Dental Stones

1

Elite® Dental StonesType 3 and 4

2

Dental Stones

Elite Base

®

Elite StoneElite StoneElite ModelElite Model

Elite OrthoElite Arti

®

®

®

®

®

EliteElite ModelModel FastFast

®

Elite RockElite Rock

3

Die stone for C&B and implant

work

Type 4 die stone

Elite Rock®

4

Pouring

Resistance to splintering

Long working time

Resistance to abrasion Compressive strength

Very low expansion

Type 4 die stone

Elite Rock®

5

Technical Data (ISO 6873)

Water/gypsum ratio XX ml – XX gr

Mixing time (by hand) XX secs

Mixing time (under vacuum) XX secs

Working time XX mins

Setting time Vicat XX mins

Setting expansion after 2 hours XX %

Setting expansion after 48 hours

XX %

Compressive strength after 1 hours XX MPa

Compressive strength after 48 hours XX MPa

Water/gypsum ratio:

Quantity of water to add to the gypsum in order to obtain a proper mixture

for a correct use

Measured in ml / gr

Water/gypsum ratio:

Quantity of water to add to the gypsum in order to obtain a proper mixture

for a correct use

Measured in ml / gr

Mixing time(by hand)

Suggested time for mixing by hand, measured in secs

A light mixing is suggested in order to avoid as much air as possible in the mixture water/gypsum

Mixing time(by hand)

Suggested time for mixing by hand, measured in secs

A light mixing is suggested in order to avoid as much air as possible in the mixture water/gypsum

Mixing time (under vacuum)

Suggested time by mixing under vacuum, expressed in

secs.

Mechanical mixing makes gypsum more flowable in the first pouring phase vs. mixing by hand with no

vacuum

Gypsum mechanical properties are better if gypsum is mixed with the machine

Mixing time (under vacuum)

Suggested time by mixing under vacuum, expressed in

secs.

Mechanical mixing makes gypsum more flowable in the first pouring phase vs. mixing by hand with no

vacuum

Gypsum mechanical properties are better if gypsum is mixed with the machine

Working time

Time of working, expressed in mins.

This is a typical property of every gypsum family and it depends on the kind of use

Working time

Time of working, expressed in mins.

This is a typical property of every gypsum family and it depends on the kind of use

Setting time (Vicat):A needle of 1mm Ø and 50mm lenght, submitted to 300 gr

weight, enters in the gypsum for no more than 2 mm

• Data measured in mins.It indicates the time of gypsum setting

Setting time (Vicat):A needle of 1mm Ø and 50mm lenght, submitted to 300 gr

weight, enters in the gypsum for no more than 2 mm

• Data measured in mins.It indicates the time of gypsum setting

Type 4 die stone

Elite Rock®

Expansion after 2 hours:

linear expansionmeasured after 2 hours

•Data measured in %

•It is an essential measure for the technical precision of the work and for the dimensional precision of the

gypsum.


linear expansionmeasured after 2 hours


•It is an essential measure for the technical precision of the work and for the dimensional precision of the

gypsum.


linear expansion after 48 hours


•It is a basic measure for the technical precision of the work and for the dimensional

precision of gypsum.


linear expansion after 48 hours


•It is a basic measure for the technical precision of the work and for the dimensional

precision of gypsum.

Compressive strength after 1 hour:

Strenght that breaks under crushing a cylinder of gypsum of definite dimensions

• Data measured in N/mm2

•It is an essential property for the resistance of gypsum and for the possibility to work on the model without

damages or abrasions.

Compressive strength after 1 hour:



•It is an essential property for the resistance of gypsum and for the possibility to work on the model without

damages or abrasions.

Compressive strength at 48 hours:



•It is an essential property for the resistance of gypsum and for the possibility to work on the

model without damages or abrasions.

Compressive strength at 48 hours:



•It is an essential property for the resistance of gypsum and for the possibility to work on the

model without damages or abrasions.

6

Type 4 die stone

Elite Rock®

7

Chrome dental stone

Type 4 dental stone

Elite Stone®

8

Compressive strength

Very low expansion

Resistance to abrasion

Type 4 dental stone

Elite Stone®

9

Type 4 dental stone

Elite Stone®

10

Model dental stone

Thixotropic consistency Good casting

Very low expansion

Good hardness even after 1 hour

Type 3 dental stone

Elite Model®

11

®

Type 3 dental stone

Elite Model

12

Thixotropic

Good Casting

Very high compressive strenght

Model removing time of only 15 minutes

Type III Dental Stone

Elite Model® FASTFAST

Model dental stone

13

Water/Powder ratio 29-30ml/100gr

Mixing time (manual) 60’’

Mixing time (under vacuum, 240 rpm)

30’’

Working time 4’

Setting time (Vicat) 8’

Time of model removing 15’

Expansion (2 h) 0,10%

Expansion (48 h) 0,10%

Compressive strenght (1 h) 36 (367 kg/cm2)

Compressive strenght (48 h) 65 (663 kg/cm2)

Technical Data* (ISO 6873)

*Data refer to 30 ml water / 100 g powder ratio


Elite Model® FASTFAST

14

Orthodontic dental stone

Thixotropic consistency

Hardness

Bright surface

Elite Ortho®


15


Elite Ortho®

16

Articulating dental stone

Very high thixotropicity

Fast setting time

Very low expansion

Elite Arti®


17


Elite Arti®

18

Dental stone for bases

Very fluid enabling easy-pouring without vibration

Very low expansion

Long working time for multiple pouring

Elite Base®

Type IV Dental Stone

19

Type IV Dental Stone

Elite Base®

20

ELITE DENTAL STONES

21

Thank you for your attention

Dental Stones