Monolithic Wide Band Gap Perovskite/ Perovskite
Tandem Solar Cells with Organic Recombination
Layers
Rui Shenga†, Maximilian T. Hörantnerb†, Zhiping Wangb, Yajie Jianga, Wei Zhang,c,
Amedeo Agostid, Shujuan Huanga, Xiaojing Haoa, Anita Ho-Bailliea*, Martin Greena, Henry
J. Snaithb*
aAustralian Centre for Advanced Photovoltaics (ACAP), School of Photovoltaic and
Renewable Energy Engineering, University of New South Wales, Sydney 2052, Australia
bDepartment of Physics, University of Oxford, Parks Road, Oxford, OX1 3PU, United
Kingdom
cAdvanced Technology Institute, University of Surrey, Guildford GU2 7XH, UK
dDepartment of Materials, ETH Zurich, CH-8093 Zurich, Switzerland
† These authors contribute equally to this work
*Corresponding author: [email protected] , [email protected]
Abstract
We demonstrate a monolithic tandem solar cell by sequentially depositing a higher-bandgap (2.3 eV)
CH3NH3PbBr3 sub-cell and a lower-bandgap (1.55 eV) CH3NH3PbI3 sub-cell bandgap perovskite
cells, in conjugation with a solution-processed organic charge carrier recombination layer, which
serves to protect the underlying sub-cell and allows for voltage addition of the two sub-cells. Owing
to the low-loss series connection, we achieve a large open-circuit voltage of 1.96 V. Through optical
and electronic modelling, we estimate the feasible efficiency of this device architecture to be 25.9 %,
achievable with integrating a best-in-class CH3NH3PbI3 sub cell and a 2.05 eV wide bandgap
perovskite cell with an optimised optical structure. Compared to previous reported all-perovskite
tandem cells, we solely employ Pb-based perovskites, which although have wider band gap than Sn
based perovskites, are not at risk of instability due to the unstable charge state of the Sn 2+ ion.
Additionally, the bandgap combination we use in this study could be an advantage for triple junction
cells on top of silicon. Our findings indicate that wide band gap all-perovskite tandems could be a
feasible device structure for higher efficiency perovskite thin-film solar cells.
Introduction
Methylammonium lead halide perovskite solar cells have attracted enormous research
interest since the seminal work of CH3NH3PbX3 (X=Br, I) perovskite-sensitized solar cells
reported by Kojima et al. in 2009, and the demonstration of highly efficient solid-state
perovskite solar cells in 20121,2. Tremendous power conversion efficiency enhancements
have been achieved since then3-8, 42. The improved photovoltaic performance has been
attributed to excellent optical properties9, long carrier diffusion lengths 10-13, and high light
emission yields14. Apart from improving the properties of the perovskite solar cell, overall
efficiency gains can be achieved by moving towards multiple junctions, where a series of
solar cells that absorb in different regions of the solar spectrum are stacked on top of each
other. By this means, more energy is extracted from the sun light, which raises the sealing on
the ultimate efficiency achievable once fully optimised. Much work thus far has focused on
developing “hybrid” tandem cells by combining perovskite with established photovoltaics
like silicon. However, compared with the tandem cell structure with a high efficiency silicon
bottom cell and a perovskite top cell15-19, the combination of two large band gap perovskite
cells is capable of providing much higher voltage, which could be very interesting for not just
solar photovoltaic electricity generation, but also enabling direct power conversion from solar
energy to chemical energy such as solar fuels20,21. There are many aspects requiring
optimisation, in order to enable a multi-junction solar cell to operate efficiently. One of which
is the recombination layer between the junctions, which serves both as charge recombination
centre and as a protection layer for the underlying cell during the deposition of second
junction. Many materials have been proposed as the recombination layer for the
perovskite/silicon tandem architecture15,19 and for perovskite/perovskite tandem structures. 20
Recently, Eperon et al. demonstrated that efficient 2-terminal all-perovskite tandem solar
cells could be fabricated by including a dense sputter-coated indium oxide tin oxide (ITO)
layer as the intermediate recombination electrode, which also served to protect the underlying
cell from subsequent processing steps22. However, sputter coating, which is a relatively
aggressive deposition technique, upon the sensitive perovskite cells requires the introduction
of multiple additional “buffer” layers in order to protect the underlying perovskite cells from
sputter damage, and prevent the potential effect of sputter induced unintentional heating. In
addition, the thick ITO layer, with a lower refractive index to the perovskite layers, is likely
to introduce optical interference loses which are non-ideal for maximising the efficiency of a
tandem solar cell. It would be desirable if a printable recombination layer could be developed
which obviated the requirement for the sputter coated ITO. Additionally, we use two
complementary Pb based absorbers which do not suffer from the same oxygen sensitivities of
the lower band gap Sn based perovskite absorbers.
