Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ......
Transcript of Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ......
![Page 1: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/1.jpg)
DNV GL © 2016
Ungraded
SAFER, SMARTER, GREENERDNV GL © 2016
Ungraded
OIL & GAS
Environmentally Assisted Fatigue and Fracture of Offshore Pipelines – Current Status and Future Needs
1
DNV GL Technology Week
November 2nd, 2016
Colum Holtam, Ramgo Thodla
![Page 2: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/2.jpg)
DNV GL © 2016
Ungraded
Agenda
Introduction to pipeline engineering critical assessment (ECA)
Corrosion fatigue and fracture testing
– Influence of key variables
Technical challenges
– Representative material properties
2
![Page 3: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/3.jpg)
DNV GL © 2016
Ungraded
Introduction to Pipeline ECA
3
![Page 4: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/4.jpg)
DNV GL © 2016
Ungraded
BS 7910
4
![Page 5: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/5.jpg)
DNV GL © 2016
Ungraded
DNV-OS-F101 (Appendix A)
Requirements for ECA
– Maximum longitudinal strain, εl,nom, larger than 0.4%
– Aggressive (e.g. sour) environments …
– Standard ECA
– Overmatching welds
5
![Page 6: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/6.jpg)
DNV GL © 2016
Ungraded
DNVGL-RP-F108 – New RP for ECA (Coming Soon)
DNV-OS-F101 >> DNVGL-ST-F101
– New fatigue and fracture limit state in Section 5
DNV-RP-F108 >> DNVGL-RP-F108
– RP for ECA
– Appendix A from OS-F101
– SENT testing guidance removed
– BS 8571
– Easier to update
6
![Page 7: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/7.jpg)
DNV GL © 2016
Ungraded
Principals of Fracture Mechanics
Equilibrium evaluation between:
– The Crack Driving Force (CDF) (load)
– The fracture toughness (capacity)
7
TestingAnalyses/Calculations
Who is the strongest?
Crack Driving Force (CDF) Fracture toughness (materials resistance)
CDF < CTODmat : Crack is stableCDF ≥ CTODmat : Crack is unstable (fracture or crack growth)
![Page 8: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/8.jpg)
DNV GL © 2016
Ungraded
Fracture Mechanics “Engineering Critical Assessment” (ECA)
Failure Assessment Diagram used to model failure by fracture / plastic collapse
Distinguishing between what is safe and unsafe
![Page 9: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/9.jpg)
DNV GL © 2016
Ungraded
Pipeline ECA
9
Crack growth modelled to calculate critical initial flaw sizes
![Page 10: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/10.jpg)
DNV GL © 2016
Ungraded
Static and Cyclic Stresses
Installation
Extreme loads
Fatigue
– Thermal cycles
– VIV (free spans)
– VIM
10
1.0E+00
1.0E+01
1.0E+02
1.0E+03
1.0E+04
1.0E+05
1.0E+06
1.0E+07
1.0E+08
0-2 4-6 8-10
12-14
16-18
20-22
24-26
28-30
32-34
36-38
40-42
44-46
48-50
52-54
56-58
60-62
64-66
68-70
72-74
76-78
80-82
84-86
Stress Range (MPa)
Num
ber o
f Cyc
les
TDP Top Weld
![Page 11: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/11.jpg)
DNV GL © 2016
Ungraded
Fracture Toughness
Fracture toughness parameter
CTOD
K
J
Specimen type
Compact Tension (CT)
Single Edge Notched Bend (SENB)
Single Edge Notched Tension (SENT)
11
![Page 12: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/12.jpg)
DNV GL © 2016
Ungraded
12
Fatigue Crack Growth Analysis
• Fracture mechanics used to model fatigue crack growth through life
• Fatigue crack growth rate law (C, m)
∆
∆ ∆
1∆
![Page 13: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/13.jpg)
DNV GL © 2016
Ungraded
Fracture Mechanics Software
FlawSizer (DNV GL internal software)– BS 7910– DNV-OS-F101 App. A– DNV-RP-F108
CRACKWISE (TWI commercial software)– BS 7910
Signal (Quest Integrity commercial software)– API/ASME 579– BS 7910
FEA– ABAQUS
Spreadsheets/MathCAD
![Page 14: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/14.jpg)
DNV GL © 2016
Ungraded
Corrosion Fatigue and Fracture Testing
14
![Page 15: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/15.jpg)
DNV GL © 2016
Ungraded
Corrosion Fatigue and Fracture
Presence of H2S (sour service) and/or CO2 (sweet service) in production fluids can reduce fracture toughness and increase fatigue crack growth rate
No standard/published guidance for assessment of environmentally assisted fatigue and fracture of offshore pipelines
Several JIPs to develop test methods and data
Published data typically not available
Project specific testing often required
15
![Page 16: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/16.jpg)
DNV GL © 2016
Ungraded
Corrosion Fatigue and Fracture Testing
16
![Page 17: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/17.jpg)
DNV GL © 2016
Ungraded
Environmental Severity - ISO 15156-2 Domain Diagram
17
![Page 18: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/18.jpg)
DNV GL © 2016
Ungraded
Fatigue and Fracture Toughness in Aggressive Environments –Critical Factors
18
Environmental Variables
– pH
– pH2S / pCO2
– Temperature
– Inhibitors
Sample Geometry
– CT vs. SENB vs. SENT
– Fully exposed vs Coated
– Pre-soak duration
– Shallow notch vs Deep notch
Material issues
– Microstructure (PP/HAZ/WCL)
– Strength
– Strain level (e.g. reeling installation)
Loading Variables
– ∆K (FCGR)
– Frequency (FCGR)
– K-rate (FT)
Loading Modes
– FCGR
– Constant/Increasing/Decreasing ∆K
– Constant R/Constant Kmax
– FT
– Rising Displacement
– Constant Load
– Step Load
– Constant Displacement
– Constant K
![Page 19: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/19.jpg)
DNV GL © 2016
Ungraded
What is the impact of the different test methods and variables on the sour/sweet service fatigue crack growth and fracture toughness behavior of line pipe steel?
