Free Machining Stainless Steel

Wire

UGITECHBP 458160 IMPHYFRANCETel.: +33 (0)3 86 21 37 98Fax: +33 (0)3 86 21 31 03

UGITECHUnit 14 & 15Erdington Industrial ParkChester RoadBIRMINGHAM B24 0RDUNITED KINGDOMTel.: +44 121 377 34 00Fax: +44 121 382 93 39

SPRINT METAL Edelstahlziehereien GmbHOstenschlahstrasse 50D-58675 HEMERGERMANYTel.: +49 23 72 90 96 0Fax: +49 23 72 90 96 45

UGITECHAvenida Rey Juan Carlos 184 Despacho 3328916 LEGANES – MADRIDSPAINTel.: +34 91 686 00 79Fax: +34 91 687 67 77

TRAFILERIE BEDINI Srl.Via G. Di Vittorio, 34/3620068 PESCHIERA BORROMEO (MI)ITALYTel.: +39 02 54 74 34 14Fax: +39 02 54 74 34 30

UGITECHUL. Drezdenska 3A03969 WARSZAWAPOLANDTel.: +48 22 616 12 52Fax: +48 22 616 18 28

UGITECH Os.Slezska 1312000 PRAHA 2CZECH REPUBLICTel.: +420 221 001 550Fax: +420 221 001 506

UGITECH ASIA LIMITEDRegus Building2/F Shui On Centre6-8 Harbour RoadWANCHAI, HONG KONGHONG KONGTel.: +852 28 24 87 28Fax: +852 28 24 82 47

UGITECH USADoylestown Commerce Center2005 South Easton Road, Suite 208DOYLESTOWN, PA 18901UNITED STATESTel.: +1 215 345 52 00Fax: +1 215 345 81 00

UGITECH Free Machining Stainless Steel Wire

ww

w.t

hu

ria

.co

m -

Cré

dit p

hoto

s : U

gite

ch -

Soc

iété

MOR

ET -

ESC

O SA

- N

on-c

ontra

ctua

l doc

umen

t - 0

2/07

- D

7457

AISIstandard

designation

EURONORMEN 10.088/3

UGITECHcommercialdesignation

Chemical compositionSpECIfIC fEATURES

C Si Mn Ni Cr Mo Cu S p

304 Cu 1.4567 UGIMA® 304 L Cu 0.030 1.0 2.08.5

10.017.018.5

0.53.04.0

0.0150.04

0.04The best compromise between corrosion resistance and machinability

Well suited for deep drilling and plastic deformation (knurling - thread rolling)

303 1.4305 UGIMA® 303 0.080 1.01.02.0

8.09.5

17.018.5

0.60 0.750.250.35

0.04 The reference in machinability Austenitic steel appropriate for all types of free machining

1.4570 UGIMA® Vitinox 18X 0.080 1.01.02.0

8.09.5

17.018.5

0.601.02.5

0.250.35

Excellent machinability

free machining grade 4305 but with the addition of Cu to further improve machinability. Recommended for difficult machining operations.

316L 1.4435 UGIMA® 4435 0.030 1.0 2.012.513.5

17.018.0

2.53.0

0.750.0100.03

0.04Ugima grade designed to meet the needs of the Watchmaking Component Industry (ICH)

Excellent corrosion resistance. ferrite content <1%. Nickel salting out <0.5mg/cm2/week

430 F 1.4105 UGITECH 430 F 0.050 1.00.41.5

0.516.018.0

0.60,250,35

0.04 The alliance of magnetic properties with machinability

ferritic grade with improved machinability

416 1.4005 UGITECH 416 0.070.1

1.00.071.2

0.512.013.5

0.30.250.35

0.04 Martensitic stainless steel with a high degree of machinability

Recommended for rough drawn parts before treatment and finishing

420 1.4028 UGITECH 420 0.280.35

1.0 1.5 0.512.014.0

0.5 0.03 0.04The option of high mechanical properties in the heat treated condition

A combination of good mechanical properties in the treated state and good corrosion resistance in environments with low aggressivity

420 F 1.4029 UGITECH 420 F 0.260.31

1.00.71.3

0.512.013.0

0.40.150.25

0.04 The alliance of mechanical properties with machinability

Recommended for machined parts with high mechanical properties used in an environment with low aggressivity

Drum - pallet with coverØ 800 - H 600 - 250 Kg (Ø 31.5” - h 23.5” - 113 Lbs )

Free machiningTo meet the demands for precision and productivity of the free machining industry, our products combine the low-cost benefits of the UGIMA® grades with geometric precision.

GRADESAnnealed Cold drawn

diatol

Average Tensile diatol

Average Tensilemm inches mpa Ksi mm inches mpa Ksi

UGIMA® 304LCu 1 to 5 .039”to.196” ISO 9 600 87 1 to 9 .039”to.354” ISO 8 700 102

UGIMA® 303 1 to 5 .039”to.196” ISO 9 630 91 1 to 9 .039”to.354” ISO 8 750 109

UGIMA® Vitinox 18X 1 to 5 .039”to.196” ISO 9 630 91 1 to 9 .039”to.354” ISO 8 750 109

UGIMA® 4435 1 to 5 .039”to.196” ISO 9 650 94 1 to 9 .039”to.354” ISO 8 850 123

UGITECH 430F 2 to 5 .078”to.196” ISO 9 530 77 2 to 9 .078”to.354” ISO 8 600 87

UGITECH 416 2 to 5 .078”to.196” ISO 9 520 75 2 to 9 .078”to.354” ISO 8 600 87

UGITECH 420 2 to 5 .078”to.196” ISO 9 680 98 2 to 9 .078”to.354” ISO 8 830 120

UGITECH 420F 2 to 5 .078”to.196” ISO 9 650 94 2 to 9 .078”to.354” ISO 8 810 118

UGIMA®

A “must” in machinabilityIn addition to the usual parameters used to improve machinability (sulfur content, cold hardening, etc.), our main grades undergo the UGIMA®. processing mode. This process consists in controlling the inclusionary condition of the product, improving free machiningproductivity by 15 to 50%.

PerformanceOur grades represent the best compromise between:• corrosion resistance• machinability

HP QualityPossibility to produce high precision wires with ISO tolerances 6 and 7, with a “slightly cold hardened” metallurgical quality, in the size range between 1 and 5 mm. (.039” and .196”)

Standard product rangeSurface roughness in the lightly cold work conditiondia 1 < 2,50 Average Ra 0,4 micron CLAdia 2,50 < 5,00 Average Ra 0,8 micron CLA dia ≥ 5,00 Average Ra 1,2 micron CLA

Coils from 30 to 100 Kg (13.5 Lbs to 45 Lbs) on palletInside coil Ø: Ø 1 to 1.50 mm = 350 mm(.039” to .196” = 13.8”)Ø > 1.50 mm = 500 mm(.060” = 19.7”)

Packaging

Reels, 250 or 400Kg(113 Lbs or 181 Lbs)Outside Ø 760 mm (30”boring Ø 40 mm (1.58”)

Wires recommended by Esco S.A.