In this study, we introduce a bi-layer of C60 and PEDOT:PSS as the recombination junction,
and demonstrate a device structure of FTO/ compact TiO2/ mesoporous TiO2/ CH3NH3PbBr3/
Spiro-OMeTAD/ PEDOT: PSS/ C60/ CH3NH3PbI3/ Spiro-OMeTAD/ Au, and achieved a high
open circuit voltage of up to 1.96 V. We subsequently perform combined optical and
electronic modelling to reveal where the present major optical loses exist, and identify a
precise device stack which could lead to tandem open-circuit voltages of up to 2.69 V, and
solar cell efficiencies of up to 25.9 %, with realistic device characteristics for the top and
bottom cells.
Results and discussion
Figure 1(a) shows the energy band diagram of the proposed tandem cells. Both top cell and
bottom cell have the regular n-i-p structure with Spiro-OMeTAD as the hole transport
material (HTM). Here we define the cell first receiving the light as the top cell, and the
bottom cell is the second cell to be processed, which is subsequently capped with a metallic
Au electrode. The primary criteria for a recombination layer is for it to have an appropriate
work function to contact the p-type side of one cell and the n-type side of the other cell. In
our current device structure the holes generated from CH3NH3PbBr3 cell and electrons from
CH3NH3PbI3 cell must recombine in the recombination layer. Therefore either a highly doped
“metallic” recombination layer is required, or a layer consisting of a highly doped p- and n-
type tunnel-junction. Another requirement for the recombination layer for all-perovskite
tandem cells is that we do not subject it to excessive thermal treatment, otherwise accelerated
degradation of the underlying bromide cell could occur. As a solution processed
recombination layer, orthogonal solvents are also required for each adjacent layer. We
employ Spiro-OMeTAD as the first p-type layer to transport holes from the bromide top cell,
and C60 as the n-type electron transporter extracting electrons from the iodine bottom cell.
For the recombination layer we simply employ a thin and pinhole-free layer of PEDOT:PSS.
Figure 1. (a) Schematic energy band diagram and (b) device architecture of perovskite/
perovskite tandem structure.
We show the complete tandem device architecture in Figure 1b, and a schematic of the
energy levels of the materials we employ in Figure 1a. For cell fabrication we spin-coated a
compact layer of TiO2 on patterned fluorine doped tin oxide (FTO) substrates, followed by a
thin layer of mesoporous TiO2. Subsequently, we fabricated the CH3NH3PbBr3 film by the
vapour-assisted solution-processing method within the mesoporous structure12,23: We first
spin-coated a PbBr2 solution in DMF on top of mesoporous TiO2. We then exposed the
annealed PbBr2 film to a CH3NH3Br vapour (crucible temperature 175 ⁰C) for 10 min in dry
air. After the bromide cell perovskite deposition we spin-coated Spiro-OMeTAD. For the
conductive charge recombination layer we diluted the PEDOT:PSS (PH1000, Heraeus) in
isopropanol (IPA) and spin-coated the film, followed by a 120 ᵒC anneal for ten minutes in
air. We subsequently deposited the C60 in dichlorobenzene by spin-coating. To increase the
wettability, and also the conductivity of C60, we added 10 mg/ml 4-(1,3-dimethyl-2,3-
dihydro-1H-benzimidazol-2-yl)-N,N-diphenylaniline (N-DPBI) (in dichlorobenzene) to the
C60 solution as an n-dopant, with a concentration of 10 µl/ml24. Encouragingly, we observed
no evidence of the Spiro-OMeTAD being dissolved by the subsequent C60 deposition process,
This implies that the PEDOT:PSS layer is suitably dense and pin-hole free so as to protect the
underlying cell. We also note that this structure is not compatible with solution processing of
the CH3NH3PbI3 film that involves the use of solvent Dimethylformamide (DMF), which we
found dissolves the underlying perovskite structure, indicating that DMF can permeate
through this multi-layer device stack. To overcome this issue we employed a sequential
vapour-solution processing method whereby we deposited a CH3NH3PbI3 film by thermal
evaporation of the PbI2 and then converted to perovskite via inter-diffusion of MAI from an
isopropanol solution25. Although perovskite films can be fabricated via this method, due to
the limited penetration of CH3NH3I, thick PbI2 films results in unreacted residual PbI2.
Therefore we found that the optimized PbI2 thickness for maximizing the single junction
device performance was only 115 nm, leading to ~200 nm thick final perovskite film.
Following this second perovskite layer deposition, we spin-coated the final Spiro-OMeTAD
film and capped the devices with a gold electrode.
