Casting using MELT IT

15
Sonal kumar | 9 th May, 2014 - 29 June, 2014 Casting using MELT IT

Transcript of Casting using MELT IT

Page 1: Casting using MELT IT

Sonal kumar | 9th May, 2014 - 29 June, 2014

Casting using MELT IT

Page 2: Casting using MELT IT

PAGE 1

INTRODUCTION

MELT IT is the name of coreless induction furnace that has been invented by tree-labs team.

MELT IT is different from conventional coreless furnaces in many aspects. This project involved

the testing of MELT IT for casting purpose and thus producing a proof of concept that MELT IT is

fit for casting. Project in a long run aims at projecting this machine in schools and colleges which

do not have foundry. This machine is so easy to use that it can be used on a small desktop to

melt metals in it and cast. This is from where it also derives it name “Desktop Foundry”. Easy

handling of MELT IT from other furnaces makes it a lot superior than conventional furnaces.

AIM

This project aims at following things:-

1. Conducting experiments on casting and declaring machine fit for it.

2. Study the pro and cons of machine.

3. Documenting all the difficulties and advantages that an inexperienced undergraduate can

face while trying casting with this machine.

4. To recommend those methods for casting which are easiest to start with.

VARIOUS STAGES

There are mainly five stages involved in this project:-

1. Pattern making

2. Mould making

3. Casting

4. Finishing

5. Testing

STAGE 1 – PATTERN MAKING

In casting, a pattern is a replica of the object to be cast, used to prepare the cavity into which

molten material will be poured during the casting process. Patterns used in casting may be

made of wood, metal, plastics or other materials. We will be using wood and plastic patterns.

Page 3: Casting using MELT IT

PAGE 2

1. Wooden pattern with two hooks 2.Plastic pattern with hook

1. Plastic pattern

A plastic pattern can be made using a 3D printer. One can feed in the cad design of pattern to 3D

printer and get a plastic pattern. Casting with the plastic pattern is easier as surface is very

smooth. Alternatively any smooth thing made up of plastic can be used as pattern.

. Cad design of pattern used.

. Made this in solid works.

. It is also beneficial as amount of metal required for

casting can also be estimated in solid works. Metal

used by me was aluminum and I expected metal required

for this pattern to be around 200 g.

2. Wooden pattern

Wooden pattern are relatively difficult to make as well as to cast, compared to plastic ones.

Pattern was made with soft wood used in school/college carpentry. These woods are relatively

easy to cut and finish.

Steps to make wooden pattern:

1. Cut the wood as per requirement.

2. File using a wood filer followed by sanding using sand paper.

Page 4: Casting using MELT IT

PAGE 3

3. Now wood needs to be polished. One can use ready-made polish available in market.

Before polishing one should ensure that surface is clean and smooth. If needed polishing

can be done several times. I did it 8 times to ensure surface is smooth enough.

After every polish let the pattern dry for some time.

Finished, polished,

wooden pattern.

Materials used in finishing.

Sand paper-150 & 400,

asian paints touch wood

polish, brush and thinner.

STAGE 2- MOULD MAKING

Mould is a a hollow container used to give shape to molten or hot liquid material when it cools

and hardens. Once we have pattern ready we can switch to mould making. I have used plaster of

paris (POP) for mould making. Reason for using POP is that it is easily available in market,

cheap and it’s easy to make mould from it. No additional material is required to make mould of

POP.

Mould making turned out to be the toughest part in whole project. Mould making with POP

requires experience and patience. More the no. of attempts one will take to make mould, better

the mould wiil be.

Steps to make mould:-

1. Mixing of POP:- Amount of POP to be mixed in water depends on quality of POP which

varies with company. I kept the POP to water ratio 2:1. But this rule does not apply very

strictly. A slight variation in ratio does not matter. There is a particular way in which POP

should be mixed. Take water in a container. Pour in all POP as per ratio. Catch is, only

after all the POP has been poured into water, start mixing it. This will ensure a

homogenous mixture as all the POP mixes with water at the same time. This will also

give sufficient time to pour mixture in another container. Keep on mixing until all the POP

powder is homogenously mixed with water.

