/09 ARCHICOM TM ALUMINIUM HONEYCOMB PANEL PRODUCT INFORMATION TECHNICAL DATA Type ARCHICOM 6mm ARCHICOM 10mm ARCHICOM 15mm ARCHICOM 20mm ARCHICOM 25mm Thickness Front Cover Sheet, thickness mm 1.00 1.00 1.00 1.00 1.00 Back Cover Sheet, thickness mm 0.70 0.70 1.00 1.00 1.00 Weight # kg/m 2 4.90 5.10 6.70 7.00 7.30 Technical Properties Section Modulus W cm 3 /m 2.60 4.60 14.00 19.00 24.00 Rigidity E.I kNcm 2 /m 7100 21900 75500 139000 221700 Alloy of Aluminium Layers A3003 H18 / A3003 H24 Modulus of Elasticity N/mm 2 70000 Linear Thermal Expansion 2.4mm/m at 100ºC temperature difference Tensile Strength of Al. Layers Rm N/mm 2 ≥125 ≥125 ≥220 ≥220 ≥220 0.2% Proof Stress Rp0.2 N/mm 2 ≥80 ≥80 ≥130 ≥130 ≥130 Elongation A50 N/mm 2 ≥ 5% ≥ 5% ≥10% ≥10% ≥10% Surface Coating Type Fluorocarbon (PVDF) Gloss Level % between 30% to 80% Pencil Hardness HB - F Acoustical Properties Sound Absorption Factor α s 0.05 0.05 0.05 0.05 0.05 Airbone Sound Insulation Index Rw dB 21 21 22 23 25 Thermal Properties Thermal Conductivity* λ [W/mK] 0.95 1.35 1.78 2.25 2.70 Thermal Resistance R [m 2 K/W] 0.0063 0.0074 0.0084 0.0089 0.0093 Heat Transition Coefficient U [W/m 2 K] 5.67 5.64 5.605 5.59 5.575 Temperature Resistance approximately -40˚C to +80˚C HONEYCOMB CORE 1/4” 3/8” 1/2” 3/4” 1” Density Kg/m 3 81 54 38 30 21 Compressive Bare Strength Kg/mm 2 0.47 0.26 0.14 0.09 0.05 Crush Strength Kg/mm 2 0.19 0.08 0.05 0.03 0.02 Bonding Strength Kg/mm 2 36 28 26 21 19 Compressive Stabilized Strength Kg/mm 2 0.50 0.27 0.15 0.09 0.06 Compressive Stabilized Modulus Kg/mm 2 111 67 31 18 12 * Depends on the total thickness of the panel (including cover sheets) # Thickness of the aluminium cover sheet will affect the weight of the panel accordingly.
-
Upload
yam-balaoing -
Category
Documents
-
view
5 -
download
0
description
honeycombpanel
Transcript of Honeycomb Productinfo
/09 archIcomtm alumInIum honeycomb Panel
PrOduct infOrmatiOn
technIcal datatype archicom
6mmarchicom
10mmarchicom
15mmarchicom
20mmarchicom
25mm
thickness
front cover sheet, thickness mm 1.00 1.00 1.00 1.00 1.00
back cover sheet, thickness mm 0.70 0.70 1.00 1.00 1.00
Weight # kg/m2 4.90 5.10 6.70 7.00 7.30
technical properties
section modulus W cm3/m 2.60 4.60 14.00 19.00 24.00
rigidity e.I kncm2/m 7100 21900 75500 139000 221700
alloy of aluminium layers a3003 h18 / a3003 h24
modulus of elasticity n/mm2 70000
linear thermal expansion 2.4mm/m at 100ºc temperature difference
tensile strength of al. layers rm n/mm2 ≥125 ≥125 ≥220 ≥220 ≥220
0.2% Proof stress rp0.2 n/mm2 ≥80 ≥80 ≥130 ≥130 ≥130
elongation a50 n/mm2 ≥ 5% ≥ 5% ≥10% ≥10% ≥10%
surface
coating type fluorocarbon (Pvdf)
gloss level % between 30% to 80%
Pencil hardness hb - f
acoustical properties
sound absorption factor αs 0.05 0.05 0.05 0.05 0.05
airbone sound Insulation Index rw db 21 21 22 23 25
thermal properties
thermal conductivity* λ [W/mK] 0.95 1.35 1.78 2.25 2.70
thermal resistance r [m2K/W] 0.0063 0.0074 0.0084 0.0089 0.0093
Heat Transition Coefficient u [W/m2K] 5.67 5.64 5.605 5.59 5.575
temperature resistance approximately -40˚C to +80˚C
honeycomb core1/4” 3/8” 1/2” 3/4” 1”
density Kg/m3 81 54 38 30 21
compressive bare strength Kg/mm2 0.47 0.26 0.14 0.09 0.05
crush strength Kg/mm2 0.19 0.08 0.05 0.03 0.02
bonding strength Kg/mm2 36 28 26 21 19
compressive stabilized strength Kg/mm2 0.50 0.27 0.15 0.09 0.06
compressive stabilized modulus Kg/mm2 111 67 31 18 12
* depends on the total thickness of the panel (including cover sheets)# thickness of the aluminium cover sheet will affect the weight of the panel accordingly.