We show a scanning electron microscope (SEM) cross-sectional image in Figure 2a of
CH3NH3PbBr3/CH3NH3PbI3 tandem solar cell, with a complete layered structure (with layer
thickness’ in brackets) of FTO (300nm) compact TiO2 (40nm), mesoporous TiO2 (350nm),
CH3NH3PbBr3 (350nm), Spiro-OMeTAD (185nm), PEDOT: PSS (80nm), C60 (30nm),
CH3NH3PbI3 (200nm), Spiro-OMeTAD (250nm) and gold (100nm). Notably, we observe a
rather rough but fully covered C60 film. This may be due to the poor wettability of C60
solution on the PEDOT: PSS film.
Figure 2. (a) Cross-sectional SEM image of tandem cell and (b) JV curves for individual
cell and monolithic tandem. (c) Stabilized efficiency and current output of tandem cell.
We show the J-V curves and photovoltaic performance parameters of the fabricated
individual cells and tandem cells in Figure 2b and in Table 1. The structure for single
junction iodine cell is glass/ FTO/ compact TiO2/ CH3NH3PbI3/ Spiro/ Au. For high band gap
single junction cell is glass/ FTO/ compact TiO2/ mesoporous TiO2/ CH3NH3PbBr3/ Spiro/
Au. We measure an open-circuit voltage of over 1.4 V for the single junction bromide cell,
which as others have observed can be attributed to the large bandgap of CH3NH3PbBr3. We
observe a significantly boosted open-circuit voltage for the tandem solar cell, up to 1.96 V.
However, this tandem cell open-circuit voltage is not the linear sum of both sub cells, which
should be up to 2.44 V, indicating that we have introduced some additional voltage losses in
the tandem cell construction or in the recombination layer. In addition, the J-V curve of
tandem device shows a low fill factor, also indicative of resistive losses in the recombination.
In Figure 2c, we show the power output measured over time for the tandem cell. We observe
that the efficiency of the tandem cell take up to 500 s before it reaches its stabilized value of
5.9%. We did not observe this severe light soaking in either of the single junction iodine and
bromide cells. This indicates that some “light healing” effect is occurring26. Previous study
suggested that the C60 layer would be partially washed away after perovskite deposition,
which would result in inhomogeneous/discontinuous morphology38. We therefore postulate
that we have some regions of direct contact of the perovskite to the PEDOT:PSS
recombination layer through pin-holes in the C60. These regions will induce rapid surface
recombination in the CH3NH3PbI3 layer being detrimental to open-circuit voltage. Upon light
soaking, defects at this interface, through which the surface recombination occurs, may
become temporarily passivated through ion migration.
Table 1. Photovoltaic performance of single junction and tandem cell.
Scan sirection
Voc (V)
Jsc (mA/cm2)
FF (%)
PCE (%)
CH3NH3PbI3Reverse 1.04 17.30 71 12.7Forward 1.04 17.66 61 11.1
CH3NH3PbBr3Reverse 1.41 6.16 64 5.2Forward 1.35 5.81 55 4.4
Monolithic tandem
Reverse 1.96 6.40 41 5.1Forward 1.87 6.00 40 4.6
We have constructed working all-perovskite tandem solar cells, however, their operation is
non-optimum and significant improvement is required in order to make them competitive and
eventually superior to the best single junction perovskite cells. However, it is valuable to
understand where the current losses are, and how efficient these wide-band-gap all-perovskite
tandem cells could become, once fully optimized.
For this purpose, we firstly estimate the optical losses in our tandem device stack, via
performing an optical transfer matrix model. We account for the roughness of each layer by
employing an effective medium approximation between the adjacent layers.
We extract the optical constants, refractive index n and extinction coefficient k, of each
individual layer by fitting ellipsometry data as well as transmission spectra over the
wavelength range of interest. We show the measured and modelled transmittance (T) of the
top bromide cell and recombination layer in Figure S2, which show good agreement between
the experimental and modelled data with the discrepancy attributable to the non-uniformity of
the mesoporous layer and the roughness of C60 layer, see Figure 2a for cross-sectional SEM
image, which propagates throughout the whole structure. This fitting also validates the optical
model36, 37.
We used the determined optical constants and thickness of each layer to calculate the total
reflection and absorption occurring within each layer of the device27. Under the assumption
that 100% IQE (Internal Quantum Efficiency) across the measured spectrum could be
achieved28,29, we determined the External Quantum Efficiency (EQE) by assuming all light
absorbed within each perovskite layer leads to photocurrent generation.
In order to estimate the current-voltage characteristic of each sub cell we employed the
detailed balance limit theory, taking into account parasitic power consuming parameters from
an equivalent one-diode circuit model, such as series resistance, shunt resistance, ideality
factor and reverse saturation current30,31. Specifically for determining these device parameters,
we extracted the shunt and series resistances, ideality factor and reverse saturation current by
fitting published experimental data from the best in class 1.55 eV band gap perovskite cells32.