2. Pouring Pop:- POP takes almost 3 minutes to change to semi-solid form. We need to

pour POP before this. Take a small box or something where you want to make the mould.

Page 5: Casting using MELT IT

PAGE 4

Pour in POP from one side thus avoiding trapping of air. Avoid air bubbles as much as

possible.

3. Putting pattern:- Immediately after the POP has been poured, we need to insert the

pattern in POP. Attach hook to pattern. Hooks are threaded metallic curve. Screw like

threading will allow attaching it to pattern. They will prove very handy while taking out

pattern. Now apply oil all over pattern. This will prevent pattern getting attached with

POP. While inserting shake pattern to & fro so that pattern is inside properly. Keep on

inserting until upper surface of pattern & POP are in level. Now spray some powder POP

at the edges of inserted pattern. This will avoid POP surface to break when pattern is

taken out.

4. Taking out pattern:- Now it’s time to take out pattern from POP. This is the trickiest part.

This step can be mastered after several tries. We will takeout pattern when POP is in

semi-solid state. After inserting pattern keep on checking if pattern has tightly attached to

POP. Usually this takes 7-8 min. Once u feel that pattern will get very tightly attached,

start taking it out. Be very slow while doing this. The more intricate pattern will be more

difficult it will get to take it out. So first try with simpler patterns.

5. Dry the mould:- Now let the mould dry in atmospheric air until it loses all it’s moisture.

Weight of mould will surprisingly go down once all moisture is lost. Now mould is ready

for casting.

FOLLOWING PHOTOS SHOW SOME MOST COMMON PROBLEMS ENCOUNTERED

WHILE MAKING MOULD

Mould 1- Failed

REASONS - 1. Sudden removal of pattern. 2. Insufficient time for mold to reach semi solid state

Page 6: Casting using MELT IT

PAGE 5

Mould 2- Failed

REASONS- 1. Inexperience to deal with intricate parts.

2.Surface crack occurred because one side of the pattern was pulled up

neglecting the other side.

Mold 3- Half failed

1. This time got intricate part right.

2. But one of the edge finish was not good

Page 7: Casting using MELT IT

PAGE 6

Mold 4- Successful

STAGE 3- CASTING

This is the step where we get to test the machine. Before casting it should be ensured that POP

has lost all it’s moisture. Presence of moisture may result in explosion of aluminum while

pouring. Therefore safety is must. Apron, helmet, long gloves and shoes are must while

casting.

Steps in casting:-

1. First we need to provide some insulating material just below the mould. Here we have

used a brick over which a tray has been put with sand on it. Thus in case any molten

metal falls, it will fall on sand.

2. Now one should check that mould kept is properly in level using a spirit level. A slant

mould may result in uneven casting.

3. Aluminum is kept in the crucible just above the mould. Put a high heat thermometer in the

crucible. Look fig. below for arrangement. Switch on the machine. Set the frequency and

let the temperature rise. We used aluminum. It melts around 660 degree Celsius. Let the

temperature rise above melting point. We let it go till 720 degree Celsius. This ensures

that metal will flow properly and will not solidify quickly once it is in mould.

Page 8: Casting using MELT IT

PAGE 7

4. One should always allow metal to flow from one side of mould to other. So metal drop

should be made at one side. And slowly molten metal will flow in other parts by it’s own.

This prevents trapping of air bubble. It should also be ensured that molten metal is

directly dropped over mould part which has got sufficient area. This is reason I poured

the metal at the center.

5. One thing should be ensured that sufficient metal has been melt to do casting. Though

we do not have proper control over metal flow, we can use plunger to control this to some

extent. Anyways extra metal will fall over cavity area which will be taken care of in

finishing.

6. Let the metal cool for 30min. . Take out metal from POP. Mostly POP mould will break in

the process. Put metal in water to cool down.

Melting machine setup.

1. Thermometer rod inserted in crucible.

2. Rod connected to plunger. On lifting this up a small hole is opened in the crucible and

metal is poured.