19
![Page 20: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/20.jpg)
DNV GL © 2016
Ungraded
Fatigue Crack Growth Rate – Effect of Frequency (Sour Service)
FCGR increases with decreasing frequency and reaches a plateau
Data in triplicate is very reproducible
FCGR of WCL samples is ~11x above air
FCGR of PP and HAZ is in the range of about 20 to 30x.
20
1E-3 0.01 0.1 1
1
10
As Fabricated5wt% NaClpH = 5p
H2S = 0.46psia
RTKmax = 1150Nmm-3/2
K = 1000Nmm-3/2
R = 0.13
Parent Pipe HAZ WCL
KD
F BS7
910
f (Hz)
OMAE2015 - 42412
![Page 21: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/21.jpg)
DNV GL © 2016
Ungraded
Fatigue Crack Growth Rate – Effect of Environment (Sweet Service)
21
OMAE2013-10216
![Page 22: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/22.jpg)
DNV GL © 2016
Ungraded
Fatigue Crack Growth Rate – Effect of Inhibitor (Sour Acidizing Service)
Tests performed in-situ in spent acid with and without inhibitor with 0.21psia H2S
FCGR increases with decreasing frequency
With inhibitor
– Maximum FCGR ~100x air
– At 0.1Hz FCGR ~15x air
Without inhibitor
– Maximum FCGR ~60x air
– At 0.1Hz FCGR ~25x air
Difference in behavior may be associated with higher corrosion rate in spent acid without inhibitor causing crack tip blunting and environmentally-induced closure due to the build-up of voluminous corrosion products inside the crack
22
OMAE2016-54388
![Page 23: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/23.jpg)
DNV GL © 2016
Ungraded
Fracture Toughness – Effect of Loading Rate (Sour Service)
23
Corrosion2012-1577
![Page 24: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/24.jpg)
DNV GL © 2016
Ungraded
Fracture Toughness – Effect of Loading Rate (Sour Service)
24
ISOPE2015-598
![Page 25: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/25.jpg)
DNV GL © 2016
Ungraded
Diffusion of Hydrogen - Hydrogen Profile in Uncoated and Coated Samples
25
Back side of specim
en
Crack Propagation
Back side of specim
en
Crack Propagation
![Page 26: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/26.jpg)
DNV GL © 2016
Ungraded
Fracture Toughness – Effect of Coating (Sour Service)
26
ISOPE2015-598
![Page 27: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/27.jpg)
DNV GL © 2016
Ungraded
Fracture Toughness – Effect of Reeling (Sour Service)
27
0
50
100
150
2005wt% NaClpH = 5pH2S = 0.46psia
K-rate: 0.05Nmm-3/2/s
Intr
ados
As
Fab
Parent Pipe HAZ WCL
J 0.2m
m (N
/mm
)
Extr
ados
OMAE2015 - 42413
![Page 28: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/28.jpg)
DNV GL © 2016
Ungraded
Technical Challenges
28
![Page 29: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/29.jpg)
DNV GL © 2016
Ungraded
Technical Challenges
Representative material properties in aggressive environments
– Fracture toughness
– Fatigue crack growth rate
Assessment clad/lined pipes
Installation method
Undermatching welds
29
![Page 30: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/30.jpg)
DNV GL © 2016
Ungraded
Loading Scenarios – Lateral Buckling
30
Time
Load
Ambient
Environmentally Assisted Crack Propagation
Fatig
ue C
ontr
olle
d
Static Crack Growth Controlled
Primary loading scenarios
– Fatigue loading from pressure transients
– Fatigue loading from thermal transients
– Static loading associated with long steady operations
Development of a single specimen methodology to capture all of the critical design parameters
![Page 31: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/31.jpg)
DNV GL © 2016
Ungraded
FCGR – Based on Average values of CGR
FCGR increases linearly with decreasing frequency.
“Plateau FCGR” is about 10x higher than the in-air values.
Addition of hold times leads to a transition to a constant CGR
31
1E-5 1E-4 1E-3 0.01 0.11E-5
1E-4
1E-3
H85
400/
R50
0
H90
00/R
500
H36
00/R
500
H0/
R50
5wt% NaClpH = 3.5pH2S = 0.21psia1000ppm Inh
Kmax = 1384Nmm-3/2
K = 519Nmm-3/2, R = 0.6
da/d
N (m
m/c
ycle
)
Frequency (Hz)
H0/
R50
0
In-Air Value - 3.910-5mm/s
thold
![Page 32: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/32.jpg)
DNV GL © 2016
Ungraded
Static Crack Growth Analysis• Fracture mechanics used to model static crack growth through life
• Static crack growth rate law (C1, n(scc))
32
1
![Page 33: Environmentally Assisted Fatigue and Fracture of … · Corrosion fatigue and fracture testing ... 60-62 64-66 68-70 ... No standard/published guidance for assessment of environmentally](https://reader031.fdocuments.in/reader031/viewer/2022021801/5b38ada87f8b9abd438d8745/html5/thumbnails/33.jpg)
DNV GL © 2016
Ungraded
SAFER, SMARTER, GREENER
www.dnvgl.com
Thank you
Questions?
33
Dr. Colum [email protected]+1 281-396-1000
Dr. Ramgo [email protected]+1 614-761-1214