We show the extracted diode parameters in Table S3 of the SI. We calculated the reverse
saturation dark current via integrating our calculated EQE spectrum over the black body
spectrum at 300K, following methods reported in the literature33.
In Figure 3a we present our modeled external quantum efficiency spectrum of the device
stack we used experimentally, which we calculate assuming 100% internal quantum
efficiency for light absorbed in each perovskite junction. It is quite apparent that there are
many optical losses in the region of the spectrum. Because PEDOT:PSS does absorb a
fraction of the solar spectrum itself. As a final optimisation, we reduced the PEDOT:PSS
thickness to zero, and allowed all layer thickness to vary. Although this seems unrealistic, it
is equivalent to swapping PEDOT:PSS for a more transparent highly doped organic
semiconductor, which for instance Bolink et al 47. have shown to work very well in all-
evaporated perovskite multi-junction cells. We fix the band gap of the rear cell to that of
MAPbI3, shift the band gap of the top cell in 0.1eV steps and allow each structure to
optimise. For calculating the efficiency of the MAPbBr3 cell, we now apply the diode
characteristics of the best-in-class lower gap perovskite cell, to estimate the ultimate
efficiency feasible once these wider gap cells can be optimised to work comparably to the
best lower gap cells. From our calculations, the band gap of the top cell which delivers the
overall highest tandem efficiency is 2.05 eV. We note that the band gap of the MAPbBr3 and
FAPbBr3 films are 2.3 eV 12 and 2.25 eV 44. Therefore, there is a requirement to drop this
band gap 2.05eV in order to optimise a top-cell for a wide band gap all-perovskite tandem,
employing only Pb based perovskites. We show the EQE of the device stack with optimum
layer thickness in Figure 3c, thickness FTO (200 nm), compact TiO2 (33 nm), CH3NH3PbBr3
(1280 nm), Spiro-OMeTAD (140 nm), C60 (44 nm), CH3NH3PbI3 (1488 nm), Spiro-OMeTAD
(141 nm) and gold (100 nm). In Figure 3b and Table 2, we show the simulated cell
performance parameters for the top, bottom and tandem junctions for all the calculated
devices. It is apparent that in optimized stack, the maximum short-circuit current density (Jsc)
we could obtain from the front cell is 11.6 mA/cm2, and the maximum Jsc from the rear cell is
12.2 mA/cm2. For the tandem cell, the maximum VOC achievable is 2.69 V, with a
corresponding power conversion efficiency of 25.9 %. Our simulated results reveal that, by
increasing the thickness of CH3NH3PbBr3 capping layer to 395 nm, and CH3NH3PbI3 layer to
313 nm, the tandem structure can reach the maximum output.
A specific challenge with fine-tuning of the band gap for perovskite solar cells is that
this relies on precise compositional control of mixed halides. The Br and I compositions can
segregate in the perovskite layer, which can lead to reduction in the open-circuit voltage 45.
Although this can be suppressed for cells with band gaps around 1.7eV, halide segregation is
especially problematic for high Br contents in the I-Br mixed halide perovskites 46. Here, we
therefor estimate the efficiency achievable in a Pb-perovskite-on-Pb-Perovskite tandem solar
cell, if the band gap of the wide band gap cell has to remain at the band gap of the neat Br
perovskite, FAPbBr3, which is 2.25eV. If we combine the 2.25 eV band gap with a 1.55 eV
rear cell, we determine a maximum efficiency of 21.3%, with Jsc of 8.37 mA/cm2 and VOC of
2.9 V. If we allow the rear-cell band gap to widen, to satisfy current matching conditions, we
combine the 2.25 eV cell with a 1.80 eV rear cell, and determine an efficiency of 22.23%,
with a Jsc of 8.34 mA/cm2, VOC of 3.12 V, and a FF of 0.85. We present the simulated data in
Figure S3, S4 and Table S1, S2. Notably, these latter efficiencies are not significantly higher
than the best single junction perovskite solar cells reported to-date, which have band gaps
between 1.55 and 1.63eV. Therefore, our calculations highlight that FAPbBr3 is not a suitable
top cell material for Pb-perovskite-on-Pb-Perovskite tandem cells. Therefore, an essential
challenge is to achieve good stable efficiency with an absorber material with a band gap
closer to 2eV.
Figure 3. (a) simulated EQE for experimental stack, and simulated (b) JV and (c) EQE of
optimized cell architecture.
Table 2. Photovoltaic performance of single junction and tandem cell for calculated devices.
