Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information...
Transcript of Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information...
![Page 1: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/1.jpg)
S-1
Supporting information
Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the
Regenerative Removal of CO2 from air
Kochukunju Adisser Saraladevi Abhilash,* Thomas Deepthi, Retnakumari Amma Sadhana, and
K. George Benny
Analytical and Spectroscopy Division, Analytical Spectroscopy and Ceramics Group,
Propellants, Polymers, Chemicals and Materials Entity, Vikram Sarabhai Space Centre,
Trivandrum 695022, Kerala, India.
e-mail: [email protected]
![Page 2: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/2.jpg)
S-2
Scheme S1. General scheme for the formation of polysilsesquioxane.
Figure S1. FT-IR spectrum of MAHSM.
![Page 3: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/3.jpg)
S-3
(a) (b)
Figure S2. a) 13C CP-MAS and b) 29Si CP-MAS NMR of MAHSM.
Figure S3. Raman spectrum of MAHSM
![Page 4: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/4.jpg)
S-4
Figure S4. XRD of MAHSM.
Figure S5. Thermogram of MAHSM.
![Page 5: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/5.jpg)
S-5
Figure S6. Heat of adsorption of MAHSM using isothermal DSC.
![Page 6: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/6.jpg)
S-6
(a)
(b)
Figure S7. (a) Thermogram and Total ion current (TIC) of the sample
(b) MS of the evolved species.
![Page 7: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/7.jpg)
S-7
Figure S8. CO2 adsorption from air by MAHSM at different temperatures.
Figure S9. Effect of temperature on desorption of CO2 shown by MAHSM.
![Page 8: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/8.jpg)
S-8
Figure S10. IR spectrum of MAHSM after (a) CO2 adsorption (b) CO2 desorption.
Figure S11. Structures of (a) Ionic carbamate (propyl ammonium carbamate)
(b) bound carbamate (silyl propyl carbamate) with corresponding IR peak positions.
![Page 9: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/9.jpg)
S-9
Figure S12. 13C CP-MAS NMR of MAHSM (a) after 1 cycle (b) after 50 cycles of adsorption at
30 °C in air and desorption at 80 °C under He flow (c) after 40 cycles of adsorption at 30 °C in
100% CO2 and desorption at 120 °C under He flow.
![Page 10: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/10.jpg)
S-10
Table S1. Effect of molar concentration of silane on the CO2 adsorption of the product.
Ratio
(x:y)a)
CO2 adsorption (120 min in 100% CO2)
(mmol/g)
Material prepared as
such from aged silane
mixture
Material prepared after
diluting aged silane mixture
in absolute ethanol
1:0 0 0.05
2:1 0.3 1.25
1:1 0.86 2.28
1:2 1.4 1.72
a)x = 3-Amino propyl triethoxy silane, y = Vinyl triethoxy siloxane
Table S2. Effect of aging period of ASVS (1:1) mixture on thermal stability and CO2 adsorption
properties of final product.
Aging
period
Td (5%)
(°C)
CO2 adsorption
(120 min in 100% CO2)
(mmol/g)
1 day 395 1.92
2 days 410 2.11
5 days 458 2.28
7 days 460 2.26
![Page 11: Functionalized Polysilsesquioxane Based Hybrid Silica ... · S-1 Supporting information Functionalized Polysilsesquioxane – Based Hybrid Silica Solid Amine Sorbents for the Regenerative](https://reader030.fdocuments.in/reader030/viewer/2022040313/5e075a429984a70e1b089741/html5/thumbnails/11.jpg)
S-11
Table S3. Comparison with the best solid amine sorbents reported for direct air capture.
Sorbent Adsorption
half time
(Thalf)
(min)
Av.rate of
adsorption to
reach Thalf
(μmol/g/min)
Maximum
Adsorption
(mmol/g)
Amine
efficiency
(%)
HAS644
(400 ppm CO2, 25°C,
Humid air)
167 5.1 1.72 17.3
AEAPDMS-NFC-FD65
(506 ppm CO2, 25°C
RH 40%)
92 7.6 1.39 28.0
MAHSM
(400 ppm CO2, 30°C, RH
60%) (This work)
50 17.9 1.68 37.3