PRODUCT DATA SHEET MD100 – 15/11/2011 Page 1 of 1 Compound GPlast ™ T128 NORSOK M-710 Rev 2 (UM) POLYMER TYPE: Perfluoroelastomer FFKM90 (+/-5°) Physical Properties Property Test Units Typical Values Method COLOUR Black HARDNESS ISO 48 °IRHD 89 TENSILE STRENGTH ISO 37 MPa 18.9 MODULUS @ 100% ISO 37 MPa n/a ELONGATGION @ BREAK ISO 37 % 93 TEAR STRENGTH ISO 34 N/mm 21.4 SPECIFIC GRAVITY ISO 2781 g/cm3 1.96 COMPRESSION SET VALUE IN AIR 25% STRAIN – 24HRS @ 204°C ISO 815 % 26.5 Description This compound is designed to give the best performance for rapid gas decompression and meets the requirements of NORSOK standard M-710 Rev 2. This Black material provides excellent temperature resistance up to +230°C (+450°F) and has similar chemical resistance to that of PTFE but with elastomeric properties comparable to standard fluorocarbon rubbers. Developed for optimum resistance through thermal cycling. Along with all our GPlast™ range, this grade is suitable for use in a wide range of applications where other polymers are not suitable. Do not use any GPlast™ grade with molten alkali metals. Service Temperatures +230°C (+450°F) to -15°C (+5°F). Chemical Resistance 1. Suitable, little or no effect. 2. Minor to moderate effect, not maximum resistance. 3. Moderate to severe effect – may be useful in some limited applications. 4. Unsuitable and not recommended – severe effect. Chemical Group Rating Chemical Group Rating Aromatics / Aliphatic Oils 1 Ethylene Oxide 1 Acids 1 Esters 1 Alkalis 1 Ketones 1 Alcohols 1 Propylene Oxide 1 Aldehydes 1 Steam/Hot Water 1 Amines 1 Strong Oxidisers 1 Ethers 1 More detailed information available on request. Norsok NORSOK M710 (Rev. 2, October 2001) in respect of rapid gas decompression resistance in 10% Carbon Dioxide at 150 bar and 100°C. Compound Summary Rating (Average of three) Result T128 1000 Pass Since development and improvement of compounds is a continuing process, Gapi reserves the right to modify their composition and characteristics. Uncontrolled Copy Seal & Design Corporate Headquarters Ph: (716)-759-3344 [email protected] www.SealAndDesign.com
Transcript of Compound GPlast T128 NORSOK M-710 Rev ... - Seal & Design, Inc
PRODUCT DATA SHEET MD100 – 15/11/2011
Page 1 of 1
Compound GPlast™ T128 NORSOK M-710 Rev 2 (UM)
POLYMER TYPE: Perfluoroelastomer FFKM90 (+/-5°)
Physical Properties
Property Test Units Typical Values Method
COLOUR Black HARDNESS ISO 48 °IRHD 89 TENSILE STRENGTH ISO 37 MPa 18.9 MODULUS @ 100% ISO 37 MPa n/a ELONGATGION @ BREAK ISO 37 % 93 TEAR STRENGTH ISO 34 N/mm 21.4 SPECIFIC GRAVITY ISO 2781 g/cm3 1.96 COMPRESSION SET VALUE IN AIR 25% STRAIN – 24HRS @ 204°C ISO 815 % 26.5
Description
This compound is designed to give the best performance for rapid gas decompression and meets the requirements of NORSOK standard M-710 Rev 2. This Black material provides excellent temperature resistance up to +230°C (+450°F) and has similar chemical resistance to that of PTFE but with elastomeric properties comparable to standard fluorocarbon rubbers. Developed for optimum resistance through thermal cycling. Along with all our GPlast™ range, this grade is suitable for use in a wide range of applications where other polymers are not suitable. Do not use any GPlast™ grade with molten alkali metals. Service Temperatures +230°C (+450°F) to -15°C (+5°F).
Chemical Resistance 1. Suitable, little or no effect. 2. Minor to moderate effect, not maximum resistance. 3. Moderate to severe effect – may be useful in some limitedapplications. 4. Unsuitable and not recommended – severe effect.
Chemical Group Rating Chemical Group Rating Aromatics / Aliphatic Oils 1 Ethylene Oxide 1
Acids 1 Esters 1 Alkalis 1 Ketones 1 Alcohols 1 Propylene Oxide 1 Aldehydes 1 Steam/Hot Water 1 Amines 1 Strong Oxidisers 1 Ethers 1
More detailed information available on request. Norsok
NORSOK M710 (Rev. 2, October 2001) in respect of rapid gas decompression resistance in 10% Carbon Dioxide at 150 bar and 100°C.
Compound Summary Rating (Average of three)
Result
T128 1000 Pass
Since development and improvement of compounds is a continuing process, Gapi reserves the right to modify their composition and characteristics. Uncontrolled Copy