Voc (V) Jsc (mA/cm2) FF PCE (%)CH3NH3PbI3 1.07 12.2 0.84 10.76CH3NH3PbX3 1.61 11.6 0.83 15.2
Monolithic tandem 2.69 11.6 0.83 25.94
Conclusion
We have demonstrated operational all-perovskite tandem solar cells employing a solution
processed interlayer. Through subsequent optical and electronic modeling we have identified
that increasing the thickness of our rear lower band gap cell is required to further improve the
tandem cells. Of equal importance, improvement to the recombination layer is required in
order to overcome our present electrical losses. Once this has been achieved, our modeling
has revealed that tandem solar cell efficiencies of 25.9 % are feasible with a 2.05 eV band
gap top junction and a 1.55 eV band gap bottom junction, once the PV performance of each
junction reaches that of the current highest efficiency single junction cells. This is in
comparison to 22% efficiency, which is the current world-record for a single junction
perovskite cell. Therefore, future research in this area should focus on developing lossless
recombination junctions, and optimizing perovskite wide gap cells with close to 2.05 eV band
gaps. As a final consideration, these wide band gap perovskite tandem cells are well matched
to sit on top of silicon in a perovskite-perovskite-silicon triple junction cells. Investigating the
prospect of such triple junction cells is the subject of ongoing work.
Experimental Section
CH3NH3Br and CH3NH3I were synthesized following a previously reported method34, by
mixing methylamine (33% in methanol, Sigma-Aldrich) with hydrobromic acid (40% in
methanol, Sigma-Aldrich) or hydriiodic acid (48% in water, Sigma-Aldrich) in a 1:1 molar
ratio in a 250ml round bottom flask under continuous stirring at 0⁰C for 2h. The precipitates
were recovered by rotary evaporation at 60⁰C. To increase the purity of products, the powder
was then dissolved in ethanol, recrystallized from diethyl ether. The final product was
collected after dehydration at 60⁰C and placed in a vacuum chamber for overnight.
Solar cell devices were fabricated on fluorine-doped tin oxide (FTO) coated glass
(Pilkington, 8 Ω/square). FTO was patterned with 2 M HCl and zinc powder. Substrates were
then cleaned in 2% Hallmanex detergent, acetone and isopropanol in ultrasonic bath for
10min in each cleaning agent followed by oxygen plasma treatment for 10min. The compact
TiO2 layer was deposited by spin-coating a mildly acidic solution of titanium isopropoxide in
ethanol at 2500 rpm for 60 s followed by annealing at 500 ⁰C for 30 min. The mp-TiO2 layer
composed of 20-nm-sized particles was deposited by spin-coating at 2000 rpm for 60s using a
commercial TiO2 paste (Dyesol 18NRT, Dyesol) diluted in ethanol (2:7, weight ratio). After
dried at 125 ⁰C, the TiO2 film was heated to 500 ⁰C, annealed at this temperature for 30 min
and gradually cooled to room temperature.
CH3NH3PbBr3 films were deposited using the vapour-assisted method. Firstly, PbBr2
solution in DMF with a concentration of 1 M was spin-coated on the mp-TiO2 at 2500 rpm
for 60s. After annealing at 70 ⁰C for 30 min, the film was treated by CH3NH3Br vapour at
175 ⁰C for 10 min in a closed glass petri-dish with CH3NH3Br powder surrounded on a
hotplate in glovebox, then rinsed in isopropanol at room temperature. HTM was then
deposited by spin-coating at 2000 rpm for 60 s. The solution was prepared by dissolving 72.3
mg (2,2’,7,7’-tetrakis-(N, N-di-p-methoxyphenyl-amine)-9,9’-spirobifluorene) (Spiro-
MeOTAD), 28.8 ml 4- tert-butylpyridine (4-TBP), anniqued 17.5 ml of a stock solution of
520 mg/ml lithium bis(trifluoromethane)sulfonimide (LiTFSI) in acetonitrile in 1 ml
Chlorobenzene. The samples were left overnight in dry air before recombination layer
deposition.
PEDOT: PSS was diluted in IPA with volume ratio of 1:4, solution was spined on oxidized
Spiro-OMeTAD films at 5000 rpm for 45 s, then was annealed at 120 ⁰C for 15 min. C60 was
dissolved in Dichlorobenzene with concentration of 10 mg/ml, solution was kept at 100 ⁰C
before spin-coating, which at 2000 rpm for 30 s. followed by annealing at 100 ⁰C for 10 min.
CH3NH3PbI3 films were deposited by inter-diffusion method. 115 nm PbI2 was evaporated
in a vacuum chamber; CH3NH3I solution in IPA with concentration of 20 mg/ml was then
spin-coated at 6000 rpm for 30s. After annealing at 100 ⁰C for 60 min, Spiro-OMeTAD was
deposited with identical recipe and spin-coating condition as described above. To complete
the devices, 100nm gold contacts were thermally evaporated on the back through a shadow
mask.