3. Crucible made up of graphite. Between crucible and copper rods refractory material

(white part) is provided.

4. Copper rods carrying current.

5. Mould just below the plunger.

6. Sand in tray to avoid metal to fall below in case of explosion.

7. Thermometer.

8. Computer controlling frequency.

Page 9: Casting using MELT IT

PAGE 8

Molten metal in crucible with plunger

Flowing metal (golden colored line)

Page 10: Casting using MELT IT

PAGE 9

Extra metal over mould.

One of the drawbacks of open casting.

Will be removed while finishing.

Casted metal

STAGE 4- FINISHING

After the metal has been casted it needs to be given proper finishing. Casting will be followed by

frettling (sanding), straightening, machining. In general, the castings must first be removed from

the tree assembly they were cast with. And then finishing steps are started.

Steps in finishing:-

1. Start with removing the extra metal. One can use milling machine or just cut off the extra

parts using a saw. Aluminum is not hard to cut.

2. Now if the surface is flat filing is done using a metal filer. Alternatively if surface is not flat,

as in my case, one can give a finish by milling machine using flat drill bits.

3. Now surface should be sanded using sand paper.

Page 11: Casting using MELT IT

PAGE 10

Milling machine in action using a flat drill

Job after finish. Encountered a crack at edge, probably because of low strength at edges

Page 12: Casting using MELT IT

PAGE 11

STAGE 5- TESTING

Hardness testing and dye testing are two important test to be conducted after finishing. While

hardness test can be done before or after finishing, dye test should be done after finishing.

Hardness testing.

Hardness test are done on sophisticated hardness testing machine. These machines have

indenter which makes a micro level dent on surface of material and predicts the hardness.

Machine used was “HMV-G, Micro –Vickers Hardness Tester”.

Steps in hardness testing:-

1. Indenter needs flat surface to make dent. So if we are testing before finishing, as in my

case, we will need to file the surface here and there thus creating some local flat surface.

Hardness is an intrinsic property so it doesn’t matter whether it is done before or after

finishing step.

2. Put the job on machine platform. This machine is controlled by computer. Machine has a

microscope and an indenter, both computer controlled, which helps in making dent. First

using micro scope find a flat surface on job. Now we set the amount of load and holding

time for indent. Make indenter to approach job & make dent. Once dent is made all the

data are received on computer (see table below).

3. Received data is analyzed, average hardness is calculated. One thing should be kept in

mind that indentation on edges will give relatively low hardness. Those data can be

ignored. And finally average hardness is compared to available data of used material.

4. In my case hardness came out to be 110.0356 HV (Vickers Pyramid number), which is

comparable to data already available for aluminum.

5. Following link contains hardness of different aluminums alloys for comparison.

http://asm.matweb.com/search/SpecificMaterial.asp?bassnum=MA2024T4

http://asm.matweb.com/search/SpecificMaterial.asp?bassnum=MA6061t6

Hardness testing machine

Page 13: Casting using MELT IT

PAGE 12

DATA FROM HARDNESS TESTING

No. Test Load Duration time Lens Hardness(HV) Comment

1 HV0.05 (490.3mN) 20 X40 0 Indenter could not penetrate surface

2 HV0.05 (490.3mN) 30 X40 157.121 Increased holding time to 30sec

3 HV0.05 (490.3mN) 30 X40 130.879

4 HV0.05 (490.3mN) 30 X40 72.3546 Indent was not proper,so this value can be ignored

5 HV0.05 (490.3mN) 30 X40 109.987

6 HV0.05 (490.3mN) 30 X40 103.006

7 HV0.1 (980.7mN) 20 X40 96.5072 Load was doubled & time was reduced to 20 sec

8 HV0.1 (980.7mN) 20 X40 95.6848

9 HV0.1 (980.7mN) 20 X40 69.6596 Indent was not proper,so this value can be ignored

10 HV0.1 (980.7mN) 20 X40 100.6

11 HV0.1 (980.7mN) 20 X40 86.5

12 HV0.1 (980.7mN) 20 X40 75.8 Indent was not proper,so this value can be ignored

Max. 157.121

Min. 72.3546

Mean: 99.8272 Considering all values

Mean : 110.0356 Considering only 8 values

Indent on job (image- X40)

Page 14: Casting using MELT IT

PAGE 13

Dye testing

Dye testing is for smooth surfaces i.e when finishing step is over. This step is useful in identifying

surface cracks, thus indicating about quality of cast. This test was not conducted because of non-

availability of testing chemicals.

