content above 3% when not necessary
Entraining excessive air in concrete (Intentionally or inadvertantly)
Providing high water content
Having water added at site
![Page 20: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/20.jpg)
Consolidation
• Insufficient amount leaves entrapped air in which a portion becomes bleed air
• Too much brings excessive fines to surface– Inviting crusting and
premature finishing
![Page 21: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/21.jpg)
Contributors to Consolidation Problems
Specifier R/M Supplier Contractor
Supplying a mix with poor composite aggregate gradation
Insufficient consolidation efforts
Supply of too wet of a mix
Overuse of vibrating screed on wetter mixes
Use of jitterbug
![Page 22: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/22.jpg)
Finishing Conditions & Procedures
• Applying stainless steel tools to the surface at the right time (at the right concrete conditions) is crucial– When bleeding has
ceased– Not necessarily when
surface seems to be hardening (Spongy)
Surface Crusting
Still plastic
![Page 23: How to Cause Scaling Two primary mechanisms and manifestations –Freeze-Thaw / Deicer Scaling –Sealed Surface Blistering and Delamination.](https://reader035.fdocuments.in/reader035/viewer/2022062516/56649de55503460f94addb88/html5/thumbnails/23.jpg)
Contributors to Inappropriate Finishing Conditions & Procedures
Specifier R/M Supplier Contractor
Mandating the timing of finishing
Ignoring atmospheric conditions
Allowing surface drying & crusting