The optical and electronic device simulation was carried out by initially applying a transfer
matrix model43 with the input of published complex refractive indices for the layered
materials. The modelled absorption spectrum was assumed to resemble the EQE, if 100%
internal quantum efficiency is present. The EQE for each of the two absorbing layers was
then used for the detailed balance theory39 to calculate JSC and J0 and plugged into the one-
diode equivalent circuit equation:
J (V )=J SC−J 0 ¿
The loss parameters (RSH, RS),ideality factor (m) and reverse saturation current (J0) were
extracted from published currently best performing JV characteristics of the corresponding
perovskite devices. The modelled JV characteristic curves were combined by limiting the
combined JSC to the lower JSC delivering cell and adding the voltages of both devices for each
current step40. The performance parameters, PCE, FF, VOC, JSC were then extracted from the
resulting JV curve. In order to find the optimal thicknesses of the layers, a differential
evolution optimisation algorithm41 was used to vary the thicknesses and maximise the
resulting PCE.
Supporting Information
The supporting information is available free of charge on the ACS Publications website.
Hysteresis of fabricated monolithic tandem solar cell, the measured and modelled
transmittance of the top bromide cell and recombination layer, as well as the calculated JV
for 2.25 eV top cell, and parameters used for simulation are presented in the supporting
information.
Acknowledgement
The Australian Centre for Advanced Photovoltaics (ACAP) encompasses the Australian-
based activities of the Australia-US Institute for Advanced Photovoltaics (AUSIAPV) and is
supported by the Australian Government through the Australian Renewable Energy Agency
(ARENA). Responsibility for the views, information or advice expressed herein is not
accepted by the Australian Government. This work is part funded by EPSRC, UK, through
EP/M024881/1.
Reference
(1) Green, M. A.; Ho-Baillie, A.; Snaith, H. J. The emergence of perovskite solar cells. Nat Photon 2014, 8, 506-514.
(2) Kojima, A.; Teshima, K.; Shirai, Y.; Miyasaka, T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. Journal of the American Chemical Society 2009, 131, 6050-6051.
(3) Im, J.-H.; Lee, C.-R.; Lee, J.-W.; Park, S.-W.; Park, N.-G. 6.5% efficient perovskite quantum-dot-sensitized solar cell. Nanoscale 2011, 3, 4088-4093.
(4) Lee, M. M.; Teuscher, J.; Miyasaka, T.; Murakami, T. N.; Snaith, H. J. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 2012, 338, 643-647.
(5) Liu, M.; Johnston, M. B.; Snaith, H. J. Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 2013, 501, 395-398.
(6) Burschka, J.; Pellet, N.; Moon, S.-J.; Humphry-Baker, R.; Gao, P.; Nazeeruddin, M. K.; Gratzel, M. Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 2013, 499, 316-319.
(7) Kim, H.-S.; Lee, C.-R.; Im, J.-H.; Lee, K.-B.; Moehl, T.; Marchioro, A.; Moon, S.-J.; Humphry-Baker, R.; Yum, J.-H.; Moser, J. E.; et al. Lead iodide perovskite sensitized all-solid-state submicron thin film mesoscopic solar cell with efficiency exceeding 9%. Scientific Reports 2012, 2, 591.
(8) Jeon, N. J.; Noh, J. H.; Yang, W. S.; Kim, Y. C.; Ryu, S.; Seo, J.; Seok, S. I. Compositional engineering of perovskite materials for high-performance solar cells. Nature 2015, advance online publication.
(9) Jiang, Y.; Green, M. A.; Sheng, R.; Ho-Baillie, A. Room temperature optical properties of organic–inorganic lead halide perovskites. Solar Energy Materials and Solar Cells 2015, 137, 253-257.
(10) Stranks, S. D.; Eperon, G. E.; Grancini, G.; Menelaou, C.; Alcocer, M. J. P.; Leijtens, T.; Herz, L. M.; Petrozza, A.; Snaith, H. J. Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 2013, 342, 341-344.
(11) Xing, G.; Mathews, N.; Sun, S.; Lim, S. S.; Lam, Y. M.; Grätzel, M.; Mhaisalkar, S.; Sum, T. C. Long-range balanced electron- and hole-transport lengths in organic-inorganic CH3NH3PbI3. Science 2013, 342, 344-347.
(12) Sheng, R.; Ho-Baillie, A.; Huang, S.; Chen, S.; Wen, X.; Hao, X.; Green, M. A. Methylammonium lead bromide perovskite-based solar cells by vapor-assisted deposition. The Journal of Physical Chemistry C 2015, 119, 3545-3549.
(13) Wehrenfennig, C.; Eperon, G. E.; Johnston, M. B.; Snaith, H. J.; Herz, L. M. High charge carrier mobilities and lifetimes in organolead trihalide perovskites. Advanced Materials 2014, 26, 1584-1589.