Steps in dye testing:-

1. Pre-cleaning: The test surface is cleaned to remove any dirt, paint, oil, grease or any

loose scale that could either keep penetrant out of a defect, or cause irrelevant or false

indications. Surface can be cleaned with acetone.

2. Applying Penetrant: Now apply penetrant in ample amount all over the surface. Now let

it dry for 20- 30 min.

3. Removal of excess of penetrant: Water is used to remove excessive penetrant. Water

pressure should not be so high that it removes dye from cracks. Water is to be applied

gently. Now remove water with a dry cloth.

4. Apply Developer: Now a white developer is applied all over the surface. Developer

draws out the dye from the cracks. This is called bleed out of surface. Thus with naked

eye one can identify the orientation of cracks or any other defects.

PRO AND CONS OF MELT IT

Pro

1. Melt is really easy to handle and setup. It uses a two phase current supply. This makes it

perfect for use at any place.

2. MELT IT is small and can be moved from one place to another very easily.

3. It has additional options like choosing frequency. Thus having a better control over the

amount of heat supplied.

4. To pour metal one need not take out crucible. Metal can be poured while crucible is still

attached to copper rods. Thus making it very safe to handle.

5. Slag is a common problem encountered in casting. Slag gets accumulated at the top of

molten metal. But while using “MELT IT” we pour metal from below of crucible by opening

plunger. So slag problem is very efficiently handled here. Whereas this use to be a great

problem in conventional furnace as metal is poured from top of crucible.

Cons

1. This machine does not have a temperature based heat supply controller. In conventional

box furnaces one can set the temperature and heat supply stops when that temperature

is reached. But here we have to put an external thermometer and switch off the machine

when required temp. is reached. Thus one needs to continuously monitor the

thermometer.

Page 15: Casting using MELT IT

PAGE 14

2. There is no metal flow control. While casting we have to pour in extra metal even when

undesired. Introduction of a mechanical system which could control the molten metal flow

will make this machine great. Plunger does not provide proper control over metal flow.

CONCLUSION

Project covers all the process right from pattern making to testing. At every stage there is

surely some alternative. These alternatives may produce better result. But all those process

has been taken up which could be done easily, for which proper materials were available.

For example closed casting has not been tried. Reason for this is that closed casting with

POP is difficult task but it is not the case with sand mould. Also one can try close casting only

when open casting has been mastered. So overall

1. This project produces a guideline to inexperienced people in casting. With this

document as a guideline one will be able to do casting by his own without any help

2. Project also declares “MELT IT” fit for use in colleges. Surely there are certain

aspects that has not been tested. For example the intricacy of casting that can be

achieved. But even then this machine is a lot superior to conventional furnaces.

3. Methods practiced in this project is so friendly that one can do most of them at their

home. Thus “MELT IT” can also be used by commoners at their home.

4. Throughout this project a lot of challenges were faced, some easy and some really

tough. Most of them have been solved. This project also emphasizes on how to deal

with these challenges. Thus making casting easier and safe.

ACKNOWLEDGEMENT

I have taken efforts in this project. However, it would not have been possible without the kind

support and help of many individuals and organizations. I would like to extend my sincere thanks

to all of them.

I would specially like to thanks Dipankar sir as he gave me chance to work on this project. I would

also like to express my special gratitude to Deepak, Himanshu, Abhijit and treelabs team for their

guidance and support.

BIBILIOGRAPHY

Wikipedia and Youtube Online resources.

Casting Lab Manual, IIt Bombay

‘Metal Casting, Computer-Aided Design And Analysis’. B.Ravi, IIT Bombay.