Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by...
-
Upload
catherine-benson -
Category
Documents
-
view
219 -
download
3
Transcript of Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by...
![Page 1: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/1.jpg)
1
Application of Galvanic Exchange Reaction for Preparation of Pt coated
Fe Nanoparticles supported by Single-Walled Carbon Nanotubes:
Fuel Selective Reduction of Oxygen over Methanol Oxidation
Kenichi Shimizu, I. Francis Cheng, Chien, M. Wai
Dept. of Chemistry at University of Idaho
208-885-6837
November 14, 2008
![Page 2: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/2.jpg)
2
Moscow, Idaho
![Page 3: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/3.jpg)
3
Area Around
www.ubcbotanicalgarden.org/potd/2007/
http://imnh.isu.edu/digitalatlas/hydr/concepts/surfhyd/main/imgs/hellscan.jpg
![Page 4: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/4.jpg)
4
Developing catalyst for fuel cells
MEA
MEA: Membrane Electrode Assembly
![Page 5: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/5.jpg)
5
Advantages of Fuel Cells:
• Better sustainability.• Larger power output.• Quick recharge.
pr.fujitsu.com/en/news
www.physorg.com/news6542.html
O’Hayre, R. et al. Fuel Cell Fundamentals. John Wiley & Sons. N.Y. 2006.
![Page 6: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/6.jpg)
6
Limitations of Fuel Cells
• Low power density.– Kinetic limitations.
• High cost.– Pt catalyst.
O’Hayre, R. et al. Fuel Cell Fundamentals. John Wiley & Sons. N.Y. 2006.
![Page 7: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/7.jpg)
7
Deposition of Pt nanoparticles on carbon nanotubes
Water-in- supercritical CO2 microemulsion
Direct supercritical CO2 deposition
Shimizu, K. et al. Energy & Fuels 2008, 22, 2543.
Yen, C.H.; Shimizu, K. et al. Energy & Fuel 2007, 21, 2268.
![Page 8: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/8.jpg)
8
Pt deposited on carbon nanotubes
• Increasing cost of synthesis.• Large amount of chemical wastes.• Little to No control in particle size.
![Page 9: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/9.jpg)
9
Nano is not small enough
• In total, up to 75 % of Pt will be wasted by using nanoparticles.
• In addition, the surface availability can be affected by surfactant resides.
Carbon nanotube 25 to 50 % of the surface is already in contact with carbon (nanotube support).
More than 50 % will in the core partand will not be utilized for catalysis.
Let’s assume there is a Pt nanoparticle with 5 nm diameter
![Page 10: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/10.jpg)
10
As produced single-walled carbon nanotubes
Replace Pt core with Fe
•Fe (also Co and Ni) are often used as catalysts to grow carbon nanotubes (HiPco).
•No purification needed.
![Page 11: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/11.jpg)
11
Galvanic Exchange
• Fe2+ + 2e- Fe0 E0 = -0.44 V• Pt2+ + 2e- Pt0 E0 = 1.19 V• Pt2+ + Fe0 Fe2+ + Pt0 E0 = 1.63 V
Carbon nanotube
Pt2+Fe2+
Fe0 Fe0 Fe0
Much better utilization of Pt than nanoparticles!!
![Page 12: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/12.jpg)
12
Only in an aqueous solution
• Pt2+ is quickly reduced by organic solvents
![Page 13: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/13.jpg)
13
Approach
Vigorous shakingby hand
for 30 seconds
Ultrasonic agitation
for 30min
![Page 14: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/14.jpg)
14
Transmission Electron Microscopy
As-received SWNT (Fe/SWNT) Pt-Fe/SWNT
Fe0
5 nm
![Page 15: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/15.jpg)
15
Selected Area AnalysisEnergy Dispersive X-ray Diffraction Spectroscopy
![Page 16: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/16.jpg)
16
Quantitative Analysis
wt.% Pt(ICP)
wt.% Fe(AAS)
As-received SWNT -- 30.4 (± 0.9)
Pt-Fe/SWNT 5.4 (± 0.1) 25.6 (± 1.4)
Pt/CB E-TEKa (20) 0
ICP: Inductive Coupled Plasma-Atomic Emission Spectroscopy.AAS: Atomic Absorption Spectroscopy.a Commercial catalyst from ETEK. 20 wt% is a vender provided value.Catalysts were dissolved in a slightly heated 50/50 HNO3/H2SO4.
![Page 17: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/17.jpg)
17
Electrochemical Characterization of Pt-Fe/SWNT
Electroactive surface area
Activity towards: Reduction of Oxygen
Oxidation of Methanol
![Page 18: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/18.jpg)
18
Half Cell Analysis
• Quick & Cheap.• Focus on one reaction
a time.• Limited amount of
catalyst (~ 5 mg per synthesis).
• Based on the result, we apply to a full size fuel cell.
Catalyst/water/methanol/Nafion®
Auxiliary Electrode
1 M H2SO4
![Page 19: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/19.jpg)
19
Use of Cyclic Voltammetry to Identify Formation of Pt0
Cao, D. et al. J. Phys. Chem. B 2007, 109, 1162.Biegler, T. J. Electroanal. Chem. 1971, 29, 269.