(14) Deschler, F.; Price, M.; Pathak, S.; Klintberg, L. E.; Jarausch, D.-D.; Higler, R.; Hüttner, S.; Leijtens, T.; Stranks, S. D.; Snaith, H. J.; et al. High photoluminescence efficiency and optically pumped lasing in solution-processed mixed halide perovskite semiconductors. The Journal of Physical Chemistry Letters 2014, 5, 1421-1426.
(15) Mailoa, J. P.; Bailie, C. D.; Johlin, E. C.; Hoke, E. T.; Akey, A. J.; Nguyen, W. H.; McGehee, M. D.; Buonassisi, T. A 2-terminal perovskite/silicon multijunction solar cell enabled by a silicon tunnel junction. Applied Physics Letters 2015, 106, 121105.
(16) Sheng, R.; Ho-Baillie, A. W. Y.; Huang, S.; Keevers, M.; Hao, X.; Jiang, L.; Cheng, Y.-B.; Green, M. A. Four-terminal tandem solar cells using CH3NH3PbBr3 by spectrum splitting. The Journal of Physical Chemistry Letters 2015, 3931-3934.
(17) Loper, P.; Moon, S.-J.; Martin de Nicolas, S.; Niesen, B.; Ledinsky, M.; Nicolay, S.; Bailat, J.; Yum, J.-H.; De Wolf, S.; Ballif, C. Organic-inorganic halide perovskite/crystalline silicon four-terminal tandem solar cells. Physical Chemistry Chemical Physics 2015, 17, 1619-1629.
(18) Sista, S.; Park, M.-H.; Hong, Z.; Wu, Y.; Hou, J.; Kwan, W. L.; Li, G.; Yang, Y. Highly efficient tandem polymer photovoltaic cells. Advanced Materials 2010, 22, 380-383.
(19) Albrecht, S.; Saliba, M.; Correa Baena, J. P.; Lang, F.; Kegelmann, L.; Mews, M.; Steier, L.; Abate, A.; Rappich, J.; Korte, L.; et al. Monolithic perovskite/silicon-heterojunction tandem solar cells processed at low temperature. Energy Environ. Sci 2016, 9, 81-88.
(20) Jiang, F.; Liu, T.; Luo, B.; Tong, J.; Qin, F.; Xiong, S.; Li, Z.; Zhou, Y. A two-terminal perovskite/perovskite tandem solar cell. Journal of Materials Chemistry A 2016, 4, 1208-1213.
(21) Heo, J. H.; Im, S. H. CH3NH3PbBr3–CH3NH3PbI3 Perovskite–perovskite tandem solar cells with exceeding 2.2 V open circuit voltage. Advanced Materials 2015, n/a-n/a.
(22) Eperon, G. E.; Leijtens, T.; Bush, K. A.; Prasanna, R.; Green, T.; Wang, J. T.-W.; McMeekin, D. P.; Volonakis, G.; Milot, R. L.; May, R.; Palmstrom, A.; et al. Perovskite-perovskite tandem photovoltaics with optimized bandgaps. Science 2016.
(23) Chen, Q.; Zhou, H.; Hong, Z.; Luo, S.; Duan, H.-S.; Wang, H.-H.; Liu, Y.; Li, G.; Yang, Y. Planar heterojunction perovskite solar cells via vapor-assisted solution process. Journal of the American Chemical Society 2013, 136, 622-625.
(24) Wang, Z.; McMeekin, D. P.; Sakai, N.; van Reenen, S.; Wojciechowski, K.; Patel, J. B.; Johnston, M. B.; Snaith, H. J. Efficient and air-stable mixed-cation lead mixed-halide perovskite solar cells with n-doped organic electron extraction layers. Advanced Materials 2017, 29, 1604186.
(25) Xiao, Z.; Bi, C.; Shao, Y.; Dong, Q.; Wang, Q.; Yuan, Y.; Wang, C.; Gao, Y.; Huang, J. Efficient, high yield perovskite photovoltaic devices grown by interdiffusion of solution-processed precursor stacking layers. Energy & Environmental Science 2014, 7, 2619-2623.
(26) deQuilettes, D. W.; Zhang, W.; Burlakov, V. M.; Graham, D. J.; Leijtens, T.; Osherov, A.; Bulović, V.; Snaith, H. J.; Ginger, D. S.; Stranks, S. D. Photo-induced halide redistribution in organic–inorganic perovskite films. Nature Communications 2016, 7, 11683.
(27) Centurioni, E. Generalized matrix method for calculation of internal light energy flux in mixed coherent and incoherent multilayers. Appl. Opt. 2005, 44, 7532-7539.
(28) Lin, Q.; Armin, A.; Nagiri, R. C. R.; Burn, P. L.; Meredith, P. Electro-optics of perovskite solar cells. Nat Photon 2015, 9, 106-112.
