HEAT EXCHANGER/PRESSURE VESSEL 

 

SPECIFICATIONS FOR INSPECTION OF HEATER AND ASSOCIATED COMPONENTS: 

1) All  materials  need  to  be  identified  against  test  certificates  at  the  vendor’s  works  before commencement of fabrication. 

2) Specimen samples must be taken and strength analysis be carried out. Heat treatment charts for all materials need to be prepared and complied with. 

3) Ensuring that edge preparation is carried out in accordance with standard welding practices for high pressure equipment. 

4) Ensure that welding procedures are carried out in accordance with the standards. Also, certified welders  are  appointed  to  perform  the  job  and  appropriate welding  electrodes  are  used  for welding the components. These must be approved before commencement of fabrication. 

5) Radiography of welds  is mandatory and  the  reports are analyzed and necessary approvals are obtained. 

6) Establish procedures for hydro test (75 bar) and carry them out. 7) An  expendable  gasket  (1  no.)  suitable  for  hydro‐test  of  the  heat  exchanger  should  be  used, 

which will be discarded thereafter. 8) A new  SS heat exchanger gasket  (AISI 304),  in packed  condition  to be  supplied  to  the  Indian 

Institute of Science as mentioned in List of Components.  9) All  the above procedures are carried out and established by  third party  inspectors, preferably 

Lloyds. 10) Variations in size of the shell may be permitted upto ±10mm. Minimum thickness of the shell to 

be 60mm.  11) Circularity  (surface  finish N12  to N25)  of  the  inner wall  of  the  shell  to  be maintained  and  if 

necessary machining  is permitted to obtain the same. Machining of the shell on the outside  is not necessary as the heat exchanger will be insulated with appropriate ceramic blankets. 

12) It  is  preferable  to  have  a  seamless  shell,  if  the  process  permits. However,  a welded  shell  is technically acceptable if statutory tests are carried out for its approval. 

 

 

 

 

 

 

 

Kindly mention  if all the major components  like shell, dished end, Weld neck RF flange, Slip on RF flange are made out of multiple welded pieces or made without welds. Please tick, if the component is manufactured in single piece else mention the number of parts in the chart given below: 

Sl. No.  Part Name  Single piece  Multiple pieces welded 1  Heater Shell     2  Dished End     3  Weld neck RF Flange     4  Slip on RF Flange