1 M H2SO4
N2 purged50 mV/s
![Page 20: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/20.jpg)
20
• Area of Pt that can potentially used for electrocatalysis.
•
*Shimizu, K. et al. Energy & Fuels 2008, 22, 2543Biegler, T.; et al. J. Electroanal. Chem. 1971, 29, 269-277
Electroactive Surface Area
24 /1010.2 cmC
AS
Wt % Pt Area (cm2/mg-Pt)
Pt-Fe/SWNT 5.4 1500
Pt/CB E-TEK 20 540
Pt/CB E-TEK* 10 91.5
Pt/CNT* 17.7 311
![Page 21: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/21.jpg)
21
Cyclic Voltammetric Response for O2 reduction
Ep (mV) Ip (mA/mg-Pt)
Pt-Fe/SWNT 472 (± 49) 290 (± 37)
Pt/CB E-TEK 495 (± 85) 72 (± 14)
( ): standard deviation (n > 3)
N2 purgedO2 purged
1 M H2SO4
50 mV/s
![Page 22: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/22.jpg)
22
Linear Sweep Voltammetry
• Better utilization of Pt than the commercial sample.
0 300 600 9000
0.5
1
1.5
2
2.5
3PtCBPt-Fe/SWNT
E /(mV vs. Ag/AgCl)
I /(
A/m
g-P
t)
1 M H2SO4
O2 purged10 mV/s500 rpm
![Page 23: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/23.jpg)
23
Cyclic Voltammetric Response for Methanol Oxidation
w/o methanolw/ 0.1 M methanol
N2 purged1 M H2SO4
50 mV/s
![Page 24: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/24.jpg)
24
Fuel Crossover
• Methanol oxidation occurs at cathode.• De-activate cathode catalyst.
Meier, F.; et al.; J. Membr. Sci. 2004, 241, 137.Mauritz, K.A.; Moore, R.B.; Chem. Rev.2004, 104, 4535.
Potential loss
PEM: Polymer Electrolyte Membrane
![Page 25: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/25.jpg)
25
Interference of Methanol in O2 Reduction
• 0.1 M methanol was added.
• Average current losses– 16 % by Pt-Fe/SWNT.– 40 % by Pt/CB.
• Seems like it is fuel selective.
i/i0 = (current w/ methanol)/(current w/o methanol)
![Page 26: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/26.jpg)
26
Why & How ?
Tafel Plot
Electrochemical Impedance Spectroscopy
![Page 27: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/27.jpg)
Tafel Analysis for Reaction Kinetics
• E vs. ln |i|• Often used in
Corrosion studies.• E0’ is zero overpotential
(Eapp — E0’ = 0) the onset potential.
• i0 is the exchange current. (i0 α kC)
27
-100 400 900
-19
-17
-15
-13
-11
-9
-7
PtFe/SWNT
E /(mV vs. Ag/AgCl)
i /(
ln|i
|)
ln(i0)
E0’
1 M H2SO4
O2 purged1 mV/s500 rpm
![Page 28: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/28.jpg)
28
Tafel Analysis for Reaction Kinetics
• Pt-Fe/SWNT has slower rate of reaction than the commercial catalyst. (!?)
-100 400 900
-19
-17
-15
-13
-11
-9
-7
PtFe/SWNT
Pt/CB
E /(mV vs. Ag/AgCl)
i /(
ln|i
|)
1 M H2SO4
O2 purged1 mV/s500 rpm
E0’ (mV) i0 (A)
Pt-Fe/SWNT 668 (± 28) 1.48 (± 0.32)
Pt/CB E-TEK 713 (± 23) 2.26 (± 0.25)
![Page 29: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/29.jpg)
29
Summary
• Galvanic deposition of Pt using the pre-existing Fe as the core metal is possible.
• Cyclic voltammetry is the cheapest and fastest way of identify Pt.
• Larger Electroactive surface area.• Higher activity towards oxygen reduction.
Better utilization of Pt.
![Page 30: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/30.jpg)
30
• Fuel selectivity of the catalyst towards O2 reduction over methanol oxidation.
• Tafel analysis indicated slow rate of reaction of Pt-Fe/SWNT over Pt/CB.
Summary
![Page 31: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/31.jpg)
31
Future Work
• Investigate how the catalyst can be fuel selective EIS.– Decreasing particle size α increasing charge
transfer resistance decreasing rate of reaction.
• Prepare thicker Pt shell. (Search for the optimal condition)
![Page 32: Application of Galvanic Exchange Reaction for Preparation of Pt coated Fe Nanoparticles supported by Single-Walled Carbon Nanotubes: Fuel Selective Reduction.](https://reader036.fdocuments.in/reader036/viewer/2022062407/56649e355503460f94b24b77/html5/thumbnails/32.jpg)
32
Acknowledgement
• Dr. I. Frank Cheng• Dr. Chien M. Wai• Dr. Chonming Wang
• EPRI (Electric Power Research Institute)• Dr. and Mrs. Renfrew Summer Scholarship• Graduate and Professional Student Association Travel
Award