(29) Ball, J. M.; Stranks, S. D.; Horantner, M. T.; Huttner, S.; Zhang, W.; Crossland, E. J. W.; Ramirez, I.; Riede, M.; Johnston, M. B.; Friend, R. H.; et al. Optical properties and limiting photocurrent of thin-film perovskite solar cells. Energy & Environmental Science 2015, 8, 602-609.
(30) Rau, U. Reciprocity relation between photovoltaic quantum efficiency and electroluminescent emission of solar cells. Physical Review B 2007, 76, 085303.
(31) Jain, A.; Kapoor, A. Exact analytical solutions of the parameters of real solar cells using Lambert W-function. Solar Energy Materials and Solar Cells 2004, 81, 269-277.
(32) http://www.nrel.gov/ncpv/images/efficiency_chart.jpg NREL efficiency chart. (accessed 25/05/2016).
(33) Jiang, Y.; Almansouri, I.; Huang, S.; Young, T.; Li, Y.; Peng, Y.; Hou, Q.; Spiccia, L.; Bach, U.; Cheng, Y.-B.; et al. Optical analysis of perovskite/silicon tandem solar cells. Journal of Materials Chemistry C 2016, 4, 5679-5689.
(34) Aharon, S.; Cohen, B. E.; Etgar, L. Hybrid lead halide iodide and lead halide bromide in efficient hole conductor free perovskite solar cell. The Journal of Physical Chemistry C 2014, 118, 17160-17165.
(35) McMeekin, D. P.; Sadoughi, G.; Rehman, W.; Eperon, G. E.; Saliba, M.; Hörantner, M. T.; Haghighirad, A.; Sakai, N.; Korte, L.; Rech, B.; et al. A mixed-cation lead mixed-halide perovskite absorber for tandem solar cells. Science 2016, 351, 151-155.
(36) Löper P.; Stuckelberger M.; Niesen B.; Werner J.; Filipic M.; Moon S.; Yum J.; Topic M.; Wolf S. De; Ballif C.; et al. Complex refractive index spectra of CH3NH3PbI3 perovskite thin films
determined by spectroscopic ellipsometry and spectrophotometry, Journal of Physical Chemistry Letters 2015, 6, pp. 66–71.
(37) Filipic M.; Löper P.; Niesen B.; Wolf S. De; Krc J.; Ballif C. and Topic M., CH3NH3PbI3 perovskite / silicon tandem solar cells: characterization based optical simulations, Optics Express 2015, 23(7), pp. A263–A278.
(38) Wojciechowski K.; Ramirez I.; Gorisse T.; Dautel O.; Dasari R.; Sakai N.; Hardigree J. M.; Song S.; Marder S.; Riede M.; et al., Cross-Linkable fullerene derivatives for solution-processed n–i–p perovskite solar cells, ACS Energy Letters 2016, 1 (4), 648-653
(39) Shockley W.; Queisser H. J., Detailed balance limit of efficiency of p-n junction solar cells J. Appl. Phys. 32, 510 (1961)
(40) Hadipour A.; Boer B. de;. Blom P. W. M. Device operation of organic tandem solar cells, Org. Electron. physics, Mater. Appl. 2008, 9, 617–624.
(41) Hörantner M. T.; Snaith H., Predicting and optimising the energy yield of perovskite-on-silicon tandem solar cells under real world conditions, Energy Environ. Sci. 2017, 1754-5692.
(42) Green M.A.; Ho-Baillie A.W.Y., 'Perovskite solar cells: the birth of a new era in photovoltaics', ACS Energy Lett., 2017, 2, pp 822–830
(43) Pettersson L. A. A.; Roman L. S.; and Ingana O., Modeling photocurrent action spectra of photovoltaic devices based on organic thin films, J. Appl, Phys, 1999, 86, 487.
(44) Hanusch F., Wiesenmayer E., Mankel E., Binek A., Angloher P., Fraunhofer C., Giesbrecht N., Feckl J., Jaegremann W., Johrendt D., et al., Efficient planer heterojunction perovsktie solar cells based on formamidinium lead bromide. J. Phys. Chem. Lett., 2014, 5 (16), pp 2791–2795
(45) Hoke E., Slotcavage D., Dohner E., Bowring A., Karunadasa H., McGehee M., Reversible photo-induced trap formation in mixed-halide hybrid perovskites for photovoltaics, Chem. Sci., 2015, 6, 613-617
(46) Rehman W. , McMeekin D. , Patel J. , Milot R. , Johnston M., Snaith H. and Herz L., Photovoltaic mixed-cation lead mixed-halide perovskite:links between crystallinity, photo-stability and electronic properties. Energy Environ. Sci., 2017, 10, 361-369
(47) Forgács D., Gil-Escrig L., Pérez-Del-Rey D., Momblona C., Werner J., Niesen B., Ballif C., Sessolo M., Bolink H., Efficient monolithic perovskite/perovskite tandem solar cells, Advanced Energy Material, 2017, 7(8), 1602121