EN ISO 3580-A: E MoV B 4 2 H5 AWS A5.5: E9018-G AWS A5.5M: E6218-G
BHLER FOX DMV 83 Kb SMAW basic electrode, low-alloyed,
high temperature Description Basic core wire alloyed stick electrode with special suitability for 14MoV6-3 (1/2 Cr 1 Mo) steels. Approved in long-term condition up to +580C service temperature. Crack resistant and ductile deposit, low hydrogen content. Good weldability in all positions except vertical down. Metal recovery approx. 115%. Typical Composition of All-weld Metal
C Si Mn Cr Mo V wt-% 0.065 0.35 1.2 0.4 1 0.5
Mechanical Properties of All-weld Metal a v yield strength Re N/mm2 (MPa): tensile strength Rm N/mm2 (MPa): elongation A (L0=5d0) %: impact work ISO-V KV J +20C:
510 (t470) 660 (t610) 22 (t20) 200 (t110)
410 (t380) 580 (t540) 26 (t24) 150 (t110)
a annealed, 720C/2h/furnace down to 300C/air v quenched/tempered 940C/0.5 h/oil + 730C/0.5 h/furnace down to 300C/air
Operating Data
re-drying if necessary: 300-350C, min. 2 h electrode identification: FOX DMV 83 Kb 9018-G E MoV B
mm 2.5 3.2 4.0
L mm 250 350 350
amps A 70-100
110-140 140-180
Preheating and interpass temperatures 200-300C. Post weld heat treatment at 700-720C for at least 2 hours followed by cooling in furnace down to 300C and still air.
Base Materials similar alloyed high temperature steels and cast steels
1.7715 14MoV6-3, 1.7733 24CrMoV5-5, 1.7709 21CrMoV5-7, 1.8070 21CrMoV5-11, 1.7706 G17CrMoV5-10
ASTM A389 Gr. C23 u. C24, A405 Gr. P24, UNS J21610
Approvals and Certificates TV-D (1094.), TV-A (119), SEPROZ, CE
Similar Alloy Filler Metals GTAW rod: DMV 83-IG GMAW solid wire: DMV 83-IG